CN103614011B - 一种含有牡蛎壳粉的防水涂料 - Google Patents

一种含有牡蛎壳粉的防水涂料 Download PDF

Info

Publication number
CN103614011B
CN103614011B CN201310516014.4A CN201310516014A CN103614011B CN 103614011 B CN103614011 B CN 103614011B CN 201310516014 A CN201310516014 A CN 201310516014A CN 103614011 B CN103614011 B CN 103614011B
Authority
CN
China
Prior art keywords
shell powder
oyster shell
waterproof paint
powder
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310516014.4A
Other languages
English (en)
Other versions
CN103614011A (zh
Inventor
肖宪书
文庆华
张俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU GAOHUA ELECTRONIC Co.,Ltd.
Original Assignee
BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU CITY GAOHUA ELECTRONIC Co Ltd filed Critical BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Priority to CN201310516014.4A priority Critical patent/CN103614011B/zh
Publication of CN103614011A publication Critical patent/CN103614011A/zh
Application granted granted Critical
Publication of CN103614011B publication Critical patent/CN103614011B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有牡蛎壳粉的防水涂料，它是由下述重量份的原料组成的：vae乳液50-57、牡蛎壳粉6-10、珍珠贝粉4-6、钟乳石粉2-4、丙三醇三甘油酸酯1-2、聚苯并咪唑纤维2-3、六溴环十二烷1-2、乙二醇2-3、聚乙烯蜡2-3、亚磷酸二氢钾0.5-1、三聚磷酸钠1-2、抗氧化剂1010？0.4-1、粘结助剂7-10、去离子水6-20，本发明的防水涂料流平性好，涂层稳定，附着力强，涂层表面有很强的硬度，抗破坏力好。

Description

一种含有牡蛎壳粉的防水涂料
技术领域
本发明主要涉及一种涂料，尤其涉及一种含有牡蛎壳粉的防水涂料。
背景技术
涂刷在建筑物表面上，经溶剂或水分的挥发或两种组分的化学反应形成一层薄膜，使建筑物表面与水隔绝，从而起到防水、密封的作用，这些涂刷的粘稠液体称为防水涂料。防水涂料经固化后形成的防水薄膜具有一定的延伸性、弹塑性、抗裂性、抗渗性及耐候性，能起到防水、防渗和保护作用。防水涂料有良好的温度适应性，操作简便，易于维修与维护。
发明内容
本发明目的就是提供一种含有牡蛎壳粉的防水涂料。
本发明是通过以下技术方案实现的：
一种含有牡蛎壳粉的防水涂料，它是由下述重量份的原料组成的：
vae乳液50-57、牡蛎壳粉6-10、珍珠贝粉4-6、钟乳石粉2-4、丙三醇三甘油酸酯1-2、聚苯并咪唑纤维2-3、六溴环十二烷1-2、乙二醇2-3、聚乙烯蜡2-3、亚磷酸二氢钾0.5-1、三聚磷酸钠1-2、抗氧化剂10100.4-1、粘结助剂7-10、去离子水6-20；
所述的粘结助剂是由下述重量份的原料组成的：
Eva乳液40-45、异丙醇铝3-5、聚酰胺蜡微粉3-4、硅烷偶联剂KH-5501-2、硬酯酸单甘油酯2-4、尿素2-3、纳米碳0.1-1；
将上述异丙醇铝加热到130-135℃，加入聚酰胺蜡微粉，球磨后造粒，将尿素与硬酯酸单甘油酯混合，在100-120℃下搅拌反应10-15分钟，冷却至常温，加入硅烷偶联剂KH-550、纳米碳，200-300转/分搅拌分散3-4分钟，与上述得到的粒子和剩余各原料混合，充分球磨，即得所述粘结助剂。
一种含有牡蛎壳粉的防水涂料的制备方法，包括以下步骤：
将上述牡蛎壳粉、珍珠贝粉、钟乳石粉混合，200-300℃下混合搅拌3-5分钟，降低温度为60-70℃，加入三聚磷酸钠和上述重量40-60%的去离子水，1000-1600转/分搅拌分散10-15分钟，冷却至常温，加入剩余各原料，高速搅拌至混合均匀，即得所述含有牡蛎壳粉的防水涂料。
本发明的优点是：
本发明的防水涂料流平性好，涂层稳定，附着力强，涂层表面有很强的硬度，抗破坏力好。
具体实施方式
实施例1
一种含有牡蛎壳粉的防水涂料，它是由下述重量份（公斤）的原料组成的：
vae乳液57、牡蛎壳粉10、珍珠贝粉6、钟乳石粉2、丙三醇三甘油酸酯2、聚苯并咪唑纤维2、六溴环十二烷1、乙二醇3、聚乙烯蜡3、亚磷酸二氢钾0.5、三聚磷酸钠1、抗氧化剂10100.4、粘结助剂10、去离子水20；
所述的粘结助剂是由下述重量份的原料组成的：
Eva乳液45、异丙醇铝5、聚酰胺蜡微粉3、硅烷偶联剂KH-5501-2、硬酯酸单甘油酯2、尿素2、纳米碳0.1；
将上述异丙醇铝加热到135℃，加入聚酰胺蜡微粉，球磨后造粒，将尿素与硬酯酸单甘油酯混合，在120℃下搅拌反应15分钟，冷却至常温，加入硅烷偶联剂KH-550、纳米碳，300转/分搅拌分散4分钟，与上述得到的粒子和剩余各原料混合，充分球磨，即得所述粘结助剂。
一种含有牡蛎壳粉的防水涂料的制备方法，包括以下步骤：
将上述牡蛎壳粉、珍珠贝粉、钟乳石粉混合，300℃下混合搅拌5分钟，降低温度为70℃，加入三聚磷酸钠和上述重量60%的去离子水，1600转/分搅拌分散15分钟，冷却至常温，加入剩余各原料，高速搅拌至混合均匀，即得所述含有牡蛎壳粉的防水涂料。
性能测试：
延伸率：≥300％；
不透水性：0.3MPa(一个小时不透水)。

