CN102875766A - 一种吸震鞋底材料的制备方法 - Google Patents
一种吸震鞋底材料的制备方法 Download PDFInfo
- Publication number
- CN102875766A CN102875766A CN2012103558612A CN201210355861A CN102875766A CN 102875766 A CN102875766 A CN 102875766A CN 2012103558612 A CN2012103558612 A CN 2012103558612A CN 201210355861 A CN201210355861 A CN 201210355861A CN 102875766 A CN102875766 A CN 102875766A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- parts
- preparation
- sole material
- sole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种吸震鞋底材料的制备方法，该方法的制备步骤如下：将100-105质量份伯羟基聚醚二元醇、45-50质量份TDI、10-12质量份米糠、3-4质量份泡沫稳定剂、3-6质量份辛酸亚锡、6质量份二氯甲烷、3质量份三乙烯二胺和2.5质量份AC加入高速搅拌混合机中混合10min；然后加入到双螺杆挤出机中熔融接枝3h后，即得到所述鞋底材料。该方法的制备工艺简单，生产成本低，弹性好，能有效的起到吸震的作用。
Description
技术领域
本发明涉及一种吸震鞋底材料的制备方法。
技术背景
目前，一双质量好的鞋能很好的保护人们的脚，为了防止运动或走路时，减少对脚底的冲击，鞋底需要具有吸震或减震的功能的材料制成，而市面上的鞋底大多数具有轻便，舒适，加工成型快等性能，虽然材料的柔软性达到要求但是其吸震效果不理想，所以为了进一步改进性能，一般要掺入大量的填料，树脂和油品，这样会大大提高的生产成本，影响鞋底的使用寿命。
发明内容
本发明目的是为了克服现有技术的不足，提供一种吸震鞋底材料的制备方法，该方法制得鞋底材料耐磨性强，且该方法的制备工艺简单。
为解决上述问题，本发明的一个技术方案是：一种吸震鞋底材料的制备方法，该方法的制备步骤如下：将100-105质量份伯羟基聚醚二元醇、45-50质量份TDI、10-12质量份米糠、3-4质量份泡沫稳定剂、3-6质量份辛酸亚锡、6质量份二氯甲烷、3质量份三乙烯二胺和2.5质量份AC加入高速搅拌混合机中混合10min；然后加入到双螺杆挤出机中熔融接枝3h后，即得到所述鞋底材料。
本发明的有益效果：该方法的制备工艺简单，生产成本低，且制备出的产物耐磨性高，弹性好，能有效的起到吸震的作用。
具体实施方式
实施例1
一种吸震鞋底材料的制备方法，该方法的制备步骤如下：将100-105质量份伯羟基聚醚二元醇、45-50质量份TDI、10-12质量份米糠、3-4质量份泡沫稳定剂、3-6质量份辛酸亚锡、6质量份二氯甲烷、3质量份三乙烯二胺和2.5质量份AC加入高速搅拌混合机中混合10min；然后加入到双螺杆挤出机中熔融接枝3h后，即得到所述鞋底材料。对该鞋底材料的性能检测效果如下：相对密度：0.22，拉伸强度/MPa：2.9，回弹率：32%。
Claims (1)
1.一种吸震鞋底材料的制备方法，其特征在于该方法的步骤如下：将100-105质量份伯羟基聚醚二元醇、45-50质量份TDI、10-12质量份米糠、3-4质量份泡沫稳定剂、3-6质量份辛酸亚锡、6质量份二氯甲烷、3质量份三乙烯二胺和2.5质量份AC加入高速搅拌混合机中混合10min；然后加入到双螺杆挤出机中熔融接枝3h后，即得到所述鞋底材料。