CN100334315C - Fiber reinforced artificial stone tomb box and its manufacturing method - Google Patents
Fiber reinforced artificial stone tomb box and its manufacturing method Download PDFInfo
- Publication number
- CN100334315C CN100334315C CNB2005102007538A CN200510200753A CN100334315C CN 100334315 C CN100334315 C CN 100334315C CN B2005102007538 A CNB2005102007538 A CN B2005102007538A CN 200510200753 A CN200510200753 A CN 200510200753A CN 100334315 C CN100334315 C CN 100334315C
- Authority
- CN
- China
- Prior art keywords
- fiber reinforced
- artificial stone
- tomb
- mentioned
- reinforced artificial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a fiber reinforced artificial stone tomb box and a manufacture method thereof, a box body and a box cover of which are made of fiber reinforced artificial stones, wherein the inner part of the box body has a hollow cavity, four edges of the box cover have downward convex fringes, and the inner edge of each downward convex fringe is engaged with the outer edge of the upper fringe of the box body. Firstly, raw material is mixed into slurry in a stirrer according to mixing proportions, and then, a fiber mesh fabric is laid in a mold according to the shape of a tomb box; next, the slurry is put into the mold, and finally, surface treating liquid is sprayed to obtain a finished product after the slurry is molded, maintained, stripped, repaired and trimmed. Proportions of the raw material comprise 35 parts to 60 parts of cement, 40 parts to 65 parts of fine aggregate, 1 part to 4 parts of fiber filaments, 1 part to 8 parts of anti-cracking permeability-reducing agent, 0.2 part to 1 part of super plasticizer, 1 part to 5 parts of silicate reinforcing agent, 0 part to 4 parts of surface treating liquid, 0 part to 0.5 part of defoaming agent and 0 part to 0.5 part of paint. The present invention not only overcomes the defects of low impact resistance performance, low permeability-reducing performance and scarce resources in traditional natural stone tomb boxes, but also has the advantages of high strength, high temperature resistance, no crack, good integrity and appearance, and low cost. The present invention is favorable for environmental protection.
Description
(1), technical field
The present invention relates to a kind of coffin pit member and preparation method thereof.
(2), background technology
At funeral profession, the tomb case (also claiming the stone case) that uses when burying cinerary casket is made by lithotomes such as marble or granite at present.The tomb case made from marble or granite has two kinds of structures.A kind of is spliced, is promptly formed by bonding by five blocks of marbles or granite surface plate: another kind of is monolithic, promptly uses a big marble or granite, and by artificial cutting, brill pick, polishing forms.On the properties of product, though marble and granite tomb case compressive strength height, impact resistance is poor, frangible and easy to leak.Spliced in addition marble or granite tomb case globality are poor, easily seepage.And monolithic marble or granite tomb case manufacture difficulty are big, and outward appearance is coarse, and on the make usually because of impact causes crack or cracked, yield rate is low, the cost height, and impermeability also can't guarantee.Advanced several years, the resource of marble and granite is fewer and feweri, and the exhaustive exploitation of even more serious is marble or granite is seriously damaged natural environment.Therefore from properties of product and protection environmental, the development of new artificial stone tomb box replaces marble and granite tomb case to have crucial meaning.
(3), summary of the invention
The purpose of this invention is to provide a kind of fiber reinforced artificial stone tomb box and preparation method thereof, solve that marble granite tomb case cost is higher, impact resistance differs from and the problem of scarcity of resources with impervious.
Technical scheme of the present invention:
This fiber reinforced artificial stone tomb box comprises casing and case lid, it is characterized in that: its casing and case lid are made by fiber reinforced artificial stone, and box house has cavity, and there is following convex edge on case lid four limits, and the outside of the inner edge of following convex edge and casing upper edge coincide.
The outside of above-mentioned casing upper edge is to the horizontal evagination of cabinet exterior direction.
Above-mentioned cabinet wall has boss, sets up the tribute platen on the boss.
Above-mentioned cabinet wall has two-layer boss up and down, and lower floor's boss sets up horizontal baffle, and the upper strata boss sets up the tribute platen.
