WO2023248906A1 - 断熱層と粘着層とを備えるシート - Google Patents
断熱層と粘着層とを備えるシート Download PDFInfo
- Publication number
- WO2023248906A1 WO2023248906A1 PCT/JP2023/022127 JP2023022127W WO2023248906A1 WO 2023248906 A1 WO2023248906 A1 WO 2023248906A1 JP 2023022127 W JP2023022127 W JP 2023022127W WO 2023248906 A1 WO2023248906 A1 WO 2023248906A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- meth
- acrylate
- hollow particles
- heat insulating
- less
- Prior art date
Abstract
断熱層と、粘着層と、を備え、粘着層が、アクリル共重合体と、エポキシ基を有する架橋剤と、を含む、シート。
Description
本発明は、断熱層と粘着層とを備えるシートに関する。
低消費電力及び高速読み書きを特徴とする不揮発性メモリが、次世代メモリとして注目を集めている。例えば、相変化メモリ（ＰＣＭ）、磁気抵抗メモリ（ＭＲＡＭ）、抵抗変化型メモリ（ＲｅＲＡＭ）等が知られている。不揮発性メモリは、熱に弱く、実装時のリフロー工程において高温環境に晒されたときの品質維持が課題となっている。
この課題に対し、例えば特許文献１では、磁気記録装置のリフロー炉内に露出する表面に断熱材を設ける第１ステップと、断熱材を備えた磁気記録装置をリフロー炉内に通し、磁気記録装置を加熱する第２ステップと、加熱された磁気記録装置から断熱材を取り除く第３ステップとを有するリフロー工程を備えた磁気記録装置の製造方法が開示されている。
本発明者らは、上記のような断熱材として、断熱層と粘着層とを備えるシートの使用を検討した。このような断熱材を用いる場合、粘着層を被着体（磁気記録装置）に粘着させることにより断熱材を被着体上に設けるが、リフロー工程の後に断熱材を取り除く際には、断熱材を容易に剥がすことができること（すなわち、断熱材が優れた剥離性を有していること）が好ましい。
そこで、本発明の一側面は、リフロー工程後の剥離性に優れた断熱材に適したシートを提供することを目的とする。
本発明者らの検討によれば、粘着層がアクリル共重合体と架橋剤とを含む場合に、架橋剤の種類によって、リフロー工程後のシートのピール強度が異なり、その結果、剥離性も異なることが明らかとなった。そして、本発明者らは、架橋剤としてエポキシ系架橋剤を用いることにより、リフロー工程後のシートのピール強度を小さくすることができ、リフロー工程後の剥離性に優れたシートを提供することができることを見出した。本発明は、いくつかの側面において、下記の［１］～［５］を提供する。
［１］断熱層と、粘着層と、を備え、粘着層が、アクリル共重合体と、エポキシ基を有する架橋剤と、を含む、シート。
［２］断熱層が、中空粒子と、マトリックスポリマーと、を含有する、［１］に記載のシート。
［３］マトリックスポリマーが、下記式（１）で表される化合物をモノマー単位として含む、［２］に記載のシート。
［式（１）中、Ｒ１１及びＲ１２はそれぞれ独立に水素原子又はメチル基を表し、Ｒ１３はポリオキシアルキレン鎖を有する２価の基を表す。］
［４］中空粒子が、有機中空粒子を含む、［２］又は［３］に記載のシート。
［５］有機中空粒子が、熱膨張性の有機中空粒子である第一の中空粒子と、第一の中空粒子以外の有機中空粒子である第二の中空粒子と、を含む、［４］に記載のシート。
［２］断熱層が、中空粒子と、マトリックスポリマーと、を含有する、［１］に記載のシート。
［３］マトリックスポリマーが、下記式（１）で表される化合物をモノマー単位として含む、［２］に記載のシート。
［４］中空粒子が、有機中空粒子を含む、［２］又は［３］に記載のシート。
［５］有機中空粒子が、熱膨張性の有機中空粒子である第一の中空粒子と、第一の中空粒子以外の有機中空粒子である第二の中空粒子と、を含む、［４］に記載のシート。
本発明の一側面によれば、リフロー工程後の剥離性に優れた断熱材に適したシートを提供することができる。
以下、本発明の実施形態について詳細に説明する。なお、本発明は、以下の実施形態に限定されない。
本明細書における、「（メタ）アクリロイル」とは、「アクリロイル」及びそれに対応する「メタクリロイル」を意味し、「（メタ）アクリレート」、「（メタ）アクリル」等の類似表現においても同様である。
本明細書における重量平均分子量（Ｍｗ）は、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）を用いて以下の条件で測定され、ポリスチレンを標準物質として決定される値を意味する。
・測定機器：ＨＬＣ－８３２０ＧＰＣ（製品名、東ソー（株）製）
・分析カラム：ＴＳＫｇｅｌ ＳｕｐｅｒＭｕｌｔｉｐｏｒｅ ＨＺ－Ｈ（３本連結）（製品名、東ソー（株）製）
・ガードカラム：ＴＳＫｇｕａｒｄｃｏｌｕｍｎ ＳｕｐｅｒＭＰ（ＨＺ）－Ｈ（製品名、東ソー（株）製）
・溶離液：ＴＨＦ
・測定温度：２５℃
・測定機器：ＨＬＣ－８３２０ＧＰＣ（製品名、東ソー（株）製）
・分析カラム：ＴＳＫｇｅｌ ＳｕｐｅｒＭｕｌｔｉｐｏｒｅ ＨＺ－Ｈ（３本連結）（製品名、東ソー（株）製）
・ガードカラム：ＴＳＫｇｕａｒｄｃｏｌｕｍｎ ＳｕｐｅｒＭＰ（ＨＺ）－Ｈ（製品名、東ソー（株）製）
・溶離液：ＴＨＦ
・測定温度：２５℃
図１は、シートの一実施形態を示す模式断面図である。図１に示されるシート１０は、断熱層１１と、粘着層１２と、を備えている。断熱層１１と粘着層１２とは、互いに接するように積層されていてよい。
粘着層１２は、アクリル共重合体と、エポキシ基を有する架橋剤と、を含む。
アクリル共重合体は、２種以上の重合性化合物の共重合体である。当該２種以上の重合性化合物が、（メタ）アクリロイル基を有する化合物を１種以上含む。アクリル共重合体は、モノマー単位として、（メタ）アクリロイル基を有する化合物を１種以上含むが、２種以上、３種以上、又は４種以上含んでいてもよい。
（メタ）アクリロイル基を有する化合物は、例えば、アルキル（メタ）アクリレートであってよい。アルキル（メタ）アクリレートにおけるアルキル基（（メタ）アクリロイル基以外のアルキル基部分）は、直鎖状であっても分岐状であっても環状であってもよい。アルキル基の炭素数は、例えば、１～３０であってよい。アルキル基の炭素数は、２以上、又は３以上であってよく、２５以下、２０以下、１５以下、１０以下、７以下、又は５以下であってよい。
直鎖状のアルキル基を有するアルキル（メタ）アクリレートとしては、例えば、炭素数１～１１の直鎖状アルキル基を有するアルキル（メタ）アクリレート、及び炭素数１２～３０の直鎖状アルキル基を有するアルキル（メタ）アクリレートが挙げられる。
炭素数１～１１の直鎖状アルキル基を有するアルキル（メタ）アクリレートとしては、メチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクリレート、ブチル（メタ）アクリレート、ペンチル（メタ）アクリレート、ｎ－ヘキシル（メタ）アクリレート、ｎ－へプチル（メタ）アクリレート、オクチル（メタ）アクリレート、ノニル（メタ）アクリレート、デシル（メタ）アクリレート、ウンデシル（メタ）アクリレート等が挙げられる。
