CN101835844A - 聚碳酸酯树脂组合物、聚碳酸酯树脂成形品及其制造方法 - Google Patents
聚碳酸酯树脂组合物、聚碳酸酯树脂成形品及其制造方法 Download PDFInfo
- Publication number
- CN101835844A CN101835844A CN200880113048A CN200880113048A CN101835844A CN 101835844 A CN101835844 A CN 101835844A CN 200880113048 A CN200880113048 A CN 200880113048A CN 200880113048 A CN200880113048 A CN 200880113048A CN 101835844 A CN101835844 A CN 101835844A
- Authority
- CN
- China
- Prior art keywords
- resin
- composition
- polycarbonate resin
- glass
- mass parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供聚碳酸酯树脂组合物以及由该组合物成形而成的聚碳酸酯树脂成形品以及由该聚碳酸酯树脂成形而成的聚碳酸酯树脂成形品的制造方法,该聚碳酸酯树脂组合物中,相对于由(A)芳香族聚碳酸酯树脂60~90质量份和(B)与上述芳香族聚碳酸酯树脂的折射率之差在0.002以下的玻璃填料40~10质量份构成的组合物100质量份,还含有(C)具有反应性官能团的聚硅氧烷化合物0.05~2.0质量份、(D)有机碱金属盐化合物和/或有机碱土类金属盐化合物0.03~1.0质量份、(E)光泽粒子0.05~7.0质量份以及(F)着色剂0.0001~3质量份。该聚碳酸酯树脂组合物含有玻璃填料,透明性、强度以及耐热性优异,同时赋予高阻燃性。
Description
技术领域
本发明涉及聚碳酸酯树脂组合物、使用该组合物的聚碳酸酯树脂成形品及其制造方法。更详细地,本发明涉及含有玻璃填料的、金属感外观、强度以及耐热性优良以及赋予高阻燃性的聚碳酸酯树脂组合物、将该树脂组合物成形而形成的聚碳酸酯树脂成形品及其制造方法。
背景技术
聚碳酸酯树脂成形品由于透明性及机械强度优良,所以被广泛用作电·电子领域、机械领域、汽车领域等的工业用透明材料以及透镜或光盘等的光学用材料等,但需要更高的机械强度时,则要添加玻璃填料等进行加强。
该玻璃填料通常使用由被称作E玻璃的玻璃构成的玻璃纤维,聚碳酸酯树脂在钠D线中的折射率(nD,下面仅记作折射率)为1.580~1.590,而E玻璃的折射率稍微小些为1.555左右,为了提高机械强度而添加必要量的玻璃填料的话,由于该折射率的差异,而产生E玻璃强化聚碳酸酯树脂组合物的透明性不能维持、不透明的问题。
也有很多关于具有金属感外观或银河感(星星散落在夜空中闪耀的模样)外观的树脂组合物的专利申请,但它们使用的是透明树脂,对玻璃填料强化树脂没有描述。这是因为,为了得到金属感外观或银河感外观而添加光泽粒子,但不透明的情况下,只看到成形品的表面附近的光泽粒子,得不到金属感外观或银河感外观。
为了解决上述的问题,讨论了聚碳酸酯树脂的改良引起的树脂侧的折射率降低或者玻璃填料组成的改良引起的玻璃填料侧的折射率增大等。
例如提出了以下的方案:(1)一种组合物,其含有:使用羟基芳烷基醇与内酯的反应生成物作为末端终止剂而得到的聚碳酸酯树脂组合物、和与该聚碳酸酯树脂组合物的折射率之差在0.01以下的玻璃填料(参见专利文献1);(2)一种组合物,其含有:聚碳酸酯树脂、与该聚碳酸酯树脂的折射率之差在0.015以下的玻璃填料和聚己内酯(参见专利文献2);(3)一种玻璃组合物,其含有成特定比例的ZrO2、TiO2、BaO及ZnO等,其折射率接近聚碳酸酯树脂(参见专利文献3);(4)具有金属感外观的玻璃填料强化聚碳酸酯树脂组合物(参见专利文献4)等等。
然而,上述(1)的聚碳酸酯树脂组合物,为了提高机械强度而添加必要的玻璃填料量时,这种程度的折射率之差是不够的,并且作为制造聚碳酸酯树脂所用的原料价格偏贵,所以并不实用。
上述(2)的聚碳酸酯树脂组合物,由于含有聚己内酯,所以用与聚碳酸酯树脂的折射率之差在0.015以下的玻璃纤维也能维持透明性,但是存在不能避免耐热性或机械物性下降的问题。
上述(3)的玻璃组合物,如果没有适当地调整ZrO2、TiO2、BaO以及ZnO等的各自的含量的话,玻璃的透明性会消失,即使其折射率与聚碳酸酯树脂相同,含有该玻璃组合物的聚碳酸酯树脂组合物有时也不能得到透明性。并且,玻璃填料自身的比重也变大,所以出于轻量化的目的而使用玻璃填料强化聚碳酸酯树脂组合物的意义减弱。
上述(4)的聚碳酸酯树脂组合物,未提及阻燃性,限于不提供阻燃性也可以使用的领域。
专利文献1:日本专利特开平7-118514号公报
专利文献2:日本专利特开平9-165506号公报
专利文献3:日本专利特开平5-155638号公报
专利文献4:日本专利特开平6-212068号公报
发明内容
发明要解决的课题
在这样的状况下,本发明的目的在于提供一种聚碳酸酯树脂组合物以及由该树脂组合物成形而成的聚碳酸酯树脂成形品以及其制造方法,所述聚碳酸酯树脂组合物含有玻璃填料,其金属感外观、强度以及耐热性优良以及赋予高阻燃性。
解决课题的手段
本发明人为了达成上述目的而反复地进行仔细研究,结果发现以下的阻燃性聚碳酸酯树脂组合物以及由该树脂组合物成形而成的聚碳酸酯树脂成形品可以达成上述目的,所述阻燃性聚碳酸酯树脂组合物含有分别为规定比例的芳香族聚碳酸酯树脂、与该树脂的折射率之差在0.002以下的玻璃填料、具有反应性官能团的聚硅氧烷化合物、有机碱金属盐化合物和/或有机碱土类金属盐化合物、光泽粒子以及着色剂,并且具有规定的阻燃等级。本发明是基于该发现而完成的发明。
也就是,本发明提供如下发明。
