CN102558563A - 一种高粘度107胶的制备方法 - Google Patents

一种高粘度107胶的制备方法 Download PDF

Info

Publication number
CN102558563A
CN102558563A CN2011104545865A CN201110454586A CN102558563A CN 102558563 A CN102558563 A CN 102558563A CN 2011104545865 A CN2011104545865 A CN 2011104545865A CN 201110454586 A CN201110454586 A CN 201110454586A CN 102558563 A CN102558563 A CN 102558563A
Authority
CN
China
Prior art keywords
glue
temperature
preparation
viscosity
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011104545865A
Other languages
English (en)
Other versions
CN102558563B (zh
Inventor
章淑娥
杨秀伟
张伶俐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangxi Bluestar Xinghuo Silicone Co Ltd
Original Assignee
JIANGXI XINGHUO ORGANIC SILICON PLANT LANXING CHEMICAL NEW MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGXI XINGHUO ORGANIC SILICON PLANT LANXING CHEMICAL NEW MATERIAL CO Ltd filed Critical JIANGXI XINGHUO ORGANIC SILICON PLANT LANXING CHEMICAL NEW MATERIAL CO Ltd
Priority to CN201110454586.5A priority Critical patent/CN102558563B/zh
Publication of CN102558563A publication Critical patent/CN102558563A/zh
Application granted granted Critical
Publication of CN102558563B publication Critical patent/CN102558563B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高粘度107胶的制备方法，将一定量的DMC和粘度为100～1500cs的107胶或将一定量的DMC加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，升温至一定温度时加入碱性催化剂，碱性催化剂包括氢氧化钾、四甲基氢氧化铵、四丁基氢氧化磷或以上碱的硅醇盐碱胶的一种；在此温度下平衡反应数小时，直接进行中和或升温分解碱性催化剂；如果中和，则加入与催化剂同样质量的磷酸或其硅醇盐酸胶中和剂，如不需中和则直接升温分解碱性催化剂，继续搅拌1小时，然后脱除低沸物。本发明制得的高粘度107胶，制备工艺简单，粘度稳定，产品收率高，满足生产的需要。

