CN101735484A - 可降解塑料、用该塑料制备的容器及其制备方法 - Google Patents
可降解塑料、用该塑料制备的容器及其制备方法 Download PDFInfo
- Publication number
- CN101735484A CN101735484A CN200910312170A CN200910312170A CN101735484A CN 101735484 A CN101735484 A CN 101735484A CN 200910312170 A CN200910312170 A CN 200910312170A CN 200910312170 A CN200910312170 A CN 200910312170A CN 101735484 A CN101735484 A CN 101735484A
- Authority
- CN
- China
- Prior art keywords
- container
- percent
- preparation
- degradable plastics
- degradable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种材料技术领域的可降解塑料、用该塑料制备的容器及其制备方法;该可降解塑料的组成及其重量百分比为:淀粉30~50%,增塑剂20~40%,聚乙烯醇10~40%,粘土0~10%;本发明还涉及利用所述塑料制备的容器;所述容器的制备方法包括如下步骤:步骤一,按重量比例取可降解塑料各组分;步骤二,搅拌进行预混合,得到预混料;步骤三,将预混料于双螺杆挤出机中130~180℃条件下混炼,挤出,造粒,得粒料;之后将粒料于注塑机上160~210℃条件下注塑成型,冷却脱模,得容器。本发明的可降解塑料原料来源丰富,价格便宜;塑料材料强度高,可塑性强,可在多种环境下完全被生物降解,不会对环境产生任何污染。
Description
技术领域
本发明涉及一种材料技术领域的塑料、用该塑料制备的容器及其制备方法,具体是一种可降解塑料、用该塑料制备的容器及其制备方法。
背景技术
目前国内使用的花盆、苗钵主要为陶土烧制和塑料制造,国外则以降解塑料和纸质花盆、苗钵为主。陶土花盆需要毁田取土,燃烧煤炭,会对环境造成破坏和污染,而且产品质重易碎,制造和运输成本较高。塑料花盆不仅消耗有限石油资源,而且不可降解,污染环境。纸制花盆也同样存在消耗木材资源、前期制浆化学处理污染环境的危害。塑料花盆、苗钵由于不透气、排水性能差而降低了花草的成活率,同时由于不可降解,移栽花草取出时增加劳动强度、使花草根部受损。
经对现有技术的文献检索发现,中国发明专利ZL95111976.1公开了一种植物纤维花盆及其生产方法,以植物纤维草浆板为主要原料,配以改性剂处理,经真空吸附网模成型而成;中国发明专利ZL02112063.3公开了一种可降解营养钵/盆,由植物纤维、粘结剂、助剂和有机肥加热固化成型制备而成。但是,上述方法均存在材料强度低,可塑性差,生产工艺复杂,不易实现连续化生产等缺点。
发明内容
本发明的目的在于克服现有技术的不足,提供一种可降解塑料、用该塑料制备的容器及其制备方法。本发明的可降解塑料原料来源丰富,价格便宜;塑料材料强度高,可塑性强,可在多种环境下完全被生物降解,不会对环境产生任何污染。
本发明是通过以下技术方案实现的,
本发明涉及一种可降解塑料,其组成及其重量百分比为:淀粉30~50%,增塑剂20~40%,聚乙烯醇10~40%,粘土0~10%。
所述增塑剂为以下组合中的一种或多种的混合物:乙二醇、甘油、木糖醇和山梨醇。
所述粘土为蒙脱土、滑石粉或高岭土。
本发明还涉及一种用所述可降解塑料制备的容器。
所述容器为花盆。
所述容器为苗钵。
本发明还涉及前述容器的制备方法,包括如下步骤:
