CN103614011B - A kind of waterproof paint containing oyster shell powder - Google Patents
A kind of waterproof paint containing oyster shell powder Download PDFInfo
- Publication number
- CN103614011B CN103614011B CN201310516014.4A CN201310516014A CN103614011B CN 103614011 B CN103614011 B CN 103614011B CN 201310516014 A CN201310516014 A CN 201310516014A CN 103614011 B CN103614011 B CN 103614011B
- Authority
- CN
- China
- Prior art keywords
- shell powder
- oyster shell
- waterproof paint
- powder
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of waterproof paint containing oyster shell powder, it is made up of the raw material of following weight parts: vae emulsion 50-57, oyster shell powder 6-10, pearl shell powder 4-6, Stalactitum powder 2-4, glycerol glycerinate 1-2, polybenzimidazole fibre 2-3, hexabromocyclododecane 1-2, ethylene glycol 2-3, polyethylene wax 2-3, potassium dihydrogen phosphite 0.5-1, tripoly phosphate sodium STPP 1-2, antioxidant 1010? 0.4-1, adhesive aid 7-10, deionized water 6-20, waterproof paint good leveling property of the present invention, coating stable, strong adhesion, coatingsurface has very strong hardness, collapse resistance power is good.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of waterproof paint containing oyster shell powder.
Background technology
Brushing is on building surface, and form thin film through the volatilization of solvent or moisture or the chemical reaction of two kinds of components, building surface and water are completely cut off, thus plays the effect of waterproof, sealing, these thick liquids brushed are called waterproof paint.The waterproofing membrane that waterproof paint is formed after solidification has certain extensibility, elastoplasticity, splitting resistance, impermeability and weathering resistance, can play waterproof, prevent blending provide protection.Waterproof paint has good thermal adaptability, easy and simple to handle, for ease of maintenaince with maintenance.
Summary of the invention
The object of the invention is just to provide a kind of waterproof paint containing oyster shell powder.
The present invention is achieved by the following technical solutions:
A waterproof paint containing oyster shell powder, it is made up of the raw material of following weight parts:
Vae emulsion 50-57, oyster shell powder 6-10, pearl shell powder 4-6, Stalactitum powder 2-4, glycerol glycerinate 1-2, polybenzimidazole fibre 2-3, hexabromocyclododecane 1-2, ethylene glycol 2-3, polyethylene wax 2-3, potassium dihydrogen phosphite 0.5-1, tripoly phosphate sodium STPP 1-2, antioxidant 1010 0.4-1, adhesive aid 7-10, deionized water 6-20;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 40-45, aluminum isopropylate 3-5, polyamide wax micropowder 3-4, silane resin acceptor kh-550 1-2, stearic acid direactive glyceride 2-4, urea 2-3, nano-sized carbon 0.1-1;
Above-mentioned aluminum isopropylate is heated to 130-135 DEG C, add polyamide wax micropowder, granulation after ball milling, mixes urea with stearic acid direactive glyceride, stirring reaction 10-15 minute at 100-120 DEG C, be cooled to normal temperature, add silane resin acceptor kh-550, nano-sized carbon, 200-300 rev/min of dispersed with stirring 3-4 minute, with particle obtained above with remain each raw material and mix, abundant ball milling, obtains described adhesive aid.
A preparation method for waterproof paint containing oyster shell powder, comprises the following steps:
By above-mentioned oyster shell powder, pearl shell powder, the mixing of Stalactitum powder, mix and blend 3-5 minute at 200-300 DEG C, reduction temperature is 60-70 DEG C, add the deionized water of tripoly phosphate sodium STPP and above-mentioned weight 40-60%, 1000-1600 rev/min of dispersed with stirring 10-15 minute, is cooled to normal temperature, adds each raw material of residue, high-speed stirring, to mixing, obtains the described waterproof paint containing oyster shell powder.
