CN101210385A - 合成纤维用处理剂及合成纤维的处理方法 - Google Patents
合成纤维用处理剂及合成纤维的处理方法 Download PDFInfo
- Publication number
- CN101210385A CN101210385A CNA2007101608461A CN200710160846A CN101210385A CN 101210385 A CN101210385 A CN 101210385A CN A2007101608461 A CNA2007101608461 A CN A2007101608461A CN 200710160846 A CN200710160846 A CN 200710160846A CN 101210385 A CN101210385 A CN 101210385A
- Authority
- CN
- China
- Prior art keywords
- synthetic fiber
- finishing agent
- aliphatic
- acid
- isocyanuric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
提供如工业材料用合成纤维那样即使在高温且高接触压力的苛刻条件下制丝时也可以抑制制丝步骤中的摆丝、绒毛和焦油的产生,防止丝强度降低的处理剂和处理方法。作为合成纤维用处理剂,使用以规定的比率含有润滑剂、乳化剂和抗静电剂且以规定的比率含有下述异氰脲酸衍生物作为润滑剂的至少一部分的合成纤维用处理剂,异氰脲酸衍生物选自三(羟基甲基)异氰脲酸和有机单羧酸的部分或完全酯化合物、三(2-羟基乙基)异氰脲酸和有机单羧酸的部分或完全酯化合物、三(2-羟基丙基)异氰脲酸和有机单羧酸的部分或完全酯化合物、异氰脲酸二(2-羟基丙基)和有机单羧酸的部分或完全酯化合物、三(2-羧基乙基)异氰脲酸和一价脂肪族羟基化合物的部分或完全酯化合物、以及异氰脲酸二(2-羧基乙基)和一价脂肪族羟基化合物的部分或完全酯化合物中的1种或2种以上。
Description
技术领域
本发明涉及合成纤维用处理剂(下文简称为处理剂)和合成纤维的处理方法(下文简称为处理方法)。对于聚酰胺纤维或聚酯纤维等合成纤维来说,在其制丝步骤中在该合成纤维上不产生绒毛等是重要的。其中,用于轮胎帘子线、带(ベルト)、软管(ホ一ス)、安全带(シ一トベルト)、气袋(エア一バツグ)等的、由于上述用途的关系要求高强度的工业材料(産業資材)用合成纤维,由于在高温且高接触压力的苛刻条件下制丝,在制丝步骤中易产生摆丝(糸摇れ)、绒毛和焦油(タ一ル),结果丝强度降低,所以不产生上述摆丝、绒毛和焦油是特别重要的。因此,对于附着于合成纤维上的处理剂,要求即使该合成纤维在高温且高接触压力下制丝时也可以抑制上述摆丝、绒毛和焦油的产生,从而防止丝强度降低的处理剂。本发明涉及对应于上述要求的处理剂和处理方法。
背景技术
以往作为即使在高温且高接触压力下也可以向合成纤维赋予平滑性、抑制产生绒毛等的处理剂,提出了1)含有以多元醇和羟基单羧酸的酯化合物的烯化氧加成物为必须成分的醇成分、与以马来酸为必须成分的羧酸成分的酯化合物的处理剂(例如,参照专利文献1),2)包含由不具有羟基的二元羧酸或单羧酸构成的羧酸成分、与由蓖麻油或氢化蓖麻油的烯化氧加成物构成的醇成分的酯化合物的处理剂(例如,参照专利文献2),3)包含由四氢呋喃和烯化氧的无规聚合物构成的二元醇成分、与二元羧酸成分或单羧酸成分的酯化合物的处理剂(例如,参照专利文献3),4)含有分子中具有聚四亚甲基二醇残基的化合物的处理剂(例如,参照专利文献4)等。此外,作为即使在高温且高接触压力下也可以向合成纤维赋予耐热性、抑制焦油等的产生的处理剂,已知5)含有多元酯化合物、阴离子表面活性剂和两种受阻酚类抗氧化剂的处理剂(例如,参照专利文献5),6)含有硫代二丙酸二烷基酯等含硫二酯化合物、磷酸酯化合物和受阻酚类抗氧化剂的处理剂(例如,参照专利文献6),7)含有多元酯化合物、具有硫醚基的酯化合物、二级磺酸酯、有机磷酸酯化合物和受阻酚类抗氧化剂的处理剂(例如,参照专利文献7),8)含有硫代二丙酸二烷基酯等含硫二酯化合物、两种受阻酚类抗氧化剂和磷酸酯金属盐的处理剂(例如,参照专利文献8),9)含有多元酯化合物和受阻酚类抗氧化剂的处理剂(例如,参照专利文献9),10)含有芳香族酯化合物、有机羧酸和各种抗氧化剂的处理剂(例如,参照专利文献10)等。
但是,这些现有的处理剂中,对于近年在更苛刻的条件下制丝得到的合成纤维,在抑制产生上述摆丝、绒毛和焦油,防止丝强度的降低方面存在明显不充分的问题。
[专利文献1]日本特开昭59-223368号公报
[专利文献2]日本特开昭63-50572号公报
[专利文献3]日本特开昭63-235576号公报
[专利文献4]日本特开昭59-59978号公报
[专利文献5]日本特开昭59-211680号公报
[专利文献6]日本特开平7-216735号公报
[专利文献7]日本特开平8-120563号公报
[专利文献8]日本特开平10-325074号公报
[专利文献9]日本特开平5-140870号公报
[专利文献10]日本特开2004-292961号公报
发明内容
本发明的目的在于,提供如工业材料用合成纤维那样,即使在高温且高接触压力的苛刻条件下制丝时,也可以抑制制丝步骤中的摆丝、绒毛和焦油的产生,从而防止丝强度的降低的处理剂和处理方法。
本发明人为了解决上述问题而进行研究,结果发现以规定的比率含有润滑剂(平滑剤)、乳化剂和抗静电剂且以规定的比率含有特定的异氰脲酸衍生物作为润滑剂的至少一部分的处理剂是合适的,此外,使上述处理剂以规定的量附着于供给到热处理步骤的合成纤维长丝丝条是合适的。
即,本发明涉及一种处理剂,其含有润滑剂、乳化剂和抗静电剂,其特征在于,含有处理剂总量的5~75质量%的润滑剂、处理剂总量的21~94质量%的乳化剂和处理剂总量的0.1~10质量%的抗静电剂,且含有处理剂总量的5~45质量%的下述异氰脲酸衍生物作为润滑剂的至少一部分。