(1)一种聚碳酸酯树脂组合物,其特征在于,相对于由(A)芳香族聚碳酸酯树脂60~90质量份和(B)与上述芳香族聚碳酸酯树脂的折射率之差在0.002以下的玻璃填料40~10质量份构成的组合物100质量份,还含有(C)具有反应性官能团的聚硅氧烷化合物0.05~2.0质量份、(D)有机碱金属盐化合物和/或有机碱土类金属盐化合物0.03~1.0质量份、(E)光泽粒子0.05~7.0质量份以及(F)着色剂0.0001~3质量份。
(2)根据上述(1)记载的聚碳酸酯树脂组合物,上述(B)成分的玻璃填料为玻璃纤维和/或磨碎纤维。
(3)根据上述(1)或(2)记载的聚碳酸酯树脂组合物,上述(B)成分的玻璃填料的折射率为1.584~1.586。
(4)一种聚碳酸酯树脂组合物,上述(E)成分的光泽粒子是选自云母、金属粒子、金属硫化物粒子、表面被金属或金属氧化物包覆的粒子、表面被金属或金属氧化物包覆的玻璃片构成的组中的1种或2种以上。
(5)一种聚碳酸酯树脂成形品,由上述(1)~(4)的任意一项记载的聚碳酸酯树脂组合物成形而成。
(6)根据上述(5)记载的聚碳酸酯树脂成形品,其在金属模温度120℃以上注射模塑成形而成。
(7)根据上述(5)或(6)记载的聚碳酸酯树脂成形品,60°镜面光泽度在80以上,且对于可见光的总透光率在40%以上。
(8)根据上述(5)~(7)的任意一项记载的聚碳酸酯树脂成形品,采用依据UL94的阻燃性评价法评价其阻燃性,结果为1.5mmV-0。
(9)一种聚碳酸酯树脂成形品的制造方法,其特征在于,在金属模温度120℃以上的条件下,对上述(1)~(4)的任意一项记载的聚碳酸酯树脂组合物进行注射模塑成形。
发明的效果
根据本发明,可以提供一种聚碳酸酯树脂组合物、由该树脂组合物成形而形成的聚碳酸酯树脂成形品以及其制造方法,所述聚碳酸酯树脂组合物含有玻璃填料,其透明性、强度以及耐热性优异,以及被赋予高阻燃性。
具体实施方式
本发明的聚碳酸酯树脂(下面,简称为PC树脂)组合物,其特征在于,相对于由(A)芳香族PC树脂60~90质量份和(B)与上述芳香族PC树脂的折射率之差在0.002以下的玻璃填料40~10质量份构成的组合物100质量份,还含有(C)具有反应性官能团的聚硅氧烷化合物0.05~2.0质量份、(D)有机碱金属盐化合物和/或有机碱土类金属盐化合物0.03~1.0质量份、(E)光泽粒子0.05~7.0质量份以及(F)着色剂0.0001~3质量份。
可以依据用UL94对本发明的阻燃性PC树脂组合物进行阻燃性评价,为1.5mmV-0。
在本发明的PC树脂组合物中,(A)成分的芳香族聚碳酸酯树脂具体可以使用通过二元酚与聚碳酸酯前躯体的反应而制造的芳香族聚碳酸酯树脂。
对于该(A)成分的PC树脂,并不特别限制其制造方法,可以使用通过以前公知的各种方法而制造得到的PC树脂。例如,可以使用由二元酚和碳酸酯前躯体通过溶液法(界面缩聚法)或熔融法(酯交换法)制造得到的PC树脂,也就是,可以使用在末端终止剂的存在下通过使二元酚和碳酰氯进行反应的界面缩聚法制造得到的PC树脂,或者使用在末端终止剂的存在下利用酯交换法使二元酚和碳酸二苯酯进行反应制造得到的PC树脂。
二元酚可以举出各种各样的,尤其可以举出2,2-双(4-羟基苯基)丙烷[双酚A]、双(4-羟基苯基)甲烷、1,1-双(4-羟基苯基)乙烷、2,2-双(4-羟基-3,5-二甲基苯基)丙烷、4,4’-二羟基二苯基、双(4-羟基苯基)环烷烃、双(4-羟基苯基)氧化物、双(4-羟基苯基)硫、双(4-羟基苯基)砜、双(4-羟基苯基)亚砜以及双(4-羟基苯基)甲酮等。其他也可以举出氢醌、间苯二酚以及儿茶酚等。它们可以单独使用也可以组合2种以上使用,其中理想的是双(羟基苯基)烷烃系,更合适的是双酚A。
而碳酸酯前躯体为羰基卤化物、羰基酯或者卤代甲酸酯(ハロホルメ一ト)等,具体地是碳酰氯、二元酚的二卤代甲酸酯、碳酸二苯酯、碳酸二甲酯以及碳酸二乙酯等。
另外,该PC树脂可以有支链结构,作为支化剂,有1,1,1-三(4-羟基苯基)乙烷、α,α’,α”-三(4-羟基苯基)-1,3,5-三异丙基苯、间苯三酚、偏苯三酸以及靛红双(邻甲酚)等。
在本发明中,作为(A)成分使用的PC树脂的粘均分子量(Mv)通常为10,000~50,000,理想的是13,000~35,000,更理想的是15,000~20,000。
使用乌伯罗德型粘度计,测定20℃下的二氯甲烷溶液的粘度,由此求出特性粘度[η],再由下式算出该粘均分子量(Mv)。
[η]=1.23×10-5Mv0.83
对于该(A)成分的芳香族PC树脂中的分子末端基没有特别的限制,可以是以前公知的末端终止剂即来自一元酚的基团,但理想的是来自具有碳原子数10~35的烷基的一元酚的基团。分子末端是来自具有碳原子数10以上的烷基的酚的基团的话,所得到的阻燃性PC树脂组合物具有良好的流动性,又,是来自具有碳原子数35以下的烷基的苯酚的基团的话,所得到的阻燃性PC树脂组合物的耐热性以及耐冲击性良好。
具有碳原子数10~35的烷基的一元酚可以举例有例如癸基苯酚、十一烷基苯酚、十二烷基苯酚、十三烷基苯酚、十四烷基苯酚、十五烷基苯酚、十六烷基苯酚、十七烷基苯酚、十八烷基苯酚、十九烷基苯酚、二十烷基苯酚、二十二烷基苯酚、二十四烷基苯酚、二十六烷基苯酚、二十八烷基苯酚、三十烷基苯酚、三十二烷基苯酚以及三十五烷基苯酚等。
这些烷基苯酚的烷基可以位于相对于羟基的邻、间、对的任意一个位置,但是理想的是对位。又,烷基可以是直链状、含支链状或者它们的混合物。
作为该取代基只要是其中至少一个为上述的碳原子数10~35的烷基即可,对其他四个没有特别的限制,可以是碳原子数1~9的烷基、碳原子数6~20的芳基、卤原子或者无取代。
利用具有碳原子数10~35的烷基的一元酚进行的末端终止可以是单末端以及两末端的任何一种,又,从所得到的PC树脂组合物的高流动化的观点考虑,末端改性率理想的是相对于全部末端在20%以上,更理想的是在50%以上。
也就是,其他的末端可以是使用羟基末端或下述其他末端终止剂进行终止的末端。
在这里,其他的末端终止剂可以举例有制造PC树脂常用的苯酚、对甲酚、对叔丁基苯酚、对叔辛基苯酚、对枯基苯酚、对壬基苯酚、对叔戊基苯酚、溴苯酚以及三溴苯酚、五溴苯酚等。
从环境问题考虑尤其理想的是不含卤素的化合物。
在本发明的PC树脂组合物中,(A)成分的芳香族PC树脂除了含有上述PC树脂之外,在不损害本发明的目的的范围,可以适当地含有对苯二甲酸等的2官能性羧酸、或其酯形成衍生物等的在酯前躯体的存在下进行聚碳酸酯的聚合而得到的聚酯-聚碳酸酯树脂等的共聚物、或者其他的聚碳酸酯树脂。
