CN100398238C - Drilled porous resin base material, and method of manufacturing porous resin base material with conductive drilled inner wall surface - Google Patents
Drilled porous resin base material, and method of manufacturing porous resin base material with conductive drilled inner wall surface Download PDFInfo
- Publication number
- CN100398238C CN100398238C CNB2004800158151A CN200480015815A CN100398238C CN 100398238 C CN100398238 C CN 100398238C CN B2004800158151 A CNB2004800158151 A CN B2004800158151A CN 200480015815 A CN200480015815 A CN 200480015815A CN 100398238 C CN100398238 C CN 100398238C
- Authority
- CN
- China
- Prior art keywords
- porous resin
- base material
- solid
- resin base
- perforation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A production process of a perforated porous resin base, comprising Step 1 of impregnating the porous structure of a porous resin base with a liquid or solution; Step 2 of forming a solid substance from the liquid or solution impregnated; Step 3 of forming a plurality of perforations extending through from the first surface of the porous resin base having the solid substance within the porous structure to the second surface in the porous resin base; and Step 4 of melting or dissolving the solid substance to remove it from the interior of the porous structure, and a production process of a porous resin base with the inner wall surfaces of the perforations made conductive, comprising the step of selectively applying a catalyst only to the inner wall surfaces of the perforations to apply a conductive metal to the inner wall surfaces.
Description
Technical field
The manufacture method of the porous resin base material (being sometimes referred to as " porous synthetic resin base material ") that the present invention relates to connect the thickness of porous resin material and bore a hole.In addition, the present invention relates to the manufacture method of the porous resin base material of the internal face conductionization that optionally will bore a hole.
The porous resin base material of the perforation that is obtained by manufacture method of the present invention can be used in, and for example, the circuit of electronic applications connects with material or anisotropic conductive material, insulating materials; The medical device as spot (パ ッ チ) repair materials of medical field; Extensive fields such as diffusion barrier.
The porous resin base material with conductive drilled inner wall surface that is obtained by manufacture method of the present invention can be used in, and for example, what the component in the semiconductor devices was mutual is electrically connected; The electric reliability inspection of carrying out in circuit substrate, semiconductor wafer, the semiconductor subassembly.
Porous resin base material is the base material with the different shape that comprises sheet, pipe, piece, but preferred sheet.In the present invention, so-called porous resin sheet is meant that not only thickness is 0.25mm or the above sheet of 0.25mm, but also refers to the film of the not enough 0.25mm of thickness.
Background technology
In the past, at electronic applications, as resin substrate, viewpoint from mechanical strength, electrical properties, hear resistance etc., can use, for example, phenolic resins, epoxy resin, glass epoxy resin, polyimide resin, mylar, polysulfone resin, polyflon (for example, " real packing technique basis lecture the 1st volume introduction of electronics ", associating microelectronics (Ha イ Block リ ッ De マ イ Network ロ エ レ Network ト ロ ニ Network ス) association compile, the census of manufacturing can be published, distribution on July 1st, 1998, the 4th chapter 203-209 page or leaf).
In recent years, be accompanied by high frequencyization, high speed in the electronic applications,, particularly require low-kization as the desired material behavior of substrate.Porous resin is compared with common atresia matter resin material, and dielectric constant is low, therefore, gets most of the attention as the resin substrate material.
Circuit connects and to have the structure that perforation (also being " through hole ") is set in the necessary place of substrate, adheres to conductive material at the internal face of this perforation with material or anisotropic conductive material.Therefore, use the porous resin material, must form the perforation bigger than the aperture of porous resin material as these baseplate materials.
Usually, as the method that perforation (through hole) is set on substrate, for example, the punching of adopting drift and punch die to carry out arranged, adopt punching that mould carries out, (for example, " Micrometer-Nanometer Processing Technology ", the Micrometer-Nanometer Processing Technology committee that compiles compiles to adopt the machining process such as perforation that drill bit carries out, Nikkan Kogyo Shimbun publishes, distribution on September 30th, 1988, the 1st chapter 8-13 page or leaf, the 2nd chapter 168-175 page or leaf).As method for punching, also known light ablation method of the instrument front end being carried out the method for ultrasonic vibration perforation, the chemical method for etching that utilizes chemical attack effect perforation, irradiating laser perforation.
But, by mechanical processing method to the porous resin material that is shaped to substrate shape (below, be called " porous resin base material ") when boring a hole, because base material distortion itself, or the seamed edge of perforation or the loose structure fragmentation of internal face, or the peristome of boring a hole generation burr, therefore, it is very difficult that the limit keeps the loose structure limit to form perforation with high accuracy.Carry out ultrasonic vibration and the method for boring a hole even porous resin base material adopts at the instrument front end, also be difficult to form high-precision perforation.
Porous resin base material irradiating laser and when boring a hole, because heating, melting deformation around the perforated portion, or the seamed edge of perforation or the loose structure fragmentation of inwall.Chemical method for etching though the possibility of perforation is arranged, is inappropriate as the method for punching that contains the porous resin base material of corrosion resistance resin according to the kind difference of the resin that constitutes porous resin base material.Though there is the short wavelength laser can shine PRK for example in porous resin base material and possibility, long processing time and the cost height of boring a hole.
Porous resin base material if the loose structure of the seamed edge of perforation or inwall is destroyed, has just damaged as the porous resin properties of materials.Porous resin base material has elasticity on thick direction, if but the loose structure of perforated portion periphery is destroyed, and only once then perforated portion fragmentation, loss of elasticity are born a heavy burden in the load compression.
The porous resin base material of perforation is connected when using with material or anisotropic conductive material as circuit, adhere to plating particle etc. at the internal face of perforation and give conductive metal, seek conductionization on thick direction.But if the loose structure fragmentation of the internal face of perforation, adhering to of plating catalyst just becomes difficult.In addition, if the loose structure of perforated portion periphery is destroyed, even so with the internal face conductionization of perforation, the elasticity of conductionization portion also can be lost, and when therefore the load compression was born a heavy burden, conductive part itself can be broken.
Have, even with the porous resin base material perforation, it also is very difficult only optionally adhering to the conductive metal conduction at the internal face of boring a hole by secondary operations after this again.Like this, porous resin base material is difficult to critically bore a hole, and the secondary operations after the perforation also is difficult.For these problem points, be example, more specifically explanation with anisotropic conductive sheet (also being " anisotropic conductive film ").
In for example electronic device field of semiconductor devices,, can use and only to give the anisotropic conductive sheet of electric conductivity in thick direction as carrying out the mutual means that are electrically connected of component compactly.For example,, but carry out mutual being electrically connected of component compactly, therefore be widely used because the anisotropic conductive sheet does not use the means of solder etc.
In addition, in the electrically conducting of semiconductor wafer or semiconductor devices, semiconductor subassembly is checked, for reaching being electrically connected between electrode and the testing fixture electrode that be examined that is formed on the circuit substrate one side of checking object, proposed, be examined the method that sandwiches the anisotropic conductive sheet between electrode and the testing fixture electrode.This anisotropic conductive sheet can not be given to be examined electrode and to bring damage, in addition, absorbs the deviation of the height that is examined electrode, for reach and the testing fixture electrode between be electrically connected the preferred anisotropic conductive sheet of rubber-like on film thickness direction.
Object lesson as the anisotropic conductive sheet has proposed, for example, electroconductive particle is distributed in the adhesive that contains epoxy resin and the connection of sheetization with anisotropic conductive material (for example, the spy opens flat 4-242010 communique).This connection only is pressed and compressed portion between opposed terminal with anisotropic conductive material, and each terminal contacts with electroconductive particle, only the thickness direction conducting between two-terminal.By adjusting the dispersity of electroconductive particle, can remain on the insulating properties on the transverse direction of sheet.
Also known, on the sheet that forms by macromolecular material, form a plurality of through holes, filled conductive material in each through hole is only with the anisotropic conductive sheet of the privileged site conductionization of thickness direction.For example, proposed, in each of a plurality of through holes that on by the insulating properties frame that forms with resin material or glass fiber-reinforced composite resin material (Off レ one system) plate, are provided with rigidity, filling has disperseed the insulating properties elasticity polymer body of electroconductive particle to make the anisotropic conductive sheet (for example, the spy opens flat 9-320667 communique) that conducting channel forms element.
A plurality of through holes have been proposed on the electrical insulating property polymeric membrane, to form, in each through hole, fill metal, only (for example with the electric connecting part of film thickness direction conductionization, the elastomeric connector (コ ネ Network ) (for example, the spy opens the 2003-22849 communique) of conductive component is set in the inside of a plurality of apertures of the thick direction that is formed at the flexure strip parts of handling through foaming Te Kaiping 2-49385 communique).
In the anisotropic conductive sheet of the structure in having each through hole that conductive material is filled in the sheet that forms by macromolecular material, as the method that forms through hole (perforation), can adopt, for example, use mechanical processing methods such as the etching method of light source such as laser or punch process, punching method, boring method.According to etching method, usually, though can form aperture 100 μ m or below the 100 μ m, even 50 μ m or the following fine through hole of 50 μ m, processing cost is than higher.The feature of mechanical processing method is, is used in the occasion that forms the above bigger through hole of aperture 100 μ m or 100 μ m usually, and processing cost is low.
On the other hand, for the electrode that do not damage joint or be examined electrode ground and connect, in addition, the deviation that is examined the height of electrode for absorption is carried out good being electrically connected, and expectation anisotropic conductive sheet has sufficient elasticity.The anisotropic conductive sheet that has elasticity at film thickness direction, can the conducting film thickness direction under low compression is born a heavy burden except that to the damage less that is examined electrode owing to have elastic recovery, can use repeatedly in electrically conducting is checked.
In addition, in each through hole of the sheet that the macromolecular material by electrical insulating property forms, fill the elastomer disperseed electroconductive particle or metal and make conducting portion (conduction road) though the anisotropic conductive sheet on film thickness direction, be able to conducting, but it is necessary that high compression is born a heavy burden, or when under the high temperature of deterioration that elastomer is passed in time or degradation etc., using, there is the problem of the elasticity reduction etc. of conducting portion.
But, use is the rubber-like porous resin base material on film thickness direction, do not destroy loose structure, form perforation with high accuracy, have again, internal face in perforation optionally adheres to secondary operations such as conductive metal, on technical level in the past, even neither be easy to for the researcher in this field.
Other aspects, at medical field, stretched polytetrafluoroethylporous porous (below, note by abridging be " stretchable porous PTFE ") can be used as the artificial blood vessel or medical device such as spot repair materials, suture uses.Stretchable porous PTFE by adjusting the fine structure that forms loose structure, also has the characteristics such as growth inside that allow biological tissue except that having highly not active chemical property.Known stretchable porous PTFE promotes the growth inside of biological tissue by the macroscopic perforation of impenetrating thickness is set.
, proposed in the past, had the fine structure that constitutes by the node that mutually combines by fibrillation (ノ one De), stretchable porous PTFE sheet material (for example, the flat 8-506777 communique of special table) with the macroscopic perforation that runs through sheet material.Put down in writing in the document, during the stretchable porous PTFE material perforation that stretched before will boring a hole with pin, this perforation has because the irregular shearing (Qie order of material) and the visible very coarse seamed edge that produces of distortion.In addition, the document has disclosed by the method for punching of removing with the stretchable porous PTFE material of sharp cutter and has also ascribed the perforation with coarse seamed edge to.When the stretchable porous PTFE material of boring a hole is used as medical devices such as repairings,, the danger that produces some infringement is in vivo arranged then if perforation has coarse seamed edge.
Therefore, above-mentioned document (the flat 8-506777 communique of special table) has proposed not with stretchable porous PTFE material perforation, but the method that stretches again after the perforation of the extrusion molding thing before will stretching.Particularly, the document discloses a kind of method of making stretchable porous PTFE material, this method is, the preformed blank of the mixture of PTFE and fluid lubricant is extruded, make extrudate, from this extrudate, remove fluid lubricant, formation runs through the macroscopic perforation of this extrusion molding thing, then, by the extrusion molding thing is carried out uniaxial tension or biaxial stretch-formed, make the stretchable porous PTFE material of macroscopic perforation with the fine structure that constitutes by the node that mutually combines by fibrillation.The document has been put down in writing, if the extrusion molding thing perforation after-drawing before will stretching then can be had the stretchable porous PTFE material of the perforation that possesses level and smooth seamed edge in fact.
In the method for above-mentioned document (the flat 8-506777 communique of special table) record, by the perforation of the extrusion molding thing before will stretching after-drawing, though the roughness of the seamed edge that produces in the time of can relaxing perforation, it is inadequate forming the perforation with highly level and smooth seamed edge.And, in the method for document record, because with the formation loose structure that stretches on single shaft direction or biaxially oriented after the perforation of extrusion molding thing, therefore the position and the aperture of control punch are difficult accurately.
As the porous resin base material of circuit connection, must set the position or the aperture of a plurality of perforation accurately with the perforation of the substrate use of material or anisotropic conductive material.If the position of control punch accurately, even the internal face in perforation has adhered to conductive metal and conduction, use such porous resin base material, can not critically carry out component each other electrical engagement or circuit substrate be examined being electrically connected between electrode and the testing fixture electrode.
Have again, in the method for above-mentioned document record,, can not be applied to optionally adhere to conductive metal and the method for conduction at the internal face of perforation though can make stretchable porous PTFE material with perforation.
Summary of the invention
Have that electrical insulating property, relative dielectric constant are low, rubber-like porous resin material is suitable as the resin base material that circuit connects with material or anisotropic conductive material etc.Use porous resin base material to make circuit and connect, do not destroy loose structure, do not deform in the necessary place of this base material or through hole (perforation) that burr form sharp seamed edge is necessary with material or each property opposite sex conductive material etc.