异氰脲酸衍生物:选自三(羟基甲基)异氰脲酸和有机单羧酸的部分或完全酯化合物、三(2-羟基乙基)异氰脲酸和有机单羧酸的部分或完全酯化合物、三(2-羟基丙基)异氰脲酸和有机单羧酸的部分或完全酯化合物、异氰脲酸二(2-羟基丙基)(イソシアヌル酸ビス(2-ヒドロキシプロピル))和有机单羧酸的部分或完全酯化合物、三(2-羧基乙基)异氰脲酸和一价脂肪族羟基化合物的部分或完全酯化合物、以及异氰脲酸二(2-羧基乙基)(イソシアヌル酸ビス(2-カルボキシエチル))和一价脂肪族羟基化合物的部分或完全酯化合物中的1种或2种以上。
此外,本发明涉及处理方法,其特征在于,使上述本发明涉及的处理剂以0.1~3质量%附着于供给到热处理步骤的合成纤维长丝丝条。
具体实施方式
首先对本发明涉及的处理剂进行说明。本发明涉及的处理剂含有润滑剂、乳化剂和抗静电剂,含有特定的异氰脲酸衍生物作为润滑剂的至少一部分。
作为用于本发明涉及的处理剂中的润滑剂的异氰脲酸衍生物,可以举出选自1)三(羟基甲基)异氰脲酸和有机单羧酸的部分或完全酯化合物、2)三(2-羟基乙基)异氰脲酸和有机单羧酸的部分或完全酯化合物、3)三(2-羟基丙基)异氰脲酸和有机单羧酸的部分或完全酯化合物、4)异氰脲酸二(2-羟基丙基)和有机单羧酸的部分或完全酯化合物、5)三(2-羧基乙基)异氰脲酸和一价脂肪族羟基化合物的部分或完全酯化合物、6)异氰脲酸二(2-羧基乙基)和一价脂肪族羟基化合物的部分或完全酯化合物中的1种或2种以上,都优选为完全酯化合物,其中更优选为2)的完全酯化合物和5)的完全酯化合物。
用于本发明涉及的处理剂中的润滑剂的异氰脲酸衍生物中,作为其原料的有机单羧酸,可以举出1)乙酸、丙酸、丁酸、戊酸、己酸、辛酸、癸酸、十一烷酸、十二烷酸、十三烷酸、十四烷酸、十五烷酸、软脂酸、硬脂酸、棕榈油酸、油酸、异辛酸、异十六烷酸、异十八烷酸等碳原子数为2~22的脂肪族单羧酸,2)苯甲酸、3,5-二(1,1-二甲基乙基)-4-羟基苯丙酸等芳香族单羧酸,3)丙二酸、马来酸、衣康酸、己二酸、癸二酸、十五烯基琥珀酸等碳原子数为3~22的脂肪族二元羧酸与一价脂肪族羟基化合物的脂肪族单酯单羧酸,4)邻苯二甲酸、间苯二甲酸、对苯二甲酸等碳原子数为8~22的芳香族二元羧酸与一价脂肪族羟基化合物的脂肪族单酯单芳香族羧酸,5)硫代二丙酸、硫代二辛酸、硫代二月桂酸、硫代二硬脂酸等碳原子数为3~22的含硫脂肪族二元羧酸与一价脂肪族羟基化合物的含硫脂肪族单酯单羧酸等,其中,优选碳原子数为2~22的脂肪族单羧酸,更优选碳原子数为3~18的脂肪族单羧酸。
此外,用于本发明涉及的处理剂中的润滑剂的异氰脲酸衍生物中,作为其原料的一价脂肪族羟基化合物,可以举出1)丁醇、戊醇、己醇、庚醇、辛醇、壬醇、癸醇、十一烷醇、十二烷醇、十三烷醇、2-甲基-戊醇、2-乙基-己醇、2-丙基-庚醇、2-丁基-辛醇等碳原子数为1~26的脂肪族一元醇,2)1,4-丁二醇、1,6-己二醇、新戊二醇、甘油、三羟甲基丙烷、脱水山梨醇等脂肪族多元醇与有机单羧酸的脂肪族单酯一元醇等,其中,优选碳原子数为1~26的脂肪族一元醇,更优选碳原子数为4~18的脂肪族一元醇。
用于本发明涉及的处理剂中的润滑剂的异氰脲酸衍生物可以用任何公知的方法合成。例如,三(羟基甲基)异氰脲酸和有机单羧酸的部分或完全酯化合物可以如下合成:相对于醇成分三(羟基甲基)异氰脲酸1摩尔,使用有机单羧酸3~5摩尔,加入硫酸等酸性化合物,一边加热一边进行脱水酯化反应,或加入吡啶等碱性化合物、在氯仿等惰性溶剂中一边加热一边进行酯化反应,由此合成上述化合物。三(2-羟基乙基)异氰脲酸和有机单羧酸的部分或完全酯化合物,除了使用三(2-羟基乙基)异氰脲酸作为醇成分之外,可以用与上述三(羟基甲基)异氰脲酸和有机单羧酸的部分或完全酯化合物相同的方法合成。三(2-羟基丙基)异氰脲酸和有机单羧酸的部分或完全酯化合物以及异氰脲酸二(2-羟基丙基)和有机单羧酸的部分或完全酯化合物也可以用相同的方法合成。
此外,例如,三(2-羧基乙基)异氰脲酸和一价脂肪族羟基化合物的部分或完全酯化合物可以如下合成:相对于酸成分三(2-羧基乙基)异氰脲酸1摩尔,使用一价脂肪族羟基化合物3~5摩尔,加入硫酸等酸性化合物、一边加热一边进行脱水酯化反应,或加入吡啶等碱性化合物、在氯仿等惰性溶剂中一边加热一边进行酯化反应,由此合成上述化合物。异氰脲酸二(2-羧基乙基)和一价脂肪族羟基化合物的部分或完全酯化合物,除了使用异氰脲酸二(2-羧基乙基)作为酸成分之外,可以用与上述三(2-羧基乙基)异氰脲酸和一价脂肪族羟基化合物的部分或完全酯化合物相同的方法合成。
作为用于本发明的处理剂中的异氰脲酸衍生物之外的润滑剂,可以举出有机酯化合物、矿物油、聚醚、硅酮化合物等,优选为有机酯化合物,其中,优选为脂肪族酯化合物、芳香族酯化合物和动植物油脂类。作为上述脂肪族酯化合物,可以举出1)辛基硬脂酸酯、油基月桂酸酯、油基油酸酯等脂肪族1元醇和脂肪族单羧酸的酯化合物,2)1,6-己二醇二癸酸酯、三羟甲基丙烷单油酸酯二月桂酸酯等脂肪族多元醇和脂肪族单羧酸的完全酯化合物,3)二月桂基己二酸酯、二油基壬二酸酯、三辛基偏苯三酸酯等脂肪族一元醇和脂肪族多元羧酸的完全酯化合物等,此外,作为芳香族酯化合物,可以举出4)苄基硬脂酸酯、苄基月桂酸酯等芳香族一元醇和脂肪族单羧酸的酯化合物,5)双酚A二月桂酸酯等芳香族多元醇和脂肪族单羧酸的完全酯化合物,6)二异硬脂基间苯二甲酸酯、三辛基偏苯三酸酯等脂肪族一元醇和芳香族多元羧酸的完全酯化合物等,进一步地,作为动植物油脂类,可以举出7)椰子油、菜籽油、葵花籽油、大豆油、蓖麻油、芝麻油、鱼油、牛脂等。其中,优选为二元或三元脂肪族多元醇和脂肪族单羧酸的完全酯化合物、脂肪族一元醇和二元或三元脂肪族多元羧酸的完全酯化合物、二元或三元芳香族多元醇和脂肪族单羧酸的完全酯化合物、脂肪族一元醇和二元或三元芳香族多元羧酸的完全酯化合物以及油脂类。