在本发明的PC树脂组合物中,作为(B)成分使用的玻璃填料需要其折射率与上述(A)成分芳香族PC树脂的折射率之差在0.002以下。该折射率差超过0.002的话,使用PC树脂组合物得到的成形品的透明性变得不充分。该折射率差理想的是在0.001以下,尤其理想的是玻璃填料的折射率与作为(A)成分的芳香族PC树脂的折射率相同。
作为构成这样的玻璃填料的玻璃可以举例有具有以下所示的组成的玻璃I以及玻璃II。
玻璃I理想的是其组成为:含有二氧化硅(SiO2)50~60质量%、氧化铝(Al2O3)10~15质量%、氧化钙(CaO)15~25质量%、氧化钛(TiO2)2~10质量%、氧化硼(B2O3)2~8质量%、氧化镁(MgO)0~5质量%、氧化锌(ZnO)0~5质量%、氧化钡(BaO)0~5质量%、氧化锆(ZrO2)0~5质量%、氧化锂(Li2O)0~2质量%、氧化钠(Na2O)0~2质量%、氧化钾(K2O)0~2质量%,并且上述氧化锂(Li2O)、上述氧化钠(Na2O)和上述氧化钾(K2O)总计为0~2质量%。
另一方面,玻璃II理想的是其组成为:含有二氧化硅(SiO2)50~60质量%、氧化铝(Al2O3)10~15质量%、氧化钙(CaO)15~25质量%、氧化钛(TiO2)2~5质量%、氧化镁(MgO)0~5质量%、氧化锌(ZnO)0~5质量%、氧化钡(BaO)0~5质量%、氧化锆(ZrO2)2~5质量%、氧化锂(Li2O)0~2质量%、氧化钠(Na2O)0~2质量%、氧化钾(K2O)0~2质量%,实际上不含有氧化硼(B2O3),并且上述氧化锂(Li2O)、上述氧化钠(Na2O)和上述氧化钾(K2O)总计为0~2质量%。
在上述玻璃I及II中,从玻璃填料的强度及制造玻璃时的溶解性的观点来看,SiO2的含量理想的是50~60质量%。从耐水性等的化学耐久性以及制造玻璃时的溶解性的观点来看,Al2O3的含量理想的是10~15质量%。从制造玻璃时的溶解性及抑制结晶化的观点来看,CaO的含量理想的是15~25质量%。
在玻璃I中,可以和E玻璃一样含有2~8质量%的B2O3。此时,从折射率提高的效果以及抑制失透等的观点来看,TiO2的含量理想的是2~10质量%。
此外,在玻璃II中,理想的是和耐酸性或耐碱性优异的ECR玻璃组成一样并不实质性地含有B2O3。此时,从调节折射率的观点来看,TiO2的含量理想的是2~5质量%。此外,从折射率增大、化学耐久性的提高以及制造玻璃时的溶解性的观点来看,ZrO2的含量理想的是2~5质量%。
在玻璃I及II中,MgO为任意成分,从提高拉伸强度等的耐久性及制造玻璃时的溶解性的观点来看,可以含有0~5质量%左右。此外,ZnO及BaO为任意成分,从折射率增大以及抑制失透的观点来看,可以分别含有0~5质量%左右。
在玻璃I中,ZrO2为任意成分,从折射率增大以及制造玻璃时的溶解性的观点来看,可以含有0~5质量%左右。
在玻璃I及II中,碱性成分Li2O、Na2O、K2O为任意成分,可以分别含有0~2质量%左右,且理想的是它们的总含量为0~2质量%。该总含量在2质量%以下时,可以抑制耐水性的降低。
如此,玻璃I及II由于碱性成分少,所以可以抑制(A)成分芳香族PC树脂分解引起的分子量的降低,防止成形品的物性降低。
该玻璃I及II中,除上述的玻璃成分以外,在不会给纺丝性、耐水性等带来不好的影响的范围内,例如也可以含有包含镧(La)、钇(Y)、钆(Gd)、铋(Bi)、锑(Sb)、钽(Ta)、铌(Nb)或钨(W)等的元素的氧化物作为提高玻璃的折射率的成分。此外,也可以含有包含钴(Co)、铜(Cu)或钕(Nd)等的元素的氧化物作为除去玻璃的黄色的成分。
此外,为了抑制着色,在用于玻璃I及II的制造的玻璃原料中,作为杂质,以氧化物为基准,Fe2O3含量相对于整个玻璃不到0.01质量%较为理想。
在本发明的PC树脂组合物中的(B)成分玻璃填料可以这样得到,即从具有上述的玻璃组成的玻璃I及II中适当选择与所使用的(A)成分芳香族聚碳酸酯树脂的折射率之差为0.002以下的填料,制作所期望的形态的玻璃填料。
对该玻璃填料的形态无特别限制,可以使用各种形态的玻璃填料如玻璃纤维、磨碎纤维、玻璃粉末、玻璃片、玻璃珠等。这些可以单独使用一种,也可以组合两种以上来使用,但从平衡最终得到的成形品的机械强度、耐冲击性、透明性及成形性等的观点来看,玻璃纤维及/或磨碎纤维适合。
玻璃纤维可以使用以前公知的玻璃长纤维的纺丝方法来得到。可以使用以下各种方法来使玻璃纤维化,例如,在熔融炉中将玻璃原料连续地玻璃化并导入供料道,在供料道的底部安装衬套进行纺丝的直接熔融(DM)法,或者将熔融的玻璃加工成弹珠、碎玻璃、棒状之后再熔融纺丝的再熔融法等。
玻璃纤维的直径无特别限制,通常适宜使用3~25μm左右的玻璃纤维。直径在3μm以上,则可以抑制漫反射,防止成形品的透明性降低,此外,若在25μm以下,则可以得到具有良好的强度的成形品。
磨碎纤维可以使用以前公知的磨碎纤维的制造方法来得到。如,通过将玻璃纤维的股线用锤击式粉碎机或球磨机粉碎,可以做成磨碎纤维。磨碎纤维的纤维直径及径厚比(aspect ratio)无特别限制,适宜使用纤维直径3~25μm左右、径厚比2~150左右的纤维。
玻璃粉末用以前公知的制造方法得到。如,熔融炉中熔融玻璃原料,将该熔融液投入水中粒状化,或者用冷却辊筒成形为片状,将该片粉碎,做成期望的粒径的粉末。玻璃粉末的粒径无特别限定,适用的是1~100μm左右的粉末。
玻璃片用以前公知的制造方法得到。如,可以在熔融炉中熔融玻璃原料,将该熔融液拉伸为管状,使玻璃的膜厚一定之后,用辊粉碎,由此得到特定的膜厚的玻璃料,将该玻璃料粉碎,做成具有期望的径厚比的片。玻璃片的厚度及径厚比无特别限定,适宜使用厚度0.1~10μm左右、径厚比5~150左右的片。
玻璃珠用以前公知的制造方法得到。如,可以在熔融炉中熔融玻璃原料,将该熔融液用燃烧器进行喷雾,做成期望的粒径的玻璃珠。玻璃珠的粒径无特别限定,5~300μm左右的理想。
为了提高与(A)成分芳香族聚碳酸酯树脂的亲和性、提高粘合性、抑制由于空隙形成引起的成形品的透明性或强度的降低,上述玻璃填料理想的是用偶联剂进行表面处理。
