CN109895314A - Fiber answers the manufacturing method and mold of material cinerary casket or cinerary urn protection structure - Google Patents
Fiber answers the manufacturing method and mold of material cinerary casket or cinerary urn protection structure Download PDFInfo
- Publication number
- CN109895314A CN109895314A CN201910230850.3A CN201910230850A CN109895314A CN 109895314 A CN109895314 A CN 109895314A CN 201910230850 A CN201910230850 A CN 201910230850A CN 109895314 A CN109895314 A CN 109895314A
- Authority
- CN
- China
- Prior art keywords
- mold
- cinerary
- fiber
- raw material
- protection structure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses manufacturing methods and mold that fiber answers material cinerary casket or cinerary urn protection structure; the described method includes: raw material is matched with sheet or dough composition; wherein each rank resin 32%; curing agent 0.4%; aluminium 35%, fiber 30%, the equal materials mixing of magnesia 0.3%; then it is combined through special-purpose machinery premixing, finally removed hydrosetting through 24 to 48 hours in drying chamber;By bulk and sheet-shaped material by product quality proportion weighing, after mold heats to 220 degrees Celsius or more, raw material is put into mold, by raw material in die cavity pressure-maintaining and heat-preservation, cure it completely;Start press-casting machine, opening mold takes out product;Finally pass through manual grinding, deburring is put in storage pending after cooling through quality inspection.The funeral and interment laws and regulations requirement that this programme meets national environmental protection and saves land, reduces irrational extraction of resources and processing to natural environment, and more environmentally-friendly, the small volume of finished product can reduce land use area, while can reduce transport, installation and management cost.
Description
Technical field
The present invention relates to cinerary casket or cinerary urn technical fields more particularly to fiber to answer material cinerary casket or cinerary urn protection knot
The manufacturing method and mold of structure.
Background technique
Since founding of New, country's promulgation (funeral and interment management rules) retains bone ash after vigorously implementing cremation and is stored in bone
Ash box and cinerary urn are put into the form of burying that falls in cemetery, and traditional technology is using mineral material as cinerary casket or the protection knot of cinerary urn
Structure.
It is had the drawback that and is caused naturally using the protection structure of traditional mineral material production cinerary casket or cinerary urn
The transition in mine is exploited, and increases land resource and environmental protection pressure, it is therefore desirable to improve.
Summary of the invention
The purpose of the present invention is to solve existing in the prior art using traditional mineral material production cinerary casket or
The shortcomings that protection structure of cinerary urn will cause the transition exploitation in natural mine, increase land resource and environmental protection pressure, and propose
Fiber answer material cinerary casket or cinerary urn protection structure manufacturing method and mold.
To achieve the goals above, present invention employs following technical solutions:
Fiber answers the manufacturing method of material cinerary casket or cinerary urn protection structure, which comprises
(1) raw material is matched with sheet or dough composition, wherein each rank resin 32%, curing agent 0.4%, aluminium 35%,
Fiber 30%, the equal materials mixing of magnesia 0.3%, is then combined through special-purpose machinery premixing, finally small through 24 to 48 in drying chamber
When remove hydrosetting;
(2) bulk and sheet-shaped material are heated to 220 degrees Celsius or more to mold by product quality proportion weighing
Afterwards, raw material is put into mold, by raw material in die cavity pressure-maintaining and heat-preservation, cure it completely;
(3) start press-casting machine, opening mold takes out product;
(4) finally pass through manual grinding, deburring is put in storage pending after cooling through quality inspection.
Preferably, pressure-maintaining and heat-preservation time of the raw material in die cavity is 10 minutes in the step 2.
Fiber answers the manufacture mold of material cinerary casket or cinerary urn protection structure, and the fibre for implementing claim 1 is arranged
The manufacturing method of multiple material cinerary casket or cinerary urn protection structure is tieed up, the mold uses P20 high strength steel mold materials, the mold
It is pressed by die casting machine, is then assembled through the machining of import high speed finishing impression and manpower.
Compared with the prior art, the beneficial effects of the present invention are:
The funeral and interment laws and regulations requirement that this programme meets national environmental protection and saves land reduces the irrational extraction of resources to natural environment and adds
Work, more environmentally-friendly, the small volume of finished product can reduce land use area, while can reduce transport, installation and management cost.