作为用于本发明的处理剂中的乳化剂,可以举出各种非离子表面活性剂。作为上述非离子表面活性剂,可以举出1)聚氧化烯辛基醚、聚氧化烯辛基醚月桂酸酯、聚氧化烯壬基苯基醚、聚氧化烯油酸酯、聚氧化烯月桂基氨基醚、聚氧化烯月桂酰胺醚等分子中具有聚氧亚烷基的醚型非离子表面活性剂,2)脱水山梨醇单月桂酸酯、脱水山梨醇三油酸酯、山梨糖醇四油酸酯、甘油单油酸酯、甘油单月桂酸酯、二甘油二月桂酸酯等多元醇部分酯型非离子表面活性剂,3)聚氧化烯脱水山梨醇三油酸酯、聚氧化烯甘油单月桂酸酯、聚氧化烯双酚A二月桂酸酯、聚氧化烯蓖麻油、聚氧化烯氢化蓖麻油、聚氧化烯氢化蓖麻油二月桂酸酯、聚氧化烯氢化蓖麻油三辛酸酯等聚氧化烯多元醇脂肪酸酯型非离子表面活性剂,4)二乙醇胺单月桂酰胺、二乙醇胺单油酰胺、二亚乙基三胺二辛基酰胺等酰胺型非离子表面活性剂,5)聚氧乙烯二乙醇胺单油基酰胺、聚氧乙烯二亚乙基三胺二月桂基酰胺等聚氧化烯脂肪酸酰胺型非离子表面活性剂等。其中,优选为多元醇部分酯型非离子表面活性剂、聚氧化烯多元醇脂肪酸酯型非离子表面活性剂,该多元醇选自甘油、蓖麻油、氢化蓖麻油、脱水山梨醇和山梨糖醇,更优选为甘油部分酯、脱水山梨醇部分酯、山梨糖醇部分酯、聚氧化烯脱水山梨醇酯、聚氧化烯山梨糖醇酯、聚氧化烯蓖麻油、聚氧化烯氢化蓖麻油、聚氧化烯氢化蓖麻油烷基酯。
作为用于本发明的处理剂中的抗静电剂,可以举出任意的各种阴离子表面活性剂、阳离子表面活性剂、两性表面活性剂等。其中,优选为阴离子表面活性剂,作为上述阴离子表面活性剂,可以举出1)十三烷基磺酸钠、十二烷基苯磺酸钠等有机磺酸盐,2)聚氧乙烯月桂基硫酸酯钠等有机硫酸酯盐,3)辛基磷酸酯钠盐、聚氧乙烯月桂基磷酸酯钾盐、油基磷酸酯三乙醇胺盐、聚氧乙烯月桂基磷酸酯-聚氧乙烯月桂基胺盐等有机磷酸酯盐,4)辛酸钾、油酸钠、烯基琥珀酸钾等有机脂肪酸盐等,其中,优选为有机磷酸酯盐,更优选为选自碳原子数为4~26的脂肪族单或二烷基磷酸酯金属盐、碳原子数为4~26的聚氧化烯脂肪族单或二烷基磷酸酯金属盐、碳原子数为4~26的脂肪族单或二烷基磷酸酯有机胺盐以及碳原子数为4~26的聚氧化烯脂肪族单或二烷基磷酸酯有机胺盐中的1种或2种以上。
本发明涉及的处理剂包含上述含有异氰脲酸衍生物的润滑剂、乳化剂和抗静电剂,异氰脲酸衍生物的含量为处理剂总量的5~45质量%、优选为处理剂总量的7~35质量%、更优选为处理剂总量的9~27质量%,含有上述异氰脲酸衍生物的润滑剂的含量为处理剂总量的5~75质量%、优选为处理剂总量的7~75质量%、更优选为处理剂总量的9~75质量%,乳化剂的含量为处理剂总量的21~94质量%、优选为处理剂总量的40~85质量%、更优选为处理剂总量的49~80质量%,抗静电剂为处理剂总量的0.1~10质量%、优选为处理剂总量的0.3~6质量%、更优选为处理剂总量的0.4~4质量%。
使本发明涉及的处理剂附着于合成纤维时,可以与本发明涉及的处理剂一起,根据目的并用其它的成分,例如,外观调整剂、抗氧化剂、耐热性提高剂、消泡剂、防腐剂、防锈剂等,其并用量尽可能少。
接着对本发明涉及的处理方法进行说明。本发明涉及的处理方法中,使上述本发明涉及的处理剂以0.1~3质量%、优选0.5~1.5质量%附着于供给到热处理步骤的合成纤维长丝丝条。作为使本发明涉及的处理剂附着于合成纤维上的步骤,可以举出纺丝步骤、拉伸步骤、同时进行纺丝和拉伸的步骤等。此外,作为使本发明涉及的处理剂附着于合成纤维上的方法,可以举出辊上油法、使用计量泵的导辊上油法、浸渍上油法、喷雾上油法等。进一步地作为使本发明涉及的处理剂附着于合成纤维上的方式,可以举出水性液(水性液)、有机溶剂溶液、纯物质(ニ一ト)等,优选为水性液,更优选为本发明涉及的处理剂的5~30质量%水性液。附着本发明涉及的处理剂的水性液时,对于供给到热处理步骤的合成纤维长丝丝条,附着本发明涉及的处理剂0.1~3质量%、优选0.5~1.5质量%。
作为本发明涉及的处理方法的适用对象的合成纤维,可以举出1)聚对苯二甲酸乙二醇酯、聚对苯二甲酸丙二醇酯、聚乳酸酯等聚酯类纤维,2)尼龙6、尼龙66等聚酰胺类纤维,3)聚丙烯酸、变性聚丙烯腈(モダアクリル)等聚丙烯酸类纤维,4)聚乙烯、聚丙烯等聚烯烃类纤维,5)聚氨酯类纤维等,对其种类或用途不加限定,但是适用于在制丝步骤中处于高温且高接触压力的苛刻条件下的工业材料用合成纤维时,表现出来的效果高,其中,尤其是适用于聚酯类纤维或聚酰胺纤维时表现出来的效果高。
以上说明的本发明中,具有如工业材料用合成纤维那样,即使在高温且高接触压力的苛刻条件下制丝时,也可以抑制制丝步骤中的摆丝、绒毛和焦油的产生,从而防止丝强度降低的效果。
虽然下文为了对本发明的结构和效果进行具体的说明而举出实施例,但是本发明不被这些实施例所限定。而且,下文的实施例和比较例中,份指的是质量份、%指的是质量%。
[实施例]
试验分类1(处理剂的制备)
实施例1{处理剂(P-1)的制备}
将下述异氰脲酸衍生物(K-1)10份、下述润滑剂(L-1)20份、下述润滑剂(L-2)10份、下述乳化剂(E-1)50份、下述乳化剂(E-2)10份、下述抗静电剂(S-3)1份均匀混合,制备实施例1的处理剂(P-1)。
异氰脲酸衍生物(K-1):三(2-羟基乙基)异氰脲酸三丙酸酯
润滑剂(L-1):二油基硫代二丙酸酯
润滑剂(L-2):双酚A二月桂酸酯
乳化剂(E-1):相对于氢化蓖麻油1摩尔加成环氧乙烷(下文简称为EO)20摩尔而得到的聚氧化烯脂肪族多元酯化合物。
乳化剂(E-2):相对于蓖麻油1摩尔加成EO40摩尔而得到的聚氧化烯蓖麻油1摩尔和癸酸3摩尔的酯化合物。
抗静电剂(S-3):油基磷酸酯三乙醇胺盐
实施例2~68和比较例1~17{处理剂(P-2)~(P-68)和处理剂(R-1)~(R-17)的制备}
与处理剂(P-1)同样地操作,制备处理剂(P-2)~(P-68)和处理剂(R-1)~(R-17)。上述各例的处理剂的制备中所使用的成分的内容如表1~表5所示,此外上述各例制备的处理剂的内容如表6~表14所示。
[表1]
