WO2024037021A1 - Antimicrobial odor-absorbing wormwood insole, and preparation method therefor and use thereof - Google Patents
Antimicrobial odor-absorbing wormwood insole, and preparation method therefor and use thereof Download PDFInfo
- Publication number
- WO2024037021A1 WO2024037021A1 PCT/CN2023/089997 CN2023089997W WO2024037021A1 WO 2024037021 A1 WO2024037021 A1 WO 2024037021A1 CN 2023089997 W CN2023089997 W CN 2023089997W WO 2024037021 A1 WO2024037021 A1 WO 2024037021A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- antibacterial
- mugwort
- absorbing
- odor
- weight
- Prior art date
Abstract
An antimicrobial odor-absorbing wormwood insole, and a preparation method therefor and the use thereof. The raw materials for preparing the antimicrobial odor-absorbing wormwood insole comprise a combination of a polymer polyol, isocyanate, a wormwood powder, activated carbon, a chain extender and a foaming agent. By adding the wormwood powder and the activated carbon in cooperation with the preparation raw materials, on one hand, the obtained wormwood insole has good antimicrobial, mildew-proof, sweat-absorbing and odor-resistant effects, and on the other hand, the problem of the wormwood powder being quickly dissipated during the use of an insole can be effectively avoided.
Description
本申请属于鞋垫技术领域,例如一种抗菌吸臭艾草鞋垫及其制备方法和应用。The present application belongs to the technical field of insoles, such as an antibacterial and odor-absorbing mugwort insole and its preparation method and application.
鞋垫是鞋子的重要组成部分,由于鞋垫在使用时会直接与人体接触,所以说鞋垫的重要性会直接影响鞋子的舒适度;同时随着人们生活水平的不断提升,对于鞋垫已经不仅仅是舒适度的要求,还要求鞋垫具有其他功能,例如透气、吸汗、防臭、防霉或按摩等功能。Insoles are an important part of shoes. Since insoles will be in direct contact with the human body during use, the importance of insoles will directly affect the comfort of shoes. At the same time, with the continuous improvement of people's living standards, insoles are no longer just comfortable. In addition, insoles are also required to have other functions, such as breathability, sweat absorption, anti-odor, anti-mildew or massage functions.
目前,相关技术中提供的鞋垫大多是由棉或者高分子材料制成。其中,棉质鞋垫仍是目前最常用的鞋垫种类,棉质鞋垫的其主要优势在于吸汗性能优异,且亲肤柔软;但是众所周知,棉的吸水性强,但是抑菌性并不强,耐磨性也较差。高分子材料中聚氨酯发泡材料是目前常用的鞋垫材料,聚氨酯发泡鞋垫具备高回弹性和耐穿性的优点,且具备良好的穿着体验,是高端鞋垫的常用选材。此外聚氨酯发泡鞋垫的制备工艺相对成熟、生产效率较高。因此,聚氨酯发泡鞋垫的产品配方和生产工艺的革新均受到广泛关注。Currently, most of the insoles provided in related technologies are made of cotton or polymer materials. Among them, cotton insoles are still the most commonly used type of insoles. The main advantages of cotton insoles are excellent sweat absorption and softness against the skin. However, as we all know, cotton has strong water absorption, but is not very antibacterial and wear-resistant. Sex is also poor. Among polymer materials, polyurethane foam is currently a commonly used insole material. Polyurethane foam insoles have the advantages of high resilience and durability, and have a good wearing experience. They are a commonly used material for high-end insoles. In addition, the preparation process of polyurethane foam insoles is relatively mature and the production efficiency is high. Therefore, innovations in the product formula and production process of polyurethane foam insoles have received widespread attention.
但是,聚氨酯发泡材料本身不具备吸汗除臭和抑菌的功能,所以目前常用下述手段来提升聚氨酯发泡鞋垫的抑菌、吸臭除汗性能。一是在聚氨酯发泡鞋垫上设置面层材料,在面层添加具有抑菌性能的粉末或者面层选用具有抑菌性能的织物。CN109924605A公开了一种防治足癣的中草药鞋垫,所述鞋垫包括表层、中间填充层和橡胶底层;所述中间填充层填充中草药粉末;所述中草药粉末是由中药组合物制成的;所述中药组合物包括如下重量份的组分:金樱根
18~23份、党参17~24份、当归20~25份、穿心莲12~16份、单面针17~25份、功劳木16~27份、鸡血藤15~20份、千斤拔12~17份;该鞋垫中使用的中草药组合物是根据中药配伍理论,针对足癣的治疗需要,充分发挥中药相生相克、相辅相成的作用,复配而成,疗效显著,制备简单,所述鞋垫对足癣的预防治疗效果显著,无毒副作用,对多种足部真菌具有显著的抑菌活性,可标本兼治,不易复发,使用方便安全舒适,应用前景好。CN112806667A公开了一种汉麻中草药足护按摩养生抑菌鞋垫及其制备方法,鞋垫本体包括聚氨酯层,聚氨酯层耐磨性高、质量轻,聚氨酯层的上表面压制有上麻布层,聚氨酯层的下表面压制有下麻布层,麻布的制作工艺使其透气性增强、抑菌性增强、吸水性增强,聚氨酯层的空腔内放置有以下原料:薰衣草1~3g、迷迭香2~3g、薄荷1~3g;艾草3~4g;桉树叶1~2g;珍珠粉1~2g;黄柏3~4g;苦参3~4g;土荆皮3~4g;罗勒2~3g;柠檬草2~3g,上述中药具有健脾、安神、清热解毒、温经通络、行气活血,解毒消肿的功效,因此使用中药后的鞋垫对人体起到养生保健的作用。但是上述方法存在抑菌效果一般、多次穿着后抑菌性能快速下降的问题。However, polyurethane foam material itself does not have the functions of absorbing sweat, deodorizing and antibacterial, so the following methods are currently commonly used to improve the antibacterial, odor absorbing and desweating properties of polyurethane foam insoles. One is to set a surface layer material on the polyurethane foam insole, add powder with antibacterial properties to the surface layer, or use a fabric with antibacterial properties for the surface layer. CN109924605A discloses a Chinese herbal medicine insole for preventing and treating tinea pedis. The insole includes a surface layer, a middle filling layer and a rubber bottom layer; the middle filling layer is filled with Chinese herbal medicine powder; the Chinese herbal medicine powder is made of a Chinese medicine composition; the Chinese medicine The composition includes the following components by weight: golden cherry root 18 to 23 parts, Codonopsis pilosula 17 to 24 parts, Angelica sinensis 20 to 25 parts, Andrographis paniculata 12 to 16 parts, Acupuncture 17 to 25 parts, Asteria japonica 16 to 27 parts, Millet Spatholobi 15 to 20 parts, Qian Jinpu 12~ 17 parts; the Chinese herbal medicine composition used in the insole is compounded based on the compatibility theory of traditional Chinese medicine, aiming at the treatment needs of tinea pedis, giving full play to the mutually reinforcing and complementary effects of traditional Chinese medicine. It has significant curative effect and is simple to prepare. The insole is effective in treating tinea pedis. It has remarkable preventive and therapeutic effects, has no toxic side effects, has significant antibacterial activity against a variety of foot fungi, can treat both the symptoms and root causes, is not easy to relapse, is easy to use, safe and comfortable, and has good application prospects. CN112806667A discloses a hemp and Chinese herbal foot massage and antibacterial insole and its preparation method. The insole body includes a polyurethane layer. The polyurethane layer has high wear resistance and is light in weight. The upper surface of the polyurethane layer is pressed with a linen layer. The polyurethane layer is There is a lower linen layer pressed on the lower surface. The production process of linen makes it more breathable, antibacterial and water absorbent. The following raw materials are placed in the cavity of the polyurethane layer: 1~3g of lavender, 2~3g of rosemary, Mint 1~3g; mugwort 3~4g; eucalyptus leaves 1~2g; pearl powder 1~2g; cork 3~4g; sophora flavescens 3~4g; wattle bark 3~4g; basil 2~3g; lemongrass 2~ 3g. The above-mentioned traditional Chinese medicine has the effects of strengthening the spleen, calming the nerves, clearing heat and detoxifying, warming the meridians and unblocking collaterals, promoting qi and blood circulation, detoxifying and reducing swelling. Therefore, the insoles after using traditional Chinese medicine play a role in health care for the human body. However, the above method has the problem that the antibacterial effect is average and the antibacterial performance declines rapidly after being worn multiple times.