炭素数１２～３０の直鎖状アルキル基を有するアルキル（メタ）アクリレートとしては、ドデシル（メタ）アクリレート（ラウリル（メタ）アクリレート）、テトラデシル（メタ）アクリレート、ヘキサデシル（メタ）アクリレート（セチル（メタ）アクリレート）、オクタデシル（メタ）アクリレート（ステアリル（メタ）アクリレート）、ドコシル（メタ）アクリレート（ベヘニル（メタ）アクリレート）、テトラコシル（メタ）アクリレート、ヘキサコシル（メタ）アクリレート、オクタコシル（メタ）アクリレート等が挙げられる。
分岐状のアルキル基を有するアルキル（メタ）アクリレートとしては、例えば、炭素数１～１１の分岐状アルキル基を有するアルキル（メタ）アクリレート、及び炭素数１２～３０の分岐状アルキル基を有するアルキル（メタ）アクリレートが挙げられる。
炭素数１～１１の分岐状アルキル基を有するアルキル（メタ）アクリレートとしては、ｓ－ブチル（メタ）アクリレート、ｔ－ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、イソペンチル（メタ）アクリレート、イソアミル（メタ）アクリレート、イソオクチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、イソノニル（メタ）アクリレート、イソデシル（メタ）アクリレート等が挙げられる。
炭素数１２～３０の分岐状アルキル基を有するアルキル（メタ）アクリレートとしては、イソミリスチル（メタ）アクリレート、２－プロピルヘプチル（メタ）アクリレート、イソウンデシル（メタ）アクリレート、イソドデシル（メタ）アクリレート、イソトリデシル（メタ）アクリレート、イソペンタデシル（メタ）アクリレート、イソヘキサデシル（メタ）アクリレート、イソヘプタデシル（メタ）アクリレート、イソステアリル（メタ）アクリレート、デシルテトラデカニル（メタ）アクリレート等が挙げられる。
脂環式（環状）であるアルキル基（シクロアルキル基）を有するアルキル（メタ）アクリレートとしては、シクロヘキシル（メタ）アクリレート、３，３，５－トリメチルシクロヘキシル（メタ）アクリレート、イソボルニル（メタ）アクリレート、テルペン（メタ）アクリレート、ジシクロペンタニル（メタ）アクリレート等が挙げられる。
（メタ）アクリロイル基を有する化合物は、（メタ）アクリロイル基に加えて、ヘテロ環を含む基、ヒドロキシル基、又はカルボキシル基を有する化合物であってもよい。
（メタ）アクリロイル基及びヘテロ環を含む基を有する化合物の例としては、Ｎ－アクリロイルモルホリン（ＡＣＭＯ）、及びテトラヒドロフルフリル（メタ）アクリレートが挙げられる。
（メタ）アクリロイル基及びヒドロキシル基を有する化合物の例としては、ヒドロキシアルキル（メタ）アクリレート、ヒドロキシアルキルシクロアルカン（メタ）アクリレート等が挙げられる。ヒドロキシアルキル（メタ）アクリレートとしては、２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、３－ヒドロキシプロピル（メタ）アクリレート、２－ヒドロキシブチル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート、６－ヒドロキシヘキシル（メタ）アクリレート、８－ヒドロキシオクチル（メタ）アクリレート、１０－ヒドロキシデシル（メタ）アクリレート、１２－ヒドロキシラウリル（メタ）アクリレート等が挙げられる。ヒドロキシアルキルシクロアルカン（メタ）アクリレートとしては、（４－ヒドロキシメチルシクロへキシル）メチル（メタ）アクリレート等が挙げられる。
（メタ）アクリロイル基及びカルボキシル基を有する化合物の例としては、（メタ）アクリル酸、カルボキシエチル（メタ）アクリレート、カルボキシペンチル（メタ）アクリレート、フタル酸モノヒドロキシエチルアクリレート（例えば、東亞合成（株）製「アロニックスＭ５４００」）、及び２－アクリロイルオキシエチルサクシネート（例えば、新中村化学株式会社製「ＮＫエステル Ａ－ＳＡ」）が挙げられる。
アクリル共重合体は、（メタ）アクリロイル基を有する化合物以外の他の重合性化合物をモノマー単位として含んでいてもよい。アクリル共重合体における他の重合性化合物（モノマー単位）の例としては、アクリロニトリルが挙げられる。
アクリル共重合体の重量平均分子量（Ｍｗ）は、２０万以上、４０万以上、５０万以上、又は６０万以上であってもよく、１２０万以下、１１０万以下、又は１００万以下であってもよい。
アクリル共重合体の多分散度（重量平均分子量（Ｍｗ）と数平均分子量（Ｍｎ）との比（Ｍｗ／Ｍｎ））は、１．１以上、又は１．５以上であってもよく、７．０以下であってもよい。
アクリル共重合体のガラス転移温度（Ｔｇ）は、－５０℃以上、又は－４５℃以上であってもよく、－５℃以下、又は－１０℃以下であってもよい。
アクリル共重合体の酸価は、２０．０ｍｇＫＯＨ／ｇ以上であってよく、３０．０ｍｇＫＯＨ／ｇ以下であってもよい。
アクリル共重合体におけるカルボキシル基の濃度は、２．００×１０―４ｍｏｌ／Ｌ以上以上であってもよく、１１．００×１０―４ｍｏｌ／Ｌ以下であってもよい。
アクリル共重合体における水酸基の濃度は、１．００×１０―４ｍｏｌ／Ｌ以上であってもよく、５．００×１０―４ｍｏｌ／Ｌ以下であってもよい。
アクリル共重合体の含有量は、粘着層１２の全質量を基準として、７０質量％以上、又は８０質量％以上であってよく、９８質量％以下、又は９５質量％以下であってよい。
エポキシ基を有する架橋剤は、エポキシ基を２個以上、３個以上、又は４個以上有していてもよい。エポキシ基を４個有する架橋剤としては、例えば、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラグリシジル－１，３－ビス（アミノメチル）シクロヘキサン（下記式（Ｂ－１）で表される架橋剤）、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラグリシジル－ｍ－キシレンジアミン（下記式（Ｂ－２）で表される架橋剤）等が挙げられる。また、エポキシ基を２個以上有する架橋剤としては、例えば、ソルビトールポリグリシジルエーテル、トリメチロールプロパンポリグリシジルエーテル、ジグリセロールポリグリシジルエーテル等が挙げられる。
エポキシ基を有する架橋剤の含有量は、粘着層１２の全質量を基準として、１質量％以上、又は５質量％以上であってよく、２０質量％以下、又は１５質量％以下であってよい。
粘着層１２は、アクリル共重合体及びエポキシ基を有する架橋剤に加えて、酸化防止剤等の添加剤を更に含んでいてよい。酸化防止剤の例としては、４，４－ビス（α，α－ジメチルベンジル）ジフェニルアミン、ｐ，ｐ’－ジオクチルジフェニルアミン等のフェニルアミン系酸化防止剤が挙げられる。
粘着層１２の厚みは、例えば、例えば、５μｍ以上、又は１０μｍ以上であってよく、５０μｍ以下、４０μｍ以下、又は３０μｍ以下であってよい。
