CN102320774A - 一种混凝土专用防腐阻锈抗渗防裂复合外加剂 - Google Patents
一种混凝土专用防腐阻锈抗渗防裂复合外加剂 Download PDFInfo
- Publication number
- CN102320774A CN102320774A CN 201110212499 CN201110212499A CN102320774A CN 102320774 A CN102320774 A CN 102320774A CN 201110212499 CN201110212499 CN 201110212499 CN 201110212499 A CN201110212499 A CN 201110212499A CN 102320774 A CN102320774 A CN 102320774A
- Authority
- CN
- China
- Prior art keywords
- concrete
- composite additive
- compound additive
- seepage
- special anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种混凝土专用防腐阻锈抗渗防裂复合外加剂,该复合外加剂由重量百分比为20%~40%的微硅粉、16%~24%的高效减水剂、10%~20%的YS链状硅酸盐纳米材料、6%~10%的三乙醇胺、20~40%的氯化亚铁和6%~10%的乳胶粉混合而成。本发明可有效发挥阻锈效果,提高混凝土的抗渗性能、抗冻融性能等耐久性能指标,有效抑制混凝土中碱骨料反应的发生,对收缩也有一定的抑制作用,可广泛用于盐渍土、盐湖及沿海地区的混凝土建构筑物,也可广泛应用于有色金属冶炼、化工、石油、钢铁等有腐蚀性物质存在的工业建筑。
Description
技术领域
本发明涉及一种混凝土外加剂,尤其涉及一种混凝土专用防腐阻锈抗渗防裂复合外加剂。
背景技术
混凝土的耐久性破坏很少是单一因素引起的腐蚀,通常氯盐引起钢筋锈蚀的同时,往往并发硫酸盐、镁盐等的侵蚀腐蚀作用。现有混凝土外加剂功能较为单一,如需同时满足抗硫、阻锈、抗渗、防裂等要求,则需掺入不同种类的外加剂,且不同种类外加剂可能相互反应,最终影响混凝土质量,无法达到预期效果,导致成品混凝土性能及质量不易控制,提高了工程建设成本。
因此,如何能够一次解决多样作用相互交织的严重问题,既保护混凝土不被环境盐类腐蚀又不发生钢筋锈蚀状况将是对混凝土结构耐久性的有力保护,已成为众多混凝土材料研究人员的关注焦点。
发明内容
本发明所要解决的技术问题是提供一种有效提高混凝土耐久性、降低工程建设成本的混凝土专用防腐阻锈抗渗防裂复合外加剂。
为解决上述问题,本发明所述的一种混凝土专用防腐阻锈抗渗防裂复合外加剂,其特征在于:该复合外加剂由重量百分比为20%~40%的微硅粉、16%~24%的高效减水剂、10%~20%的YS链状硅酸盐纳米材料、6%~10%的三乙醇胺、20~40%的氯化亚铁和6%~10%的乳胶粉混合而成。
所述微硅粉为比表面积为16000~28000m2/kg,氯离子含量≤0.25%。
所述高效减水剂为粉状的萘系减水剂。
所述三乙醇胺为纯度大于99%的三乙醇胺。
所述乳胶粉为可再分散乳胶粉。
本发明与现有技术相比具有以下优点:
1、本发明根据混凝土及钢筋混凝土在盐渍土、沿海地区的腐蚀规律,设计出能够抵抗硫酸根、氯离子以及它们复合存在情况下,冻融破坏、碱骨料反应、收缩等单一破坏形式或二种及以上的破坏形式同时发生时的耐久性混凝土复合外加剂,为腐蚀环境中混凝土的耐久性设计提出有效的解决方案,为工业与民用建筑混凝土的耐久性提供有力保护,从而提高混凝土的使用寿命,降低混凝土结构用于维修和重建的费用,同时形成耐久性混凝土外加剂的产业化基地。