异氰脲酸衍生物 | |
种类 | 化合物名称 |
K-1 | 三(2-羟基乙基)异氰脲酸三丙酸酯 |
K-2 | 三(2-羟基乙基)异氰脲酸三油酸酯 |
K-3 | 三辛基三(2-羧基乙基)异氰脲酸酯 |
K-4 | 三油基三(2-羧基乙基)异氰脲酸酯 |
K-5 | 三(羟基甲基)异氰脲酸三月桂酸酯 |
K-6 | 三(2-羟基丙基)异氰脲酸三癸酸酯 |
K-7 | 异氰脲酸二(2-羟基丙基)三癸酸酯 |
K-8 | 三(2-羟基乙基)异氰脲酸三单辛基硫代二丙酸酯 |
K-9 | 二癸基异氰脲酸二(2-羧基乙基) |
K-10 | 三单甲基聚乙二醇三(2-羧基乙基)异氰脲酸酯 |
K-11 | 三(2-羟基乙基)异氰脲酸二油酸酯 |
K-12 | 三(2-羟基乙基)异氰脲酸单油酸酯 |
K-13 | 二油基三(2-羧基乙基)异氰脲酸酯 |
K-14 | 单油基三(2-羧基乙基)异氰脲酸酯 |
[表2]
异氰脲酸衍生物之外的润滑剂 | |
种类 | 化合物名称 |
L-1 | 二油基硫代二丙酸酯 |
L-2 | 双酚A二月桂酸酯 |
L-3 | 偏苯三酸三辛酯 |
L-4 | 菜籽油 |
L-5 | 油基油酸酯 |
L-6 | 季戊四醇四壬酸酯 |
L-7 | 30℃的粘度为3.2×10-5m2/s的矿物油 |
[表3]
乳化剂 | |
种类 | 化合物名称 |
E-1 | 相对于氢化蓖麻油1摩尔加成EO20摩尔而得到的聚氧化烯脂肪族多元酯化合物 |
E-2 | 相对于蓖麻油1摩尔加成EO40摩尔而得到的聚氧化烯蓖麻油1摩尔和癸酸3摩尔的酯化合物 |
E-3 | 在山梨糖醇四油酸酯1摩尔上加成EO25摩尔而得到的聚氧乙烯多元醇部分酯化合物 |
E-4 | 相对于氢化蓖麻油1摩尔加成EO20摩尔而得到的聚氧化烯氢化蓖麻油2摩尔、马来酸1摩尔和硬脂酸3摩尔的酯化合物 |
E-5 | 脱水山梨醇三油酸酯 |
E-6 | 甘油二油酸酯 |
E-7 | 在脱水山梨醇单油酸酯1摩尔上加成EO14摩尔而得到的聚氧乙烯多元醇部分酯化合物 |
E-8 | 在辛醇1摩尔上加成EO8摩尔而得到的醚一元醇 |
E-9 | 在乙二醇上以50/50(质量比)的比率无规状加成EO和PO而得到的聚醚二醇(数均分子量为1400) |
E-10 | 在油醇1摩尔上加成EO10摩尔而得到的醚一元醇 |
E-11 | 相对于双酚A1摩尔加成EO4摩尔而得到的双酚A的聚氧乙烯加成物1摩尔和月桂酸2摩尔的酯化合物 |
E-12 | 相对于1,6-己二醇1摩尔加成EO10摩尔而得到的聚氧乙烯加成物1摩尔和月桂酸2摩尔的酯化合物 |
E-13 | 二乙醇胺单油酰胺 |
E-14 | 二乙醇胺单油酰胺的EO15摩尔加成物 |
E-15 | 在壬基苯酚1摩尔上加成EO7摩尔而得到的醚一元醇 |
表3中,化合物的数均分子量为用东ソ一株式会社生产的HLC-8120GPC测定的值。
[表4]
抗静电剂 | |
种类 | 化合物名称 |
S-1 | 聚氧乙烯(EO=3)月桂基磷酸酯钾盐 |
S-2 | 聚氧乙烯(EO=6)油基磷酸酯二乙醇胺盐 |
S-3 | 油基磷酸酯三乙醇胺盐 |
S-4 | 油基磷酸酯钠盐 |
S-5 | 三癸基磺酸钠 |
S-6 | 十二碳烯基琥珀酸二钾 |
S-7 | 2-十七碳烯基-羟基乙基咪唑硫酸乙酯(2-ヘプタデセニル-ヒドロキシエチルイミダゾリウムエトサルフエ一ト) |
S-8 | 辛基二甲基乙酸铵 |
[表5]
并用成分 | |
种类 | 化合物名称 |
T-1 | 油醇 |
T-2 | 乙二醇 |
T-3 | 2,2’-亚甲基二(4-甲基-6-叔丁基苯酚) |
T-4 | 聚氧乙烯改性硅氧烷 |
T-5 | 硬脂酸 |
[表6]
分类 | 实施例 | ||||||||||
1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | ||
种类 | P-1 | P-2 | P-3 | P-4 | P-5 | P-6 | P-7 | P-8 | P-9 | P-10 | |
异氰脲酸衍生物 | K-1K-2K-3K-4K-5K-6K-7K-8K-9K-10K-11K-12K-13K-14 | 10 | 24.5 | 24.5 | 20 | 14 | 15 | 18 | 7 | 30 | 10 |
其它的润滑剂 | L-1L-2L-3L-4L-5L-6L-7 | 209 | 5 | 9.515 | 520 | 15 | 1015 | 181010 | 55 | 151210 | |
乳化剂 | E-1E-2E-3E-4E-5E-6E-7E-8E-9E-10E-11E-12E-13E-14E-15 | 5010 | 101432145 | 141026614 | 2071315 | 253106106 | 30861410 | 2051020 | 2016810 | 205101410 | 2041810 |
抗静电剂 | S-1S-2S-3S-4S-5S-6S-7S-8 | 1 | 0.5 | 0.5 | 0.5 | 1 | 2 | 2 | 1 | 1 | 1 |
并用成分 | T1T2T3T4T-5 |
[表7]
分类 | 实施例 | ||||||||||
11 | 12 | 13 | 14 | 15 | 16 | 17 | 18 | 19 | 20 | ||
种类 | P-11 | P-12 | P-13 | P-14 | P-15 | P-16 | P-17 | P-18 | P-19 | P-20 | |
异氰脲酸衍生物 | K-1K-2K-3K-4K-5K-6K-7K-8K-9K-10K-11K-12K-13K-14 | 24 | 10 | 27 | 17 | 24 | 20 | 22 | 20 | 146 | 812 |
其它的润滑剂 | L-1L-2L-3L-4L-5L-6L-7 | 920 | 208610 | 1030 | 1036 | 176 | 1017 | 1015 | 1220 | 2012 | 81212 |