The cavity of above-mentioned box house is L-shaped, corner part wall at cabinet wall is fluted, be placed with vertical dividing plate in the groove, the end face part of this vertical dividing plate is in above-mentioned groove, another part is just in time as the boss that supports the tribute platen, and the other end of tribute platen is supported by the boss of cabinet wall.
Above-mentioned box house has two cavitys side by side, sets up the tribute platen in two cavitys respectively.
The preparation method of this fiber reinforced artificial stone tomb box, it is characterized in that: in agitator, raw material is mixed into slurry by proportioning, in mould, press tomb box shape shop fiber mesh cloth then, again above-mentioned slurry is gone into mould, through moulding, maintenance, the demoulding, repairing and finishing, spray surface treatment liquid at last and go out finished product;
Raw material weight proportioning: 35-60 part cement, 40-65 part fine aggregate, 1-4 part fibre, the agent of 1-8 part anti-crack and anti-seepage, 0.2-1 part super plasticizer, 1-5 part silicate reinforcing agent, 0-4 part S Tiao I condensate of melamine and formaldehyde, 0-0.5 part defoamer, 0-5 pigment.
Above-mentioned fibre is alkali resistant glass fiber silk, polypropylene filaments or nylon fiber silk, and fiber mesh cloth is alkali resistant glass fiber screen cloth, polypropylene fibre screen cloth or nylon fiber screen cloth.
Above-mentioned anti-crack and anti-seepage agent is HF anti-crack and anti-seepage reinforcing agent, crystallization permeable waterproof agent, land plaster or expansion agent; Super plasticizer is high-efficiency water-reducing agent of poly-carboxylic acid, super plastotype melamine water reducing agent, naphthalenesulfonate formaldehyde condensation compound, calcium lignosulfonate, sodium lignin sulfonate or sulfamate water reducer.
Above-mentioned fine aggregate is colored or white quartz sand, quartz powder, colour or white limestone sand, pulverized limestone; The silicate reinforcing agent is kieselguhr, silica flour, flyash or breeze.
Fiber reinforced artificial stone tomb box of the present invention is a kind of advanced composite material (ACM) goods that adopt inorganic composite material to make, it is a base material with hydraulic cementing materials, super plasticizer, anti-crack and anti-seepage agent, composite assistant, with fiber, fine aggregate is reinforcing material, makes by process for artificial.The present invention is as the substitute products of marble, granite tomb case, both had and made easily, extensive, the rakish advantage of material source, can satisfy the requirement of high-strength, shock resistance, impervious, moistureproof, high temperature resistant, good endurance again, have intensity height, good toughness, shock resistance, impervious protection against the tide, corrosion-resistant, high temperature resistant, do not ftracture, aging, the performance of stable performance, combination property meet or exceed the tomb case made from marble or granite.
The present invention improves the anti-intensity of tomb case, impact, anti-drying shrinkage, impervious moisture resistance and heat-resisting quantity by three-dimensional fiber enhancing, compensate for shrinkage, dispersion enhancing and microstructure optimization principle; Improve the compactness and the brightness of tomb case by rational technological measure.Composite modified by material, multiple technology interactive effects such as structure design, fiber reinforcement, moulding process and surfacing, both solved the problem of marble granite tomb case impact resistance and impervious difference and resource shortage, have again high-strengthly, high temperature resistant do not ftracture, globality and the good characteristics of aesthetic appearance.Cost of manufacture than traditional marble or granite tomb case reduces greatly, more helps protecting environment, particularly the unrivaled advantage of marble granite tomb case is arranged aspect the complex-shaped tomb case making, and places cinerary casket when can be used for the funeral profession grave.
(4), description of drawings
Fig. 1 is the structural representation of fiber reinforced artificial stone tomb box embodiment 1 of the present invention;
Fig. 2 is the A-A sectional drawing of Fig. 1.
Fig. 3 is the structural representation of fiber reinforced artificial stone tomb box embodiment 2 of the present invention;
Fig. 4 is the A-A sectional drawing of Fig. 3.
