CN101063016A - 用牡蛎壳制备的吸音环保涂料 - Google Patents
用牡蛎壳制备的吸音环保涂料 Download PDFInfo
- Publication number
- CN101063016A CN101063016A CN 200610035132 CN200610035132A CN101063016A CN 101063016 A CN101063016 A CN 101063016A CN 200610035132 CN200610035132 CN 200610035132 CN 200610035132 A CN200610035132 A CN 200610035132A CN 101063016 A CN101063016 A CN 101063016A
- Authority
- CN
- China
- Prior art keywords
- oyster shell
- sound
- environment protection
- protection paint
- absorbing environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种用牡蛎壳制备的吸音环保涂料,由于牡蛎壳粉多孔、质轻的特性,因而使涂料具有良好的吸音效果;又由于牡蛎壳粉具有强度高、耐磨性好的特性,因而具有良好的抗拉力作用和色泽好的效果。
Description
用牡蛎壳制备的吸音环保涂料,属建筑涂料。
牡蛎壳粉是一种多孔材料,它具有强度高、耐磨性好、质轻、密度小、导热系数低等特性。目前牡蛎壳用于煅烧成石灰或用于作为活性钙的主要成分,但牡蛎壳粉尚未应用于建筑涂料中,而且目前建筑涂料存在无吸音效果、抗拉力(弹性)差、色彩光泽细腻缺乏等缺点。
本发明的目的在于提供一种用牡蛎壳制备的吸音环保涂料,该涂料具有吸音、抗拉力强、色泽好的特性。
本发明通过以下措施实现:用牡蛎壳制备的吸音环保涂料由涂料和牡蛎壳粉组成,牡蛎壳粉所占总质量百分比为1-7。
所述的牡蛎壳粉为牡蛎壳清洗干净,粉碎至20-200目,加入牡蛎壳质量十倍的0.1M/L的稀盐酸,浸泡、搅拌10--20分钟,以通孔穴而成的粉末。
所述的涂料主要有水乳液、乳化液、粘联剂、消泡剂、钛白粉、双飞粉组成,各组分所占总质量百分比为:
水乳液 44-56 乳化剂 9-12
粘联剂 4-8 消泡剂 1-3
钛白粉 7-10 双飞粉 11-20
所述的水乳液可以是聚醋酸乙烯或PVA等;乳化液是非离子型的OP-10和阴离子型的十二烷基苯磺酸钠复合乳化剂。
所述的涂料各组分所占总质量的最佳百分比为:
水乳液 50 乳化剂 10
粘联剂 9 消泡剂 3
钛白粉 10 双飞粉 12
实施实例:
首先把水乳液、乳化剂、粘联剂倒入容器中,加入牡蛎壳粉、钛白粉、双飞粉分散研磨,均匀后倒入混合器,搅拌均匀,研磨过滤,经检验进入包装得用牡蛎壳制备的吸音环保涂料。
本发明在建筑涂料中采用牡蛎壳粉,由于牡蛎壳粉多孔、质轻的特性,因而使涂料具有良好的吸音效果;又由于牡蛎壳粉具有强度高、耐磨性好的特性,因而具有良好的抗拉力作用和色泽好的效果。
残音室内吸音率:
规格(mm) | 性能 | ||
密度(kg/m3) | 吸声系数(相应频率) | 混响室 | |
300×300×(10或18或20) | 49 | 0.45~0.99 | ≥0.45 |
抗拉力:
序号 | 项目 | 指标 |
1 | 抗拉强度Mpa | ≥1.66 |
2 | 延伸率% | ≥250 |
3 | 低温柔性C | -20℃ |
4 | 潮湿基面粘强度Mpa | ≥0.5 |
5 | 涂膜表面干时间h | ≤7.5 |
6 | 涂膜实干时间h | ≤24 |
7 | 抗渗性Mpa | ≥0.7 |
8 | 固体含量 | ≥95 |
绿色指标(HJBZ-1999):
序号 | 项目 | 指标 |
1 | 有机挥发物VOC< | 250g/l |
2 | 重金属化合物(以铅计)< | 500mg/kg |
3 | 甲醛及其甲醛聚合物< | 500mg/kg |
4 | 负离子浓度(25℃) | 2×10个CM3 |
5 | 抗菌性(霉菌、细菌) | 55-60% |
6 | 无异味 | 14-19% |
Claims (3)
1.用牡蛎壳制备的吸音环保涂料,其特征是:它由涂料和牡蛎壳粉组成。
2.据权利要求1所述的用牡蛎壳制备的吸音环保涂料,其特征是:所述的涂料主要有水乳液、乳化液、粘联剂、消泡剂、钛白粉、双飞粉组成,各组分所占总质量百分比为:
水乳液 44-56 乳化剂 9-12
粘联剂 4-8 消泡剂 1-3
钛白粉 7-10 双飞粉 11-20
3.据权利要求1所述的用牡蛎壳制备的吸音环保涂料,其特征是:所述的涂料各组分所占总质量的最佳百分比为:
水乳液 50 乳化剂 10
粘联剂 9 消泡剂 3
钛白粉 10 双飞粉 12