About this point, if with the anisotropic conductive sheet is that example describes, then as mentioned above, for the electrode that do not damage joint or be examined electrode, in addition, absorption is examined the deviation (バ ラ Star キ) of the height of electrode, carries out good being electrically connected, and expectation anisotropic conductive sheet has sufficient elasticity.Therefore, present inventors had before proposed, the porous resin sheet of electrical insulating property as basement membrane, is provided with through hole in a plurality of places of this basement membrane, develops the anisotropic conductive sheet (being willing to 2003-096173 number) of the structure of on the wall of this through hole, adhering to conductive metal with reference to special.
Having electrical insulating property and rubber-like porous resin sheet is suitable as the basement membrane of anisotropic conductive sheet.In addition, be substituted in the method for the conductive material of filling the elastomer that disperseed electroconductive particle or metal etc. in each through hole of the sheet that forms by macromolecule, when employing is adhered to the method for conductive metal formation conducting portion at the internal face of a plurality of through holes that are arranged at the porous resin sheet, except that the elasticity excellence of film thickness direction, can be with low compression heavy burden conducting film thickness direction, have again, because can restoring by elastic recovery, conducting portion is therefore can obtain the anisotropic conductive sheet that in the electrically conducting inspection, can use repeatedly by original state.
Adhere to the method for conductive metal as the wall at each through hole of porous resin sheet, the electroless plating method is suitable.But, want only to separate out conductive metal particle conduction at the internal face of via by the electroless plating method, add in the operation at the catalyst (plating catalyst) that promotes chemical reduction reaction before this, sheltering the internal face part in addition that is arranged on each through hole on the porous resin sheet is necessary at this internal face attached catalyst only.
As the method for sheltering, for example, employing at the identical porous resin sheet of basement membrane two sides lamination as mask layer, on the laminated body that obtains, form through hole, then, after the full surface attachment of the laminated body that contains through hole promotes the catalyst of chemical reduction reaction, during the method for lift off mask layer, inwall catalyst and the mask layer in addition that is attached to through hole can be removed together.After removing mask layer, utilize the catalyst of wall adhere to and to remain in each through hole of porous resin sheet to carry out electroless plating when covering, can be only adhere to conductive metal and form conducting portion (above-mentioned spy is willing to 2003-096173 number) at the internal face of through hole.
But, when on the porous resin sheet, opening 100 μ m φ or the big through hole more than the 100 μ m φ, if use technology mechanical processing method with low cost, contain the through hole loose structure fragmentation on every side of internal face, on the internal face of through hole, adhere to conductive metal fully by electroless plating and become difficult.If, can damage elasticity at perforated portion because perforation causes the loose structure fragmentation.
Problem of the present invention is to provide a kind of manufacture method of porous resin base material of perforation, this method is, necessary place at porous resin base material, do not cause the destruction of loose structure or the distortion of base material, the generation of burr, can form the manufacture method of the perforation porous resin base material of perforation (through hole) accurately with level and smooth seamed edge.
Other problem of the present invention is to provide a kind of manufacture method of porous resin base material of conduction, this method is, on porous resin base material, form a plurality of perforation (through hole), adhere to the manufacture method of porous resin base material that conductive metal forms the conductionization of conducting portion at the internal face of each perforation, when forming perforation by mechanical processing method, remove the destruction that prevents perforated portion loose structure on every side, and can form outside the perforation with smooth seamed edge accurately, can also optionally adhere to the plating catalyst that promotes the metal ion reduction reaction at the internal face of each perforation, thus, cover etc. and can positively adhere to conductive metal by electroless plating at this internal face.
Present inventors expect for the result who finishes above-mentioned problem further investigation, loose structure at porous resin base material includes immersion fluid or solution, liquid or solution by impregnation form solid, and, connect to second surface from the first surface of the porous resin base material that in loose structure, has solid, thereby form the method for a plurality of perforation.
According to the present invention, even adopt the perforation method of machinery, can not destroy loose structure yet, can critically form perforation in the place of necessity.The perforation that forms, seamed edge is smooth, and bad phenomenon such as can not deform yet.After the perforation,, can in loose structure, remove solid fusion or dissolving.As containing liquid or the solution that is dipped in porous resin base material, can make various materials such as water, alcohol, hydrocarbon, polymer.
In addition, present inventors expect, by using said method, can be manufactured on the perforation internal face and optionally adhere to the porous resin base material of conductive metal.
Discovery is in the loose structure on the two sides of containing porous resin base material, impregnation soluble polymer or alkane form composite sheet, the soluble polymer of the solid by will being present in the porous resin base material two sides or alkane layer are as masking material, after a plurality of perforation formed, promotion reduction of metal ion catalyst for reaction can be optionally adhered in discovery at the internal face of each perforation.
Soluble polymer or alkane are made liquid (fused solution) or solution to be contained and is immersed in the loose structure that contains the porous resin base material two sides.If adopt this method,, can not destroy the perforated portion loose structure on every side that contains internal face even form perforation by mechanical processing method yet.Perforation is implemented keeping to contain under the temperature that the soluble polymer that is dipped in the loose structure or alkane be solid state.As soluble polymer or alkane, when using under the normal temperature (15~30 ℃) material as solid, can bore a hole at normal temperatures.After solvent shown that deliquescent soluble polymer or alkane use as masking material, can easily dissolve by solvent and remove.This method also can be implemented by using the compound replacement soluble polymer or the alkane that can be formed solid by the chemical reaction of for example polymerizable monomer.
In addition, optionally adhere to the additive method of the porous resin base material of conductive metal as being manufactured on the perforation internal face, present inventors expect, use to contain and can form the liquid of compound of solid or the method for solution by chemical reaction.
Particularly, two sides at porous resin base material, as mask layer, the lamination porous resin layer, form the laminated body of 3-tier architecture, in each loose structure of this laminated body, impregnation contains the liquid or the solution that can form the compound of solid by chemical reaction, makes the liquid of impregnation or the compound in the solution carry out chemical reaction formation solid.
After the first surface that formation has the laminated body of solid in each loose structure such as was through at a plurality of perforation on two surfaces, the dissolving solid was also removed.Laminated body surface attachment at the internal face that contains each perforation promotes the reduction of metal ion catalyst for reaction.Then, peel off the mask layer on two sides from porous resin base material, and, utilization adhere to and remain in porous resin base material each the perforation internal face on above-mentioned catalyst, adhere to conductive metal at this internal face, thus, can make the optionally porous resin base material of conduction of internal face of to bore a hole.This method also can be implemented by the compound that chemical reaction can obtain solid by using the replacement of soluble polymer or alkane.The present invention is based on these discoveries and finishes.
Like this, according to the present invention, provide the manufacture method of the porous resin base material of perforation, this method contains following operation 1~4:
(1) includes the operation 1 of immersion fluid or solution at the loose structure of porous resin base material;
(2) operation 2 that forms solid by the liquid or the solution of impregnation;
(3) be formed on the operation 3 that the first surface that has the porous resin base material of solid in the loose structure runs through a plurality of perforation of second surface; And
(4) with solid fusion or dissolving, the operation 4 of removing in the loose structure.
In addition, according to the present invention, provide the manufacture method with the porous resin base material of conductive drilled inner wall surface, this method comprises following operation I~VI:
(1) in the loose structure on the two sides of containing porous resin base material, impregnation soluble polymer or alkane maybe can form the operation I of the compound of solid by chemical reaction;
(2) maybe can form solid by the soluble polymer of impregnation or alkane by the compound that chemical reaction forms solid, be formed on have the layer of solid on the two sides of porous resin base material and in loose structure impregnation the operation II of composite sheet of structure of solid;
(3) form the operation III that runs through a plurality of perforation of second surface from the first surface of this composite sheet;
(4) containing the respectively operation IV of the catalyst of the surface attachment promotion metal ion reduction reaction of the composite sheet of the internal face of perforation;
(5) remove the operation V of solid from composite sheet; And
(6) utilize the above-mentioned catalyst that adheres to and remain in each internal face of boring a hole of porous resin base material, adhere to the operation VI of conductive metal at this internal face.
Have, according to the present invention, provide the manufacture method with the porous resin base material of conductive drilled inner wall surface, this method comprises following operation i~viii:
(1) on the two sides of porous resin base material (A), lamination reaches (C) as the porous resin layer (B) of mask layer, forms the operation i of the laminated body of 3-tier architecture;
(2) in each loose structure of this laminated body, impregnation soluble polymer or alkane maybe can form the operation ii of the compound of solid by chemical reaction;
(3) maybe can form the operation iii of solid by the compound that chemical reaction forms solid by the soluble polymer of impregnation or alkane;
(4) form the operation iv that runs through a plurality of perforation of second surface from the first surface that in each loose structure, has the laminated body of solid;
(5) dissolving solid, the operation v that removes in each loose structure;
(6), adhere to the operation vi that promotes the reduction of metal ion catalyst for reaction on the surface of the laminated body that contains each internal face of boring a hole;
(7) peel off the operation vii of the mask layer on two sides from porous resin base material (A); And
(8) utilize the above-mentioned catalyst that adheres to and remain in each internal face of boring a hole of porous resin base material (A), adhere to the operation viii of conductive metal at this internal face.
Description of drawings
Fig. 1 is the zoom microscope photo by the perforation of the manufacture method formation of the porous resin base material of perforation of the present invention.
Fig. 2 is the zoom microscope photo by the perforation that the method for porous resin base material perforation is formed with mechanical processing method.
Fig. 3 is the flow chart that illustrates the operation of the manufacture method of the porous resin base material of conductive drilled inner wall surface of the present invention.
Fig. 4 is the flow chart that illustrates the operation of other manufacture methods of the porous resin base material of conductive drilled inner wall surface of the present invention.
Fig. 5 is the section sketch that device is confirmed in the conducting heavy burden of anisotropic conductive film.
The preferred plan that carries out an invention
1.
Porous resin base material (basement membrane)
As the resin material that constitutes the porous resin base material that uses in the present invention, so long as can form the material of porous resin, then any resin can use.Porous resin base material is, in order to tolerate adhering to of method for punching that the present invention adopts or conductive metal, be suitable for purposes, the material that preferred selection is formed by excellent resin material such as hear resistance, processability, mechanical property, dielectric property in electronic applications or medical field.
For example, component between mutually be electrically connected or electrically conducting check in the excellent heat resistance of employed anisotropic conductive sheet preferred substrates (basement membrane).Particularly in senile experiment, because to carry out the high temperature accelerated deterioration with the state that is examined between electrode and the testing fixture electrode that the anisotropic conductive sheet is sandwiched circuit substrate, therefore, it is necessary using the base material of excellent heat resistance.
In addition, the anisotropic conductive sheet can be necessary at transverse direction (direction vertical with respect to film thickness direction) for electrical insulating property on film thickness direction in the conductionization.Therefore, formation is that electrical insulating property is necessary as the synthetic resin of the porous resin base material of basement membrane.Particularly, be electrically connected the anisotropic conductive sheet of usefulness, can not become the reason that signal delay takes place, the preferred porous resin base material that contains the low synthetic resin of relative dielectric constant that uses when under high-frequency signal, using semiconductor devices etc.
As the synthetic resin that forms porous resin base material, can enumerate, for example, polytetrafluoroethylene (PTFE), tetrafluoroethylene/hexafluoropropylene copolymer (FEP), tetrafluoroethylene/perfluoro alkyl vinyl ether co-polymer (PFA), Kynoar (PVDF), polyvinylidene fluoride alkene copolymer, Tefzel fluororesin such as (ETFE resins); Polyimides (PI), polyamidoimide (PAI), polyamide (PA), Noryl (mPPE), polyphenylene sulfide (PPS), polyether-ether-ketone (PEEK), polysulfones (PSU), polyether sulfone (PES), liquid crystal polymer engineering plastics such as (LCP).
In these synthetic resin, from the viewpoint of hear resistance, resistance to chemical reagents, processability, mechanical property, dielectric property (low-k) etc., preferred fluororesin.Preferred especially PTFE.
In manufacture method of the present invention, to for example solvent be shown that the polymer or the alkane of solubility use as masking material, after adding the catalyst that promotes the metal ion reduction reaction, usually, owing to adopt soluble polymer or alkane be dissolved in the method for removing in the solvent, therefore the synthetic resin that constitutes base material preferably shows insolubility or slightly solubility for solvent, preferably at least dissolving soluble polymer or the employed solvent of alkane is shown insolubility or slightly solubility.In the manufacture method of the porous resin base material of boring a hole, this also is suitable for removing with dissolution with solvents the occasion of the solid in the loose structure.From viewpoint for the behavior of such solvent, preferred fluororesin, preferred especially PTFE.
As the method for making porous resin base material, can enumerate port-creating method, phase separation method, solvent extraction, pulling method, laser irradiation etc.The shape of porous resin base material is looked application target can suitably be set at sheet, pipe, piece etc., but most occasion is sheet (comprising film).For example, by the porous resin sheet is used as basement membrane, can further reduce dielectric constant in the film thickness direction rubber-like while of anisotropic conductive sheet
The preferred porosity of porous resin base material is in 20~80% scope.The preferred average pore size of porous resin base material is 10 μ m or below the 10 μ m, or bubbling point is at 2kPa or more than the 2kPa, from the viewpoint that the accurate spacing (Off ァ イ Application ピ ッ チ) of conducting portion is changed, preferred average pore size is that the following or bubbling point of 1 μ m or 1 μ m is 10kPa or more than the 10kPa.
The thickness of porous resin base material can suitably be selected according to the place of application target or use, but is generally 3mm or below the 3mm, preferred 1mm or below the 1mm, its lower limit is generally 5 μ m, preferred 10 μ m.For example, use in the anisotropic conductive sheet in the electrically conducting test, preferred 5~500 μ m of the thickness of porous synthetic resin sheet, more preferred 10~200 μ m are about preferred especially 15~100 μ m.