断熱層１１は、断熱性を有する層であればよい。断熱層１１の２５℃における熱伝導率は、好ましくは、１３０ｍＷ／（ｍ・Ｋ）以下、１００ｍＷ／（ｍ・Ｋ）以下、又は８０ｍＷ／（ｍ・Ｋ）以下である。
断熱層１１の材質は特に制限されない。断熱層１１は、多孔質材料で構成される層であってよい。多孔質材料は、有機多孔質材料であってよく、無機多孔質材料であってもよい。有機多孔質材料の例としては、樹脂製の多孔質材料が挙げられる。樹脂製の多孔質材料の例としては、メラミン樹脂製の多孔質材料（メラミンスポンジ）が挙げられる。無機多孔質材料の例としては、炭素製の多孔質材料、ガラス製の多孔質材料が挙げられる。炭素製の多孔質材料の例としては、カーボンフェルトが挙げられる。ガラス製の多孔質材料の例としては、ガラス繊維紙、ガラスフェルトが挙げられる。
断熱層１１は、中空粒子を含む層であってもよい。断熱層１１は、例えば、中空粒子と、マトリックスポリマーと、を含有していてもよい。
中空粒子は、外殻と中空部とを有する粒子である。中空粒子はその外殻が有機材料により構成されている有機中空粒子であってもよく、その外殻が無機材料により構成されている無機中空粒子であってもよい。中空粒子は、無機中空粒子及び有機中空粒子のいずれか一方を含んでいてよく、両方を含んでいてよい。
有機中空粒子としては、熱膨張性の有機中空粒子である第一の中空粒子、及び、当該第一の中空粒子以外の有機中空粒子である第二の中空粒子が挙げられる。有機中空粒子は、第一の中空粒子及び第二の中空粒子のいずれか一方又は両方を含んでいてよく、好ましくは第一の中空粒子及び第二の中空粒子の両方を含んでいる。
第一の中空粒子は、熱により膨張する（熱膨張性の）有機中空粒子である。本明細書における熱膨張性の有機中空粒子とは、２５℃における体積に対する最大体積膨張倍率が１０倍以上である有機中空粒子である。断熱層１１が第一の中空粒子を含有する場合、リフロー工程において、断熱層１１の断熱性を低下させる方向にはたらく現象が生じた場合でも（例えば、後述する第二の中空粒子が収縮して、中空部の体積が減少した場合でも）、第一の中空粒子が熱によって膨張し、断熱層１１の断熱性に寄与する中空部の体積が増加する。そのため、断熱層１１（シート１０）の断熱性の低下を抑制することができる。
第一の中空粒子の最大体積膨張倍率は、熱機械分析（ＴＭＡ）にて、昇温速度１０℃／分で昇温したときの、第一の中空粒子の最大体積と２５℃における体積との比（最大体積／２５℃における体積）として測定される。第一の中空粒子の最大体積膨張倍率は、例えば、２０倍以上、３０倍以上、又は４０倍以上であってもよく、１２０倍以下であってもよい。
第一の中空粒子の外殻は、好ましくはポリマーで構成されており、更に好ましくは熱可塑性ポリマーで構成されている。この場合、外殻が加熱により軟らかくなるため、中空部に内包されている液体が気化して内圧が上がっても、中空粒子は割れにくく、容易に膨張する。熱可塑性ポリマーは、例えば、アクリロニトリル、塩化ビニリデン等をモノマー単位として含むポリマーであってよい。外殻の厚さは、２μｍ以上であってよく、１５μｍ以下であってよい。
第一の中空粒子の中空部には、例えば液体が内包されている。第一の中空粒子は、例えば、常温常圧下（例えば、少なくとも大気圧下かつ３０℃）において液体を内包している。当該液体は、例えば、リフロー工程における加熱温度及び後述する第二の中空粒子の収縮開始温度に応じて適宜選択される。当該液体は、例えば、リフロー工程における最高加熱温度以下の温度で気化する液体である。当該液体は、第二の中空粒子の収縮開始温度以下の温度で気化する液体であってもよい。当該液体は、例えば、沸点（大気圧下）が、５０℃以上、１００℃以上、１５０℃以上、又は２００℃以上の炭化水素であってよい。第一の中空粒子の中空部には、上記の液体に加えて、気体が更に内包されていてもよい。
第一の中空粒子の中空部に内包されている成分としては、例えば、プロパン、プロピレン、ブテン、ノルマルブタン、イソブタン、ノルマルペンタン、イソペンタン、ネオペンタン、ノルマルヘキサン、イソヘキサン、ヘプタン、イソオクタン、ノルマルオクタン、イソアルカン（炭素数：１０～１３）、石油エーテル等の炭化水素；メタンのハロゲン化物、テトラアルキルシラン等の低沸点化合物；アゾジカルボンアミド等の熱分解によりガス化する化合物が挙げられる。
第一の中空粒子の平均粒子径は、５μｍ以上、又は１０μｍ以上であってよく、５０μｍ以下、４０μｍ以下、又は３０μｍ以下であってよい。第一の中空粒子の平均粒子径は、レーザー回折・散乱法により（例えば、（株）島津製作所製「ＳＡＬＤ－７５００ｎａｎｏ」を用いて）測定される。
シート１０がリフロー工程（一般的に２６０℃まで加熱される）における断熱材としてより好適に用いられる観点から、第一の中空粒子の膨張開始温度は、後述する第二の中空粒子の収縮開始温度以下であることが好ましい。第一の中空粒子の膨張開始温度は、好ましくは、１５０℃以上、又は１８０℃以上であり、好ましくは、２６０℃以下、２４０℃以下、２２０℃以下、又は２００℃以下である。第一の中空粒子の膨張開始温度は、熱機械分析（ＴＭＡ）にて、昇温速度１０℃／分で昇温したときの温度（横軸）－体積変化（縦軸）のプロファイルにおいて、３倍以上／５℃の体積変化が生じる点の接線と、体積変化がゼロ（初期体積）の直線（横軸）との交点の温度を意味する。
シート１０がリフロー工程における断熱材としてより好適に用いられる観点から、第一の中空粒子の最大膨張温度は、好ましくは、１００℃以上、１５０℃以上、２００℃以上、又は２１０℃以上であり、好ましくは、２９０℃以下、２８０℃以下、又は２７０℃以下である。第一の中空粒子の最大膨張温度は、第一の中空粒子が上述した最大体積膨張倍率を示すときの温度を意味する。
第一の中空粒子の含有量（大気圧下かつ３０℃における含有量。以下同様。）は、シート１０の断熱性の低下を更に抑える観点から、断熱層１１の全質量を基準として、好ましくは１質量％以上、より好ましくは２質量％以上、更に好ましくは４質量％以上、特に好ましくは５質量％以上であり、２０質量％以下、又は１５質量％以下であってよい。
第一の中空粒子の含有量は、シート１０の断熱性の低下を抑える観点から、断熱層１１の全体積を基準として、好ましくは０．５体積％以上、より好ましくは１．０体積％以上、更に好ましくは１．５体積％以上である。シート１０の体積の過度な膨張を抑える観点から、第一の中空粒子の含有量は、断熱層１１の全体積を基準として、１０体積％以下、７体積％以下、５体積％以下、又は４体積％以下であってよい。
第二の中空粒子は、第一の中空粒子以外の有機中空粒子である。すなわち、第二の中空粒子は、２５℃における体積に対する最大体積膨張倍率が１０倍未満である有機中空粒子である。第二の中空粒子を用いることにより、断熱層１１の断熱性が向上し、シート１０を断熱材としてより好適に利用することができる。第二の中空粒子の最大体積膨張倍率は、第一の中空粒子の最大体積膨張倍率と同じ方法で測定される。
第二の中空粒子の外殻は、有機材料により構成されている。第二の中空粒子の外殻は、好ましくはポリマーで構成されており、より好ましくは熱可塑性ポリマーで構成されている。この場合、中空粒子は加圧されても割れにくく、中空構造を保持できるため、シート１０の断熱性が維持されやすくなる。熱可塑性ポリマーは、例えば、アクリロニトリル、塩化ビニリデン等をモノマー単位として含むポリマーであってよい。外殻の厚さは、０．００５μｍ以上であってよく、１５μｍ以下であってよい。
