CN101874074B - 聚碳酸酯树脂组合物、聚碳酸酯树脂成形品及其制造方法 - Google Patents
聚碳酸酯树脂组合物、聚碳酸酯树脂成形品及其制造方法 Download PDFInfo
- Publication number
- CN101874074B CN101874074B CN200880118698XA CN200880118698A CN101874074B CN 101874074 B CN101874074 B CN 101874074B CN 200880118698X A CN200880118698X A CN 200880118698XA CN 200880118698 A CN200880118698 A CN 200880118698A CN 101874074 B CN101874074 B CN 101874074B
- Authority
- CN
- China
- Prior art keywords
- resin
- composition
- mass parts
- glass
- polycarbonate resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种聚碳酸酯树脂组合物以及该树脂成形品以及其制造方法,该聚碳酸酯树脂组合物分别含有特定量的玻璃填料和光泽粒子,目测看不出成形物的熔接线左右有亮度差,光学特性以及阻燃性优异。上述聚碳酸酯树脂组合物中,相对于由(A)超过90质量份、99质量份以下的含有10~40质量份的聚碳酸酯-聚有机硅氧烷共聚物的芳香族聚碳酸酯树脂和(B)1质量份以上、不到10质量份的与上述芳香族聚碳酸酯树脂的折射率之差在0.002以下的玻璃填料构成的组合物100质量份,还含有(C)光泽粒子0.01~3.0质量份以及(D)具有反应性官能团的聚硅氧烷化合物0.05~2.0质量份。
Description
技术领域
本发明涉及聚碳酸酯树脂组合物、使用该组合物的聚碳酸酯树脂成形品及其制造方法。更详细地,本发明涉及含有玻璃填料的、银河感外观(整体呈现星星散落在夜空闪耀的外观)、金属感外观等优异、且具有阻燃性的聚碳酸酯树脂组合物、将该树脂组合物成形而形成的聚碳酸酯树脂成形品及其制造方法。
背景技术
聚碳酸酯树脂成形品由于透明性及机械强度优良,所以被广泛用作电·电子领域、机械领域、汽车领域等的工业用透明材料以及透镜或光盘等的光学用材料等,但需要更高的机械强度时,则要添加玻璃填料等进行强化来使用。
该玻璃填料通常使用由被称作E玻璃的玻璃构成的玻璃纤维,聚碳酸酯树脂对于钠D线的折射率(nD,下面仅记作折射率)为1.580~1.590,而E玻璃的折射率稍微小些为1.555左右,为了提高机械强度而添加必要量的玻璃填料的话,由于该折射率的差异,E玻璃强化聚碳酸酯树脂组合物得不到透明性,即使添加光泽粒子,也只看见成形品表面附近的光泽粒子,较难得到金属感外观或银河感外观。
为了解决上述的问题,讨论了聚碳酸酯树脂的改良引起的树脂侧的折射率降低或者玻璃填料组成的改良引起的玻璃填料侧的折射率增大等。
例如提出了以下的方案:(1)一种树脂组合物,其含有:使用羟基芳烷基醇与内酯的反应生成物作为末端终止剂而得到的聚碳酸酯树脂组合物、和与该聚碳酸酯树脂组合物的折射率之差在0.01以下的玻璃填料(参见专利文献1);(2)一种树脂组合物,由聚碳酸酯树脂、与该聚碳酸酯树脂的折射率之差在0.015以下的玻璃填料和聚己内酯构成(参见专利文献2);(3)一种玻璃组合物,其含有成特定比例的ZrO2、TiO2、BaO及ZnO等,其折射率接近聚碳酸酯树脂(参见专利文献3)。
然而,专利文献1中的树脂组合物,为了提高尺寸稳定性或机械强度而添加必要的玻璃填料量时,这种程度的折射率之差是不够的,并且作为制造聚碳酸酯树脂所用的原料价格偏贵,所以并不实用。
专利文献2的聚碳酸酯树脂组合物,为了使折射率下降而添加的聚己内酯的软化温度低,所以用与聚碳酸酯树脂的折射率之差在0.015以下的玻璃纤维也能维持透明性,但是存在不能避免耐热性或机械物性下降的问题。
专利文献3的玻璃组合物,如果没有适当地调整ZrO2、TiO2、BaO以及ZnO等的各自的含量的话,玻璃填料的透明性会消失,即使其折射率与聚碳酸酯树脂接近,含有该玻璃组合物的聚碳酸酯树脂组合物有时也不能得到透明性。并且,玻璃填料自身的比重也变大,削弱了出于轻量化的目的而使用玻璃填料强化聚碳酸酯树脂组合物的意义。并且,对于熔接线以及光泽粒子的定向降低的课题,专利文献1~3没有任何的记载。
此外,含有光泽粒子的聚碳酸酯树脂组合物,形成该树脂组合物时,熔融的树脂组合物之间合流,熔敷部分产生熔接线,结果在熔接线的左右产生亮度差。
如下根据图1说明该现象。
树脂组合物中不含玻璃填料时,如图1的1)记载,熔融的树脂组合物之间在中央部合并而产生熔接线,为了得到金属感外观或银河感外观而添加的光泽粒子在其附近不倒而立着(定向)。由于该现象,光泽粒子引起的光的反射被打乱,结果看见熔接线附近带有黑色。
出现上述现象的话,树脂成形品的商品价值下降,所以提出了形形色色的防止该现象的方法。
例如,提出了(4)含有平均粒径10~300μm、具有厚径比1/8~1的形状的粒子作为光泽粒子的树脂组合物(参见专利文献4);(5)含有四边形的在一个角上设置缺口的金属微粒的树脂组合物(参见专利文献5),通过这些光泽粒子自身的形状来防止熔接线的形成和光泽粒子的定向的降低效果。
然而,专利文献4及5没有记载添加玻璃填料的情况,当然也没有记载通过玻璃填料可以降低光泽粒子的定向。并且,也没有记载阻燃性,不赋予阻燃性的话,可以使用的领域受到限制。
另外,也提出了(6)具有金属感外观的玻璃填料强化聚碳酸酯树脂组合物(参见专利文献6),但没有记载在这种情况下降低熔接线中的光泽粒子的定向这样的课题。并且,也没有记载阻燃性,不赋予阻燃性的话,可以使用的领域受到限制。
进一步地,公开了(7)在成形物中,为了不发生熔接线、熔接两色性等外观不良,在具有光泽的鳞片状微粒的存在下,进行不定形聚合物的沉淀聚合,使不定形聚合物粒子附着在鳞片状微粒上(参见专利文献7)。
还提出了(8)一种聚碳酸酯树脂组合物,其添加聚碳酸酯树脂和添加了各种金属的氧化物的特定玻璃,使该玻璃的折射率提高,将其与该聚碳酸酯树脂的折射率之差设定在0.001以下(参见专利文献8)。
