CN103172290B - 一种环保型钢筋阻锈剂 - Google Patents
一种环保型钢筋阻锈剂 Download PDFInfo
- Publication number
- CN103172290B CN103172290B CN201310058577.3A CN201310058577A CN103172290B CN 103172290 B CN103172290 B CN 103172290B CN 201310058577 A CN201310058577 A CN 201310058577A CN 103172290 B CN103172290 B CN 103172290B
- Authority
- CN
- China
- Prior art keywords
- reinforcing bar
- corrosion
- corrosion inhibitor
- concrete
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种环保型钢筋阻锈剂,该钢筋阻锈剂由以下质量百分比的组分组成:苯甲酸钠0.5%~1.5%,硅酸钠0.5%~1.5%,葡萄糖酸0.5%~1.5%,柠檬酸0.5%~1.5%,余量为水。本发明的环保型钢筋阻锈剂,采用阳极型阻锈成分与混合型阻锈成分复配,用量少且阻锈作用强,与钢筋的吸附力强,与混凝土的适应性好,可直接涂覆于钢筋表面,生成致密的保护膜,既提高了阻锈剂的有效利用率,又在不影响混凝土性能的同时起到阻锈作用;可有效减缓和阻止钢筋混凝土中钢筋的腐蚀,具有无亚硝酸盐、无碱、无毒、无污染等特点,可广泛用于水利、铁路、民用建筑等钢筋混凝土结构。
Description
技术领域
本发明属于建筑材料技术领域,具体涉及一种环保型钢筋阻锈剂。
背景技术
作为一种经济实用的结构材料,钢筋混凝土广泛地应用在桥梁、建筑物、堤坝、海底隧道和大型海洋平台等结构中。混凝土中钢筋腐蚀已成为当今世界影响钢筋混凝土结构耐久性的主要因素。新建的钢筋混凝土中,由于高碱度孔隙液的存在,钢筋表面会生成一层钝化膜,对钢筋起到保护作用。但随着时间的推移,由于CO2的侵入造成混凝土的碳化,混凝土孔隙液的碱度降低,钢筋表面的钝化膜变得不稳定,如果周围介质中氯离子向钢筋表面渗透,会造成钢筋的严重点蚀。
钢筋阻锈剂能阻止或减缓钢筋腐蚀,其作用机理在于使钢筋表面形成完整致密的钝化膜,钝化膜受到局部破坏时(如Cl-侵入),阻锈剂可使钝化膜及时、自动修复,从而有效地阻止有害离子对钢筋的侵蚀。即使钢筋表面已经形成腐蚀微电池,阻锈剂也能抑制钢筋腐蚀的电化学过程,使腐蚀速率大幅度降低。
钢筋阻锈剂按作用机理可分为阳极型和阴极型。阳极型钢筋阻锈剂是指能够阻止或减缓阳极过程的物质,典型的化学物质有铬酸盐、亚硝酸盐等,它们能在钢筋表面形成钝化膜,其中亚硝酸盐是应用最早的钢筋阻锈剂,其缺点为:当掺入量不足时会导致局部腐蚀,加速腐蚀的进行;该类阻锈剂有毒,为致癌物质,在一些国家和地区已明令禁止使用;阴极型钢筋阻锈剂是能够阻止或减缓阴极过程的物质,如某些磷酸盐以及一些有机化合物,这类物质虽然没有危险性,但是其单独使用时,其阻锈效果不理想,还不能满足使用的要求;现有技术中的阻锈剂多是在混凝土搅拌时掺入混凝土中,使用量大,无法保证在钢筋表面上的均匀分布且会影响混凝土的性能。
发明内容