二是直接对聚氨酯发泡材料进行改性,包括在聚氨酯的制备原料中添加有机/无机抗菌剂来提升聚氨酯材料本身的抗菌、吸汗除臭性能。CN113519978A一种含珍珠麻的抗菌除臭发泡鞋垫及其制备方法。所述抗菌除臭发泡鞋垫从上到下依次为珍珠纤维和麻类纤维混纺而成的珍珠麻贴脚层、发泡层和聚氨酯面料制备的底层,所述发泡层中添加凹凸棒土、珍珠粉和抗菌粉体。该申请制备的抗菌除臭发泡鞋垫,柔软亲肤,具有良好的吸湿排汗能力,可以吸附臭味,抑制微生物的生长,为足部提供一个健康的环境。但是这种方法鞋垫的舒适性较差,且抗菌时效性很短。The second is to directly modify the polyurethane foam material, including adding organic/inorganic antibacterial agents to the raw materials for polyurethane preparation to improve the antibacterial, sweat-absorbing and deodorizing properties of the polyurethane material itself. CN113519978A An antibacterial and deodorizing foam insole containing pearl hemp and its preparation method. The antibacterial and deodorant foam insoles are from top to bottom, a pearl hemp foot layer made of a blend of pearl fiber and hemp fiber, a foam layer and a bottom layer made of polyurethane fabric. Attapulgite is added to the foam layer. , pearl powder and antibacterial powder. The antibacterial and deodorizing foam insoles prepared by this application are soft and skin-friendly, have good moisture absorption and perspiration capabilities, can absorb odors, inhibit the growth of microorganisms, and provide a healthy environment for the feet. However, the comfort of the insoles of this method is poor, and the antibacterial effectiveness is very short.
因此,针对上述问题,急需开发一种具有持久抗菌、吸臭功能,且穿着舒
适的鞋垫。Therefore, in order to solve the above problems, there is an urgent need to develop an antibacterial and odor absorbing device that is comfortable to wear and has long-lasting antibacterial and odor absorbing functions. Fitted insoles.
发明内容Contents of the invention
以下是对本文详细描述的主题的概述。本概述并非是为了限制权利要求的保护范围。The following is an overview of the topics described in detail in this article. This summary is not intended to limit the scope of the claims.
本申请的目的在于提供一种抗菌吸臭艾草鞋垫及其制备方法和应用,所述抗菌吸臭艾草鞋垫的制备原料包括聚合物多元醇、异氰酸酯、艾草粉、活性炭、扩链剂和发泡剂,通过在制备原料添加活性炭和艾草粉进行搭配,可以使得到的抗菌吸臭艾草鞋垫具有持久的抗菌和吸臭功能,且穿戴舒适度高。The purpose of this application is to provide an antibacterial and odor-absorbing mugwort insole and its preparation method and application. The raw materials for preparing the antibacterial and odor-absorbing mugwort insole include polymer polyol, isocyanate, mugwort powder, activated carbon, chain extender and foaming By adding activated carbon and mugwort powder to the preparation raw materials, the resulting antibacterial and odor-absorbing mugwort insole can have long-lasting antibacterial and odor-absorbing functions and be highly comfortable to wear.
为达此目的,本申请采用以下技术方案:To achieve this purpose, this application adopts the following technical solutions:
第一方面,本申请实施例提供一种抗菌吸臭艾草鞋垫,所述抗菌吸臭艾草鞋垫的制备原料包括如下组分:
In a first aspect, embodiments of the present application provide an antibacterial and odor-absorbing mugwort insole. The raw materials for preparing the antibacterial and odor-absorbing mugwort insole include the following components:
In a first aspect, embodiments of the present application provide an antibacterial and odor-absorbing mugwort insole. The raw materials for preparing the antibacterial and odor-absorbing mugwort insole include the following components:
其中,所述聚合物多元醇可以为42重量份、44重量份、46重量份、48重量份、50重量份、52重量份、54重量份、56重量份或58重量份等。Wherein, the polymer polyol can be 42 parts by weight, 44 parts by weight, 46 parts by weight, 48 parts by weight, 50 parts by weight, 52 parts by weight, 54 parts by weight, 56 parts by weight or 58 parts by weight, etc.
所述异氰酸酯可以为26重量份、27重量份、28重量份、29重量份、30重量份、31重量份、32重量份、33重量份或34重量份等。The isocyanate may be 26 parts by weight, 27 parts by weight, 28 parts by weight, 29 parts by weight, 30 parts by weight, 31 parts by weight, 32 parts by weight, 33 parts by weight or 34 parts by weight, etc.
所述艾草粉可以为3.5重量份、4重量份、4.5重量份、5重量份、5.5重量份、6重量份或6.5重量份等。
The mugwort powder can be 3.5 parts by weight, 4 parts by weight, 4.5 parts by weight, 5 parts by weight, 5.5 parts by weight, 6 parts by weight or 6.5 parts by weight, etc.
所述活性炭可以为1.2重量份、1.4重量份、1.6重量份、1.8重量份、2重量份、2.2重量份、2.4重量份、2.6重量份或2.8重量份等。The activated carbon may be 1.2 parts by weight, 1.4 parts by weight, 1.6 parts by weight, 1.8 parts by weight, 2 parts by weight, 2.2 parts by weight, 2.4 parts by weight, 2.6 parts by weight or 2.8 parts by weight, etc.
所述扩链剂可以为2.5重量份、3重量份、3.5重量份、4重量份、4.5重量份、5重量份或5.5重量份等。The chain extender may be 2.5 parts by weight, 3 parts by weight, 3.5 parts by weight, 4 parts by weight, 4.5 parts by weight, 5 parts by weight or 5.5 parts by weight, etc.
所述发泡剂可以为1.2重量份、1.4重量份、1.6重量份、1.8重量份、2重量份、2.2重量份、2.4重量份、2.6重量份或2.8重量份等。The foaming agent may be 1.2 parts by weight, 1.4 parts by weight, 1.6 parts by weight, 1.8 parts by weight, 2 parts by weight, 2.2 parts by weight, 2.4 parts by weight, 2.6 parts by weight or 2.8 parts by weight, etc.
