CN101801851B - 非晶性复合碱金属钛酸盐组合物和摩擦材料 - Google Patents
非晶性复合碱金属钛酸盐组合物和摩擦材料 Download PDFInfo
- Publication number
- CN101801851B CN101801851B CN200880107761.XA CN200880107761A CN101801851B CN 101801851 B CN101801851 B CN 101801851B CN 200880107761 A CN200880107761 A CN 200880107761A CN 101801851 B CN101801851 B CN 101801851B
- Authority
- CN
- China
- Prior art keywords
- alkali metal
- weight
- metal titanate
- sio
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
非晶性复合碱金属钛酸盐组合物,其包含60重量%以上通式M2O·nTiO2(式中,M是碱金属元素中的1种或2种以上,n是1~4的数)所表示的碱金属钛酸盐、10重量%以上的SiO2,且M2O/SiO2≤2.5,化学上稳定,耐吸湿性优异,适合作为摩擦材料的基材材料。根据需要,可以包含选自B、Mg、Al、P、Ca和Zn中的至少1种元素的氧化物,和/或选自V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、Nb和Ba中的至少1种元素的氧化物。
Description
技术领域
本发明涉及非晶性复合碱金属钛酸盐组合物,涉及化学稳定性和热稳定性优异的非晶性复合碱金属钛酸盐组合物以及混合了该组合物的摩擦材料。
背景技术
通式M2O·nTiO2(式中,M是碱金属元素中的1种或2种以上)所表示的碱金属钛酸盐通常作为纤维状化合物获得,例如有M为K且n=2的二钛酸钾、M为Na且n=3的三钛酸钠、M为K且n=4的四钛酸钾。然而,由于这些碱金属钛酸盐的碱成分多、结晶结构为层状,因此化学上不稳定,会出现摩擦材料成型时存在于层间的碱金属离子溶出,使构成摩擦材料基材的树脂劣化的问题。
另一方面,当TiO2增加时,碱金属钛酸盐的结晶结构变成隧道状且化学稳定性升高。作为该碱金属钛酸盐,例如有M为K且n=6的六钛酸钾、M为Na且n=6的六钛酸钠、M为K且n=8的八钛酸钾,其具有化学稳定性而且耐热性和绝热性也优异,因而广泛用作摩擦材料的基材。
六钛酸钾通过作为代表性制造方法的熔融法制造,首先,将熔融的原料冷却固化以制作二钛酸钾的纤维块,然后通过水合反应使纤维块膨润分离。接着,对分离的纤维进行酸处理,使钾浸出直到组成变为六钛酸钾,然后进行固液分离、进行热处理,转化为隧道结构的六钛酸钾(日本专利第2946107号)。
发明内容
发明所要解决的课题
根据前述熔融法制造的六钛酸钾需要从二钛酸钾向六钛酸钾转化的工序,制造工序复杂。此外,由于有钾的浸出,因而理论收率低。
而且,通过该熔融法得到的形状是板状纤维,难以根据所需性能制作板状以外的不同形状。
本发明的目的是提供非晶性复合碱金属钛酸盐组合物,其不需要迄今为止的制造法所需的组成转化或结构转化工序、化学上稳定、耐吸湿性优异、且热稳定,适合作为摩擦材料的基材。
发明者们进行了深入研究,结果发现:单独的非晶性1~4钛酸钾与结晶结构的钛酸钾同样,化学稳定性差、耐吸湿性不充分,但是通过合并预定量的SiO2,化学上稳定,可以具备耐吸湿性。
解决课题的手段
