CN101397435A - 环保水性氟碳金属漆 - Google Patents

环保水性氟碳金属漆 Download PDF

Info

Publication number
CN101397435A
CN101397435A CNA2008100404423A CN200810040442A CN101397435A CN 101397435 A CN101397435 A CN 101397435A CN A2008100404423 A CNA2008100404423 A CN A2008100404423A CN 200810040442 A CN200810040442 A CN 200810040442A CN 101397435 A CN101397435 A CN 101397435A
Authority
CN
China
Prior art keywords
agent
percent
solvent
environment friendly
aluminium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100404423A
Other languages
English (en)
Inventor
黄银贤
何生才
池钟慷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI SAN-YIN PAINTS Co Ltd
Original Assignee
SHANGHAI SAN-YIN PAINTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI SAN-YIN PAINTS Co Ltd filed Critical SHANGHAI SAN-YIN PAINTS Co Ltd
Priority to CNA2008100404423A priority Critical patent/CN101397435A/zh
Publication of CN101397435A publication Critical patent/CN101397435A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种环保水性氟碳金属漆，由下述原料按质量百分比组成：氟乳35％～65％、铝银浆5％～12％、消泡剂0.1％～0.5％、润湿剂0.1％～0.3％、流平剂0.1％～0.3％、分散剂0.2％～0.8％、金属定向剂2％～8％、增稠剂：有机改性蒙脱石0.1％～0.3％、聚氨酯缔合型增稠剂1.0％～5.0％、成膜助剂1％～3％、防冻剂1％～3％、溶剂6％～10％、余量为去离子水；本发明的有益效果是：能减少环境污染及在保温装饰体系中使用的风险，而性能可完全等同溶剂型氟碳铝银浆(珠光粉)涂料。

Description

环保水性氟碳金属漆
技术领域
本发明涉及一种金属漆，尤其涉及一种应用于建筑外墙装饰及外保温装饰体系的金属漆。
背景技术
氟碳涂料以其超耐候性、高装饰性、耐化性、耐污性，已被广泛应用于建筑外墙装饰及外保温装饰体系，尤其是氟碳铝银浆(珠光)涂料以其较低成本，高装饰性而逐渐替代高成本的金属幕墙，但因溶剂型氟碳铝银浆(珠光)漆VOC偏高，污染环境，且在外墙外保温体系中，因保温材料耐溶剂性差，溶剂型涂料有破坏保温层的风险，使其使用受到限制。
发明内容
本发明需要解决的技术问题是提供了一种环保水性氟碳金属漆，旨在解决上述的问题。
为了解决上述技术问题，本发明是通过以下技术方案实现的：
本发明由下述原料按质量百分比组成：
氟乳液                   35％～65％
铝银浆(珠光颜料)         5％～12％
消泡剂                   0.1％～0.5％
润湿剂                   0.1％～0.3％
流平剂                   0.1％～0.3％
分散剂                   0.2％～0.8％
金属定向剂               2％～8％
增稠剂：有机改性蒙脱石     0.1％～0.3％
        聚氨酯缔合型增稠剂  1.0％～5.0％
成膜助剂                   1％～3％
防冻剂                     1％～3％
溶剂                       6％～10％
余量为去离子水。
与现有技术相比，本发明的有益效果是：能减少环境污染及在保温装饰体系中使用的风险，而性能可完全等同溶剂型氟碳铝银浆(珠光粉)涂料。
具体实施方式
下面结合具体实施方式对本发明作进一步详细描述：
本发明中的原料在市场上都有售：
氟乳液为FEVE乳液或含氟丙烯酸乳液，如：常熟中昊ZH-01、大连振邦F600、F500、青岛宏丰HFS-F-3300、HFS-F-3301、长兴化工4312；
铝银浆为SilBerLine的
Figure A200810040442D0006095448QIETU
系列、
Figure A200810040442D0006095501QIETU
 AQ系列产品、Schlenk的AQUAMET NPW系列产品、Eckart Hydrolan系列产品、深圳族兴的ZW系列产品；
珠光颜料为德国Merk产品及国内珠光颜料产品；
消泡剂为BYK-093(德国毕克)及同类型产品；
润湿剂为布莱克本的CF-10及同类型产品；
流平剂为BYK-348(德国毕克)及同类型产品；
分散剂为BYK-190(德国毕克)及同类型产品；
金属定向剂为阴离子型EVA共聚乳液，如BYK AQUACER 526等产品；
增稠剂为无机增稠剂如海名斯的B-4000及聚氨酯缔合型增稠剂如海名斯的Rheolate 278、罗门哈斯的RM 2020、日本旭电化的Uh-420等；
成膜助剂为EASTMAN的Texanol或其它醇酯十二类产品；
防冻剂为丙二醇或乙二醇；
溶剂为乙醇或者异丙醇。
本发明制造方法是通过以下步骤实现的：
1.铝银浆(珠光颜料)的预处理
将铝银浆(珠光粉)、溶剂、润湿剂混合用材棍搅拌成均匀糊状，浸泡4h以上备用；
2.将部分去离子水、防冻剂、分散剂、消泡剂、流平剂、定向剂逐一混合，慢速分散20分钟，缓慢加入氟碳乳液，搅拌均匀；
3.将无机增稠剂用水预溶后，再加入上述混合液中；
4.将成膜助剂、缔合型增稠剂、部分去离子水逐一加入，搅拌均匀；
5.将搅拌均匀的混合溶液缓慢加入浸泡好的金属颜料浆中，慢速搅拌均匀即可。
实施例1
本发明由下述原料按质量百分比组成：
氟乳液                    45.5％
铝银浆(珠光颜料)          10％
消泡剂                    0.4％
润湿剂                    0.2％
流平剂                    0.2％
分散剂                    0.6％
金属定向剂                6％
增稠剂：有机改性蒙脱石    0.2％
        聚氨酯缔合型增稠剂 4.0％
成膜助剂                  2％
防冻剂                   2％
溶剂                     8％
余量为去离子水。
实施例2
本发明由下述原料按质量百分比组成：
氟乳液                     50％
铝银浆(珠光颜料)           8％
消泡剂                     0.3％
润湿剂                     0.1％
流平剂                     0.3％
分散剂                     0.2％
金属定向剂                 2％
增稠剂：有机改性蒙脱石     0.1％
        聚氨酯缔合型增稠剂  5.0％
成膜助剂                   2％
防冻剂                     2％
溶剂                       6％
余量为去离子水。
实施例3
本发明由下述原料按质量百分比组成：
氟乳液                      65％
铝银浆(珠光颜料)            5％
消泡剂                      0.5％
润湿剂                      0.1％
流平剂                      0.2％
分散剂                    0.7％
金属定向剂                5％
增稠剂：有机改性蒙脱石    0.3％
        聚氨酯缔合型增稠剂 3.0％
成膜助剂                  1％
防冻剂                    1％
溶剂                      6％
余量为去离子水。