第二の中空粒子の中空部には、例えば気体が内包されている。第二の中空粒子は、例えば、常温常圧下（例えば、少なくとも大気圧下かつ３０℃）において気体を内包している。第二の中空粒子の中空部には、気体に加えて、液体が更に内包されていてもよい。
第二の中空粒子の中空部に内包されている成分としては、例えば、プロパン、プロピレン、ブテン、ノルマルブタン、イソブタン、ノルマルペンタン、イソペンタン、ネオペンタン、ノルマルヘキサン、イソヘキサン、ヘプタン、イソオクタン、ノルマルオクタン、イソアルカン（炭素数：１０～１３）、石油エーテル等の炭化水素；メタンのハロゲン化物、テトラアルキルシラン等の低沸点化合物；アゾジカルボンアミド等の熱分解によりガス化する化合物の分解生成物が挙げられる。また、第二の中空粒子の中空部に内包されている成分は、空気であってもよい。
第二の中空粒子の平均粒子径は、断熱性を高める観点から、好ましくは１５０μｍ以下であり、より好ましくは１２０μｍ以下であり、更に好ましくは１００μｍ以下であり、例えば、５μｍ以上、１０μｍ以上、２０μｍ以上、又は３０μｍ以上であってよい。第二の中空粒子の平均粒子径は、レーザー回折・散乱法により（例えば、（株）島津製作所製「ＳＡＬＤ－７５００ｎａｎｏ」を用いて）測定される。
第二の中空粒子の密度は、５００ｋｇ／ｍ３以下、３００ｋｇ／ｍ３以下、１００ｋｇ／ｍ３以下、５０ｋｇ／ｍ３以下、又は４０ｋｇ／ｍ３以下であってよく、１０ｋｇ／ｍ３以上、又は２０ｋｇ／ｍ３以上であってよい。本明細書における第二の中空粒子の密度は、タップ密度法にて測定される密度を意味する。すなわち、１０ｍＬのメスシリンダーに第二の中空粒子（約５ｇ）を投入し、５０回タッピングし、最上面が安定した時の体積を安定時体積として、以下の式により求められる密度である。
密度＝初期投入量（ｋｇ）／安定時体積（ｍ３）
密度＝初期投入量（ｋｇ）／安定時体積（ｍ３）
シート１０がリフロー工程（一般的に２６０℃まで加熱される）における断熱材としてより好適に用いられる観点から、第二の中空粒子の収縮開始温度は、好ましくは、１５０℃以上、１７０℃以上、又は１８０℃以上であり、２６０℃以下、２４０℃以下、２２０℃以下、又は２００℃以下であってもよい。第二の中空粒子の収縮開始温度は、熱機械分析（ＴＭＡ）にて、昇温速度１０℃／分で昇温したときの温度（横軸）－体積変化（縦軸）のプロファイルにおいて、体積変化が極大値となったときの温度を意味する。
第二の中空粒子の含有量（大気圧下かつ３０℃における含有量。以下同様。）は、シート１０の断熱性を高める観点から、断熱層１１の全質量を基準として、好ましくは１質量％以上であり、より好ましくは３質量％以上であり、更に好ましくは５質量％以上であり、例えば２０質量％以下であってよい。
第二の中空粒子の含有量は、シート１０の断熱性を高める観点から、断熱層１１の全体積を基準として、好ましくは５０体積％以上であり、より好ましくは６０体積％以上であり、例えば９５体積％以下であってよい。
第一の中空粒子の含有量に対する第二の中空粒子の含有量の質量比（第二の中空粒子の含有量（質量）／第一の中空粒子の含有量（質量））は、好ましくは１／５以上であり、より好ましくは１／３以上である。第一の中空粒子の含有量に対する第二の中空粒子の含有量の質量比は、好ましくは３以下であり、より好ましくは２以下であり、更に好ましくは１以下である。
第一の中空粒子の含有量に対する第二の中空粒子の含有量の体積比（第二の中空粒子の含有量（体積）／第一の中空粒子の含有量（体積））は、好ましくは１０以上であり、より好ましくは１５以上である。第一の中空粒子の含有量に対する第二の中空粒子の含有量の体積比は、好ましくは８０以下であり、より好ましくは６０以下であり、更に好ましくは４５以下である。
無機中空粒子の外殻を構成する無機材料は、例えば、ホウケイ酸ガラス（ホウケイ酸ナトリウムガラス等）、アルミノケイ酸ガラス、それらを複合化させたガラス等の無機ガラスであってよい。無機中空粒子の中空部には、例えば気体が内包されている。無機中空粒子は、例えば、常温常圧下（例えば、少なくとも大気圧下かつ３０℃）において気体を内包している。
中空粒子の合計含有量（大気圧下かつ３０℃における、第一の中空粒子、第二の中空粒子、及び無機中空粒子の合計含有量。以下同様。）は、シート１０の全質量を基準として、例えば、４質量％以上、８質量％以上、又は１０質量％以上であってよく、４０質量％以下、３５質量％以下、又は３０質量％以下であってよい。
中空粒子の合計含有量は、シート１０の全体積を基準として、例えば、５０体積％以上、６０体積％以上、又は７０体積％以上であってよく、９５体積％以下であってよい。
マトリックスポリマーは、断熱層１１に含まれる中空粒子等の他の材料を保持するための母体となる（連続相を形成する）ポリマー（バインダーポリマー）である。中空粒子は、マトリックスポリマーに保持されていてよく、マトリックスポリマー中に分散されていてよい。
マトリックスポリマーは、下記式（１）で表される化合物をモノマー単位として含んでいてよい。言い換えれば、マトリックスポリマーは、下記式（１）で表される化合物を含む重合性化合物の重合体であってよい。
式（１）中、Ｒ１１及びＲ１２はそれぞれ独立に水素原子又はメチル基を表し、Ｒ１３はポリオキシアルキレン鎖を有する２価の基を表す。
マトリックスポリマーが、上記式（１）で表される化合物をモノマー単位として含む場合、断熱層１１が低弾性で伸びに優れるため、シート１０の被着体への追従性を高めることができる。
一実施形態において、Ｒ１１及びＲ１２の一方が水素原子であり、かつ他方がメチル基であってよい。他の一実施形態において、Ｒ１１及びＲ１２の両方が水素原子であってよい。他の実施形態において、Ｒ１１及びＲ１２の両方がメチル基であってよい。
一実施形態において、ポリオキシアルキレン鎖は、下記式（２）で表される構造単位を含む。これにより、断熱層１１の強度を高めることができる。
この場合、Ｒ１３はポリオキシエチレン鎖を有する２価の基であってよく、式（１）で表される化合物は、好ましくは下記式（１－２）で表される化合物（ポリエチレングリコールジ（メタ）アクリレート）である。
式（１－２）中、Ｒ１１及びＲ１２は式（１）におけるＲ１１及びＲ１２とそれぞれ同義であり、ｍは２以上の整数である。
他の一実施形態において、ポリオキシアルキレン鎖は、下記式（３）で表される構造単位を含む。
この場合、Ｒ１３はポリオキシプロピレン鎖を有する２価の基であってよく、式（１）で表される化合物は、好ましくは下記式（１－３）で表される化合物（ポリプロピレングリコールジ（メタ）アクリレート）である。
式（１－３）中、Ｒ１１及びＲ１２は式（１）におけるＲ１１及びＲ１２とそれぞれ同義であり、ｎは２以上の整数である。
他の一実施形態において、ポリオキシアルキレン鎖は、好ましくは、上述した、式（２）で表される構造単位、及び式（３）で表される構造単位を含む共重合鎖である。共重合鎖は、交互共重合鎖、ブロック共重合鎖、又はランダム共重合鎖のいずれであってもよい。共重合鎖は、好ましくはランダム共重合鎖である。
上述した各実施形態において、ポリオキシアルキレン鎖は、式（２）で表される構造単位及び式（３）で表される構造単位以外に、オキシテトラメチレン基、オキシブチレン基、オキシペンチレン基等の、炭素数４～５のオキシアルキレン基を構造単位として有していてもよい。