本发明中涉及的第1非晶性复合碱金属钛酸盐组合物具有如下组成:通式M2O·nTiO2(式中,M是碱金属元素中的1种或2种以上,n是1~4的数)所表示的碱金属钛酸盐:60~90重量%,SiO2:10~40重量%,且M2O/SiO2≤2.5。
本发明中涉及的第2非晶性复合碱金属钛酸盐组合物具有如下组成:通式M2O·nTiO2(式中,M是碱金属元素中的1种或2种以上,n是1~4的数)所表示的碱金属钛酸盐:60重量%以上至低于90重量%,SiO2:10重量%以上至低于40重量%,以及选自B、Mg、Al、P、Ca和Zn中的至少1种元素的氧化物:大于0重量%至10重量%以下,且M2O/SiO2≤2.5。
本发明中涉及的第3非晶性复合碱金属钛酸盐组合物具有如下组成:通式M2O·nTiO2(式中,M是碱金属元素中的1种或2种以上,n是1~4的数)所表示的碱金属钛酸盐:60重量%以上至低于90 重量%,SiO2:10重量%以上至低于40重量%,以及选自V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、Nb和Ba中的至少1种元素的氧化物:大于0重量%至10重量%以下,且M2O/SiO2≤2.5。
本发明中涉及的第4非晶性复合碱金属钛酸盐组合物具有如下组成:通式M2O·nTiO2(式中,M是碱金属元素的1种或2种以上,n是1~4的数)所表示的碱金属钛酸盐:60重量%以上至低于90重量%,SiO2:10重量%以上至低于40重量%,选自B、Mg、Al、P、Ca和Zn中的至少1种元素的氧化物:大于0重量%至10重量%以下,以及选自V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、Nb和Ba中的至少1种元素的氧化物:大于0重量%至10重量%以下,且M2O/SiO2≤2.5。
附图简述
图1是制备例1中获得的扁平状非晶性复合碱金属钛酸盐组合物粉末的、由扫描电子显微镜获得的显微镜照片。
图2是制备例1中获得的扁平状非晶性复合碱金属钛酸盐组合物粉末的、由扫描电子显微镜获得的显微镜照片。
图3是制备例2中获得的纤维状非晶性复合碱金属钛酸盐组合物纤维的、由扫描电子显微镜获得的显微镜照片。
图4是制备例3中获得的球状非晶性复合碱金属钛酸盐组合物粉末的、由扫描电子显微镜获得的显微镜照片。
具体实施方式
如上所述,本发明中涉及的非晶性复合碱金属钛酸盐组合物包含60重量%以上通式M2O·nTiO2(式中,M是碱金属元素中的1种或2种以上,n是1~4的数)所表示的碱金属钛酸盐,10重量%以上的SiO2,且M2O/SiO2≤2.5,根据需要,可以包含选自B、Mg、Al、P、Ca和Zn中的至少1种元素的氧化物,和/或选自V、Cr、Mn、 Fe、Co、Ni、Cu、Y、Zr、Nb和Ba中的至少1种元素的氧化物。
本发明中涉及的非晶性复合碱金属钛酸盐组合物适合用作摩擦材料的基材,通过在摩擦材料中混合3~50重量%,可以赋予优异的摩擦特性。
[碱金属钛酸盐]
碱金属元素是元素周期表的第1族元素,具体为Li、Na、K、Cs或Rb。
碱金属钛酸盐的非晶性是通过将起始原料混合物加热熔融,然后对该熔融物进行淬火处理而获得的。淬火处理通常通过双辊法进行,使相向的一对金属辊高速旋转,同时使熔融物在双辊间隙流下,使熔融物边与金属辊接触而淬火边通过辊间隙,作为薄片状的凝固物排至下方。由于该淬火效果而成为非晶性的。
对于由此得到的非晶性碱金属钛酸盐,即使是在式M2O·nTiO2中n的数为4以下的钛酸盐的情况下,通过合并SiO2也可以确保优异的化学稳定性和耐吸湿性,因此在摩擦材料成型时,可以防止碱金属离子的溶出,不会对摩擦材料的基材构成树脂产生不良影响。