作为偶联剂,可以使用硅烷系偶联剂、甲硼烷系偶联剂、铝酸酯(盐)系偶联剂或钛酸酯(盐)系偶联剂等。尤其,从芳香族PC树脂与玻璃的粘合性良好方面来看,理想的是使用硅烷系偶联剂。
作为该硅烷系偶联剂的具体例子,举例有三乙氧基硅烷、乙烯基三(β-甲氧基乙氧基)硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷、γ-环氧丙氧基丙基三甲氧基硅烷、β-(1,1-环氧环己基)乙基三甲氧基硅烷、β-(3,4-环氧环己基)乙基三甲氧基硅烷、N-β-(氨基乙基)-γ-氨基丙基三甲氧基硅烷、N-β-(氨基乙基)-γ-氨基丙基甲基二甲氧基硅烷、γ-氨基丙基三乙氧基硅烷、N-苯基-γ-氨基丙基三甲氧基硅烷、γ-巯基丙基三甲氧基硅烷、γ-氯丙基三甲氧基硅烷、γ-氨基丙基三甲氧基硅烷、γ-氨基丙基三(2-甲氧基-乙氧基)硅烷、N-甲基-γ-氨基丙基三甲氧基硅烷、N-乙烯基苄基-γ-氨基丙基三乙氧基硅烷、三氨基丙基三甲氧基硅烷、3-脲基丙基三甲氧基硅烷、3-(4,5-二氢咪唑基)丙基三乙氧基硅烷、六甲基二硅氮烷(silazane)、N,O-(双三甲基甲硅烷基)酰胺、N,N-双(三甲基甲硅烷基)脲等。这其中理想的是γ-氨基丙基三甲氧基硅烷、N-β-(氨基乙基)-γ-氨基丙基三甲氧基硅烷、γ-环氧丙氧基丙基三甲氧基硅烷、β-(3,4-环氧环己基)乙基三甲氧基硅烷等的氨基硅烷、环氧硅烷。
要使用这样的偶联剂进行上述玻璃填料的表面处理,可以用通常公知的方法进行,无特别限制。如,可以用将上述偶联剂的有机溶剂溶液或悬浊液作为所谓上胶剂涂布在玻璃填料上的加胶处理法、或者使用亨舍尔搅拌机、高速混合机、莱迪盖(Loedige)混合机、V型混合机等的干式混合法、喷涂法、整体混合法、干式浓缩法等,根据玻璃填料的形状用适当的方法进行,理想的是利用加胶处理法、干式混合法、喷涂法进行。
在本发明的PC树脂组合物中,上述(A)成分芳香族聚碳酸酯树脂和(B)成分玻璃填料的含有比例,基于它们的总量100质量份,必须是(A)成分为60~90质量份,(B)成分为40~10质量份。(B)成分的含量不到10质量份,无法充分发挥刚性的提高效果,又,超过40质量份时,比重变大的同时耐冲击性降低。从刚性、耐冲击性以及比重等的观点来看,上述(A)成分和(B)成分的含有比例理想的是(A)成分为70~90质量份,(B)成分为30~10质量份。
在本发明的PC树脂组合物中,出于进一步提高阻燃性的目的,添加具有反应性官能团的聚硅氧烷化合物作为(C)成分。
作为上述(C)成分即具有反应性官能团的聚硅氧烷化合物(以下有时称含反应性官能团的聚硅氧烷化合物),可以举出如具有通式(1)所表示的基本结构的聚有机硅氧烷聚合物及/或共聚物。
R1 aR2 bSiO(4-a-b)/2.....(1)
在上述通式(1)中,R1表示反应性官能团。作为该反应性官能团,举出的有烷氧基、芳氧基、聚氧基亚烷基、氢基、羟基、羧基、硅烷醇基、氨基、巯基、环氧基以及乙烯基等。这其中,烷氧基、羟基、氢基、环氧基以及乙烯基理想。
R2表示碳原子数1~12的烃基。作为该烃基,可举出直链或含支链状的碳原子数1~12的烷基、碳原子数5~12的环烷基、碳原子数6~12的芳基、碳原子数7~12的芳烷基等,具体地,可以举出甲基、乙基、正丙基、异丙基、各种丁基、各种戊基、各种己基、各种辛基、环戊基、环己基、苯基、甲苯基、二甲苯基、苄基、苯乙基等。
a及b表示满足0<a≤3、0<b≤3、0<a+b≤3的关系的数。R1为多个时,多个R1可以相同也可以不同,R2为多个时,多个R2可以相同也可以不同。
在本发明中,可以并用具有多个相同的反应性官能团的聚有机硅氧烷聚合物及/或共聚物以及具有多个不同的反应性官能团的聚有机硅氧烷聚合物及/或共聚物。
具有以通式(1)表示的基本结构的聚有机硅氧烷聚合物及/或共聚物中,其反应性官能团(R1)数/烃基(R2)数之比为通常0.1~3,理想的是0.3~2左右。又,为了保持添加时的透光性,这些含有反应性官能团的聚硅氧烷化合物的折射率为1.45~1.65,理想的是1.48~1.60。
这些含有反应性官能团的聚硅氧烷化合物为液状物、粉末等,理想的是在熔融混练中分散性良好的物质。如,可以例示室温下的粘度为10~500,000mm2/s左右的液状化合物。
本发明的PC树脂组合物中,含有反应性官能团的聚硅氧烷化合物即使是液状,也具有均一地分散在组合物的同时成形时或成形品的表面上渗出的情况较少的特征。
在本发明的阻燃性PC树脂组合物中,需要相对于由(A)成分的芳香族PC树脂和(B)成分的玻璃填料构成的组合物100质量份,含有0.05~2.0质量份的该(C)成分即含反应性官能团的聚硅氧烷化合物。该(C)成分的含量不到0.05质量份时,燃烧时的熔融滴落(dripping)防止效果不充分,此外超过2.0质量份时混练时发生螺旋桨(screw)的滑动,加料不顺利,生产能力降低。从防止熔融滴落及生产率的观点来看,该(C)成分的理想的含量为0.1~1.0质量份,更理想的含量为0.2~0.8质量份。
在本发明的PC树脂组合物中,出于赋予阻燃性等的目的,添加有机碱金属盐化合物及/或有机碱土类金属盐化合物作为(D)成分。作为有机碱金属盐化合物及/或有机碱土类金属盐化合物,可以举各种各样的,是具有至少一个碳原子的有机酸或有机酸酯的碱金属盐或碱土类金属盐。
这里,作为有机酸或有机酸酯,可以举出有机磺酸、有机羧酸、聚苯乙烯磺酸等。另一方面,作为碱金属,举出有钠、钾、锂及铯等。作为碱土类金属,举出有镁、钙、锶以及钡等。尤其,理想的是使用钠、钾及铯的盐。此外,其有机酸的盐也可以被氟、氯及溴这样的卤原子取代。
作为上述各种有机碱金属盐化合物或有机碱土类金属盐化合物中的有机磺酸,理想的是使用通式(2)所表示的全氟链状烷烃磺酸的碱金属盐化合物或碱土类金属盐化合物。作为这些化合物,如适合的是日本专利特公昭47-40445号公报中记载的物质。
(CcF2c+1SO3)dM.......(2)
(式中,c表示1~10的整数,M表示锂、钠、钾及铯等的碱金属、或者镁、钙、锶以及钡等的碱土类金属,d表示M的原子价。)