然而,专利文献7中,作为不定形聚合物,实施例、比较例等具体记载的仅仅是AAS树脂,没有记载聚碳酸酯树脂。并且,也没有记载添加玻璃填料的情况,当然也没有记载通过玻璃填料可以降低光泽粒子的定向。并且,也没有记载阻燃性,不赋予阻燃性的话,可以使用的领域受到限制。专利文献8的聚碳酸酯树脂组合物中,没有记载降低熔接线中的光泽粒子的定向这样的课题,并且也未提及阻燃性,不赋予阻燃性的话,可以使用的领域受到限制。
专利文献1:日本专利特开平7-118514号公报
专利文献2:日本专利特开平9-165506号公报
专利文献3:日本专利特开平5-155638号公报
专利文献4:日本专利特公平6-99594号公报
专利文献5:日本专利特开平7-53768号公报
专利文献6:日本专利特开平6-212068号公报
专利文献7:日本专利特开2001-262003号公报
专利文献8:日本专利特开2006-022236号公报
发明内容
在这样的状况下,本发明的目的在于提供一种聚碳酸酯树脂组合物以及由该树脂组合物成形而成的聚碳酸酯树脂成形品以及其制造方法,通过使聚碳酸酯树脂组合物含有限定的特定量的玻璃填料,目测看不出熔接线左右有亮度差,可以得到良好的金属感外观或银河感外观,其强度以及耐热性优异且被赋予高的阻燃性。
本发明人为了达成上述目的而反复地进行仔细研究,结果发现以下的具有优异的阻燃性的聚碳酸酯树脂组合物以及由该树脂组合物成形而成的聚碳酸酯树脂成形品可以达成上述目的,所述聚碳酸酯树脂组合物包含含有聚碳酸酯-聚有机硅氧烷共聚树脂的芳香族聚碳酸酯树脂和特定量的光泽粒子,且将与上述树脂的折射率之差在0.002以下的玻璃填料的混合量设定为相对于上述树脂为特定量,还含有特定比例的具有反应性官能团的聚硅氧烷化合物。本发明是基于该发现而完成的发明。
也就是,本发明提供:
(1)一种聚碳酸酯树脂组合物,其中,相对于由(A)超过90质量份、99质量份以下的含有聚碳酸酯-聚有机硅氧烷共聚物的芳香族聚碳酸酯树脂和(B)1质量份以上、不到10质量份的与上述芳香族聚碳酸酯树脂的折射率之差在0.002以下的玻璃填料构成的组合物100质量份,还含有(C)光泽粒子0.01~3.0质量份以及(D)具有反应性官能团的聚硅氧烷化合物0.05~2.0质量份。
(2)根据上述(1)记载的聚碳酸酯树脂组合物,(A)成分芳香族聚碳酸酯树脂含有聚碳酸酯-聚有机硅氧烷共聚物10~40质量份。
(3)根据上述(1)记载的聚碳酸酯树脂组合物,聚碳酸酯-聚有机硅氧烷共聚物含有0.3~5.0质量%的比例的聚有机硅氧烷部。
(4)根据上述(1)记载的聚碳酸酯树脂组合物,上述(B)成分的玻璃填料为玻璃纤维。
(5)根据上述(1)记载的聚碳酸酯树脂组合物,上述(B)成分的玻璃填料的折射率为1.583~1.587。
(6)根据上述(1)记载的聚碳酸酯树脂组合物,上述(C)成分的光泽粒子是选自云母、金属粒子、金属硫化物粒子、表面被金属或金属氧化物包覆的粒子、表面被金属或金属氧化物包覆的玻璃片构成的组中的1种或2种以上。
(7)根据上述(1)记载的聚碳酸酯树脂组合物,相对于由上述(A)成分和(B)成分构成的组合物100质量份,还含有(E)着色剂0.0001~1质量份。
(8)一种聚碳酸酯树脂成形品,由上述(1)记载的聚碳酸酯树脂组合物成形而成。
(9)根据上述(8)记载的聚碳酸酯树脂成形品,其在金属模温度120℃以上注射模塑成形而成。
(10)根据上述(8)记载的聚碳酸酯树脂成形品,采用依据UL94的阻燃性评价法评价其阻燃性,结果为1.5mmV-0。
(11)根据上述(8)记载的聚碳酸酯树脂成形品,聚碳酸酯树脂组合物颗粒中或者其成形品中的玻璃填料的平均长度为300μm以上。
(12)一种聚碳酸酯树脂成形品的制造方法,其特征在于,在金属模温度120℃以上的条件下,对上述(1)记载的聚碳酸酯树脂组合物进行注射模塑成形。
发明的效果
根据本发明,可以提供透明性、强度以及耐热性优异、同时赋予高的阻燃性的聚碳酸酯树脂组合物以及银河感外观或金属感外观优异的聚碳酸酯树脂成形品。还提供银河感外观或金属感外观优异的聚碳酸酯树脂成形品的制造方法。
附图说明
图1是说明在熔接线的左右,根据玻璃填料的有无而变化的光泽粒子的状态的图。
具体实施方式
本发明的聚碳酸酯树脂(以下有时简称为PC树脂)组合物,其特征在于,相对于由
(A)超过90质量份、99质量份以下的含有聚碳酸酯-聚有机硅氧烷共聚物的芳香族聚碳酸酯树脂和(B)1质量份以上、不到10质量份的与上述芳香族聚碳酸酯树脂的折射率之差在0.002以下的玻璃填料构成的组合物100质量份,还含有(C)光泽粒子0.01~3.0质量份、(D)具有反应性官能团的聚硅氧烷化合物0.05~2.0质量份,根据需要也可以添加(E)0.0001~3质量份的着色剂。
对本发明的PC树脂组合物可以依据UL94进行阻燃性评价,结果为1.5mmV-0。
本发明的PC树脂组合物中,使用含有聚碳酸酯-聚有机硅氧烷共聚物(以下有时简称为PC-POS共聚物)的芳香族聚碳酸酯树脂作为(A)成分芳香族PC树脂。
具体地,优选使用以下的芳香族PC树脂,其含有(a-1)通过二元酚和碳酸酯前驱体的反应制造的芳香族PC树脂(以下,通常有时简称为PC树脂)以及(a-2)PC-POS共聚物,上述PC-POS共聚物的含量为10~40质量份。
(A)成分的芳香族聚碳酸酯树脂中的(a-2)成分即PC-POS共聚物的含量在10质量份以上的话,可以得到具有良好的刚性的PC树脂组合物,在40质量份以下的话,比重不会过大,并且可以得到具有良好的抗冲击性的PC树脂组合物。
对于该(A)成分中的(a-1)成分即普通PC树脂,并不特别限制其制造方法,可以使用通过以前的各种方法而制造得到的PC树脂。例如,可以使用由二元酚和碳酸酯前躯体通过溶液法(界面缩聚法)或熔融法(酯交换法)制造得到的PC树脂,也就是,可以使用在末端终止剂的存在下通过使二元酚和碳酰氯进行反应的界面缩聚法制造得到的PC树脂,或者使用在末端终止剂的存在下利用酯交换法使二元酚和碳酸二苯酯进行反应制造得到的PC树脂。
