CN108300212A - A kind of impregnation enveloping material and preparation method thereof with exceptional overcoat pressure resistance - Google Patents
A kind of impregnation enveloping material and preparation method thereof with exceptional overcoat pressure resistance Download PDFInfo
- Publication number
- CN108300212A CN108300212A CN201711391686.1A CN201711391686A CN108300212A CN 108300212 A CN108300212 A CN 108300212A CN 201711391686 A CN201711391686 A CN 201711391686A CN 108300212 A CN108300212 A CN 108300212A
- Authority
- CN
- China
- Prior art keywords
- parts
- pressure resistance
- resin
- agent
- enveloping material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of impregnation enveloping material and preparation method thereof with exceptional overcoat pressure resistance, are made up of:10 30 parts of alkyd resin, 10 20 parts of polyurethane resin, 58 parts of organic siliconresin, 0.5 5 parts of curing agent, 15 parts of pigment, 40 70 parts of filler, 0.5 2 parts of thixotropic agent, 5 20 parts of solvent, 0.1 2 parts of coupling agent, 0.5 5 parts of antifoaming agent, and it is 25 45% that three kinds of resin total amounts, which account for the weight percent of formula gross weight,.Liquid infiltration encapsulating material provided by the invention has good craftsmanship, for encapsulating the electronic components such as varistor, thermistor, there is excellent coating pressure resistance after the curing of coatings encapsulated, coating can reach 2500VAC under 0.4mm thickness, 1min does not puncture, also, the coating after curing also has the excellent properties such as high temperature resistant, cold-resistant thermal shock and high temperature resistant direct current aging.
Description
Technical field
The present invention relates to a kind of liquid infiltration encapsulating material with exceptional overcoat pressure resistance, it be it is a kind of with alkyd resin, it is poly-
Based on the three kinds of resin collocation uses of urethane resin and organic siliconresin, using silica flour or aluminium oxide as main stuffing, and it is dissolved in
Liquid-type impregnation enveloping material in solvent, coating can reach 2500VAC under 0.4mm thickness after solidification, and 1min does not puncture.
Background technology
In Electronic Packaging field, mainly uses epoxy resin, phenolic resin and organic siliconresin as matrix resin, match
Curing agent, filler, auxiliary agent are closed to have the function that insulation, heat-resisting, isolation vapor, for varistor, to coating
It is required that it is also higher and higher, in addition to requiring coating that there is the pressure resistance of higher coating, while also requiring coating that there is high temperature resistant, cold-hot
Impact and high temperature resistant direct current ageing properties.
The system of currently used epoxy resin and phenolic resin can accomplish reach under 0.4mm thickness
2500VAC, 1min do not puncture, but the resin system heat-resisting quantity is poor, cannot meet the requirement being used for a long time at high temperature,
And cold-resistant thermal impact and high temperature resistant direct current ageing properties are poor.
Silicone resin system heat-resisting quantity is good, while having excellent cold-resistant thermal impact and high temperature resistant direct current aging
Can, but coating pressure resistance is poor, in order to reach 2500VAC, 1min does not puncture, and silicone resin system needs to increase coating layer thickness
It is added to about 1.0mm, this aspect can use more coating to cause cost to improve, on the other hand also be unsatisfactory for electronic component
The requirement increasingly minimized is not used to have thickness in the product strictly limited.
Currently, single resin system can not meet these requirements simultaneously substantially, the present inventor by largely studying,
It was found that by the collocation of different resins, may be implemented to meet these requirements simultaneously.
Invention content
In view of the deficiencies of the prior art, the invention discloses a kind of liquid infiltration encapsulating material with exceptional overcoat pressure resistance,
Solve the problems, such as the existing resistance to pressure difference of encapsulating material coating, meanwhile, the coating after solidification also has high temperature resistant, cold-resistant thermal shock and Nai Gao
The excellent properties such as warm direct current aging.
Technical scheme is as follows:
A kind of impregnation enveloping material with exceptional overcoat pressure resistance, it is characterised in that:It is composed of the following components:Alkyd resin
10-30 parts, 10-20 parts of polyurethane resin, 5-8 parts of organic siliconresin, 0.5-5 parts of curing agent, 1-5 parts of pigment, filler 40-70
Part, 0.5-2 parts of thixotropic agent, 5-20 parts of solvent, 0.1-2 parts of coupling agent, 0.5-5 parts of antifoaming agent, and three kinds of resin total amounts account for and match
The weight percent of square gross weight is 25-45%.