在通式(2)中,作为全氟链状烷烃磺酸可以举出如全氟甲磺酸、全氟乙磺酸、全氟丙磺酸、全氟丁磺酸、全氟甲基丁磺酸、全氟己磺酸、全氟庚磺酸及全氟辛磺酸等。尤其,理想地使用的是它们的钾盐。
其他,可以举出烷基磺酸、苯磺酸、烷基苯磺酸、二苯基磺酸、萘磺酸、2,5-二氯苯磺酸、2,4,5-三氯苯磺酸、二苯基磺基-3-磺酸、二苯基磺基-3,3’-二磺酸、萘三磺酸及它们的氟取代物以及聚苯乙烯磺酸等的有机磺酸的碱金属盐或碱土类金属盐等。尤其,作为有机磺酸,全氟链状烷烃磺酸以及二苯基磺酸理想。
接着,作为聚苯乙烯磺酸的碱金属盐化合物及/或碱土类金属盐化合物,可以举出以通式(3)所表示的含有磺酸盐基的芳香族乙烯基系树脂。
[化1]
(式中,X表示磺酸盐基,m表示1~5。Y表示氢原子或碳原子数1~10的烃基。n表示摩尔分数,0<n≤1。)
这里,磺酸盐基是磺酸的碱金属盐及/或碱土类金属盐,作为金属可举出钠、钾、锂、铷、铯、铍、镁、钙、锶以及钡等。
还有,Y是氢原子或碳原子数1~10的烃基,理想的是氢原子或甲基。m是1~5,n是0<n≤1的关系。即,磺酸盐基(X)相对于芳香环,既可以是全部取代的,部分取代的,或者含有无取代的物质。
为了得到本发明PC树脂组合物的阻燃性的效果,要考虑含有磺酸盐基的芳香族乙烯基系树脂的含量等来决定磺酸盐基的取代比例,并无特别限制,一般使用10~100%取代的。
还有,在聚苯乙烯磺酸的碱金属盐及/或碱土类金属盐中,含有磺酸盐基的芳香族乙烯基系树脂并不局限于含有上述通式(3)的磺酸盐基的芳香族乙烯系树脂,也可以是与能够和苯乙烯系单体共聚的其他单体的共聚物。
这里,含有酸盐基的芳香族乙烯基系树脂的制造方法有以下的方法,例如(a)将具有上述的磺酸根等的芳香族乙烯基系单体聚合、或者与可以与它们共聚的其他单体共聚的方法,(b)将芳香族乙烯基系聚合物、或芳香族乙烯基系单体与其他可以共聚的单体的共聚物、又或者将这些混合聚合物磺化,用碱金属及/或碱土类金属中和的方法。
如,作为(b)的方法,通过在聚苯乙烯树脂的1,2-二氯乙烷溶液中加入浓硫酸和无水乙酸的混合溶液并加热,反应数小时,制造聚苯乙烯磺酸化物。然后,通过用与磺酸根相同摩尔量的氢氧化钾或氢氧化钠进行中和,来得到聚苯乙烯磺酸钾盐或钠盐。
作为上述的含有磺酸盐基的芳香族乙烯基系树脂的重均分子量为1,000~300,000,理想的是2,000~200,000左右。还有,重均分子量可以用凝胶渗透色谱(GPC)法测定。
作为有机羧酸,可以举出如全氟蚁酸、全氟甲烷羧酸、全氟乙烷羧酸、全氟丙烷羧酸、全氟丁烷羧酸、全氟甲基丁烷羧酸、全氟己烷羧酸、全氟庚烷羧酸以及全氟辛烷羧酸等,使用这些有机羧酸的碱金属盐或碱土类金属盐。碱金属盐或碱土类金属盐与上述的相同。
在有机碱金属盐以及有机碱土类盐中,磺酸碱金属盐、磺酸碱土类金属盐、聚苯乙烯磺酸碱金属盐以及聚苯乙烯磺酸碱土类金属盐较理想。
有机碱金属盐化合物及/或有机碱土类盐化合物可以使用一种,也可以组合两种以上来使用。
在本发明的PC树脂组合物中,需要相对于由(A)成分的芳香族PC树脂和(B)成分的玻璃填料构成的组合物100质量份,含有0.03~1.0质量份的该(D)成分即有机碱金属盐化合物及/或有机碱土类金属盐化合物。该(D)成分的含量不到0.03质量份时,阻燃性的体现不充分,此外,超过1.0质量份,难以维持透明性。从阻燃性的体现及透明性的维持的观点来看,该(D)成分的理想的含量为0.05~0.4质量份,更理想的含量为0.1~0.3质量份。
本发明的PC树脂组合物中的(E)成分的光泽粒子可以举例有选自云母、金属粒子、金属硫化物粒子、表面被金属或金属氧化物包覆的粒子、表面被金属或金属氧化物包覆的玻璃片。
金属粒子的具体例举例有铝、金、银、铜、镍、钛、不锈钢等金属粉末,表面被金属或金属氧化物包覆的粒子的具体例举例有氧化钛包覆的云母钛、三氯化铋包覆的云母这样的金属氧化覆膜云母系,金属硫化物粒子的具体例举例有硫化镍、硫化钴、硫化锰等金属硫化物粉末,用于表面被金属或金属氧化物包覆的玻璃片的金属举例有金、银、铂、钯、镍、铜、铬、锡、钛、硅等。
(E)成分即光泽粒子的体积平均粒径理想的是10~300μm左右。
上述(E)成分的光泽材料的混合量相对于由(A)、(B)成分构成的组合物100质量份,为0.05~7.0质量份,理想的是0.5~5质量份。不到0.05质量份的话,表面外观难以形成金属感的模样,超过7.0质量份的话,光泽粒子自身浮出表面的量变多,外观被损害,同时阻燃性也降低,因此不理想。
上述(F)成分的着色剂以不具有隐蔽性的为宜,例如举例有甲炔系染料、吡唑啉酮系染料、周因酮系染料、偶氮系染料、奎酞酮系染料、蒽醌系染料等。
上述(F)成分的着色剂的混合量相对于由(A)成分芳香族PC树脂和(B)成分玻璃填料构成的组合物100质量份,为0.0001~3.0质量份,理想的是0.1~3.0质量份。不到0.0001质量份的话,得不到所期望的色调,超过3.0质量份的话,隐蔽性提高,得不到金属感外观。
除上述的(A)成分、(B)成分、(C)成分、(D)成分、(E)成分以及(F)成分以外,在不损害本发明的目的的范围,可以使本发明的PC树脂组合物根据需要适当含有抗氧化剂、紫外线吸收剂、脱模剂、防静电剂、荧光增白剂以及硅烷偶联剂(用干式混合法对玻璃填料进行表面处理的情况)等。
作为抗氧化剂,可以理想地使用酚系抗氧化剂以及磷系抗氧化剂。
作为酚系抗氧化剂,可以举出如三乙二醇-双[3-(3-叔丁基-5-甲基-4-羟基苯基)丙酸酯]、1,6-己二醇-双[3-(3,5-二叔丁基-4-羟基苯基)丙酸酯]、季戊四醇-四[3-(3,5-二叔丁基-4-羟基苯基)丙酸酯]、十八烷基-3-(3,5-二叔丁基-4-羟基苯基)丙酸酯、1,3,5-三甲基-2,4,6-三(3,5-二叔丁基-4-羟基苄基)苯、N,N-六亚甲基双(3,5-二叔丁基-4-羟基-氢化肉桂酰胺)、3,5-二叔丁基-4-羟基-苄基膦酸酯二乙酯、三(3,5-二叔丁基-4-羟基苄基)异氰酸酯、3,9-双[1,1-二甲基-2-[β-(3-叔丁基-4-羟基-5-甲基苯基)丙酰氧基]乙基]-2,4,8,10-四氧杂螺(5,5)十一碳烷等。