二元酚可以举出各种各样的,尤其可以举出2,2-双(4-羟基苯基)丙烷[双酚A]、双(4-羟基苯基)甲烷、1,1-双(4-羟基苯基)乙烷、2,2-双(4-羟基-3,5-二甲基苯基)丙烷、4,4’-二羟基联苯(ジヒドロキシジフエニル)、双(4-羟基苯基)环烷烃、双(4-羟基苯基)氧化物、双(4-羟基苯基)硫、双(4-羟基苯基)砜、双(4-羟基苯基)亚砜以及双(4-羟基苯基)甲酮等。其他也可以举出对苯二酚、间苯二酚以及儿茶酚等。它们可以单独使用也可以组合2种以上使用,其中理想的是双(羟基苯基)烷烃系,特别适合的是双酚A。
而碳酸酯前躯体为羰基卤化物、羰基酯或者卤代甲酸酯(ハロホルメ一ト)等,具体地是碳酰氯、二元酚的二卤代甲酸酯、碳酸二苯酯、碳酸二甲酯以及碳酸二乙酯等。
另外,该芳香族PC树脂可以有支链结构,作为支化剂,有1,1,1-三(4-羟基苯基)乙烷、α,α’,α”-三(4-羟基苯基)-1,3,5-三异丙基苯、间苯三酚、偏苯三酸以及靛红双(邻甲酚)等。
在本发明中,作为(a-1)成分使用的普通PC树脂的粘均分子量(Mv)通常为10,000~50,000,理想的是13,000~35,000,更理想的是15,000~20,000。
使用乌伯罗德型粘度计,测定20℃下的二氯甲烷溶液的粘度,由此求出特性粘度[η],再由下式算出该粘均分子量(Mv)。
[η]=1.23×10-5Mv0.83
在该(A)成分芳香族聚碳酸酯树脂中,作为(a-2)成分使用的PC-POS共聚物是由聚碳酸酯部和聚有机硅氧烷部构成的共聚物,可以通过如下方法制造,例如,使预先制造的构成聚碳酸酯部的聚碳酸酯低聚物(以下简称为PC低聚物)、和构成聚有机硅氧烷部(链段)的聚有机硅氧烷溶解在二氯甲烷、氯苯、氯仿等溶剂中,该聚有机硅氧烷的末端具有邻烯丙基苯酚残基、对羟基苯乙烯残基、丁香酚残基等反应性基团,在上述溶液中加入二元酚的苛性碱水溶液,使用叔胺(三乙胺等)或季铵盐(三甲基苯甲基铵氯等)作为催化剂,在末端终止剂的存在下进行界面缩聚反应。
该PC-POS共聚物的制造中所使用的PC低聚物可以通过如下方法容易地制造,例如使上述的二元酚和碳酰氯等的碳酸酯前驱体在二氯甲烷等溶剂中反应,或者使二元酚和碳酸酯化合物例如碳酸二苯酯这样的碳酸酯前驱体反应。
作为碳酸酯化合物,可以举例有碳酸二苯酯等碳酸二芳基酯或碳酸二甲酯、碳酸二乙酯等碳酸二烷基酯。
供PC-POS共聚物的制造用的PC低聚物可以是使用一种上述二元酚得到的低均聚物,也可以是使用两种以上得到的低共聚物。
进一步地,可以是并用多官能性芳香族化合物与上述二元酚得到的热塑性无规支化低聚物。
此时,支化剂(多官能性芳香族化合物)可以使用1,1,1-三(4-羟基苯基)乙烷、α,α′,α″-三(4-羟基苯基)-1,3,5-三异丙基苯、1-[α-甲基-α-(4′-羟基苯基)乙基]-4-[α′,α′-双(4″-羟基苯基)乙基]苯、间苯三酚、偏苯三酸、靛红双(邻甲酚)等。
例如,日本专利特开平3-292359号公报、日本专利特开平4-202465号公报、日本专利特开平8-81620号公报、日本专利特开平8-302178号公报和日本专利特开平10-7897号公报等公开了该PC-POS共聚物。
该PC-POS共聚物优选使用聚碳酸酯部的聚合度为3~100左右、聚有机硅氧烷部的聚合度为2~500左右的。
此外,从平衡赋予得到的PC树脂组合物阻燃性的效果与经济性之间等观点看,该PC-POS共聚物中的聚有机硅氧烷部的含量为0.3~5.0质量%,理想的是0.5~4.0质量%。
进一步地,该PC-POS共聚物的粘均分子量(Mv)通常为5,000~100,000,理想的是10,000~30,000,特别理想的是12,000~30,000。
在这里,可以与上述普通PC树脂一样地求出它们的粘均分子量(Mv)。
该PC-POS共聚物中的聚有机硅氧烷部优选聚二甲基硅氧烷、聚二乙基硅氧烷、聚甲基苯基硅氧烷等构成的链段,特别优选聚二甲基硅氧烷链段。
对于该(A)成分的芳香族PC树脂中的分子末端基没有特别的限制,可以是以前公知的末端终止剂即来自一元酚的基团,但优选来自具有碳原子数10~35的烷基的一元酚的基团。分子末端是来自具有碳原子数10以上的烷基的酚的基团的话,所得到的PC树脂组合物具有良好的流动性,是来自具有碳原子数35以下的烷基的酚的基团的话,所得到的PC树脂组合物的耐热性以及抗冲击性良好。
具有碳原子数10~35的烷基的一元酚可以举例有例如癸基苯酚、十一烷基苯酚、十二烷基苯酚、十三烷基苯酚、十四烷基苯酚、十五烷基苯酚、十六烷基苯酚、十七烷基苯酚、十八烷基苯酚、十九烷基苯酚、二十烷基苯酚、二十二烷基苯酚、二十四烷基苯酚、二十六烷基苯酚、二十八烷基苯酚、三十烷基苯酚、三十二烷基苯酚以及三十五烷基苯酚等。
这些烷基苯酚的烷基可以位于相对于羟基的邻、间、对的任意一个位置,但是理想的是对位。又,烷基可以是直链状、含支链状或者它们的混合物。
作为该取代基只要是其中至少一个为上述的碳原子数10~35的烷基即可,对其他四个没有特别的限制,可以是碳原子数1~9的烷基、碳原子数6~20的芳基、卤原子或者无取代。
利用具有碳原子数10~35的烷基的一元酚进行的末端终止可以是一末端以及两末端的任何一种,又,从所得到的PC树脂组合物的高流动化的观点考虑,末端改性率理想的是相对于全部末端在20%以上,更理想的是在50%以上。也就是,其他的末端可以是羟基末端或使用下述其他末端终止剂进行终止的末端。
在这里,其他的末端终止剂可以举例有制造芳香族PC树脂常用的苯酚、对甲酚、对叔丁基苯酚、对叔辛基苯酚、对枯基苯酚、对壬基苯酚、对叔戊基苯酚、溴苯酚、三溴苯酚以及五溴苯酚等。从环境问题考虑尤其理想的是不含卤素的化合物。
在本发明的PC树脂组合物中,(A)成分的芳香族PC树脂除了含有上述芳香族PC树脂之外,在不损害本发明的目的的范围,可以适当地含有对苯二甲酸等的2官能性羧酸、或其酯形成衍生物等的在酯前躯体的存在下进行聚碳酸酯的聚合而得到的聚酯-聚碳酸酯树脂等的共聚树脂、或者其他的聚碳酸酯树脂。
在本发明的PC树脂组合物中,必须是,作为(B)成分使用的玻璃填料的折射率与上述(A)成分即芳香族PC树脂的折射率之差在0.002以下,以及在PC树脂和玻璃填料的组合物100重量份中,芳香族PC树脂的含量超过90质量份、99质量份以下,玻璃填料的含量在1质量份以上、不到10质量份。
玻璃填料与芳香族PC树脂的折射率差超过0.002的话,使用PC树脂组合物得到的成形品的银河感或者金属感外观变得不充分。该折射率差理想的是在0.001以下,尤其理想的是玻璃填料的折射率与作为(A)成分的芳香族PC树脂的折射率相同。作为这样的玻璃填料,优选使用折射率为1.583~1.587的玻璃填料。