The alkyd resin can be dry alkyd resin, semi-drying alkyd resin, non-drying alkyd resin, preferably not
Dry alkyd resin, and the alkyd resin is modified by acrylic resin, and the alkyd resin is at normal temperatures
For liquid condition, and it is soluble in dimethylbenzene equal solvent.
The polyurethane is the reaction product of polyester diol and polyester trihydroxylic alcohol and diisocyanate, and polyester binary
The ratio between alcohol and the dosage of polyester trihydroxylic alcohol are 3:2, polyurethane resin provides excellent resistance to low temperature for system and cold-hot is handed over
Denaturation.
The organic siliconresin can be methyl silicon resin, phenyl polysiloxane, methyl phenyl silicone resin, and organic siliconresin is
System provides excellent high temperature resistance and high temperature resistant direct current ageing properties, and methyl phenyl silicone resin is more suitable for the system.
Due to containing hydroxyl in alkyd resin, and also contain hydroxyl in organic siliconresin, the hydroxyl in two kinds of resins
It along with the hydroxyl in polyester diol and polyester trihydroxylic alcohol, can be chemically reacted with diisocyanate, to modified poly-
The performance of urethane itself, alkyd resin have excellent insulation pressure resistance, and organic siliconresin has excellent heat resistance, so passing through
Chemical reaction and modified resin system has excellent coating pressure resistance, meanwhile, the coating after solidification also has high temperature resistant, resistance to
The excellent properties such as thermal shock and high temperature resistant direct current aging.
The curing agent is the substance that can accelerate system reaction speed, is two bays suitable for resin system of the present invention
Sour dibutyl tin, stannous octoate, two sad dibutyl tins, aluminium acetylacetonate.
The pigment can be aluminium powder, chrome green, carbon black, chrome yellow, Chinese husky of common dye, ultramarine, blue or green blue, iron oxide red, copper-chrome black,
Ferrimanganic is black.
The filler be alundum (Al2O3), silicon nitride, graphite, precipitated calcium carbonate, powdered whiting, barium sulfate, titanium dioxide,
Glass powder with low melting point, silicon powder, mica powder, talcum powder, kaolin.
The thixotropic agent is fume colloidal silica, mica powder, talcum powder, bentonite, rilanit special, polyamide wax.It touches
It is in order to make system have good thixotropic effects, to make liquid envelope material be applied when encapsulating varistor thermistor to become agent
Layer can be uniform, and not sagging, is commonly fume colloidal silica.
Wherein, solvent is dimethylbenzene, toluene, ethylbenzene, benzene, n-butanol, isopropanol, ethyl alcohol, propyl alcohol, cyclohexanone.Solvent body
System's reply has preferable dissolubility, and so as to form evenly dispersed liquid component, the effect of single solvent is not as good as mixing
The effect of solvent, such as can be arranged in pairs or groups with dimethylbenzene and isopropanol collocation or toluene and ethyl alcohol etc., while the solvent of different boiling
Collocation can also adjust the evaporation rate of liquid infiltration encapsulating material mutually, to meet the requirement of craftsmanship.
Wherein, it in order to improve the strength of coating after the solidification of liquid infiltration encapsulating material and coating to the adhesive force of base material, needs
Using coupling agent, the coupling agent can be KH550, KH560, KH570, KH792, DL602, DL171, NDZ101,
NDZ201, phosphate, phthalate ester.
Wherein, it since whole system is liquid component, and needs to stir in sample making course, may mix in this process
Enter to have bubble, so needing to use antifoaming agent, the antifoaming agent that can be silicone emulsion, the fatty acid ester compounded object of higher alcohols, gather
Ethylene oxide polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and polyoxypropylene polyoxy second
Alkene glycerin ether, dimethyl silicone polymer, Polyether Modified Polysiloxanes Defoaming Agent.
Wherein, the method for preparing the liquid infiltration encapsulating material, includes the following steps:
(1) organic siliconresin, curing agent, pigment, filler and the thixotropic agent of formula ratio are weighed;
(2) it is pulverized and mixed in pulverizer, and mixed component is sieved by 180 mesh screens, using can be by this
The component of sieve;
(3) this is added by the component of sieve into reaction kettle, while being sequentially added into solvent, coupling agent, antifoaming agent,
30min is stirred under 50~100Hz rotating speeds;
(4) the alkyd resin and polyurethane resin of formula ratio is then added, 2h is stirred under 100~200Hz rotating speeds, you can
Obtain the liquid infiltration encapsulating material of the present invention.