In porous resin base material, owing to excellences such as the stretchable porous PTFE sheet hear resistance of making by pulling method, processability, mechanical property, dielectric properties, have uniform pore-size distribution, therefore be excellent material as the basement membrane of anisotropic conductive sheet.In addition, stretchable porous PTFE sheet also is suitable as medical devices such as spot repair materials.
The stretchable porous PTFE sheet of Shi Yonging can be by for example method manufacturing of special public clear 42-13560 communique record in the present invention.At first, mixing material lubricant in the not sintered powder of PTFE is extruded by plunger type and to be tubulose or tabular.When expectation is the sheet of thin thickness, carry out the calendering of plate body by stack.After the extrusion calendaring operation, optionally, from extrusion molding article or calendering formation product, remove fluid lubricant.
The tabular extrusion molding article that obtains like this or calendering formation product when single shaft direction or biaxially oriented stretch, can be obtained unsintered porous PTFE sheet.If unsintered porous PTFE sheet limit is fixed in the mode that does not cause contraction, the limit is heated to the temperature more than 327 ℃ or 327 ℃ as the PTFE fusing point, and the structure that sintering stretches and fixedly the time can obtain the high stretchable porous PTFE sheet of intensity.If extrusion molding article uniaxial tension and sintering with tubulose can obtain stretchable porous PTFE tube.Stretchable porous PTFE tube can be made sheet by cutting along its length.
Stretchable porous PTFE sheet has and comprises very thin a large amount of fibrillation of being formed respectively by PTFE and by the interlink fine structure (being also referred to as " microfibre shape tissue ") of a large amount of nodes of forming of this fibrillation.In stretchable porous PTFE sheet, this fine structure forms loose structure.Therefore, in stretchable porous PTFE sheet, the resin portion of loose structure is divided into fibrillation and node, and (being also referred to as " space part " or " pore portion ") is the space that forms by fibrillation and node in the loose structure.The elasticity excellence of stretchable porous PTFE sheet film thickness direction, elastic recovery are also excellent.
2.
The liquid of impregnation or solution (material of impregnation)
In the present invention, before perforation, include immersion fluid or solution at the loose structure of porous resin base material.These liquid or solution are the materials that can form solid.This solid is can fusion or dissolved substances.In the present invention, the material of impregnation is called liquid or solution, but it is the state performance during with impregnation, wherein, also contains and be the material of solid state under the normal temperature.
When liquid and solution contain in the loose structure that is immersed in porous resin base material, so long as liquid or solution get final product.For example, be after the material of solid can be heated as liquid (liquation), to contain in the loose structure that is dipped in porous resin base material under freezing point or fusing point height, the normal temperature (temperature of 15~30 ℃ of scopes).After the impregnation, be cooled to the following temperature of freezing point or fusing point or its and solidify.
Normal temperature down be the material of liquid, after the impregnation, is cooled to freezing point or fusing point or the temperature below it and solidifies.Solution can be after impregnation solvent flashing separate out the solute of solid.The material that can form solid by the chemical reaction of polymerizable monomer etc. forms for example solid of solid polymer by chemical reactions such as polymerisations after making liquid or solution and impregnation.
In loose structure, remove solid, be heated to above the temperature of freezing point or fusing point and fusion is removed as liquid, perhaps use dissolution with solvents, remove as solution.The method of using solvent to remove is called extraction or the stripping of adopting solvent sometimes.
Liquid is can be by solidifying or during the material of cooling curing preferred-150~150 ℃ of its freezing point or fusing point, more preferred-80~100 ℃.Freezing point or fusing point are crossed when hanging down, and solidify the cooling means cost height of usefulness.When freezing point or fusing point are too high,, therefore might promote the deterioration of porous resin base material owing to softening point or decomposition point near porous resin base material.In addition, when freezing point or fusing point are too high, even liquid is made in heating, owing to have high viscosity, need vacuumize during impregnation, operation becomes numerous and diverse.
As can so long as get final product, preferably in the said temperature scope, having the material of freezing point or fusing point by solidifying or the liquid (material) of cooling curing at the softening point of the porous resin base material that uses or the material of decomposition point or the temperature-curable below it.As such liquid (material), can enumerate water, alcohol, hydrocarbon, polymer, their mixture more than 2 kinds or 2 kinds.
More specifically,, can enumerate as the liquid (material) of impregnation, for example, water; Methyl alcohol, ethanol, 1-propyl alcohol, 2-propyl alcohol, 1-butanols, 2-butanols, 2-methyl isophthalic acid-propyl alcohol, 2-methyl-2-propyl alcohol, 1-amylalcohol, cyclohexanol, 1 methyl cyclohexanol, 2 methyl cyclohexanol, 1,2-ethylene glycol, 1,2-propane diols, 1, ammediol, 1,4-butanediol, 2,3-butanediol, 1,5-pentanediol, glycerine, 2-ethyl-(methylol)-1, alcohol such as ammediol; Butane, pentane, n-hexane, 2,2-dimethylbutane, 2,3-dimethylbutane, heptane, normal octane, 2,2, hydrocarbon such as 3-trimethylpentane, isooctane, positive nonane, n-decane, n-dodecane, toluene, ortho-xylene, meta-xylene, paraxylene, naphthalene, pentamethylene, cyclohexane.
As the liquid (material) of impregnation, be liquid polymer, the following low melting point polymer of normal temperature, the following high-melting-point alkane (alkane of normal temperature under the normal temperature as solid as solid because can use; Hydrocarbon a kind of) etc.These polymer or alkane also can be made solution and use.
When normal temperature is down made solution and is used for the material of solid, as solvent, selection can dissolve polymer or the normal temperature of alkane, naphthalene etc. be the material of solid down, and the material of or slightly solubility insoluble to the porous resin base material demonstration.Solvent preferably can not corrode, dissolve, decompose the material of porous resin base material.
Solution preferably is applicable to by The tape casting (cast method) or infusion process (dip method) and contains in the loose structure that is immersed in porous resin base material, by removing the method for the solid of separating out solute of desolvating.After the perforation, can use solvent stripping solid from loose structure of using.
As aforesaid liquid or solution, if use soluble polymer or dystectic alkane, except that can carrying out high-precision perforation, optionally with the perforation the internal face conductionization time, soluble polymer or alkane can also be used as masking material.
In first kind of manufacture method of the porous resin base material of conductive drilled inner wall surface of the present invention,, for example use solvent is shown that the polymeric material of solubility or normal temperature are the alkane of solid down as masking material.As soluble polymer, then there is no particular limitation so long as water or organic solvent equal solvent are shown the polymer of solubility, but preferred with the adaptation excellence of porous resin base material, contain in the loose structure that is immersed in porous resin base material easily and the easy material of removing by dissolution with solvents.
As soluble polymer, the solvent of this soluble polymer of preferred dissolution soaks into the material to the loose structure of porous resin base material easily.Soluble polymer preferably is the material of solid down at normal temperature (15~30 ℃) can easily forming at normal temperatures on perforation (through hole) this point by the machine drilling method.
For example, as porous resin base material, when using porous fluoride resin sheets such as stretchable porous PTFE sheet, as the preferred acrylic resin of soluble polymer.Can use the homopolymers or the copolymer of polymethyl methacrylate alkyl acrylates (that is, acrylate) such as (PMMA) or alkyl methacrylate (that is methacrylate) as acrylic resin.
As alkyl acrylate and alkyl methacrylate, can enumerate, for example, acrylate such as methyl acrylate, ethyl acrylate, isopropyl acrylate, n-butyl acrylate, tert-butyl acrylate, 2-EHA, acrylic acid n-octyl, Isooctyl acrylate monomer, acrylic acid ester in the different ninth of the ten Heavenly Stems, decyl acrylate, dodecylacrylate; Methacrylates such as methyl methacrylate, EMA, isopropyl methacrylate, n-BMA, metering system tert-butyl acrylate, methacrylic acid 2-Octyl Nitrite, n octyl methacrylate, EHMA, methacrylic acid ester in the different ninth of the ten Heavenly Stems, decyl-octyl methacrylate, lauryl methacrylate, cyclohexyl methacrylate, methacrylic acid benzyl ester, isobornyl methacrylate.
Soluble polymer also can be the acrylic resin with (methyl) alkyl acrylate and other vinyl monomer copolymerization that can copolymerization.As other vinyl monomer, can enumerate, for example, acrylic acid, methacrylic acid, maleic acid, maleic anhydride, itaconic acid etc. contain the monomer of carboxyl; (methyl) acrylamide and derivatives thereof such as acrylamide, Methacrylamide, N-methylol-acrylamide; (methyl) glycidyl acrylate etc. contains the monomer of epoxy radicals; Unsaturated nitrile such as acrylonitrile, methacrylonitrile; Vinyl aromatic compounds such as styrene, p-methylstyrene etc.Other vinyl monomer is usually with 30 weight % or below the 30 weight %, and the following copolymerization ratio of preferred 20 weight % or 20 weight % is used.
In the present invention, as masking material, can use alkane (that is alkane).As alkane, from forming the viewpoint of through hole easily at normal temperatures, preferred normal temperature is the alkane of solid down.The fusing point of alkane is preferred more than 15 ℃ or 15 ℃, and is more preferred more than 20 ℃ or 20 ℃, preferred especially more than 25 ℃ or 25 ℃.If the fusing point of alkane is low excessively, when forming perforation, need to reduce the operating environment temperature by mechanical processing method, or cooling combined, be not preferred on the energy cost this point.
As the preferred concrete example of alkane, can enumerate hexadecane, heptadecane, octadecane, nonadecane, eicosane, heneicosane, docosane, melissane, heptacontane (ヘ プ コ Application Application) etc.Alkane can use more than 2 kinds or 2 kinds separately alone or in combination.Alkane also can be the mixture more than 2 kinds or 2 kinds, and at this moment, even contain the low melting point alkane, but as long as the fusing point of mixture is preferably then can use well more than 15 ℃ or 15 ℃.Equally, alkane also can contain the impurity of sneaking into when synthetic etc.As alkane, can use commercially available dystectic alkane.
As soluble polymer, with the adaptation excellence of porous resin base materials such as stretchable porous PTFE sheet, form perforation easily by mechanical processing method, forming operation or catalyst in perforation adheres in the operation etc. and can not peel off, and can use solvent easily to dissolve after using as masking material and remove on this point preferred especially PMMA.Be the high-melting-point alkane of solid at normal temperatures preferably equally, also.
In the present invention, as the liquid or the solution that contain in the loose structure that is dipped in porous resin base material, can use and contain the liquid or the solution that can form the compound of solid by chemical reaction.Compound as forming solid by chemical reaction is typically polymerizable monomer.
As polymerizable monomer, use monofunctional monomer, preferred use only has the monofunctional monomer of an acryloyl group or methacryl.When use has the polyfunctional monomer of the functional group more than two senses or two senses,, become insoluble or slightly solubility, can not carry out solvent extraction solvent owing to form cross-linked structure by polymerisation, therefore not preferred.
As monofunctional monomer, so long as can form after the polymerisation the material of solvent polymer soluble, then there is no particular limitation.As the object lesson of monofunctional monomer, can use to form acrylate or the methacrylate that uses in the above-mentioned soluble polymer.Wherein, preferable methyl methyl acrylate, methyl acrylate, isobornyl acrylate, isobornyl methacrylate etc.
The polymer that is generated by these polymerizable monomers has solubility for dimethylbenzene, MEK, acetone and other organic solvent.These polymerizable monomers can use more than 2 kinds or 2 kinds separately alone or in combination.
In order to contain easily in the loose structure that is dipped in porous resin base material, polymerizable monomer preferred viscosities and surface tension are hanged down the person, in this, and special preferable methyl methyl acrylate.But,, also can reduce viscosity and impregnation by heating even the high polymerizable monomer of viscosity contains when being dipped in porous resin base material.The high polymerizable monomer of surface tension can reduce surface tension and contain and be dipped in porous resin base material by adding surfactant.
When adopting the machining perforation, from preventing the viewpoint of burr, polymerizable monomer preferably can form hard and crisp polymer.Generate the high person of glass transition temperature of polymer, when adopting the machining perforation, even produce frictional heat, the temperature of working position rises, and also can not soften, and is therefore preferred.In this, preferably generate the isobornyl methacrylate of the polymer of glass transition temperature height to 180 ℃.
In polymerizable monomer, use dissolved the solution that makes the polymer that the polymerizable monomer polymerization obtains in advance (below, be sometimes referred to as " polymerizable monomer solution ") time, the volume contraction that produces in the time of can suppressing the polymerizable monomer polymerization, thus, can suppress the warpage or the distortion of porous resin base material, furtherly, can bore a hole accurately, therefore preferred.The concentration of polymer can suitably be selected in the too high scope of viscosity that can not make monomer solution, but is generally 50 weight % or below the 50 weight %, preferred 30 weight % or below the 30 weight %.The number-average molecular weight of polymer preferred 10000~1000000.The molecular weight of polymer is crossed when hanging down, and the inhibition effect of volume contraction diminishes, when too high, to the dissolubility reduction of monomer.
As the method that makes the polymerizable monomer polymerization, the legal and light polymerization method of hot polymerization is arranged.For shortening the operating time, preferably adopt light polymerization method.When the film thickness of porous resin base material was thick, light was difficult to see through, and therefore, this moment, the preferred hot polymerization that uses was legal.
During photopolymerization, in polymerizable monomer or polymerizable monomer solution, add Photoepolymerizationinitiater initiater.The adding proportion of Photoepolymerizationinitiater initiater is that benchmark is generally 0.1~5 weight % with the monomer total amount.As Photoepolymerizationinitiater initiater, as dehydrogenation type Photoepolymerizationinitiater initiater, can enumerate benzophenone, thioxanthones etc., as the Photoepolymerizationinitiater initiater of molecule internal fissure, can enumerate alpha-aminoalkyl benzophenone, Alpha-hydroxy alkyl phenones, oxidation acylphosphanes etc.