Ｒ１３は、上述したポリオキシアルキレン鎖に加えて、その他の有機基を更に有する２価の基であってもよい。その他の有機基は、ポリオキシアルキレン鎖以外の鎖状の基であってよく、例えば、メチレン鎖（－ＣＨ２－を構造単位とする鎖）、ポリエステル鎖（－ＣＯＯ－を構造単位中に含む鎖）、ポリウレタン鎖（－ＯＣＯＮ－を構造単位中に含む鎖）等であってよい。
例えば、式（１）で表される化合物は、下記式（１－４）で表される化合物であってもよい。
式（１－４）中、Ｒ１１及びＲ１２は式（１）におけるＲ１１及びＲ１２とそれぞれ同義であり、Ｒ１４及びＲ１５は、それぞれ独立に炭素数２～５のアルキレン基であり、ｋ１、ｋ２及びｋ３はそれぞれ独立に２以上の整数である。ｋ２は、例えば１６以下の整数であってよい。
複数存在するＲ１４及びＲ１５は、それぞれ、互いに同一であってよく、互いに異なっていてもよい。複数存在するＲ１４及びＲ１５は、それぞれ、好ましくは、エチレン基及びプロピレン基を含む。すなわち、（Ｒ１４Ｏ）ｋ１で表されるポリオキシアルキレン鎖、及び（Ｒ１５Ｏ）ｋ３で表されるポリオキシアルキレン鎖は、それぞれ、好ましくは、オキシエチレン基（上記式（２）で表される構造単位）、及びオキシプロピレン基（上記式（３）で表される構造単位）を含む共重合鎖である。
上述した各実施形態において、ポリオキシアルキレン鎖におけるオキシアルキレン基の数は、好ましくは１００以上である。ポリオキシアルキレン鎖におけるオキシアルキレン基の数が１００以上であると、式（１）で表される化合物の主鎖が長くなることにより、断熱層１１の伸びが更に優れ、断熱層１１の強度も高めることができる。オキシアルキレン基の数は、式（１－２）におけるｍ、式（１－３）におけるｎ、並びに式（１－４）におけるｋ１及びｋ３のそれぞれに相当する。
ポリオキシアルキレン鎖におけるオキシアルキレン基の数は、より好ましくは、１３０以上、１８０以上、２００以上、２２０以上、２５０以上、２７０以上、３００以上、又は３２０以上である。ポリオキシアルキレン鎖におけるオキシアルキレン基の数は、６００以下、５７０以下、又は５３０以下であってよい。
式（１）で表される化合物の重量平均分子量は、断熱層１１が低弾性で伸びに優れる観点から、好ましくは、５０００以上、６０００以上、７０００以上、８０００以上、９０００以上、１００００以上、１１０００以上、１２０００以上、１３０００以上、１４０００以上、又は１５０００以上である。式（１）で表される化合物の重量平均分子量は、好ましくは、１０００００以下、８００００以下、６００００以下、３４０００以下、３１０００以下、又は２８０００以下である。
マトリックスポリマーは、モノマー単位として式（１）で表される化合物のみを含有してよい。マトリックスポリマーは、式（１）で表される化合物以外の他の重合性化合物（詳細は後述する）をモノマー単位として更に含有してもよい。この場合、式（１）で表される化合物の含有量は、断熱層１１がより低弾性で伸びに優れる観点から、式（１）で表される化合物及び他の重合性化合物の合計（以下、「モノマー単位の含有量の合計」という）１００質量部に対して、好ましくは、２０質量部以上、３０質量部以上、又は４０質量部以上である。式（１）で表される化合物の含有量は、モノマー単位の含有量の合計１００質量部に対して、８０質量部以下、７０質量部以下、又は６０質量部以下であってよい。
マトリックスポリマーにおける他の重合性化合物（モノマー単位）は、例えば、（メタ）アクリロイル基を一つ有する化合物であってよい。当該化合物の例としては、上述した、アクリル共重合体がモノマー単位として含み得る、（メタ）アクリロイル基を有する化合物が挙げられる。また、マトリックスポリマーにおける他の重合性化合物は、一つの（メタ）アクリロイル基に加えて、芳香族炭化水素基、ポリオキシアルキレン鎖を含む基、アルコキシ基、フェノキシ基、シラン基を含む基、シロキサン結合を含む基、ハロゲン原子、アミノ基、又はエポキシ基を有する化合物であってもよい。特に、マトリックスポリマーが、（メタ）アクリロイル基に加えて、ヒドロキシル基、カルボキシル基、アミノ基、又はエポキシ基を有する化合物を含有することにより、断熱層１１の他の部材に対する密着性を更に向上できる。
（メタ）アクリロイル基及び芳香族炭化水素基を有する化合物としては、ベンジル（メタ）アクリレート等が挙げられる。
（メタ）アクリロイル基、及びポリオキシアルキレン鎖を含む基を有する化合物としては、ポリエチレングリコール（メタ）アクリレート、メトキシポリエチレングリコール（メタ）アクリレート、ポリプロピレングリコール（メタ）アクリレート、メトキシポリプロピレングリコール（メタ）アクリレート、ポリブチレングリコール（メタ）アクリレート、メトキシポリブチレングリコール（メタ）アクリレート等が挙げられる。
（メタ）アクリロイル基及びアルコキシ基を有する化合物としては、２－メトキシエチルアクリレート等が挙げられる。
（メタ）アクリロイル基及びフェノキシ基を有する化合物としては、フェノキシエチル（メタ）アクリレート等が挙げられる。
（メタ）アクリロイル基、及びシラン基を含む基を有する化合物としては、３－アクリロキシプロピルトリエトキシシラン、１０－メタクリロイルオキシデシルトリメトキシシラン、１０－アクリロイルオキシデシルトリメトキシシラン、１０－メタクリロイルオキシデシルトリエトキシシラン、１０－アクリロイルオキシデシルトリエトキシシラン等が挙げられる。
（メタ）アクリロイル基、及びシロキサン結合を含む基を有する化合物としては、シリコーン（メタ）アクリレート等が挙げられる。
（メタ）アクリロイル基及びハロゲン原子を有する化合物としては、トリフルオロメチル（メタ）アクリレート、２，２，２－トリフルオロエチル（メタ）アクリレート、１，１，１，３，３，３－ヘキサフルオロ－２－プロピル（メタ）アクリレート、パーフルオロエチルメチル（メタ）アクリレート、パーフルオロプロピルメチル（メタ）アクリレート、パーフルオロブチルメチル（メタ）アクリレート、パーフルオロペンチルメチル（メタ）アクリレート、パーフルオロヘキシルメチル（メタ）アクリレート、パーフルオロヘプチルメチル（メタ）アクリレート、パーフルオロオクチルメチル（メタ）アクリレート、パーフルオロノニルメチル（メタ）アクリレート、パーフルオロデシルメチル（メタ）アクリレート、パーフルオロウンデシルメチル（メタ）アクリレート、パーフルオロドデシルメチル（メタ）アクリレート、パーフルオロトリデシルメチル（メタ）アクリレート、パーフルオロテトラデシルメチル（メタ）アクリレート、２－（トリフルオロメチル）エチル（メタ）アクリレート、２－（パーフルオロエチル）エチル（メタ）アクリレート、２－（パーフルオロプロピル）エチル（メタ）アクリレート、２－（パーフルオロブチル）エチル（メタ）アクリレート、２－（パーフルオロペンチル）エチル（メタ）アクリレート、２－（パーフルオロヘキシル）エチル（メタ）アクリレート、２－（パーフルオロヘプチル）エチル（メタ）アクリレート、２－（パーフルオロオクチル）エチル（メタ）アクリレート、２－（パーフルオロノニル）エチル（メタ）アクリレート、２－（パーフルオロトリデシル）エチル（メタ）アクリレート、２－（パーフルオロテトラデシル）エチル（メタ）アクリレート等のフッ素原子を有する（メタ）アクリレートなどが挙げられる。