The invention has the beneficial effects that:
This liquid infiltration encapsulating material after encapsulating the solidifications such as varistor thermistor there is excellent coating pressure resistance, coating to exist
2500VAC can be reached under 0.4mm thickness, 1min does not puncture, also, also there is the coating after solidification high temperature resistant, cold-hot to rush
It hits and the excellent properties such as high temperature resistant direct current aging.
Specific implementation mode
The invention will be further described below and by specific embodiment, and following embodiment is descriptive, is not
Limited, protection scope of the present invention cannot be limited successively.
Embodiment 1
A kind of impregnation enveloping material with exceptional overcoat pressure resistance, it is composed of the following components:Acrylic graft-modified alkyd
15 parts of resin, 20 parts of polyurethane resin, 8 parts of methylphenylsiloxane, 1.5 parts of dibutyl tin laurate, 3 parts of chrome green,
20 parts of aluminium oxide, 40 parts of silicon powder, 1.5 parts of fume colloidal silica, 20 parts of dimethylbenzene, KH550:1.2 parts, 0.8 part of silicone emulsion,
The weight percent that three kinds of resin total amounts account for formula gross weight is 32.8%.
Preparation process is as follows:
1, methylphenylsiloxane, chrome green, aluminium oxide, silicon powder, the fume colloidal silica of formula ratio are weighed;
2, said components are pulverized and mixed in pulverizer, are sieved by 180 mesh screens after crushing, leaves sieving component;
3, sieving component is added into reaction kettle, while is sequentially added into the dimethylbenzene, KH550, emulsification silicon of formula ratio
Oil, and stir 30min under 100Hz rotating speeds;
4, dibutyl tin laurate, alkyd resin, the polyurethane resin of formula ratio is added, is stirred under 200Hz rotating speeds
2h, take the dish out of the pot to get to the present invention liquid infiltration encapsulating material.
Embodiment 2
A kind of impregnation enveloping material with exceptional overcoat pressure resistance, it is composed of the following components:30 parts of alkyd resin, polyurethane tree
15 parts of fat, 6 parts of phenyl organic siliconresin, 1.5 parts of stannous octoate, 5 parts of chrome yellow, 20 parts of precipitated calcium carbonate, 4 parts of mica powder, silicon is micro-
40 parts of powder, 1.5 parts of bentonite, 20 parts of ethyl alcohol, 2 parts of phthalate ester, 0.8 part of Polyether Modified Polysiloxanes Defoaming Agent, three kinds of resin total amounts
The weight percent for accounting for formula gross weight is 35%.
Preparation process step as described in Example 1.
Embodiment 3
A kind of impregnation enveloping material with exceptional overcoat pressure resistance, it is composed of the following components:15 parts of alkyd resin, polyurethane tree
15 parts of fat, 5 parts of methylsiloxane resin, 1.5 parts of aluminium acetylacetonate, 5 parts of copper-chrome black, 10 parts of glass powder with low melting point, kaolin 10
Part, 45 parts of silicon powder, 1.5 parts of polyamide wax, 20 parts of cyclohexanone, KH560:1.2 parts, polyoxyethylene polyoxypropylene pentaerythrite
0.8 part of ether, the weight percent that three kinds of resin total amounts account for formula gross weight are 28%.
Preparation process step as described in Example 1.
Comparative example:
Liquid infiltration encapsulating material, it is composed of the following components:20 parts of methylphenylsiloxane, 1.5 parts of aluminium acetylacetonate,
5 parts of copper-chrome black, 10 parts of glass powder with low melting point, 10 parts of kaolin, 45 parts of silicon powder, 1.5 parts of polyamide wax, 20 parts of cyclohexanone,
KH560:1.2 parts, 0.8 part of polyoxyethylene polyoxypropylene pentaerythrite ether, organic siliconresin total amount accounts for the weight hundred of formula gross weight
Divide than being 17.4%.
Preparation process step as described in Example 1.
By the liquid infiltration encapsulating material of the liquid infiltration encapsulating material of embodiment 1-3 and comparative example, encapsulate respectively pressure-sensitive
Then resistance cures 1h at 150 DEG C, measure the data such as coating pressure resistance, as shown in the table:
Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example | |
Coating layer thickness (mm) | 0.4 | 0.4 | 0.4 | 0.4 |
Cure rear surface quality | It is smooth | It is smooth | It is smooth | It is smooth |
Coating pressure resistance | 3100 | 3800 | 2900 | 1400 |
Temperature follows number | 1500 | 1200 | 1300 | 1200 |
Legs and feet intensity (kg) | 5 | 4 | 4 | 3 |
Note:1. coating voltage-withstand test is to apply certain alternating current voltage, coating institute energy when then 1min coatings do not puncture
The maximum voltage value born.