本申请实施例提供的抗菌吸臭艾草鞋垫的制备原料中包括特定份数的聚合物多元醇、异氰酸酯、艾草粉、活性炭、扩链剂和发泡剂的组合,通过在制备原料中添加艾草粉,可以使得到的鞋垫具备良好的抑菌性能,同时搭配加入特定份数的活性炭,一方面,所述活性炭可以与艾草粉协调配合共同起到抑菌的作用,同时还可以增强鞋垫的抗菌除汗吸臭功能,另一方面,利用所述活性炭的吸附能力,牢固地吸附艾草粉,避免艾草粉在鞋垫使用过程中易于消散的问题,进而实现了鞋垫的长效抗菌和吸臭;同时本申请实施例提供的鞋垫还具有耐磨、防滑以及穿戴舒适性高的优势。The raw materials for preparing the antibacterial and odor-absorbing mugwort insoles provided by the embodiments of the present application include a combination of specific parts of polymer polyol, isocyanate, mugwort powder, activated carbon, chain extender and foaming agent. By adding mugwort to the preparation raw materials, Grass powder can make the insoles obtained have good antibacterial properties, and at the same time, a specific proportion of activated carbon can be added. On the one hand, the activated carbon can coordinate with mugwort powder to play an antibacterial role, and can also strengthen the insoles. On the other hand, the adsorption capacity of the activated carbon is used to firmly adsorb mugwort powder, avoiding the problem that mugwort powder is easy to dissipate during the use of the insole, thereby achieving long-term antibacterial and odor absorption of the insole ; At the same time, the insole provided by the embodiment of the present application also has the advantages of wear resistance, anti-slip, and high wearing comfort.
在一个实施例中,所述聚合物多元醇包括聚醚多元醇和聚酯多元醇。In one embodiment, the polymer polyols include polyether polyols and polyester polyols.
在一个实施例中,所述抗菌吸臭艾草鞋垫的制备原料中聚醚多元醇的含量为20~30重量份,例如21重量份、22重量份、23重量份、24重量份、25重量份、26重量份、27重量份、28重量份或29重量份等。In one embodiment, the content of polyether polyol in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 20 to 30 parts by weight, such as 21 parts by weight, 22 parts by weight, 23 parts by weight, 24 parts by weight, and 25 parts by weight. , 26 parts by weight, 27 parts by weight, 28 parts by weight or 29 parts by weight, etc.
在一个实施例中,所述聚醚多元醇包括聚四氢呋喃醚二醇、聚环氧丙烷醚二醇、聚环氧丙烷醚三醇、聚环氧丙烷/环氧乙烷醚二醇或聚乙二醇单甲醚中的任意一种或至少两种的组合。In one embodiment, the polyether polyol includes polytetrahydrofuran ether glycol, polypropylene oxide ether glycol, polypropylene oxide ether triol, polypropylene oxide/ethylene oxide ether glycol or polyethylene oxide. Any one or a combination of at least two of glycol monomethyl ethers.
在一个实施例中,所述抗菌吸臭艾草鞋垫的制备原料中聚酯多元醇的含量为20~30重量份,例如21重量份、22重量份、23重量份、24重量份、25重量
份、26重量份、27重量份、28重量份或29重量份等。In one embodiment, the content of polyester polyol in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 20 to 30 parts by weight, such as 21 parts by weight, 22 parts by weight, 23 parts by weight, 24 parts by weight, and 25 parts by weight. parts, 26 parts by weight, 27 parts by weight, 28 parts by weight or 29 parts by weight, etc.
在一个实施例中,所述聚酯多元醇包括聚碳酸酯二醇、聚己内酯二醇、聚己二酸新戊二醇酯二醇、聚己二酸己二醇酯二醇或聚己二酸丁二醇酯二醇中的任意一种或至少两种的组合。In one embodiment, the polyester polyol includes polycarbonate diol, polycaprolactone diol, polyneopentyl adipate diol, polyhexylene adipate diol or poly Any one or a combination of at least two of butylene glycol adipate diols.
在一个实施例中,所述活性炭和艾草粉的质量比为1:(2~4),例如1:2.2、1:2.4、1:2.6、1:2.8、1:3、1:3.2、1:3.4、1:3.6或1:3.8等。In one embodiment, the mass ratio of activated carbon and mugwort powder is 1: (2-4), such as 1:2.2, 1:2.4, 1:2.6, 1:2.8, 1:3, 1:3.2, 1:3.4, 1:3.6 or 1:3.8 etc.
作为本申请实施例的可选技术方案,限定活性炭和艾草粉的质量比为1:(2~4)可以使二者的协调配合作用达到最优化,保证得到的鞋垫具有最优异的抗菌、吸臭效果,同时持续效果最持久。As an optional technical solution for the embodiments of this application, limiting the mass ratio of activated carbon and mugwort powder to 1: (2-4) can optimize the coordination between the two and ensure that the obtained insoles have the best antibacterial and antibacterial properties. The odor absorbing effect is the longest lasting at the same time.
在一个实施例中,所述异氰酸酯包括1,6-已二异氰酸酯、异佛尔酮二异氰酸酯、4,4-二苯基甲烷二异氰酸酯、六亚甲基二异氰酸酯、双环己基甲烷二异氰酸酯、四甲基苯二亚甲基二异氰酸酯或甲苯二异氰酸酯中的任意一种或至少两种的组合,进一步可选为异佛尔酮二异氰酸酯、双环己基甲烷二异氰酸酯、甲苯二异氰酸酯、六亚甲基二异氰酸酯或4,4-二苯基甲烷二异氰酸酯中的任意一种或至少两种的组合。In one embodiment, the isocyanate includes 1,6-hexane diisocyanate, isophorone diisocyanate, 4,4-diphenylmethane diisocyanate, hexamethylene diisocyanate, biscyclohexylmethane diisocyanate, tetrakis Any one or a combination of at least two of toluene diisocyanate or toluene diisocyanate, further optional isophorone diisocyanate, biscyclohexylmethane diisocyanate, toluene diisocyanate, hexamethylene diisocyanate Any one of diisocyanate or 4,4-diphenylmethane diisocyanate or a combination of at least two.
在一个实施例中,所述扩链剂包括乙二醇和二乙醇氨的组合。In one embodiment, the chain extender includes a combination of ethylene glycol and diethanolamine.
在一个实施例中,所述抗菌吸臭艾草鞋垫的制备原料中乙二醇的含量为3~5重量份,例如3.2重量份、3.4重量份、3.6重量份、3.8重量份、4重量份、4.2重量份、4.4重量份、4.6重量份或4.8重量份等。In one embodiment, the content of ethylene glycol in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 3 to 5 parts by weight, such as 3.2 parts by weight, 3.4 parts by weight, 3.6 parts by weight, 3.8 parts by weight, 4 parts by weight, 4.2 parts by weight, 4.4 parts by weight, 4.6 parts by weight or 4.8 parts by weight, etc.
在一个实施例中,所述抗菌吸臭艾草鞋垫的制备原料中二乙醇胺的含量为1~2重量份,例如1.1重量份、1.2重量份、1.3重量份、1.4重量份、1.5重量份、1.6重量份、1.7重量份、1.8重量份或1.9重量份等。In one embodiment, the content of diethanolamine in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 1 to 2 parts by weight, such as 1.1 parts by weight, 1.2 parts by weight, 1.3 parts by weight, 1.4 parts by weight, 1.5 parts by weight, 1.6 parts by weight parts by weight, 1.7 parts by weight, 1.8 parts by weight or 1.9 parts by weight, etc.
