CN103382366A - High-temperature resistance organic silicon impregnating varnish and preparation method thereof - Google Patents
High-temperature resistance organic silicon impregnating varnish and preparation method thereof Download PDFInfo
- Publication number
- CN103382366A CN103382366A CN2013102615951A CN201310261595A CN103382366A CN 103382366 A CN103382366 A CN 103382366A CN 2013102615951 A CN2013102615951 A CN 2013102615951A CN 201310261595 A CN201310261595 A CN 201310261595A CN 103382366 A CN103382366 A CN 103382366A
- Authority
- CN
- China
- Prior art keywords
- parts
- varnish
- preparation
- resistance
- impregnating varnish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A high-temperature resistance organic silicon impregnating varnish and a preparation method thereof are disclosed. The varnish is characterized by being composed of following components in parts by weight: 32 to 35 parts of organic silicon resin, 2 to 3 parts of vinyl triamine, 6 to 8 parts of alkyd resin, 10 to 12 parts of ethyl acetate, 14 to 16 parts of E-12 epoxy resin, 4 to 6 parts of maleic anhydride, 6 to 7 parts of glycol, 2 to 3 parts of dibutyltin dilaurate, 1 to 2 parts of cyanuric acid zinc, 4 to 5 parts of polyisobutylene, 2 to 3 parts of rosin acid polyoxyethylene ester, 3 to 4 parts of vinyl tri(beta- methoxyl ethoxyl) silane, 35 to 38 parts of xylene and 4 to 5 parts of film forming agent. The impregnating varnish has the advantages of good varnish membrane toughness, high impact resistance strength, varnish membrane compactness, yellowing resistance, high-temperature resistance, high dampness resistance, corrosion resistance, good electric insulation property and high mechanic strength, the heat conductivity of the varnish is improved, so the varnish can work at the temperature of 200 DEG C for a long period, and at the temperature of 220 DEG C for a short period, and the design requirements are fulfilled.
Description
Technical field
The invention belongs to the insulating material field, relate to a kind of impregnating varnish, especially a kind of high-temperature resistant silicone impregnating varnish and preparation method thereof.
Background technology
Pressure impregnation technique is generally adopted in the productions such as motor, transformer, wire.The workpiece preliminary drying is gone after tide cooling, be placed in vacuum environment, get rid of inner air and volatile matter, rely on paint liquid gravity in vacuum, apply the effect of certain pressure, make paint liquid rapid permeability and be full of the insulation system internal layer.This technique can obtain the paint film of continuous densification, free of pinholes.
Existing impregnating varnish is to be solidifying agent by epoxy resin as matrix resin, acid anhydrides.But the temperature resistant grade of this system cured product and toughness are not enough, need to carry out modification to epoxy anhydride impregnating varnish system, are the requirements that impregnating varnish system cured article satisfies temperature resistant grade and mechanical property simultaneously.
Summary of the invention
The purpose of this invention is to provide a kind of high-temperature resistant silicone impregnating varnish and preparation method thereof.
Technical scheme of the present invention is as follows:
A kind of high-temperature resistant silicone impregnating varnish is characterized in that being made by the raw material of following weight part:
Silicone resin 32-35, vinyl triamine 2-3, Synolac 6-8, ethyl acetate 10-12, E-12 epoxy resin 14-16, MALEIC ANHYDRIDE 4-6, ethylene glycol 6-7, dibutyl tin laurate 2-3, cyanuric acid zinc 1-2, polyisobutene 4-5, sylvic acid polyoxyethylene ester 2-3, vinyl three ('beta '-methoxy oxyethyl group) silane 3-4, dimethylbenzene 35-38, membrane-forming agent 4-5.
Described membrane-forming agent is made by the raw material of following weight part: Silane coupling agent KH550 2-4,582-2 aminoresin 16-21, polyisobutene 3-4, cobalt naphthenate 1-2, sec.-propyl distearyl acyl-oxygen base Aluminate 1-2, two ten four carbon alcohols ester 4-5, aluminium nitride 1-2, nano-attapulgite 1-2, epoxy soybean oil 4-5, morpholine 1-2;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
The preparation method of described high-temperature resistant silicone impregnating varnish, it is characterized in that comprising the following steps: MALEIC ANHYDRIDE, ethylene glycol, dibutyl tin laurate, cyanuric acid zinc, polyisobutene, sylvic acid polyoxyethylene ester, vinyl three ('beta '-methoxy oxyethyl group) silane, dimethylbenzene are mixed, be heated to 120-130 ℃, stirring reaction 2-3 hour, then, add other remaining component, insulated and stirred reaction 3-4 hour, and get final product.