作为构成这样的玻璃填料的玻璃可以举例有具有以下所示的组成的“玻璃I”以及“玻璃II”。
“玻璃I”理想的是其组成为:含有二氧化硅(SiO2)50~60质量%、氧化铝(Al2O3)10~15质量%、氧化钙(CaO)15~25质量%、氧化钛(TiO2)2~10质量%、氧化硼(B2O3)2~8质量%、氧化镁(MgO)0~5质量%、氧化锌(ZnO)0~5质量%、氧化钡(BaO)0~5质量%、氧化锆(ZrO2)0~5质量%、氧化锂(Li2O)0~2质量%、氧化钠(Na2O)0~2质量%、氧化钾(K2O)0~2质量%,并且上述氧化锂(Li2O)、上述氧化钠(Na2O)和上述氧化钾(K2O)总计为0~2质量%。
另一方面,“玻璃II”理想的是其组成为:含有二氧化硅(SiO2)50~60质量%、氧化铝(Al2O3)10~15质量%、氧化钙(CaO)15~25质量%、氧化钛(TiO2)2~5质量%、氧化镁(MgO)0~5质量%、氧化锌(ZnO)0~5质量%、氧化钡(BaO)0~5质量%、氧化锆(ZrO2)2~5质量%、氧化锂(Li2O)0~2质量%、氧化钠(Na2O)0~2质量%、氧化钾(K2O)0~2质量%,实质上不含有氧化硼(B2O3),并且上述氧化锂(Li2O)、上述氧化钠(Na2O)和上述氧化钾(K2O)总计为0~2质量%。
在上述“玻璃I及II”中,从玻璃填料的强度及制造玻璃时的溶解性的观点来看,SiO2的含量理想的是50~60质量%。从耐水性等的化学耐久性以及制造玻璃时的溶解性的观点来看,Al2O3的含量理想的是10~15质量%。从制造玻璃时的溶解性及抑制结晶化的观点来看,CaO的含量理想的是15~25质量%。
在“玻璃I”中,可以和E玻璃一样含有2~8质量%的B2O3。此时,从折射率提高的效果以及抑制失透等的观点来看,TiO2的含量理想的是2~10质量%。
此外,在“玻璃II”中,理想的是和耐酸性或耐碱性优异的ECR玻璃组成一样,实质性上不含有B2O3。此时,从调整折射率的观点来看,TiO2的含量理想的是2~5质量%。此外,从折射率增大、化学耐久性的提高以及制造玻璃时的溶解性的观点来看,ZrO2的含量理想的是2~5质量%。
在“玻璃I及II”中,MgO为任意成分,从提高拉伸强度等耐久性及制造玻璃时的溶解性的观点来看,可以含有0~5质量%左右。此外,ZnO及BaO为任意成分,从折射率增大以及抑制失透的观点来看,可以分别含有0~5质量%左右。
在“玻璃I”中,ZrO2为任意成分,从折射率增大以及制造玻璃时的溶解性的观点来看,可以含有0~5质量%左右。
在“玻璃I及II”中,碱性成分Li2O、Na2O、K2O为任意成分,可以分别含有0~2质量%左右,且理想的是它们的总含量为0~2质量%。其总含量在2质量%以下时,可以抑制耐水性的降低。
如此,“玻璃I及II”由于碱性成分少,所以可以抑制(A)成分芳香族PC树脂分解引起的分子量降低,防止成形品的物性降低。
该“玻璃I及II”中,除上述的玻璃成分以外,在不会给纺丝性、耐水性等带来不好的影响的范围内,例如也可以含有包含镧(La)、钇(Y)、钆(Gd)、铋(Bi)、锑(Sb)、钽(Ta)、铌(Nb)或钨(W)等的元素的氧化物作为提高玻璃的折射率的成分。此外,也可以含有包含钴(Co)、铜(Cu)或钕(Nd)等的元素的氧化物作为除去玻璃的黄色的成分。
此外,为了抑制着色,在用于“玻璃I及II”的制造的玻璃原料中,作为杂质,以氧化物为基准,Fe2O3含量相对于整个玻璃不到0.01质量%较为理想。
在本发明的PC树脂组合物中的(B)成分玻璃填料可以这样得到,即从具有上述的玻璃组成的“玻璃I及II”中适当选择与所使用的(A)成分芳香族PC树脂的折射率之差为0.002以下的填料,制作所期望的形态的玻璃填料。对该玻璃填料的形态没有特别的限制,为了使熔接线的左右的亮度差降低到目测不能确认的程度,PC树脂组合物的颗粒中或该成形品中的玻璃填料的平均纤维长在300μm以上,从该观点出发,适宜的是玻璃纤维。
玻璃纤维可以使用以前公知的玻璃长纤维的纺丝方法来得到。可以使用以下各种方法来使玻璃纤维化,例如,在熔融炉中将玻璃原料连续地玻璃化并导入供料道,在供料道的底部安装衬套进行纺丝的直接熔融(DM)法,或者将熔融的玻璃加工成玻璃球、碎玻璃、棒状之后再熔融纺丝的再熔融法等。
玻璃纤维的直径无特别限制,通常适宜使用3~25μm左右的玻璃纤维。直径在3μm以上,则可以抑制漫反射,防止成形品的银河感或者金属感外观降低,此外,若在25μm以下,则可以得到具有良好的强度的成形品。
如上所述,PC树脂组合物的颗粒中或其成形品中的玻璃纤维的平均长度在300μm以上,理想的是在350μm以上。玻璃纤维长的平均长度不足300μm,有较难得到降低熔接线左右的亮度差的效果的倾向。另外,平均长度可以通过在电炉中,在空气中、600℃的条件下将树脂组合物、颗粒或成形品的一部分焚烧2小时,通过显微镜观察燃烧残渣等进行测定。
为了提高与(A)成分芳香族PC树脂的亲和性、提高粘合性、抑制由于空隙形成引起的成形品的透明性或强度的降低,上述玻璃填料理想的是用偶联剂进行表面处理。作为偶联剂,可以使用硅烷系偶联剂、甲硼烷系偶联剂、铝酸酯系偶联剂或钛酸酯系偶联剂等。尤其,从芳香族PC树脂与玻璃的粘合性良好方面来看,理想的是使用硅烷系偶联剂。
作为该硅烷系偶联剂的具体例子,举例有三乙氧基硅烷、乙烯基三(β-甲氧基乙氧基)硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷、γ-环氧丙氧基丙基三甲氧基硅烷、β-(1,1-环氧环己基)乙基三甲氧基硅烷、β-(3,4-环氧环己基)乙基三甲氧基硅烷、N-β-(氨基乙基)-γ-氨基丙基三甲氧基硅烷、N-β-(氨基乙基)-γ-氨基丙基甲基二甲氧基硅烷、γ-氨基丙基三乙氧基硅烷、N-苯基-γ-氨基丙基三甲氧基硅烷、γ-巯基丙基三甲氧基硅烷、γ-氯丙基三甲氧基硅烷、γ-氨基丙基三甲氧基硅烷、γ-氨基丙基三(2-甲氧基-乙氧基)硅烷、N-甲基-γ-氨基丙基三甲氧基硅烷、N-乙烯基苄基-γ-氨基丙基三乙氧基硅烷、三氨基丙基三甲氧基硅烷、3-脲基丙基三甲氧基硅烷、3-(4,5-二氢咪唑基)丙基三乙氧基硅烷、六甲基二硅氮烷(silazane)、N,O-(双三甲基甲硅烷基)酰胺、N,N-双(三甲基甲硅烷基)脲等。这其中理想的是γ-氨基丙基三甲氧基硅烷、N-β-(氨基乙基)-γ-氨基丙基三甲氧基硅烷、γ-环氧丙氧基丙基三甲氧基硅烷、β-(3,4-环氧环己基)乙基三甲氧基硅烷等氨基硅烷、环氧硅烷。