在一个实施例中,所述发泡剂包括水。
In one embodiment, the blowing agent includes water.
在一个实施例中,所述抗菌吸臭艾草鞋垫中还添加有石墨烯。In one embodiment, graphene is added to the antibacterial and odor-absorbing mugwort insoles.
作为本申请实施例的可选技术方案,所述抗菌吸臭艾草鞋垫中还添加有石墨烯,所述石墨烯呈疏松的蠕虫状结构,具有优异的吸臭和抑菌性能,在制备原料中加入一定量的石墨烯,可以与艾草粉、活性炭共同搭配,进一步提升鞋垫的吸臭和抑菌性能。As an optional technical solution for the embodiments of this application, graphene is also added to the antibacterial and odor-absorbing mugwort insoles. The graphene has a loose worm-like structure and has excellent odor-absorbing and antibacterial properties. Adding it to the preparation raw materials A certain amount of graphene can be combined with mugwort powder and activated carbon to further improve the odor absorption and antibacterial performance of the insole.
在一个实施例中,所述抗菌吸臭艾草鞋垫的制备原料中石墨烯的含量为1~2重量份,例如1.1重量份、1.2重量份、1.3重量份、1.4重量份、1.5重量份、1.6重量份、1.7重量份、1.8重量份或1.9重量份等。In one embodiment, the content of graphene in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 1 to 2 parts by weight, such as 1.1 parts by weight, 1.2 parts by weight, 1.3 parts by weight, 1.4 parts by weight, 1.5 parts by weight, and 1.6 parts by weight. parts by weight, 1.7 parts by weight, 1.8 parts by weight or 1.9 parts by weight, etc.
在一个实施例中,所述抗菌吸臭艾草鞋垫的制备原料中还包括催化剂、硅油、色浆或水中的任意一种或至少两种的组合。In one embodiment, the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles also include any one or a combination of at least two of catalysts, silicone oil, color paste, or water.
在一个实施例中,所述抗菌吸臭艾草鞋垫的制备原料中催化剂的含量为0.005~0.04重量份。In one embodiment, the content of the catalyst in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 0.005 to 0.04 parts by weight.
在一个实施例中,所述催化剂包括为三乙基二胺、辛酸亚锡、二月桂酸二丁基锡或三乙胺中的任意一种或至少两种的组合。In one embodiment, the catalyst includes any one or a combination of at least two of triethyldiamine, stannous octoate, dibutyltin dilaurate or triethylamine.
在一个实施例中,所述抗菌吸臭艾草鞋垫的制备原料中硅油的含量为0.5~1.5重量份,例如0.6重量份、0.7重量份、0.8重量份、0.9重量份、1重量份、1.1重量份、1.2重量份、1.3重量份或1.4重量份等。In one embodiment, the content of silicone oil in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 0.5 to 1.5 parts by weight, such as 0.6 parts by weight, 0.7 parts by weight, 0.8 parts by weight, 0.9 parts by weight, 1 part by weight, and 1.1 parts by weight parts, 1.2 parts by weight, 1.3 parts by weight or 1.4 parts by weight, etc.
在一个实施例中,所述抗菌吸臭艾草鞋垫的制备原料中色浆的含量为0.5~1.5重量份,例如0.6重量份、0.7重量份、0.8重量份、0.9重量份、1重量份、1.1重量份、1.2重量份、1.3重量份或1.4重量份等。In one embodiment, the content of color paste in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 0.5 to 1.5 parts by weight, such as 0.6 parts by weight, 0.7 parts by weight, 0.8 parts by weight, 0.9 parts by weight, 1 part by weight, 1.1 parts by weight parts by weight, 1.2 parts by weight, 1.3 parts by weight or 1.4 parts by weight, etc.
在一个实施例中,所述抗菌吸臭艾草鞋垫的制备原料中水的含量为0.5~1.5重量份,例如例如0.6重量份、0.7重量份、0.8重量份、0.9重量份、1重量份、1.1重量份、1.2重量份、1.3重量份或1.4重量份等。
In one embodiment, the water content in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 0.5 to 1.5 parts by weight, such as 0.6 parts by weight, 0.7 parts by weight, 0.8 parts by weight, 0.9 parts by weight, 1 part by weight, 1.1 parts by weight parts by weight, 1.2 parts by weight, 1.3 parts by weight or 1.4 parts by weight, etc.
第二方面,本申请实施例提供一种如第一方面所述抗菌吸臭艾草鞋垫的制备方法,所述制备方法包括:将聚合物多元醇、艾草粉、活性炭、扩链剂、发泡剂、任选地石墨烯、任选地催化剂、任选地色浆和任选地硅油在水中混合,加入异氰酸酯进行反应,发泡成型,得到所述抗菌吸臭艾草鞋垫。In a second aspect, embodiments of the present application provide a method for preparing an antibacterial and odor-absorbing mugwort insole as described in the first aspect. The preparation method includes: combining polymer polyol, mugwort powder, activated carbon, chain extender, foaming Agent, optionally graphene, optionally catalyst, optionally color paste and optionally silicone oil are mixed in water, isocyanate is added for reaction, foaming is formed, and the antibacterial and odor-absorbing mugwort insole is obtained.
在一个实施例中,所述混合的温度为70~90℃,例如72℃、74℃、76℃、78℃、80℃、82℃、84℃、86℃或88℃等。In one embodiment, the mixing temperature is 70-90°C, such as 72°C, 74°C, 76°C, 78°C, 80°C, 82°C, 84°C, 86°C or 88°C, etc.
在一个实施例中,所述混合的时间为1~30min,例如2min、4min、6min、8min、10min、12min、14min、16min、18min、20min、22min、24min、26min或28min等。In one embodiment, the mixing time is 1 to 30 min, such as 2 min, 4 min, 6 min, 8 min, 10 min, 12 min, 14 min, 16 min, 18 min, 20 min, 22 min, 24 min, 26 min or 28 min, etc.
在一个实施例中,所述反应的温度为90~110℃,例如92℃、94℃、96℃、98℃、100℃、102℃、104℃、106℃或108℃等。In one embodiment, the reaction temperature is 90-110°C, such as 92°C, 94°C, 96°C, 98°C, 100°C, 102°C, 104°C, 106°C or 108°C, etc.
在一个实施例中,所述反应的时间为1~2h,例如1.1h、1.2h、1.3h、1.4h、1.5h、1.6h、1.7h、1.8h或1.9h等。In one embodiment, the reaction time is 1 to 2 h, such as 1.1 h, 1.2 h, 1.3 h, 1.4 h, 1.5 h, 1.6 h, 1.7 h, 1.8 h or 1.9 h, etc.
在一个实施例中,所述发泡成型的温度为60~100℃,例如65℃、70℃、75℃、80℃、85℃、90℃、95℃或100℃或等。In one embodiment, the foam molding temperature is 60 to 100°C, such as 65°C, 70°C, 75°C, 80°C, 85°C, 90°C, 95°C or 100°C or the like.
第三方面,本申请实施例提供一种如第一方面所述的抗菌吸臭艾草鞋垫在鞋中的应用。In a third aspect, embodiments of the present application provide an application of the antibacterial and odor-absorbing mugwort insole described in the first aspect in shoes.