需要说明的是,对于非晶性碱金属钛酸盐,在式M2O·nTiO2中n的数为大于4的钛酸盐的情况下,即使不包含SiO2也是稳定的,但也可以含有SiO2或B、Mg、Al、P、Ca、Zn、V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、Nb、Ba等的氧化物。
此外,由于不需要如结晶六钛酸钾那样,通过热处理、脱碱金属处理、烧成等向隧道结构转化的工序以获得化学稳定性,因此可以简化制造工序,此外,也可以避免由脱碱金属处理引起的产率降低。
此外,已知对于碱金属钛酸盐的非晶性结构,当适用于摩擦材料时,根据摩擦条件(温度、速度、压力等)发生软化、熔融反应,向摩擦界面供给适量的碱成分和钛成分,由此在各种条件下产生耐摩 耗性显著提高的效果。为了获得这些效果,优选使非晶性复合碱金属钛酸盐组合物中所含的碱金属钛酸盐为60重量%以上。
[SiO2]
SiO2通过使非晶性碱金属钛酸盐的非晶性结构的网络坚固、抑制常态时碱金属的溶出,使化学稳定性提高、耐吸湿性提高。
因此,使非晶性复合碱金属钛酸盐组合物中含有10重量%以上的SiO2,同时将碱金属钛酸盐的M2O与SiO2之比,即M2O/SiO2规定为2.5以下。
这样,非晶性复合碱金属钛酸盐组合物中所含的SiO2的含量为10重量%以上,因此碱金属钛酸盐为90重量%以下。需要说明的是,由于碱金属钛酸盐为60重量%以上,因此SiO2为40重量%以下。
[B、Mg、Al、P、Ca和Zn的氧化物]
B、Mg、Al、P、Ca和Zn的氧化物具有提高化学耐久性·稳定性的作用,还具有提高热稳定性的功能。因此,希望包含选自B、Mg、Al、P、Ca和Zn中的至少1种元素的氧化物。然而,含量过多时,碱金属钛酸盐与SiO2的混合平衡破坏,因此上限设为10重量%。
需要说明的是,在包含选自B、Mg、Al、P、Ca和Zn中的至少1种元素的氧化物的情况下,碱金属钛酸盐低于90重量%、SiO2低于40重量%。
[V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、Nb和Ba的氧化物]
当将V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、Nb和Ba的氧化物用作摩擦材料时,摩擦系数显著提高。因此,希望包含选自V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、Nb和Ba中的至少1种的氧化物。然而,含量过多时,碱金属钛酸盐与SiO2的混合平衡破坏,因 此上限设为10重量%。
在包含选自V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、Nb和Ba中的至少1种元素的氧化物的情况下,碱金属钛酸盐低于90重量%,SiO2低于40重量%。需要说明的是,在除了前述的选自B、Mg、Al、P、Ca和Zn中的至少1种元素的氧化物之外,还包含这些元素的氧化物的情况下也同样。
[摩擦材料]
本发明的非晶性复合碱金属钛酸盐组合物适合用作摩擦材料的基材,所述摩擦材料具体为构成汽车、铁道车辆、航空器、工业机械类等的制动装置中的制动衬片、制动盘衬垫(disk pad)、离合器衬片等的滑动面的摩擦材料。
适合用作摩擦材料的基材的非晶性复合碱金属钛酸盐组合物的混合量优选为摩擦材料的3~50重量%。
需要说明的是,摩擦材料中可以复合混合非晶性复合碱金属钛酸盐组合物,以及根据需要的其它公知材料(例如聚酰胺纤维、芳族聚酰胺纤维、钢纤维、铜纤维、玻璃纤维、陶瓷纤维、结晶钛酸盐化合物纤维等)。此外,这些材料可以根据需要、按照常规方式用硅烷类偶联剂、钛酸酯类偶联剂进行表面处理(偶联处理)后使用,以提高分散性、与粘合剂树脂的粘结性等。