乳化剂 | E-1E-2E-3E-4E-5E-6E-7E-8E-9E-10E-11E-12E-13E-14E-15 | 20616 | 141714 | 13108 | 81012 | 20510610 | 151010610 | 15101610 | 101010105 | 10151010 | 13610107 |
抗静电剂 | S-1S-2S-3S-4S-5S-6S-7S-8 | 41 | 1 | 2 | 34 | 2 | 11 | 2 | 111 | 111 | 11 |
并用成分 | T-1T-2T-3T-4T-5 | 1 | 2 |
[表8]
分类 | 实施例 | ||||||||||
21 | 22 | 23 | 24 | 25 | 26 | 27 | 28 | 29 | 30 | ||
种类 | P-21 | P-22 | P-23 | P-24 | P-25 | P-26 | P-27 | P-28 | P-29 | P-30 | |
异氰脲酸衍生物 | K-1K-2K-3K-4K-5K-6K-7K-8K-9K-10K-11K-12K-13K-14 | 1012 | 20 | 16 | 10 | 10 | 17.8 | 24 | 168 | 146 | 104 |
其它的润滑剂 | L-1L-2L-3L-4L-5L-6L-7 | 2210 | 20410 | 81410 | 3410 | 201212 | 20620 | 23 | 1018 | 2416 | |
乳化剂 | E-1E-2E-3E-4E-5E-6E-7E-8E-9E-10E-11E-12E-13E-14E-15 | 201510 | 101010105 | 2021214 | 161612 | 201014 | 16614 | 2010156 | 201018206 | 2030 | 2021210 |
抗静电剂 | S-1S-2S-3S-4S-5S-6S-7S-8 | 1 | 1 | 121 | 2 | 11 | 0.2 | 2 | 11 | 2 | 2 |
并用成分 | T-1T-2T-3T-4T-5 | 1 | 0.5 |
[表9]
分类 | 实施例 | ||||||||||
31 | 32 | 33 | 34 | 35 | 36 | 37 | 38 | 39 | 40 | ||
种类 | P-31 | P-32 | P-33 | P-34 | P-35 | P-36 | P-37 | P-38 | P-39 | P-40 | |
异氰脲酸衍生物 | K-1K-2K-3K-4K-5K-6K-7K-8K-9K-10K-11K-12K-13K-14 | 15.9 | 66 | 12 | 88 | 104 | 12 | 104 | 66 | 10.95 | 15.9 |
其它的润滑剂 | L-1L-2L-3L-4L-5L-6L-7 | 45 | 52013 | 10235 | 533 | 5530 | 41216 | 1618 | 830 | 102015 | 162010 |
乳化剂 | E-1E-2E-3E-4E-5E-6E-7E-8E-9E-10E-11E-12E-13E-14E-15 | 191010 | 12611145 | 54121314 | 101010104 | 128888 | 1441620 | 14410126 | 10101414 | 1010145 | 184664 |
抗静电剂 | S-1S-2S-3S-4S-5S-6S-7S-8 | 0.1 | 11 | 11 | 11 | 11 | 11 | 6 | 2 | 0.1 | 0.1 |
并用成分 | T-1T-2T-3T-4T-5 |
[表10]
分类 | 实施例 | ||||||||||
41 | 42 | 43 | 44 | 45 | 46 | 47 | 48 | 49 | 50 | ||
种类 | P-41 | P-42 | P-43 | P-44 | P-45 | P-46 | P-47 | P-48 | P-49 | P-50 | |
异氰脲酸衍生物 | K-1K-2K-3K-4K-5K-6K-7K-8K-9K-10K-11K-12K-13K-14 | 10.95 | 6 | 41 | 9 | 1017 | 9 | 105 | 8 | 201068 | 6 |
其它的润滑剂 | L-1L-2L-3L-4L-5L-6I-7 | 46 | 1415 | 6 | 20714 | 15105 | 4 | 106 | 2 | 2 | 10330 |
乳化剂 | E-1E-2E-3E-4E-5E-6E-7E-8E-9E-10E-11E-12E-13E-14E-15 | 1820 | 251010810 | 255616 | 207814 | 18156 | 25510201016 | 201051610 | 2014201020 | 151617 | 1512145 |
抗静电剂 | S-1S-2S-8S-4S-5S-6S-7S-8 | 0.1 | 2 | 2 | 1 | 211 | 1 | 3821 | 411 | 411 | 14 |
并用成分 | T-1T-2T-3T-4T-5 | 0.5 |
[表11]
分类 | 实施例 | ||||||||||
51 | 52 | 53 | 54 | 55 | 56 | 57 | 58 | 59 | 60 | ||
种类 | P-51 | P-52 | P-53 | P-54 | P-55 | P-56 | P-57 | P-58 | P-59 | P-60 | |
异氰脲酸衍生物 | K-1K-2K-3K-4K-5K-6K-7K-8K-9K-10K-11K-12K-13K-14 | 6 | 5 | 12 | 27.6 | 16.920 | 1510 | 8 | 5 | 12 | 25 |
