CN101077928A - 无卤阻燃热塑性工程塑料 - Google Patents

无卤阻燃热塑性工程塑料 Download PDF

Info

Publication number
CN101077928A
CN101077928A CN 200610026804 CN200610026804A CN101077928A CN 101077928 A CN101077928 A CN 101077928A CN 200610026804 CN200610026804 CN 200610026804 CN 200610026804 A CN200610026804 A CN 200610026804A CN 101077928 A CN101077928 A CN 101077928A
Authority
CN
China
Prior art keywords
flame retardant
thermoplastic engineering
engineering plastic
nylon
glass fibre
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200610026804
Other languages
English (en)
Inventor
陈宝勋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI NYTEX COMPOSITES PRODUCT CO Ltd
Original Assignee
SHANGHAI NYTEX COMPOSITES PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI NYTEX COMPOSITES PRODUCT CO Ltd filed Critical SHANGHAI NYTEX COMPOSITES PRODUCT CO Ltd
Priority to CN 200610026804 priority Critical patent/CN101077928A/zh
Publication of CN101077928A publication Critical patent/CN101077928A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种无卤阻燃热塑性工程塑料，包括尼龙66树脂、玻璃纤维、阻燃剂体系、抗氧化剂，所述的尼龙66树脂为200－700重量份，所述的玻璃纤维为100－500重量份，所述的阻燃剂体系包括重量份为50－300的含磷阻燃剂与重量份为10－300的矿物阻燃剂，所述的抗氧化剂为重量份为1－10的受阻酚类主抗氧剂。与现有技术相比，本发明具有较高的CTI，在燃烧时具有发烟量低、毒性小等优点，有利于环境保护。

Description

无卤阻燃热塑性工程塑料
技术领域
本发明涉及一种阻燃热塑性组合物，尤其涉及一种无卤阻燃热塑性工程塑料。
背景技术
用于家用电器开关和电动工具外壳等材料的热塑性材料对耐热防火有一定的要求。而尼龙66树脂本身为一种易燃的高分子材料，燃烧时会释放出大量烟雾和有害气体，以致于在燃烧过程中导致“二次灾害”。例如：尼龙66材料为1/8″UL-V2级，极限氧指数为28.3。这样使得尼龙66在电子电器方面的应用受到一定限制。
目前，改善尼龙66阻燃性能最常用的方法是添加含卤阻燃剂。卤系阻燃剂的成本效能平衡好，适应面广，但是由于发烟量大，释放出的气体具有高腐蚀性，而且溴系阻燃剂在特定的条件下分解出多溴代二苯并二噁烷(PBDD)和多溴代二苯并呋喃(PBDF)物质，它们有较强的致癌作用。为此，传统的含卤阻燃剂面临着巨大的环境压力，非卤化已经成为阻燃开发应用的主要趋势。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种燃烧时发烟量低、毒性小、有利于环保的无卤阻燃热塑性工程塑料。
本发明的目的可以通过以下技术方案来实现：无卤阻燃热塑性工程塑料，其特征在于，包括尼龙66树脂、玻璃纤维、阻燃剂体系、抗氧化剂，所述的尼龙66树脂为200-700重量份，所述的玻璃纤维为100-500重量份，所述的阻燃剂体系包括重量份为50-300的含磷阻燃剂与重量份为10-300的矿物阻燃剂，所述的抗氧化剂为重量份为1-10的受阻酚类主抗氧剂。
所述的尼龙66树脂选自己二胺和己二酸通过直接或间接法缩聚生成的共聚物、尼龙66纱线经过挤出机制得的尼龙切片中的一种或两种。
所述的玻璃纤维选自二氧化硅、三氧化硼、三氧化铝、氧化钙、氧化钠、氧化钾的一种或几种作为主要成分的纤维状物质。
所述的纤维状物质包括无碱玻璃纤维、E-玻璃纤维或C-玻璃纤维。
所述的含磷阻燃剂选自无机磷酸盐、有机磷酸盐、磷-氮化合物以及红磷中的一种或几种。
所述的含磷阻燃剂包括聚磷酸铵、磷酸二氢铵、焦磷酸三铵、磷酸酯、氧化膦或红磷浓缩母。
所述的矿物阻燃剂选自硅酸钙、硅酸铁、硅酸铝、硅酸镁、硅酸锰的一种或几种为主要成分。
还包括稳定剂、润滑剂、脱模剂、成核剂、抗静电剂以及颜料中的一种或几种。
本发明采用以磷或磷化物为主的无卤阻燃体系对尼龙66热塑性树脂进行阻燃改性，运用本发明所述配方共混而成的材料不仅具有优异的阻燃性能和耐电压性，而且燃烧时具有发烟量低、毒性小等优点，有利于环境保护。
具体实施方式
以下是按照本发明技术方案提供的配方所作的实施例，用以进一步解释本发明。
实施例1
  组分   重量份数
  尼龙66   323
  玻璃纤维   500
  红磷   120
  硅酸钙   30
  Irganox 1010   2
  黑色母   20
  色份   5
注：Irganox 1010为汽巴公司抗氧剂。
所得共混物材料的测试结果如下美标(ASTM)：
  抗张强度(MPa)   180
  抗折强度(MPa)   260
  抗折弹性系数(MPa)   15000
  Izod缺口冲击强度(KJ/m2)   11
  阻燃性UL94(1.6mm)   V0
  相对漏电起痕指数(CTI)   600
可以看出，本发明的阻燃体系与尼龙66树脂共混得到的材料，有较好的阻燃性和较高的CTI值。
实施例2
  组分   重量份数
  尼龙66   393
  玻璃纤维   400
  红磷   150
  硅酸钙   30
  Irganox 1010   2
  黑色母   20
  色份   5
所得共混组合物材料的测试结果如下(ASTM)：
  抗张强度(MPa)   160
  抗折强度(MPa)   240
  抗折弹性系数(MPa)   13000
  Izod缺口冲击强度(KJ/m2)   10
  阻燃性UL94(1.6mm)   V0
  相对漏电起痕指数(CTI)   600
可以看出，本发明的阻燃体系与尼龙66树脂共混得到的材料，有较好的阻燃性和较高的CTI值。
实施例3
  组分   重量份数
  尼龙66   235
  无碱玻璃纤维   300
  聚磷酸铵   300
  硅酸镁   130
  Irganox 1010   10
  黑色母   20
  色份   5
注：Irganox 1010为汽巴公司抗氧剂。
所得共混物材料的测试结果如下美标(ASTM)：
  抗张强度(MPa)   130
  抗折强度(MPa)   210
  抗折弹性系数(MPa)   10000
  Izod缺口冲击强度(KJ/m2)   9
  阻燃性UL94(1.6mm)   V0
  相对漏电起痕指数(CTI)   500
可以看出，本发明的阻燃体系与尼龙66树脂共混得到的材料，有较好的阻燃性和较高的CTI值。
实施例4
  组分   重量份数
  尼龙66   370
  E-玻璃纤维   200
  磷酸二氢铵   300
  硅酸铝   100
  Irganox 1010   5
  黑色母   20
  色份   5
所得共混组合物材料的测试结果如下(ASTM)：
  抗张强度(MPa)   100
  抗折强度(MPa)   160
  抗折弹性系数(MPa)   6000
  Izod缺口冲击强度(KJ/m2)   7
  阻燃性UL94(1.6mm)   V0
  相对漏电起痕指数(CTI)   500
可以看出，本发明的阻燃体系与尼龙66树脂共混得到的材料，有较好的阻燃性和较高的CTI值。