（メタ）アクリロイル基及びアミノ基を有する化合物としては、例えば、Ｎ，Ｎ－ジメチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ－ジエチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ－ジメチルアミノプロピル（メタ）アクリレート、Ｎ，Ｎ－ジエチルアミノプロピル（メタ）アクリレート等が挙げられる。
（メタ）アクリロイル基及びエポキシ基を有する化合物としては、例えば、（メタ）アクリル酸グリシジル、α－エチル（メタ）アクリル酸グリシジル、α－ｎ－プロピル（メタ）アクリル酸グリシジル、α－ｎ－ブチル（メタ）アクリル酸グリシジル、（メタ）アクリル酸－３，４－エポキシブチル、（メタ）アクリル酸－４，５－エポキシペンチル、（メタ）アクリル酸－６，７－エポキシヘプチル、α－エチル（メタ）アクリル酸－６，７－エポキシヘプチル、（メタ）アクリル酸－３－メチル－３，４－エポキシブチル、（メタ）アクリル酸－４－メチル－４，５－エポキシペンチル、（メタ）アクリル酸－５－メチル－５，６－エポキシヘキシル、（メタ）アクリル酸－β－メチルグリシジル、α－エチル（メタ）アクリル酸－β－メチルグリシジル等が挙げられる。
マトリックスポリマーは、モノマー単位として、上記他の重合性化合物のうちの１種を含有してもよく、２種以上を含有してもよい。また、式（１）で表される化合物を更に含有してもよく、含有しなくてもよい。
マトリックスポリマーの含有量は、断熱層１１の全質量を基準として、例えば、４０質量％以上、５０質量％以上、６０質量％以上、又は７０質量％以上であってよく、９５質量％以下、又は９０質量％以下であってよい。
断熱層１１は、必要に応じて、その他の添加剤を更に含有することができる。その他の添加剤としては、例えば、可塑剤、酸化防止剤（例えばフェノール系酸化防止剤）、表面調整剤（例えばシランカップリング剤）、分散剤、硬化促進剤、着色剤、結晶核剤、熱安定剤、発泡剤、難燃剤、制振剤、脱水剤、難燃助剤（例えば金属酸化物）等が挙げられる。その他の添加剤の含有量は、断熱層１１の全質量を基準として、０．１質量％以上であってよく、３０質量％以下であってよい。
断熱層１１の厚みは、例えば、１００μｍ以上、２００μｍ以上、又は５００μｍ以上であってよく、１０ｍｍ以下、５ｍｍ以下、又は２ｍｍ以下であってよい。
シート１０は、図１に示す一実施形態のように、断熱層１１及び粘着層１２のみからなっていてよい。他の一実施形態において、シートは、断熱層及び粘着層以外の他の層を更に備えていてもよい。この場合、シートにおいて、断熱層と粘着層とは互いに接していてよく（他の層を介さず積層されていてよく）、断熱層と粘着層とは他の層を介して積層されていてもよい。他の層の例としては、表面保護層、接着層、及び支持層が挙げられる。
他の層を備えるシートは、一実施形態において、表面保護層（第一の表面保護層）と、断熱層と、接着層（第一の接着層）と、支持層（第一の支持層）と、接着層（第二の接着層）と、支持層（第二の支持層）と、粘着層と、表面保護層（第二の表面保護層）と、を備えるシートであってよい。表面保護層は、例えば、断熱層又は粘着層と接する面が易剥離処理された樹脂フィルム（ＰＥＴフィルム等）で構成されていてよい。接着層は、例えば、アクリル系接着剤、エポキシ系接着剤等を含有していてよい。支持層は、例えば、樹脂フィルム（ポリイミドフィルム等）で構成されていてよい。
シート１０の厚みは、例えば、１００μｍ以上、２００μｍ以上、又は５００μｍ以上であってよく、１１ｍｍ以下、５ｍｍ以下、３ｍｍ以下、又は２ｍｍ以下であってよい。
シート１０は、例えば、断熱層１１及び粘着層１２をそれぞれ作製し、断熱層１１と粘着層１２とを、貼り合わせることにより作製することができる。例えば、上記の他の層を備えるシートの製造方法は、表面保護層（第一の表面保護層）及び断熱層の積層体Ａと、接着層（第一の接着層）、支持層（第一の支持層）、及び接着層（第二の接着層）の積層体Ｂと、支持層（第二の支持層）、粘着層、及び表面保護層（第二の表面保護層）の積層体Ｃとをそれぞれ準備する工程と、積層体Ａの断熱層と積層体Ｂの接着層（第一の接着層）とを貼り合わせると共に、積層体Ｂの接着層（第二の接着層）と積層体Ｃの支持層（第二の支持層）とを貼り合わせる工程とを備えていてよい。
積層体Ａは、例えば、上述した第一の中空粒子、第二の中空粒子及び重合性化合物を含む混合物を準備した後、表面保護層（第一の表面保護層）上で当該混合物中の重合性化合物を重合させてマトリックスポリマーを形成することにより得られる。積層体Ｂとしては、例えば、支持層（第一の支持層）と、支持層の両面それぞれに設けられた接着層（第一の接着層）及び接着層（第二の接着層）とを備える両面接着テープを用いることができる。積層体Ｃは、例えば、アクリル系粘着剤等の材料を混合して得た粘着剤組成物を、表面保護層（第二の表面保護層）上に塗工し、粘着剤組成物の乾燥及び／又は粘着剤組成物中の硬化性成分の硬化を進行させて粘着層を形成した後、粘着層の表面保護層（第二の表面保護層）と反対側の面に支持層（第二の支持層）を設けることにより得られる。積層体Ａ、積層体Ｂ、及び積層体Ｃを貼り合わせる工程では、例えば、ロールラミネーターを用いることができる。
以下、実施例に基づいて本発明を更に具体的に説明するが、本発明はこれらの実施例に何ら限定されるものではない。
＜粘着層＞
［粘着層の作製］
粘着層を作製するために、以下の各成分を用いた。
（アクリル共重合体）
Ａ－１：ブチルアクリレート（ＢＡ）、エチルアクリレート（ＥＡ）、アクリロニトリル（ＡＮ）、２－ヒドロキシエチルメタクリレート（ＨＥＭＡ）、及びアクリル酸（ＡＡ）の共重合体（モノマー比：ＢＡ／ＥＡ／ＡＮ／ＨＥＭＡ／ＡＡ＝６１／１９／１５／２．５／２．５、カルボキシル基の濃度：２．７７×１０―４ｍｏｌ／Ｌ、水酸基の濃度：２．０５×１０―４ｍｏｌ／Ｌ、Ｔｇ：－２８℃。）
Ａ－２：ＢＡ及びＮ－アクリロイルモルホリン（ＡＣＭＯ）の共重合体（モノマー単位の含有比率（質量比）：ＢＡ／ＡＣＭＯ＝９９．９／０．１、多分散度：Ｍｗ／Ｍｎ＝１．７、酸価：２３．３ｍｇＫＯＨ／ｇ。）
Ａ－３：ＢＡ、ＡＮ及びＡＡの共重合体（モノマー単位の含有比率（質量比）：ＢＡ／ＡＮ／ＡＡ＝８５／７．５／７．５、Ｍｗ＝６７万～９５万、多分散度：Ｍｗ／Ｍｎ＝３．８～６．５、カルボキシル基の濃度：１０．４１×１０―４ｍｏｌ／Ｌ、Ｔｇ：－４４℃。）
（架橋剤）
Ｂ－１：下記式（Ｂ－１）で表される架橋剤
Ｂ－２：下記式（Ｂ－２）で表される架橋剤（三菱ガス化学（株）製「テトラッドＸ」）
ｂ－１：３個のイソシアネート基を有する（エポキシ基を有さない）架橋剤（東ソー（株）製「コロネートＬ３８ＥＴ」）
（酸化防止剤）
Ｃ：４，４－ビス（α，α－ジメチルベンジル）ジフェニルアミン（精工化学（株）製「ノンフレックスＤＣＤ」）
［粘着層の作製］
粘着層を作製するために、以下の各成分を用いた。
（アクリル共重合体）