其它的润滑剂 | L-1L-2L-3L-4L-5L-6L-7 | 2033 | 103017 | 620 | 61114 | 52115 | 20 | 2 | 60 | 8513 | 20 |
乳化剂 | E-1E-2E-3E-4E-5E-6E-7E-8E-9E-10E-11E-12E-13E-14E-15 | 151010 | 256 | 15515520 | 1261472 | 22 | 111625 | 14202030 | 28 | 2510620 | 11161014 |
抗静电剂 | S-1S-2S-3S-4S-5S-6S-7S-8 | 1212 | 223 | 11 | 0.4 | 0.1 | 3 | 24 | 7 | 1 | 4 |
并用成分 | T-1T-2T-3T-4T-5 | 0.5 |
[表12]
分类 | 实施例 | ||||||||
61 | 62 | 63 | 64 | 65 | 66 | 67 | 68 | ||
种类 | P-61 | P-62 | P-63 | P-64 | P-65 | P-66 | P-67 | P-68 | |
异氰脲酸衍生物 | K-1K-2K-3K-4K-5K-6K-7K-8K-9K-10K-11K-12K-13K-14 | 8 | 5 | 14 | 20 | 1015 | 14 | 18 | 1015 |
其它的润滑剂 | L-1L-2L-3L-4L-5L-6L-7 | 2 | 57 | 204 | 1510 | 812 | 1016 | 22 | 20 |
乳化剂 | E-1E-2E-3E-4E-5E-6E-7E-8E-9E-10E-11E-12E-13E-14E-15 | 201450 | 2011 | 146830 | 2612105 | 2210O510 | 16141216 | 20161210 | 10101420 |
抗静电剂 | S-1S-2S-3S-4S-5S-6S-7S-8 | 321 | 7 | 112 | 21 | 21 | 2 | 2 | 1 |
并用成分 | T-1T-2T-3T-4T-5 |
[表13]
分类 | 比较例 | ||||||||||
1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | ||
种类 | R-1 | R-2 | R-8 | R-4 | R-5 | R-6 | R-7 | R-8 | R-9 | R-10 | |
异氰脲酸衍生物 | K-1K-2K-3K-4K-5K-6K-7K-8K-9K-10K-11K-12K-13K-14 | 3020 | 6.5 | 201210 | 2.4 | 16 | 14 | 45 | 2025 | 30 | |
其它的润滑剂 | L-1L-2L-3L-4L-5L-6L-7 | 209 | 9 | 17550 | 1022 | 50 | 5207 | 53 | 53-5 | 55 | |
乳化剂 | E-1E-2E-3E-4E-5E-6E-7E-8E-9E-10E-11E-12E-13E-14E-15 | 34212515 | 818104 | 156 | 108 | 2030207.520 | 51415 | 58820 | 2 | 1.5 | 5 |
抗静电剂 | S-1S-2S-3S-4S-5S-6S-7S-8 | 12 | 1 | 0.5 | 8 | 0.1 | 13 | 433 | |||
并用成分 | T-1T-2T-3T-4T-5 | 12 | 12.5 |
[表14]
分类 | 比较例 | |||||||
11 | 12 | 13 | 14 | 15 | 16 | 17 | ||
种类 | R-11 | R-12 | R-13 | R-14 | R-15 | R-16 | R-17 | |
异氰脲酸衍生物 | K-1K-2K-3K-4K-5K-6K-7K-8K-9K-10K-11K-12K-13K-14 | 3030 | 100 | 20 | 20 | |||
其它的润滑剂 | L-1L-2L-3L-4L-5L-6L-7 | 30 | 525 | |||||
乳化剂 | E-1E-2E-3E-4E-5E-6E-7E-8E-9E-10E-11E-12E-13E-14E-15 | 207125 | 10203012820 | 2251310 | 3010251510 | |||
抗静电剂 | S-1S-2S-3S-4S-5S-6S-7S-8 | 0.5 | 40152025 | 201515 | 433 | |||
并用成分 | T-1T-2T-3T-4T-5 |
试验分类2(各处理剂在合成纤维上的附着以及评价)
各处理剂在合成纤维上的附着
将由试验分类1制备的各处理剂和稀释水或稀释有机溶剂均匀混合,制成10%稀释溶液。对特性粘度为1.10、羧基末端浓度为15当量/106g的聚对苯二甲酸乙二醇酯的切片(チツプ)通过常规方法进行干燥后,使用挤出机在295℃下纺丝,在从喷丝头吐出并冷却固化后的移动丝条上,通过使用计量泵进行的导辊上油法附着所制备的10%稀释溶液,然后用导辊集束、用表面速度3000m/分钟的牵引辊牵引,然后通过240℃的拉伸辊、松弛辊进行拉伸至总拉伸倍率为1.7倍,以10kg丝饼的形式得到1670dtex 192长丝的拉伸丝。
处理剂的附着量的测定
根据JIS-L1073(合成纤维长丝试验方法),使用正己烷/乙醇(50/50体积比)混合溶剂作为萃取溶剂,测定处理剂在合成纤维上的附着量。结果如表15~17所示。
摆丝的评价
在上述纺丝步骤中,目视对在拉伸辊上产生的移动丝的摆动程度进行观察,按下述基准进行评价。结果如表15~表17所示。
AAA:未产生摆丝
AA:几乎未产生摆丝
A:偶尔产生摆丝
B:频繁产生摆丝
C:摆丝的产生显著、相邻的丝之间相接触
绒毛的评价
在上述纺丝步骤中,在将丝卷取成丝饼前,用绒毛计数装置(东レエンジニアリング公司生产的DT-105)对每1小时的绒毛数进行测定,按下述基准进行评价。结果如表15~表17所示。