Fig. 5 is the structural representation of fiber reinforced artificial stone tomb box embodiment 3 of the present invention;
Fig. 6 is the A-A sectional drawing of Fig. 5.
Fig. 7 is the structural representation of fiber reinforced artificial stone tomb box embodiment 4 of the present invention;
Fig. 8 is the A-A sectional drawing of Fig. 7.
Fig. 9 is the structural representation of fiber reinforced artificial stone tomb box embodiment 5 of the present invention;
Figure 10 is the A-A sectional drawing of Fig. 9.
Figure 11 is the structural representation of fiber reinforced artificial stone tomb box embodiment 6 of the present invention;
Figure 12 is the A-A sectional drawing of Figure 11.
(5), the specific embodiment
Embodiment 4 is referring to Fig. 7, Fig. 8, and above-mentioned cabinet wall has two-layer boss up and down, and lower floor's boss sets up horizontal baffle 7, and the upper strata boss sets up the tribute platen.
Embodiment 5 is referring to Fig. 9, Figure 10, the cavity of above-mentioned box house is L-shaped, corner part wall fluted 8 at cabinet wall, be placed with vertical dividing plate 9 in the groove, the end face part of this vertical dividing plate is in above-mentioned groove, another part is just in time as the boss that supports tribute platen 6, and the other end of tribute platen is supported by the boss of cabinet wall.
The raw-material weight proportion of fiber reinforced artificial stone tomb box of the present invention:
Cement: fine aggregate=35: 65 or 40: 60 or 45: 55 or 50: 50 or 55: 45 or 60: 40.
Fortifying fibre: any part between 1-4 part;
Anti-crack and anti-seepage agent: any part between the 1-8;
Super plasticizer: any part between the 0.2-1;
Any part between the silicate reinforcing agent 1-5;
S Tiao I condensate of melamine and formaldehyde: any part between the 0-4;
Defoamer: any part between the 0-0.5;
Pigment: any part between the 0-5;
Surface conditioning agent: evenly in the tank surface spraying.
Cementitious material can be high alumina cement, sulphate aluminium cement, ferrous aluminate cement, portland cement or slag cements.
Fine aggregate can be colored or white quartz sand, quartz powder, colour or white limestone sand, pulverized limestone etc.
Fortifying fibre can be alkali resistant glass fiber silk or screen cloth, polypropylene filaments or screen cloth, nylon fiber silk or screen cloth.
The anti-crack and anti-seepage agent can be HF anti-crack and anti-seepage reinforcing agent, crystallization permeable waterproof agent, land plaster or expansion agent.
Super plasticizer can be high-efficiency water-reducing agent of poly-carboxylic acid, super plastotype melamine water reducing agent, naphthalenesulfonate formaldehyde condensation compound, calcium lignosulfonate, sodium lignin sulfonate, sulfamate water reducer etc.
Reinforcing agent can be kieselguhr, silica flour, flyash, breeze.
The concrete preparation method of fiber reinforced artificial stone tomb box of the present invention: in agitator, raw material is mixed into slurry by proportioning, in mould, press tomb box shape shop fiber mesh cloth then, again above-mentioned slurry is gone into mould,, spray surface treatment liquid at last and go out finished product through moulding, maintenance, the demoulding, repairing and finishing.
Raw material: the base material of artificial stone tomb box is selected according to the compliance of color, intensity, demould time and fortifying fibre that the tomb case requires.The selection of quartz sand has certain requirement to granularity and color and luster.In principle, quartz sand is thin, and the product surface glossiness is just high, but drying shrinkage is easy to crack greatly; Otherwise quartz sand is thick, and the product density is poor, and glossiness is low, and drying shrinkage is little not to ftracture.Preferably the quartz sand collocation of different fineness is used.It is more satisfactory that band colored stone powder is used to make the identical tomb case of color.Band colored stone powder can not be used to make white artificial stone tomb box, then can make the artificial stone tomb box of various colors of white stone flour.Therefore select the pure white marble stone flour of white, calcite stone flour, white stone stone flour etc. as far as possible for use.So not only can guarantee tone U.S. of product, and the stone texture of goods is strong.Other auxiliary base material and reinforcing materials have different requirements to granularity and color and luster equally.Also must consider the rational proportion between auxiliary material and the stone flour simultaneously.