要使用这样的偶联剂进行上述玻璃填料的表面处理,可以用通常公知的方法进行,无特别限制。如,可以用将上述偶联剂的有机溶剂溶液或悬浊液作为所谓上胶剂涂布在玻璃填料上的加胶处理法、或者使用亨舍尔搅拌机、高速混合机、莱迪盖(Loedige)混合机、V型混合机等的干式混合法、喷涂法、整体混合法、干式浓缩法等,根据玻璃填料的形状用适当的方法进行,理想的是利用加胶处理法、干式混合法、喷涂法进行。
在本发明的PC树脂组合物中,上述(A)成分芳香族PC树脂和(B)成分玻璃填料的含有比例基于它们的总量100重量份,(A)成分为超过90质量份、99质量份以下,(B)成分为1质量份以上、不到10质量份,理想的是(A)成分为92~98质量份,(B)成分为2~8质量份。
(B)成分的含量不到1质量份的话,看不到刚性的提高效果,在10质量份以上的话,可以目测确认熔接线左右有亮度差,无论哪种情况都不理想。
本发明中,通过将玻璃填料的含量设定为特定范围,在成形品的熔接线的左右不会产生亮度差,用图1说明其理由。
图1的2)显示本发明这样的树脂组合物中含有玻璃填料时的光泽粒子的状态。
也就是,本发明中,即使树脂组合物从左右流过来在中央合流而产生熔接线,玻璃填料的流动与树脂组合物的流动方向平行,由于该作用光泽粒子的定向也会被阻止,光泽粒子的流动也与玻璃填料平行,在熔接线的左右也几乎没有光泽粒子立着。因此,在本发明中,即使观察熔接线的左右,光泽粒子引起的光的反射也大致均匀,目测不能看出有亮度差。
本发明的PC树脂组合物中的(C)成分光泽粒子可以举例有云母、金属粒子、金属硫化物粒子、表面被金属或金属氧化物包覆的粒子、表面被金属或金属氧化物包覆的玻璃片。
金属粒子的具体例举例有铝、金、银、铜、镍、钛、不锈钢等金属粉末,表面被金属或金属氧化物包覆的粒子的具体例举例有氧化钛包覆的云母钛、三氯化铋包覆的云母这样的金属氧化覆膜云母系,金属硫化物粒子的具体例举例有硫化镍、硫化钴、硫化锰等金属硫化物粉末,用于表面被金属或金属氧化物包覆的玻璃片的金属举例有金、银、铂、钯、镍、铜、铬、锡、钛、硅等。
(C)成分即光泽粒子的体积平均粒径理想的是10~300μm左右。
上述(C)成分的光泽粒子的混合量相对于由上述(A)成分和(B)成分构成的组合物100质量份,为0.01~3.0质量份,理想的是0.3~1.5质量份。通过将(C)成分设定在0.01质量份以上,形成银河感外观或金属感外观,通过设定在3.0质量份以下,防止光泽粒子自身露出表面的量变多,不损害上述外观,并且防止阻燃性降低。
在本发明的PC树脂组合物中,出于提高阻燃性的目的,进一步添加具有反应性官能团的聚硅氧烷化合物作为(D)成分。
作为具有反应性官能团的聚硅氧烷化合物(以下有时称含反应性官能团的聚硅氧烷化合物),可以举出如具有通式(1)所表示的基本结构的聚有机硅氧烷聚合物及/或共聚物。
R1 aR2 bSiO(4-a-b)/2.....(1)
在上述通式(1)中,R1表示反应性官能团。作为该反应性官能团,举出的有烷氧基、芳氧基、聚氧基亚烷基、氢基、羟基、羧基、硅烷醇基、氨基、巯基、环氧基以及乙烯基等。这其中,烷氧基、羟基、氢基、环氧基以及乙烯基理想。
R2表示碳原子数1~12的烃基。作为该烃基,可举出直链状或含支链状的碳原子数1~12的烷基、碳原子数5~12的环烷基、碳原子数6~12的芳基、碳原子数7~12的芳烷基等,具体地,可以举出甲基、乙基、正丙基、异丙基、各种丁基、各种戊基、各种己基、各种辛基、环戊基、环己基、苯基、甲苯基、二甲苯基、苄基、苯乙基等。
a及b表示满足0<a≤3、0<b≤3、0<a+b≤3的关系的数。R1为多个时,多个R1可以相同也可以不同,R2为多个时,多个R2可以相同也可以不同。
在本发明中,可以并用具有多个相同的反应性官能团的聚有机硅氧烷聚合物及/或共聚树脂以及具有多个不同的反应性官能团的聚有机硅氧烷聚合物及/或共聚物。
具有以通式(1)表示的基本结构的聚有机硅氧烷聚合物及/或共聚物中,其反应性官能团(R1)数/烃基(R2)数之比为通常0.1~3,理想的是0.3~2左右。
这些含有反应性官能团的聚硅氧烷化合物为液状物、粉末等,理想的是在熔融混练中分散性良好的物质。如,可以例示室温下的粘度为10~500,000mm2/s左右的液状化合物。
本发明的PC树脂组合物中,含有反应性官能团的聚硅氧烷化合物即使是液状,也具有均一地分散在组合物、同时成形时或成形品的表面上渗出的情况较少的特征。
在本发明的PC树脂组合物中,相对于由上述(A)成分和(B)成分构成的组合物100质量份,含有0.05~2.0质量份的该(D)成分即含反应性官能团的聚硅氧烷化合物。
上述(D)成分的含量不到0.05质量份时,燃烧时的熔融滴落(dripping)防止效果不充分,此外超过2.0质量份时混练时发生螺旋桨(screw)的滑动,加料不顺利,生产能力降低。从防止熔融滴落及生产率的观点来看,上述(D)成分的理想的含量为0.1~1.0质量份,更理想的含量为0.2~0.8质量份。又,为了保持添加时的透光性,这些含有反应性官能团的聚硅氧烷化合物的折射率为1.45~1.65,理想的是1.48~1.60。
根据需要添加的(E)成分着色剂以不具有隐蔽性的为宜,例如举例有甲炔系染料、吡唑啉酮系染料、周因酮系染料、偶氮系染料、喹酞酮系染料、蒽醌系(アンスラキノン)染料等。
(E)成分的着色剂的混合量相对于由(A)成分芳香族PC树脂和(B)成分玻璃填料构成的组合物100质量份,理想的是为0.0001~1.0质量份,更理想的是0.3~1.0质量份。通过设定在0.0001质量份,可以得到所期望的色调,通过设定在1.0质量份,隐蔽性提高、防止得不到银河感或者金属感外观。
除上述成分以外,在不损害本发明的目的的范围,可以使本发明的PC树脂组合物根据需要适当含有抗氧化剂、紫外线吸收剂、脱模剂、防静电剂、荧光增白剂以及硅烷偶联剂(用干式混合法对玻璃填料进行表面处理的情况)等。
作为抗氧化剂,可以理想地使用酚系抗氧化剂以及磷系抗氧化剂。
