CN100538915C - 糊组合物及使用该糊组合物的太阳能电池元件 - Google Patents
糊组合物及使用该糊组合物的太阳能电池元件 Download PDFInfo
- Publication number
- CN100538915C CN100538915C CNB200580018625XA CN200580018625A CN100538915C CN 100538915 C CN100538915 C CN 100538915C CN B200580018625X A CNB200580018625X A CN B200580018625XA CN 200580018625 A CN200580018625 A CN 200580018625A CN 100538915 C CN100538915 C CN 100538915C
- Authority
- CN
- China
- Prior art keywords
- paste composite
- semiconductor substrate
- quality
- type silicon
- silicon semiconductor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种糊组合物和具有使用该组合物形成的电极的太阳能电池元件,其中,所述糊组合物即使不含作为对环境带来不良影响的物质的玻璃粉、或者即使降低作为对环境带来不良影响的物质的玻璃粉的含量,也可以维持作为太阳能电池的背面电极所希望的功能,同时可以强化铝电极层与p型硅半导体基片的结合。糊组合物是一种用于在p型硅半导体基片(1)上形成铝电极层(8)的糊组合物,其包含铝粉末、有机载体及金属醇盐。太阳能电池元件具有铝电极层(8),该铝电极层(8)是通过将具有上述特征的糊组合物涂布在p型硅半导体基片(1)上后、进行焙烧而形成的。
Description
技术领域
本发明一般来讲涉及一种糊组合物及使用该糊组合物的太阳能电池元件,特别是涉及一种在构成结晶硅太阳能电池的p型硅半导体基片上形成背面铝电极时使用的糊组合物、以及使用该糊组合物的太阳能电池元件。
背景技术
作为一种既安全又不会对环境带来不良影响的清洁能源,太阳能电池有望在更广泛的范围实用化。
图1是示意地表示太阳能电池元件的一般剖面结构的图。
如图1所示,在厚度为300~600μm的p型硅半导体基片1的受光面侧,依次形成厚度为0.3~0.5μm的n型杂质层2、防反射膜3及栅极4。
另外,在p型硅半导体基片1的背面侧,形成作为背面电极的铝电极层8。铝电极层8由铝烧结层5和铝硅混合层6构成,是通过如下操作形成的:利用丝网印刷等将由铝粉末、玻璃粉及有机载体构成的糊组合物进行涂布、并干燥后,在660℃(铝的熔点)以上的温度进行焙烧。在焙烧时,铝扩散到p型硅半导体基片1的内部,由此在铝烧结层5和p型硅半导体基片1之间形成铝硅混合层6,同时,通过铝原子的扩散形成作为扩散层的p+层(或p++层)7。通过该p+层7的存在,可以得到提高所生成载流子的收集效率的BSF(Back Surface Field)效果。实际上,背面电极以下述情况的形式使用:直接使用焙烧后的铝烧结层5、铝硅混合层6及p+层7的三层的情况;以及为了降低电阻,而利用化学方法等除去焙烧后的铝烧结层5或焙烧后的铝烧结层5与铝硅混合层6后,在其表面形成并使用银和铜构成的电极层的情况。不管在哪种情况下,p+层7都发挥BSF效果。
为了形成作为背面电极的铝电极层8而使用的糊组合物,通常由铝粉末、玻璃粉(glass frit)及有机载体构成。
为了形成铝烧结层5、铝硅混合层6及由铝原子的扩散而产生的p+层7,添加约60~约80质量%的铝粉末。
为了利用玻璃粉在焙烧时不挥发而溶解、冷却时再凝固的作用,强化铝电极层8和p型硅半导体基片1的结合,添加约1~约5质量%的玻璃粉。
