CN101040631A - 金铃大枣保鲜专用膜、袋 - Google Patents
金铃大枣保鲜专用膜、袋 Download PDFInfo
- Publication number
- CN101040631A CN101040631A CNA2007100110251A CN200710011025A CN101040631A CN 101040631 A CN101040631 A CN 101040631A CN A2007100110251 A CNA2007100110251 A CN A2007100110251A CN 200710011025 A CN200710011025 A CN 200710011025A CN 101040631 A CN101040631 A CN 101040631A
- Authority
- CN
- China
- Prior art keywords
- film
- master batch
- jinling
- jujube
- fresh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种金铃大枣保鲜专用膜、袋,其特征在于生产的原料组分及重量份比例为:线性聚乙烯树脂(LLDPE)100、高压聚乙烯树脂(LDPE)50~100、乙烯-醋酸乙烯树脂(EVA)15~25、10%防雾滴母粒(MD/PE)5~10、20%含银抗菌母粒(Ag/PE)5~10、20%碳酸钙母粒(CaCO3/PE)5~15、油酸辛酯0.2~1。本发明的优点是具有O2和CO2双向调节能力,进行大枣小包装贮藏时,可利用自发气调原理,有效地调节气体指标,使之保持相对稳定的最佳状态,达到气调贮藏的结果和目的。有较好的防雾和透湿性能,可以保持(袋内)基本不结露。对O2、CO2、水蒸气、乙烯气体等有较强的吸附作用和透过能力。薄膜性能和结构稳定,可抗氧化和防老化。透明度、抗拉性、柔软性、开口性良好。
Description
技术领域
本发明属于农产品保鲜用品,特别是一种金铃大枣保鲜专用膜、袋。
背景技术
目前农产品保鲜技术有很多用品,如保鲜剂,保鲜膜。所有的保鲜剂和保鲜膜等保鲜用品对保鲜的对象都是有选择性使用的。不同品种的农产品要使用不同的保鲜用品。目前还没有针对金铃大枣保鲜的专用保鲜膜和保鲜袋。
发明内容
本发明的目的是提供一种金铃大枣保鲜专用膜、袋,适应金铃大枣贮藏保鲜使用。
本发明的技术方案是:生产大枣保鲜膜、袋原料组分及重量份比例为:
线性聚乙烯树脂(LLDPE) 100、
高压聚乙烯树脂(LDPE) 50~100、
乙烯-醋酸乙烯树脂(EVA) 15~25、
10%防雾滴母粒(MD/PE) 5~10、
20%含银抗菌母粒(Ag/PE) 5~10、
20%碳酸钙母粒(CaCO3/PE) 5~15、
油酸辛酯 0.2~1。
生产方法:按上述比例称配料,经塑料粒子混合机混匀后,采用单螺杆挤出吹塑机吹塑成膜或袋。
上述大枣保鲜膜、袋,其特征是:按原料组分最佳重量份比例为:
线性聚乙烯树脂(LLDPE) 100
高压聚乙烯树脂(LDPE) 50
乙烯-醋酸乙烯树脂(EVA) 20
10%防雾滴母粒(MD/PE) 8
20%含银抗菌母粒(Ag/PE) 7
20%碳酸钙母粒(CaCO3/PE) 10
油酸辛酯 0.6
按上述重量比配料,将所有配料经塑料粒子混合机混合均匀后,采用聚乙烯单螺杆挤出吹塑机吹塑成所需薄膜。
最后将薄膜按贮藏实际装量要求,采用工频热合方式,制成不同尺寸规格的袋。
本发明的优点:
(1)具有O2和CO2双向调节能力,进行大枣小包装贮藏时,可利用自发气调原理,有效地调节气体指标,使之保持相对稳定的最佳状态,达到气调贮藏的结果和目的。
(2)有较好的防雾和透湿性能,在贮藏期内虽有温度(<±3℃)波动,但可以保持(袋内)基本不结露。
(3)对O2、CO2、水蒸气、乙烯气体等有较强的吸附作用和透过能力。
(4)薄膜性能和结构稳定,可抗氧化和防老化。
(5)透明度、抗拉性、柔软性、开口性良好。
本发明应具备的性能指标:
拉伸强度(MPa)纵向/横向 | 断裂伸长率(%)纵向/横向 | O2透过率cm3/m2·d·0.1MPa | CO2透过率cm3/m2·d·0.1MPa | 水分渗透率g/m2·dy |
17~20/10~13 | 480~500/930~950 | >1×105 | >1×105 | 18~20 |
保鲜效果:金铃大枣专用保鲜膜贮藏效果(微红枣)