作为酚系抗氧剂,可以举出如三乙二醇-双[3-(3-叔丁基-5-甲基-4-羟基苯基)丙酸酯]、1,6-己二醇-双[3-(3,5-二叔丁基-4-羟基苯基)丙酸酯]、季戊四醇四[3-(3,5-二叔丁基-4-羟基苯基)丙酸酯]、十八烷基-3-(3,5-二叔丁基-4-羟基苯基)丙酸酯、1,3,5-三甲基-2,4,6-三(3,5-二叔丁基-4-羟基苯甲基)苯、N,N-六亚甲基双(3,5-二叔丁基-4-羟基-氢化肉桂酰胺)、3,5-二叔丁基-4-羟基-苄基膦酸酯二乙酯、三(3,5-二叔丁基-4-羟基苄基)异氰酸酯、3,9-双[1,1-二甲基-2-[β-(3-叔丁基-4-羟基-5-甲基苯基)丙酰氧基]乙基]-2,4,8,10-四氧杂螺(5,5)十一碳烷等。
作为磷系抗氧化剂,可以举出如磷酸三苯酯、磷酸三壬基苯酯、磷酸三(2,4-二叔丁基苯基)酯、磷酸十三烷基酯、磷酸三辛酯、磷酸三(十八烷基)酯、磷酸二癸基单苯酯、磷酸二辛基单苯酯、磷酸二异丙基单苯酯、磷酸单丁基二苯酯、磷酸单癸基二苯酯、磷酸单辛基二苯酯、双(2,6-二叔丁基-4-甲基苯基)季戊四醇二磷酸酯、磷酸-2,2-亚甲基双(4,6-二叔丁基苯基)辛酯、双(壬基苯基)季戊四醇二磷酸酯、双(2,4-二叔丁基苯基)季戊四醇二磷酸酯、二(十八烷酰基)季戊四醇二磷酸酯等。
这些抗氧化剂可以单独使用一种,也可以组合两种以上使用。其添加量相对于由上述(A)成分芳香族PC树脂和(B)成分玻璃填料构成的组合物100质量份,通常为0.05~1.0质量份左右。
作为紫外线吸收剂,可以使用苯并***系紫外线吸收剂、三嗪系紫外线吸收剂、苯并噁嗪系紫外线吸收剂或者二苯甲酮系紫外线吸收剂等。
作为苯并***系紫外线吸收剂,举例有如2-(2’-羟基-5’-甲基苯基)苯并***、2-(2’-羟基-3’-(3,4,5,6-四氢邻苯二甲酰亚胺甲基)-5’-甲基苯基)苯并***、2-(2’-羟基-3’,5’-二叔丁基苯基)苯并***、2-(2’-羟基-5’-叔辛基苯基)苯并***、2-(3’-叔丁基-5’-甲基-2’-羟基苯基)-5-氯苯并***、2,2’-亚甲基双(4-(1,1,3,3-四甲基丁基)-6-(2H-苯并***-2-基)苯酚、2-(2’-羟基-3’,5’-双(α,α-二甲基苄基)苯基)-2H-苯并***、2-(3’,5’-二叔戊基-2’-羟基苯基)苯并***、5-三氟代甲基-2-(2-羟基-3-(4-甲氧基-α-枯基)-5-叔丁基苯基)2H-苯并***等。尤其,2-(2’-羟基-5’-叔辛基苯基)苯并***较理想。
作为三嗪系的紫外线吸收剂,羟基苯基三嗪系的商品名チヌビン400(チバ·スペシヤルテイ·ケミカルズ公司制造)较为理想。
作为苯并噁嗪系的紫外线吸收剂,举例有2-甲基-3,1-苯并噁嗪-4-酮、2-丁基-3,1-苯并噁嗪-4-酮、2-苯基-3,1-苯并噁嗪-4-酮、2-(1-或2-萘基)-3,1-苯并噁嗪-4-酮、2-(4-联苯基)-3,1-苯并噁嗪-4-酮、2,2’-双(3,1-苯并噁嗪-4-酮)、2,2’-对亚苯基双(3,1-苯并噁嗪-4-酮)、2,2’-间亚苯基双(3,1-苯并噁嗪-4-酮)、2,2’-(4,4’-二亚苯基)双(3,1-苯并噁嗪-4-酮)、2,2’-(2,6或1,5-萘)双(3,1-苯并噁嗪-4-酮)、1,3,5-三(3,1-苯并噁嗪-4-酮-2-基)苯等,尤其,2,2’-对亚苯基双(3,1-苯并噁嗪-4-酮)理想。
作为二苯甲酮系紫外线吸收剂,举例有2-羟基-4-甲氧基二苯甲酮、2-羟基-4-正辛氧基二苯甲酮、2-羟基-4-甲氧基-2’-羧基二苯甲酮、2,4-二羟基二苯甲酮、2,2’-二羟基-4-甲氧基二苯甲酮等,尤其,2-羟基-4-正辛氧基二苯甲酮理想。
这些紫外线吸收剂,可以单独使用一种,也可以组合两种以上使用。其添加量相对于由上述(A)成分和(B)成分构成的组合物100质量份,通常为0.05~2.0质量份左右。
作为脱模剂,可以使用一元或多元醇的高级脂肪酸酯。作为所述高级脂肪酸酯,理想的是碳原子数1~20的一元或多元醇与碳原子数10~30的饱和脂肪酸的部分酯或完全酯。作为一元或多元醇与饱和脂肪酸的部分酯或完全酯,可以举例硬脂酸单甘油酯、硬脂酸单脱水山梨糖醇酯(ソルビテ一ト)、二十二烷酸单甘油酯、季戊四醇单硬脂酸酯、季戊四醇四硬脂酸酯、丙二醇单硬脂酸酯、硬脂酸十八烷酰基酯、棕榈酸棕榈酰酯、硬脂酸丁酯、月桂酸甲酯、棕榈酸异丙酯、硬脂酸-2-乙基己酯等,尤其,优选使用硬脂酸单甘油酯、季戊四醇四硬脂酸酯。
这些脱模剂,可以单独使用一种,也可以组合两种以上使用。其添加量相对于由上述(A)成分和(B)成分构成的组合物100质量份,通常为0.1~5.0质量份左右。
作为防静电剂,可以使用例如碳原子数14~30的脂肪酸的单甘油酯、具体地硬脂酸单甘油酯、十六烷酸单甘油酯等或者聚酰胺聚醚嵌段共聚物等。
作为荧光增白剂,可以举例有例如1,2-二苯乙烯系、苯并咪唑系、萘二甲酰亚胺系、若丹明系、香豆素系、噁嗪系化合物等。具体地,可以使用ユビテツク(商品名 チバ·スペシヤルテイ·ケミカルズ公司制造)、OB-1(商品名 イ一ストマン(株)制造)、TBO(商品名 住友精化(株)制造)、ケイコ一ル(商品名 日本曹达(株)制造)、カヤライト(商品名 日本化药(株)制造)、リユ一コプアEGM(商品名 クラリアントジヤパン(株)制造)等的市售品。
另外,硅烷偶联剂可以使用上述例示的化合物。
对本发明的PC树脂组合物的制备方法没有特别的限制,可以采用以前公知的方法。具体地,可以通过分别混合规定比例的上述的(A)成分芳香族PC树脂即(a-1)普通PC树脂和(a-2)PC-POS共聚物、(B)成分玻璃填料、(C)成分光泽粒子、(D)成分含反应性官能团的聚硅氧烷化合物、根据需要添加的(E)成分着色剂以及其他上述各种任意成分,进行混炼来制备。
可以用通常所用的机器例如螺带式掺混机、转鼓等进行予混合,再采用使用亨舍尔混合机、本伯里密炼机、单轴螺旋挤压机、双轴螺旋挤压机、多轴螺旋挤压机以及捏合挤压机等的方法进行混合及混炼。混炼时的加热温度通常在240~300℃的范围适当地选定。
另外,除芳香族PC树脂之外的含有成分可以预先与该芳香族PC树脂的一部分熔融混炼,也就是可以作为母料添加。
对这样制备的本发明的PC树脂组合物根据UL94评价阻燃性,结果为1.5mmV-0,具有优良的阻燃性。另外,在后面对阻燃性评价试验进行说明。
接着,对本发明的PC树脂成形品进行说明。