为了提高利用丝网印刷等将糊组合物涂布时的涂布性和印刷性,添加约15~约40质量%的有机载体。
由于太阳能电池作为安全且不会对环境带来不良影响的清洁能源受到关注,因此从太阳能电池的构成物中除去或减少对环境带来不良影响的物质,推进其在广泛范围的实用化成为一个课题。
顺便,对于用于在维持作为太阳能电池的背面电极所希望的功能的同时防止在焙烧过程中p型硅半导体基片发生翘曲或破裂的糊组合物正在进行各种研究。
在特开2000-90734号公报(专利文献1)中,作为可以用于在维持作为太阳能电池的背面电极所希望的功能的同时防止p型硅半导体基片在焙烧过程中发生翘曲或破裂而使铝电极层变薄的导电糊,公开了在含有铝粉末、玻璃粉、有机载体的基础上,还含有含铝有机化合物的糊。
另外,在特开2003-223813号公报(专利文献2)中,作为即使在使p型硅半导体基片变薄时不减少涂布量也可以充分达到所希望的BSF效果,且可以抑制焙烧后的p型硅半导体基片变形的糊组合物,公开了在含有铝粉末、有机载体的基础上,还含有热膨胀系数比铝小、且熔融温度、软化温度及分解温度的任一个比铝的熔点高的无机化合物的组合物。
而且,在特开2004-134775号公报(专利文献3)中,作为用于在维持作为太阳能电池的背面电极所希望的功能的同时将焙烧过程中的铝电极层的收缩减小从而防止翘曲或破裂产生的导电糊组合物,公开了在含有铝粉末、玻璃粉、有机载体的基础上,还含有难溶于或不溶于该有机载体的有机化合物粒子及碳粒子中的至少一种的组合物。
但是,目前的现状是,即使在这些公报公开的糊组合物中,玻璃粉也是必须的成分。一直以来,使用对环境带来不良影响的含铅玻璃作为玻璃粉。
因此,从不会对环境带来不良影响的观点考虑,正在研究使用Bi2O3-SiO2-B2O3类、ZnO类等无铅玻璃作为SiO2-PbO类、SiO2-B2O3-PbO类等含铅玻璃的替代物。
但是,存在的问题在于,无铅玻璃的熔点高,为了使其均匀溶解,需要提高焙烧温度,还要延长焙烧时间。
专利文献1:特开2000-90734号公报
专利文献2:特开2003-223813号公报
专利文献3:特开2004-134775号公报
发明内容
因此,该发明的目的在于,为了解决上述问题,提供一种糊组合物和具有使用该组合物形成的电极的太阳能电池元件,所述糊组合物即使不含作为对环境带来不良影响的物质的玻璃粉、或者即使降低作为对环境带来不良影响的物质的玻璃粉的含量,也可以维持作为太阳能电池的背面电极所希望的功能,同时可以强化铝电极层与p型硅半导体基片的结合。
本发明者为了解决现有技术的这些问题,反复进行了专心致志地研究,结果发现,通过使用具有特定组成的糊组合物,可以实现上述目的。基于这种发现,依照本发明的糊组合物具有下述特征。
依照该发明的一方面的糊组合物,其为用于在p型硅半导体基片上形成电极的糊组合物,其包含:铝粉末、有机载体及金属醇盐。在此,所谓的“金属醇盐”,是指包含金属、半金属或半导体作为“金属”的醇盐。
依照该发明的一方面的糊组合物,优选包含:铝粉末60质量%以上75质量%以下、有机载体10质量%以上35质量%以下和金属醇盐0.1质量%以上20质量%以下。
依照该发明的另一方面的糊组合物,其为用于在p型硅半导体基片上形成电极的糊组合物,其包含:铝粉末、有机载体以及通过将金属醇盐水解缩聚得到的溶胶和/或凝胶。在此,所谓的“金属醇盐”,是指包含金属、半金属或半导体作为“金属”的醇盐。
依照该发明的另一方面的糊组合物,优选包含:铝粉末60质量%以上75质量%以下、有机载体10质量%以上35质量%以下、通过将金属醇盐水解缩聚得到的溶胶和/或凝胶0.1质量%以上20质量%以下。
在依照本发明的一方面的糊组合物、或者依照本发明的另一方面的糊组合物中,优选金属醇盐是含有硅作为金属的金属醇盐。