AAA:测定的绒毛数为0个
AA:测定的绒毛数小于1个(但是不包括0)
A:测定的绒毛数为1~2个
B:测定的绒毛数为3~9个
C:测定的绒毛数为10个以上
焦油防止性的评价
将由上述得到的丝饼采取的试验丝以初期张力1kg、丝速度500m/分钟卷缠于表面温度240℃的热辊上使其移动,肉眼对产生于热辊上的12小时后的焦油的量进行观察,按下述基准进行评价。结果如表15~表17所示。
AAA:未发现焦油。
AA:稍有焦油。
A:发现少量的焦油。
B:明显发现焦油。
C:发现大量的焦油。
丝强度的评价
对于由上述得到的丝饼采取的试验丝的强度,用强度测定装置(岛津制作所社生产的岛津オ一トグラフAGS-1KNG)进行测定,按下述基准进行评价。结果如表15~表17所示。
AAA:测得的丝强度为8.0cN/dtex以上
AA:测得的丝强度为7.8以上而小于8.0cN/dtex
A:测得的丝强度为7.4以上而小于7.8cN/dtex
B:测得的丝强度为7.0以上而小于7.4cN/dtex
C:测得的丝强度小于7.0cN/dtex
[表15]
分类 | 处理剂 | 评价 | |||||
种类 | 赋予方式 | 附着量(%) | 摆丝 | 绒毛 | 焦油防止性 | 丝强度 | |
实施例69707172737475767778798081828384858687888990919293949596979899100101102 | P-1P-2P-3P-4P-5P-6P-7P-8P-9P-10P-11P-12P-13P-14P-15P-16P-17P-18P-19P-20P-21P-22P-23P-24P-25P-26P-27P-28P-29P-30P-31P-32P-33P-34 | 水性液水性液水性液水性液水性液水性液水性液水性液水性液水性液水性液水性液纯物质纯物质水性液水性液水性液水性液水性液水性液有机溶剂溶液有机溶剂溶液水性液水性液纯物质纯物质有机溶剂溶液水性液水性液水性液有机溶剂溶液水性液水性液有机溶剂溶液 | 0.80.80.80.61.00.80.80.80.81.00.80.81.00.80.80.80.80.80.80.80.70.81.20.80.81.40.80.81.00.80.80.81.00.8 | AAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAA | AAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAA | AAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAA | AAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAA |
[表16]
分类 | 处理剂 | 评价 | |||||
种类 | 赋予方式 | 附着量(%) | 摆丝 | 绒毛 | 焦油防止性 | 丝强度 | |
实施例103104105106107108109110111112113114115116117118119120121122123124125126127128129130131132133134135136 | P-35P-36P-37P-38P-39P-40P-41P-42P-43P-44P-45P-46P-47P-48P-40P-50P-51P-52P-53P-54P-55P-56P-57P-58P-59P-60P-61P-62P-63P-64P-65P-66P-67P-68 | 水性液纯物质水性液水性液有机溶剂溶液纯物质纯物质水性液水性液水性液有机溶剂溶液水性液水性液水性液水性液水性液有机溶剂溶液有机溶剂溶液水性液水性液纯物质水性液水性液纯物质水性液水性液水性液纯物质水性液水性液水性液水性液水性液水性液 | 0.80.80.80.80.80.80.60.80.80.81.20.80.90.80.81.00.80.80.80.80.60.80.80.80.61.00.80.80.80.80.80.80.80.8 | AAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAA | AAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAA | AAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAA | AAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAA |
[表17]
分类 | 处理剂 | 评价 | |||||
种类 | 赋予方式 | 附着量(%) | 摆丝 | 绒毛 | 焦油防止性 | 丝强度 | |
比较例181920212223242526272829303132333435 | R-1R-2R-3R-4R-5R-6R-7R-8R-9R-10R-11R-12R-12R-13R-14R-15R-16R-17 | 水性液有机溶剂溶液纯物质纯物质水性液有机溶剂溶液纯物质纯物质纯物质纯物质水性液水性液纯物质水性液水性液水性液水性液水性液 | 0.80.80.80.80.80.80.80.81.00.80.80.80.80.80.80.80.80.8 | CBCBBCCCCCBCCCCCCC | BCBCCCCCCCCCCCCCCC | CBCBCBCBBCBCCCCBCC | CCBCCCCCCCCCCCCCCC |
表15~17中,赋予方式列的有机溶剂溶液的有机溶剂是40℃下的粘度为2.0×10-6m2/s的正烷烃。
Claims (24)
1.合成纤维用处理剂,其含有润滑剂、乳化剂和抗静电剂,其特征在于,润滑剂的含量为处理剂总量的5~75质量%、乳化剂的含量为处理剂总量的21~94质量%、抗静电剂的含量为处理剂总量的0.1~10质量%,且含有处理剂总量的5~45质量%的下述异氰脲酸衍生物作为润滑剂的至少一部分,
