CN101338180B - 处理老化油的硫离子抑制剂及其制备方法 - Google Patents
处理老化油的硫离子抑制剂及其制备方法 Download PDFInfo
- Publication number
- CN101338180B CN101338180B CN2008101178877A CN200810117887A CN101338180B CN 101338180 B CN101338180 B CN 101338180B CN 2008101178877 A CN2008101178877 A CN 2008101178877A CN 200810117887 A CN200810117887 A CN 200810117887A CN 101338180 B CN101338180 B CN 101338180B
- Authority
- CN
- China
- Prior art keywords
- oil
- sodium
- passivating agent
- sulfur ion
- treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
处理老化油的硫离子抑制剂,应用于油田的老化油脱水用的硫离子抑制剂。特征是:其特征是:各组分重量百分比为:a、多肽缩合试剂(HATU)C10H15F6N6OP,含量为0.05%的水溶液:15.2~26.0%;b、亚硝酸钠:4.0~6.5%;c、硫酸钠:2.0~3.5%;d、乳酸钠:3.0~6.5%;e、维生素C:0.05~0.1%;f、其余为水。效果是:老化油的处理过程中,加量在50mg/l~100mg/l时,既能保证老化油进入电脱平稳运行,又能保证分离出的污水质量。
Description
技术领域
本发明属于石油工业用化学品技术领域,尤其涉及一种在老化油处理过程中使用的解决老化油脱水用的硫离子抑制剂及其制备方法。是一种在老化油处理过程中使用的,加量在50mg/l~100mg/l时,既能使老化油进行电脱水并平稳运行,又能保证污水水质的处理剂。
背景技术
随着油田的开采历史的增长,注水与注聚采油工艺的深入开展,特别是一些中后期开采的油田,或者是在一些高含水油田,在地面原油脱水过程中,老化油的产生和积累就会愈来愈多。老化油的脱水或净化处理工作的难度也就越来越大。所述的老化油是就是现有技术手段难以处理的原油。老化油乳状液成分复杂,含有许多导电性较强的粘土和FeS等机械杂质。在回收老化油时,脱水***中发现黑色过度层,其主要成分为胶态硫化物(包括硫化亚铁颗粒),它是由硫酸盐还原菌在集输***的设备、管线中大量繁殖而引起铁的腐蚀产物。随着黑色过度层厚度增大,增强了介质的导电性,导致电脱水器运行不稳、跳闸或直至造成电脱水器极板击穿事故,严重影响电脱水器的正常运行。在当前,老化油的处理一直是困扰着我们油田实行正常生产的难题,特别是油田脱水过程中因处理老化油造成脱水***瘫痪的情况屡屡发生,严重影响了油田的正常生产工作。为了提高原油的产量,减少采油成本,积累出来的老化油还不得不处理。多年来,油田科技工作者和工程技术人员对老化油的处理进行了大量的试验与研究,也取得了不少非常有价值的科研成果。但是,老化油的处理问题没有得到有效的解决,或从根本上进行解决。这就不得不改变我们对老化油的再认识,寻找新的思路和解决的办法。
发明内容
本发明的目的是:提供一种处理老化油的硫离子抑制剂的配方及其制备方法。在老化油的处理过程中,加量在50mg/l~100mg/l时,既能保证老化油进入电脱平稳运行,又能保证分离出的污水质量。
本发明为解决其技术问题所采取的技术方案是:
一、处理老化油的硫离子抑制剂的原料包括:
1、多肽缩合试剂含量为0.05%的水溶液;
多肽缩合试剂C10H15F6N6OP,分子量:380.2(工业品)成都凯泰新技术有限责任公司生产;产品名称:HATU,结构式:
2、亚硝酸钠(工业品);分子式:NaNO2,
3、硫酸钠(工业品);
4、乳酸钠(工业品);分子式:Na2SO4
5、维生素C(工业品);分子式:C6H8O6
6、水。
处理老化油的硫离子抑制剂的各组分重量比:
1、多肽缩合试剂(HATU)C10H15F6N6OP(工业品)含量为0.05%的水溶液:15.2~26.0%
2、亚硝酸钠(工业品):4.0~6.5%
3、硫酸钠(工业品):2.0~3.5%
4、乳酸钠(工业品):3.0~6.5%
5、维生素C(工业品):0.05~0.1%
