CN104478341A - 一种低碱混凝土 - Google Patents

一种低碱混凝土 Download PDF

Info

Publication number
CN104478341A
CN104478341A CN201410807301.5A CN201410807301A CN104478341A CN 104478341 A CN104478341 A CN 104478341A CN 201410807301 A CN201410807301 A CN 201410807301A CN 104478341 A CN104478341 A CN 104478341A
Authority
CN
China
Prior art keywords
parts
powder
concrete
low
alkali
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410807301.5A
Other languages
English (en)
Inventor
许雷明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU WANSHENG CONCRETE Co Ltd
Original Assignee
SUZHOU WANSHENG CONCRETE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU WANSHENG CONCRETE Co Ltd filed Critical SUZHOU WANSHENG CONCRETE Co Ltd
Priority to CN201410807301.5A priority Critical patent/CN104478341A/zh
Publication of CN104478341A publication Critical patent/CN104478341A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种低碱混凝土，包括如下重量配比组分：水泥，100份；水，50~60份；砂，150~250份；混凝土改性剂，5~8份；所述混凝土改性剂包括如下重量配比组分：钙粉，5~15份；木质素磺酸钙粉，1~5份；二氧化硅粉，4~8份；分散性乳胶粉，2~6份；煤灰粉，20~40份。本发明低碱混凝土，加入混凝土改性剂，使其结合能力强，抗冻抗侵蚀能力佳，能够广泛使用于北方寒冷地区和盐碱化地区。

Description

一种低碱混凝土
技术领域
本发明涉及建筑材料领域，特别是涉及一种低碱混凝土。
背景技术
混凝土，简称为“砼（tóng）”：是指由胶凝材料将集料胶结成整体的工程复合材料的统称。通常讲的混凝土一词是指用水泥作胶凝材料，砂、石作集料；与水（可含外加剂和掺合料）按一定比例配合，经搅拌而得的水泥混凝土，也称普通混凝土，它广泛应用于土木工程。
在北方寒冷地区和盐碱化地区，因环境恶劣，混凝土建筑物的冻害破坏，会产生裂缝和剥落等，另外盐碱化的侵蚀也均较严重，从而会导致混凝土工程的渗漏、开裂等，降低其耐久性和安全性。而普通混凝土得强度等级较低，抗冻性和抗侵蚀能力差，因而亟需一种抗冻和抗侵蚀能力强的混凝土。
发明内容
本发明主要解决的技术问题是提供一种低碱混凝土，加入混凝土改性剂，使其结合能力强，抗冻抗侵蚀能力佳。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种低碱混凝土，包括如下重量配比组分：
水泥        100份
水                    50~60份
砂                    150~250份
混凝土改性剂          5~8份；
所述混凝土改性剂包括如下重量配比组分：
钙粉                5~15份
木质素磺酸钙粉      1~5份
二氧化硅粉      4~8份
分散性乳胶粉        2~6份
煤灰粉              20~40份。
在本发明一个较佳实施例中，所述混凝土改性剂包括如下重量配比组分：
钙粉                8份
木质素磺酸钙粉      3份
二氧化硅粉      5份
分散性乳胶粉        4份
煤灰粉              25份。
在本发明一个较佳实施例中，所述分散性乳胶粉的成膜温度大于等于0℃。
在本发明一个较佳实施例中，所述二氧化硅粉为纳米二氧化硅粉。
在本发明一个较佳实施例中，所述水泥为低碱硅酸盐水泥。
本发明的有益效果是：本发明低碱混凝土，加入混凝土改性剂，使其结合能力强，抗冻抗侵蚀能力佳，能够广泛使用于北方寒冷地区和盐碱化地区。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1
制作混凝土改性剂：按照下列重量配比称取以下组分：钙粉，8份；木质素磺酸钙粉，3份；二氧化硅粉，5份；分散性乳胶粉，4份；煤灰粉；25份。将上述称取的组分混合均匀，形成混凝土改性剂样本一。
制作混凝土：按照下述重量配比称取以下组分：硅酸盐水泥100份，砂80份、碎石150份、水50份、混凝土改性剂样本一5份。将称取的混凝土改性剂样本一加入称取的1/2水中搅拌5秒形成混合溶液，然后将称取的硅酸盐水泥，砂和混合溶液一起加入混凝土搅拌机中，搅拌15秒，搅拌速度为30转/分钟；最后加入称取的碎石和剩余的水，搅拌20秒，搅拌速度为30转/分钟，形成混凝土混合料。
浇注试件：用上述混凝土混合料浇注成型试件一。
实施例2
制作混凝土改性剂：按照下列重量配比称取以下组分：钙粉，10份；木质素磺酸钙粉，2份；二氧化硅粉，6份；分散性乳胶粉，5份；煤灰粉；35份。将上述称取的组分混合均匀，形成混凝土改性剂样本二。
制作混凝土：按照下述重量配比称取以下组分：低碱硅酸盐水泥100份，砂100份、碎石180份、水60份、混凝土改性剂样本二6份。将称取的混凝土改性剂样本一加入称取的2/3水中搅拌5秒形成混合溶液，然后将称取的硅酸盐水泥，砂和混合溶液一起加入混凝土搅拌机中，搅拌15秒，搅拌速度为35转/分钟；最后加入称取的碎石和剩余的水，搅拌20秒，搅拌速度为35转/分钟，形成混凝土混合料。
浇注试件：用上述混凝土混合料浇注成型试件二。
对上述试件一和试件二进行冻融试验，硫酸盐侵蚀试验，抗冻能力和抗侵蚀能力提高3~5倍。
本发明低碱混凝土，加入混凝土改性剂，使其结合能力强，抗冻抗侵蚀能力佳，能够广泛使用于北方寒冷地区和盐碱化地区。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (5)

1.一种低碱混凝土，其特征在于，包括如下重量配比组分：
水泥        100份
水                    50~60份
砂                    150~250份
混凝土改性剂          5~8份；
所述混凝土改性剂包括如下重量配比组分：
钙粉                5~15份
木质素磺酸钙粉      1~5份
二氧化硅粉      4~8份
分散性乳胶粉        2~6份
煤灰粉              20~40份。
2.根据权利要求1所述的低碱混凝土，其特征在于，所述混凝土改性剂包括如下重量配比组分：
钙粉                8份
木质素磺酸钙粉      3份
二氧化硅粉      5份
分散性乳胶粉        4份
煤灰粉              25份。
3.根据权利要求1所述的低碱混凝土，其特征在于，所述分散性乳胶粉的成膜温度大于等于0℃。
4.根据权利要求1所述的低碱混凝土，其特征在于，所述二氧化硅粉为纳米二氧化硅粉。
5.根据权利要求1所述的低碱混凝土，其特征在于，所述水泥为低碱硅酸盐水泥。
CN201410807301.5A 2014-12-23 2014-12-23 一种低碱混凝土 Pending CN104478341A (zh)