摩擦材料中可以根据需要适量混合公知的摩擦摩耗调节剂(例如天然·合成橡胶粉末、槚如树脂粉粒体、有机物粉末、石墨、二硫化钼、无机粉末、金属粉末、氧化物粉末等),关于各种添加剂(例如防锈剂、润滑剂、研磨剂等),也可以根据其用途·使用方式等适量混合。
本发明的摩擦材料可如下制备:将基材分散在粘合剂树脂中,添加根据需要混合的摩擦摩耗调节剂和添加剂,均匀混合后配制原料组合物,预成型后进行模具成型,在加热·加压下(施加压力为约 10~40MPa,温度为约150~200℃)进行粘结成型,从模具中取出后,根据需要在加热炉内实施热处理(150~200℃,保持约1~12小时),然后对该成型体进行机械加工、研磨加工,制成具有预定形状的摩擦材料。
实施例
[制备例1:扁平状非晶性复合碱金属钛酸盐组合物]
称量碳酸钾(K2CO3)和二氧化钛(TiO2),使TiO2/K2O的摩尔比为2,将二者的均匀混合物在800℃下进行2小时加热处理,获得钛酸钾(K2O·2TiO2)的粉末。向所得钛酸钾(K2O·2TiO2)中加入二氧化硅(SiO2)和氢氧化镁(Mg(OH)2),使K2O·2TiO2/SiO2/MgO的重量比为75/20/5,并将这些物质的混合物加入铂坩埚中,在1200℃下熔融1小时。
使所得熔融物流入以圆周速度3.6m/s旋转的金属双辊之间、淬火,然后用锤磨机将所得的淬火固化物粉碎,由此获得粉末。
用扫描电子显微镜观察所得粉末,其显微镜照片如图1和图2所示。此外,用X射线衍射来检查有无结晶相,通过荧光X射线分析进行成分的定量,结果确认该粉末为原料组成几乎一致、平均直径约300μm,平均厚度约80μm的扁平状非晶性复合碱金属钛酸盐组合物。
制备例1得到的待测组合物在表1中表示为No.2。
作为与制备例1的TiO2/K2O的摩尔比和混合物组成不同的实例,由TiO2/K2O为1.9、K2O·1.9TiO2/SiO2=82/18的混合物制作待测组合物,在表1中表示为No.1。
作为与制备例1的TiO2/K2O的摩尔比和混合物组成不同的实例,由TiO2/K2O为2、K2O·2TiO2/SiO2/Fe2O3=75/20/5的混合物制作待测组合物,在表1中表示为No.5。
作为与制备例1的TiO2/K2O的摩尔比和混合物组成不同的实例, 由TiO2/K2O为2、K2O·2TiO2/SiO2/MgO/ZrO2=73/18/4/5的混合物制作待测组合物,在表1中表示为No.6。
作为与制备例1的TiO2/K2O的摩尔比和混合物组成不同的实例,由TiO2/K2O为2、K2O·2TiO2=100的混合物(不包含SiO2)制作待测组合物,在表1中表示为No.11。
作为与制备例1的TiO2/K2O的摩尔比和混合物组成不同的实例,由TiO2/K2O为1.7、K2O·1.7TiO2/SiO2/Al2O3=85/11/4的混合物制作待测组合物,在表1中表示为No.12。
作为与制备例1的TiO2/K2O的摩尔比和混合物组成不同的实例,由TiO2/K2O为3、K2O·3TiO2/SiO2/MgO=83/8/9的混合物制作待测组合物,在表1中表示为No.13。
[制备例2:纤维状非晶性复合碱金属钛酸盐组合物]
改变碳酸钾(K2CO3)和二氧化钛(TiO2)的摩尔比,向以与制备例1同样的方法得到的钛酸钾(K2O·1.7TiO2)中加入二氧化硅(SiO2)和氧化铝(Al2O3),使K2O·1.7TiO2/SiO2/Al2O3的重量比为78/18/4,将这些物质的混合物加入铂坩埚中,在1150℃下熔融2小时。
