CN103382318A - Compound impregnating varnish and preparation method thereof - Google Patents
Compound impregnating varnish and preparation method thereof Download PDFInfo
- Publication number
- CN103382318A CN103382318A CN201310261380XA CN201310261380A CN103382318A CN 103382318 A CN103382318 A CN 103382318A CN 201310261380X A CN201310261380X A CN 201310261380XA CN 201310261380 A CN201310261380 A CN 201310261380A CN 103382318 A CN103382318 A CN 103382318A
- Authority
- CN
- China
- Prior art keywords
- parts
- varnish
- preparation
- stirring reaction
- tts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A compound impregnating varnish and a preparation method thereof are disclosed. The varnish is characterized by being composed of following components in parts by weight: 34 to 36 parts of E-12 epoxy resin, 10 to 12 parts of terpolycyantoamino-formaldehyde resin, 4 to 6 parts of dimethyl dichlorosilane, 6 to 8 parts of styrene, 2 to 3 parts of butadiene, 3 to 4 parts of neopentylene glycol, 6 to 7 parts of bis-dodecanol ester, 1 to 2 parts of tert butyl peroxypivalate, 3 to 4 parts of acrylic acid-2-hydroxypropyl, 1 to 2 parts of titanate coupling agent TMC-TTS, 34 to 36 parts of xylene, 12 to 14 parts of ethyl acetate, and 4 to 5 parts of film forming agent. The preparation method adopts epoxy resin compound and induces titanate coupling agent TMC-TTS, so the compactness of the varnish membrane is increased. The compound impregnating varnish has the advantages of high-temperature and high-dampness resistance, good electric insulation property and high mechanic strength, the heat conductivity of the varnish is improved, so the varnish can work at the temperature of 180 DEG C for a long period and at the temperature of 220 for a short period, and the design requirements are satisfied.
Description
Technical field
The invention belongs to the insulating material field, relate to a kind of compound impregnating varnish and preparation method thereof.
Background technology
Pressure impregnation technique is generally adopted in the productions such as motor, transformer, wire.The workpiece preliminary drying is gone after tide cooling, be placed in vacuum environment, get rid of inner air and volatile matter, rely on paint liquid gravity in vacuum, apply the effect of certain pressure, make paint liquid rapid permeability and be full of the insulation system internal layer.This technique can obtain the paint film of continuous densification, free of pinholes.
Existing impregnating varnish is to be solidifying agent by epoxy resin as matrix resin, acid anhydrides.But the temperature resistant grade of this system cured product and toughness are not enough, need to carry out modification to the compound impregnating varnish system of epoxy anhydride, are the requirements that compound impregnating varnish system cured article satisfies temperature resistant grade and mechanical property simultaneously.
Summary of the invention
The purpose of this invention is to provide a kind of compound impregnating varnish and preparation method thereof,
Technical scheme of the present invention is as follows:
A kind of compound impregnating varnish is characterized in that being made by the raw material of following weight part: E-12 epoxy resin 34-36, terpolycyantoamino-formaldehyde resin 10-12, dimethyldichlorosilane(DMCS) 4-6, vinylbenzene 6-8, divinyl 2-3, neopentyl glycol 3-4, two Lauryl Alcohol ester 6-7, peroxidation trimethylacetic acid tert-butyl ester 1-2, vinylformic acid-2-hydroxy propyl ester 3-4, titanate coupling agent TMC-TTS 1-2, dimethylbenzene 34-36, ethyl acetate 12-14, membrane-forming agent 4-5.
Described membrane-forming agent is made by the raw material of following weight part: phenyl triethoxysilane 1-2, anilinomethyl triethoxysilane 1-2, ferrocene 2-3, aluminium nitride 1-2, nano-attapulgite 1-2, epoxy soybean oil 4-5, morpholine 1-2, polyisobutene 3-4;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
The preparation method of described compound impregnating varnish, it is characterized in that comprising the following steps: dimethyldichlorosilane(DMCS), vinylbenzene, divinyl, neopentyl glycol, two Lauryl Alcohol ester, dimethylbenzene are mixed, add the peroxidation trimethylacetic acid tert-butyl ester, stirring reaction 3-4 hour, then, be warming up to 120-135 ℃, continued to add titanate coupling agent TMC-TTS stirring reaction 30-40 minute, add again other remaining component, stirring reaction 2-3 hour, obtain.