本发明的PC树脂成形品是采用注射模塑成形法等方法将上述本发明的PC树脂组合物成形而成的成形品。此时,PC成形品的厚度理想的是作成0.3~10mm左右,根据该成形品的用途从上述范围中进行适当的选定。
对本发明的PC树脂成形品的制造方法没有特别的限制,可以使用以前公知的各种成形方法,例如注射模塑成形法、注塑压缩成形法、挤压成形法、吹塑成形法、冲压成形法、真空成形法以及发泡成形法等,但理想的是在金属模温度120℃以上进行注射模塑成形。此时,注射模塑成形中的树脂温度通常在240~300℃左右,理想的是在260~280℃左右。
通过在金属模温度120℃以上进行注射模塑成形,可以得到玻璃填料沉淀、可得到良好的外观等的优点。更理想的金属模温度在125℃以上、140℃以下,更理想的是在130~140℃。
理想的是,通过上述熔融混炼方法将成形原料即本发明的PC树脂组合物做成颗粒状进行使用。另外,注射模塑成形方法可以采用可防止外观瑕疵或者可轻量化的气体注入成形。
这样得到的本发明的PC树脂成形品,即使形成熔接线,目测也看不出来其左右的亮度差,在成形品的整个表面得到良好的金属感外观或银河感外观。
另外,关于熔接线的左右的亮度差的测定方法在后说明。
本发明也提供一种PC树脂成形品的制造方法,其特征在于,在金属模温度120℃以上、优选在120℃~140℃对上述本发明的PC树脂组合物进行注射模塑成形,制作优选厚度0.3~10mm的成形品。
本发明的PC树脂组合物含有折射率与芳香族PC树脂的折射率相同或近似的玻璃填料以及光泽粒子,其透明性、机械强度、耐冲击性以及耐热性等优异,同时因为含有具有反应性官能团的聚硅氧烷化合物,可以得到高阻燃性。并且,使用该组合物得到的本发明的PC树脂成形品的金属感外观或银河感外观优异,并且其透明性、阻燃性、机械强度、耐冲击性和耐热性等优异。
本发明的PC树脂成形品可以适当地用于下述零件。
(1)电视机、收录机、摄像机、录像机、音频播放器、DVD播放器、空调、手机、显示器、计算机、现金出纳机(register)、计算器、复印机、打印机、传真机等的各种零件、外板以及外壳材等的电·电子机器用零件;
(2)PDA、照相机、幻灯片放映机、钟表、计测器、显示器械等的精密机械等的外壳及外罩类的精密机器用零件;
(3)仪表面板、上部装饰罩、散热器护栅、扬声器护栅、轮毂装饰罩、活动车顶、前照灯反射镜、门遮阳板、阻流板、后窗、侧窗等的汽车内装饰材料、外部装饰品以及车体零件等的汽车用零件;
(4)椅子、饭桌、书桌、百叶窗、照明罩、室内装饰器具类等的家具用零件等。
实施例
接着,根据实施例和比较例对本发明进行更详细的说明,但本发明并不是通过这些例子做任何的限定。
另外,使用下述实施例和比较例得到的PC树脂组合物颗粒如下所述地形成试验片,评价各个特性。
(1)玻璃纤维长
称取PC树脂组合物的颗粒数g,放到SiO2/Al2O3坩埚,在ヤマト科学公司制造的马氟炉(muffle furmace)FP-21在空气中、600℃下煅烧2小时。然后,用玻璃片夹住燃烧残渣的一部分,用日本光学工业公司制造的万能投影仪V-24观察纤维长,每一次的测定都测定200根的纤维的长度,求出平均值。对于每个样品,进行3次这样的测定,将其平均值作为平均纤维长。
(2)机械特性
使用100t注射模塑成形机[东芝机械(株)制造,机型名“IS100E”]使PC树脂组合物的颗粒在金属模温度130℃、树脂温度280℃下进行注射模塑成形,制作规定形状的各试验片。
依据ASTM D648测定各试验片的负荷挠曲温度,将其作为耐热性的指标。比重依据ASTMD792进行测定。
(3)光学特性(光泽粒子定向的有无)
使用100t注射模塑成形机[住友重机械工业(株)制造,机型名“SG100M-HP”],用具有2点浇口的金属模,在金属模温度130℃下,将PC树脂组合物的颗粒注射模塑成形,制作具有熔接线的80×80×2mm的试验片。使日光倾斜45°照射到这样得到的试验片上,测定是否可以目测确认熔接线左右的光泽粒子有亮度差。
(4)外观
使用上述光学特性测定用的试验片,目测观察其表面外观,用是否具有作为本发明目的的银河感(裂纹感)来区别。
(5)阻燃性
使用45t注射模塑成形机[东芝机械(株)制造,机型名“IS45PV”]使PC树脂组合物的颗粒在金属模温度130℃、树脂温度280℃下进行注射模塑成形,制作127×12.7×1.5mm的试验片。根据UL94(アンダ一ライタ一ズラボラトリ一·サブジエクト94)测定该试验片的阻燃性。
PC树脂组合物颗粒的制作所用的各成分种类如下所示。
(1)PC1(成分(A)):粘均分子量19000的双酚A聚碳酸酯[出光兴产(株)制造,商品名“タフロンFN1900A”,折射率1.585];
(2)PC2(成分(A)〕:粘均分子量15000的PC-POS共聚树脂、POS部含量为4质量%、POS部链长(n)为30、折射率为1.584;
(3)折射率改良GF1〔成分(B)〕:由φ13μm×3mm的短玻璃丝构成的玻璃纤维[旭フアイバ一グラス(株)制造,玻璃成分(质量%):SiO2(52.6)、Al2O3(13.3)、CaO(21.8)、TiO2(5.9)、B2O3(5.9)、MgO(0.5),折射率1.585、比重2.70];
(4)折射率改良GF2〔成分(B)〕:由φ13μm×3mm的短玻璃丝构成的玻璃纤维[旭フアイバ一ガラス(株)制,玻璃成分(质量%):SiO2(57.5)、Al2O3(12.0)、CaO(21.0)、TiO2(5.0)、MgO(2.5)、ZnO(1.5)、Na2O+K2O+Li2O(0.5)、折射率1.584,比重2.69];
(5)GF1〔与成分(B)比较用〕:E玻璃制的φ13μm×3mm的短玻璃丝构成的玻璃纤维[旭フアイバ一ガラス(株)制,商品名「03MA409C」、玻璃成分(质量%):SiO2(55.4)、Al2O3(14.1)、CaO(23.2)、B2O3(6.0)、MgO(0.4)、Na2O+K2O+Li2O(0.7)、Fe2O3(0.2)、F2(0.6)、折射率1.555、比重2.54];
(6)GF2〔与成分(B)比较用〕:ECR玻璃制的φ13μm×3mm的短玻璃丝构成的玻璃纤维[旭フアイバ一ガラス(株)制,玻璃成分(质量%):SiO2(58.0)、Al2O3(11.4)、CaO(22.0)、TiO2(2.2)、MgO(2.7)、ZnO(2.7)、Na2O+K2O+Li2O(0.8)、Fe2O3(0.2)、折射率1.579、比重2.72];