将所得熔融物转移至底部具有喷嘴孔的加热坩埚中,作为从喷嘴端部喷出的细流,向其吹压缩空气,由此获得纤维。
用扫描电子显微镜观察所得纤维,其显微镜照片如图3所示。此外,由X射线衍射检查有无结晶相,通过荧光X射线分析进行成分的定量,结果确认该纤维是原料组成几乎一致、平均纤维长度约1500μm、平均纤维直径约30μm、平均纵横比(长度/直径)为50的纤维状非晶性复合碱金属钛酸盐组合物。
制备例2制备的待测组合物在表1中表示为No.3。
[制备例3:球状非晶性复合碱金属钛酸盐组合物]
改变碳酸钾(K2CO3)和二氧化钛(TiO2)的摩尔比,向以与制备例1同样的方法得到的钛酸钾(K2O·2.8TiO2)中加入二氧化硅(SiO2)和碳酸钙(CaCO3),使K2O·2.8TiO2/SiO2/CaO的重量比为82/12/6,用热喷射装置(日本Eutectic株式会社制造,CASTON DYN DS8000)热喷射这些物质的混合物,在水中淬火,由此获得粉末。
用扫描电子显微镜观察所得粉末,其显微镜照片如图4所示。此外,由X射线衍射检查有无结晶相,通过荧光X射线分析进行成分的定量,结果确认该粉末是原料组成几乎一致、平均粒径约30μm的球状非晶性复合碱金属钛酸盐组合物。
制备例3制备的待测组合物在表1中表示为No.4。
需要说明的是,No.14是公知的结晶六钛酸钾的实例,其通过如下步骤制备:将按照TiO2/K2O的摩尔比为2混合的混合物在1200℃下加热熔融1小时,使所得熔融物冷却固化,制作二钛酸钾的纤维块,通过水合反应使纤维块膨润分离,在酸处理和钾浸出处理后进行固液分离和热处理。平均纤维长度约150μm,平均纤维宽度约30μm。
表1中,No.1~No.6是本发明的实施例,No.11~No.13是比较例,No.14是结晶结构的现有例。No.11是不包含SiO2的实例,No.12是M2O/SiO2的值大于本发明的值2.5的实例,No.13是SiO2的含量低、且M2O/SiO2的值大于本发明的值2.5的实例。
参照表1可以看出,与比较例No.11~No.13相比,本发明的实施例No.1~No.6中由水分吸收引起的重量增加率小、耐吸湿性优异。
需要说明的是,No.14中由水分吸收引起的重量增加率比本发明的实施例更小,但其为结晶性的,如前所述,需要从二钛酸钾向六钛酸钾转化的工序,制造工序复杂,并且由于有钾的浸出,会出现理论收率低的问题。
[吸湿性试验]
为了检查No.1~No.6和No.11~No.14的待测组合物的耐吸湿性能,在30℃、80%RH的恒温恒湿气氛中放置72小时后检测水分吸收引起的重量增加率。重量增加率如表1所示。
[摩擦试验]
准备包含No.1~No.6和No.11~No.14的组合物的摩擦材料用原料,用Eirich混合机混合3分钟,然后进行预成型(16MPa、常温、2分钟)和热成型(40MPa、170℃、10分钟,由成型2次的缓慢减压排气)。成型后实施热处理(200℃、5小时),切割成预定尺寸,实施研磨加工,获得待测摩擦材料。
前述摩擦材料用原料按重量%计包含20%上面准备的组合物、4%Kevlar浆粕、17%铜纤维、4%陶瓷纤维、10%研磨材料、5%云母、4%有机粉末、6%润滑材料、20%硫酸钡、10%酚醛树脂,在表2中,使用No.1~No.6和No.11~No.14的各组合物的待测摩擦材料分别表示为No.1a~No.6a和No.11a~No.14a。
关于各待测摩擦材料,依照JASO C427“制动衬片、衬垫摩耗测力计试验方法”进行摩耗试验,关于摩擦系数(μ)、衬垫摩耗量(mm)和制动盘摩耗量(μm),得到表2所示的结果。需要说明的是,摩擦系数是各温度下稳定时的平均摩擦系数,衬垫摩耗量和制动盘摩耗量是每制动1000次的平均摩耗量。