2. temperature is followed at a temperature of the alternating hot and cold that number refers to 125 DEG C/30min of -40 DEG C/30min -, what coating can bear follows
Number of rings is until coating cracking.
Claims (10)
1. a kind of impregnation enveloping material with exceptional overcoat pressure resistance, it is characterised in that:It is composed of the following components:Alkyd resin 10-
30 parts, 10-20 parts of polyurethane resin, 5-8 parts of organic siliconresin, 0.5-5 parts of curing agent, 1-5 parts of pigment, 40-70 parts of filler, touch
Become 0.5-2 parts of agent, 5-20 parts of solvent, 0.1-2 parts of coupling agent, 0.5-5 parts of antifoaming agent, and three kinds of resin total amounts account for formula gross weight
Weight percent be 25-45%.
2. the impregnation enveloping material according to claim 1 with exceptional overcoat pressure resistance, it is characterised in that:The alkyd resin
For dry alkyd resin, semi-drying alkyd resin, non-drying alkyd resin, preferably non-drying alkyd resin, and the alcohol
Acid resin carries out grafting modification by acrylic resin.
3. the impregnation enveloping material according to claim 1 with exceptional overcoat pressure resistance, it is characterised in that:The polyurethane tree
Fat is the reaction product of polyester diol and polyester trihydroxylic alcohol and diisocyanate, and polyester diol and polyester trihydroxylic alcohol
Dosage is 3 according to mass ratio:2.
4. the impregnation enveloping material according to claim 1 with exceptional overcoat pressure resistance, it is characterised in that:The organosilicon tree
Fat is methyl resin, phenyl polysiloxane or methyl phenyl silicone resin.
5. the impregnation enveloping material according to claim 1 with exceptional overcoat pressure resistance, it is characterised in that:The curing agent is
Dibutyl tin laurate, stannous octoate, two sad dibutyl tins or aluminium acetylacetonate.
6. the impregnation enveloping material according to claim 1 with exceptional overcoat pressure resistance, it is characterised in that:The solvent is two
Toluene, toluene, ethylbenzene, benzene, n-butanol, isopropanol, ethyl alcohol, propyl alcohol or cyclohexanone;The thixotropic agent is fume colloidal silica, cloud
Female powder, talcum powder, bentonite, rilanit special or polyamide wax.
7. the impregnation enveloping material according to claim 1 with exceptional overcoat pressure resistance, it is characterised in that:The coupling agent is
KH550, KH560, KH570, KH792, DL602, DL171, NDZ101, NDZ201, phosphate or phthalate ester.
8. the impregnation enveloping material according to claim 1 with exceptional overcoat pressure resistance, it is characterised in that:The antifoaming agent is
The fatty acid ester compounded object of silicone emulsion, higher alcohols, polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxy Propanolamine
Ether, polypropylene glycerol aether and polyoxyethylene polyoxypropylene glycerin ether, dimethyl silicone polymer or organic silicon modified by polyether defoaming
Agent.
9. the impregnation enveloping material according to claim 1 with exceptional overcoat pressure resistance, it is characterised in that:The pigment can be with
It is black for aluminium powder, chrome green, carbon black, chrome yellow, Chinese husky of common dye, ultramarine, blue or green blue, iron oxide red, copper-chrome black, ferrimanganic;The filler is three
Al 2 O, silicon nitride, graphite, precipitated calcium carbonate, powdered whiting, barium sulfate, titanium dioxide, glass powder with low melting point, silicon powder,
Mica powder, talcum powder, kaolin.
10. a kind of preparation method of the impregnation enveloping material described in claim 1 with exceptional overcoat pressure resistance, feature exist
In:Steps are as follows
(1) organic siliconresin, curing agent, pigment, filler and the thixotropic agent of formula ratio are weighed;
(2) it is pulverized and mixed in pulverizer, and mixed component is sieved by 150-200 mesh screens, using can be by this
The component of sieve;
(3) this is added by the component of sieve into reaction kettle, while being sequentially added into solvent, coupling agent, antifoaming agent, 50
30min is stirred under~100Hz rotating speeds;
(4) the alkyd resin and polyurethane resin of formula ratio is then added, stirs 2h under 100~200Hz rotating speeds, you can obtain
The liquid infiltration encapsulating material of the present invention.