CN105238910A - 一种六角轴热处理工艺 - Google Patents
一种六角轴热处理工艺 Download PDFInfo
- Publication number
- CN105238910A CN105238910A CN201510767741.7A CN201510767741A CN105238910A CN 105238910 A CN105238910 A CN 105238910A CN 201510767741 A CN201510767741 A CN 201510767741A CN 105238910 A CN105238910 A CN 105238910A
- Authority
- CN
- China
- Prior art keywords
- hexagonal axis
- carbon potential
- controlling
- heat
- heating furnace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种六角轴热处理工艺,其包括以下步骤:A、将六角轴放入加热炉中,并将加热炉加热至900-920℃,恒温保持30-40min,控制此期间加热炉中的碳势为0.90-1.00%;B、强渗处理,强渗时间200min,控制此期间加热炉内碳势在0.90-1.00%;C、扩散阶段,扩散时间50min,控制此期间加热炉内碳势在0.70-0.80%;D、降温处理,降温至800℃,并恒温保持60min,控制此期间加热炉内碳势在0.70-0.80%;E、油淬处理,油淬温度为130℃,控制此期间碳势在0.70-0.80%;F、回火处理,加热至160-180℃,保温时间200min;G、空冷至室温,完成热处理并入库。本发明六角轴热处理工艺,工序简单、处理成本低,能提高六角轴的质量稳定性。
Description
技术领域
本发明涉及一种热处理工艺,特别涉及一种六角轴热处理工艺。
背景技术
六角轴是汽车部件上一个重要部件,其由圆柱体和六角轴体焊接而成,由于其是关键部件,因此对其质量要求有极高要求。传统的热处理工艺工序复杂,成本高。
发明内容
【1】要解决的技术问题
本发明要解决的技术问题是提供一种工序简单、成本低的六角轴热处理工艺。
【2】解决问题的技术方案
本发明提供一种六角轴热处理工艺,其包括以下步骤:
A、将六角轴放入加热炉中,并将加热炉加热至900-920℃,恒温保持30-40min,控制此期间加热炉中的碳势为0.90-1.00%;
B、强渗处理,强渗时间200min,控制此期间加热炉内碳势在0.90-1.00%;
C、扩散阶段,扩散时间50min,控制此期间加热炉内碳势在0.70-0.80%;
D、降温处理,降温至800℃,并恒温保持60min,控制此期间加热炉内碳势在0.70-0.80%;
E、油淬处理,油淬温度为130℃,控制此期间碳势在0.70-0.80%;
F、回火处理,加热至160-180℃,保温时间200min;
G、空冷至室温,完成热处理并入库。
【3】有益效果
本发明六角轴热处理工艺,工序简单、处理成本低,能提高六角轴的质量稳定性。
具体实施方式
下面详细介绍本发明实施例。
本发明提供一种六角轴热处理工艺,其包括以下步骤:
A、将六角轴放入加热炉中,并将加热炉加热至900-920℃,恒温保持30-40min,控制此期间加热炉中的碳势为0.90-1.00%;
B、强渗处理,强渗时间200min,控制此期间加热炉内碳势在0.90-1.00%;
C、扩散阶段,扩散时间50min,控制此期间加热炉内碳势在0.70-0.80%;
D、降温处理,降温至800℃,并恒温保持60min,控制此期间加热炉内碳势在0.70-0.80%;
E、油淬处理,油淬温度为130℃,控制此期间碳势在0.70-0.80%;
F、回火处理,加热至160-180℃,保温时间200min;
G、空冷至室温,完成热处理并入库。
本发明六角轴热处理工艺,工序简单、处理成本低,能提高六角轴的质量稳定性。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.一种六角轴热处理工艺,其特征在于,包括以下步骤:
A、将六角轴放入加热炉中,并将加热炉加热至900-920℃,恒温保持30-40min,控制此期间加热炉中的碳势为0.90-1.00%;
B、强渗处理,强渗时间200min,控制此期间加热炉内碳势在0.90-1.00%;
C、扩散阶段,扩散时间50min,控制此期间加热炉内碳势在0.70-0.80%;
D、降温处理,降温至800℃,并恒温保持60min,控制此期间加热炉内碳势在0.70-0.80%;
E、油淬处理,油淬温度为130℃,控制此期间碳势在0.70-0.80%;
F、回火处理,加热至160-180℃,保温时间200min;
G、空冷至室温,完成热处理并入库。