WO2023048248A1 - 鋼材 - Google Patents

鋼材 Download PDF

Info

Publication number
WO2023048248A1
WO2023048248A1 PCT/JP2022/035434 JP2022035434W WO2023048248A1 WO 2023048248 A1 WO2023048248 A1 WO 2023048248A1 JP 2022035434 W JP2022035434 W JP 2022035434W WO 2023048248 A1 WO2023048248 A1 WO 2023048248A1
Authority
WO
WIPO (PCT)
Prior art keywords
content
less
particles
steel material
steel
Prior art date
Application number
PCT/JP2022/035434
Other languages
English (en)
French (fr)
Inventor
慶 宮西
利治 間曽
Original Assignee
日本製鉄株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本製鉄株式会社 filed Critical 日本製鉄株式会社
Priority to CN202280063814.2A priority Critical patent/CN117980518A/zh
Priority to KR1020247013110A priority patent/KR20240075857A/ko
Priority to JP2023549757A priority patent/JPWO2023048248A1/ja
Publication of WO2023048248A1 publication Critical patent/WO2023048248A1/ja

Abstract

被削性に優れ、熱間加工時の割れ及び高周波焼入れ時の溶融割れを抑制でき、機械構造用部品とした場合に優れた疲労強度を有する鋼材を提供する。本実施形態の鋼材は、質量％で、Ｃ：０．０５～０．３０％、Ｓｉ：０．０５～０．４５％、Ｍｎ：０．３０～２．００％、Ｐ：０．０３０％以下、Ｓ：０．０１０～０．０９５％、Ｃｒ：０．０１～２．００％、Ｂｉ：０．００５１～０．１５００％、Ｎ：０．００３０～０．０２５０％、を含有し、次の式（１）を満たす。鋼材中において、微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２であり、粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下である。　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ≦１．００　（１）