6、其余为水,各组分重量百分数之和为100%。
处理老化油的硫离子抑制剂,各组分较好的重量百分比为:
a、多肽缩合试剂(HATU)C10H15F6N6OP(工业品)含量为0.05%的水溶液:19~26.0%;
b、亚硝酸钠(工业品):4.5~5.5%;
c、硫酸钠(工业品):2.0~3.5%;
d、乳酸钠(工业品):3.0~6.5%;
e、维生素C(工业品):0.05~0.1%;
f、其余为水,各组分重量百分数之和为100%。
二、处理老化油的硫离子抑制剂的生产方法
主要设备:
具有搅拌、加热、冷却功能,并有真空***的2000L的搪瓷反应釜。
生产方法:
首先,将多肽缩合试剂(HATU)C10H15F6N6OP(工业品)含量为0.05%的水溶液、亚硝酸钠、硫酸钠、乳酸钠、维生素C等五种原料按比例加入具有搅拌、加热、冷却功能,并有真空***的搪瓷反应釜中,并缓慢升温到35~45℃。
其次,在不断搅拌下加入水,继续搅拌30分钟后,停止加热。
最后,边冷却边搅拌,冷却至常温。得到处理老化油的硫离子抑制剂。
本发明的有益效果是:采用本方法制备的处理老化油的硫离子抑制剂。在老化油的处理过程中,加量在50mg/l~100mg/l时,既能保证老化油进入电脱平稳运行,又能保证分离出的污水质量。
具体实施方式
利用本发明自2006年起分别在华北油田的十余座联合站老化油处理过程中试用,加量在50mg/l~100mg/l时,既能保证老化油进入电脱平稳运行,又能保证脱出的污水质量。以5次制备处理老化油的硫离子抑制剂为例,对发明作进一步详细说明。
实施例1:
处理老化油的硫离子抑制剂的原料组分重量比:
1、多肽缩合试剂(HATU)C10H15F6N6OP(工业品)含量为0.05%的水溶液:22.0%
2、亚硝酸钠(工业品):5.1%
3、硫酸钠(工业品):3.2%
4、乳酸钠(工业品):3.8%
5、维生素C(工业品):0.07%
6、其余为水,各组分重量百分数之和为100%。
首先,将多肽缩合试剂(HATU)C10H15F6N6OP(工业品)含量为0.05%的水溶液、亚硝酸钠、硫酸钠、乳酸钠、维生素C等五种原料按比例全部加入具有搅拌、加热、冷却功能,并有真空***的2000L的搪瓷反应釜中,并缓慢升温到40℃。
其次,在不断搅拌下加入水,继续搅拌30分钟搅拌均匀,停止加热。
最后,边冷却边搅拌,冷却至常温。得到处理老化油的硫离子抑制剂。
实施例2~5的各组分重量比列表如下:
组分名称 | 例2% | 例3% | 例4% | 例5% |
多肽缩合试剂(HATU)C10H15F6N6OP含量为0.05%的水溶液 | 17 | 23.5 | 24.5 | 26 |
亚硝酸钠 | 4.5 | 5 | 4.8 | 4.5 |
硫酸钠 | 3.2 | 2.8 | 3.5 | 2.3 |
乳酸钠 | 3.8 | 6.2 | 5.7 | 4.5 |
维生素C | 0.07 | 0.075 | 0.081 | 0.089 |
水 | 其余 | 其余 | 其余 | 其余 |
实施例2~5的处理老化油的硫离子抑制剂,各组分重量百分数之和为100%,制备方法与实施例1相同。
Claims (3)
1.一种处理老化油的硫离子抑制剂,其特征是:各组分重量百分比为:
a、分子式为C10H15F6N6OP的多肽缩合试剂HATU含量为0.05%的水溶液:15.2~26.0%;
b、亚硝酸钠:4.0~6.5%;
c、硫酸钠:2.0~3.5%;
d、乳酸钠:3.0~6.5%;
e、维生素C:0.05~0.1%;
f、其余为水,各组分重量百分数之和为100%。
2.根据权利要求1所述的处理老化油的硫离子抑制剂,其特征是:各组分重量百分比为:
a、分子式为C10H15F6N6OP的多肽缩合试剂HATU含量为0.05%的水溶液:19~26.0%;
b、亚硝酸钠:4.5~5.5%;
c、硫酸钠:2.0~3.5%;
d、乳酸钠:3.0~6.5%;
e、维生素C:0.05~0.1%;
f、其余为水,各组分重量百分数之和为100%。
3.根据权利要求1或2所述的处理老化油的硫离子抑制剂的制备方法,其特征是:
首先,将分子式为C10H15F6N6OP的多肽缩合试剂HATU含量为0.05%的水溶液、亚硝酸钠、硫酸钠、乳酸钠、维生素C等五种原料按比例加入具有搅拌、加热、冷却功能,并有真空***的搪瓷反应釜中,并缓慢升温到35~45℃;
其次,在不断搅拌下加入水,继续搅拌30分钟后,停止加热;
最后,边冷却边搅拌,冷却至常温,得到处理老化油的硫离子抑制剂。