Description

一种高粘度107胶的制备方法
技术领域
本发明涉及一种107胶的制备方法，尤其是一种高粘度107胶的制备方法。
背景技术
107胶是一种羟基封端聚二甲基硅氧烷。与交联剂、催化剂，在室温下固化，能在-60～200℃温度范围内长期保持弹性，具有优良的电性能和化学稳定性，能耐水、耐气候老化。广泛用于建筑填缝、电子元件的绝缘、防震、防潮、防腐蚀，橡塑制品的制模、脱模及作皮革滑爽剂、隔离剂等，特种规格可用于织物整理和日用化工业上。
目前高粘度107胶（>20万CS）的工艺流程是DMC先在一定的温度和真空下脱水，DMC脱水后，升至一定温度加四甲基氢氧化铵碱性催化剂，开环聚合至一定粘度，加水降解，升温破坏碱性催化剂，然后脱除低沸。此工艺中间过程控制是依靠中控分析的结果来决定，过程控制存在不稳定性，也存在等待浪费。
DMC是二甲基环硅氧烷混合物的简称。
发明内容
本发明目的在于提供一种高粘度107胶的制备方法，利用低粘度107胶为封端剂，过程控制稳定，不存在等待浪费。
一种高粘度107胶的制备方法，按以下重量配比：将200份DMC和6-50份粘度为100-1500cs 的107胶加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，升温至90-150℃时加入15-110ppm催化剂，并在90～170℃下平衡反应2～4小时，升温分解或直接进行中和碱性催化剂；如果中和，则加入与催化剂同样质量的磷酸或其硅醇盐酸胶中和剂，如不需中和则直接升温分解碱性催化剂，继续搅拌1小时，在1KPa /180℃下脱至无馏出物为止。
一种高粘度107胶的制备方法，按以下重量配比：将300gDMC加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，在50～60℃，2Kpa下脱水20min，消除真空，升温至90-170℃时加入15-110ppm催化剂，在此温度下反应2～3小时，加0.05-0.1份水降解，3小时升温分解或直接进行中和碱性催化剂；如果中和，则加入与催化剂同样质量的磷酸或其硅醇盐酸胶中和剂，如不需中和则直接升温分解碱性催化剂，继续搅拌1小时，然后在1KPa /180℃下脱至无馏出物为止。
其中催化剂为氢氧化钾、四甲基氢氧化铵、四丁基氢氧化磷或以上碱的硅醇盐碱胶的一种。
本发明制得的高粘度107胶，制备工艺简单，粘度稳定，产品收率高，满足生产的需要。
粘度越高的107胶，粘合能力强，适应面较广。
具体实施方式
实施例1：
一种高粘度107胶的制备方法，按以下重量配比：将200份DMC和6份粘度为100cs 的107胶加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，升温至110℃时加入15ppm氢氧化钾或其硅醇盐碱胶，并在150℃下平衡反应2小时，加15ppm磷酸或其硅醇盐酸胶直接进行中和，搅拌1小时，在1KPa /180℃下脱至无馏出物为止，得粘度（25℃）48万cs、无色透明高粘度的改性107胶178.2份，收率86.5%。
实施例2：
一种高粘度107胶的制备方法，按以下重量配比：200份DMC和30份粘度为750cs的 107胶加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，升温至110℃时加入50ppm四甲基氢氧化铵或其硅醇盐碱胶催化剂，并在此温度下反应3小时，升温分解催化剂，然后在1KPa /180℃下脱至无馏出物为止，得粘度（25℃）32万cs、无色透明高粘度的改性107胶199.4份，收率86.7%；收率高。
实施例3：
一种高粘度107胶的制备方法，按以下重量配比：200份DMC和50份粘度为1500cs 的107胶加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，升温至100℃时加入110ppm四丁基氢氧化磷硅醇盐碱胶催化剂，并在此温度下反应4小时，升温分解碱性催化剂，然后在1KPa /180℃下脱至无馏出物为止，得粘度（25℃）80万cs、无色透明高粘度的改性107胶215份，收率86.0%。
实施例4：
一种高粘度107胶的制备方法，按以下重量配比：300份DMC加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，在50℃，2Kpa脱水20min，消除真空，升温至110℃时加入15ppm氢氧化钾或其硅醇盐碱胶催化剂，并在150℃下平衡反应2小时，加0.05份水降解，3小时后，加15ppm磷酸或其硅醇盐酸胶直接进行中和，搅拌1小时，然后在1KPa /180℃下脱至无馏出物为止，得粘度（25℃）47万cs、无色透明高粘度的改性107胶253.5份，收率84.5%。
实施例5：
一种高粘度107胶的制备方法，按以下重量配比：将300份DMC加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，在55℃，2Kpa下脱水20min，消除真空，升温至100℃时加入50ppm四丁基氢氧化磷硅醇盐碱胶催化剂，在此温度下反应2.5小时，加0.07份水降解，3小时后升温分解碱性催化剂，然后在1KPa /180℃下脱至无馏出物为止，得粘度（25℃）46万cs、无色透明高粘度的改性107胶254.7份，收率84.9%；收率高。
实施例6：
   一种高粘度107胶的制备方法，按以下重量配比：将300份DMC加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，在60℃，2Kpa脱水20min，消除真空，升温至90℃时加入110ppm四甲基氢氧化铵或其硅醇盐碱胶催化剂，在此温度下反应3小时，加0.1份水降解，3小时后升温分解碱性催化剂，然后在1KPa /180℃下脱至无馏出物为止，得粘度（25℃）35万cs、无色透明高粘度的改性107胶253份，收率84.3%。
实施例7：
一种高粘度107胶的制备方法，按以下重量配比：200份DMC和30份粘度为750cs的 107胶加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，升温至110℃时加入30ppm四甲基氢氧化铵或其硅醇盐催化剂，并在此温度下反应3小时，升温分解催化剂，然后在1KPa /180℃下脱至无馏出物为止，得粘度（25℃）32万cs、无色透明高粘度的改性107胶151.3份，收率65.8%。
实施例8：
一种高粘度107胶的制备方法，按以下重量配比：将300份DMC加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，在55℃，2Kpa下脱水20min，消除真空，升温至110℃时加入 25ppm四丁基氢氧化磷硅醇盐碱胶催化剂，在此温度下反应2.5小时，加0.07份水降解，3小时后升温分解碱性催化剂，然后在1KPa /180℃下脱至无馏出物为止，得粘度（25℃）46万cs、无色透明高粘度的改性107胶191.1份，收率63.7%。
实施例9：
一种高粘度107胶的制备方法，按以下重量配比：200份DMC和60份粘度为1600cs的 107胶加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，升温至100℃时加入13ppm氢氧化钾或其硅醇盐碱胶催化剂，并在140℃下反应3小时，加13ppm磷酸或其硅醇盐酸胶直接进行中和，搅拌1小时，然后在1KPa /180℃下脱至无馏出物为止，得粘度（25℃）18万cs、无色透明高粘度的改性107胶179.7份，收率69.1%。
实施例10：
一种高粘度107胶的制备方法，按以下重量配比：将300份DMC加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，在45℃，2Kpa下脱水20min，消除真空，升温至100℃时加入 120ppm四甲基氢氧化铵或其硅醇盐碱胶催化剂，在此温度下反应3.5小时，加0.13份水降解，3小时后升温分解碱性催化剂，然后在1KPa /180℃下脱至无馏出物为止，得粘度（25℃）16万cs、无色透明高粘度的改性107胶195.3份，收率65.1%。

