CN101805198A - 莫来石钢纤维浇注料 - Google Patents
莫来石钢纤维浇注料 Download PDFInfo
- Publication number
- CN101805198A CN101805198A CN 201010158847 CN201010158847A CN101805198A CN 101805198 A CN101805198 A CN 101805198A CN 201010158847 CN201010158847 CN 201010158847 CN 201010158847 A CN201010158847 A CN 201010158847A CN 101805198 A CN101805198 A CN 101805198A
- Authority
- CN
- China
- Prior art keywords
- mullite
- steel fiber
- fiber castable
- castable
- corundum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种莫来石钢纤维浇注料,以重量百分含量表示,该莫来石钢纤维浇注料原料配比中含有棕刚玉29~40%,高铝矾土熟料10~15%,烧结莫来石18~32%,电熔莫来石8~12%,硅微粉3~7%,促凝剂2~5%和不锈钢纤维1~3%。将按照莫来石钢纤维浇注料原料配比比例配制好的各种原料混合进行搅拌,搅拌5~10分钟即可。利用本发明技术方案制备的莫来石钢纤维浇注料,与现有普通高铝浇注料相比,具有较高的耐压强度和抗折强度,并且体积密度大。本发明产品莫来石钢纤维浇注料具有良好的抗热震性能、抗冲刷性能和体积稳定性。
Description
一、技术领域:
本发明涉及一种不定形耐火材料,特别是涉及一种莫来石钢纤维浇注料。
二、背景技术:
在耐火材料的应用中,不定形耐火材料具有投资少、能耗省、制成之整体衬体热震稳定性好、气密性好、能修补炉衬等优点,因此它与耐火砖等定性耐火材料相比,应用更为广泛。浇注料是目前生产和使用最广泛的一种不定形耐火材料,主要用于构筑加热炉内衬等整体构筑物,其优质品种也可用于冶炼炉,工业上常使用的耐火浇注料主要有铝酸盐浇注料、水玻璃浇注料和磷酸盐浇注料等。
目前,铁钩沟盖、出铁嘴下部等部位使用的一种不定形耐火材料也是浇注料,该浇注料大多数是普通高铝浇注料。由于普通高铝浇注料在使用过程中发现,其热震性能和抗冲刷性能较差,从而严重影响了使用寿命;并且使用过程中局部还很容易出现裂纹和塌陷现象,体积受高温影响后收缩变化特别大,给现场操作机安全方面造成了极大的不利条件。因此,为了更好的满足铁钩沟盖、出铁嘴下部等部位对浇注料性能的更高要求,需要对普通高铝浇注料的抗热震、抗冲刷、体积稳定性等方面进行有效的改进。
目前,关于普通高铝浇注料的专利文献报道也有不少,例如:1、申请号为88102344.2、发明名称为高铝出铁钩浇注料,该发明浇注料采用棕刚玉为主要原料,适当配入炭化硅、碳质材料、粘土、高铝水泥、超微粉、外加剂制备而成,该浇注料原料易得、成本低廉、施工方便、使用寿命长。2、申请号200410012778.0、发明名称为一种Al2O3-SiC-C铁沟浇注料的制备方法,该浇注料采用电熔致密刚玉和SiC为骨料,基质部分包括刚玉粉、超细粉、高铝水泥,以及氮化硅、金属硅,外加分散剂,将物料混合加水搅拌后,浇注成型、养护、干燥。该发明的铁沟浇注料易施工、强度高,且具有优良的抗铁水、熔渣的侵蚀、渗透、冲刷性能。
为了进一步改善普通高铝浇注料的抗热震、抗冲刷和体积稳定性,更好的满足铁钩沟盖、出铁嘴下部等部位的要求,本发明研制出了一种莫来石钢纤维浇注料。
三、发明内容:
本发明要解决的技术问题是提供一种莫来石钢纤维浇注料,本发明产品莫来石钢纤维浇注料与目前普通高铝浇注料相比,具有良好的抗热震性能和抗冲刷性能。
为了解决上述问题,本发明采用的技术方案是:
本发明提供一种莫来石钢纤维浇注料,以重量百分含量表示,所述莫来石钢纤维浇注料原料配比中含有棕刚玉29~40%,高铝矾土熟料10~15%,烧结莫来石18~32%,电熔莫来石8~12%,硅微粉3~7%,促凝剂2~5%和不锈钢纤维1~3%。