Description

鋼材
　本発明は、鋼材に関し、さらに詳しくは、機械構造用部品の素材となる鋼材に関する。
　機械構造用部品は、自動車及び建設車両の足回り部品及び車軸等に利用される。機械構造用部品には、高い疲労強度が要求される。
　機械構造用部品の製造工程では、機械構造用部品の素材となる鋼材に対して、切削加工が実施される場合がある。そのため、機械構造用部品の素材となる鋼材では、高い被削性が求められる。
　機械構造用部品の素材となる鋼材は、例えば、特開昭５７－１９３６６号公報（特許文献１）、特開２００４－１８８７９号公報（特許文献２）及び特開２００８－１６９４１１号公報（特許文献３）に開示されている。
　特許文献１に開示された鋼材は、Ｃａを０．００１～０．０５％、Ｐｂ及びＢｉを単独又は複合して０．０２～０．１５％含有し、Ｓを０．００５％以下に規制し、介在物をＣａＳ－ＣａＯ、Ｐｂ、Ｂｉ系介在物とし、かつ、Ａｌ２Ｏ３介在物を０．００１％未満に抑える。この文献では、溶鋼中にＣａを多量に連続的に添加し、溶存しているＳをＣａＳに変化させる。また、Ｃａによる還元反応により、Ａｌ２Ｏ３をなくすか、又は、極めて少なくする。そのため、介在物はＣａＳ－ＣａＯ系の介在物となる。その後、溶鋼中にＰｂ、Ｂｉの１種又は２種を少量添加し、Ｐｂ又はＢｉの単独介在物を生成させる。これにより、鋼材の被削性が向上する、と特許文献１には記載されている。
　特許文献２に開示された鋼材は、質量％でＢ：０．００１～０．０１０％、Ｎ：０．００２～０．０１０％及びＢｉ：０．００５～０．１０％を含有する。この冷間鍛造用鋼では、横断面０．５ｍｍ×０．５ｍｍの視野面積当たりに、直径０．７μｍ以上のＢＮと、Ｂを含有するＢｉ析出物とが総計で１５個以上存在する。この鋼材では、ＢＮとしてＮを固定することにより、固溶Ｎ量を低減し、加工硬化を低減する。さらに、Ｂを含有するＢｉ析出物を生成して、切り屑処理性を高める、と特許文献２には記載されている。
　特許文献３に開示された鋼材は、質量％で、Ｃ：０．１５～０．５５％、Ｓｉ：０．０１～２．０％、Ｍｎ：０．０１～２．５％、Ｃｕ：０．０１～２．０％、Ｎｉ：０．０１～２．０％、Ｃｒ：０．０１～２．５％、Ｍｏ：０．０１～３．０％、及び、Ｖ及びＷからなる群から選ばれる少なくとも１種の総量：０．０１～１．０％を含有し、残部がＦｅ及び不可避的不純物からなる。この鋼材を、１０１０℃～１０５０℃で均熱し、その後、２００℃／分以上の冷却速度で５００℃～５５０℃まで冷却し、その後、１００℃／分以上の冷却速度で１５０℃以下まで冷却し、その後、５５０℃～７００℃の温度域で加熱する。これらの熱処理及び冷却処理が施された鋼材の、室温におけるＨＲＣ硬さの最大値を与えるＬＭＰが１７．６６以上である。この鋼材では、ＬＭＸが１７．６６以上であるため、軟化抵抗が高まり、熱疲労強度が高まる、と特許文献３では記載されている。
特開昭５７－１９３６６号公報 特開２００４－１８８７９号公報 特開２００８－１６９４１１号公報
　ところで、鋼材を素材とした機械構造用部品の製造工程の一例は、次のとおりである。素材となる鋼材を熱間加工して、機械構造用部品の粗形状を有する中間品を製造する。熱間加工は例えば、熱間鍛造である。製造された中間品に対して機械加工（切削加工）を実施して、中間品を所定の形状にする。切削加工後の中間品に対して、焼入れ焼戻しを実施する。以上の製造工程により、機械構造用部品が製造される。
　上述の製造工程中の焼入れでは、機械構造用部品の一部の部位の強度を高めるために、中間品（鋼材）に対して高周波焼入れを実施する場合がある。この場合、中間品（鋼材）のうち、強度を高めたい部位に対して、高周波誘導加熱を実施し、その後、急冷（焼入れ）する。
　しかしながら、高周波誘導加熱時において、中間品（鋼材）の形状に起因して、鋼材が局所的に過剰に加熱される場合がある。そして、鋼材の表層及び内部の一部が溶融して割れが発生する場合がある。このような割れを本明細書では、「溶融割れ」とも称する。機械構造用部品の製造工程において高周波焼入れを実施する場合、鋼材では溶融割れの抑制が求められる。
　さらに、鋼材の製造工程時、及び、その鋼材を用いた機械構造用部品の製造工程時には、熱間加工（例えば、熱間圧延、熱間鍛造等）が実施される。したがって、機械構造用部品の素材となる鋼材には、溶融割れの抑制だけでなく、熱間加工時の割れの抑制も求められる。ここで、熱間加工時の割れを、本明細書では、「熱間加工割れ」とも称する。したがって、機械構造用部品の素材となる鋼材には、優れた被削性が求められ、その鋼材を機械構造用部品とした場合に高い疲労強度が得られることが求められるだけでなく、熱間加工割れの抑制、及び、溶融割れの抑制も求められる。
　上述の特許文献１～特許文献３では、少なくとも、熱間加工割れの抑制及び溶融割れの抑制に関して、検討されていない。
