CN102617890A - 可降解果树专用嫁接带 - Google Patents
可降解果树专用嫁接带 Download PDFInfo
- Publication number
- CN102617890A CN102617890A CN2012100872754A CN201210087275A CN102617890A CN 102617890 A CN102617890 A CN 102617890A CN 2012100872754 A CN2012100872754 A CN 2012100872754A CN 201210087275 A CN201210087275 A CN 201210087275A CN 102617890 A CN102617890 A CN 102617890A
- Authority
- CN
- China
- Prior art keywords
- parts
- coupling agent
- grafting
- proportioning
- degradable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
可降解果树专用嫁接带涉及农业生产中的嫁接绑扎带,尤其是果树嫁接改良过程中的用于绑扎的嫁接带。本发明提供一种可完全生物降解的、且具有抗菌性的可降解果树专用嫁接带。本发明原料组分及配比如下:生物降解母料35~60份,改性淀粉25~40份,增塑剂5~12份,润滑剂5~12份,抗菌剂0.5~5份,热稳定剂0.8~2份,偶联剂0~5份。本发明不仅生物降解效果好,能迅速降解、与环境同化,对环境不会造成污染或板结;而且还具有抗菌性,以保证嫁接口处的快速愈合;另外,本发明由于添加有增塑剂、热稳定剂和润滑剂,故其机械性能比较优越,使其具有嫁接专用带的良好特性。
Description
技术领域:
本发明涉及农业生产中的嫁接绑扎带,尤其是果树嫁接改良过程中的用于绑扎的嫁接带。
背景技术:
我国现有各种嫁接技术,用于嫁接绑扎的材料在改进历史上用麻皮、树皮后,至今一直多采用塑料薄膜,也有少量的使用纸质嫁接膜。无论是塑料薄膜还是纸质嫁接膜,多是一次性不完全降解的,会对环境造成污染;而且由于嫁接成活后需要人工去除绑扎用的塑料薄膜或者纸质嫁接膜,从而增加了劳动强度。
最近几年出现的生物降解塑料,其既具有传统塑料的功能和特性,又可在土壤和水中的微生物作用下,或通过阳光中紫外线的作用,在自然环境中***降解和还原,最终以无毒形式重新进入生态环境中,回归大自然。降解塑料最突出的优点是可降解,不污染环境,它代替聚乙烯等塑料已是发展的必然趋势。目前使用和报道最多的可降解塑料是淀粉基塑料,但由于其制品中含有一定比例的聚烯烃塑料,使其使用后不能完全降解,只是其中的淀粉部分被降解,但是塑料成分还将长期存在于环境中,造成土地板结。脂肪族聚酯是目前发展最快的可完全生物降解塑料,但是由于大部分生物降解树脂的玻璃温度很低,一般仅为50℃-70℃,使得成品的应用领域受到限制。
目前农业嫁接带方面还没有见相关报道。
发明内容:
就是针对上述问题,本发明的目的是提供一种可完全生物降解的、且具有抗菌性的可降解果树专用嫁接带。
为实现上述目的,本发明采用如下技术方案,其原料组分及配比如下:
生物降解母料 35~60份
改性淀粉 25~40 份
增塑剂 5~12 份
润滑剂 5~12 份
抗菌剂 0.5~5份
热稳定剂 0.8~2份
偶联剂 0~5份
所述生物降解母料为热塑性淀粉塑料、脂肪族聚酯、聚乳酸、淀粉/聚乙烯醇其中至少一种。
所述偶联剂为硅烷偶联剂或铝酸酯偶联剂。
所述增塑剂为邻苯二甲酸酯类。
所述润滑剂为硬脂酸或石蜡。