When carrying out thermal polymerization,, in polymerization rerum natura monomer or polymerizable monomer solution, add peroxide such as azo-compound such as azodiisobutyronitrile or cumyl peroxide as thermal polymerization.The adding proportion of thermal polymerization is that benchmark is generally 0.1~5 weight % with the monomer total amount.
In polymerization rerum natura monomer or the polymerizable monomer solution, except that polymerization initiator, optionally, can also add additives such as surfactant, antioxidant, sensitising agent, lubricant, releasing agent.
As the method that polymerizable monomer is contained in the loose structure that is dipped in porous resin base material, can use The tape casting or infusion process.After the impregnation, look the kind that is added into the polymerization initiator in the polymerizable monomer, carry out illumination and penetrate or heat, carry out polymerisation, generate the polymer of solid.
3.
The manufacture method of the porous resin base material of perforation
Among the present invention, by the porous resin base material that the series of processes manufacturing of following operation 1~4 is bored a hole, this series of processes comprises:
(1) includes the operation 1 of immersion fluid or solution at the loose structure of porous resin base material;
(2) operation 2 that forms solid by the liquid or the solution of impregnation;
(3) form the operation 3 that runs through a plurality of perforation of second surface from the first surface of the porous resin base material that in loose structure, has solid; And
(4) with solid fusion or dissolving, the operation 4 of removing in the loose structure.
Like this, method of the present invention has following feature, in the loose structure of porous resin base material, contains immersion fluid or solution, form solid by the liquid of impregnation or solution after, bore a hole.
In the perforation, can use mechanical processing method.Porous resin base material and since loose structure in filled by solid, therefore, perforation can with the perforation of atresia matter resin base material is similarly implemented.
As porous resin base material, can use the porous resin sheet usually.As the porous resin sheet, preferred porous fluoride resin sheet, more preferred stretchable porous PTFE sheet.Stretchable porous PTFE sheet, the fine structure with the node that contains fibrillation and link mutually by this fibrillation is as loose structure.
In operation 1, preferably by The tape casting or infusion process with liquid or solution impregnation in the loose structure of porous resin base material.Liquid as using can use the material that has freezing point or fusing point in above-mentioned-150~150 ℃ of scopes.As such material, preferred water, alcohol, hydrocarbon, polymer or the mixture more than 2 kinds or 2 kinds in them.In addition, have the material of freezing point or fusing point in-150~150 ℃ scope, preferred fusing point is at the alkane more than 15 ℃ or 15 ℃.
In operation 1, the liquid that the material (for example, water, alcohol, hydrocarbon, polymer) that will have freezing point or fusing point in-150~150 ℃ scope is made above the temperature of freezing point or fusing point contains in the loose structure that is dipped in porous resin base material.In operation 2, this material is solidified at freezing point or fusing point or the temperature below it, become solid.
In operation 3, in loose structure, exist under the state of solid and bore a hole.In the operation 4 behind perforation process, the fusion under the temperature that surpasses freezing point or fusing point of this material is removed.When the material of impregnation is high-melting-point, also can use the solvent stripping.
As the solution that uses in operation 1, can use fusing point is 15~30 ℃ the soluble polymer or the solution of alkane.When using such solution, in operation 1, the solution of impregnation soluble polymer or alkane in the loose structure of porous resin base material, in operation 2, solvent flashing forms the solid of polymer or alkane.In operation 3, in loose structure, exist under the state of solid and bore a hole.In the operation 4 behind perforation process, this solid is removed with dissolution with solvents.
In operation 1,, can use and contain the liquid or the solution that can form the compound of solid by chemical reaction as liquid or solution.Can preferably carry out the polymerizable monomer that polymerisation forms polymer by the compound that chemical reaction forms solid by heat or light.As containing the liquid or the solution that can form the compound of solid by chemical reaction, can use except that polymerizable monomer, also contain the polymerizable monomer solution of the polymer that the polymerization by this polymerizable monomer obtains.As polymerizable monomer, the acrylate or the methacrylate of preferred simple function.
When using polymer monomer etc., in operation 1, impregnation contains the liquid or the solution that can form the compound of solid by chemical reaction in the loose structure of porous resin base material, in operation 2, makes this compound carry out chemical reaction and forms solid.In operation 3, in loose structure, exist under the state of solid and bore a hole.In the operation 4 after perforation, this solid is removed with dissolution with solvents.
In perforation process 3, by for example i) method of machine drilling, ii) carry out etching method, iii) use the ultrasonic head (ヘ ッ De) that has 1 oscillator at leading section at least by light ablation method, push the front end of this oscillator, apply the method that ultrasonic energy is bored a hole, form perforation.
The first surface and the second surface of so-called porous resin base material are meant the part with big surface area.For example, when porous resin base material was sheet, so-called first surface and second surface were not the surfaces of the part of thin thickness, but the surface of open and flat portions (the just surface of sheet and the back side).
As method for punching, preferred mechanical perforation method or use the ultrasonic head that has an oscillator at leading section is at least pushed the front end of this oscillator, applies the method (the instrument front end of making carries out the method for punching of ultrasonic vibration) that ultrasonic energy is bored a hole.As machine drilling method (mechanical processing method), can enumerate punching method, punch method, boring processing method etc.By ultrasonic vibration, process velocity increases, and operability improves.
Sponges etc. are rich in flexibility or flexible porous resin material, and are same with elastomeric material, usually, maybe under the temperature or near the temperature the first order transition point below this, can carry out the processing of precision favorable mechanical at the resin first order transition point.But, contain the porous resin material of loose structure in a large number, at first order transition point maybe under the temperature below this, during machining because near the fragility the perforated portion is difficult to keep shape.
The present invention has following feature, is filled in state in the loose structure of porous resin base material by making with solid, can easily carry out machine drilling.One of other characteristic points of excellence of the present invention are, by selecting to have the freezing point that depends on application target or the material of fusing point, and can it doesn't matter that processing temperature is selected on ground with the first order transition point of the resin that constitutes porous resin base material.If the macromolecule that will can remove easily later on is filled in the loose structure of porous resin base material, can easily carry out machining equally.
When porous resin base material is continuous sheet, list, for example, the perforation process of impregnation operation, refrigerating work procedure, employing machining carries out these operations successively, can obtain goods continuously.Behind the perforation process, be warming up to the above temperature of freezing point or fusing point or its, make solid become liquid and remove.
During solution such as use polymer solution, the dry operation of desolvating of removing also can be set replace above-mentioned refrigerating work procedure.After the perforation process, the operation of removing with the dissolution with solvents solid is set.
The porous resin base material of the perforation that obtains by manufacture method of the present invention is looked purposes, has perforation (through hole) in a plurality of places of regulation.The porous resin base material of perforation can be owing to perforation be out of shape, and at the periphery of the internal face that comprises perforation, loose structure can be not destroyed, can not produce burr, has again, and perforation has sharp seamed edge.
Fig. 1 is with the microphotograph of the perforated portion of the stretchable porous PTFE sheet of embodiments of the invention 1 perforation, as can be known, has formed the perforation with sharp seamed edge.In contrast, Fig. 2 is by the microphotograph of comparative example 3 with the perforated portion of the stretchable porous PTFE sheet of stretchable porous PTFE sheet perforation, can observe the generation of burr or the partial destruction of loose structure.
The porous resin base material of the perforation that obtains by manufacture method of the present invention also can keep loose structure at the internal face of perforation, therefore is suitable as diffusion barrier.If the internal face in perforation adheres to conductive metal, can be used as circuit and connect with material or anisotropic conductive material use.Porous resin base material is when having the stretchable porous PTFE sheet of fine structure of the node that contains fibrillation and link by this fibrillation, owing to can keep loose structure, to be rich in flexibility or elasticity, and relative dielectric constant is little, and electrical insulating property is excellent especially.Stretchable porous PTFE base material is because even the chemical stability excellence as medical device, also is very useful.
4.
Manufacture method (1) with the porous resin base material of conductive drilled inner wall surface
Of the present invention with the perforation internal face optionally conduction porous resin base material (for example, the anisotropic conductive sheet) manufacture method is, by the internal face optionally method of conduct electricity of following operation I~VI series of processes with perforation, this series of processes comprises:
(1) in the loose structure on the two sides of containing porous resin base material, impregnation soluble polymer or alkane maybe can form the operation I of the compound of solid by chemical reaction;
(2) maybe can form solid by the soluble polymer of impregnation or alkane by the compound that chemical reaction forms solid, the two sides that is formed on porous resin base material have the layer of solid and in loose structure impregnation the operation II of composite sheet of structure of solid;
(3) form the operation III that is through to a plurality of perforation on the 2nd surface from the first surface of this composite sheet;
(4) containing the respectively operation IV of the catalyst of the surface attachment promotion metal ion reduction reaction of the composite sheet of the internal face of perforation;
(5) remove the operation V of solid from composite sheet; And
(6) utilize the above-mentioned catalyst that adheres to and remain in each internal face of boring a hole of porous resin base material, adhere to the operation VI of conductive metal at this internal face.
In operation I, impregnation soluble polymer or alkane maybe can form the compound of solid by chemical reaction in the loose structure on the two sides that comprises the porous resin base material of electrical insulating property (being generally the porous resin sheet).
In operation II, maybe can form solid by the compound that chemical reaction forms solid by the soluble polymer of impregnation or alkane, the two sides that is formed on porous resin base material has the solid layer and solid contains the composite sheet that is dipped in the structure in the loose structure.
As the method that forms composite sheet, following method is arranged: in operation I, solution or fused solution by curtain coating soluble polymer or alkane on the two sides of porous resin base material, or porous resin base material is immersed in the solution of soluble polymer or alkane or the method in the fused solution, impregnation soluble polymer or alkane are then, in operation II, by solvent flashing or be cooled to freezing point or two sides that fusing point or the method for temperature below it are formed on porous resin base material has the soluble polymer of solid or the layer of alkane, and the soluble polymer of solid or alkane contain the composite sheet that is dipped in the structure in the loose structure.
As the additive method that forms composite sheet, following method is arranged, in operation I, have by curtain coating on the two sides of porous resin base material and contain the liquid or the solution that can form the compound of solid by chemical reaction, perhaps porous resin base material is immersed in the liquid that contains this compound or the method in the solution, this compound of impregnation, then, in operation II, by formed the method for solid by chemical reaction, the two sides that is formed on porous resin base material has the solid layer and solid contains the composite sheet that is dipped in the structure in the loose structure.
Under the latter's the situation, in operation I, the following method of preferred employing: contain liquid or the solution that carries out the polymerizable monomer of polymerisation formation polymer by heat or light by curtain coating on the two sides of porous resin base material, perhaps porous resin base material is immersed in to contain and carries out polymerisation by heat or light and form the liquid of polymerizable monomer of polymer or the method in the solution, the impregnation polymerizable monomer, then, in operation II, by made the polymerizable monomer polymerization form the method for the polymer of solid by heat or light, the two sides that is formed on porous resin base material has the polymeric layer of solid, and the polymer of solid contains the composite sheet that is dipped in the structure in the loose structure.
The solution that uses soluble resin or alkane is in the two sides of porous synthetic resin sheet curtain coating, or when containing in the space that is dipped in loose structure, as solvent, can use, for example, and ketones such as acetone, MEK; Ester such as ethyl acetate, butyl acetate class; Halogenated hydrocarbons such as dichloroethanes, carrene; Dimethylbenzene, toluene etc. are aromatic hydrocarbon based; Oxolane, chloroform, diacetone alcohol, dimethyl formamide isopolarity organic solvent etc.
Solvent can suitably be selected according to the kind of soluble polymer, alkane and porous resin base material.For example, use stretchable porous PTFE sheet as porous resin base material, when using polymethyl methacrylate (PMMA) as soluble polymer, as solvent, preferred use can be dissolved PMMA, and soaks into acetone, oxolane isopolarity solvent to the loose structure of stretchable porous PTFE sheet easily.
The fusing point of soluble polymer is low, preferably is heated to temperature below 100 ℃ or 100 ℃ can fusion the time, can use its fused solution to carry out curtain coating or impregnation.The fusing point of alkane is so not high yet, preferably, if fusing point is below 100 ℃ or 100 ℃, can use to be heated to fusing point or the above temperature of fusing point and the fused solution of fusion carries out curtain coating or impregnation.
Manufacture method as composite sheet, for example, use stretchable porous PTFE sheet as the porous synthetic resin sheet, use PMMA as masking material, contain when being dipped in the loose structure, the preferred use can dissolved PMMA, and soaks in acetone to the loose structure of stretchable porous PTFE sheet, the oxolane isopolarity solvent solution with the dissolving of the concentration about 10~30 weight % PMMA easily.Be immersed in stretchable porous PTFE sheet in this solution lentamente and make in the loose structure not residual air, as long as make it impregnation.According to infusion process, can use in the loose structure of the filling porous resin base material of soluble polymer, and simultaneously, surface portion is also covered by soluble polymer.This soluble polymer layer performance is as the function of mask layer.When using the high-melting-point alkane, similarly, the two sides of the coated porous resin base material of alkane forms mask layer.
Use stretchable porous PTFE sheet as porous resin base material, use PMMA as masking material, when the two sides of stretchable porous PTFE sheet forms the PMMA film as mask layer, with above-mentioned same, preferred employing will have been dissolved PMMA with the concentration about 10~40 weight % in acetone, oxolane etc. the method for solution casting on the two sides of stretchable porous PTFE sheet.At this moment, stretchable porous PTFE sheet is heated to temperature about 30~60 ℃, preferred limit promotes the evaporation limit curtain coating of solvent.According to The tape casting, not only the surface portion of porous resin base material is also soaked into by soluble polymer in subsurface loose structure.