保鲜膜种类 | 膜厚度(mm) | 透气性 | 透湿性 | 结露性 | 贮藏时间(天) | O2/% | CO2/% | 好果率/% |
PE | 0.08 | 差 | 差 | 重 | 30 | 14.3 | 5.2 | 20 |
60 | 5.2 | 9.4 | 0 | |||||
90 | - | - | 0 | |||||
0.06 | 差 | 差 | 重 | 30 | 15.0 | 4.2 | 25 | |
60 | 7.4 | 8.2 | 0 | |||||
90 | - | - | 0 | |||||
0.04 | 一般 | 一般 | 稍微 | 30 | 16.2 | 3.8 | 30 | |
60 | 8.2 | 7.4 | 0 | |||||
90 | - | - | 0 | |||||
0.02 | 好 | 好 | 轻 | 30 | 18.2 | 2.4 | 38 | |
60 | 14.6 | 4.8 | 10 | |||||
90 | - | - | 0 | |||||
PVC | 0.05 | 一般 | 一般 | 稍微 | 30 | 17.8 | 2.6 | 41 |
60 | 14.2 | 4.6 | 5 |
90 | - | - | 0 | |||||
0.03 | 较好 | 较好 | 无 | 30 | 18.2 | 2.1 | 44 | |
60 | 12.4 | 4.0 | 7 | |||||
90 | - | - | 0 | |||||
金铃大枣贮藏专用袋 | 较好 | 较好 | 无 | 30 | 19.8 | 0.7 | 99 | |
60 | 19.6 | 1.1 | 95 | |||||
90 | - | - | 90 |
具体实施方式
实施例1
大枣贮藏保鲜专用膜制作原料组分按以下重量比:
线性聚乙烯树脂(LLDPE) 100公斤
高压聚乙烯树脂(LDPE) 50公斤
乙烯-醋酸乙烯树脂(EVA) 15公斤
10%防雾滴母粒(MD/PE) 5公斤
20%含银抗菌母粒(Ag/PE) 5公斤
20%碳酸钙母粒(CaCO3/PE) 5公斤
油酸辛酯 0.2公斤
按上述重量比配料,将所有配料经塑料粒子混合机混合均匀后,采用聚乙烯单螺杆挤出吹塑机吹塑成所需薄膜。
最后将薄膜按贮藏实际装量要求,采用工频热合方式,制成不同尺寸规格的袋。
实施例2
大枣贮藏保鲜专用膜制作原料组分按以下重量比:
线性聚乙烯树脂(LLDPE) 100公斤
高压聚乙烯树脂(LDPE) 100公斤
乙烯-醋酸乙烯树脂(EVA) 25公斤
10%防雾滴母粒(MD/PE) 10公斤
20%含银抗菌母粒(Ag/PE) 10公斤
20%碳酸钙母粒(CaCO3/PE) 15公斤
油酸辛酯 1.0公斤
按上述重量比配料,将所有配料经塑料粒子混合机混合均匀后,采用聚乙烯单螺杆挤出吹塑机吹塑成所需薄膜。
最后将薄膜按贮藏实际装量要求,采用工频热合方式,制成不同尺寸规格的袋。
实施例3
大枣贮藏保鲜专用膜制作原料组分按以下重量比(最佳配比):
线性聚乙烯树脂(LLDPE) 100公斤
高压聚乙烯树脂(LDPE) 50公斤
乙烯-醋酸乙烯树脂(EVA) 20公斤
10%防雾滴母粒(MD/PE) 8公斤
20%含银抗菌母粒(Ag/PE) 7公斤
20%碳酸钙母粒(CaCO3/PE) 10公斤
油酸辛酯 0.6公斤
按上述重量比配料,将所有配料经塑料粒子混合机混合均匀后,采用聚乙烯单螺杆挤出吹塑机吹塑成所需薄膜。
最后将薄膜按贮藏实际装量要求,采用工频热合方式,制成不同尺寸规格的袋。
经过五年的试验和中试,选出最佳金铃大枣贮藏保鲜专用膜,应用该膜,可使金铃大枣大半红枣贮75天以上、半红贮80天以上、微红枣贮藏90天以上仍鲜脆如初。
Claims (2)
1、一种金铃大枣保鲜专用膜、袋,其特征在于:生产的原料组分及重量份比例为:
线性聚乙烯树脂(LLDPE) 100、
高压聚乙烯树脂(LDPE) 50~100、
乙烯-醋酸乙烯树脂(EVA) 15~25、
10%防雾滴母粒(MD/PE) 5~10、
20%含银抗菌母粒(Ag/PE) 5~10、
20%碳酸钙母粒(CaCO3/PE) 5~15、
油酸辛酯 0.2~1。
2、根据权利要求1所述的金铃大枣保鲜专用膜、袋,其特征在于:生产的原料组分最佳重量比例为:
线性聚乙烯树脂(LLDPE) 100、
高压聚乙烯树脂(LDPE) 50、
乙烯-醋酸乙烯树脂(EVA) 20、
10%防雾滴母粒(MD/PE) 8、
20%含银抗菌母粒(Ag/PE) 7、
20%碳酸钙母粒(CaCO3/PE) 10、
油酸辛酯 0.6。