所述抗菌剂为含有抗菌成份的植物的提取液或提取粉。
所述热稳定剂为钙锌复合热稳定剂。
本发明的制备方法为:
将原料称量准备好,生物降解母料采用常规办法进行改性,改性后和改性淀粉、增塑剂、润滑剂、偶联剂、热稳定剂、抗菌剂依次送入高速混料机内进搅拌均匀,之后按照常规方法制得本发明。
本发明的有益效果:
本发明不仅生物降解效果好,能迅速降解、与环境同化,对环境不会造成污染或板结;而且还具有抗菌性,以保证嫁接口处的快速愈合;另外,本发明由于添加有增塑剂、热稳定剂和润滑剂,故其机械性能比较优越,使其具有嫁接专用带的良好特性。
具体实施方式:
实施例一: 其原料组分及配比如下:
热塑性淀粉塑料 35~60份
改性淀粉 25~40 份
邻苯二甲酸酯类 5~12 份
硬脂酸 5~12 份
抗菌植物提取液 1.2~5份
钙锌复合热稳定剂 0.8~2份
硅烷偶联剂 0~5份
实施例二: 其原料组分及配比如下:
脂肪族聚酯 35~60份
改性淀粉 25~40 份
邻苯二甲酸酯类 5~12 份
石蜡 5~12 份
抗菌植物提取粉 0.5~5份
钙锌复合热稳定剂 0.8~2份
铝酸酯 0~5份
实施例三:其原料组分及配比如下:
淀粉/聚乙烯醇 35~60份
改性淀粉 25~40 份
邻苯二甲酸酯类 5~12 份
硬脂酸 5~12 份
钙锌复合热稳定剂 0.8~2份
抗菌植物提取液 2~5份
铝酸酯偶联剂 0~5份
实施例四:其原料组分及配比如下:
聚乳酸 35~60份
改性淀粉 25~40 份
邻苯二甲酸酯类 5~12 份
硬脂酸 5~12 份
钙锌复合热稳定剂 0.8~2份
抗菌植物提取液 2~5份
铝酸酯偶联剂 0~5份
本发明的制备方法为:
将原料称量准备好,生物降解母料采用常规办法进行改性,改性后和改性淀粉、增塑剂、润滑剂、偶联剂、热稳定剂、抗菌剂依次送入高速混料机内进搅拌均匀,之后按照常规方法制得本发明。
Claims (10)
1.可降解果树专用嫁接带,其特征在于:其原料组分及配比如下:
生物降解母料 35~60份
改性淀粉 25~40 份
增塑剂 5~12 份
润滑剂 5~12 份
抗菌剂 0.5~5份
热稳定剂 0.8~2份
偶联剂 0~5份
所述生物降解母料为热塑性淀粉塑料、脂肪族聚酯、聚乳酸、淀粉/聚乙烯醇其中至少一种。
2.所述偶联剂为硅烷偶联剂或铝酸酯偶联剂。
3.所述增塑剂为邻苯二甲酸酯类。
4.所述润滑剂为硬脂酸或石蜡。
5.所述抗菌剂为含有抗菌成份的植物的提取液或提取粉。
6.所述热稳定剂为钙锌复合热稳定剂。
7.根据权利要求1所述的嫁接带,其特征在于:其原料组分及配比如下:
热塑性淀粉塑料 35~60份
改性淀粉 25~40 份
邻苯二甲酸酯类 5~12 份
硬脂酸 5~12 份
抗菌植物提取液 1.2~5份
钙锌复合热稳定剂 0.8~2份
硅烷偶联剂 0~5份。
8.根据权利要求1所述的嫁接带,其特征在于:其原料组分及配比如下:
脂肪族聚酯 35~60份
改性淀粉 25~40 份
邻苯二甲酸酯类 5~12 份
石蜡 5~12 份
抗菌植物提取粉 0.5~5份
钙锌复合热稳定剂 0.8~2份
铝酸酯 0~5份。
9.根据权利要求1所述的嫁接带,其特征在于:其原料组分及配比如下:
淀粉/聚乙烯醇 35~60份
改性淀粉 25~40 份
邻苯二甲酸酯类 5~12 份
硬脂酸 5~12 份
钙锌复合热稳定剂 0.8~2份
抗菌植物提取液 2~5份
铝酸酯偶联剂 0~5份 。
10.根据权利要求1所述的嫁接带,其特征在于:其原料组分及配比如下:
聚乳酸 35~60份
改性淀粉 25~40 份
邻苯二甲酸酯类 5~12 份
硬脂酸 5~12 份
钙锌复合热稳定剂 0.8~2份
抗菌植物提取液 2~5份
铝酸酯偶联剂 0~5份 。