When using alkane, preferably adopt heating and melting to be the alkane of solid at normal temperatures, stretchable porous PTFE sheet is immersed in the fused solution that obtains, with the method in the filling porous structure of alkane.
If in the loose structure with soluble polymer or the filling porous resin base material of alkane, even when forming perforation by mechanical processing method, also can prevent to add near the Ministry of worker is near the perforated portion loose structure fragmentation.If in the loose structure with soluble polymer or the filling porous resin base material of alkane, the loose structure in the time of can fully keeping perforation formation, but the surface portion of the internal face that the interpolation of catalyst only limits to bore a hole.
On the other hand, only when the near surface of porous resin base material forms mask layer, when forming perforation by mechanical processing method, near the performance of keeping of the loose structure perforation reduces, but in the operation of the internal face that catalyst is attached to perforation, though depend on the porosity of porous resin base material, the degree of depth about catalyst can being attached to from the surface of internal face to number μ m.Therefore, on porous resin base material, soluble polymer or alkane contained when being dipped in the loose structure by The tape casting or infusion process, degree in its impregnation of control, when two surfaces form mask layer, if suppress the impregnation amount in loose structure, behind perforation process, can be with catalyst fully attached to the resin part of internal face of perforation.
In the present invention, form a plurality of perforation (through hole) that run through second surface from the first surface of composite sheet.As the method that forms perforation, can enumerate, i) method of machine drilling, ii) carry out etching method or iii) use the ultrasonic head that has 1 oscillator at leading section at least by light ablation method, by pushing the front end of this oscillator, apply method that ultrasonic energy bores a hole etc.
Carry out machine drilling, can adopt, for example, mechanical processing methods such as pressing, punching method, boring method.According to mechanical processing method, can form at an easy rate that to have 100 μ m or 100 μ m usually above, most cases is the through hole in the above bigger aperture of 300 μ m or 300 μ m.
Form through hole by the laser irradiation, the preferred employing by have the light shielding plate of independently a plurality of separately light transmission parts (peristome) on the pattern form of regulation to the surface irradiation laser of composite sheet, forms the method for the through hole of pattern form thus.Light is from a plurality of peristomes of light shielding plate see through and shine local etched and the formation through hole.According to this method, can form the little through hole in aperture.
In supercritical ultrasonics technology, use the ultrasonic head that has 1 oscillator at leading section at least, by applying ultrasonic energy, on composite sheet, form the perforation of pattern form.Only before oscillator the composite sheet of end in contact near apply ultrasonic energy, by from hyperacoustic vibrational energy, local temperature rises, resin is easily cut off and is removed, and forms perforation.
The shape of perforation (through hole) can be arbitrary shapes such as circle, ellipse, star, octagonal, hexagon, quadrangle, triangle.The aperture of perforation, the purposes field being fit to the small-bore can be set to 5~100 μ m usually, about preferred 5~30 μ m, other aspects are in the field that is fit to bigger aperture, usually can be set to 100~3000 μ m, preferred 150~2000 μ m are about more preferred 200~1500 μ m.Preferred a plurality of perforation is fit to the distribution of electrodes of circuit substrate etc., forms the pattern form of regulation.
When forming perforation on composite sheet, the resin portion of the loose structure of porous resin base material is exposed on the internal face of perforation.The situation of stretchable porous PTFE sheet, the resin portion of loose structure are fibrillation and the nodes that is formed by PTFE.
In the present invention, on the surface of the composite sheet that contains each internal face of boring a hole, adhere to the catalyst that promotes the metal ion reduction reaction.As the method for adhering to conductive metal on the internal face of the perforation of porous resin base material, preferred electroless plating covers method.Cover in the method at electroless plating,, adhere to the catalyst that promotes chemical reduction reaction in advance usually in the place of wanting to separate out coating.Only carry out electroless plating when covering at the internal face of the perforation of porous resin base material, must be only at this place's attached catalyst.In case coating is adhered in the place beyond the internal face of perforation, each conducting portion that forms by the conductive metal attached to the internal face of each perforation has risk of short-circuits.
A plurality of perforation are set on composite sheet, when the surface attachment catalyst of composite sheet of the internal face that contains each perforation, also attached catalyst on the resin portion of the loose structure that exposes on the internal face of the perforation of porous resin base material.
Add the catalyst of the chemical reduction reaction that promotes metal ion, can fully stir on the limit, the composite sheet that the limit will form perforation for example is impregnated into that palladium-tin colloid catalyst adheres in the liquid.
In the present invention, after the above-mentioned operation, from composite sheet, remove soluble polymer or alkane.The soluble polymer layer or the alkane layer that are positioned at the two sides of porous resin base material can be peeled off and remove, but preferred soluble polymer or the method for alkane by using dissolution with solvents to remove that is immersed in the loose structure with containing that adopt.
Remove the solvent of soluble polymer or alkane as being used in dissolving, so long as can dissolve the material of soluble polymer or alkane, then there is no particular limitation, but preferably show the solvent of solubility or slightly solubility for porous resin base material.Use stretchable porous PTFE as porous resin base material, when using PMMA,, preferably use acetone, oxolane isopolarity solvent as solvent as masking material.The situation of alkane also can use dissolvings such as acetone to remove.Usually, dissolving is removed soluble polymer or alkane is undertaken by the method that composite sheet is immersed in the solvent.
When composite sheet was removed soluble polymer or alkane, catalyst adhered to and remains on the internal face of perforation of porous resin base material.
In the present invention, utilize the catalyst on the internal face of the perforation (through hole) adhere to and remain in the porous synthetic resin sheet, with conductive metal attached on this internal face.As the method for adhering to conductive metal, preferably adopt electroless plating to cover method.
Carry out before electroless plating covers, activation remains in catalyst on the internal face of perforation (for example, palladium-Xi).Particularly, by impregnated in as in the commercially available acylate of plating catalyst activation usefulness etc. dissolving tin, activating catalyst.
Be immersed in electroless plating by the porous resin base material that will on the internal face of perforation, adhere to catalyst and cover in the liquid, can only separate out conductive metal, thus, form the conducting portion (also being called conduction road or electrode) of tubular at the internal face of perforation.As conductive metal, can enumerate, copper, nickel, silver, gold, nickel alloy etc., but when needing high conductivity especially, preferably use copper.
When using stretchable porous PTFE sheet, plating particle (crystal grain) is originally separated out in the mode of exposing to the fibrillation of the internal face of the perforation of porous PTFE sheet with tight the entanglement, therefore, by the control plating time, can control the attachment state of conductive metal.If the plating time is too short, be difficult to obtain electric conductivity at film thickness direction.During the electroless plating overlong time, conductive metal becomes metal derby, and under common use compression was born a heavy burden, it is difficult that the elastic recovery of sheet becomes.By being adjusted into the plating amount of appropriateness, can form the conductive metal layer with the state of keeping loose structure, can give the electric conductivity that the flexible while also can give film thickness direction.
The rugosity of the resin portion of loose structure (for example, the fibriilar rugosity of stretchable porous PTFE sheet) preferred 50 μ m or below the 50 μ m.About preferred 0.001~5 μ m of the particle diameter of conductive metal.For keeping loose structure and elasticity, the adhesion amount of conductive metal preferably is set to about 0.01~4.0g/ml.
The conducting portion of the tubular of above-mentioned making be to improve antioxygen and electric contact, preferably uses antioxidant or coats with the alloy of noble metal or noble metal.As noble metal, on the little this point of resistance, preferred palladium, rhodium, gold.The thickness of the clad of noble metal etc., preferred 0.005~0.5 μ m is more preferably 0.01~0.1 μ m.The thickness of this clad is crossed when thin, electric contact to improve effect little, when blocked up, clad is peeled off easily, and is therefore, all not preferred.For example, with golden coating conducting portion the time, behind the nickel coating conducting metal level about 8nm, the method for carrying out immersion gold plating is effective.
According to manufacture method of the present invention, can run through the perforation of second surface in a plurality of local formation of porous resin base material from first surface, in addition, can be manufactured on and have the conducting portion and each conducting portion that form by conductive metal on the internal face of perforation and can only on film thickness direction, give the anisotropic conductive sheet of electric conductivity attached to the resin portion of loose structure.
The limit is with reference to accompanying drawing, and the limit describes above-mentioned manufacture method as example with the situation of using soluble polymer or alkane.Fig. 3 is the flow chart that an example of manufacture method of the present invention is shown.Shown in Fig. 3 (a), prepare porous resin base material (for example, stretchable porous PTFE sheet) 1.Shown in Fig. 3 (b), soluble polymer 2 contained be dipped in the loose structure that comprises this two sides, the composite sheet 3 of soluble polymer that had in soluble polymer layer (clad), the loose structure also impregnation on the modulation two sides.Then, shown in Fig. 3 (c),, make the composite sheet that forms a plurality of perforation 4,4 with the composite sheet perforation.
Shown in Fig. 3 (d),, adhere to plating catalyst 5 on the surface of the internal face composite sheet that contains each perforation.Then, shown in Fig. 3 (e), when soluble polymer is removed in dissolving, plating catalyst attached to soluble polymer layer (mask layer) surface on the two sides of porous resin base material is removed with soluble polymer, the catalyst on the internal face of only residual perforation attached to porous resin base material.Fig. 3 (f) illustrates electroless plating and covers operation.Carry out electroless plating when covering, plating particle (conductive metal particle) is only separated out on the internal face of the perforation of having adhered to catalyst, forms conductive metal layer 6.Like this, only can obtain optionally porous resin base material 7 with the internal face conductionization of perforation.
In above-mentioned manufacture method, as porous resin base material, preferably use the porous resin sheet as the porous resin sheet, preferred porous fluoride resin sheet, as loose structure, be more preferably to have and comprise fibrillation and by the stretchable porous PTFE of the fine structure of the interconnective node of this fibrillation.Soluble polymer or alkane preferably are solid under the temperature in 15~30 ℃ scope.
In operation I, solution or fused solution at the two sides of porous resin base material curtain coating soluble polymer or alkane, perhaps porous resin base material is immersed in the solution or fused solution of soluble polymer or alkane, then, in operation II, by solvent flashing or be cooled to freezing point or fusing point or the method for temperature below it, the two sides that is formed on porous resin base material has the soluble polymer of solid or alkane layer, in loose structure impregnation the composite sheet of structure of the soluble polymer of solid or alkane be preferred.
In operation III, preferably pass through i) method of machine drilling, ii) carry out etching method or iii) use the ultrasonic head that has 1 oscillator at leading section at least by light ablation method, push the front end of this oscillator, apply the method that ultrasonic energy is bored a hole, on composite sheet, form a plurality of perforation.
In operation V, use to demonstrate insoluble or slightly solubility, but soluble polymer or alkane are shown deliquescent solvent porous resin base material, it is preferred dissolving soluble polymer or alkane and removing.In operation V, also can and remove the fusion of soluble polymer or alkane.
In operation VI, preferably overlay on each internal face of boring a hole and adhere to conductive metal by electroless plating.According to manufacture method of the present invention, the porous resin base material of the internal face conductionization of perforation, can be produced on the internal face that runs through a plurality of perforation of second surface from first surface and have the conducting portion that forms by conductive metal, but each conducting portion is only given the anisotropic conductive sheet of electric conductivity on film thickness direction attached to the resin portion of loose structure.
For above-mentioned manufacture method, mainly the situation of using soluble polymer or alkane is set forth, but also can by use polymerizable monomer for example such can replace them by the compound that chemical reaction forms solid, similarly, form the mask layer manufacturing only at the porous resin base material (anisotropic conductive sheet) of the internal face conductionization of perforation by solid matter.
5.
The manufacture method of the porous resin base material of conductive drilled inner wall surface (2)
Of the present invention is by containing following operation i~viii with another manufacture method of porous resin base material (for example, anisotropic conductive sheet) of the internal face conductionization of perforation optionally:
(1) on the two sides of porous resin base material (A), as mask layer, lamination porous resin layer (B) reaches (C), forms the operation i of the laminated body of 3 layers of formation;
(2) in each loose structure in this laminated body, impregnation soluble polymer or alkane maybe can form the operation ii of the compound of solid by chemical reaction;
(3) maybe can form the operation iii of solid by the compound that chemical reaction forms solid by the soluble polymer of impregnation or alkane;
(4) form the operation iv that runs through a plurality of perforation of second surface from the first surface that in each loose structure, has the laminated body of solid;
(5) dissolving solid, the operation v that removes in each loose structure;
(6), adhere to the operation vi that promotes the reduction of metal ion catalyst for reaction on the surface of the laminated body that comprises each internal face of boring a hole;
(7) peel off the operation vii of the mask layer on two sides from porous resin base material (A); And
(8) utilize the above-mentioned catalyst that adheres to and remain in each internal face of boring a hole of porous resin base material (A), adhere to the operation viii of conductive metal at this internal face;
Series of processes with the method for internal face conductionization of perforation.
In said method, preferably, in operation ii, by solution or fused solution, perhaps laminated body is immersed in the solution or fused solution of soluble polymer or alkane impregnation soluble polymer or alkane at the two sides of laminated body curtain coating soluble polymer or alkane, then, in operation iii, by solvent flashing or be cooled to freezing point or fusing point or the method for temperature below it, form the polymer or the alkane of solid.
In addition, in said method, preferably, in operation ii, in each loose structure of laminated body, impregnation as can by chemical reaction form solid compound, contain by heat or light and carry out liquid or the solution that polymerisation forms the polymerizable monomer of polymer, then, in operation iii, make the polymerizable monomer polymerization by heat or light, form solid polymer.
The limit is with reference to accompanying drawing, and the limit describes above-mentioned manufacture method as example with the situation of using polymerizable monomer.Fig. 4 is the flow chart that each operation that adopts in the manufacture method of the present invention is shown.As Fig. 4 (A) and (B), on the surface of porous resin base material 41, as mask layer, lamination porous resin layer 42 and 43, the laminated body 44 of 3 layers of formation of formation.As the porous resin layer of mask layer, can be identical with porous resin base material, also can be different.Usually use 3 identical porous resin base materials to form laminated body.
