CN104031488B - A kind of wall dampproof paint - Google Patents
A kind of wall dampproof paint Download PDFInfo
- Publication number
- CN104031488B CN104031488B CN201410275571.6A CN201410275571A CN104031488B CN 104031488 B CN104031488 B CN 104031488B CN 201410275571 A CN201410275571 A CN 201410275571A CN 104031488 B CN104031488 B CN 104031488B
- Authority
- CN
- China
- Prior art keywords
- parts
- naphthenate
- water
- paint
- urea
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of wall dampproof paint, its raw materials by weight portion proportioning is as follows: 100 parts, water; Methyl iso-butyl ketone (MIBK) 20-30 part; Alum 50-60 part; Dimethylbenzene 25-45 part; Urea 15-35 part; Butanols 10-20 part; Polyvinyl alcohol 60-80 part; Zinc powder 5-15 part; Pigment extender 20-30 part; Manganese naphthenate 30-40 part; Ethylene glycol 25-45 part; Cobalt naphthenate 5-25 part; Softening agent 1-10 part; Lead naphthenate 10-20 part; Formaldehyde 15-25 part; Process white 10-30 part; Product soaks 4-8 week non-foaming, not dry linting in saturated calcium hydroxide, surface drying 40-60min; Do solid work 4-6h; Without exception soak 8-10 week in water after; The film 11000-13000 of resistance to wiping time, the widespread production not division of history into periods can replace current material.
Description
Technical field
The application belongs to paint field, particularly relates to a kind of wall dampproof paint.
Background technology
Coating, is called paint in Chinese tradition name.So-called coating is coated in protected or decorated body surface; and the continuous film of firm attachment can be formed with coated article; normally based on resin or oily or emulsion; add or do not add pigment extender, filler; add corresponding additive, with organic solvent or the formulated thick liquid of urea.Paint finishing can bond very well with body material in body surface and form the material of complete and tough and tensile protective membrane, is called coating.Coating and paint are identical concepts.Paint is people's custom titles used for a long time, after introducing China, just utilizes in building trade always.The effect of coating may be summarized to be three aspects: provide protection, decoration function, specific function effect.The general composition of coating: comprise filmogen, color stuffing, solvent, auxiliary agent.
Coating refers to and is applied to body surface and the general name forming the material of tough and tensile protective membrane, and building coating is an important class in coating, in China, generally will be used for inner wall of building, exterior wall, ceiling, ground, and the coating of toilet is called building coating.Building coating has decoration functions, defencive function and livability and improves function.Proportion shared by various function is not quite similar because application target is different.Decoration functions is the function of beautifying the appearance value improving it by buildings.Mainly comprise the design design of plane color, pattern and gloss aspect and the design design of three-dimensional pattern.But to match with the size and shape of the moulding of buildings itself and base material itself, just can fully play out.
Defencive function refers to architecture protection thing not by the impact of environment and the function of destruction.The content that different types of protected body requires defencive function is also different.As just very large in the indoor index difference with reaching required by outdoor application.Building coating is mainly used in the coating products of house decoration as a class, and its market development and real estate industry develop closely related.Since " in history the tightest policy of real estate " is put into effect, market of real estate development is absorbed in low ebb, and since especially entering 2012, the policy of before expecting loosens and do not occur, is that firmly the portion of building clearly represents that in the short period of time, policy of regulation and control can not change on the contrary.Some buildingss to mildew-resistant, fire prevention, heat insulating, corrosion-resistant etc. have particular requirement.Livability improves function mainly for indoor application, contributes to the function improving living environment exactly, as sound-proofing, sound absorbing, antisweat etc.And universal along with humanity concept, and the formation of novel harmonious society, designs that a kind of alkali resistance is good, the wall dampproof paint of fast drying, water tolerance and resistance to wiping excellence is very important.
Summary of the invention
The technical problem solved:
The application, for above-mentioned technical problem, provides a kind of wall dampproof paint, solves that existing wall dampproof paint alkali resistance is poor, dry slow, the technical problem such as water tolerance and resistance to wiping difference.
Technical scheme:
A kind of wall dampproof paint, the raw materials by weight portion proportioning of described wall dampproof paint is as follows: 100 parts, water; Methyl iso-butyl ketone (MIBK) 20-30 part; Alum 50-60 part; Dimethylbenzene 25-45 part; Urea 15-35 part; Butanols 10-20 part; Polyvinyl alcohol 60-80 part; Zinc powder 5-15 part; Pigment extender 20-30 part; Manganese naphthenate 30-40 part; Ethylene glycol 25-45 part; Cobalt naphthenate 5-25 part; Softening agent 1-10 part; Lead naphthenate 10-20 part; Formaldehyde 15-25 part; Process white 10-30 part.
As a preferred technical solution of the present invention: the raw materials by weight portion proportioning of described wall dampproof paint is as follows: 100 parts, water; Methyl iso-butyl ketone (MIBK) 25 parts; 55 parts, alum; Dimethylbenzene 35 parts; 25 parts, urea; 15 parts, butanols; Polyvinyl alcohol 70 parts; Zinc powder 10 parts; Pigment extender 25 parts; Manganese naphthenate 35 parts; Ethylene glycol 35 parts; Cobalt naphthenate 15 parts; 5 parts, softening agent; Lead naphthenate 15 parts; 20 parts, formaldehyde; Process white 20 parts.