根据上述的莫来石钢纤维浇注料,所述棕刚玉29~40%是由3~5mm棕刚玉8~12%、1~3mm棕刚玉13~16%和细度为200目棕刚玉8~12%组成;所述棕刚玉中Al2O3的含量≥95%。
根据上述的莫来石钢纤维浇注料,所述高铝矾土熟料为山西优质高铝矾土熟料,其中Al2O3的含量≥85%;所述高铝矾土熟料的粒度为5~8mm。
根据上述的莫来石钢纤维浇注料,所述烧结莫来石18~32%是由1~3mm烧结莫来石10~20%和0~1mm烧结莫来石8~12%组成;所述烧结莫来石中Al2O3的含量≥72%。
根据上述的莫来石钢纤维浇注料,所述电熔莫来石的细度为200目;所述电熔莫来石中Al2O3的含量≥72%。
根据上述的莫来石钢纤维浇注料,所述硅微粉的粒度<1μm,硅微粉中SiO2的含量≥90%。
根据上述的莫来石钢纤维浇注料,所述促凝剂为拉法基水泥或纯铝酸钙水泥。
本发明莫来石钢纤维浇注料的制备方法:按照上述莫来石钢纤维浇注料原料配比比例配制好各种原料,将各种原料混合进行搅拌,搅拌5~10分钟即可。
本发明的积极有益效果:
1、本发明以棕刚玉、高铝矾土熟料、莫来石为主要原料,外加硅微粉、促凝剂和不锈钢纤维制备而成的莫来石钢纤维浇注料,具有良好的抗热震性能和抗冲刷性能,完全能够满足铁钩沟盖、出铁嘴下部等部位对浇注料的更高要求。
2、利用本发明技术方案制备的莫来石钢纤维浇注料,与现有普通高铝浇注料相比,具有较高的耐压强度和抗折强度,并且体积密度大。因而,本发明产品莫来石钢纤维浇注料具有良好的抗热震性能、抗冲刷性能和体积稳定性(其性能指标详见表一)。
3、本发明技术方案以棕刚玉、高铝矾土孰料、烧结莫来石和电熔莫来石为主要原料生产莫来石钢纤维浇注料,其生产成本较低,具有显著的经济效益。
表一本发明产品的性能指标
四、具体实施方式:
以下实施例仅为了进一步说明本发明,并不限制本发明的内容。
实施例1:
本发明莫来石钢纤维浇注料原料配比:以重量百分含量表示,由棕刚玉35%,山西优质高铝矾土熟料(粒度为5~8mm)15%,烧结莫来石30%,电熔莫来石(细度为200目)10%,硅微粉5%,促凝剂(拉法基水泥)3%和不锈钢纤维2%组成。
所采用原料棕刚玉中中Al2O3的含量≥95%;山西优质高铝矾土熟料中Al2O3的含量≥85%;所述烧结莫来石中Al2O3的含量≥72%;所述电熔莫来石中Al2O3的含量≥72%;
本发明莫来石钢纤维浇注料所用原料棕刚玉35%是由3~5mm棕刚玉10%、1~3mm棕刚玉15%和细度为200目棕刚玉10%组成;
本发明莫来石钢纤维浇注料所用原料烧结莫来石30%是由1~3mm烧结莫来石20%和0~1mm烧结莫来石10%组成;
所采用原料硅微粉的粒度<1μm,硅微粉中SiO2的含量≥90%。
莫来石钢纤维浇注料制备方法:按照上述莫来石钢纤维浇注料原料配比比例配制好各种原料,将各种原料混合进行搅拌,搅拌5~10分钟即可。
实施例2:与实施例1基本相同,不同之处在于:
本发明莫来石钢纤维浇注料原料配比:以重量百分含量表示,由棕刚玉29%,山西优质高铝矾土熟料(粒度为5~8mm)15%,烧结莫来石32%,电熔莫来石(细度为200目)12%,硅微粉6%,促凝剂(拉法基水泥)3.5%和不锈钢纤维2.5%组成。
本发明莫来石钢纤维浇注料所用原料棕刚玉29%是由3~5mm棕刚玉8%、1~3mm棕刚玉13%和细度为200目棕刚玉8%组成。
本发明莫来石钢纤维浇注料所用原料烧结莫来石32%是由1~3mm烧结莫来石20%和0~1mm烧结莫来石12%组成。
实施例3:与实施例1基本相同,不同之处在于:
本发明莫来石钢纤维浇注料原料配比:以重量百分含量表示,由棕刚玉40%,山西优质高铝矾土熟料(粒度为5~8mm)10%,烧结莫来石30%,电熔莫来石(细度为200目)8%,硅微粉7%,促凝剂(拉法基水泥)2%和不锈钢纤维3%组成。
本发明莫来石钢纤维浇注料所用原料棕刚玉40%是由3~5mm棕刚玉12%、1~3mm棕刚玉16%和细度为200目棕刚玉12%组成。
本发明莫来石钢纤维浇注料所用原料烧结莫来石30%是由1~3mm烧结莫来石18%和0~1mm烧结莫来石12%组成。
实施例4:与实施例1基本相同,不同之处在于:
本发明莫来石钢纤维浇注料原料配比:以重量百分含量表示,由棕刚玉40%,山西优质高铝矾土熟料(粒度为5~8mm)15%,烧结莫来石18%,电熔莫来石(细度为200目)12%,硅微粉7%,促凝剂(拉法基水泥)5%和不锈钢纤维3%组成。
本发明莫来石钢纤维浇注料所用原料棕刚玉40%是由3~5mm棕刚玉12%、1~3mm棕刚玉16%和细度为200目棕刚玉12%组成。
本发明莫来石钢纤维浇注料所用原料烧结莫来石18%是由1~3mm烧结莫来石10%和0~1mm烧结莫来石8%组成。
实施例5:与实施例1基本相同,不同之处在于:
本发明莫来石钢纤维浇注料原料配比:以重量百分含量表示,由棕刚玉38%,山西优质高铝矾土熟料(粒度为5~8mm)13%,烧结莫来石28%,电熔莫来石(细度为200目)10%,硅微粉6%,促凝剂(拉法基水泥)4%和不锈钢纤维1%组成。
本发明莫来石钢纤维浇注料所用原料棕刚玉38%是由3~5mm棕刚玉10%、1~3mm棕刚玉16%和细度为200目棕刚玉12%组成。
本发明莫来石钢纤维浇注料所用原料烧结莫来石28%是由1~3mm烧结莫来石16%和0~1mm烧结莫来石12%组成。
实施例6:与实施例1基本相同,不同之处在于:
本发明莫来石钢纤维浇注料原料配比:以重量百分含量表示,由棕刚玉33%,山西优质高铝矾土熟料(粒度为5~8mm)15%,烧结莫来石25%,电熔莫来石(细度为200目)12%,硅微粉7%,促凝剂(拉法基水泥)5%和不锈钢纤维3%组成。
本发明莫来石钢纤维浇注料所用原料棕刚玉33%是由3~5mm棕刚玉9%、1~3mm棕刚玉15%和细度为200目棕刚玉9%组成。
本发明莫来石钢纤维浇注料所用原料烧结莫来石25%是由1~3mm烧结莫来石15%和0~1mm烧结莫来石10%组成。
实施例7:与实施例1基本相同,不同之处在于:
本发明莫来石钢纤维浇注料原料配比:以重量百分含量表示,由棕刚玉40%,山西优质高铝矾土熟料(粒度为5~8mm)15%,烧结莫来石22%,电熔莫来石(细度为200目)12%,硅微粉5%,促凝剂(拉法基水泥)3%和不锈钢纤维3%组成。
本发明莫来石钢纤维浇注料所用原料棕刚玉40%是由3~5mm棕刚玉12%、1~3mm棕刚玉16%和细度为200目棕刚玉12%组成。
本发明莫来石钢纤维浇注料所用原料烧结莫来石22%是由1~3mm烧结莫来石12%和0~1mm烧结莫来石10%组成。
实施例8:与实施例1基本相同,不同之处在于:
本发明莫来石钢纤维浇注料原料配比:以重量百分含量表示,由棕刚玉38%,山西优质高铝矾土熟料(粒度为5~8mm)12%,烧结莫来石30%,电熔莫来石(细度为200目)10%,硅微粉5%,促凝剂(拉法基水泥)3.5%和不锈钢纤维1.5%组成。
本发明莫来石钢纤维浇注料所用原料棕刚玉38%是由3~5mm棕刚玉12%、1~3mm棕刚玉16%和细度为200目棕刚玉10%组成。
本发明莫来石钢纤维浇注料所用原料烧结莫来石30%是由1~3mm烧结莫来石19%和0~1mm烧结莫来石11%组成。
Claims (7)
1.一种莫来石钢纤维浇注料,其特征在于:以重量百分含量表示,所述莫来石钢纤维浇注料原料配比中含有棕刚玉29~40%,高铝矾土熟料10~15%,烧结莫来石18~32%,电熔莫来石8~12%,硅微粉3~7%,促凝剂2~5%和不锈钢纤维1~3%。
2.根据权利要求1所述的莫来石钢纤维浇注料,其特征在于:所述棕刚玉29~40%是由3~5mm棕刚玉8~12%、1~3mm棕刚玉13~16%和细度为200目棕刚玉8~12%组成;所述棕刚玉中Al2O3的含量≥95%。
3.根据权利要求1所述的莫来石钢纤维浇注料,其特征在于:所述高铝矾土熟料为山西优质高铝矾土熟料,其中Al2O3的含量≥85%;所述高铝矾土熟料的粒度为5~8mm。
4.根据权利要求1所述的莫来石钢纤维浇注料,其特征在于:所述烧结莫来石18~32%是由1~3mm烧结莫来石10~20%和0~1mm烧结莫来石8~12%组成;所述烧结莫来石中Al2O3的含量≥72%。
5.根据权利要求1所述的莫来石钢纤维浇注料,其特征在于:所述电熔莫来石的细度为200目;所述电熔莫来石中Al2O3的含量≥72%。
6.根据权利要求1所述的莫来石钢纤维浇注料,其特征在于:所述硅微粉的粒度<1μm,硅微粉中SiO2的含量≥90%。
7.根据权利要求1所述的莫来石钢纤维浇注料,其特征在于:所述促凝剂为拉法基水泥或纯铝酸钙水泥。