2、由于本发明中添加具有抗渗、防腐、防止混凝土碱骨料反应的微硅粉,同时还添加有链状硅酸盐纳米材料,因此,可有效发挥阻锈效果,提高混凝土的抗渗性能、抗冻融性能等耐久性能指标,有效抑制混凝土中碱骨料反应的发生,对收缩也有一定的抑制作用。
3、无毒、环保:本发明所涉及材料反应前、反应中及反应后无毒、无异味,对环境无污染。
4、由于本发明中既有有机复合阻锈成分,也有无机复合阻锈成分,因此,将本发明应用于混凝土中时,其综合造价低于抗硫酸盐硅酸盐水泥+有机或无机阻锈剂配制的混凝土,且性能优于抗硫酸盐硅酸盐水泥混凝土,可广泛用于盐渍土、盐湖及沿海地区的混凝土建构筑物,也可广泛应用于有色金属冶炼、化工、石油、钢铁等有腐蚀性物质存在的工业建筑。
5、本发明已成功应用在青藏铁路二期工程、青藏铁路复线工程、酒钢榆中钢厂等国家重点工程,并获得广泛好评,取得了很好的社会效益和经济效益。
具体实施方式
设备:砂浆混合机,(上海升立机械制造有限公司,WZL无重力混合机)。
材料:
1、微硅粉为为比表面积大于16000~28000m2/kg,氯离子含量≤0.25%,市售。
2、高效减水剂为粉状萘系减水剂,生产厂家为甘肃蔚蓝建科新材料有限公司。
3、YS链状硅酸盐纳米材料的生产厂家为兰州有色建筑新技术实业开发公司。
4、三乙醇胺为浓度大于99%的市售三乙醇胺。
5、氯化亚铁为市售,一级品。
6、乳胶粉为可再分散乳胶粉(VAE),市售。
实施例1一种混凝土专用防腐阻锈抗渗防裂复合外加剂,由重量百分比为20%的微硅粉、18%的高效减水剂、15%的YS链状硅酸盐纳米材料、6%的三乙醇胺、34%的氯化亚铁和7%的乳胶粉混合而成。
其制备方法是:将各组分按配比称量后,放入混合机中,混合30~50min后,按每袋25kg包装成袋即得。
实施例2一种混凝土专用防腐阻锈抗渗防裂复合外加剂,由重量百分比为32%的微硅粉、16%的高效减水剂、20%的YS链状硅酸盐纳米材料、6%的三乙醇胺、20%的氯化亚铁和6%的乳胶粉混合而成。
其制备方法同实施例1。
实施例3一种混凝土专用防腐阻锈抗渗防裂复合外加剂,由重量百分比为40%的微硅粉、17%的高效减水剂、10%的YS链状硅酸盐纳米材料、7%的三乙醇胺、20%的氯化亚铁和6%的乳胶粉混合而成。
其制备方法同实施例1。
实施例4一种混凝土专用防腐阻锈抗渗防裂复合外加剂,由重量百分比为24%的微硅粉、24%的高效减水剂、11%的YS链状硅酸盐纳米材料、10%的三乙醇胺、21%的氯化亚铁和10%的乳胶粉混合而成。
其制备方法同实施例1。
实施例5一种混凝土专用防腐阻锈抗渗防裂复合外加剂,由重量百分比为21%的微硅粉、16%%的高效减水剂、11%的YS链状硅酸盐纳米材料、6%的三乙醇胺、40%的氯化亚铁和6%的乳胶粉混合而成。
其制备方法同实施例1。
实施例6一种混凝土专用防腐阻锈抗渗防裂复合外加剂,由重量百分比为26%的微硅粉、19%的高效减水剂、14%的YS链状硅酸盐纳米材料、7%的三乙醇胺、26%的氯化亚铁和8%的乳胶粉混合而成。
其制备方法同实施例1。
Claims (5)
1.一种混凝土专用防腐阻锈抗渗防裂复合外加剂,其特征在于:该复合外加剂由重量百分比为20%~40%的微硅粉、16%~24%的高效减水剂、10%~20%的YS链状硅酸盐纳米材料、6%~10%的三乙醇胺、20~40%的氯化亚铁和6%~10%的乳胶粉混合而成。
2.如权利要求1所述的一种混凝土专用防腐阻锈抗渗防裂复合外加剂,其特征在于:所述微硅粉为比表面积为16000~28000m2/kg,氯离子含量≤0.25%。
3.如权利要求1所述的一种混凝土专用防腐阻锈抗渗防裂复合外加剂,其特征在于:所述高效减水剂为粉状的萘系减水剂。
4.如权利要求1所述的一种混凝土专用防腐阻锈抗渗防裂复合外加剂,其特征在于:所述三乙醇胺为纯度大于99%的三乙醇胺。
5.如权利要求1所述的一种混凝土专用防腐阻锈抗渗防裂复合外加剂,其特征在于:所述乳胶粉为可再分散乳胶粉。