　本発明の目的は、被削性に優れ、熱間加工時の割れを抑制でき、高周波焼入れ時の溶融割れを抑制でき、機械構造用部品とした場合に優れた疲労強度が得られる鋼材を提供することである。
　本開示の鋼材は、
　質量％で、
　Ｃ：０．０５～０．３０％、
　Ｓｉ：０．０５～０．４５％、
　Ｍｎ：０．３０～２．００％、
　Ｐ：０．０３０％以下、
　Ｓ：０．０１０～０．０９５％、
　Ｃｒ：０．０１～２．００％、
　Ｂｉ：０．００５１～０．１５００％、及び、
　Ｎ：０．００３０～０．０２５０％、を含有し、
　残部はＦｅ及び不純物からなり、式（１）を満たし、
　前記鋼材中において、
　円相当径が０．１～１．０μｍの微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２であり、
　円相当径が１０．０μｍ以上の粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下である。
　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ≦１．００　（１）
　ここで、式中の各元素記号には、対応する元素の含有量が質量％で代入される。元素が含有されていない場合、対応する元素記号には「０」が代入される。
　本開示の鋼材は、
　質量％で、
　Ｃ：０．０５～０．３０％、
　Ｓｉ：０．０５～０．４５％、
　Ｍｎ：０．３０～２．００％、
　Ｐ：０．０３０％以下、
　Ｓ：０．０１０～０．０９５％、
　Ｃｒ：０．０１～２．００％、
　Ｂｉ：０．００５１～０．１５００％、及び、
　Ｎ：０．００３０～０．０２５０％、を含有し、
　さらに、第１群～第５群からなる群から選択される１種以上を含有し、
　残部はＦｅ及び不純物からなり、さらに、式（１）を満たし、
　前記鋼材中において、
　円相当径が０．１～１．０μｍの微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２であり、
　円相当径が１０．０μｍ以上の粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下である。
　［第１群］
　Ａｌ：０．０６０％以下、及び、
　Ｍｇ：０．０１００％以下、からなる群から選択される１種以上
　［第２群］
　Ｔｉ：０．１５００％以下、
　Ｎｂ：０．０８００％以下、
　Ｗ：０．４０００％以下、及び
　Ｚｒ：０．２０００％以下、からなる群から選択される１種以上
　［第３群］
　Ｃａ：０．０１００％以下、
　Ｔｅ：０．０１００％以下、
　Ｂ：０．００５０％以下、
　Ｓｎ：０．０１００％以下、及び、
　希土類元素：０．０１００％以下、からなる群から選択される１種以上
　［第４群］
　Ｃｏ：０．０１００％以下、
　Ｓｅ：０．０１００％以下、
　Ｓｂ：０．０１００％以下、及び、
　Ｉｎ：０．０１００％以下、からなる群から選択される１種以上
　［第５群］
　Ｖ：０．２００％以下、
　Ｍｏ：１．００％以下、
　Ｃｕ：０．２０％以下、及び、
　Ｎｉ：０．２０％以下、からなる群から選択される１種以上
　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ≦１．００　（１）
　ここで、式中の各元素記号には、対応する元素の含有量が質量％で代入される。元素が含有されていない場合、対応する元素記号には「０」が代入される。
　本開示の鋼材は、被削性に優れ、熱間加工時の割れを抑制でき、高周波焼入れ時の溶融割れを抑制でき、機械構造用部品とした場合に優れた疲労強度が得られる。
図１は、本実施形態の鋼材の範囲外である鋼材を１００℃／秒の昇温速度で１３９０℃まで加熱して１５秒間保持し、その後、水冷した後のミクロ組織の模式図である。 図２は、本実施形態の鋼材を１００℃／秒の昇温速度で１３９０℃まで加熱して１５秒間保持し、その後、水冷した後のミクロ組織の模式図である。 図３は、実施例で用いた回転曲げ疲労試験片の側面図である。
　本発明者らは、初めに、被削性に優れ、機械構造用部品とした場合に優れた疲労強度が得られる鋼材の化学組成について検討を行った。その結果、本発明者らは、化学組成が、質量％で、Ｃ：０．０５～０．３０％、Ｓｉ：０．０５～０．４５％、Ｍｎ：０．３０～２．００％、Ｐ：０．０３０％以下、Ｓ：０．０１０～０．０９５％、Ｃｒ：０．０１～２．００％、Ｎ：０．００３０～０．０２５０％、Ａｌ：０～０．０６０％、Ｍｇ：０～０．０１００％、Ｔｉ：０～０．１５００％、Ｎｂ：０～０．０８００％、Ｗ：０～０．４０００％、Ｚｒ：０～０．２０００％、Ｃａ：０～０．０１００％、Ｔｅ：０～０．０１００％、Ｂ：０～０．００５０％、Ｓｎ：０～０．０１００％、希土類元素：０～０．０１００％、Ｃｏ：０～０．０１００％、Ｓｅ：０～０．０１００％、Ｓｂ：０～０．０１００％、Ｉｎ：０～０．０１００％、Ｖ：０～０．２００％、Ｍｏ：０～１．００％、Ｃｕ：０～０．２０％、及び、Ｎｉ：０～０．２０％、を含有し、残部はＦｅ及び不純物からなる鋼材であれば、優れた被削性が優れ、機械構造用部品とした場合に優れた疲労強度が得られる可能性があると考えた。
