CN102503460B - 一种采用复合促硬剂的磷酸盐结合浇注料 - Google Patents

一种采用复合促硬剂的磷酸盐结合浇注料 Download PDF

Info

Publication number
CN102503460B
CN102503460B CN201110321754.3A CN201110321754A CN102503460B CN 102503460 B CN102503460 B CN 102503460B CN 201110321754 A CN201110321754 A CN 201110321754A CN 102503460 B CN102503460 B CN 102503460B
Authority
CN
China
Prior art keywords
aggregate
powder
corundum
hardening
micro mist
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201110321754.3A
Other languages
English (en)
Other versions
CN102503460A (zh
Inventor
赵洪亮
袁林
王俊涛
王杰曾
陈雪峰
刘锡俊
叶亚红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
RUITAI TECHNOLOGY Co.,Ltd.
Original Assignee
RUITAI TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by RUITAI TECHNOLOGY Co Ltd filed Critical RUITAI TECHNOLOGY Co Ltd
Priority to CN201110321754.3A priority Critical patent/CN102503460B/zh
Publication of CN102503460A publication Critical patent/CN102503460A/zh
Application granted granted Critical
Publication of CN102503460B publication Critical patent/CN102503460B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种采用复合促硬剂的磷酸盐结合浇注料，属于耐火材料技术领域。以质量百分比计，其主要原料如下：骨料采用刚玉或高铝矾土，骨料所占比重55～75wt％；粉料采用刚玉粉、矾土粉、SiO2微粉及α-Al2O3微粉，粉料所占比重9～40wt％，其中刚玉粉0～37wt％，矾土粉0～37wt％，SiO2微粉1～8wt％，α-Al2O3微粉3～12wt％；复合促硬剂为纯铝酸钙水泥和ρ-Al2O3微粉，添加比例为5～16wt％；缓蚀剂为NH66型抑制剂，主要化学成分是碘氧鞣酸铋，外加比例为0.1～0.25wt％；结合剂为磷酸盐(磷酸铝溶液)，其P2O5/Al2O3分子比为1/2.5～1/3.8，施工时外加比例为8～18wt％。该磷酸盐结合浇注料具有高强、耐磨、抗热震、脱模时间短、可快速烘烤等优点，且具有良好的耐高温性能。