(7)光泽粒子1〔成分(C)〕:涂布氧化钛的玻璃片[日本板硝子(株)制造,商品名“MC1030RS”];
(8)光泽粒子2〔成分(C)〕:涂布氧化钛以及氧化硅的玻璃片[MERCK公司制造,商品名“Mirava1 5411”];
(9)光泽粒子3〔成分(C)〕:涂布着色材的铝箔[日本防湿工业(株)制造,商品名“アストロフレ一ク”];
(10)阻燃助剂1〔成分(D)〕:折射率1.51、具有乙烯基以及甲氧基作为官能团的反应性聚硅氧烷化合物[信越化学工业(株)制造,商品名“KR-219”];
(11)阻燃助剂2〔成分(D)〕:折射率1.49、含有乙烯基以及甲氧基作为官能团的反应性聚硅氧烷化合物[东レ·ダウコ一ニング(株)制造,商品名“DC3037”];
(12)阻燃助剂3〔与成分(D)比较用〕:聚四氟乙烯树脂[旭フロロポリマ一(株)制造,商品名“CD076”];
(13)着色剂1〔成分(E)〕:蒽醌系橙色染料[三菱化学(株)制造,商品名“ダイヤレジンオレンジHS”];
(14)着色剂2〔成分(E)〕:蒽醌系绿色染料[住友化学(株)制造,商品名“スミプラストグリ一ンG”];
(15)脱模剂1:季戊四醇四硬脂酸酯[理研ビタミン(株)制造,商品名“EW440A”];
(16)稳定化剂1:抗氧化剂[十八烷基-3-(3,5-二叔丁基-4-羟基苯基)丙酸酯、チバ·スペシヤルテイ·ケミカルズ(株)制造,商品名“Irganox1076”];
(17)稳定化剂2:抗氧化剂,[三(2,4-二叔丁基苯基)磷酸酯、チバ·スペシヤルテイ·ケミカルズ(株)制造,商品名“Irgafos168”]。
实施例1~7以及比较例1~7
通过以表1所示的混合比例混合各成分,使用双轴挤压机[东芝机械(株)制造,机型名“TEM-35B”],在280℃下进行熔融混炼,来制作各PC树脂组合物颗粒。使用上述各颗粒,如前所述地形成试验片,求出物理特性、光学特性以及阻燃性。其结果表示于第1表中。
[表1]
从表1可以看出:
从各实施例可以明白,混合特定量的芳香族PC树脂和PC-POS共聚树脂、与该PC树脂的折射率之差在0.002以下的特定量的玻璃填料、特定量的光泽粒子及具有反应性官能团的聚硅氧烷化合物,得到PC树脂组合物,通过将该PC树脂组合物成形,目测看不出成形品的熔接线左右有亮度差,可以得到良好的银河感外观。还可以在维持强度以及耐热性的情况下,赋予优异的阻燃性。
从表1还可以看出:
从比较例1可以明白,不添加玻璃填料时,目测确认熔接线左右有亮度差。
从比较例2、3可以明白,由芳香族PC树脂、PC-POS共聚树脂、与该PC树脂的折射率之差在0.002以下的玻璃填料、光泽粒子、具有反应性官能团的聚硅氧烷构成树脂组合物,由该树脂组合物得到成形体,玻璃填料的混合量超过本发明规定的范围的话,比较例2中,比重变大,且目测确认熔接线左右有亮度差,比较例3,比重没有变大,但目测确认熔接线左右有亮度差。
从比较例4可以明白,由添加有阻燃助剂3的树脂组合物得到的成形物,其他的特性没有问题,但外观变成裂纹感,不能得到作为本发明的目的的银河感外观、金属感外观等优异的聚碳酸酯树脂成形品。
从比较例5可以明白,即使是由芳香族PC树脂、PC-POS共聚树脂、与该PC树脂的折射率之差在0.002以下的玻璃填料、光泽粒子、具有反应性官能团的聚硅氧烷构成的树脂组合物得到的成形体,光泽粒子的混合量超过本发明所规定的范围的话,阻燃性不好,目测确认熔接线左右有亮度差。
从比较例6、7可以明白,由芳香族PC树脂、PC-POS共聚树脂、与该PC树脂的折射率之差超过0.002的由E玻璃(折射率1.555)或者ECR玻璃(折射率1.579)构成的玻璃填料、光泽粒子、具有反应性官能团的聚硅氧烷的树脂组合物得到的成形体,其阻燃性可以维持,但表面模样为裂纹感,不能赋予银河感外观。
产业上的可利用性
本发明的PC树脂组合物是具有折射率与芳香族PC树脂的折射率相同或者相近的玻璃填料、光泽粒子、反应性聚硅氧烷化合物的组合物,通过将进一步根据需要添加了着色剂的PC树脂组合物为原料进行成形,成形物即使生成熔接线,目测也看不出熔接线的左右有亮度差,赋予高的阻燃性,使用这些组合物得到的本发明的PC树脂成形品可适宜地用于各种领域。
Claims (10)
1.一种聚碳酸酯树脂组合物,其中,相对于由(A)超过90质量份、99质量份以下的含有10~40质量份聚碳酸酯-聚有机硅氧烷共聚物的芳香族聚碳酸酯树脂和(B)1质量份以上、不到10质量份的与上述芳香族聚碳酸酯树脂的折射率之差在0.002以下的玻璃填料构成的组合物100质量份,还含有(C)光泽粒子0.01~3.0质量份以及(D)具有反应性官能团的聚硅氧烷化合物0.05~2.0质量份;所述(B)的玻璃填料是,直径为3~25μm的玻璃纤维,且在聚碳酸酯树脂组合物的颗粒中或其成形品中的平均长度为300μm以上的玻璃填料。
2.根据权利要求1记载的聚碳酸酯树脂组合物,聚碳酸酯-聚有机硅氧烷共聚物含有0.3~5.0质量%的比例的聚有机硅氧烷部。
3.根据权利要求1记载的聚碳酸酯树脂组合物,上述(B)成分的玻璃填料的折射率为1.583~1.587。
4.根据权利要求1记载的聚碳酸酯树脂组合物,上述(C)成分的光泽粒子是选自云母、金属粒子、金属硫化物粒子、表面被金属或金属氧化物包覆的粒子、表面被金属或金属氧化物包覆的玻璃片构成的组中的1种或2种以上。
5.根据权利要求1记载的聚碳酸酯树脂组合物,相对于由上述(A)成分和(B)成分构成的组合物100质量份,还含有(E)着色剂0.0001~1质量份。
6.一种聚碳酸酯树脂成形品,由权利要求1记载的聚碳酸酯树脂组合物成形而成。
7.根据权利要求6记载的聚碳酸酯树脂成形品,其在金属模温度120℃以上注射模塑成形而成。
8.根据权利要求6记载的聚碳酸酯树脂成形品,采用依据UL94的阻燃性评价法评价其阻燃性,结果为1.5mmV-0。
9.根据权利要求6记载的聚碳酸酯树脂成形品,聚碳酸酯树脂组合物颗粒中或者其成形品中的玻璃填料的平均长度为300μm以上。
10.一种聚碳酸酯树脂成形品的制造方法,其特征在于,在金属模温度120℃以上的条件下,对权利要求1记载的聚碳酸酯树脂组合物进行注射模塑成形。