作为磷系抗氧化剂,可以举出如磷酸三苯酯、磷酸三壬基苯酯、磷酸三(2,4-二叔丁基苯基)酯、磷酸十三烷基酯、磷酸三辛酯、磷酸三(十八烷基)酯、磷酸二癸基单苯酯、磷酸二辛基单苯酯、磷酸二异丙基单苯酯、磷酸单丁基二苯酯、磷酸单癸基二苯酯、磷酸单辛基二苯酯、双(2,6-二叔丁基-4-甲基苯基)季戊四醇二磷酸酯、磷酸-2,2-亚甲基双(4,6-二叔丁基苯基)辛酯、双(壬基苯基)季戊四醇二磷酸酯、双(2,4-二叔丁基苯基)季戊四醇二磷酸酯、二(十八烷酰基)季戊四醇二磷酸酯等。
这些抗氧化剂可以单独使用一种,也可以组合两种以上使用。其添加量相对于由上述(A)成分芳香族PC树脂和(B)成分玻璃填料构成的组合物100质量份,通常为0.05~1.0质量份左右。
作为紫外线吸收剂,可以使用苯并***系紫外线吸收剂、三嗪系紫外线吸收剂、苯并噁嗪系紫外线吸收剂或者二苯甲酮系紫外线吸收剂等。
作为苯并***系紫外线吸收剂,举例有如2-(2’-羟基-5’-甲基苯基)苯并***、2-(2’-羟基-3’-(3,4,5,6-四氢邻苯二甲酰亚胺甲基)-5’-甲基苯基)苯并***、2-(2’-羟基-3’,5’-二叔丁基苯基)苯并***、2-(2’-羟基-5’-叔辛基苯基)苯并***、2-(3’-叔丁基-5’-甲基-2’-羟基苯基)-5-氯苯并***、2,2’-亚甲基双(4-(1,1,3,3-四甲基丁基)-6-(2H-苯并***-2-基)苯酚、2-(2’-羟基-3’,5’-双(α,α-二甲基苄基)苯基)-2H-苯并***、2-(3’,5’-二叔戊基-2’-羟基苯基)苯并***、5-三氟代甲基-2-(2-羟基-3-(4-甲氧基-α-枯基)-5-叔丁基苯基)2H-苯并***等。
尤其,2-(2’-羟基-5’-叔辛基苯基)苯并***较理想。
作为三嗪系的紫外线吸收剂,羟基苯基三嗪系的如商品名チヌビン400(チバ·スペシヤルテイ·ケミカルズ公司制造)较为理想。
作为苯并噁嗪系的紫外线吸收剂,举例有2-甲基-3,1-苯并噁嗪-4-酮、2-丁基-3,1-苯并噁嗪-4-酮、2-苯基-3,1-苯并噁嗪-4-酮、2-(1-或2-萘基)-3,1-苯并噁嗪-4-酮、2-(4-联苯基)-3,1-苯并噁嗪-4-酮、2,2’-双(3,1-苯并噁嗪-4-酮)、2,2’-对亚苯基双(3,1-苯并噁嗪-4-酮)、2,2’-间亚苯基双(3,1-苯并噁嗪-4-酮)、2,2’-(4,4’-二亚苯基)双(3,1-苯并噁嗪-4-酮)、2,2’-(2,6或1,5-萘)双(3,1-苯并噁嗪-4-酮)、1,3,5-三(3,1-苯并噁嗪-4-酮-2-基)苯等,尤其,2,2’-对亚苯基双(3,1-苯并噁嗪-4-酮)理想。
作为二苯甲酮系紫外线吸收剂,举例有2-羟基-4-甲氧基二苯甲酮、2-羟基-4-正辛氧基二苯甲酮、2-羟基-4-甲氧基-2’-羧基二苯甲酮、2,4-二羟基二苯甲酮、2,2’-二羟基-4-甲氧基二苯甲酮等,尤其,2-羟基-4-正辛氧基二苯甲酮理想。
这些紫外线吸收剂,可以单独使用一种,也可以组合两种以上使用。其添加量相对于由上述(A)成分和(B)成分构成的组合物100质量份,通常为0.05~2.0质量份左右。
作为脱模剂,可以使用一元或多元醇的高级脂肪酸酯。作为所述高级脂肪酸酯,理想的是碳原子数1~20的一元或多元醇与碳原子数10~30的饱和脂肪酸的部分酯或完全酯。作为一元或多元醇与饱和脂肪酸的部分酯或完全酯,可以举例硬脂酸单甘油酯、硬脂酸单脱水山梨糖醇酯(ソルビテ一ト)、二十二烷酸单甘油酯、季戊四醇单硬脂酸酯、季戊四醇四硬脂酸酯、丙二醇单硬脂酸酯、硬脂酸十八烷酰基酯、棕榈酸棕榈酰酯、硬脂酸丁酯、月桂酸甲酯、棕榈酸异丙酯、硬脂酸-2-乙基己酯等,尤其,优选使用硬脂酸单甘油酯、季戊四醇四硬脂酸酯。
这些脱模剂,可以单独使用一种,也可以组合两种以上使用。其添加量相对于由上述(A)成分芳香族PC树脂和(B)成分玻璃填料构成的组合物100质量份,通常为0.1~5.0质量份左右。
作为防静电剂,可以使用例如碳原子数14~30的脂肪酸的单甘油酯、具体地硬脂酸单甘油酯、十六烷酸单甘油酯等或者聚酰胺聚醚嵌段共聚物等。
作为荧光增白剂,可以举例有例如1,2-二苯乙烯系、苯并咪唑系、萘二甲酰亚胺系、若丹明系、香豆素系、噁嗪系化合物等。具体地,可以使用ユビテツク(商品名チバ·スペシヤルテイ·ケミカルズ公司制造)、OB-1(商品名イ一ストマン(株)制造)、TBO(商品名住友精化(株)制造)、ケイコ一ル(商品名日本曹达(株)制造)、カヤライト(商品名日本化药(株)制造)、リユ一コプアEGM(商品名クラリアントジヤパン(株)制造)等的市售品。
另外,硅烷偶联剂可以使用上述例示的化合物。
对本发明的PC树脂组合物的制备方法没有特别的限制,可以采用以前公知的方法。具体地,通过分别混合规定比例的上述的(A)成分芳香族PC树脂、(B)成分玻璃填料、(C)成分含反应性官能团的聚硅氧烷化合物、(D)成分有机碱金属盐化合物及/或有机碱土类金属盐化合物、(E)成分光泽粒子、(F)成分着色剂以及根据需要使用的上述各种任意成分,进行混炼,可以制备。
可以用通常所用的机器例如螺带式掺混机、转鼓等进行予混合,再采用使用亨舍尔混合机、本伯里密炼机、单轴螺旋挤压机、双轴螺旋挤压机、多轴螺旋挤压机以及捏合挤压机等的方法进行混合及混炼。混炼时的加热温度通常在240~300℃的范围适当地选定。
另外,除芳香族PC树脂之外的含有成分可以预先与该芳香族PC树脂的一部分熔融混炼,也就是可以作为母料添加。
对这样制备的本发明的PC树脂组合物根据UL94评价阻燃性,为1.5mmV-0,具有优良的阻燃性。另外,在后面对阻燃性评价进行说明。
接着,对本发明的PC树脂成形品进行说明。
本发明的PC树脂成形品是由上述本发明的阻燃性PC树脂组合物成形而成的成形品。该成形品,此时,PC树脂组合物的厚度理想的是作成0.3~10mm左右,根据该成形品的用途从上述范围中进行适当地选定。
对本发明的PC树脂成形品的制造方法没有特别的限制,可以使用以前公知的各种成形方法,例如注射模塑成形法、注塑压缩成形法、挤压成形法、吹塑成形法、冲压成形法、真空成形法以及发泡成形法等,但理想的是在金属模温度120℃以上、理想的是120℃~140℃进行注射模塑成形。此时,注射模塑成形中的树脂温度通常在240~300℃左右,理想的是在260~280℃左右。
