CN103966000B - 一种长效半乳化铜拉丝液 - Google Patents
一种长效半乳化铜拉丝液 Download PDFInfo
- Publication number
- CN103966000B CN103966000B CN201410126239.3A CN201410126239A CN103966000B CN 103966000 B CN103966000 B CN 103966000B CN 201410126239 A CN201410126239 A CN 201410126239A CN 103966000 B CN103966000 B CN 103966000B
- Authority
- CN
- China
- Prior art keywords
- wire drawing
- drawing liquid
- deionized water
- emulsifying
- long
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种拉丝液，具体涉及一种长效半乳化铜拉丝液，本发明拉丝液由以下重量份的原料制成：环氧大豆油18-20、偏苯三酸酯20-25、普鲁兰多糖1-2、聚氧乙烯聚氧丙烯聚戊四醇醚1-2、吐温80？4-5、单甘酯3-5、丁基羟基茴香醚2-3、二硫化钼0.5-1、异噻唑啉酮1-2、助剂4-5、去离子水800-1000；本发明拉丝液以环氧大豆油与偏苯三酸酯混合作为基础油，添加吐温80、单甘酯以及异噻唑啉酮等添加剂，使其氧化安定性好，不易析油、破乳以及酸败等，此外，普鲁兰多糖具有一定的成膜性，能提高拉丝液与金属表面的附着性，降低摩擦系数；本发明制备的拉丝液环保高效、使用寿命长，极大的节约了生产成本。
Description
技术领域
本发明涉及一种拉丝液，具体涉及一种长效半乳化铜拉丝液及其制备工艺。
背景技术
拉丝工艺是一种金属加工工艺，是指金属线材在压力作用下强行通过模具，获得所要求的截面积形状和尺寸的技术加工方法，而拉丝液则是拉丝工艺中必不可少的辅助剂，它主要的作用是在多种铜丝、铝丝多种线材的中拉、小拉、微细拉等拉丝、拉线工艺过程中起润滑作用，兼具保护线材、模具，达到良好的拉丝效果，拉丝液的品质直接影响到拉丝效果，性能优良的拉丝液可以很好的保护模具，减少线材断头、模具磨损现象，兼具防锈、冷却、清洗等作用，反之，则会严重影响拉丝质量；随着拉丝工艺的应用逐渐广泛，市场对拉丝液的品质需求越来越高，现有的拉丝液主要存在乳液稳定性差、腐蚀金属线材、能耗高、不易清洗等问题，制约着拉丝、拉拔质量，急需改进其配方和工艺，使其更为高效环保。
发明内容
本发明的目的在于，提供一种长效半乳化铜拉丝液，以期提高乳化液的使用寿命，为了实现上述目的，本发明采用的技术方案如下：
一种长效半乳化铜拉丝液，其特征在于，本发明材料由以下重量份的原料制成：环氧大豆油18-20、偏苯三酸酯20-25、普鲁兰多糖1-2、聚氧乙烯聚氧丙烯聚戊四醇醚1-2、吐温804-5、单甘酯3-5、丁基羟基茴香醚2-3、二硫化钼0.5-1、异噻唑啉酮1-2、助剂4-5、去离子水800-1000；
所述的助剂由以下重量份的原料制成：油酸异辛酯10-12、膨润土2-3、硬脂酰胺4-5、硅酸钠0.05-0.1、聚氧化乙烯0.1-0.2、硅烷偶联剂KH5500.01-0.02、氯化石蜡421-2、丙二醇脂肪酸酯1-2、去离子水12-15，制备方法为：先将膨润土在600-650℃下高温煅烧2-3h，冷却后研磨成300目粉体，粉体与硅烷偶联剂KH550混合，球磨10-15min后，与硅酸钠、聚氧化乙烯一起加入去离子水中，以500-600转/分钟转速搅拌20-30min，随后对溶液进行喷雾干燥，得到的粉体与其它剩余物料混合，加热至40-50℃，继续搅拌40-50min，搅拌结束冷却至室温，即得浆料。
所述的一种长效半乳化铜拉丝液，其制备工艺为：
（1）先将去离子水加热至50-60℃，加入普鲁兰多糖、吐温80、单甘酯，搅拌至其完全溶解分散，随后加入二硫化钼，充分搅拌至其完全分散，混合液保温备用；