Ａ－１：ブチルアクリレート（ＢＡ）、エチルアクリレート（ＥＡ）、アクリロニトリル（ＡＮ）、２－ヒドロキシエチルメタクリレート（ＨＥＭＡ）、及びアクリル酸（ＡＡ）の共重合体（モノマー比：ＢＡ／ＥＡ／ＡＮ／ＨＥＭＡ／ＡＡ＝６１／１９／１５／２．５／２．５、カルボキシル基の濃度：２．７７×１０―４ｍｏｌ／Ｌ、水酸基の濃度：２．０５×１０―４ｍｏｌ／Ｌ、Ｔｇ：－２８℃。）
Ａ－２：ＢＡ及びＮ－アクリロイルモルホリン（ＡＣＭＯ）の共重合体（モノマー単位の含有比率（質量比）：ＢＡ／ＡＣＭＯ＝９９．９／０．１、多分散度：Ｍｗ／Ｍｎ＝１．７、酸価：２３．３ｍｇＫＯＨ／ｇ。）
Ａ－３：ＢＡ、ＡＮ及びＡＡの共重合体（モノマー単位の含有比率（質量比）：ＢＡ／ＡＮ／ＡＡ＝８５／７．５／７．５、Ｍｗ＝６７万～９５万、多分散度：Ｍｗ／Ｍｎ＝３．８～６．５、カルボキシル基の濃度：１０．４１×１０―４ｍｏｌ／Ｌ、Ｔｇ：－４４℃。）
（架橋剤）
Ｂ－１：下記式（Ｂ－１）で表される架橋剤
（酸化防止剤）
Ｃ：４，４－ビス（α，α－ジメチルベンジル）ジフェニルアミン（精工化学（株）製「ノンフレックスＤＣＤ」）
表１に示す量の各成分と、下記の溶媒とを混合し、自公転ミキサーにて回転数１０００ｒｐｍで５分間撹拌した後、常温で気泡がなくなるまで放置することにより粘着剤組成物を得た。各例で用いた溶媒の種類及び量は下記のとおりである。なお、下記の溶媒の量は、表１に示す各成分の合計１００質量部に対する量を意味する。
（比較例１）トルエン：メチルエチルケトン＝４：１の混合溶媒３７質量部
（実施例１）トルエン：メチルエチルケトン＝４：１の混合溶媒３７質量部
（実施例２）酢酸エチル１２１質量部
（実施例３）トルエン：メチルエチルケトン＝４：１の混合溶媒１１．５質量部
（比較例１）トルエン：メチルエチルケトン＝４：１の混合溶媒３７質量部
（実施例１）トルエン：メチルエチルケトン＝４：１の混合溶媒３７質量部
（実施例２）酢酸エチル１２１質量部
（実施例３）トルエン：メチルエチルケトン＝４：１の混合溶媒１１．５質量部
得られた粘着剤組成物を、片面にシリコーン系剥離剤による易剥離処理が施されている厚さ３８μｍのポリエステルフィルム（商品名：ピューレックスＡ３１、東洋紡(株)製）の易剥離処理面上に塗工した後、乾燥オーブンにより１００℃で２分間乾燥し、厚さ１０μｍの粘着層を形成した。次いで、室温（２５℃）にて、形成した粘着層の露出面上に、厚さ２５μｍのポリイミドフィルム基材（商品名：カプトン１００Ｈ、東レ・デュポン社製）をラミネートすることにより、表面保護層（ポリエステルフィルム）、各実施例及び比較例の粘着層、及び支持層（ポリイミドフィルム基材）がこの順に積層された積層体（積層体Ｃ）を作製した。また、積層体Ｃの表面保護層を剥離することにより、支持層付き粘着層を得た。
［粘着層のピール強度］
各粘着層の９０°ピール強度を、下記の手順で測定した。縦２５ｍｍ×横７０ｍｍのＳｉウエハと縦２０ｍｍ×横６０ｍｍにカットした支持層付き粘着層を準備した。粘着層とＳｉウエハとが接し、かつ両者の間に気泡が入らないように、Ｓｉウエハ上に支持層付き粘着層を設置した。支持層付き粘着層が設置されたＳｉウエハを縦３８０ｍｍ×横５００ｍｍ×厚み０．５ｍｍのステンレス板の上に乗せ、ロールラミネーター（大成ラミネーター（株）製「ＶＡ－７７０Ｈ特殊型ラミネーター」）により圧力６ｋｇｆ／ｃｍ２、回転速度０．２ｒｐｍ、温度４０℃の条件で粘着層とＳｉウエハとを貼り付けて、サンプルを作製した。得られたサンプルの支持層付き粘着層を幅５ｍｍでカットし、長さ方向の片側１０ｍｍをＳｉウエハから剥がし、引っ張り試験機（（株）島津製作所製「Ａｕｔｏｇｒａｐｈ ＥＺ－ＴＥＳＴ ＥＺ－Ｓ」）により、９０°ピール強度（初期９０°ピール強度）を測定した。また、作製したサンプルをリフロー炉(タムラ製作所製ＴＮＰ２５－３３７ＥＭシリーズ Ｎ２リフロー装置)に通して熱履歴を加え、放冷した後、同様に９０°ピール強度（加熱後９０°ピール強度）を測定した。熱履歴は、具体的には、リフロー炉において、昇温速度４７℃／分で室温（２５℃）から２００℃まで昇温した後、昇温速度３８℃／分で２００℃から２６０℃まで昇温することにより加えられた。また、放冷は、具体的には、リフロー炉内で６０℃まで冷却し、リフロー炉からとり出して２５℃まで冷却するというものであった。結果を表１に示す。
各粘着層の９０°ピール強度を、下記の手順で測定した。縦２５ｍｍ×横７０ｍｍのＳｉウエハと縦２０ｍｍ×横６０ｍｍにカットした支持層付き粘着層を準備した。粘着層とＳｉウエハとが接し、かつ両者の間に気泡が入らないように、Ｓｉウエハ上に支持層付き粘着層を設置した。支持層付き粘着層が設置されたＳｉウエハを縦３８０ｍｍ×横５００ｍｍ×厚み０．５ｍｍのステンレス板の上に乗せ、ロールラミネーター（大成ラミネーター（株）製「ＶＡ－７７０Ｈ特殊型ラミネーター」）により圧力６ｋｇｆ／ｃｍ２、回転速度０．２ｒｐｍ、温度４０℃の条件で粘着層とＳｉウエハとを貼り付けて、サンプルを作製した。得られたサンプルの支持層付き粘着層を幅５ｍｍでカットし、長さ方向の片側１０ｍｍをＳｉウエハから剥がし、引っ張り試験機（（株）島津製作所製「Ａｕｔｏｇｒａｐｈ ＥＺ－ＴＥＳＴ ＥＺ－Ｓ」）により、９０°ピール強度（初期９０°ピール強度）を測定した。また、作製したサンプルをリフロー炉(タムラ製作所製ＴＮＰ２５－３３７ＥＭシリーズ Ｎ２リフロー装置)に通して熱履歴を加え、放冷した後、同様に９０°ピール強度（加熱後９０°ピール強度）を測定した。熱履歴は、具体的には、リフロー炉において、昇温速度４７℃／分で室温（２５℃）から２００℃まで昇温した後、昇温速度３８℃／分で２００℃から２６０℃まで昇温することにより加えられた。また、放冷は、具体的には、リフロー炉内で６０℃まで冷却し、リフロー炉からとり出して２５℃まで冷却するというものであった。結果を表１に示す。
＜断熱層＞
［式（１－５）で表される化合物の合成］
撹拌機、温度計、窒素ガス導入管、排出管及び加熱ジャケットから構成された５００ｍＬフラスコを反応器とし、ポリオキシアルキレン鎖を有するグリコール（三洋化成（株）製「ニューポール７５Ｈ－９００００」）２２５ｇ、トルエン３００ｇを反応器に加え、４５℃、撹拌回転数２５０回／分で撹拌し、窒素を１００ｍＬ／分で流し、３０分撹拌した。その後、２５℃に降温し、降温完了後、塩化アクリロイル２．９ｇを反応器に滴下し、３０分撹拌した。その後、トリエチルアミン３．８ｇを滴下し、２時間撹拌した。その後、４５℃に昇温し、２時間反応させた。反応液を濾過し、濾液を脱溶し、式（１－５）で表される化合物（重量平均分子量：１５０００、式（１－５）中のｍ１＋ｍ２が概ね２５２±５、ｎ１＋ｎ２が概ね６３±５の整数（ただし、ｍ１、ｍ２、ｎ１及びｎ２はそれぞれ２以上の整数であり、ｍ１＋ｎ１≧１００、ｍ２＋ｎ２≧１００）である混合物、２５℃における粘度：５０Ｐａ・ｓ）を得た。
［式（１－５）中、－ｒ－はランダム共重合を表す符号である。］
［式（１－５）で表される化合物の合成］
撹拌機、温度計、窒素ガス導入管、排出管及び加熱ジャケットから構成された５００ｍＬフラスコを反応器とし、ポリオキシアルキレン鎖を有するグリコール（三洋化成（株）製「ニューポール７５Ｈ－９００００」）２２５ｇ、トルエン３００ｇを反応器に加え、４５℃、撹拌回転数２５０回／分で撹拌し、窒素を１００ｍＬ／分で流し、３０分撹拌した。その後、２５℃に降温し、降温完了後、塩化アクリロイル２．９ｇを反応器に滴下し、３０分撹拌した。その後、トリエチルアミン３．８ｇを滴下し、２時間撹拌した。その後、４５℃に昇温し、２時間反応させた。反応液を濾過し、濾液を脱溶し、式（１－５）で表される化合物（重量平均分子量：１５０００、式（１－５）中のｍ１＋ｍ２が概ね２５２±５、ｎ１＋ｎ２が概ね６３±５の整数（ただし、ｍ１、ｍ２、ｎ１及びｎ２はそれぞれ２以上の整数であり、ｍ１＋ｎ１≧１００、ｍ２＋ｎ２≧１００）である混合物、２５℃における粘度：５０Ｐａ・ｓ）を得た。