另外,优选地,依照本发明的一方面的糊组合物、或者依照本发明的另一方面的糊组合物还包含选自由无机化合物粒子、有机化合物粒子及碳粒子构成的组中的至少一种粒子。这时,无机化合物粒子和/或有机化合物粒子的平均粒径优选为10μm以下。碳粒子的平均粒径优选为1μm以下。
而且,优选地,依照本发明的一方面的糊组合物、或者依照本发明的另一方面的糊组合物还包含玻璃粉。
依照本发明的太阳能电池元件,具有通过将具有上述任一特征的糊组合物涂布到p型硅半导体基片上后进行焙烧而形成的电极。这时,优选在p型硅半导体基片与电极之间,形成包含于金属醇盐中的金属的化合物。
如上所述,根据该发明,可以得到一种糊组合物和具有使用该组合物形成的电极的太阳能电池元件,所述糊组合物,通过将涂布了包含金属醇盐、或者通过将金属醇盐水解缩聚得到的溶胶和/或凝胶的糊组合物的p型硅半导体基片烧结,从而即使不含作为对环境带来不良影响的物质的玻璃粉、或者即使降低作为对环境带来不良影响的物质的玻璃粉的含量,也可以维持作为太阳能电池的背面电极所希望的BSF效果和太阳能电池所希望的能量转换效率,同时可以强化铝电极层与p型硅半导体基片的结合。
附图说明
[图1]是示意地表示作为一实施方式的本发明适用的太阳能电池元件的普通剖面结构的图。
[图2]是示意地表示在实施例与现有例中,测定形成了铝电极层的焙烧后的p型硅半导体基片的变形量的方法的图。
符号说明
1:p型硅半导体基片;2:n型杂质层;3:防反射膜;4:栅极;5:铝烧结层;6:铝硅混合层;7:p+层;8:铝电极层。
具体实施方式
本发明的糊组合物的特征在于,在含有铝粉末、有机载体的基础上,还含有金属醇盐、或者通过将金属醇盐水解缩聚得到的溶胶和/或凝胶。金属醇盐是金属有机化合物的一种,是至少具有一个M-O-C(M:金属、半金属或半导体)键的化合物。在金属醇盐中,存在多种化合物,包括由金属元素的种类和其价数的不同而不同的化合物、由烷氧基的种类和其组合的不同而不同的化合物、还有包括两种金属的双醇盐、和用其它有机基团部分取代的化合物。
在本发明的糊组合物中,除常态的金属醇盐之外,也可以含有通过水解缩聚得到的溶胶和/或凝胶状态的金属醇盐。例如,通过将四甲氧基硅烷、水、甲醇及氨水以1:10:2.2:3.7×10-4的摩尔比混合、并水解缩聚,而形成硅氧烷,可以得到溶胶状态的硅氧烷,当进一步进行反应时,可以得到凝胶状态的硅氧烷。
将含有金属醇盐的糊组合物涂布在p型硅半导体基片上进行焙烧、冷却时,在形成的铝电极层和p型硅半导体基片之间,致密地形成金属醇盐热分解生成的金属氧化物等金属化合物,可以强化铝电极层和p型硅半导体基片的结合。
因而,以往为了强化焙烧后的铝电极层和p型硅半导体基片的结合,除了在糊组合物中添加玻璃粉之外,还没有实质上有效的手段,但是当使用本发明的糊组合物时,不含有玻璃粉或者即使使其含有玻璃粉而玻璃粉的含量也减少,可以强化上述结合。
近年来,根据太阳能电池元件的薄型化要求将硅半导体基片变薄的同时以薄膜形式涂布导电糊时,通常使用的平均粒径为约1~约2μm的玻璃粉,由于玻璃粉散布在糊组合物中,因此,产生如图1所示的焙烧后的铝电极层8和p型硅半导体基片1的结合弱的部位,产生结合力变得不均匀的问题。结果,可能铝电极层8会剥离。
另外,为了不对环境带来不良影响而使用熔点高的无铅玻璃作为玻璃粉时,粒子状玻璃的溶解和再凝固进一步不均匀,铝电极层8剥离的可能性会变大。而且,由于无铅玻璃粉的熔点高,因此,为了使粒子状玻璃的溶解和再凝固变得均匀,就必须提高焙烧温度、延长焙烧时间。因此,由于铝烧结层5的烧结过度地进行,并且过度地形成铝硅混合层6,因此,p型硅半导体基片1的翘曲等变形量增大、铝烧结层5膨胀(起泡)、表面产生铝球等,结果,不能用作太阳能电池元件。