Detailed description of the invention
Fig. 1 is that fiber proposed by the present invention answers material cinerary casket or cinerary urn protects the process of the manufacturing method of structure to illustrate
Figure.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
In the description of the present invention, it is to be understood that, term " on ", "lower", "front", "rear", "left", "right", "top",
The orientation or positional relationship of the instructions such as "bottom", "inner", "outside" is to be based on the orientation or positional relationship shown in the drawings, merely to just
In description the present invention and simplify description, rather than the device or element of indication or suggestion meaning must have a particular orientation, with
Specific orientation construction and operation, therefore be not considered as limiting the invention.
Referring to Fig.1, fiber answers the manufacturing method of material cinerary casket or cinerary urn protection structure, and method includes:
(1) raw material is matched with sheet or dough composition, wherein each rank resin 32%, curing agent 0.4%, aluminium 35%,
Fiber 30%, the equal materials mixing of magnesia 0.3%, is then combined through special-purpose machinery premixing, finally small through 24 to 48 in drying chamber
When remove hydrosetting;
(2) bulk and sheet-shaped material are heated to 220 degrees Celsius or more to mold by product quality proportion weighing
Afterwards, raw material is put into mold, by raw material in die cavity pressure-maintaining and heat-preservation, cure it completely;
(3) start press-casting machine, opening mold takes out product;
(4) finally pass through manual grinding, deburring is put in storage pending after cooling through quality inspection.
Pressure-maintaining and heat-preservation time of the raw material in die cavity is 10 minutes in step 2.
Fiber answers the manufacture mold of material cinerary casket or cinerary urn protection structure, is arranged and answers material cinerary casket for implementing fiber
Or the manufacturing method of cinerary urn protection structure, mold use P20 high strength steel mold materials, mold is pressed by die casting machine,
Then assemble through the machining of import high speed finishing impression and manpower.
In the present invention, mold uses P20 high strength steel mold materials, through the machining of import high speed finishing impression and manpower assembling
At the product list that completes tool mold weight reaches 3 tons or more (depending on product specifications), and 150 tons -550 tons of Die-casting Machines (are advised depending on product
Lattice) punching block is pressed by die casting machine, product is cured, is formed, complex process is mainly because die surface carries out firmly
(after common material die hardness processing, hardness only has 35 degree, heats work through 220 degrees Celsius of oil in actual production process for degree processing
When sequence, since intensity is inadequate, can generate can not demould situation, lead to not normally produce), using P20 high strength steel mold materials,
For its hardness after desalt processing, hardness will not generate product size, object up to 55 degree or more, then after 220 degrees Celsius of oil heatings
The problems such as managing performance variations.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (3)
1. the manufacturing method that fiber answers material cinerary casket or cinerary urn protection structure, which comprises
(1) raw material is matched with sheet or dough composition, wherein each rank resin 32%, curing agent 0.4%, aluminium 35%, fiber
30%, then the equal materials mixing of magnesia 0.3% is combined through special-purpose machinery premixing, was finally removed in drying chamber through 24 to 48 hours
Hydrosetting;
(2) by bulk and sheet-shaped material by product quality proportion weighing, after mold heats to 220 degrees Celsius or more, to
Raw material is put into mold, by raw material in die cavity pressure-maintaining and heat-preservation, cure it completely;
(3) start press-casting machine, opening mold takes out product;
(4) finally pass through manual grinding, deburring is put in storage pending after cooling through quality inspection.
2. the manufacturing method that fiber according to claim 1 answers material cinerary casket or cinerary urn protection structure, which is characterized in that
Pressure-maintaining and heat-preservation time of the raw material in die cavity is 10 minutes in the step 2.
3. fiber answers the manufacture mold of material cinerary casket or cinerary urn protection structure, the fiber for implementing claim 1 is set
The manufacturing method of multiple material cinerary casket or cinerary urn protection structure, the mold use P20 high strength steel mold materials, and the mold is logical
It crosses die casting machine to be pressed, then assemble through the machining of import high speed finishing impression and manpower.