在一个实施例中,所述鞋包括运动鞋。In one embodiment, the footwear includes athletic shoes.
相对于相关技术,本申请具有以下有益效果:Compared with related technologies, this application has the following beneficial effects:
(1)本申请提供的抗菌吸臭艾草鞋垫的制备原料中包括特定份数的聚合物多元醇、异氰酸酯、艾草粉、活性炭、扩链剂和发泡剂的组合;通过在制备原料中添加艾草粉,可以使得到的鞋垫具备良好的抑菌性能,同时搭配加入特定份数的活性炭,利用所述活性炭可以与艾草粉协调配合共同起到抑菌的作用,
且还可以吸附艾草粉,进而避免艾草粉在鞋垫使用过程中易于消散,有利于艾草粉长期有效释放,进而实现了鞋垫的长效抗菌和吸臭;同时本申请提供的鞋垫还具有耐磨、防滑以及穿戴舒适性高的优势。(1) The raw materials for preparing the antibacterial and odor-absorbing mugwort insoles provided by this application include a combination of specific parts of polymer polyol, isocyanate, mugwort powder, activated carbon, chain extender and foaming agent; by adding Mugwort powder can make the insoles obtained have good antibacterial properties, and at the same time, a specific amount of activated carbon can be added. The activated carbon can be coordinated with the mugwort powder to jointly play an antibacterial effect. And it can also absorb mugwort powder, thereby preventing mugwort powder from easily dissipating during the use of the insole, which is conducive to the long-term effective release of mugwort powder, thereby achieving long-term antibacterial and odor absorption of the insole; at the same time, the insole provided by this application is also resistant It has the advantages of wear resistance, anti-slip and high wearing comfort.
(2)本申请进一步在制备原料中添加特定份数的石墨烯,所述石墨烯呈疏松的蠕虫状结构,具有优异的吸臭和抑菌性能,所述石墨烯可以与艾草粉、活性炭三者搭配,进一步提升鞋垫的吸收和抑菌性能。(2) This application further adds a specific proportion of graphene to the raw materials. The graphene has a loose worm-like structure and has excellent odor absorption and antibacterial properties. The graphene can be combined with mugwort powder and activated carbon. It can further improve the absorption and antibacterial performance of the insole.
(3)具体而言,本申请提供的抗菌吸臭艾草鞋垫的防臭性能测试显示对氨气的吸收率可达98.1~99.9%,吸水性测试显示吸水率为325~350mg/cm2,抗菌性能测试显示对于金黄色葡萄球菌的抑菌率为98.8~99.99%,对肺炎克雷伯氏菌的抑菌率为97.9~99.9%,对白色念珠菌的抑菌率为97.1~99.9%;且将所述鞋垫放置1个月后再进行抗菌性测试显示,对于金黄色葡萄球菌的抗菌率仍高达98.1~99.1%,对于肺炎克雷伯氏菌的抗菌率为97.1~98.9%,对于白色念珠菌的抗菌率为97.1~98.4%。(3) Specifically, the anti-odor performance test of the antibacterial and odor-absorbing mugwort insoles provided by this application shows that the ammonia absorption rate can reach 98.1~99.9%, and the water absorption test shows that the water absorption rate is 325~350mg/ cm2 . The antibacterial performance Tests show that the antibacterial rate against Staphylococcus aureus is 98.8-99.99%, the antibacterial rate against Klebsiella pneumoniae is 97.9-99.9%, and the antibacterial rate against Candida albicans is 97.1-99.9%; and it will An antibacterial test conducted after the insole was placed for one month showed that the antibacterial rate against Staphylococcus aureus was still as high as 98.1-99.1%, the antibacterial rate against Klebsiella pneumoniae was 97.1-98.9%, and the antibacterial rate against Candida albicans The antibacterial rate is 97.1~98.4%.
下面通过具体实施方式来进一步说明本申请的技术方案。本领域技术人员应该明了,所述实施例仅仅是帮助理解本申请,不应视为对本申请的具体限制。The technical solutions of the present application will be further described below through specific implementations. Those skilled in the art should understand that the embodiments are only to help understand the present application and should not be regarded as specific limitations of the present application.
在具体实施方式部分涉及到的原料及其来源,包括厂家和型号的信息如下表1所示:The raw materials and their sources involved in the specific implementation section, including manufacturer and model information are shown in Table 1 below:
表1
Table 1
Table 1
实施例1Example 1
一种抗菌吸臭艾草鞋垫,其制备原料按照重量份包括如下组分:An antibacterial and odor-absorbing mugwort insole, the raw materials for preparing it include the following components in parts by weight:
聚四氢呋喃醚二醇25重量份、聚碳酸酯二醇25重量份、4,4-二苯基甲烷二异氰酸酯33重量份、艾草粉5重量份、活性炭1.5重量份、乙二醇4重量份、二乙醇氨1.5重量份、水2重量份、色浆1重量份、硅油1重量份、石墨烯2重量份和水1重量份;25 parts by weight of polytetrahydrofuran ether glycol, 25 parts by weight of polycarbonate diol, 33 parts by weight of 4,4-diphenylmethane diisocyanate, 5 parts by weight of mugwort powder, 1.5 parts by weight of activated carbon, and 4 parts by weight of ethylene glycol , 1.5 parts by weight of diethanol ammonia, 2 parts by weight of water, 1 part by weight of color paste, 1 part by weight of silicone oil, 2 parts by weight of graphene and 1 part by weight of water;
本实施例提供的抗菌吸臭艾草鞋垫的制备方法包括:80℃下将聚酯多元醇、聚醚多元醇、艾草粉、活性炭、乙二醇、二乙醇氨、发泡剂、石墨烯、色浆和硅油在水中混合20min,加入4,4-二苯基甲烷二异氰酸酯在100℃下反应60min,70℃下发泡成型,得到所述抗菌吸臭艾草鞋垫。The preparation method of the antibacterial and odor-absorbing mugwort insole provided in this embodiment includes: polyester polyol, polyether polyol, mugwort powder, activated carbon, ethylene glycol, diethanol ammonia, foaming agent, graphene, The color paste and silicone oil were mixed in water for 20 minutes, 4,4-diphenylmethane diisocyanate was added, reacted at 100°C for 60 minutes, and foamed at 70°C to obtain the antibacterial and odor-absorbing mugwort insole.
实施例2Example 2
一种抗菌吸臭艾草鞋垫,其制备原料按照重量份包括如下组分:An antibacterial and odor-absorbing mugwort insole, the raw materials for preparing it include the following components in parts by weight:
聚醚多元醇20重量份、聚酯多元醇20重量份、4,4-二苯基甲烷二异氰酸酯25重量份、艾草粉3重量份、活性炭1重量份、乙二醇3重量份、二乙醇氨1重量份、水1重量份、色浆0.5重量份、硅油0.5重量份、石墨烯1重量份和水0.5重量份;20 parts by weight of polyether polyol, 20 parts by weight of polyester polyol, 25 parts by weight of 4,4-diphenylmethane diisocyanate, 3 parts by weight of mugwort powder, 1 part by weight of activated carbon, 3 parts by weight of ethylene glycol, 1 part by weight of ethanol ammonia, 1 part by weight of water, 0.5 part by weight of color paste, 0.5 part by weight of silicone oil, 1 part by weight of graphene and 0.5 part by weight of water;
本实施例提供的抗菌吸臭艾草鞋垫的制备方法与实施例1相同。The preparation method of the antibacterial and odor-absorbing mugwort insole provided in this embodiment is the same as that in Example 1.