由于该发明的糊组合物没有必要含有用于强化焙烧后的铝电极层和p型硅半导体基片之间的结合的玻璃粉、或者可以减少有助于强化焙烧后的铝电极层和p型硅半导体基片之间的结合的玻璃粉的含量,因此,可以不使用对环境带来不良影响的物质、或者即使含有作为对环境带来不良影响的物质的玻璃粉,也可以减少对环境带来不良影响的物质的含量。另外,由于该发明的糊组合物没有必要使用熔点高的无铅玻璃、或者即使含有无铅玻璃也可以减少无铅玻璃的含量,因此,铝电极层不会剥离,可以提高焙烧后的铝电极层和p型硅半导体基片的密合性,与使用无铅玻璃的情况相比,可以抑制p型硅半导体基片的翘曲等变形。
包含于本发明的糊组合物中的金属醇盐,除了丁醇铝或者丙醇钛等之外,也可以适当使用甲醇硼等任意材料。特别优选使用四乙氧基硅烷等包含硅的金属醇盐。另外,本发明的糊组合物也可以含有作为通过将这些金属醇盐水解缩聚得到的溶胶和/或凝胶状态的金属醇盐。例如,通过将四乙氧基硅烷进行水解缩聚,生成硅氧烷,得到其溶胶状态的物质,当进一步进行反应时,得到凝胶状态的物质。
本发明的糊组合物中包含的金属醇盐的含量、或者通过将金属醇盐水解缩聚得到的溶胶和/或凝胶的含量,优选为0.1质量%以上20质量%以下。当金属醇盐的含量、通过将金属醇盐水解缩聚得到的溶胶和/或凝胶的含量低于0.1质量%时,不能得到对于强化焙烧后的铝电极层和p型硅半导体基片的结合充分的添加效果。当金属醇盐的含量、通过将金属醇盐水解缩聚得到的溶胶和/或凝胶的含量超过20质量%时,焙烧后生成的金属化合物使得铝烧结层的电阻增高、太阳能电池元件的特性降低。
而且,包含于本发明的糊组合物中的金属醇盐、或者通过将金属醇盐水解缩聚得到的溶胶和/或凝胶,通过利用其烷氧基的性质,也可以一部分用于替代有机载体。
包含于本发明的糊组合物中的铝粉末,优选平均粒径为10μm以下。当平均粒径超过10μm时,在涂布糊组合物时,铝粉末和硅半导体基片的接触点变少,因此有时焙烧后不能得到均匀的铝硅合金层。
另外,包含于本发明的糊组合物中的铝粉末的含量,优选为60质量%以上75质量%以下。当铝粉末的含量低于60质量%时,可能会使焙烧后的铝电极层的表面电阻增大,能量转换效率降低。当铝粉末的含量超过75质量%时,丝网印刷时糊的涂布性降低。
作为包含于本发明的糊组合物中的有机载体,使用根据需要溶解有各种添加剂及树脂的溶剂。
可以使用公知的溶剂,具体例如有:二乙二醇一丁基醚、二乙二醇一丁基醚乙酸酯、二丙二醇一甲基醚等。
可以使用的各种添加剂例如有:抗氧化剂、腐蚀抑制剂、消泡剂、增稠剂、增塑剂、分散剂、增粘剂、偶联剂、静电提供剂、阻聚剂、触变剂、防沉淀剂等。
具体地,可以使用例如:聚乙二醇酯化合物、聚乙二醇醚化合物、聚氧乙烯脱水山梨糖醇酯化合物、脱水山梨糖醇烷基酯化合物、脂肪族多元羧酸化合物、磷酸酯化合物、聚酯酸的酰胺胺盐、氧化聚乙烯类化合物、脂肪酸酰胺蜡等。
可以使用公知的树脂,可以使用下述树脂中的一种或两种以上的组合:乙基纤维素、硝基纤维素、聚乙烯醇缩丁醛、酚树脂、密胺树脂、尿素树脂、二甲苯树脂、醇酸树脂、不饱和聚酯树脂、丙烯酸树脂、聚酰亚胺树脂、呋喃树脂、聚氨酯树脂、异氰酸酯化合物和氰酸酯化合物等的热固性树脂、聚乙烯、聚丙烯、聚苯乙烯、ABS树脂、聚甲基丙烯酸甲酯、聚氯乙烯、聚偏氯乙烯、聚醋酸乙烯酯、聚乙烯醇、聚缩醛、聚碳酸酯、聚对苯二甲酸乙二醇酯、聚对苯二甲酸丁二醇酯、聚苯醚、聚砜、聚酰亚胺、聚醚砜、聚芳酯、聚醚醚酮、聚四氟乙烯、硅树脂等。另外,包含于本发明的糊组合物中的有机载体,也包含没有溶解树脂的有机载体。
有机载体的含量优选为10质量%以上35质量%以下,当有机载体的含量低于10质量%或超过35质量%时,糊的印刷性降低。
而且,为了进一步强化铝电极层和p型硅半导体基片的结合,本发明的糊组合物也可以含有玻璃粉。玻璃粉的含量优选为5质量%以下。当玻璃粉的含量超过5质量%时,可能会发生玻璃的偏析。另外,此时,最优选使用不会对环境带来不良影响的无铅玻璃作为玻璃粉,但是,为了尽可能缓和由无铅玻璃粉的熔点高而导致的上述问题,也可以使用含铅玻璃。即使使用含铅玻璃作为玻璃粉,由于本发明的糊组合物与以往的相比可以使有助于上述结合的含铅玻璃的含量减少,因此,可以减少对环境带来不良影响的物质的含量。