（2）将环氧大豆油、偏苯三酸酯混合，加热至50-60℃，加入聚氧乙烯聚氧丙烯聚戊四醇醚、丁基羟基茴香醚，混合搅拌20-30min，再加入步骤（1）所得的物料及其它剩余物料，搅拌40-50min，搅拌结束后，静置2-3h，即得成品。
本发明制备得到的拉丝液优点在于：以环氧大豆油与偏苯三酸酯混合作为基础油，这类基础油综合了合成酯类油与植物油脂的优点，具有优良的耐高温低温特性，不易挥发，低毒无害，同时为了改善乳化液的氧化安定性，延长使用寿命，在配方中添加了吐温80、单甘酯以及异噻唑啉酮等添加剂，有效的增进了乳化液的氧化安定性，在贮存及使用过程中不易出现析油、破乳以及酸败等现象，普鲁兰多糖具有一定的成膜性，能提高拉丝液与金属表面的附着性，从而降低摩擦系数，保护线材和模具；综上所述，本发明制备的拉丝液环保高效、润滑性能优良、使用寿命长，极大的节约了生产成本。
具体实施方式
实施例
本实施例拉丝液由以下重量份（公斤）的原料制成：环氧大豆油20、偏苯三酸酯25、普鲁兰多糖2、聚氧乙烯聚氧丙烯聚戊四醇醚2、吐温805、单甘酯3、丁基羟基茴香醚3、二硫化钼0.5、异噻唑啉酮2、助剂5、去离子水1000；
助剂由以下重量份的原料制成：油酸异辛酯12、膨润土3、硬脂酰胺5、硅酸钠0.1、聚氧化乙烯0.1、硅烷偶联剂KH5500.02、氯化石蜡421、丙二醇脂肪酸酯2、去离子水15，制备方法为：先将膨润土在600-650℃下高温煅烧3h，冷却后研磨成300目粉体，粉体与硅烷偶联剂KH550混合，球磨15min后，与硅酸钠、聚氧化乙烯一起加入去离子水中，以600转/分钟转速搅拌25min，随后对溶液进行喷雾干燥，得到的粉体与其它剩余物料混合，加热至50℃，继续搅拌50min，搅拌结束冷却至室温，即得浆料。
所述的一种长效半乳化铜拉丝液，其制备工艺为：
（1）先将去离子水加热至50-60℃，加入普鲁兰多糖、吐温80、单甘酯，搅拌至其完全溶解分散，随后加入二硫化钼，充分搅拌至其完全分散，混合液保温备用；
（2）将环氧大豆油、偏苯三酸酯混合，加热至50-60℃，加入聚氧乙烯聚氧丙烯聚戊四醇醚、丁基羟基茴香醚，混合搅拌30min，再加入步骤（1）所得的物料及其它剩余物料，搅拌50min，搅拌结束后，静置3h，即得成品。
本发明拉丝液在常温下可贮存至少1.5年以上，换液周期延长至10个月以上，拉丝时不易断线，线材表面光洁无垢，其具体测试性能指标如下：
| 项目 | 指标 |
| 运动粘度（50℃） | ≤100mm2/s |
| 凝点 | ≤-5℃ |
| pH值 | 7.6 |
| 乳化液腐蚀（55±2）℃，全浸铜片1h | 合格 |
| 乳化液稳定性（15-35℃）1h | 无分层，无沉淀，无皂、油析出 |
| 消泡性（55±2℃,5min） | ≤4mL |
Claims (1)
1.一种长效半乳化铜拉丝液，其特征在于，该拉丝液由以下重量份的原料制成：环氧大豆油18-20、偏苯三酸酯20-25、普鲁兰多糖1-2、聚氧乙烯聚氧丙烯聚戊四醇醚1-2、吐温804-5、单甘酯3-5、丁基羟基茴香醚2-3、二硫化钼0.5-1、异噻唑啉酮1-2、助剂4-5、去离子水800-1000；
所述的助剂由以下重量份的原料制成：油酸异辛酯10-12、膨润土2-3、硬脂酰胺4-5、硅酸钠0.05-0.1、聚氧化乙烯0.1-0.2、硅烷偶联剂KH5500.01-0.02、氯化石蜡421-2、丙二醇脂肪酸酯1-2、去离子水12-15，制备方法为：先将膨润土在600-650℃下高温煅烧2-3h，冷却后研磨成300目粉体，粉体与硅烷偶联剂KH550混合，球磨10-15min后，与硅酸钠、聚氧化乙烯一起加入去离子水中，以500-600转/分钟转速搅拌20-30min，随后对溶液进行喷雾干燥，得到的粉体与其它剩余物料混合，加热至40-50℃，继续搅拌40-50min，搅拌结束冷却至室温，即得浆料；
所述一种长效半乳化铜拉丝液的制备工艺如下：
（1）先将去离子水加热至50-60℃，加入普鲁兰多糖、吐温80、单甘酯，搅拌至其完全溶解分散，随后加入二硫化钼，充分搅拌至其完全分散，混合液保温备用；
（2）将环氧大豆油、偏苯三酸酯混合，加热至50-60℃，加入聚氧乙烯聚氧丙烯聚戊四醇醚、丁基羟基茴香醚，混合搅拌20-30min，再加入步骤（1）所得的物料及其它剩余物料，搅拌40-50min，搅拌结束后，静置2-3h，即得成品。