For sheltering the two sides of porous resin base material 41 effectively, preferably that each interlayer fusion is integrated.As porous resin base material and mask layer, when using stretchable porous PTFE sheet, can be the fusion easily of each interlayer is integrated by adding hot pressing, when mask layer need be peeled off, can easily peel off.
Then, shown in Fig. 4 (C), in each loose structure of laminated body 44, impregnation contains the liquid or the solution that can form the compound of solid by chemical reaction.As the compound that can form solid, preferably carry out the polymerizable monomer that polymerisation forms polymer by heat or light by chemical reaction.Containing the liquid or the solution that can form the compound of solid by chemical reaction is except that polymerizable monomer, also contains the solution of the polymer that the polymerization by this polymerizable monomer obtains.
As polymerizable monomer, the acrylate or the methacrylate of the simple function of preference as above-mentioned methyl methacrylate.In polymerizable monomer, add Photoepolymerizationinitiater initiater or thermal polymerization.
Shown in Fig. 4 (D), the liquid of impregnation or the compound in the solution carry out chemical reaction and form solid.In this operation, polymerizable monomer carries out photopolymerization or thermal polymerization, form normal temperature down for solid polymer (for example, PMMA).Like this, obtain whole laminated body 46 that are aggregated the thing filling of 3 layers of laminated body.
Then, shown in Fig. 4 (E), form a plurality of perforation 48 that run through second surface from the first surface of the laminated body that in each loose structure, has solid (polymer).Shown in Fig. 4 (F), from the laminated body 47 that has formed perforation,, in each loose structure, remove with dissolution with solvents solid (polymer).
Shown in Fig. 4 (G),, adhere to promotion reduction of metal ion catalyst for reaction (plating catalyst) on the surface of each internal face of boring a hole that comprises solvent-extracted laminated body 49.At this moment, the porous resin layer 42,43 that is arranged on the two sides prevents the two sides of catalyst attached to porous resin base material 41 as mask layer performance function.
Then, shown in Fig. 4 (H),, obtain the only porous resin base material 51 of attached catalyst on the internal face of perforation from the laminated body 50 upper glass mask layers 42,43 that adhered to the plating catalyst.Shown in Fig. 4 (I), utilize the above-mentioned catalyst of the internal face that adheres to each perforation that remains in this porous resin base material 51, on this internal face, adhere to conductive metal.The adhering to of conductive metal covering method by electroless plating usually carries out.Like this, only can obtain porous resin base material 52 with the internal face conductionization of perforation.
As porous resin base material, preferred porous resin sheet.As the porous resin sheet, preferred porous fluoride resin sheet as loose structure, is more preferably the stretchable porous PTFE sheet of the fine structure with the node that comprises fibrillation and linked mutually by this fibrillation.
In operation iv, preferably pass through i) method of machine drilling, ii) carry out etching method or iii) use the ultrasonic head that has 1 oscillator at leading section at least by light ablation method, push the front end of this oscillator, apply the method that ultrasonic energy is bored a hole, on laminated body, form a plurality of perforation.
In operation v, the preferred use demonstrates insoluble or slightly solubility to porous resin base material, but solid is shown deliquescent solvent, dissolving solid and removing.
In operation vi, on the surface of the laminated body that comprises each internal face of boring a hole, adhere to the catalyst (plating catalyst) that promotes the metal ion reduction reaction.In this manufacture method, before adhering to the plating catalyst, in operation v,, in loose structure, to remove for the dissolving solid, the resin part (for example fibrillation of PTFE) of the internal face of perforation should fully be exposed.Thus, can be with the plating catalyst securely attached to the inner a little resin part of the loose structure that reaches the perforation internal face (the resin part of the degree of depth about from the surface of internal face to number μ m).In operation viii, preferably cover by electroless plating, on the internal face of each perforation, adhere to conductive metal.
Can make according to manufacture method of the present invention, the porous resin base material of the internal face conductionization of perforation, have the conducting portion that forms by conductive metal at the internal face that runs through a plurality of perforation of second surface from first surface, but each conducting portion is only given the anisotropic conductive sheet of electric conductivity on film thickness direction attached to the resin portion of loose structure.
Embodiment
Below, for embodiment and comparative example, the present invention is more specifically illustrated, but the present invention only is defined in these embodiment.The assay method of rerum natura is as follows.
(1) bubbling point (BP):
Adopt the bubbling point of the porous PTFE film of pulling method making to use isopropyl alcohol, measure according to ASTM-F-316-76.
(2) porosity:
Adopt the porosity of the porous PTFE film of pulling method making to measure according to ASTM D-792.
(3) conducting begins to bear a heavy burden:
Use conducting shown in Figure 5 to confirm device, the conducting of measuring anisotropic conductive film begins to bear a heavy burden.Confirm in the device that in conducting shown in Figure 5 anisotropic conductive sheet 501 is placed on has implemented on the gold-plated copper coin (being called " Au plate ") 502, its integral installation is loaded on the weight meter 506.The copper post 503 that uses external diameter 2mm φ applies heavy burden as probe.Measure the resistance value of anisotropic conductive sheet by 4 terminal methods.The 504th, decide current and power supply, 505 is potentiometer.
Prepare area and be that 10cm is square, the porosity is 60%, average pore size is that 0.1 μ m, thickness are the porous PTFE base material of 0.5mm.This porous PTFE base material is the stretchable porous PTFE sheet of making by pulling method, is the material with fine structure of the node that comprises fibrillation and linked by this fibrillation.
Should stretchable porous PTFE sheet impregnated in carry out hydrophilic treated in the ethanol after, contain immersion, and the temperature that is cooled to below 0 ℃ or 0 ℃ makes water-setting solid.Filled in loose structure on the stretchable porous PTFE sheet of the water that solidifies, the diameter that is used in combination through hole is that drift and the punch die of 250 μ m bored a hole.Punching rate is 100 holes/1 minute.Normal temperature is recovered in the perforation back, and the water drying is removed.
The perforated portion of perforated sheet is carried out microscopic examination, as shown in Figure 1, do not subside around the perforation, the internal face of perforation also becomes the face that cuts off along punch face basically.Around the perforation be and the identical density of density in perforated portion place in addition, fine structure is also found to change.
Prepare the stretchable porous PTFE sheet identical materials used with embodiment 1, it contained immersion, be cooled to the following temperature of freezing point or freezing point after, uses according to through-hole diameter and bores a hole as the punch knife of 1mm making.Punching rate needs 4 minutes for getting through 100 holes.After the perforation, recover normal temperature, after the water drying is removed, observe the hole portion of perforated sheet, similarly to Example 1, find distortion or burr around the perforation, the fine structure around the perforation also keep and perforated portion beyond local same shape.
Prepare the stretchable porous PTFE sheet identical materials used with embodiment 1, it contained immersion, be cooled to the following temperature of freezing point or freezing point after, using according to through-hole diameter is that the drill bit that 250 μ m adjust is bored a hole.The revolution of the drill bit of this moment is 100000rpm.Punching rate is to finish in 2 minutes to drill through 100 holes.Normal temperature is recovered in the perforation back, after the water drying is removed, observes the hole portion of perforated sheet, similarly to Example 1, does not have burr around the perforation, does not also observe subsiding of perforated portion periphery.
Prepare the stretchable porous PTFE sheet identical materials used with embodiment 1, it contained immersion, be cooled to the following temperature of freezing point or freezing point after, uses according to through-hole diameter and bores a hole as the punch knife of 1mm making.Apply the ultrasonic vibration of 40kHz, 25W during perforation at point of a knife.
Punching rate is to finish in 2 minutes to drill through 100 holes.Compare with embodiment 2, just can handle with the time of half.Afterwards, recover normal temperature, the water drying is removed, observe perforation, do not find around the perforation to subside or burr, be processed into slick and sly and sharp seamed edge.
Prepare stretchable porous PTFE sheet identical materials with embodiment 1 use.Prepare the acetone soln of polymethyl methacrylate (PMMA) in addition.Can add acetone soln in the container of level dipping in size for the PTFE sheet, by the stretchable porous PTFE sheet of infusion process impregnation, drying is removed acetone, makes the PTFE-PMMA composite sheet.The use through-hole diameter is that the drill bit of 250 μ m is bored a hole to this composite sheet with revolution 100000rpm.Drill through 100 holes and need 4 minutes.Boring is immersed in stretchable porous PTFE sheet in the acetone stripping PMMA, the stretchable porous PTFE sheet that obtains boring a hole after finishing.Microscopic examination is carried out in perforation, do not compared not variation with other local micro organizations around the perforation, the seamed edge of perforation is not found depression or burr.
Comparative example 1
Prepare stretchable porous PTFE sheet identical materials with embodiment 1 use.Under the state of its former state, the use through-hole diameter is that drift and the punch die of 500 μ m bored a hole.Aperture time was handled 100 holes in 1 minute similarly to Example 1.After the processing, observe perforation, produce burr, the aperture that does not keep 500 μ m.In addition, the part of the fine structure around the perforation becomes the scar state, can not keep loose structure.
Comparative example 2
Prepare stretchable porous PTFE sheet identical materials with embodiment 1 use.Under the state of its former state, bore a hole by the punch knife that uses among the embodiment 2.Aperture time is identical with embodiment 2,4 minutes processing 100 holes.After the processing, observe perforation, produce burr.In addition, the periphery of perforation is a collapsed mode, and the fine structure of this part has obviously different with other places as can be seen.
Comparative example 3
Prepare stretchable porous PTFE sheet identical materials with embodiment 1 use.Under the state of its former state, bore a hole by drill bit.Drill bit uses and the identical drill bit of drill bit that uses in embodiment 3, and revolution also is set to 100000rpm.Aperture time is to drill through 100 holes in 2 minutes, similarly to Example 3.After the perforation, observe perforation, as shown in Figure 2, except that the generation burr, observe the scar of the resin that produces owing to rotation, and the fine structure of observing around the portion of hole is the state of fragmentation.
With methacrylic resin (PMMA; Sumitomo Chemical system, trade name " LG6A ") 25g at room temperature is dissolved among the acetone 75g, modulation methacrylic resin solution.The square stretchable porous PTFE sheet of 2cm (the Off ァ イ of Sumitomo Electric Industries Application Port リ マ one Co., Ltd.'s system, trade name " HP-010-30 " will be cut into; Isopropyl alcohol bubbling point 150kPa, the porosity 60%) the marginal not meaning not in its loose structure the residual air limit impregnated in lentamente in the methacrylic resin solution.Confirm stretchable porous PTFE sheet become translucent, methacrylic resin solution contain fully be dipped in its loose structure after, take out about 18 hours of air dry at room temperature.On the composite sheet that obtains like this,, form through holes (perforation) in a plurality of places with 100000rpm with the drill bit of diameter 250 μ m.
Then, after the composite sheet that has formed through hole is immersed in the ethanol 1 minute and carries out hydrophiling, under 60 ℃ temperature, be immersed among the メ Le プ レ one ト PC-321 that dilution makes for the メ Le テ ッ Network ス (strain) of 100ml/L 4 minutes, carry out conditioning and handle.In addition, this composite sheet flooded 1 minute in 10% sulfuric acid after, as pre-preg, be dissolved in the solution of 0.8% hydrochloric acid dipping 2 minutes at the エ Application プ レ one ト PC-23 6 that メ Le テ ッ Network ス (strain) is made with the ratio of 180g/L.
Have again, this composite sheet was dissolved in エ Application プ レ that 3% メ Le テ ッ Network ス (strain) makes, one ト activator 444,1% エ Application プ レ one ト assistant activator, 3% the aqueous solution of hydrochloric acid dipping 5 minutes being dissolved at the エ Application プ レ one ト PC-236 that メ Le テ ッ Network ス (strain) is made with the ratio of 150g/L, with surface and the through hole wall of tin-palladium colloidal particle attached to composite sheet.
Then, this composite sheet is immersed in the acetone, extraction (dissolving is removed) contains the methacrylic resin that is immersed in the stretchable porous PTFF sheet, only obtains the stretchable porous PTFE sheet at the wall adhesion palladium-Xi particle of the through hole of stretchable porous PTFE sheet.In addition, this sheet is immersed in the solution of the PA-360 that makes with pure water dilution メ Le テ ッ Network ス (strain) with the ratio of 50ml/L dissolving tin, activating catalyst.
In initial plating bath, added メ Le プ レ one ト Cu-3000A, メ Le プ レ one ト Cu-3000B that メ Le テ ッ Network ス (strain) makes, メ Le プ レ one ト Cu-3000C, メ Le プ レ one ト Cu-3000D separately 5%, in the electroless plating copper liquid of メ Le プ レ one ト Cu-3000 stabilizing agent 0.1%, the limit is carried out sufficient air and is stirred, limit this stretchable porous PTFE sheet of dipping 30 minutes is only separated out copper particle and conduction on the wall of through hole.Then, the contact for antirust, raising and device carries out the gold-plated of copper particle.In accordance with the following methods gold-plated, adopt immersion gold plating method by nickel.
As pre-preg, the stretchable porous PTFE sheet that will adhere to copper particle on the wall of through hole was immersed in the activator オ one ロ テ ッ Network SIT auxiliary agent (80ml/L) that ア ト ッ テ ッ Network makes after 3 minutes, as adding catalyst, adding the オ one ロ テ ッ Network SIT activator コ Application Network (125mg/L) that ア ト ッ テ ッ Network is made, dipping is 1 minute in the initial plating bath liquid of the activator オ one ロ テ ッ Network SIT auxiliary agent (80ml/L) that ア ト ッ テ ッ Network is made, behind the オ one ロ テ ッ Network SIT that ア ト ッ テ ッ Network is made, flooded 1 minute adhesion palladium catalyst on copper particle again in the maceration extract (25ml/L).