为了防止由铝电极层和p型硅半导体基片的热膨胀系数差异引起的焙烧后的太阳能电池元件的翘曲等变形,本发明的糊组合物还可以含有无机化合物粒子、有机化合物粒子及碳粒子中的任一种以上。无机化合物粒子、有机化合物粒子及碳粒子中的任一种以上的含量,以总量计优选为0.1质量%以上10质量%以下。当无机化合物粒子、有机化合物粒子及碳粒子中的任一种以上的含量以总量计低于0.1质量%时,不能得到防止翘曲的充分的添加效果。另外,当其超过10质量%时,可能会导致铝电极层的电阻值增大,妨碍糊的焙烧性。
只要是热膨胀系数比铝小,而且熔融温度、软化温度及分解温度的任一项比铝的熔点高的无机化合物粉末,则任一种材料都可以适当用作无机化合物粒子。无机化合物粒子的平均粒径为10μm以下、优选5μm以下。
有机化合物粒子有例如:聚乙烯、聚丙烯、丙烯酸树脂、环氧树脂等。有机化合物粒子的平均粒径为10μm以下、优选5μm以下。
作为碳粉末,特别是不仅碳黑等,只要是碳纤维、玻璃状碳等平均粒径为1μm以下、优选0.5μm以下的微细粉末,则任一种材料都可以适当使用。
实施例
下面,对本发明的一个实施例进行说明。
首先,制作各种糊组合物,其中在有机载体中含有70质量%的铝粉末以及表1所示比例的金属醇盐、添加粒子及玻璃粉。
具体地,在使用乙二醇醚类有机溶剂的有机载体中,添加各种金属醇盐,并以表1所示的比例添加铝粉末、添加粒子及玻璃粉,用公知的混合机进行混合,得到糊组合物。
在此,从确保和p型硅半导体基片的反应性、涂布性及涂布膜的均匀性方面考虑,铝粉末使用包括具有平均粒径0.5~10μm的球形或接近球形的形状的粒子的粉末。
另外,添加粒子时,使用平均粒径为0.025μm的碳粒子或平均粒径为0.3μm的氧化硅。
另外,添加玻璃粉时,使用平均粒径为1.5μm的Bi2O3-SiO2-B2O3类玻璃作为无铅玻璃。
使用180目的丝网印刷版,将上述各种糊组合物涂布印刷在大小为2英寸(50.8mm)×2英寸(50.8mm)、厚度为280μm的p型硅半导体基片上。设定涂布量,使得焙烧后的铝电极层的厚度为40~50μm。
将印刷了糊的p型硅半导体基片进行干燥后,利用红外线焙烧炉,在空气环境中以400℃/分钟的升温速度进行加热,在温度700℃保持30秒的条件下进行焙烧。焙烧后,通过进行冷却,如图1所示,得到p型硅半导体基片1上形成作为背面电极的铝电极层8的各试样。
对各试样的特性如下进行评价,结果如表1所示。
(密合性)
形成了铝电极层的焙烧后的铝电极层和p型硅半导体基片的密合性,通过采用玻璃带的剥离试验进行如下评价。
○:没有剥离;△:稍有剥离;×:严重剥离。
(外观)
形成了铝电极层的焙烧后的铝电极层的外观,通过目测进行如下评价。
○:没有气泡或裂痕;△:稍有气泡或裂痕;×:气泡或裂痕明显。
(变形量)
形成了铝电极层的焙烧后的p型硅半导体基片的变形量,通过如下方法进行评价:在焙烧、冷却后,如图2所示,使铝电极层朝上,将基片四角的一端沿箭头所示方向按压,测定位于其对角位置的一端的上升量(包括基片的厚度)x。用“变形量(mm)”表示其上升量x。
(铝电极层表面电阻)
作为制成太阳能电池元件时的能量转换效率的指标,用四点探针表面电阻测定器(ナプソン社制RG-5型薄层电阻计)测定铝电极层的表面电阻。测定条件设定为:电压4mV、电流100mA、表面施加的负荷200grf(1.96N)。用电极层表面电阻(mΩ/□)表示其测定值。
(p+层表面电阻)
然后,通过将形成了上述铝电极层的p型硅半导体基片浸渍在盐酸水溶液中而溶解去除铝电极层8后,用4端子式表面电阻测定器测定形成了p+层7的p型硅半导体基片1的表面电阻,作为BSF效果的指标。用p+层表面电阻(Ω/□)表示其测定值。