通过在金属模温度120℃以上、理想的是120℃~140℃进行注射模塑成形,可以得到玻璃填料沉淀、可得到良好的外观等的优点。更理想的金属模温度在125℃以上、140℃以下,更理想的是在130~140℃。
理想的是,通过上述熔融混炼方法将成形原料本发明的PC树脂组合物做成颗粒状进行使用。
另外,注射模塑成形方法可以采用可防止外观瑕疵或者可轻量化的气体注入成形。
希望这样得到的本发明的PC树脂成形品的光学特性如下,对于可见光的总透光率在40%以上,理想的是在42%以上,并且60°镜面光泽度通常在80以上,理想的是85以上。另外,关于光学特性的测定方法在后说明。
本发明也提供一种PC树脂成形品的制造方法,其特征在于,在金属模温度120℃以上、理想的是120℃~140℃对上述本发明的PC树脂组合物进行注射模塑成形,制作厚度0.3~10mm的成形品。
本发明的PC树脂组合物含有折射率与芳香族PC树脂的折射率相同或近似的玻璃填料,其透明性、机械强度、耐冲击性以及耐热性等优异,同时赋予高阻燃性,使用该组合物所得到的本发明的PC树脂成形品的透明性、阻燃性、机械强度、耐冲击性以及耐热性等优异。
本发明的PC树脂成形品可以适当地用于下述零件。
(1)电视机、收录机、摄像机、录像机、音频播放器、DVD播放器、空调、手机、显示器、计算机、现金出纳机(register)、计算器、复印机、打印机、传真机等的各种零件、外板以及外壳等的电·电子机器用零件;
(2)PDA、照相机、幻灯片放映机、钟表、计测器、显示器械等的精密机械等的外壳及外罩类的精密机器用零件;
(3)仪表面板、上部装饰罩、散热器护栅、扬声器护栅、轮毂装饰罩、活动车顶、前照灯反射镜、门遮阳板、阻流板、后窗、侧窗等的汽车内装饰材料、外部装饰品以及车体零件等的汽车用零件;
(4)椅子、饭桌、书桌、百叶窗、照明罩、室内装饰器具类等的家具用零件等。
实施例
接着,根据实施例、比较例对本发明进行更详细的说明,但本发明并不是通过这些例子做任何的限定。
另外,使用各例得到的PC树脂组合物颗粒如下所述地形成试验片,评价各个特性。
(1)机械特性
使用100t注射模塑成形机[东芝机械(株)制造,机型名“IS100E”]使颗粒在金属模温度130℃、树脂温度280℃下进行注射模塑成形,制作规定形状的各试验片。
对于各试验片,根据ASTM D638测定其拉伸特性(抗断强度,伸长率),根据ASTM790测定其弯曲特性(强度、弹性模量)。并且,根据ASTM D256测定其Izod冲击强度,根据ASTM D648测定负荷挠曲温度,根据ASTM D792测定比重。
(2)阻燃性
使用45t注射模塑成形机[东芝机械(株)制造,机型名“IS45PV”]使颗粒在金属模温度130℃、树脂温度280℃下进行注射模塑成形,制作127×12.7×1.5mm的试验片。根据UL94(アンダ一ライタ一ズラボラトリ一·サブジエクト94)测定该试验片的阻燃性。
(3)光学特性
使用80t注射模塑成形机[(株)小松制作所制造,机型名“FK80HG”],使颗粒在金属模温度130℃、树脂温度280℃下进行注射模塑成形,制作12.7×127×0.4mm的试验片。对于该试验片,根据JIS K 7105使用分光光度计[株日立制作所制造,机型名“U-4100”]测定380~780nm的可见光区域的总透光率。
60°镜面光泽度使用光泽仪根据JIS K 7105测定。
也就是,使用光泽仪[日本电色(株)制造,机型名“VGS-∑901”],根据JIS K7105,以规定的入射角向试样面入射规定的开口角的光束,用受光器测定镜面反射方向反射的规定的开口角的光束,以标准面的光泽度和来自标准面的镜面反射光束为基础,算出镜面光泽度。60°镜面光泽度是将此时的入射角设定为60±0.2°时的光泽度。
又,PC树脂组合物颗粒的制作所用的各成分种类如下所示。
(1)PC树脂:粘均分子量19000的双酚A聚碳酸酯[出光兴产(株)制造,商品名“タフロンFN1900A”,折射率1.585]
(2)折射率改良GF1:由折射率1.585、φ13μm×3mm的短玻璃丝构成的玻璃纤维[旭フアイバ一グラス(株)制造,玻璃成分:SiO257.5质量%、Al2O312.0质量%、CaO21.0质量%、TiO25.0质量%、MgO2.5质量%、ZnO1.5质量%、Na2O+K2O+Li2O=0.5质量%]
(3)折射率改良GF2:将由折射率1.585、φ13μm×3mm的短玻璃丝构成的玻璃纤维磨碎而得到的磨碎纤维[旭フアイバ一グラス(株)制造,玻璃成分与上述(2)相同)
(4)GF1:由折射率1.555的E玻璃制造的φ13μm×3mm的短玻璃丝构成的玻璃纤维[旭フアイバ一グラス(株)制造,商品名“03MA409C”,玻璃成分:SiO255.4质量%、Al2O314.1质量%、CaO23.2质量%、B2O36.0质量%、MgO0.4质量%、Na2O+K2O+Li2O=0.7质量%、Fe2O30.2质量%、F20.6质量%]
(5)GF2:由折射率1.579的ECR玻璃制造的φ13μm×3mm的短玻璃丝构成的玻璃纤维[旭フアイバ一グラス(株)制造,玻璃成分SiO258.0质量%、Al2O311.4质量%、CaO22.0质量%、TiO22.2质量%、MgO2.7质量%、ZnO2.7质量%、Na2O+K2O+Li2O=0.8质量%、Fe2O30.2质量%]
(6)稳定剂1:抗氧化剂,十八烷基-3-(3,5-二叔丁基-4-羟基苯基)丙酸酯[チバ·スペシヤルテイ·ケミカルズ(株)制造,商品名“Irganox1076”]
(7)稳定剂2:抗氧化剂,三(2,4-二叔丁基苯基)磷酸酯[チバ·スペシヤルテイ·ケミカルズ(株)制造,商品名“Irgafos168”]
(8)脱模剂:季戊四醇四硬脂酸酯[理研ビタミン(株)司制造,商品名“EW440A”]
(9)阻燃剂1:全氟丁烷羧酸钾[大日本インキ化学工业(株)制造,商品名“メガフアツクF114”]
(10)阻燃剂2:重均分子量20000、且磺基化率为100%的聚苯乙烯磺酸钠的浓度30质量%的水溶液[ライオン(株)制造,商品名“レオスタツドFRPSS-N430”]