Preparation technology of the present invention is simple, cost is low, be conducive to realize suitability for industrialized production; And the room temperature tensile shearing resistance of this high-temperature resistant silicone impregnating varnish is high, also has excellent thermotolerance, and hydrophobicity is strong, in fields such as superpower traction electric machine, high-power generator, drilling motor, mining motors, has broad application prospects.
Impregnating varnish paint film good toughness of the present invention, excellent in cushion effect, paint film is fine and close, and anti-xanthochromia can be high temperature resistant, high humidity, corrosion, and electrical insulation capability is good, and physical strength is high, has improved thermal conductivity, but 200 ℃ of long term operations, 220 ℃ of short-terms have satisfied design requirements.
Embodiment
A kind of high-temperature resistant silicone impregnating varnish, made by the raw material (kilogram) of following weight part:
Silicone resin 32, vinyl triamine 3, Synolac 8, ethyl acetate 12, E-12 epoxy resin 16, MALEIC ANHYDRIDE 6, ethylene glycol 7, dibutyl tin laurate 2, cyanuric acid zinc 2, polyisobutene 4, sylvic acid polyoxyethylene ester 2, vinyl three ('beta '-methoxy oxyethyl group) silane 4, dimethylbenzene 38, membrane-forming agent 5.
Described membrane-forming agent is made by the raw material of following weight part: Silane coupling agent KH550 4,582-2 aminoresin 16, polyisobutene 4, cobalt naphthenate 2, sec.-propyl distearyl acyl-oxygen base Aluminate 2, two ten four carbon alcohols esters 5, aluminium nitride 2, nano-attapulgite 2, epoxy soybean oil 4, morpholine 2;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
The preparation method of high-temperature resistant silicone impregnating varnish, comprise the following steps: MALEIC ANHYDRIDE, ethylene glycol, dibutyl tin laurate, cyanuric acid zinc, polyisobutene, sylvic acid polyoxyethylene ester, vinyl three ('beta '-methoxy oxyethyl group) silane, dimethylbenzene are mixed, be heated to 120-130 ℃, stirring reaction 2-3 hour, then, add other remaining component, insulated and stirred reaction 3-4 hour, and get final product.
Curing process: smoked under 110 ~ 150 ℃ 3-5 hour;
After it solidifies, cohesive strength is greater than 25N, and temperature classification is the H level, and volume specific resistance is not less than 1 * 1014 Ω m, and surface resistivity is not less than 1 * 1014 Ω, and after immersion, volume specific resistance is not less than 1 * 1012 Ω m, and surface resistivity is not less than 1 * 1012 Ω.Impregnating varnish of the present invention can high temperature resistant, high humidity, and electrical insulation capability is good, and physical strength is high, has improved thermal conductivity, but 200 ℃ of long term operations, and 220 ℃ of short-terms have satisfied design requirements.
Claims (2)
1. high-temperature resistant silicone impregnating varnish is characterized in that being made by the raw material of following weight part:
Silicone resin 32-35, vinyl triamine 2-3, Synolac 6-8, ethyl acetate 10-12, E-12 epoxy resin 14-16, MALEIC ANHYDRIDE 4-6, ethylene glycol 6-7, dibutyl tin laurate 2-3, cyanuric acid zinc 1-2, polyisobutene 4-5, sylvic acid polyoxyethylene ester 2-3, vinyl three ('beta '-methoxy oxyethyl group) silane 3-4, dimethylbenzene 35-38, membrane-forming agent 4-5;
Described membrane-forming agent is made by the raw material of following weight part: Silane coupling agent KH550 2-4,582-2 aminoresin 16-21, polyisobutene 3-4, cobalt naphthenate 1-2, sec.-propyl distearyl acyl-oxygen base Aluminate 1-2, two ten four carbon alcohols ester 4-5, aluminium nitride 1-2, nano-attapulgite 1-2, epoxy soybean oil 4-5, morpholine 1-2;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
2. the preparation method of high-temperature resistant silicone impregnating varnish according to claim 1, it is characterized in that comprising the following steps: MALEIC ANHYDRIDE, ethylene glycol, dibutyl tin laurate, cyanuric acid zinc, polyisobutene, sylvic acid polyoxyethylene ester, vinyl three ('beta '-methoxy oxyethyl group) silane, dimethylbenzene are mixed, be heated to 120-130 ℃, stirring reaction 2-3 hour, then, add other remaining component, insulated and stirred reaction 3-4 hour, and get final product.