Then, added in the electroless plating nickel liquid of sodium hypophosphite (20g/L), trisodium citrate (40g/L), ammonium borate (13g/L), nickelous sulfate (22g/L) dipping stretchable porous PTFE sheet 5 minutes at initial plating bath liquid, with this copper particle nickel plating.
Afterwards, [メ Le プ レ one ト AU-6630A (200ml/L), メ Le プ レ one ト AU-6630B (100ml/L), メ Le プ レ one ト AU-6630C (20g/L), the gold sodium sulfide aqueous solution are (as gold at immersion gold plating liquid that メ Le テ ッ Network ス makes, be 1.0g/L)] the middle dipping 5 minutes, carry out the gold-plated of copper particle, only obtain adopting the anisotropic conductive sheet that the stretchable porous PTFE sheet of conductionization on the wall of the through hole of 1.00mm is made.
It is square that the anisotropic conductive sheet that will be basement membrane with the stretchable porous PTFE sheet that obtains according to the method described above is cut into 10mm, measures conducting with device shown in Figure 5 and begin to bear a heavy burden.The copper post that uses 2mm φ is as probe, and 1 electrode of contact of will popping one's head in is measured resistance value with 4 terminal methods.Consequently, pushing under the heavy burden 5.0MPa, is 3.1 Ω.
The rustless steel container that alkane (pure pharmaceutical worker already makes with light, 68~70 ℃ of fusing points) is put on the heating plate that is placed on 80 ℃ dissolves.Be cut into the square foursquare stretchable porous PTFE sheet of 2cm (the Off ァ イ of Sumitomo Electric Industries Application Port リ マ one Co., Ltd.'s system, HP-010-30) marginal not meaning not in the space of loose structure the residual air limit impregnated in lentamente in the alkane of dissolving.After confirming that stretchable porous PTFE sheet becomes translucent and soaks into fully, take out at room temperature natural cooling curing.On the composite sheet that obtains like this,, form through holes (perforation) in a plurality of places with 100000rpm with the drill bit of diameter 250 μ m.
After the composite sheet that has formed through hole was immersed in the ethanol 1 minute and carries out hydrophiling, under 60 ℃ temperature, dipping was 4 minutes in the メ Le プ レ one ト PC-321 that dilution is made for the メ Le テ ッ Network ス (strain) of 100ml/L, carries out conditioning and handles.In addition, this composite sheet flooded 1 minute in 10% sulfuric acid after, as pre-preg, be dissolved in the solution of 0.8% hydrochloric acid dipping 2 minutes at the エ Application プ レ one ト PC-236 that メ Le テ ッ Network ス (strain) is made with the ratio of 180g/L.
Have again, this composite sheet was dissolved in エ Application プ レ that 3% メ Le テ ッ Network ス (strain) makes, one ト activator 444,1% エ Application プ レ one ト assistant activator, 3% the aqueous solution of hydrochloric acid dipping 5 minutes being dissolved at the エ Application プ レ one ト PC-236 that メ Le テ ッ Network ス (strain) is made with the ratio of 150g/L, with surface and the through hole wall of tin-palladium colloidal particle attached to composite sheet.In addition, this sheet is immersed in the solution of the PA-360 that makes with pure water dilution メ Le テ ッ Network ス (strain) with the ratio of 50ml/L dissolving tin, activating catalyst.
Then, this composite sheet is immersed in the acetone, extraction is removed and is contained the alkane that is immersed in the stretchable porous PTFE sheet, obtains the only stretchable porous PTFE sheet of adhesion palladium-Xi particle on the wall of through hole.
In initial plating bath, added メ Le プ レ one ト Cu-3000A, メ Le プ レ one ト Cu-3000B that メ Le テ ッ Network ス (strain) makes, メ Le プ レ one ト Cu-3000C, メ Le プ レ one ト Cu-3000D separately 5%, in the electroless plating copper liquid of メ Le プ レ one ト Cu-3000 stabilizing agent 0.1%, the limit is carried out sufficient air and is stirred, limit this stretchable porous PTFE sheet of dipping 30 minutes is only separated out copper particle and conduction on the wall of through hole.
Then, the contact for antirust, raising and device carries out the gold-plated of copper particle.In accordance with the following methods gold-plated, adopt immersion gold plating method by nickel.
As pre-preg, the stretchable porous PTFE sheet that will adhere to copper particle on the wall of through hole was immersed in the activator オ one ロ テ ッ Network SIT auxiliary agent (80ml/L) that ア ト ッ テ ッ Network makes after 3 minutes, as adding catalyst, adding the オ one ロ テ ッ Network SIT activator コ Application Network (125mg/L) that ア ト ッ テ ッ Network is made, dipping is 1 minute in the initial plating bath liquid of the activator オ one ロ テ ッ Network SIT auxiliary agent (80ml/L) that ア ト ッ テ ッ Network is made, behind the オ one ロ テ ッ Network SIT that ア ト ッ テ ッ Network is made, flooded 1 minute adhesion palladium catalyst on copper particle again in the maceration extract (25ml/L).
Then, in initial plating bath liquid, added in the electroless plating nickel liquid of sodium hypophosphite (20g/L), trisodium citrate (40g/L), ammonium borate (13g/L), nickelous sulfate (22g/L) dipping stretchable porous PTFE sheet 5 minutes, with this copper particle nickel plating.
Afterwards, [メ Le プ レ one ト AU-6630A (200ml/L), メ Le プ レ one ト AU6630B (100ml/L), メ Le プ レ one ト AU-6630C (20g/L), the gold sodium sulfide aqueous solution are (as gold for the immersion gold plating liquid that メ Le テ ッ Network ス makes, be 1.0g/L)] the middle dipping 5 minutes, carry out the gold-plated of copper particle, only obtain adopting the anisotropic conductive sheet that the stretchable porous PTFE sheet of conductionization on the wall of the through hole of 1.00mm is made.
It is square that the anisotropic conductive sheet that will be basement membrane with the stretchable porous PTFE sheet that obtains according to the method described above is cut into 10mm, measures conducting with device shown in Figure 5 and begin to bear a heavy burden.The copper post that uses 2mm φ is as probe, and 1 electrode of contact of will popping one's head in is measured resistance value with 4 terminal methods.Consequently, pushing under the heavy burden 5.0MPa, is 3.9 Ω.
Comparative example 4
On stretchable porous PTFE sheet (the Off ァ イ of Sumitomo Electric Industries Application Port リ マ one Co., Ltd. system HP-010-30), use the drill bit of diameter 250 μ m, with the revolution of 100000rpm at a plurality of local through holes (perforation) that form.Then, use the method identical, only attempt conductionization at the wall of through hole with embodiment 1, but the loose structure of the internal face of through hole (fine structure) fragmentation, copper particle can not be fixed, and can not separate out copper particle.
Embodiment 8
In methyl methacrylate (chemistry society of common prosperity society system, ラ イ ト エ ス テ Le M) 100g, add azodiisobutyronitrile (with the pure pharmaceutical worker's industry of light society system) 0.2g, stir as thermal polymerization.Prepare the stretchable porous PTFE sheet of use among the embodiment 1, impregnation methyl methacrylate solution.With impregnation the stretchable porous PTFE sheet of methyl methacrylate solution with heating plate 80 ℃ of heating 4 hours down, make methyl methacrylate carry out thermal polymerization.
After the polymerization, the diameter that is used in combination through hole is that drift and the punch die of 250 μ m bored a hole to stretchable porous PTFE sheet.Punching rate is 100 holes/1 minute.After the perforation, using the Soxhlet withdrawal device, is solvent with the MEK, dissolving Polymerization of Methyl thing (polymethyl methacrylate), and extraction is removed.
Microscopic examination is carried out in perforation to the perforated sheet that obtains like this, similarly to Example 1, does not subside around the perforation, and the internal face of perforation also becomes the face that cuts off along punching basically.Do not find distortion or burr around the perforation, the fine structure around the perforation has also been kept and other local identical shapes.
Embodiment 9
In methyl methacrylate (chemistry society of common prosperity society system, ラ イ ト エ ス テ Le M) 100g, add イ Le ガ キ ュ ア 184 (with the pure pharmaceutical worker's industry of light society system) 0.2g, stir as Photoepolymerizationinitiater initiater.Prepare the stretchable porous PTFE sheet identical, impregnation methyl methacrylate solution with embodiment 1.
Then, use high-pressure mercury-vapor lamp, with 50mW/cm
2Irradiation ultraviolet radiation 10 minutes carries out photopolymerization with methyl methacrylate.After boring a hole similarly to Example 8, the polymer extraction is removed with solution.
Microscopic examination is carried out in perforation to the perforated sheet that obtains like this, similarly to Example 1, does not subside around the perforation, and the internal face of perforation also becomes the face that cuts off along punching basically.Do not find distortion or burr around the perforation, the fine structure around the perforation has also been kept and other local identical shapes.
Embodiment 10
With polymethyl methacrylate (Sumitomo Chemical society system, ス ミ ペ ッ Network ス LG3 5) 20g, under 40 ℃, 12 hours condition, be dissolved in methyl methacrylate (chemistry society of common prosperity society system, ラ イ ト エ ス テ Le M) among the 80g, interpolation is stirred as イ Le ガ キ ュ ア 184 (with the pure pharmaceutical worker's industry of the light society system) 0.2g of Photoepolymerizationinitiater initiater.Prepare the stretchable porous PTFE sheet identical, impregnation methyl methacrylate solution with embodiment 1.
Then, use high-pressure mercury-vapor lamp, with 50mW/cm
2Irradiation ultraviolet radiation 10 minutes carries out photopolymerization with methyl methacrylate.After boring a hole similarly to Example 8, the polymer extraction is removed with solvent.
Microscopic examination is carried out in perforation to the perforated sheet that obtains like this, similarly to Example 1, does not subside around the perforation, and the internal face of perforation also becomes the face that cuts off along punching basically.Do not find distortion or burr around the perforation, the fine structure around the perforation has also been kept and other local identical shapes.
Embodiment 11
With the square area of 10cm, the porosity be 60%, average pore size is that 0.1 μ m (isopropyl alcohol bubbling point 150kPa), thickness are that 3 of the stretchable porous PTFE sheets of 30 μ m are overlapping, be clipped between the corrosion resistant plate that 2 thickness are 3mm, long 150mm, wide 100mm, when corrosion resistant plate is applied heavy burden, under 350 ℃, carry out 30 minutes heat treated.After the heating, carry out chilling but, obtain being fused to the laminated body of 3 layers stretchable porous PTFE film from corrosion resistant plate top water.
In methyl methacrylate (chemistry society of common prosperity society system, ラ イ ト エ ス テ Le M) 100g, add azodiisobutyronitrile (with the pure pharmaceutical worker's industry of light society system) 0.2g, stir as thermal polymerization.Methyl methacrylate solution is contained in the laminated body that is dipped in above-mentioned making.With impregnation the laminated body of methyl methacrylate solution with heating plate 80 ℃ of down heating 4 hours, make methyl methacrylate carry out thermal polymerization.
After the polymerization, the diameter that is used in combination through hole is that drift and the punch die of 250 μ m bored a hole to stretchable porous PTFE sheet.Punching rate is 100 holes/1 minute.After the perforation, using the Soxhlet withdrawal device, is solvent with the MEK, dissolving Polymerization of Methyl thing (polymethyl methacrylate), and extraction is removed.
After laminated body is immersed in the ethanol 1 minute and carries out hydrophiling, under 60 ℃ temperature, be immersed among the メ Le プ レ one ト PC-321 that dilution makes for the メ Le テ ッ Network ス (strain) of 100ml/L 4 minutes, carry out conditioning and handle.In addition, laminated body flooded 1 minute in 10% sulfuric acid after, as pre-preg, be dissolved in the solution of 0.8% hydrochloric acid dipping 2 minutes at the エ Application プ レ one ト PC-236 that メ Le テ ッ Network ス (strain) is made with the ratio of 180g/L.
Laminated body was dissolved in エ Application プ レ that 3% メ Le テ ッ Network ス (strain) makes, one ト activator 444,1% エ Application プ レ one ト assistant activator, 3% the aqueous solution of hydrochloric acid dipping 5 minutes being dissolved at the エ Application プ レ one ト PC-236 that メ Le テ ッ Network ス (strain) is made with the ratio of 150g/L, on the internal face of tin-palladium colloidal particle attached to the surface of laminated body and perforation.In addition, laminated body is immersed in the solution of the PA-360 that makes with pure water dilution メ Le テ ッ Network ス (strain) with the ratio of 50ml/L dissolving tin, activating catalyst.Then, peel off the mask layer on two sides, only obtain stretchable porous PTFE sheet (basement membrane) at the wall attached catalyst palladium particle of through hole.
In initial plating bath, added メ Le プ レ one ト Cu-3000A, メ Le プ レ one ト Cu-3000B that メ Le テ ッ Network ス (strain) makes, メ Le プ レ one ト Cu-3000C, メ Le プ レ one ト Cu-3000D separately 5%, in the electroless plating copper liquid of メ Le プ レ one ト Cu-3000 stabilizing agent 0.1%, the limit is carried out sufficient air and is stirred, above-mentioned basement membrane was flooded 20 minutes in the limit, only with on the internal face of perforation with the copper particle conductionization.Then, the エ Application テ ッ Network Cu-56 that makes at the メ Le テ ッ Network ス (strain) that modulates initial plating bath with 5ml/L carries out 30 seconds dipping, carries out antirust processing, the anisotropic conductive film that to obtain with stretchable porous PTFE sheet be basement membrane.
In plating process, after each solution impregnation beyond the pre-preg operation of electroless plating ketone and catalyst add between the operation, carry out from about 30 seconds to 1 minute washing with distilled water.The temperature of each liquid is except that preliminary treatment, and (20 ℃~30 ℃) carry out all at normal temperatures.