Advantage of the present invention is:
Waterproof paint good leveling property of the present invention, coating stable, strong adhesion, coatingsurface has very strong hardness, and collapse resistance power is good.
Embodiment
Embodiment 1
A waterproof paint containing oyster shell powder, it is made up of the raw material of following weight parts (kilogram):
Vae emulsion 57, oyster shell powder 10, pearl shell powder 6, Stalactitum powder 2, glycerol glycerinate 2, polybenzimidazole fibre 2, hexabromocyclododecane 1, ethylene glycol 3, polyethylene wax 3, potassium dihydrogen phosphite 0.5, tripoly phosphate sodium STPP 1, antioxidant 1010 0.4, adhesive aid 10, deionized water 20;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 45, aluminum isopropylate 5, polyamide wax micropowder 3, silane resin acceptor kh-550 1-2, stearic acid direactive glyceride 2, urea 2, nano-sized carbon 0.1;
Above-mentioned aluminum isopropylate is heated to 135 DEG C, add polyamide wax micropowder, granulation after ball milling, mixes urea with stearic acid direactive glyceride, stirring reaction 15 minutes at 120 DEG C, be cooled to normal temperature, add silane resin acceptor kh-550, nano-sized carbon, 300 revs/min of dispersed with stirring 4 minutes, with particle obtained above with remain each raw material and mix, abundant ball milling, obtains described adhesive aid.
A preparation method for waterproof paint containing oyster shell powder, comprises the following steps:
By above-mentioned oyster shell powder, pearl shell powder, the mixing of Stalactitum powder, mix and blend 5 minutes at 300 DEG C, reducing temperature is 70 DEG C, add the deionized water of tripoly phosphate sodium STPP and above-mentioned weight 60%, 1600 revs/min of dispersed with stirring 15 minutes, are cooled to normal temperature, add each raw material of residue, high-speed stirring, to mixing, obtains the described waterproof paint containing oyster shell powder.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. the waterproof paint containing oyster shell powder, is characterized in that it is made up of the raw material of following weight parts: vae emulsion 50-57, oyster shell powder 6-10, pearl shell powder 4-6, Stalactitum powder 2-4, glycerol glycerinate 1-2, polybenzimidazole fibre 2-3, hexabromocyclododecane 1-2, ethylene glycol 2-3, polyethylene wax 2-3, potassium dihydrogen phosphite 0.5-1, tripoly phosphate sodium STPP 1-2, antioxidant 1010 0.4-1, adhesive aid 7-10, deionized water 6-20; Described adhesive aid is made up of the raw material of following weight parts: EVA emulsion 40-45, aluminum isopropylate 3-5, polyamide wax micropowder 3-4, silane resin acceptor kh-550 1-2, stearic acid direactive glyceride 2-4, urea 2-3, nano-sized carbon 0.1-1; Above-mentioned aluminum isopropylate is heated to 130-135 DEG C, add polyamide wax micropowder, granulation after ball milling, mixes urea with stearic acid direactive glyceride, stirring reaction 10-15 minute at 100-120 DEG C, be cooled to normal temperature, add silane resin acceptor kh-550, nano-sized carbon, 200-300 rev/min of dispersed with stirring 3-4 minute, with particle obtained above with remain each raw material and mix, abundant ball milling, obtains described adhesive aid.
2. the preparation method of the waterproof paint as claimed in claim 1 containing oyster shell powder, it is characterized in that comprising the following steps: by above-mentioned oyster shell powder, pearl shell powder, the mixing of Stalactitum powder, mix and blend 3-5 minute at 200-300 DEG C, reduction temperature is 60-70 DEG C, add the deionized water of tripoly phosphate sodium STPP and above-mentioned weight 40-60%, 1000-1600 rev/min of dispersed with stirring 10-15 minute, be cooled to normal temperature, add each raw material of residue, high-speed stirring, to mixing, obtains the described waterproof paint containing oyster shell powder.