The present invention adopts epoxy resin compound, introduces titanate coupling agent TMC-TTS, has increased the compactness of paint film, high temperature resistant, the high humidity of the compound impregnating varnish energy of the present invention, electrical insulation capability is good, and physical strength is high, has improved thermal conductivity, but 180 ℃ of long term operations, 220 ℃ of short-terms have satisfied design requirements.
Embodiment
A kind of compound impregnating varnish, made by the raw material (kilogram) of following weight part:
E-12 epoxy resin 36, terpolycyantoamino-formaldehyde resin 12, dimethyldichlorosilane(DMCS) 6, vinylbenzene 8, divinyl 3, neopentyl glycol 3, two Lauryl Alcohol ester 7, the peroxidation trimethylacetic acid tert-butyl ester 2, vinylformic acid-2-hydroxy propyl ester 4, titanate coupling agent TMC-TTS 2, dimethylbenzene 36, ethyl acetate 14, membrane-forming agent 5.
Described membrane-forming agent is made by the raw material of following weight part: phenyl triethoxysilane 2, anilinomethyl triethoxysilane 2, ferrocene 2, aluminium nitride 1, nano-attapulgite 2, epoxy soybean oil 5, morpholine 1, polyisobutene 4;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
The preparation method of compound impregnating varnish comprises the following steps:
Dimethyldichlorosilane(DMCS), vinylbenzene, divinyl, neopentyl glycol, two Lauryl Alcohol ester, dimethylbenzene are mixed, add the peroxidation trimethylacetic acid tert-butyl ester, stirring reaction 3-4 hour, then, be warming up to 120-135 ℃, continued to add titanate coupling agent TMC-TTS stirring reaction 30-40 minute, then add other remaining component, stirring reaction 2-3 hour, obtain.
Curing process: smoked under 110 ~ 150 ℃ 3-5 hour;
After it solidifies, cohesive strength is greater than 25N, and temperature classification is the H level, and volume specific resistance is not less than 1 * 1014 Ω m, and surface resistivity is not less than 1 * 1014 Ω, and after immersion, volume specific resistance is not less than 1 * 1012 Ω m, and surface resistivity is not less than 1 * 1012 Ω.The compound impregnating varnish of the present invention can high temperature resistant, high humidity, and electrical insulation capability is good, and physical strength is high, has improved thermal conductivity, but 180 ℃ of long term operations, 220 ℃ of short-terms.
Claims (2)
1. compound impregnating varnish is characterized in that being made by the raw material of following weight part:
E-12 epoxy resin 34-36, terpolycyantoamino-formaldehyde resin 10-12, dimethyldichlorosilane(DMCS) 4-6, vinylbenzene 6-8, divinyl 2-3, neopentyl glycol 3-4, two Lauryl Alcohol ester 6-7, peroxidation trimethylacetic acid tert-butyl ester 1-2, vinylformic acid-2-hydroxy propyl ester 3-4, titanate coupling agent TMC-TTS 1-2, dimethylbenzene 34-36, ethyl acetate 12-14, membrane-forming agent 4-5;
Described membrane-forming agent is made by the raw material of following weight part: phenyl triethoxysilane 1-2, anilinomethyl triethoxysilane 1-2, ferrocene 2-3, aluminium nitride 1-2, nano-attapulgite 1-2, epoxy soybean oil 4-5, morpholine 1-2, polyisobutene 3-4; The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
2. the preparation method of compound impregnating varnish according to claim 1, it is characterized in that comprising the following steps: dimethyldichlorosilane(DMCS), vinylbenzene, divinyl, neopentyl glycol, two Lauryl Alcohol ester, dimethylbenzene are mixed, add the peroxidation trimethylacetic acid tert-butyl ester, stirring reaction 3-4 hour, then, be warming up to 120-135 ℃, continued to add titanate coupling agent TMC-TTS stirring reaction 30-40 minute, add again other remaining component, stirring reaction 2-3 hour, obtain.