It is square that the anisotropic conductive sheet that will be basement membrane with the stretchable porous PTFE sheet that obtains according to the method described above is cut into 10mm, measures conducting with device shown in Figure 5 and begin to bear a heavy burden.The copper post that uses 2mm φ is as probe, and 1 electrode of contact of will popping one's head in is measured resistance value with 4 terminal methods.Consequently, pushing under the heavy burden 5.0MPa, is 3.5 Ω.
Industrial applicibility
According to the present invention, can not provide and can bring loose structure to the periphery of the internal face that contains perforation Destruction, do not produce burr, form in the place of necessity and have near level and smooth and sharp seamed edge, the opening The porous resin base material of also boring a hole uniformly.
Perforation porous resin base material by manufacture method of the present invention obtains connects usefulness as for example circuit The insulating materials of material or anisotropic conductive material is useful, has again, can be used in spot and repair material The medical devices such as material or diffusion barrier etc. be the field widely.
In addition, according to the present invention, as be used for limiting covering of the conducting portion that is arranged on the porous resin base material Cover material, by using soluble polymer or alkane, can form and firmly be sealed at covering of this base material The mould layer after sheltering, can easily be removed. Soluble polymer or alkane contained be immersed in loose structure In, become solid state after, when boring a hole by mechanical processing method, can not destroy loose structure, can To form accurately perforation. The method can use polymerizable monomer for example such can be by chemistry Reaction forms the compound of solid and implements.
Have again, according to the present invention, be provided as the porous resin of mask layer on the two sides of porous resin base material Layer is made laminated body, by maybe forming by chemical reaction soluble polymer or alkane solid-state The compound of thing contains and is immersed in this laminated body, forms the method for solid, also can be only with the inwall of perforation The face conductionization.
According to manufacture method of the present invention, can not destroy loose structure ground and form perforation, therefore, even The porous resin base material with the fluorine resin material formation of for example plating adaptation difference, also can be to be anchored on The mode of the resin portion of the loose structure of the internal face of formation perforation is adhered to the plating that contains conductive metal Particle.
The porous resin base material of the perforation that obtains by manufacture method of the present invention can utilize at for example electricity The circuit in sub-field connects with material or anisotropic conductive material, insulating materials; Medical field for example The medical devices such as spot repair materials; Diffusion barriers etc. are the field widely.
By the porous resin base material with conductive drilled inner wall surface that manufacture method of the present invention obtains, can So that be used in mutual being electrically connected of component in the semiconductor devices for example; Circuit substrate, partly lead The electric reliability inspection of carrying out in body wafer, the semiconductor subassembly.
Claims (40)
1. the manufacture method of the porous resin base material of a perforation, this method contains following operation 1~4:
(1) includes the operation 1 of immersion fluid or solution at the loose structure of porous resin base material;
(2) operation 2 that forms solid by the liquid or the solution of impregnation;
(3) first surface that has the porous resin base material of solid in the loose structure runs through the operation 3 that second surface ground forms a plurality of perforation; And
(4) with solid fusion or dissolving, the operation 4 of removing in the loose structure.
2. according to the manufacture method of claim 1 record, wherein, porous resin base material is the porous resin sheet.
3. according to the manufacture method of claim 2 record, wherein, the porous resin sheet is, the fine structure with the node that contains fibrillation and link mutually by this fibrillation is as stretched polytetrafluoroethylporous porous of loose structure.
4. according to the manufacture method of claim 1 record, wherein, in operation 1, by The tape casting or infusion process with liquid or solution impregnation in the loose structure of porous resin base material.
5. according to the manufacture method of claim 1 record, wherein, the liquid that uses in operation 1 is the material that has freezing point or fusing point in-150~150 ℃ of scopes.
6. according to the manufacture method of claim 5 record, wherein, the material that has freezing point or fusing point in-150~150 ℃ scope is the mixture more than 2 kinds or 2 kinds in water, alcohol, hydrocarbon, polymer or water, alcohol, hydrocarbon, the polymer.
7. according to the manufacture method of claim 5 record, wherein, the material that has freezing point or fusing point in-150~150 ℃ scope is that fusing point is the alkane more than 15 ℃ or 15 ℃.
8. according to the manufacture method of claim 1 record, wherein, in operation 1, the liquid that the material that will have freezing point or fusing point in-150~150 ℃ scope is made above the temperature of freezing point or fusing point contains in the loose structure that is dipped in porous resin base material, in operation 2, this material is solidified at freezing point or fusing point or the temperature below it, become solid, and, in operation 4, the fusion under the temperature that surpasses freezing point or fusing point of this material is removed.
9. according to the manufacture method of claim 1 record, wherein, the solution that uses in operation 1 is the solution of soluble polymer or alkane.
10. according to the manufacture method of claim 9 record, wherein, be solid under soluble polymer or the alkane temperature in 15~30 ℃ scope.
11. manufacture method according to claim 1 record, wherein, in operation 1, the solution of the solution of impregnation soluble polymer or alkane in the loose structure of porous resin base material, in operation 2, solvent flashing forms the solid of polymer or alkane, and, in operation 4, this solid is removed with dissolution with solvents.
12. according to the manufacture method of claim 1 record, wherein, the liquid or the solution that use in operation 1 are to contain the liquid or the solution that can form the compound of solid by chemical reaction.
13. according to the manufacture method of claim 12 record, wherein, the compound that can form solid by chemical reaction is to carry out the polymerizable monomer that polymerisation forms polymer by heat or light.
14. according to the manufacture method of claim 13 record, wherein, containing the liquid or the solution that can form the compound of solid by chemical reaction is except that polymerizable monomer, also contains the liquid or the solution of the polymer that obtains by this polymerizable monomer polymerization.
15. according to the manufacture method of claim 13 record, wherein, polymerizable monomer is acrylate or methacrylate.
16. manufacture method according to claim 1 record, wherein, in operation 1, impregnation contains the compound liquid or the solution that can form solid by chemical reaction in the loose structure of porous resin base material, in operation 2, make this compound carry out chemical reaction and form solid, and, in operation 4, this solid is removed with dissolution with solvents.
17. manufacture method according to claim 1 record, wherein, in perforation process 3, pass through i) method of machine drilling, ii) carry out etching method or iii) use the ultrasonic head that has at least 1 oscillator at leading section by light ablation method, push the front end of this oscillator, apply the method that ultrasonic energy is bored a hole, form perforation.
18. the manufacture method of the porous resin base material of a conductive drilled inner wall surface, this method comprises following operation I~VI:
(1) in the loose structure on the two sides that comprises porous resin base material, impregnation soluble polymer or alkane maybe can form the operation I of the compound of solid by chemical reaction;
(2) maybe can form solid by the soluble polymer of impregnation or alkane by the compound that chemical reaction forms solid, form the operation II of composite sheet, described composite sheet be have the layer of solid on the two sides of porous resin base material and in loose structure impregnation the composite sheet of structure of solid;
(3) first surface from this composite sheet runs through the operation III that second surface ground forms a plurality of perforation;
(4) comprising the respectively operation IV of the catalyst of the surface attachment promotion metal ion reduction reaction of the composite sheet of the internal face of perforation;
(5) remove the operation V of solid from composite sheet; And
(6) utilize and to adhere to and remain in above-mentioned catalyst on internal face of each perforation of porous resin base material, on this internal face, adhere to the operation VI of conductive metal.
19. according to the manufacture method of claim 18 record, wherein, porous resin base material is the porous resin sheet.
20. according to the manufacture method of claim 19 record, wherein, the porous resin sheet is, the fine structure with the node that contains fibrillation and link mutually by this fibrillation is as stretched polytetrafluoroethylporous porous of loose structure.
21., wherein, be solid under soluble polymer or the alkane temperature in 15~30 ℃ scope according to the manufacture method of claim 18 record.
22. manufacture method according to claim 18 record, wherein, in operation I, solution or fused solution by curtain coating soluble polymer on the two sides of porous resin base material, or the solution of curtain coating alkane or fused solution, or porous resin base material is immersed in the solution or the fused solution of soluble polymer, or be immersed in the solution of alkane or the method in the fused solution, impregnation soluble polymer or alkane, then, in operation II, by solvent flashing or be cooled to freezing point or fusing point or the method for temperature below it, the two sides that is formed on porous resin base material has the soluble polymer or the alkane layer of solid, and the soluble polymer of solid or alkane contain the composite sheet that is dipped in the structure in the loose structure.
23. manufacture method according to claim 18 record, wherein, in operation I, contain as the compound that can form solid by on the two sides of porous resin base material curtain coating by chemical reaction, form the liquid or the solution of the polymerizable monomer of polymer by heat or light polymerization reaction take place, perhaps porous resin base material is immersed in to contain and forms the liquid of polymerizable monomer of polymer or the method in the solution by heat or light polymerization reaction take place, the impregnation polymerizable monomer, then, in operation II, by made the polymerizable monomer polymerization form the method for the polymer of solid by heat or light, the two sides that is formed on porous resin base material has the polymeric layer of solid, and the polymer of solid contains the composite sheet that is dipped in the structure in the loose structure.
24. manufacture method according to claim 18 record, wherein, in operation III, pass through i) method of machine drilling, ii) carry out etching method or iii) use the ultrasonic head that has at least 1 oscillator at leading section by light ablation method, push the front end of this oscillator, apply the method that ultrasonic energy is bored a hole, on composite sheet, form a plurality of perforation.
25. according to the manufacture method of claim 18 record, wherein, in operation V, using porous resin base material is insoluble or slightly solubility but solid is shown deliquescent solvent, dissolving solid and removing.
26., wherein, in operation V, the solid fusion is removed according to the manufacture method of claim 18 record.
27., wherein, in operation VI, overlay on by electroless plating on internal face of each perforation and adhere to conductive metal according to the manufacture method of claim 18 record.
28. manufacture method according to claim 18 record, wherein, the porous resin base material of the internal face conductionization of perforation is, have the conducting portion that is formed by the conductive metal attached to the resin portion of loose structure at the internal face that runs through a plurality of perforation of second surface from first surface, each conducting portion only can be given the anisotropic conductive sheet of electric conductivity on film thickness direction.
29. the manufacture method of the porous resin base material of a conductive drilled inner wall surface, this method contains following operation i~viii:
(1) on the two sides of porous resin base material A, as mask layer, lamination porous resin layer B and C, the operation i of the laminated body of formation 3-tier architecture;
(2) in each loose structure of this laminated body, impregnation soluble polymer or alkane maybe can form the operation ii of the compound of solid by chemical reaction;
(3) maybe can form the operation iii of solid by the compound that chemical reaction forms solid by the soluble polymer of impregnation or alkane;
(4) first surface that has the laminated body of solid in each loose structure runs through the operation iv that second surface forms a plurality of perforation;
(5) dissolving solid, the operation v that solid is removed in each loose structure;
(6), adhere to the operation vi that promotes the reduction of metal ion catalyst for reaction on the surface of the laminated body that comprises each internal face of boring a hole;
(7) peel off the operation vii of the mask layer on two sides from porous resin base material A; And
(8) utilize and to adhere to and remain in above-mentioned catalyst on internal face of each perforation of porous resin base material A, on this internal face, adhere to the operation viii of conductive metal.
30. according to the manufacture method of claim 29 record, wherein, porous resin base material is the porous resin sheet.
31. according to the manufacture method of claim 30 record, wherein, the porous resin sheet is, the fine structure with the node that contains fibrillation and link mutually by this fibrillation is as stretched polytetrafluoroethylporous porous of loose structure.
32. according to the manufacture method of claim 29 record, wherein, the compound that can form solid by chemical reaction is to carry out the polymerizable monomer that polymerisation forms polymer by heat or light.
33. according to the manufacture method of claim 32 record, wherein, containing the compound liquid or the solution that can form solid by chemical reaction is except that polymerizable monomer, also contains the liquid or the solution of the polymer that obtains by this polymerizable monomer polymerization.
34. according to the manufacture method of claim 32 record, wherein, polymerizable monomer is acrylate or methacrylate.
35. manufacture method according to claim 29 record, wherein, in operation ii, solution or fused solution by curtain coating soluble polymer on the two sides of laminated body, or the solution of curtain coating alkane or fused solution, perhaps laminated body is immersed in the solution or the fused solution of soluble polymer, or be immersed in the solution or fused solution of alkane, impregnation soluble polymer or alkane, then, in operation iii, by solvent flashing or be cooled to freezing point or fusing point or the method for temperature below it, form the polymer or the alkane of solid.
36. manufacture method according to claim 29 record, wherein, in operation ii, in each loose structure of laminated body, impregnation as can by chemical reaction form solid compound, contain by heat or light and carry out liquid or the solution that polymerisation forms the polymerizable monomer of polymer, then, in operation iii, by heat or photopolymerization polymerizable monomer, form solid polymer.
37. manufacture method according to claim 29 record, wherein, in operation iv, pass through i) method of machine drilling, ii) carry out etching method or iii) use the ultrasonic head that has at least 1 oscillator at leading section by light ablation method, push the front end of this oscillator, apply the method that ultrasonic energy is bored a hole, on laminated body, form a plurality of perforation.
38. according to the manufacture method of claim 29 record, wherein, in operation v, using porous resin base material is insoluble or slightly solubility, but solid is shown deliquescent solvent, dissolving solid and removing.
39. according to the manufacture method of claim 29 record, wherein, in operation viii, cover, on the internal face of each perforation, adhere to conductive metal by electroless plating.
40. manufacture method according to claim 29 record, wherein, the porous resin base material of the internal face conductionization of perforation is, have the conducting portion that is formed by the conductive metal attached to the resin portion of loose structure at the internal face that runs through a plurality of perforation of second surface from first surface, each conducting portion only can be given the anisotropic conductive sheet of electric conductivity on film thickness direction.