实施例3Example 3
一种抗菌吸臭艾草鞋垫,其制备原料按照重量份包括如下组分:An antibacterial and odor-absorbing mugwort insole, the raw materials for preparing it include the following components in parts by weight:
聚醚多元醇30重量份、聚酯多元醇30重量份、4,4-二苯基甲烷二异氰酸酯35重量份、艾草粉7重量份、活性炭3重量份、乙二醇5重量份、二乙醇氨1
重量份、水3重量份、色浆1.5重量份、硅油1.5重量份、石墨烯2重量份和水1.5重量份;30 parts by weight of polyether polyol, 30 parts by weight of polyester polyol, 35 parts by weight of 4,4-diphenylmethane diisocyanate, 7 parts by weight of mugwort powder, 3 parts by weight of activated carbon, 5 parts by weight of ethylene glycol, Ethanol ammonia 1 Parts by weight, 3 parts by weight of water, 1.5 parts by weight of color paste, 1.5 parts by weight of silicone oil, 2 parts by weight of graphene and 1.5 parts by weight of water;
本实施例提供的抗菌吸臭艾草鞋垫的制备方法与实施例1相同。The preparation method of the antibacterial and odor-absorbing mugwort insole provided in this embodiment is the same as that in Example 1.
实施例4Example 4
一种抗菌吸臭艾草鞋垫,其与实施例1的区别在于,没有添加石墨烯,艾草粉的添加量为6.5重量份,活性炭的添加量为2重量份,其他组分、用量和制备方法均与实施例1相同。An antibacterial and odor-absorbing mugwort insole, which differs from Example 1 in that no graphene is added, the amount of mugwort powder added is 6.5 parts by weight, the amount of activated carbon added is 2 parts by weight, and other components, dosages and preparation methods All are the same as Example 1.
实施例5Example 5
一种抗菌吸臭艾草鞋垫,其与实施例1的区别在于,艾草粉的添加量为4重量份,活性炭的添加量为2.5重量份,其他组分、用量和制备方法均与实施例1相同。An antibacterial and odor-absorbing mugwort insole differs from Example 1 in that the added amount of mugwort powder is 4 parts by weight, the added amount of activated carbon is 2.5 parts by weight, and other components, dosages and preparation methods are the same as those in Example 1 same.
实施例6Example 6
一种抗菌吸臭艾草鞋垫,其与实施例1的区别在于,艾草粉的添加量为5.5重量份,活性炭的添加量为1重量份,其他组分、用量和制备方法均与实施例1相同。An antibacterial and odor-absorbing mugwort insole differs from Example 1 in that the added amount of mugwort powder is 5.5 parts by weight, the added amount of activated carbon is 1 part by weight, and other components, dosages and preparation methods are the same as those in Example 1 same.
对比例1Comparative example 1
一种抗菌吸臭艾草鞋垫,其与实施例1的区别在于,不添加石墨烯和活性炭,艾草粉的添加量为8.5重量份,其他组分、用量和制备方法均与实施例1相同。An antibacterial and odor-absorbing mugwort insole differs from Example 1 in that graphene and activated carbon are not added, the amount of mugwort powder added is 8.5 parts by weight, and other components, dosages and preparation methods are the same as in Example 1.
对比例2Comparative example 2
一种抗菌吸臭艾草鞋垫,其与实施例1的区别在于,不添加石墨烯和艾草粉,活性炭的添加量为8.5重量份,其他组分、用量和制备方法均与实施例1相同。
An antibacterial and odor-absorbing mugwort insole differs from Example 1 in that graphene and mugwort powder are not added, the amount of activated carbon added is 8.5 parts by weight, and other components, dosages and preparation methods are the same as in Example 1.
对比例3Comparative example 3
一种抗菌吸臭艾草鞋垫,其与实施例1的区别在于,不添加艾草粉和活性炭,石墨烯的添加量为8.5重量份,其他组分、用量和制备方法均与实施例1相同。An antibacterial and odor-absorbing mugwort insole differs from Example 1 in that no mugwort powder and activated carbon are added, the amount of graphene added is 8.5 parts by weight, and other components, dosages and preparation methods are the same as in Example 1.
对比例4Comparative example 4
一种抗菌吸臭艾草鞋垫,其与实施例1的区别在于,不添加活性炭,艾草粉的添加量为6.5重量份,其他组分、用量和制备方法均与实施例1相同。An antibacterial and odor-absorbing mugwort insole differs from Example 1 in that no activated carbon is added, the amount of mugwort powder added is 6.5 parts by weight, and other components, dosages and preparation methods are the same as in Example 1.
对比例5Comparative example 5
一种抗菌吸臭艾草鞋垫,其与实施例1的区别在于,不添加艾草粉,活性炭的添加量为6.5重量份,其他组分、用量和制备方法均与实施例1相同。An antibacterial and odor-absorbing mugwort insole differs from Example 1 in that no mugwort powder is added, the amount of activated carbon added is 6.5 parts by weight, and other components, dosages and preparation methods are the same as in Example 1.
对比例6Comparative example 6
一种抗菌吸臭艾草鞋垫,其与实施例1的区别在于,不添加和艾草粉、活性炭和石墨烯,其他组分、用量和制备方法均与实施例1相同。An antibacterial and odor-absorbing mugwort insole differs from Example 1 in that no mugwort powder, activated carbon and graphene are added, and other components, dosages and preparation methods are the same as in Example 1.
性能测试:Performance Testing:
(1)防臭性能:根据《一般社团法人纤维评价技术协议会标准》中的规定采氨气的减少率来评定防臭性,采用检知管法进行,具体操作包括:将100cm2的样品放入采样袋中,然后注入3L氨气使其达到规定的初始浓度,然后2h后使用检测管测定采样袋中氨气的浓度,计算得到氨气或者醋酸的减少率;(1) Deodorization performance: According to the provisions of the "General Corporate Fiber Evaluation Technology Council Standards", the reduction rate of ammonia gas is used to evaluate the deodorization performance, and the detection tube method is used. The specific operations include: placing a 100cm2 sample into into the sampling bag, and then inject 3L ammonia gas to reach the specified initial concentration, and then use a detection tube to measure the concentration of ammonia gas in the sampling bag 2 hours later, and calculate the reduction rate of ammonia gas or acetic acid;
(2)抗菌性能:按照《QB/T2881-2013》提供的测试方法进行测试,测试菌种包括金黄色葡萄球菌(浓度为5.8×105CFU/mL)、肺炎克雷伯氏菌(浓度为7.2×105CFU/mL)和白色念珠菌(浓度为9.1×105CFU/mL);(2) Antibacterial performance: Tested according to the test method provided by "QB/T2881-2013". The test strains include Staphylococcus aureus (concentration: 5.8×10 5 CFU/mL), Klebsiella pneumonia (concentration: 7.2×10 5 CFU/mL) and Candida albicans (concentration 9.1×10 5 CFU/mL);
(3)抗菌持久性:将样品室外自然光下放置一个月后进行抗菌性测试;(3) Antibacterial persistence: Place the sample outdoors under natural light for one month and conduct an antibacterial test;
(4)吸水性:按照《GB21148-2020》提供的测试方法进行测试。
(4) Water absorption: Test according to the test method provided by "GB21148-2020".