Claims (5)

1.一种高粘度107胶的制备方法，其特征为：按以下重量配比：将200份DMC和6-50份粘度为100-1500cs 的107胶加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，升温至90-150℃时加入15-110ppm碱性催化剂，并在90～170℃下平衡反应2～4小时，升温分解或直接进行中和碱性催化剂；如果中和，则加入与催化剂同样质量的酸性中和剂，如不需中和则直接升温分解碱性催化剂，继续搅拌1小时，在1KPa /180℃下脱至无馏出物为止。
2.一种高粘度107胶的制备方法，其特征为：按以下重量配比：将300份DMC加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，在50～60℃，2Kpa下脱水20min，消除真空，升温至90-170℃时加入15-110ppm碱性催化剂，在此温度下反应2～3小时，加0.05-0.1份水降解，3小时后升温分解或直接进行中和碱性催化剂；如果中和，则加入与催化剂同样质量的酸性中和剂，如不需中和则直接升温分解碱性催化剂，继续搅拌1小时，然后在1KPa /180℃下脱至无馏出物为止。
3.如权利要求1、2所述的一种高粘度107胶的制备方法，其特征为：碱性催化剂为氢氧化钾、四甲基氢氧化铵、四丁基氢氧化磷或以上碱的硅醇盐碱胶的一种；酸性中和剂为磷酸或其硅醇盐酸胶。
4.如权利要求1所述的一种高粘度107胶的制备方法，其特征为：按以下重量配比：将200份DMC和30份粘度为750cs的 107胶加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，升温至110℃时加入50ppm四甲基氢氧化铵硅醇盐碱胶催化剂，并在此温度下反应3小时，升温分解催化剂，然后在1KPa /180℃下脱至无馏出物为止。
5.如权利要求2所述的一种高粘度107胶的制备方法，其特征为：按以下重量配比：将300份DMC加入装有搅拌器、温度计及冷凝回流管的反应器皿中，开启搅拌，在55℃，2Kpa下脱水20min，消除真空，升温至100℃时加入15ppm氢氧化钾或其硅醇盐碱胶催化剂，在此温度下反应2.5小时，加0.07份水降解，3小时后加入与催化剂同样质量的磷酸或其硅醇盐酸胶中和剂，然后在1KPa /180℃下脱至无馏出物为止。
CN201110454586.5A 2011-12-30 2011-12-30 一种高粘度107胶的制备方法 Active CN102558563B (zh)