Description

一种采用复合促硬剂的磷酸盐结合浇注料
技术领域
本发明涉及耐火材料领域，具体涉及一种采用复合促硬剂的磷酸盐结合浇注料。
背景技术
磷酸盐结合浇注料具有热震稳定性好，耐压强度高，耐磨、耐冲刷等优越性能，被广泛的应用于各种热工窑炉的炉衬材料。
但是，目前常用的磷酸盐结合浇注料所采用的促硬剂主要为高铝水泥和MgO细粉，采用高铝水泥做促硬剂时，引入的CaO降低了材料的高温性能；采用MgO细粉做促硬剂时，由于MgO细粉与磷酸盐反应迅速，导致施工工艺复杂困难。同时，由于原料中和原料在破碎过程中引入了部分金属铁，使得目前常用的磷酸盐结合浇注料在使用时需要困料，给施工带来麻烦。
发明内容
本发明的目的在于研究一种采用复合促硬剂的磷酸盐结合浇注料，要解决的技术问题是提供一种采用复合促硬剂的磷酸盐结合浇注料，通过采用复合促硬剂解决其常温固化问题，常温可正常固化脱模，高温热处理后，由于降低了CaO的引入量，其具有良好的高温性能；该材料具有高强、耐磨、抗热震、脱模时间短、可快速烘烤等优点，且具有良好的耐高温性能。
本发明采用的技术方案是：
采用复合促硬剂和缓蚀剂，以质量百分比计，其主要原料如下：骨料采用刚玉或高铝矾土，骨料所占比重55～75wt％；粉料采用刚玉粉、矾土粉、SiO2微粉及α-Al2O3微粉，粉料所占比重11～40wt％，其中刚玉粉0～36.5wt％，矾土粉0～36.5wt％，SiO2微粉0.5～8wt％，α-Al2O3微粉3～12wt％；复合促硬剂为纯铝酸钙水泥和ρ-Al2O3微粉，添加比例为2～14wt％；缓蚀剂为NH66型抑制剂，主要化学成分是碘氧鞣酸铋，外加比例为0.1～0.25wt％；结合剂为磷酸盐(磷酸铝溶液)，其P2O5/Al2O3分子比为1/2.5～1/3.8，施工时外加比例为8～18wt％。
上述骨料分为三级粒度：粗骨料--5～3mm，中骨料--3～1mm，细骨料--1～0mm，所述粉料的粒度为0.088mm以下；
上述骨料为刚玉和高铝矾土的至少一种，所述刚玉Al2O3＞95wt％，高铝矾土Al2O3＞75wt％。
上述刚玉为板状刚玉、白刚玉、棕刚玉中的至少一种。
上述高铝矾土为特级高铝矾土、一级高铝矾土中的至少一种。
上述复合促硬剂中各组分所占比例为：纯铝酸钙水泥8～50wt％，ρ-Al2O3微粉50～92wt％。
本发明具有积极有益的效果：
(1)本发明产品采用ρ-Al2O3和铝酸盐水泥复合促硬，极大地减低作为促硬剂的水泥含量，磷酸盐浇注料耐高温性得以大幅度提高；
(2)本发明具有高强、耐磨、抗热震、可快速烘烤，且具有良好的耐高温性能等优点，易于推广使用。
(3)该采用复合促硬剂的磷酸盐结合浇注料的综合性能指标如表1所示：
表1 采用复合促硬剂的磷酸盐结合浇注料的性能指标
Figure BSA00000596077000021
Figure BSA00000596077000031
具体实施方式
实施例1 一种采用复合促硬剂的磷酸盐结合浇注料，具体重量百分比配比如下：
Figure BSA00000596077000032
实施例2 一种采用复合促硬剂的磷酸盐结合浇注料，具体重量百分比配比如下：
Figure BSA00000596077000033
实施例3 一种采用复合促硬剂的磷酸盐结合浇注料，具体重量百分比配比如下：
Figure BSA00000596077000041
实施例4 一种采用复合促硬剂的磷酸盐结合浇注料，具体重量百分比配比如下：
Figure BSA00000596077000042
实施例5 一种采用复合促硬剂的磷酸盐结合浇注料，具体重量百分比配比如下：
实施例6 一种采用复合促硬剂的磷酸盐结合浇注料，具体重量百分比配比如下：
实施例1～6的性能指标如下表所示：

Claims (1)

1.一种采用复合促硬剂的磷酸盐结合浇注料，其特征在于：采用复合促硬剂和缓蚀剂，以质量百分比计，其主要原料如下：骨料采用刚玉或高铝矾土，骨料所占比重55～75wt％；粉料采用刚玉粉、矾土粉、SiO2微粉及α-Al2O3微粉，粉料所占比重9～40wt％，其中刚玉粉0～37wt％，矾土粉0～37wt％，SiO2微粉1～8wt％，α-Al2O3微粉3～12wt％；复合促硬剂为纯铝酸钙水泥和ρ-Al2O3微粉，添加比例为5～16wt％；缓蚀剂为NH66型抑制剂，主要化学成分是碘氧鞣酸铋，外加比例为0.1～0.25wt％；结合剂为磷酸铝溶液，其P2O5/Al2O3分子比为1/2.5～1/3.8，施工时外加比例为8～18wt％；所述骨料分为三级粒度：粗骨料--5～3mm，中骨料--3～1mm，细骨料--1～0mm，所述粉料的粒度为0.088mm以下；所述骨料为刚玉和高铝矾土的至少一种，所述刚玉Al2O3＞90wt％，高铝矾土Al2O3＞80wt％所述刚玉为板状刚玉、白刚玉、棕刚玉中的至少一种；所述高铝矾土为特级高铝矾土、一级高铝矾土中的至少一种；所述复合促硬剂中各组分所占比例为：纯铝酸钙水泥8～50wt％，ρ-Al2O3微粉50～92wt％。
CN201110321754.3A 2011-10-12 2011-10-12 一种采用复合促硬剂的磷酸盐结合浇注料 Active CN102503460B (zh)