Claims (8)

1.无卤阻燃热塑性工程塑料，其特征在于，包括尼龙66树脂、玻璃纤维、阻燃剂体系、抗氧化剂，所述的尼龙66树脂为200-700重量份，所述的玻璃纤维为200-400重量份，所述的阻燃剂体系包括重量份为10-300的含磷阻燃剂与重量份为10-300的矿物阻燃剂，所述的抗氧化剂为重量份为1-10的受阻酚类主抗氧剂。
2.根据权利要求1所述的无卤阻燃热塑性工程塑料，其特征在于，所述的尼龙66树脂选自己二胺和己二酸通过直接或间接法缩聚生成的共聚物、尼龙66纱线经过挤出机制得的尼龙切片中的一种或两种。
3.根据权利要求1所述的无卤阻燃热塑性工程塑料，其特征在于，所述的玻璃纤维选自二氧化硅、三氧化硼、三氧化铝、氧化钙、氧化钠、氧化钾的一种或几种作为主要成分的纤维状物质。
4.根据权利要求3所述的无卤阻燃热塑性工程塑料，其特征在于，所述的纤维状物质包括无碱玻璃纤维、E-玻璃纤维或C-玻璃纤维。
5.根据权利要求1所述的无卤阻燃热塑性工程塑料，其特征在于，所述的含磷阻燃剂选自无机磷酸盐、有机磷酸盐、磷-氮化合物以及红磷中的一种或几种。
6.根据权利要求5所述的无卤阻燃热塑性工程塑料，其特征在于，所述的含磷阻燃剂包括聚磷酸铵、磷酸二氢铵、焦磷酸三铵、磷酸酯、氧化膦或红磷浓缩母。
7.根据权利要求1所述的无卤阻燃热塑性工程塑料，其特征在于，所述的矿物阻燃剂选自硅酸钙、硅酸铁、硅酸铝、硅酸镁、硅酸锰的一种或几种为主要成分。
8.根据权利要求1所述的无卤阻燃热塑性工程塑料，其特征在于，还包括稳定剂、润滑剂、脱模剂、成核剂、抗静电剂以及颜料中的一种或几种。
CN 200610026804 2006-05-23 2006-05-23 无卤阻燃热塑性工程塑料 Pending CN101077928A (zh)