Mould and processing thereof: produce the used mould of artificial stone tomb box and be divided into internal mold and external mold part.The surface gloss of template is related to the surface property of tomb case.Seeking template must be highly smooth, bright, and has certain rigidity.Template is cleaned out earlier, the release agent saponified oil.
Batch mixing: batch mixing is meant that the base material that will be in harmonious proportion by proportioning and reinforcing material fully mix and make the slurry of certain degree of mobilization.Slurry both can be made into monochromatic, also can be manufactured with the artificial stone tomb box of natural figure according to the method for inhomogeneous mixing.
Moulding: moulding can adopt cast molding also can adopt compression molding.Cast molding: the base material slurry complete and die assembling after, just cast and moulding is smash in shake.The purpose that shake is smash is to make the product molding densification solid, eliminates bubble, makes colorant to surface seepage simultaneously.Compression molding: base material fully mixes and makes the dry material of certain workability in reinforcing material, lays the lining mould in model; According to compression ratio cloth and suppressing for the first time, carry out secondary material distributing then and suppress again.
Repair and finishing: after the moulding of tomb case, at room temperature place, allow its sclerosis.The post processing of product comprises repairs and surfacing.By post processing, make artificial stone tomb box reach smooth, smooth.
Example 1:
In agitator, add 40-65 part quartz powder or quartz sand, 35-60 part sulphate aluminium cement, the agent of 1-5 part HF anti-crack and anti-seepage, the active breeze of 0-5 part, 0.1-0.5 part S Tiao I condensate of melamine and formaldehyde, the short silk of 1-4 part alkali resistant glass fiber, 1-3 part land plaster, start agitator and do mixing 2 minutes, after treating that respectively organizing powder mixes, slowly adding 12-18 part water stirred 3 minutes, according to the degree of mobilization of slurry regulate amount of water up to slurry reach degree of mobilization 200-300mm, add 0.1 part of tributyl phosphate defoamer and 0.3 part of iron oxide green at last, 0.2 part iron oxide black or prior deployed compound mill base are also done inhomogeneous mix.The addition of pigment or compound mill base color is as requested determined.In mould, lay grid cloth according to the tomb box shape, then the slurry that makes is molded into mould, and shake closely knit.The tomb case curing in the mold demoulding in 3-24 hour after the moulding at tomb case surface spraying uncle PD-9 acrylic emulsion surface conditioning agent, is promptly made the artificial stone tomb box with natural figure after the demoulding.
Example 2:
In agitator, add colored quartz powder of 40-65 part or quartz sand, 35-60 part portland cement, the agent of 1-5 part HF anti-crack and anti-seepage, 0-5 part silica flour, 0.1-0.5 part S Tiao I naphthalenesulfonate formaldehyde condensation compound, the short silk of 1-4 part polypropylene fibre, 0-1 part early strength admixture starts mixer to be mixed 2 minutes, after treating that respectively organizing powder mixes, slowly adding 15-20 part water stirred 3 minutes, according to the degree of mobilization of slurry regulate amount of water up to slurry reach degree of mobilization 200-300mm, add 0.1 part of S-29 defoamer and 0.3 part of iron oxide green at last, 0.2 part iron oxide black or prior deployed compound mill base are also done inhomogeneous mix.The addition of pigment or compound mill base color is as requested determined.In mould, lay grid cloth according to the tomb box shape, then the slurry that makes is molded into mould, and shake closely knit.The tomb case curing in the mold demoulding in 3-24 hour after the moulding at tomb case surface spraying uncle PD-9 acrylic emulsion surface conditioning agent, is promptly made the artificial stone tomb box with natural figure after the demoulding.
