CN103613147A - La0.7Sr0.3CoO3钙钛矿复合材料的制备 - Google Patents
La0.7Sr0.3CoO3钙钛矿复合材料的制备 Download PDFInfo
- Publication number
- CN103613147A CN103613147A CN201310650618.8A CN201310650618A CN103613147A CN 103613147 A CN103613147 A CN 103613147A CN 201310650618 A CN201310650618 A CN 201310650618A CN 103613147 A CN103613147 A CN 103613147A
- Authority
- CN
- China
- Prior art keywords
- solution
- room temperature
- preparation
- pmma
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种La0.7Sr0.3CoO3钙钛矿复合材料的制备方法。该方法过程包括将K2S2O8溶液与甲基丙烯酸甲酯和丙烯酸的混合溶液反应,得到含聚甲基丙烯酸甲酯小球的微乳液;将乳液离心分离得到PMMA胶体晶体;按照摩尔比配制La(NO3)3·6H2O、Sr(NO3)2和Co(NO3)2·6H2O的浸渍液,将该浸渍液与得到的PMMA胶晶粉末等体积浸渍,经焙烧得到三维大孔La0.7Sr0.3CoO3钙钛矿结构材料。本发明优点在于可以克服普通聚合物微球耐热性差,高温处理大孔结构容易坍塌的缺点,可以得到完美的三维大孔La0.7Sr0.3CoO3钙钛矿复合材料。
Description
技术领域
本发明涉及一种La 0.7 Sr 0.3 CoO 3 钙钛矿复合材料的制备方法,属于钙钛矿型复合材料的技术领域。
背景技术
目前制备三维有序La 0.7 Sr 0.3 CoO 3 钙钛矿复合材料最有效的方法,是以单分散聚合物微球为模板的胶体晶体模板法。但由于普通聚合物微球的耐热性能差,导致胶体晶体模板的热稳定性较低,在600℃到800℃高温热处理时会导致大孔结构的坍塌。由于钙钛矿氧化物需要高温热处理才能得到完美的晶型,因此这种方法具有很大的缺陷。
发明内容
本发明的目的在于提供一种La
0.7
Sr
0.3
CoO
3
钙钛矿复合材料的制备方法,该方法能在高温下制得三维有序、晶体完美的La
0.7
Sr
0.3
CoO
3
钙钛矿复合材料。
本发明是通过下述技术方案加以实现的,一种La
0.7
Sr
0.3
CoO
3
钙钛矿复合材料的制备方法,其制备过程包括以下步骤:
(1)在室温下,将K
2
S
2
O
8
加入去离子水中配成3.2×10
-3
g/ml的溶液,将甲基丙烯酸甲酯(MMA)和丙烯酸(AA)按照体积比10:1配制成混合溶液,在搅拌下升温至75
,按K
2
S
2
O
8
溶液与混合液的体积比为10:1向K
2
S
2
O
8
溶液中加入混合溶液,在N
2
保护下反应2h,得到白色的乳液,冷却至室温,超声30min,得到含聚甲基丙烯酸甲酯(PMMA)小球的微乳液;
(2)将含有PMMA微球的白色乳液离心分离,得到PMMA胶体晶体;
(3)按照7:3:10的摩尔比称取一定量的La(NO
3
)
3
·6H
2
O、Sr(NO
3
)
2
和Co(NO
3
)
2
·6H
2
O,将其分别溶于按体积比为6:4的乙二醇(EG)和甲醇(Me)混合溶液中,采用超声震荡促进其溶解,配制成0.3mol/L浓度的金属离子浸渍液,将该浸渍液与步骤(2)得到的PMMA胶晶粉末等体积浸渍,超声分散后,静置5h,室温干燥后,置于管式炉中在空气气氛下700℃焙烧5h,最终得到大孔钙钛矿结构材料。
本发明优点在于可以克服普通聚合物微球耐热性差,高温处理大孔结构容易坍塌的缺点,可以得到完美的三维大孔La
0.7
Sr
0.3
CoO
3
钙钛矿复合材料。
附图说明:
图1为实施例1中所制得的三维有序大孔的La
0.7
Sr
0.3
CoO
3
钙钛矿复合材料的SEM图。
具体实施方式
实施例1
La 0.7 Sr 0.3 CoO 3 钙钛矿制备:取1.6g的K 2 S 2 O 8 溶解于500mL去离子水中加入三口烧瓶,在恒压漏斗中加入45.5mL的甲基丙烯酸甲酯(MMA)和4.5mL的丙烯酸(AA),室温下向溶液中通入流速为10ml/min的N 2 ,在350rpm的搅拌速度下持续搅拌1h后,升温至75 ,打开恒压漏斗,慢慢滴加MMA和AA的混合溶液,待完全加入后,在75反应2h,得到白色的乳液,停止加热,维持搅拌冷却至室温,抽滤掉大块的爆聚物,超声30min,得到含PMMA小球的微乳液。此乳液离心,得到PMMA胶体晶体。再分别称取的7.5779g La(NO 3 ) 3 ·6H 2 O、1.5872g 的Sr(NO 3 ) 2 和7.2758g 的Co(NO 3 ) 2 ·6H 2 O,将其溶解于75ml的乙二醇(EG)和甲醇(Me)混合溶液中,采用超声震荡促进其溶解,得到金属离子浸渍液。取7.25ml金属离子浸渍液滴加到5g PMMA胶晶粉末上,10min促进溶液分散后,静置5h,干燥后,置于管式炉中在空气气氛下700℃焙烧,最终得到大孔钙钛矿结构材料。
Claims (1)
1.一种La0.7Sr0.3CoO3钙钛矿复合材料的制备方法,其制备过程包括以下步骤:
(1)在室温下,将K2S2O8加入去离子水中配成3.2×10-3g/ml的溶液,将甲基丙烯酸甲酯和丙烯酸按照体积比10:1配制成混合溶液,在搅拌下升温至75 ,按K2S2O8溶液与混合液的体积比为10:1向K2S2O8溶液中加入混合溶液,在N2保护下反应2h,得到白色的乳液,冷却至室温,超声30min,得到含聚甲基丙烯酸甲酯小球的微乳液;
(2)将含有聚甲基丙烯酸甲酯微球的白色乳液离心分离,得到聚甲基丙烯酸甲酯胶体晶体;
(3)按照7:3:10的摩尔比称取一定量的La(NO3)3·6H2O、Sr(NO3)2和Co(NO3)2·6H2O,将其分别溶于按体积比为6:4的乙二醇和甲醇混合溶液中,采用超声震荡促进其溶解,配制成0.3mol/L浓度的金属离子浸渍液,将该浸渍液与步骤(2)得到的聚甲基丙烯酸甲酯胶晶粉末等体积浸渍,超声分散后,静置5h,室温干燥后,置于管式炉中在空气气氛下700℃焙烧5h,得到大孔钙钛矿结构材料。