Claims (4)

1.一种环保水性氟碳金属漆，由下述原料按质量百分比组成：
氟乳液                      35％～65％
铝银浆                      5％～12％
消泡剂                      0.1％～0.5％
润湿剂                      0.1％～0.3％
流平剂                      0.1％～0.3％
分散剂                      0.2％～0.8％
金属定向剂                  2％～8％
增稠剂：有机改性蒙脱石      0.1％～0.3％
        聚氨酯缔合型增稠剂  1.0％～5.0％
成膜助剂                    1％～3％
防冻剂                      1％～3％
溶剂                        6％～10％
余量为去离子水。
2.根据权利要求1所述的环保水性氟碳金属漆，其中：
氟乳液                      45％
铝银浆                      10％
消泡剂                      0.4％
润湿剂                      0.2％
流平剂                      0.2％
分散剂                      0.6％
金属定向剂                  6％
增稠剂：有机改性蒙脱石      0.2％
        聚氨酯缔合型增稠剂  4.0％
成膜助剂              2％
防冻剂                2％
溶剂                  8％
余量为去离子水。
3.根据权利要求1所述的环保水性氟碳金属漆，其中：
氟乳液                     50％
铝银浆                     8％
消泡剂                     0.3％
润湿剂                     0.1％
流平剂                     0.3％
分散剂                     0.2％
金属定向剂                 2％
增稠剂：有机改性蒙脱石     0.1％
        聚氨酯缔合型增稠剂 5.0％
成膜助剂                   2％
防冻剂                     2％
溶剂                       6％
余量为去离子水。
4.根据权利要求1所述的环保水性氟碳金属漆，其中：
氟乳液                     65％
铝银浆                     5％
消泡剂                     0.5％
润湿剂                     0.1％
流平剂                     0.2％
分散剂                     0.7％
金属定向剂                  5％
增稠剂：有机改性蒙脱石      0.3％
        聚氨酯缔合型增稠剂  3.0％
成膜助剂                    1％
防冻剂                      1％
溶剂                        6％
余量为去离子水。
CNA2008100404423A 2008-07-10 2008-07-10 环保水性氟碳金属漆 Pending CN101397435A (zh)