［断熱層の作製］
式（１－５）で表される化合物３９．２質量％、ジシクロペンタニルアクリレ－ト（昭和電工マテリアルズ（株）製「ファンクリル（登録商標） ＦＡ－５１３Ａ」）２３．５質量％、４－ヒドロキシブチルアクリレート（大阪有機化学工業（株）製）１５．７質量％、第一の中空粒子（松本油脂製薬（株）製「マツモトマイクロスフェアー（登録商標） ＦＮ－１９０ＳＳＤ」、平均粒子径：１０～１５μｍ、最大体積膨張倍率：５０倍以上、膨張開始温度：１９０℃、最大膨張温度：２１０～２２０℃）１１．０質量％、第二の中空粒子（日本フィライト（株）製「Ｅｘｐａｎｃｅｌ（登録商標） ９２０ＤＥ８０ｄ３０」、平均粒子径６０～９０μｍ、密度３０±３ｋｇ／ｍ３、最大体積膨張倍率：５倍未満）５．８質量％、重合開始剤（パーブチルオキサイド、日油（株）製「パーブチル（登録商標）Ｏ」）０．９質量％、フェノール系酸化防止剤（ＢＡＳＦジャパン（株）製「Ｉｒｇａｎｏｘ１０１０」）３．１質量％、及び表面調整剤（ＢＹＫ（株）製「ＢＹＫ（登録商標）３５０」）０．８質量％を混合し、断熱層作製用組成物を得た。なお、該断熱層作製用組成物全量を基準として、第一の中空粒子の配合量は３．８体積％であり、第二の中空粒子の配合量は６７．３体積％であった。
式（１－５）で表される化合物３９．２質量％、ジシクロペンタニルアクリレ－ト（昭和電工マテリアルズ（株）製「ファンクリル（登録商標） ＦＡ－５１３Ａ」）２３．５質量％、４－ヒドロキシブチルアクリレート（大阪有機化学工業（株）製）１５．７質量％、第一の中空粒子（松本油脂製薬（株）製「マツモトマイクロスフェアー（登録商標） ＦＮ－１９０ＳＳＤ」、平均粒子径：１０～１５μｍ、最大体積膨張倍率：５０倍以上、膨張開始温度：１９０℃、最大膨張温度：２１０～２２０℃）１１．０質量％、第二の中空粒子（日本フィライト（株）製「Ｅｘｐａｎｃｅｌ（登録商標） ９２０ＤＥ８０ｄ３０」、平均粒子径６０～９０μｍ、密度３０±３ｋｇ／ｍ３、最大体積膨張倍率：５倍未満）５．８質量％、重合開始剤（パーブチルオキサイド、日油（株）製「パーブチル（登録商標）Ｏ」）０．９質量％、フェノール系酸化防止剤（ＢＡＳＦジャパン（株）製「Ｉｒｇａｎｏｘ１０１０」）３．１質量％、及び表面調整剤（ＢＹＫ（株）製「ＢＹＫ（登録商標）３５０」）０．８質量％を混合し、断熱層作製用組成物を得た。なお、該断熱層作製用組成物全量を基準として、第一の中空粒子の配合量は３．８体積％であり、第二の中空粒子の配合量は６７．３体積％であった。
縦２００ｍｍ×横２００ｍｍ×厚さ５ｍｍのガラス板の上に、縦２００ｍｍ×横２００ｍｍ×厚さ０．１ｍｍの離型処理されたポリエステルシート（東洋紡（株）製「Ａ３１」）の離型処理面を上向きにのせた成形板を２組準備した。一方の成形板の離型処理面上に、１２０ｍｍ×１２０ｍｍ×２．０ｍｍの穴が形成されているシリコーンゴム製型枠（２００ｍｍ×２００ｍｍ）を設置し、当該型枠の内側に断熱層作製用組成物を充填した。さらに、他方の成形板の離型処理面を組成物側にして、上蓋をした後に、１３５℃の条件で４０分間加熱した。その後、一方の成形板と、シリコーンゴム製型枠と、他方の成形板におけるガラス板とを取り除き、表面保護層（ポリエステルシート）と断熱層（厚さ２．０ｍｍ）との積層体（積層体Ａ）を作製した。また、積層体Ａの表面保護層を剥離することにより、断熱層を得た。
［断熱層の熱伝導率］
作製した断熱層の熱伝導率を、下記の手順で測定した。断熱層を、８ｃｍ×１３ｃｍ×２．０ｍｍに切断し、レファレンスプレートと測定プローブで挟み込み、迅速熱伝導率計（京都電子工業（株）製「ＱＴＭ－７１０」、測定プローブＰＤ－１１Ｎ、薄膜測定モード）にて２５℃の条件で熱伝導率（初期熱伝導率）を測定した。また、断熱層を幅２０ｍｍ×長さ５０ｍｍに切断して断熱層の試験片を作製し、試験片に対し、上記［粘着層のピール強度］と同様に熱履歴を加え、放冷した後、上記と同様に熱伝導率（加熱後熱伝導率）を測定した。レファレンスは、離型処理されたポリエステルシート（東洋紡（株）製「Ａ３１」）を２枚重ねてレファレンスプレートと測定プローブで挟みこみ測定した。その結果、初期熱伝導率は６４ｍＷ／（ｍ・Ｋ）であり、加熱後熱伝導率は、６７ｍＷ／（ｍ・Ｋ）であった。
作製した断熱層の熱伝導率を、下記の手順で測定した。断熱層を、８ｃｍ×１３ｃｍ×２．０ｍｍに切断し、レファレンスプレートと測定プローブで挟み込み、迅速熱伝導率計（京都電子工業（株）製「ＱＴＭ－７１０」、測定プローブＰＤ－１１Ｎ、薄膜測定モード）にて２５℃の条件で熱伝導率（初期熱伝導率）を測定した。また、断熱層を幅２０ｍｍ×長さ５０ｍｍに切断して断熱層の試験片を作製し、試験片に対し、上記［粘着層のピール強度］と同様に熱履歴を加え、放冷した後、上記と同様に熱伝導率（加熱後熱伝導率）を測定した。レファレンスは、離型処理されたポリエステルシート（東洋紡（株）製「Ａ３１」）を２枚重ねてレファレンスプレートと測定プローブで挟みこみ測定した。その結果、初期熱伝導率は６４ｍＷ／（ｍ・Ｋ）であり、加熱後熱伝導率は、６７ｍＷ／（ｍ・Ｋ）であった。
＜シート＞
［シートの作製］
ロールラミネーター（（株）ラミーコーポレーション製 ホットドック ＬＭＰ－３５０ＥＸ）を用いて、各粘着層を備える積層体Ｃの支持層側に接着テープ（支持層と、該支持層の両面に設けられた接着層とを備えるテープ。昭和電工マテリアルズ（株）製、ハイボン１１－６５２。）をラミネートした。さらに、上記ロールラミネーターを用いて、当該テープ上に、積層体Ａをテープと断熱層とが接するようにラミネートして、比較例１及び実施例１～３に係るシートを得た。シートの厚みは、２１３５μｍであった。
［シートの作製］
ロールラミネーター（（株）ラミーコーポレーション製 ホットドック ＬＭＰ－３５０ＥＸ）を用いて、各粘着層を備える積層体Ｃの支持層側に接着テープ（支持層と、該支持層の両面に設けられた接着層とを備えるテープ。昭和電工マテリアルズ（株）製、ハイボン１１－６５２。）をラミネートした。さらに、上記ロールラミネーターを用いて、当該テープ上に、積層体Ａをテープと断熱層とが接するようにラミネートして、比較例１及び実施例１～３に係るシートを得た。シートの厚みは、２１３５μｍであった。
１０…シート、１１…断熱層、１２…粘着層。
Claims (5)
- 断熱層と、粘着層と、を備え、
前記粘着層が、アクリル共重合体と、エポキシ基を有する架橋剤と、を含む、シート。 - 前記断熱層が、中空粒子と、マトリックスポリマーと、を含有する、請求項１に記載のシート。
- 前記マトリックスポリマーが、下記式（１）で表される化合物をモノマー単位として含む、請求項２に記載のシート。
- 前記中空粒子が、有機中空粒子を含む、請求項２又は３に記載のシート。
- 前記有機中空粒子が、熱膨張性の有機中空粒子である第一の中空粒子と、第一の中空粒子以外の有機中空粒子である第二の中空粒子と、を含む、請求項４に記載のシート。