步骤一,按重量比例取可降解塑料各组分;
步骤二,搅拌进行预混合,得到预混料;
步骤三,将预混料于双螺杆挤出机中130~180℃条件下混炼,挤出,造粒,得粒料;之后将粒料于注塑机上160~210℃条件下注塑成型,冷却脱模,得容器。
步骤二中,所述搅拌的时间为10~20min。
与现有技术相比,本发明具有如下的有益效果:本发明的可降解塑料原料来源丰富,价格便宜;塑料材料强度高,可塑性强,可在多种环境下完全被生物降解,不会对环境产生任何污染。
具体实施方式
本实施例在以本发明技术方案为前提下进行实施,给出了详细的实施方式和过程,但本发明的保护范围不限于下述的实施例。下列实施例中未注明具体条件的实验方法,通常按照常规条件,或按照制造厂商所建议的条件。
实施例1
本实施例涉及的可降解塑料的组分及重量百分比为:
淀粉50%,乙二醇40%,聚乙烯醇10%;
利用该可降解塑料制备花盆的方法,包括如下步骤:
步骤一,按重量比例取各组分;
步骤二,高速混合机中搅拌20min进行预混合,得到预混料;
步骤三,将预混料于双螺杆挤出机中180℃条件下混炼,挤出,造粒,得粒料;之后将粒料于注塑机上210℃条件下注塑成型,冷却脱模,得可降解花盆。
实施例2
本实施例涉及的可降解塑料的组分及重量百分比为:
淀粉30%,甘油20%,聚乙烯醇40%,蒙脱土10%。
利用该可降解塑料制备苗钵的方法,包括如下步骤:
步骤一,按重量比例取各组分;
步骤二,高速混合机中搅拌10min进行预混合,得到预混料;
步骤三,将预混料于双螺杆挤出机中130℃条件下混炼,挤出,造粒,得粒料;之后将粒料于注塑机上160℃条件下注塑成型,冷却脱模,得可降解苗钵。
实施例3
本实施例涉及的可降解塑料的组分及重量百分比为:
淀粉40%,增塑剂(木糖醇和山梨醇按质量比为1∶1混合而得)30%,聚乙烯醇25%,高岭土5%。
利用该可降解塑料制备苗钵的方法,包括如下步骤:
步骤一,按重量比例取各组分;
步骤二,高速混合机中搅拌15min进行预混合,得到预混料;
步骤三,将预混料于双螺杆挤出机中150℃条件下混炼,挤出,造粒,得粒料;之后将粒料于注塑机上190℃条件下注塑成型,冷却脱模,得可降解苗钵。
实施例4
本实施例涉及的可降解塑料的组分及重量百分比为:
淀粉35%,木糖醇30%,聚乙烯醇25%,滑石粉10%。
利用该可降解塑料制备花盆的方法,包括如下步骤:
步骤一,按重量比例取各组分;
步骤二,高速混合机中搅拌15min进行预混合,得到预混料;
步骤三,将预混料于双螺杆挤出机中150℃条件下混炼,挤出,造粒,得粒料;之后将粒料于注塑机上190℃条件下注塑成型,冷却脱模,得可降解花盆。
实施效果:
实施例1~4制备的花盆或苗钵,强度适宜,透气性好,栽种花草后可直接植入土中,180天后花盆或苗钵即可完全降解。
Claims (8)
1.一种可降解塑料,其特征在于,其组成及其重量百分比为:淀粉30~50%,增塑剂20~40%,聚乙烯醇10~40%,粘土0~10%。
2.根据权利要求1所述的可降解塑料,其特征是,所述增塑剂为以下组合中的一种或多种的混合物:乙二醇、甘油、木糖醇和山梨醇。
3.根据权利要求1所述的可降解塑料,其特征是,所述粘土为蒙脱土、滑石粉或高岭土。
4.一种用权利要求1所述的可降解塑料制备的容器。
5.根据权利要求4所述的容器,其特征是,所述容器为花盆。
6.根据权利要求4所述的容器,其特征是,所述容器为苗钵。
7.一种制备权利要求4所述容器的方法,其特征在于,包括如下步骤:
步骤一,按重量比例取可降解塑料各组分;
步骤二,搅拌进行预混合,得到预混料;
步骤三,将预混料于双螺杆挤出机中130~180℃条件下混炼,挤出,造粒,得粒料;之后将粒料于注塑机上160~210℃条件下注塑成型,冷却脱模,得容器。
8.根据权利要求7所述的制备容器的方法,其特征是,步骤二中,所述搅拌的时间为10~20min。