按照上述测试方法对实施例1~6和对比例1~6提供的抗菌吸臭艾草鞋垫进行测试,测试结果如表2所示:The antibacterial and odor-absorbing mugwort insoles provided in Examples 1 to 6 and Comparative Examples 1 to 6 were tested according to the above test method. The test results are shown in Table 2:
表2
Table 2
Table 2
根据表2数据可以看出:本申请提供的抗菌吸臭艾草鞋垫兼具优异的吸臭性、抗菌性、抗菌持久性和吸水性;具体而言,实施例1~6提供的抗菌吸臭艾草鞋垫的防臭性能测试显示,对氨气的吸收率可达98.1~99.9%,吸水性测试显
示吸水率为325~350mg/cm2,抗菌性能测试显示对于金黄色葡萄球菌的抑菌率为98.8~99.99%,对肺炎克雷伯氏菌的抑菌率为97.9~99.9%,对白色念珠菌的抑菌率为97.1~99.9%;且将所述鞋垫放置1个月后再进行抗菌性测试显示,对于金黄色葡萄球菌的抗菌率仍高达98.1~99.1%,对于肺炎克雷伯氏菌的抗菌率为97.1~98.9%,对于白色念珠菌的抗菌率为97.1~98.4%。According to the data in Table 2, it can be seen that the antibacterial and odor-absorbing mugwort insoles provided by the present application have excellent odor absorption, antibacterial properties, antibacterial persistence and water absorption; specifically, the antibacterial and odor-absorbing mugwort insoles provided in Examples 1 to 6 The anti-odor performance test shows that the ammonia absorption rate can reach 98.1~99.9%, and the water absorption test shows that The water absorption rate is 325-350 mg/cm 2 . The antibacterial performance test shows that the antibacterial rate against Staphylococcus aureus is 98.8-99.99%, the antibacterial rate against Klebsiella pneumoniae is 97.9-99.9%, and the antibacterial rate against Candida albicans The antibacterial rate of bacteria is 97.1-99.9%; and the antibacterial test after placing the insole for one month shows that the antibacterial rate against Staphylococcus aureus is still as high as 98.1-99.1%, and against Klebsiella pneumoniae The antibacterial rate is 97.1-98.9%, and the antibacterial rate against Candida albicans is 97.1-98.4%.
比较实施例1和对比例1~3可以发现,不添加石墨烯和活性炭而仅添加艾草粉得到的鞋垫、(对比例1)的防臭性、抗菌性和抗菌持久性均有所降低,特别是抗菌持久性;而不添加石墨烯和艾草粉,仅添加活性炭得到的鞋垫(对比例2)虽然防臭性较优异,但是抗菌性和抗菌持久性较差;而不添加艾草粉和活性炭,仅添加石墨烯得到的鞋垫(对比例3)的抗菌性和防臭性同样较差;这说明仅仅添加石墨烯、活性炭或者艾草粉中任意一种得到鞋垫均无法兼具优异的防臭性能、抗菌性和抗菌持久性。Comparing Example 1 and Comparative Examples 1 to 3, it can be found that the insole obtained by adding only mugwort powder without adding graphene and activated carbon (Comparative Example 1) has reduced deodorization, antibacterial properties and antibacterial durability, especially It is antibacterial persistence; without adding graphene and mugwort powder, the insole obtained by adding only activated carbon (Comparative Example 2) has excellent deodorization, but poor antibacterial properties and antibacterial durability; without adding mugwort powder and activated carbon , the antibacterial and deodorizing properties of the insole obtained by adding only graphene (Comparative Example 3) are also poor; this shows that the insole obtained by adding only graphene, activated carbon or mugwort powder cannot have excellent deodorizing properties. Antimicrobial properties and antimicrobial persistence.
再比较实施例1和对比例4~6可以发现,不添加活性炭,仅采用艾草和石墨烯进行搭配(对比例4)、不添加艾草粉,而仅采用石墨烯和活性炭进行搭配(对比例5),或不添加石墨烯、活性炭和艾草粉(对比例6)得到的鞋垫同样无法兼具优异防臭性、抗菌性和抗菌持久性。Comparing Example 1 and Comparative Examples 4 to 6, it can be found that no activated carbon is added, only mugwort and graphene are used for matching (Comparative Example 4), no mugwort powder is added, and only graphene and activated carbon are used for matching (comparative example 4). Ratio 5), or the insoles obtained without adding graphene, activated carbon and mugwort powder (Comparative Example 6) are also unable to have excellent deodorization, antibacterial properties and antibacterial durability.
申请人声明,本申请通过上述实施例来说明一种抗菌吸臭艾草鞋垫及其制备方法和应用,但本申请并不局限于上述实施例,即不意味着本申请必须依赖上述实施例才能实施。所属技术领域的技术人员应该明了,对本申请的任何改进,对本申请产品各原料的等效替换及辅助成分的添加、具体方式的选择等,均落在本申请的保护范围和公开范围之内。
The applicant declares that this application uses the above embodiments to illustrate an antibacterial and odor-absorbing mugwort insole and its preparation method and application. However, this application is not limited to the above embodiments, which does not mean that this application must rely on the above embodiments to implement it. . Those skilled in the art should understand that any improvements to the present application, equivalent replacement of raw materials of the product of the present application, addition of auxiliary ingredients, selection of specific methods, etc., all fall within the protection scope and disclosure scope of the present application.
Claims (17)
- 一种抗菌吸臭艾草鞋垫,所述抗菌吸臭艾草鞋垫的制备原料包括如下组分:
An antibacterial and odor-absorbing mugwort insole. The raw materials for preparing the antibacterial and odor-absorbing mugwort insole include the following components:
- 根据权利要求1所述的抗菌吸臭艾草鞋垫,其中,所述聚合物多元醇包括聚醚多元醇和/或聚酯多元醇。The antibacterial and odor-absorbing mugwort insole according to claim 1, wherein the polymer polyol includes polyether polyol and/or polyester polyol.
- 根据权利要求2所述的抗菌吸臭艾草鞋垫,其中,所述抗菌吸臭艾草鞋垫的制备原料中聚醚多元醇的含量为20~30重量份。The antibacterial and odor-absorbing mugwort insole according to claim 2, wherein the content of the polyether polyol in the raw materials for preparing the antibacterial and odor-absorbing mugwort insole is 20 to 30 parts by weight.
- 根据权利要求2或3所述的抗菌吸臭艾草鞋垫,其中,所述聚醚多元醇包括聚四氢呋喃醚二醇、聚环氧丙烷醚二醇、聚环氧丙烷醚三醇、聚环氧丙烷/环氧乙烷醚二醇或聚乙二醇单甲醚中的任意一种或至少两种的组合。The antibacterial odor-absorbing mugwort insole according to claim 2 or 3, wherein the polyether polyol includes polytetrahydrofuran ether diol, polypropylene oxide ether diol, polypropylene oxide ether triol, polypropylene oxide / Any one or a combination of at least two of ethylene oxide ether glycol or polyethylene glycol monomethyl ether.
- 根据权利要求2-4任一项所述的抗菌吸臭艾草鞋垫,其中,所述抗菌吸臭艾草鞋垫的制备原料中聚酯多元醇的含量为20~30重量份。The antibacterial and odor-absorbing mugwort insole according to any one of claims 2 to 4, wherein the content of polyester polyol in the raw materials for preparing the antibacterial and odor-absorbing mugwort insole is 20 to 30 parts by weight.