为了改善现有例1和2的试样的密合性,在温度750℃保持30秒的条件下进行焙烧、作成试样,进行评价。结果如表2所示。
[表2]
由表1及2的结果可知,实施例与现有例相比,在将铝电极层表面电阻和p+层表面电阻大致维持在同等程度的同时,可以改善铝电极层的密合性。而且还可知,实施例与现有例相比,还可以使焙烧后的p型硅半导体基片的变形量减少。
应该注意的是,以上公开的实施方式和实施例在其所有点上都是示例性的而不是限制性的。本发明的范围不是以上的实施方式和实施例,而是由权利要求书的范围所示,包含在和权利要求书同等含义及范围内的所有的修正及变形。
产业实用性
本发明的糊组合物在构成结晶硅太阳能电池的p型硅半导体基片上形成背面铝电极时使用,即使不含作为对环境带来不良影响的物质的玻璃粉、或者即使降低作为对环境带来不良影响的物质的玻璃粉的含量,也可以维持作为太阳能电池的背面电极所希望的BSF效果和太阳能电池所希望的能量转换效率,同时可以强化太阳能电池元件中铝电极层和p型硅半导体基片的结合。
Claims (17)
1.一种糊组合物,用于在p型硅半导体基片(1)上形成电极(8),其包含:铝粉末、有机载体及含有硅作为金属的金属醇盐。
2.如权利要求1所述的糊组合物,其包含:铝粉末60质量%以上75质量%以下、有机载体10质量%以上35质量%以下、以及金属醇盐0.1质量%以上20质量%以下。
3.如权利要求1所述的糊组合物,其中,还包含选自由无机化合物粒子、有机化合物粒子及碳粒子构成的组中的至少一种粒子。
4.如权利要求3所述的糊组合物,其中,所述无机化合物粒子和/或所述有机化合物粒子的平均粒径为10μm以下。
5.如权利要求3所述的糊组合物,其中,所述碳粒子的平均粒径为1μm以下。
6.如权利要求1所述的糊组合物,其中,还包含玻璃粉。
7.一种糊组合物,用于在p型硅半导体基片(1)上形成电极(8),其包含:铝粉末、有机载体、以及通过将金属醇盐水解缩聚得到的溶胶和/或凝胶,其中,所述金属醇盐是指包含金属、半金属或半导体作为金属的醇盐。
8.如权利要求7所述的糊组合物,其包含:铝粉末60质量%以上75质量%以下、有机载体10质量%以上35质量%以下、以及通过将金属醇盐水解缩聚得到的溶胶和/或凝胶0.1质量%以上20质量%以下。
9.如权利要求7所述的糊组合物,其中,所述金属醇盐是含有硅作为金属的金属醇盐。
10.如权利要求7所述的糊组合物,其中,还包含选自由无机化合物粒子、有机化合物粒子及碳粒子构成的组中的至少一种粒子。
11.如权利要求10所述的糊组合物,其中,所述无机化合物粒子和/或所述有机化合物粒子的平均粒径为10μm以下。
12.如权利要求10所述的糊组合物,其中,所述碳粒子的平均粒径为1μm以下。
13.如权利要求7所述的糊组合物,其中,还包含玻璃粉。
14.一种太阳能电池元件,其具有电极(8),该电极(8)是通过将用于在p型硅半导体基片(1)上形成电极(8)的糊组合物,即包含铝粉末、有机载体及含有硅作为金属的金属醇盐的糊组合物涂布在p型硅半导体基片上后,进行焙烧而形成的。
15.如权利要求14所述的太阳能电池元件,其中,在所述p型硅半导体基片(1)与所述电极(8)之间,形成包含于所述金属醇盐中的金属的化合物。
16.一种太阳能电池元件,其具有电极(8),该电极(8)是通过将用于在p型硅半导体基片(1)上形成电极(8)的糊组合物,即包含铝粉末、有机载体以及通过将金属醇盐水解缩聚得到的溶胶和/或凝胶的糊组合物涂布在p型硅半导体基片上后,进行焙烧而形成的,其中,所述金属醇盐是指包含金属、半金属或半导体作为金属的醇盐。
17.如权利要求16所述的太阳能电池元件,其中,在所述p型硅半导体基片(1)与所述电极(8)之间,形成包含于所述金属醇盐中的金属的化合物。