本发明的目的是提供一种环保型钢筋阻锈剂,无亚硝酸盐,无毒无污染,用量少且阻锈作用强。
为了实现以上目的,本发明所采用的技术方案是:一种环保型钢筋阻锈剂,由以下质量百分比的组分组成:苯甲酸钠0.5%~1.5%,硅酸钠0.5%~1.5%,葡萄糖酸0.5%~1.5%,柠檬酸0.5%~1.5%,余量为水。
所述钢筋阻锈剂是由以下方法制备的:将各组分按质量百分比称量,混合并搅拌均匀,即得。
本发明的环保型钢筋阻锈剂,使用时可直接涂覆于钢筋表面。
本发明的环保型钢筋阻锈剂以多种有机、无机物为合成基料,以水为分散介质复配而成。其中,苯甲酸钠和硅酸钠作为阳极型阻锈成分,可在阳极区形成一层致密的保护膜,对钢筋的腐蚀起到很大的抑制作用。葡萄糖酸和柠檬酸作为混合型阻锈成分,通过和氯离子竞争吸附,最终通过螯合作用在钢筋表面形成致密的保护膜,削弱氯离子的吸附,对钢筋起到保护作用;混合型阻锈成分,对腐蚀过程的对腐蚀过程的阴极反应、阳极反应均具有显著的抑制作用。本发明的环保型钢筋阻锈剂利用葡糖糖酸、柠檬酸与苯甲酸钠和硅酸钠之间的协同效应,提高阻锈剂的阻锈性能,提升混凝土的耐久性能及混凝土的综合抗腐蚀能力,显著延长建筑物的使用年限,可以带来显著的经济效益和社会效益。
本发明的环保型钢筋阻锈剂,采用阳极型阻锈成分与混合型阻锈成分复配,用量少且阻锈作用强,与钢筋的吸附力强,与混凝土的适应性好,可直接涂覆于钢筋表面,生成致密的保护膜,既提高了阻锈剂的有效利用率,又在不影响混凝土性能的同时起到阻锈作用;可有效减缓和阻止钢筋混凝土中钢筋的腐蚀,具有无亚硝酸盐、无碱、无毒、无污染等特点,可广泛用于水利、铁路、民用建筑等钢筋混凝土结构。
具体实施方式
下面结合具体实施方式对本发明作进一步说明。
实施例1
本实施例的环保型钢筋阻锈剂,由以下质量百分比的组分组成:苯甲酸钠1.5%,硅酸钠0.5%,葡萄糖酸1.0%,柠檬酸1.0%,余量为水。所述钢筋阻锈剂是由以下方法制备的:将各组分按质量百分比称量,混合并搅拌均匀,即得。
实施例2
本实施例的环保型钢筋阻锈剂,由以下质量百分比的组分组成:苯甲酸钠1.0%,硅酸钠1.0%,葡萄糖酸0.5%,柠檬酸1.5%,余量为水。所述钢筋阻锈剂是由以下方法制备的:将各组分按质量百分比称量,混合并搅拌均匀,即得。
实施例3
本实施例的环保型钢筋阻锈剂,由以下质量百分比的组分组成:苯甲酸钠0.5%,硅酸钠1.5%,葡萄糖酸1.5%,柠檬酸0.5%,余量为水。所述钢筋阻锈剂是由以下方法制备的:将各组分按质量百分比称量,混合并搅拌均匀,即得。
实验例
根据JT/T537-2004《钢筋混凝土阻锈剂》及YB/T9231-98《钢筋阻锈剂使用技术规程》的要求,对本发明的实施例1、实施例2、实施例3所述的环保型钢筋阻锈剂进行耐盐水浸渍性能测试,测试结果(见表1)符合规范要求。
表1钢筋HPB235在3.5%NaCl溶液中的锈蚀失重率(%)
阻锈剂 | 腐蚀10天 | 腐蚀20天 | 腐蚀30天 |
无 | 0.08 | 0.11 | 0.18 |
实施例1 | 0.01 | 0.04 | 0.07 |
实施例2 | 0.02 | 0.04 | 0.08 |
实施例3 | 0.02 | 0.05 | 0.08 |
Claims (1)
1.一种环保型钢筋阻锈剂,其特征在于:由以下质量百分比的组分组成:苯甲酸钠0.5%~1.5%,硅酸钠0.5%~1.5%,葡萄糖酸0.5%~1.5%,柠檬酸0.5%~1.5%,余量为水。