- 根据权利要求2-5任一项所述的抗菌吸臭艾草鞋垫,其中,所述聚酯多元醇包括聚碳酸酯二醇、聚己二酸-1,4-丁二醇酯二醇、聚己内酯二醇、聚己二酸新戊二醇酯二醇、聚己二酸己二醇酯二醇或聚己二酸丁二醇酯二醇中的任意一种或至少两种的组合。The antibacterial odor-absorbing mugwort insole according to any one of claims 2 to 5, wherein the polyester polyol includes polycarbonate diol, polybutylene adipate diol, poly Any one or a combination of at least two of caprolactone diol, polyneopentyl adipate diol, polyhexylene adipate diol or polybutylene adipate diol .
- 根据权利要求1-6任一项所述的抗菌吸臭艾草鞋垫,其中,所述活性炭和艾草粉的质量比为1:(2~4)。 The antibacterial and odor-absorbing mugwort insole according to any one of claims 1 to 6, wherein the mass ratio of the activated carbon and mugwort powder is 1: (2-4).
- 根据权利要求1-7任一项所述的抗菌吸臭艾草鞋垫,其中,所述异氰酸酯包括1,6-已二异氰酸酯、异佛尔酮二异氰酸酯、4,4-二苯基甲烷二异氰酸酯、六亚甲基二异氰酸酯、双环己基甲烷二异氰酸酯、四甲基苯二亚甲基二异氰酸酯或甲苯二异氰酸酯中的任意一种或至少两种的组合,可选为异佛尔酮二异氰酸酯、双环己基甲烷二异氰酸酯、甲苯二异氰酸酯、六亚甲基二异氰酸酯或4,4-二苯基甲烷二异氰酸酯中的任意一种或至少两种的组合。The antibacterial odor-absorbing mugwort insole according to any one of claims 1 to 7, wherein the isocyanate includes 1,6-hexane diisocyanate, isophorone diisocyanate, 4,4-diphenylmethane diisocyanate, Any one or a combination of at least two of hexamethylene diisocyanate, bicyclohexylmethane diisocyanate, tetramethylxylylene diisocyanate or toluene diisocyanate, optionally isophorone diisocyanate, bicyclohexyl diisocyanate Any one or a combination of at least two of hexylmethane diisocyanate, toluene diisocyanate, hexamethylene diisocyanate or 4,4-diphenylmethane diisocyanate.
- 根据权利要求1-8任一项所述的抗菌吸臭艾草鞋垫,其中,所述扩链剂包括乙二醇和二乙醇氨的组合;The antibacterial odor-absorbing mugwort insole according to any one of claims 1 to 8, wherein the chain extender includes a combination of ethylene glycol and diethanol ammonia;可选地,所述抗菌吸臭艾草鞋垫的制备原料中乙二醇的含量为3~5重量份;Optionally, the content of ethylene glycol in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 3 to 5 parts by weight;可选地,所述抗菌吸臭艾草鞋垫的制备原料中二乙醇胺的含量为1~2重量份;Optionally, the content of diethanolamine in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 1 to 2 parts by weight;可选地,所述发泡剂包括水。Optionally, the foaming agent includes water.
- 根据权利要求1~9任一项所述的抗菌吸臭艾草鞋垫,其中,所述抗菌吸臭艾草鞋垫中还添加有石墨烯;The antibacterial and odor-absorbing mugwort insole according to any one of claims 1 to 9, wherein graphene is also added to the antibacterial and odor-absorbing mugwort insole;可选地,所述抗菌吸臭艾草鞋垫的制备原料中石墨烯的含量为1~2重量份。Optionally, the content of graphene in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 1 to 2 parts by weight.
- 根据权利要求1~10任一项所述的抗菌吸臭艾草鞋垫,其中,所述抗菌吸臭艾草鞋垫的制备原料中还包括催化剂、硅油、色浆或水中的任意一种或至少两种的组合;The antibacterial odor-absorbing mugwort insole according to any one of claims 1 to 10, wherein the raw materials for preparing the antibacterial odor-absorbing mugwort insole also include any one or at least two of catalyst, silicone oil, color paste or water. combination;可选地,所述抗菌吸臭艾草鞋垫的制备原料中催化剂的含量为0.005~0.04重量份;Optionally, the content of the catalyst in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 0.005 to 0.04 parts by weight;可选地,所述抗菌吸臭艾草鞋垫的制备原料中硅油的含量为0.5~1.5重量份;Optionally, the content of silicone oil in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 0.5 to 1.5 parts by weight;可选地,所述抗菌吸臭艾草鞋垫的制备原料中色浆的含量为0.5~1.5重量份; Optionally, the content of color paste in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 0.5 to 1.5 parts by weight;可选地,所述抗菌吸臭艾草鞋垫的制备原料中水的含量为0.5~1.5重量份。Optionally, the water content in the raw materials for preparing the antibacterial and odor-absorbing mugwort insoles is 0.5 to 1.5 parts by weight.
- 根据权利要求11所述的抗菌吸臭艾草鞋垫,其中,所述催化剂包括三乙基二胺、辛酸亚锡、二月桂酸二丁基锡或三乙胺中的任意一种或至少两种的组合。The antibacterial and odor-absorbing mugwort insole according to claim 11, wherein the catalyst includes any one or a combination of at least two of triethyldiamine, stannous octoate, dibutyltin dilaurate or triethylamine.
- 一种如权利要求1~12任一项所述抗菌吸臭艾草鞋垫的制备方法,所述制备方法包括:将聚合物多元醇、艾草粉、活性炭、扩链剂、发泡剂、任选地石墨烯、任选地催化剂、任选地色浆和任选地硅油在水中混合,加入异氰酸酯进行反应,发泡成型,得到所述抗菌吸臭艾草鞋垫。A method for preparing antibacterial and odor-absorbing mugwort insoles according to any one of claims 1 to 12, the preparation method comprising: combining polymer polyol, mugwort powder, activated carbon, chain extender, foaming agent, and optionally Graphene, optional catalyst, optional color paste and optional silicone oil are mixed in water, isocyanate is added for reaction, and foaming is formed to obtain the antibacterial and odor-absorbing mugwort insole.
- 根据权利要求13所述的制备方法,其中,所述混合的温度为70~90℃;The preparation method according to claim 13, wherein the mixing temperature is 70-90°C;可选地,所述混合的时间为1~30min。Optionally, the mixing time is 1 to 30 minutes.
- 根据权利要求13或14所述的制备方法,其中,所述反应的温度为90~110℃;The preparation method according to claim 13 or 14, wherein the temperature of the reaction is 90-110°C;可选地,步骤(2)所述反应的时间为1~2h。Optionally, the reaction time in step (2) is 1 to 2 hours.
- 根据权利要求13~15任一项所述的制备方法,其中,所述发泡成型的温度为60~100℃。The preparation method according to any one of claims 13 to 15, wherein the foam molding temperature is 60 to 100°C.
- 一种如权利要求1~12任一项所述的抗菌吸臭艾草鞋垫在鞋中的应用;An application of the antibacterial and odor-absorbing mugwort insole in shoes according to any one of claims 1 to 12;可选地,所述鞋包括运动鞋。 Optionally, the shoes include sports shoes.