As a preferred technical solution of the present invention: described pigment extender adopts light calcium carbonate.
As a preferred technical solution of the present invention: described softening agent adopts dibutyl phthalate.
Beneficial effect:
A kind of wall dampproof paint of the present invention adopts above technical scheme compared with prior art, has following technique effect: 1, product soaks 4-8 week non-foaming, not dry linting in saturated calcium hydroxide, surface drying 40-60min; 2,4-6h is done solid work; Without exception soak 8-10 week in water after; 3, the film 11000-13000 of resistance to wiping time, the widespread production not division of history into periods current material can be replaced.
Embodiment
Embodiment 1:
A kind of wall dampproof paint, its raw materials by weight portion proportioning is as follows: 100 parts, water; Methyl iso-butyl ketone (MIBK) 20 parts; 50 parts, alum; Dimethylbenzene 25 parts; 15 parts, urea; 10 parts, butanols; Polyvinyl alcohol 60 parts; Zinc powder 5 parts; Light calcium carbonate 20 parts; Manganese naphthenate 30 parts; Ethylene glycol 25 parts; Cobalt naphthenate 5 parts; Dibutyl phthalate 1 part; Lead naphthenate 10 parts; 15 parts, formaldehyde; Process white 10 parts.
Methyl iso-butyl ketone (MIBK) is added after dissolving in polyvinyl alcohol, add water, alum, urea, light calcium carbonate, dibutyl phthalate, ethylene glycol, formaldehyde, with ball mill ball milling 30min, then add dimethylbenzene, butanols and surplus stock, ball milling 30min both obtained finished product.
Product soaks 4 weeks non-foaming, not dry lintings in saturated calcium hydroxide, surface drying 60min; Do solid work 6h; Soak after 8 weeks without exception in water; The resistance to wiping of film 11000 times.
Embodiment 2:
A kind of wall dampproof paint, its raw materials by weight portion proportioning is as follows: 100 parts, water; Methyl iso-butyl ketone (MIBK) 30 parts; 60 parts, alum; Dimethylbenzene 45 parts; 35 parts, urea; 20 parts, butanols; Polyvinyl alcohol 80 parts; Zinc powder 15 parts; Light calcium carbonate 30 parts; Manganese naphthenate 40 parts; Ethylene glycol 45 parts; Cobalt naphthenate 25 parts; Dibutyl phthalate 10 parts; Lead naphthenate 20 parts; 25 parts, formaldehyde; Process white 30 parts.
Methyl iso-butyl ketone (MIBK) is added after dissolving in polyvinyl alcohol, add water, alum, urea, light calcium carbonate, dibutyl phthalate, ethylene glycol, formaldehyde, with ball mill ball milling 30min, then add dimethylbenzene, butanols and surplus stock, ball milling 30min both obtained finished product.
Product soaks 6 weeks non-foaming, not dry lintings in saturated calcium hydroxide, surface drying 50min; Do solid work 5h; Soak after 9 weeks without exception in water; The resistance to wiping of film 12000 times.
Embodiment 3:
A kind of wall dampproof paint, its raw materials by weight portion proportioning is as follows: 100 parts, water; Methyl iso-butyl ketone (MIBK) 25 parts; 55 parts, alum; Dimethylbenzene 35 parts; 25 parts, urea; 15 parts, butanols; Polyvinyl alcohol 70 parts; Zinc powder 10 parts; Light calcium carbonate 25 parts; Manganese naphthenate 35 parts; Ethylene glycol 35 parts; Cobalt naphthenate 15 parts; Dibutyl phthalate 5 parts; Lead naphthenate 15 parts; 20 parts, formaldehyde; Process white 20 parts.
Methyl iso-butyl ketone (MIBK) is added after dissolving in polyvinyl alcohol, add water, alum, urea, light calcium carbonate, dibutyl phthalate, ethylene glycol, formaldehyde, with ball mill ball milling 30min, then add dimethylbenzene, butanols and surplus stock, ball milling 30min both obtained finished product.
Product soaks 8 weeks non-foaming, not dry lintings in saturated calcium hydroxide, surface drying 40min; Do solid work 6h; Soak after 10 weeks without exception in water; The resistance to wiping of film 13000 times.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for setting forth content of the present invention, instead of restriction, and any change therefore in the implication suitable with claims of the present invention and scope, all should think to be included in the scope of claims.
Claims (1)
1. a wall dampproof paint, is characterized in that the raw materials by weight portion proportioning of described wall dampproof paint is as follows:
100 parts, water; Methyl iso-butyl ketone (MIBK) 25 parts; 55 parts, alum; Dimethylbenzene 35 parts; 25 parts, urea; 15 parts, butanols; Polyvinyl alcohol 70 parts; Zinc powder 10 parts; Pigment extender 25 parts; Manganese naphthenate 35 parts; Ethylene glycol 35 parts; Cobalt naphthenate 15 parts; 5 parts, softening agent; Lead naphthenate 15 parts; 20 parts, formaldehyde; Process white 20 parts;
Described pigment extender adopts light calcium carbonate;
Described softening agent adopts dibutyl phthalate.