异氰脲酸衍生物:选自三(羟基甲基)异氰脲酸和有机单羧酸的部分或完全酯化合物、三(2-羟基乙基)异氰脲酸和有机单羧酸的部分或完全酯化合物、三(2-羟基丙基)异氰脲酸和有机单羧酸的部分或完全酯化合物、异氰脲酸二(2-羟基丙基)和有机单羧酸的部分或完全酯化合物、三(2-羧基乙基)异氰脲酸和一价脂肪族羟基化合物的部分或完全酯化合物、以及异氰脲酸二(2-羧基乙基)和一价脂肪族羟基化合物的部分或完全酯化合物中的1种或2种以上。
2.如权利要求1所述的合成纤维用处理剂,其中,所述异氰脲酸衍生物为选自三(羟基甲基)异氰脲酸和有机单羧酸的完全酯化合物、三(2-羟基乙基)异氰脲酸和有机单羧酸的完全酯化合物、三(2-羟基丙基)异氰脲酸和有机单羧酸的完全酯化合物、异氰脲酸二(2-羟基丙基)和有机单羧酸的完全酯化合物、三(2-羧基乙基)异氰脲酸和一价脂肪族羟基化合物的完全酯化合物、以及异氰脲酸二(2-羧基乙基)和一价脂肪族羟基化合物的完全酯化合物中的1种或2种以上。
3.如权利要求1所述的合成纤维用处理剂,其中,所述异氰脲酸衍生物为选自三(2-羟基乙基)异氰脲酸和有机单羧酸的完全酯化合物、以及三(2-羧基乙基)异氰脲酸和一价脂肪族羟基化合物的完全酯化合物中的1种或2种以上。
4.如权利要求1所述的合成纤维用处理剂,其中,有机单羧酸是碳原子数为2~22的脂肪族单羧酸、一价脂肪族羟基化合物是碳原子数为1~26的脂肪族一元醇。
5.如权利要求3所述的合成纤维用处理剂,其中,有机单羧酸是碳原子数为2~22的脂肪族单羧酸、一价脂肪族羟基化合物是碳原子数为1~26的脂肪族一元醇。
6.如权利要求1所述的合成纤维用处理剂,其中,异氰脲酸衍生物之外的润滑剂为选自脂肪族酯化合物、芳香族酯化合物和动植物油脂类中的1种或2种以上。
7.如权利要求5所述的合成纤维用处理剂,其中,异氰脲酸衍生物之外的润滑剂为选自脂肪族酯化合物、芳香族酯化合物和动植物油脂类中的1种或2种以上。
8.如权利要求7所述的合成纤维用处理剂,其中,所述脂肪族酯化合物为选自二元或三元脂肪族多元醇和脂肪族单羧酸的完全酯化合物、以及脂肪族一元醇和二元或三元脂肪族多元羧酸的完全酯化合物中的1种或2种以上,所述芳香族酯化合物为选自二元或三元芳香族多元醇和脂肪族单羧酸的完全酯化合物、以及脂肪族一元醇和二元或三元芳香族多元羧酸的完全酯化合物中的1种或2种以上。
9.如权利要求1所述的合成纤维用处理剂,其中,所述乳化剂为选自在分子中具有聚氧亚烷基的醚型非离子表面活性剂、多元醇部分酯型非离子表面活性剂、聚氧化烯多元醇脂肪酸酯型非离子表面活性剂、酰胺型非离子表面活性剂和聚氧化烯脂肪酸酰胺型非离子表面活性剂中的1种或2种以上。
10.如权利要求1所述的合成纤维用处理剂,其中,所述乳化剂为选自多元醇部分酯型非离子表面活性剂、以及聚氧化烯多元醇脂肪酸酯型非离子表面活性剂中的1种或2种以上,该多元醇选自甘油、蓖麻油、氢化蓖麻油、脱水山梨醇和山梨糖醇。
11.如权利要求8所述的合成纤维用处理剂,其中,所述乳化剂为选自多元醇部分酯型非离子表面活性剂、以及聚氧化烯多元醇脂肪酸酯型非离子表面活性剂中的1种或2种以上,该多元醇选自甘油、蓖麻油、氢化蓖麻油、脱水山梨醇和山梨糖醇。
12.如权利要求1所述的合成纤维用处理剂,其中,所述抗静电剂为选自有机磺酸盐、有机硫酸酯盐、有机磷酸酯盐和有机脂肪酸盐中的1种或2种以上。
13.如权利要求1所述的合成纤维用处理剂,其中,所述抗静电剂为选自有机磷酸酯盐的1种或2种以上,该有机磷酸酯盐选自碳原子数为4~26的脂肪族单或二烷基磷酸酯金属盐、碳原子数为4~26的聚氧化烯脂肪族单或二烷基磷酸酯金属盐、碳原子数为4~26的脂肪族单或二烷基磷酸酯有机胺盐以及碳原子数为4~26的聚氧化烯脂肪族单或二烷基磷酸酯有机胺盐。
14.如权利要求11所述的合成纤维用处理剂,其中,所述抗静电剂为选自有机磷酸酯盐的1种或2种以上,该有机磷酸酯盐选自碳原子数为4~26的脂肪族单或二烷基磷酸酯金属盐、碳原子数为4~26的聚氧化烯脂肪族单或二烷基磷酸酯金属盐、碳原子数为4~26的脂肪族单或二烷基磷酸酯有机胺盐以及碳原子数为4~26的聚氧化烯脂肪族单或二烷基磷酸酯有机胺盐。
15.如权利要求1所述的合成纤维用处理剂,其中,含有处理剂总量的7~75质量%的润滑剂、处理剂总量的40~85质量%的乳化剂和处理剂总量的0.3~6质量%的抗静电剂,且含有处理剂总量的7~35质量%的异氰脲酸衍生物作为润滑剂的至少一部分。
16.如权利要求14所述的合成纤维用处理剂,其中,含有处理剂总量的7~75质量%的润滑剂、处理剂总量的40~85质量%的乳化剂和处理剂总量的0.3~6质量%的抗静电剂,且含有处理剂总量的7~35质量%的异氰脲酸衍生物作为润滑剂的至少一部分。
17.一种合成纤维的处理方法,其特征在于,使权利要求1所述的合成纤维用处理剂以0.1~3质量%附着于供给到热处理步骤的合成纤维长丝丝条。
18.一种合成纤维的处理方法,其特征在于,使权利要求16所述的合成纤维用处理剂以0.1~3质量%附着于供给到热处理步骤的合成纤维长丝丝条。
19.如权利要求17所述的合成纤维的处理方法,其中,将合成纤维用处理剂制成5~30质量%的水性液,使该水性液以0.1~3质量%附着于供给到热处理步骤的合成纤维长丝丝条。
20.如权利要求18所述的合成纤维的处理方法,其中,将合成纤维用处理剂制成5~30质量%的水性液,使该水性液以0.1~3质量%附着于供给到热处理步骤的合成纤维长丝丝条。
21.如权利要求17所述的合成纤维的处理方法,其中,合成纤维为工业材料用合成纤维。
22.如权利要求20所述的合成纤维的处理方法,其中,合成纤维为工业材料用合成纤维。
23.如权利要求21所述的合成纤维的处理方法,其中,工业材料用合成纤维为聚酯类纤维或聚酰胺类纤维。
24.如权利要求22所述的合成纤维的处理方法,其中,工业材料用合成纤维为聚酯类纤维或聚酰胺类纤维。