CN101128296A - 可发性聚苯乙烯微球的制备方法 - Google Patents
可发性聚苯乙烯微球的制备方法 Download PDFInfo
- Publication number
- CN101128296A CN101128296A CNA200680005553XA CN200680005553A CN101128296A CN 101128296 A CN101128296 A CN 101128296A CN A200680005553X A CNA200680005553X A CN A200680005553XA CN 200680005553 A CN200680005553 A CN 200680005553A CN 101128296 A CN101128296 A CN 101128296A
- Authority
- CN
- China
- Prior art keywords
- static mixer
- polymer
- temperature
- blowing agent
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
序号 | MFI/Mw×10-5 | Gp/GEA | 静态混合器中的温度,℃ | 最终产品中发泡剂含量,重量% | 粒径 | 产品的填充密度,kg/m3 | ||
第一 | 第二 | 第三 | ||||||
1. | 0.80 | 19.0 | 216 | 195 | 175 | 5.0 | 0.7..0.9 | 30...55 |
2. | 1.93 | 17.2 | 212 | 190 | 165 | 5.5 | 0.7..0.9 | 25...45 |
3. | 2.96 | 14.4 | 204.5 | 181 | 156 | 6.5 | 1.4..2.0 | 15...35 |
4. | 4.49 | 13.4 | 201 | 176 | 151 | 6.9 | 0.9..1.4 | 12...25 |
5. | 6.82 | 15.1 | 206 | 183 | 158 | 6.2 | 0.9..1.4 | 25...35 |
6. | 12.0 | 13.3 | 200 | 175 | 150 | 7.0 | 1.4..2.0 | 15...25 |
7. | 8.75 | 14.4 | 204.5 | 181 | 156 | 6.5 | 0.9..1.4 | 16...35 |
8. | 2.23 | 14.4 | 204.5 | 181 | 156 | 6.5 | 0.7..0.9 | 25...40 |
Claims (4)