Example 3:
In agitator, add colored quartz powder of 45-65 part or quartz sand, 35-55 part portland slag cement, the agent of 1-5 part HF anti-crack and anti-seepage, 0-5 part silica flour, 0.1-0.5 part S Tiao I naphthalenesulfonate formaldehyde condensation compound, the short silk of 1-4 part nylon fiber, starting mixer mixed 2 minutes, after treating that respectively organizing powder mixes, slowly add entry and 0.3 part of iron oxide green, 0.2 part of iron oxide black or in advance deployed compound mill base and stirred 3 minutes, regulate amount of water according to the workability of slurry and reach suitable compression moulding up to the workability of slurry.The addition of pigment or compound mill base color is as requested determined.The material of mixing is added in the mould, be pressed.Tomb case belt material mould maintenance after moulding 1-2 days, reach demoulding strength after, take off behind the lining mould at tomb case surface spraying uncle PD-9 acrylic emulsion surface conditioning agent, promptly make artificial stone tomb box with requirement color.
Claims (9)
1. a fiber reinforced artificial stone tomb box comprises casing and case lid, it is characterized in that: its casing and case lid are made by fiber reinforced artificial stone, and box house has cavity, and there is following convex edge on case lid four limits, and the outside of the inner edge of following convex edge and casing upper edge coincide;
Above-mentioned cabinet wall has two-layer boss up and down, and lower floor's boss sets up horizontal baffle, and the upper strata boss sets up the tribute platen.
2. fiber reinforced artificial stone tomb box according to claim 1 is characterized in that: the outside of above-mentioned casing upper edge is to the horizontal evagination of cabinet exterior direction.
3. fiber reinforced artificial stone tomb box according to claim 1 is characterized in that: above-mentioned cabinet wall has boss, sets up the tribute platen on the boss.
4. fiber reinforced artificial stone tomb box according to claim 1, it is characterized in that: the cavity of above-mentioned box house is L-shaped, corner part wall at cabinet wall is fluted, be placed with vertical dividing plate in the groove, the end face part of this vertical dividing plate is in above-mentioned groove, another part is just in time as the boss that supports the tribute platen, and the other end of tribute platen is supported by the boss of cabinet wall.
5. fiber reinforced artificial stone tomb box according to claim 1 is characterized in that: above-mentioned box house has two cavitys side by side, sets up the tribute platen in two cavitys respectively.
6. the preparation method of a fiber reinforced artificial stone tomb box, it is characterized in that: in agitator, raw material is mixed into slurry by proportioning, in mould, press tomb box shape shop fiber mesh cloth then, again above-mentioned slurry is gone into mould, through moulding, maintenance, the demoulding, repairing and finishing, spray surface treatment liquid at last and go out finished product;
Raw material weight proportioning: 35-60 part cement, 40-65 part fine aggregate, 1-4 part fibre, the agent of 1-8 part anti-crack and anti-seepage, 0.2-1 part super plasticizer, 1-5 part silicate reinforcing agent, 0-4 part S Tiao I condensate of melamine and formaldehyde, 0-0.5 part defoamer, 0-5 pigment.
7. the preparation method of fiber reinforced artificial stone tomb box according to claim 7, it is characterized in that: above-mentioned fibre is alkali resistant glass fiber silk, polypropylene filaments or nylon fiber silk, and fiber mesh cloth is alkali resistant glass fiber screen cloth, polypropylene fibre screen cloth or nylon fiber screen cloth.
8. the preparation method of fiber reinforced artificial stone tomb box according to claim 7, its feature
Be: above-mentioned anti-crack and anti-seepage agent is HF anti-crack and anti-seepage reinforcing agent, crystallization permeable waterproof agent, land plaster or expansion agent; Super plasticizer is high-efficiency water-reducing agent of poly-carboxylic acid, super plastotype melamine water reducing agent, naphthalenesulfonate formaldehyde condensation compound, calcium lignosulfonate, sodium lignin sulfonate or sulfamate water reducer.
9. the preparation method of fiber reinforced artificial stone tomb box according to claim 7 is characterized in that: above-mentioned fine aggregate is colored or white quartz sand, quartz powder, colour or white limestone sand, pulverized limestone; The silicate reinforcing agent is kieselguhr, silica flour, flyash or breeze.