[表2]
参照表2可以看出,与比较例No.11a和No.12a相比,本发明的实施例No.1a~No.6a在对应较低制动初速度的低温区域(100℃)至与摩擦面的升温相伴的对应高制动初速度的高温区域(400℃)具有高摩擦系数,衬垫和制动盘的摩耗量小、耐摩耗性优异。认为其原因是:在本发明的实施例中,从低温区域至高温区域,在摩擦界面上形成稳定的流动层,同时在配对制动盘表面上形成均匀的转移层。
需要说明的是,No.13a与本发明的实施例几乎具有同等水平的高摩擦系数,但与本发明的实施例相比,衬垫摩耗量大、制动盘摩耗量大。认为其原因是:在制动盘表面形成的转移层比本发明的实施例中形成的转移层脆。
No.14a在摩擦系数这一点上与本发明的实施例同等或大于本发明的实施例,但衬垫摩耗量和制动盘摩耗量比本发明的实施例大。认为其原因是:No.14a是结晶性的,熔点高,不发生软化现象,因此与本发明的实施例相比,摩擦界面的流动层的稳定形成稍差。
发明效果
如上所述,本发明的非晶性复合碱金属钛酸盐组合物在化学上稳定且耐吸湿性优异,通过适用于汽车的制动盘衬垫等的摩擦材料,具有与以往的结晶碱金属六钛酸盐相比,在高温、高负荷下的摩擦系数几乎同等的稳定性,且可以获得耐摩耗性、对应面损伤得到改善的摩擦摩耗特性。
另一方面,不需要如以往的结晶碱金属六钛酸盐那样进行组成转化或向隧道型结晶结构转化的结晶结构转化工序,也没有伴随前述工序中的碱金属浸出的收率降低,因此可以显著降低制造成本。
此外,对于本发明的非晶性复合碱金属钛酸盐组合物具有如下优点:通过选择适当的制造方法,可以任意制作扁平状、纤维状或球状的组合物。
从气孔的形成和强度提高的观点出发,适合选择扁平形状,典型的尺寸是平均直径为10~600μm,平均厚度为3~200μm。从气孔的形成和强度进一步提高的观点出发,适合选择纤维形状,典型的尺寸是平均直径为5~100μm,纵横比(长度/直径)为10以上。从流动性和分散性的观点出发,适合选择球状形状,典型的尺寸是平均粒径为5~100μm。
Claims (5)
1.一种非晶性复合碱金属钛酸盐组合物,具有如下组成:通式M2O·nTiO2所表示的碱金属钛酸盐:60~90重量%,SiO2:10~40重量%,并且按重量比计M2O/SiO2≤2.5;通式中M是碱金属元素中的1种或2种以上,n是1~4的数。
2.权利要求1的非晶性复合碱金属钛酸盐组合物,含有60重量%以上至低于90重量%的碱金属钛酸盐,10重量%以上至低于40重量%的SiO2,大于0重量%至10重量%以下的选自B、Mg、Al、P、Ca和Zn中的至少1种元素的氧化物。
3.权利要求1的非晶性复合碱金属钛酸盐组合物,其含有60重量%以上至低于90重量%的碱金属钛酸盐,10重量%以上至低于40重量%的SiO2,大于0重量%至10重量%以下的选自V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、Nb和Ba中的至少1种元素的氧化物。
4.权利要求2的非晶性复合碱金属钛酸盐组合物,其含有60重量%以上至低于90重量%的碱金属钛酸盐,10重量%以上至低于40重量%的SiO2,大于0重量%至10重量%以下的选自V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、Nb和Ba中的至少1种元素的氧化物。
5.一种用于制动器或离合器的摩擦材料,其包含权利要求1-4中任一项所述的非晶性复合碱金属钛酸盐组合物中的一种以上。