Claims (2)

1.一种含有牡蛎壳粉的防水涂料，其特征在于它是由下述重量份的原料制成的：vae乳液50-57、牡蛎壳粉6-10、珍珠贝粉4-6、钟乳石粉2-4、丙三醇三甘油酸酯1-2、聚苯并咪唑纤维2-3、六溴环十二烷1-2、乙二醇2-3、聚乙烯蜡2-3、亚磷酸二氢钾0.5-1、三聚磷酸钠1-2、抗氧化剂10100.4-1、粘结助剂7-10、去离子水6-20；所述的粘结助剂是由下述重量份的原料组成的：EVA乳液40-45、异丙醇铝3-5、聚酰胺蜡微粉3-4、硅烷偶联剂KH-5501-2、硬酯酸单甘油酯2-4、尿素2-3、纳米碳0.1-1；将上述异丙醇铝加热到130-135℃，加入聚酰胺蜡微粉，球磨后造粒，将尿素与硬酯酸单甘油酯混合，在100-120℃下搅拌反应10-15分钟，冷却至常温，加入硅烷偶联剂KH-550、纳米碳，200-300转/分搅拌分散3-4分钟，与上述得到的粒子和剩余各原料混合，充分球磨，即得所述粘结助剂。
2.一种如权利要求1所述的含有牡蛎壳粉的防水涂料的制备方法，其特征在于包括以下步骤：将上述牡蛎壳粉、珍珠贝粉、钟乳石粉混合，200-300℃下混合搅拌3-5分钟，降低温度为60-70℃，加入三聚磷酸钠和上述重量40-60%的去离子水，1000-1600转/分搅拌分散10-15分钟，冷却至常温，加入剩余各原料，高速搅拌至混合均匀，即得所述含有牡蛎壳粉的防水涂料。
CN201310516014.4A 2013-10-28 2013-10-28 一种含有牡蛎壳粉的防水涂料 Active CN103614011B (zh)