(11)阻燃助剂1:折射率1.51、具有乙烯基以及甲氧基作为官能团的反应性聚硅氧烷化合物[信越化学工业(株)制造,商品名“KR-219”]
(12)阻燃助剂2:折射率1.49、具有乙烯基以及甲氧基作为官能团的反应性聚硅氧烷化合物[东レ·ダウコ一ニング(株)制造,商品名“DC3037”]
(13)阻燃助剂3:聚四氟乙烯树脂[旭硝子(株)制造,商品名“CD076”]
(14)光泽粒子1:涂布氧化钛的玻璃片[日本板硝子(株)制造,商品名“MC1030RS”]
(15)光泽粒子2:涂布氧化钛以及氧化硅的玻璃片[MERCK公司制造,商品名“Mirava15411”]
(16)光泽粒子3:涂布着色材的铝箔[日本防湿工业(株)制造,商品名“アストロフレ一ク”]
(17)着色剂1:蒽醌系橙色染料[三菱化学(株)制造,商品名“ダイヤレジンオレンジHS”]
(18)着色剂2:蒽醌系绿色染料[住友化学(株)制造,商品名“スミプラストグリ一ンG”]
实施例1~7以及比较例1~9
通过以第1表所示的混合比例混合各成分,使用双轴挤压机[东芝机械(株)制造,机型名“TEM-35B”],在280℃下进行熔融混炼,来制作各PC树脂组合物颗粒。
使用上述各颗粒,如前所述地形成试验片,求出机械特性、阻燃性以及光学特性,其结果表示于第1表中。
[表1]
第1表-1
[表2]
第1表-2
[表3]
第1表-3
从第1表可以看出:
实施例1~7通过在由芳香族PC树脂和与该PC树脂的折射率差在0.002以下的玻璃填料构成的组合物中添加含反应性官能团的聚有机硅氧烷化合物、有机碱金属盐化合物、光泽粒子以及着色剂,可以在维持具有金属感外观的透明性、强度以及耐热性的情况下赋予优异的阻燃性。
比较例1、2,是由芳香族PC树脂、与该PC树脂的折射率差在0.002以下的玻璃填料、光泽粒子和着色剂构成的组合物,或者是在该组合物添加有机金属盐化合物得到的组合物,可以维持良好的金属感外观(总透光率在40%以上,且60°镜面光泽度在80以上)、强度以及耐热性,但不能赋予充分的阻燃性。
比较例3,是在由芳香族PC树脂、与该PC树脂的折射率差在0.002以下的玻璃填料、有机金属盐化合物、光泽粒子以及着色剂构成的树脂组合物中添加聚四氟乙烯树脂作为阻燃助剂得到的组合物,可以维持强度、耐热性以及阻燃性,但不能赋予良好的金属感外观(总透光率在40%以上,且60°镜面光泽度在80以上)。
比较例4,是由芳香族PC树脂、与该PC树脂的折射率差在0.002以下的玻璃填料、有机金属盐化合物、反应性聚硅氧烷、光泽粒子以及着色剂构成的树脂组合物,其光泽粒子的添加量过多,强度以及耐热性可以维持,但不能赋予充分的阻燃性以及良好的金属感外观(总透光率在40%以上,且60°镜面光泽度在80以上)。
比较例5,是由芳香族PC树脂、与该PC树脂的折射率差在0.002以下的玻璃填料、有机金属盐化合物、反应性聚硅氧烷、光泽粒子以及着色剂构成的树脂组合物,其光泽粒子的添加量过多,强度、耐热性以及充分的阻燃性可以维持,但不能赋予良好的金属感外观(总透光率在40%以上,且60°镜面光泽度在80以上)。
比较例6、7,是在由芳香族PC树脂、由E玻璃(折射率1.555)或者ECR玻璃(折射率1.579)构成的玻璃填料、有机金属盐化合物、光泽粒子以及着色剂构成的树脂组合物中添加聚四氟乙烯树脂作为阻燃助剂得到的组合物,可以维持强度、耐热性以及阻燃性,但不能赋予良好的金属感外观(总透光率在40%以上,且60°镜面光泽度在80以上)。
比较例8,是由芳香族PC树脂、与该PC树脂的折射率差在0.002以下的玻璃填料、有机金属盐化合物、反应性聚硅氧烷、光泽粒子以及着色剂构成的树脂组合物,其有机金属盐化合物的添加量过多,白浊了,强度、耐热性以及阻燃性可以维持,但不能赋予良好的金属感外观(总透光率在40%以上,且60°镜面光泽度在80以上)。
比较例9,是由芳香族PC树脂、与该PC树脂的折射率差在0.002以下的玻璃填料、有机金属盐化合物、反应性聚硅氧烷、光泽粒子以及着色剂构成的树脂组合物,其有机金属盐化合物的添加量过少,强度、耐热性以及金属感外观(总透光率在40%以上,且60°镜面光泽度在80以上)可以维持,但不能赋予充分的阻燃性。
产业上的可利用性
本发明的PC树脂组合物含有折射率与芳香族PC树脂的折射率相同或近似的玻璃填料、反应性聚硅氧烷、有机碱金属盐化合物和/或有机碱土类金属盐化合物、光泽粒子以及着色剂,其透明性、机械强度、耐冲击性以及耐热性等优异,同时赋予高阻燃性,使用该组合物所得到的本发明的PC树脂成形品适用于各个领域。
Claims (9)
1.一种聚碳酸酯树脂组合物,其特征在于,相对于由(A)芳香族聚碳酸酯树脂60~90质量份和(B)与上述芳香族聚碳酸酯树脂的折射率之差在0.002以下的玻璃填料40~10质量份构成的组合物100质量份,还含有(C)具有反应性官能团的聚硅氧烷化合物0.05~2.0质量份、(D)有机碱金属盐化合物和/或有机碱土类金属盐化合物0.03~1.0质量份、(E)光泽粒子0.05~7.0质量份以及(F)着色剂0.0001~3质量份。
2.根据权利要求1记载的聚碳酸酯树脂组合物,上述(B)成分的玻璃填料为玻璃纤维和/或磨碎纤维。
3.根据权利要求1或2记载的聚碳酸酯树脂组合物,上述(B)成分的玻璃填料的折射率为1.584~1.586。
4.根据权利要求1~3的任意一项记载的聚碳酸酯树脂组合物,上述(E)成分的光泽粒子是选自云母、金属粒子、金属硫化物粒子、表面被金属或金属氧化物包覆的粒子、表面被金属或金属氧化物包覆的玻璃片构成的组中的1种或2种以上。
5.一种聚碳酸酯树脂成形品,由权利要求1~4的任意一项记载的聚碳酸酯树脂组合物成形而成。
6.根据权利要求5记载的聚碳酸酯树脂成形品,其在金属模温度120℃以上注射模塑成形而成。
7.根据权利要求5或6记载的聚碳酸酯树脂成形品,60°镜面光泽度在80以上,且对于可见光的总透光率在40%以上。
8.根据权利要求5~7的任意一项记载的聚碳酸酯树脂成形品,采用依据UL94的阻燃性评价法评价其阻燃性,结果为1.5mmV-0。
9.一种聚碳酸酯树脂成形品的制造方法,其特征在于,在金属模温度120℃以上的条件下,对权利要求1~4的任意一项记载的聚碳酸酯树脂组合物进行注射模塑成形。