　しかしながら、鋼材を上述の化学組成としただけでは、優れた被削性が得られ、機械構造用部品とした場合に優れた疲労強度が得られるとは限らない。化学組成中の各元素含有量が上述の範囲内であっても、鋼材の硬さが高ければ、鋼材の被削性が低下してしまう。一方、化学組成中の各元素含有量が上述の範囲内であっても、鋼材の硬さが低ければ、その鋼材を素材として製造された機械構造用部品の疲労強度が低くなってしまう。したがって、機械構造用部品の疲労強度及び鋼材の被削性を両立するためには、機械構造用部品の素材である鋼材の硬さを適切な範囲とするのが有効である。
　そこで、本発明者らは、化学組成中の各元素含有量が上述の範囲内である鋼材の硬さに影響する元素の含有量について検討した。上述の化学組成中の元素のうち、Ｃ、Ｓｉ、Ｍｎ、Ｃｒ及びＶは特に、鋼材を素材として製造された機械構造用部品の内部硬さを高め、その結果、機械構造用部品の疲労強度を高める。一方、Ｓは内部硬さを低下させる。したがって、本発明者らは、これらの元素の含有量を適切な範囲とすることにより、鋼材の被削性の向上、及び、鋼材を素材として製造された機械構造用部品の疲労強度の向上を両立できると考えた。さらなる検討の結果、本発明者らは、化学組成中の各元素含有量が上述の範囲内である鋼材において、式（１）を満たせば、鋼材において、優れた被削性が得られ、さらに、機械構造用部品としたときに優れた疲労強度が得られることを見出した。
　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ≦１．００　（１）
　ここで、式中の各元素記号には、対応する元素の含有量が質量％で代入される。元素が含有されていない場合、対応する元素記号には「０」が代入される。
　次に、本発明者らは、化学組成中の各元素含有量が上述の範囲内であり、かつ、式（１）を満たす鋼材において、高周波焼入れ時の溶融割れを抑制できる手段を検討した。初めに、本発明者らは、高周波焼入れ時に、鋼材に溶融割れが発生する原因を特定するために、溶融割れが発生した部位のミクロ組織を観察した。その結果、溶融割れが発生した部位には、脱炭が生じていなかった。一方、脱炭している部位では、溶融割れが発生しなかった。
　この結果から、本発明者らは、高周波焼入れ時の鋼材に発生する溶融割れには、Ｃ含有量が影響すると考えた。具体的には、粒界に偏析するＣにより溶融割れが発生しやすくなる。そこで、本発明者らは、粒界にＣが偏析するのを抑制する手段について検討した。
　検討の結果、上述の化学組成にさらに、Ｆｅの一部に代えて、Ｂｉを０．００５１～０．１５００％含有することにより、高周波焼入れ時の鋼材の溶融割れが抑制できることを、本発明者らは見出した。その理由は、次のとおりと考えられる。Ｂｉを適量含有すれば、Ｂｉは鋼材中で介在物として存在する。以下、Ｂｉからなる介在物をＢｉ粒子という。Ｂｉ粒子は、ピンニング効果により、高周波焼入れ時の鋼材中のオーステナイト粒の粗大化を抑制する。Ｂｉ粒子が微細であれば、ピンニング効果が高まる。高周波焼入れ時において、オーステナイト粒が微細に維持されれば、オーステナイト粒の粒界面積が増大する。粒界面積が増大すれば、単位面積当たりのオーステナイト粒界に偏析するＣの濃度が減少する。その結果、溶融割れの発生が抑制される。
　以上のとおり、Ｂｉを適量含有することにより、高周波焼入れ時の溶融割れの発生は抑制される。しかしながら、鋼材に対して熱間加工を実施する場合に、割れが発生する場合があることが判明した。ここでいう熱間加工は例えば、鋼材の製造工程中で実施される熱間圧延、又は、機械構造用部品の製造工程中で実施される熱間鍛造等である。そこで、熱間加工時の割れの原因について調査した。その結果、本発明者らは、次の新たな知見を得た。
　溶融割れの抑制のために鋼材にＢｉを含有する場合、鋼材中に、円相当径が１．０μｍ以下の微細なＢｉ粒子（Ｂｉ介在物）とともに、円相当径が１０．０μｍ以上の粗大Ｂｉ粒子が生成する場合がある。粗大Ｂｉ粒子は、熱間加工時の割れの起点となりやすい。そのため、粗大Ｂｉ粒子の個数密度が高すぎれば、熱間加工時に割れ（熱間加工割れ）が発生しやすい。
　以上のとおり、Ｂｉを含有する鋼材では、高周波焼入れ時の溶融割れが抑制されやすいものの、粗大Ｂｉ粒子に起因した熱間加工割れが発生しやすい。鋼材中のＢｉ粒子が微細であれば、高周波焼入れ時の溶融割れが抑制される。一方、鋼材中のＢｉ粒子が粗大であれば、熱間加工割れが発生しやすくなる。
　以上の検討結果に基づいて、本発明者らは、鋼材中の微細Ｂｉ粒子の個数密度をある程度確保しつつ、鋼材中の粗大Ｂｉ粒子の個数密度をなるべく抑制することにより、高周波焼入れ時の溶融割れを抑制でき、かつ、熱間加工割れも抑制できると考えた。そこで、これらの効果を十分に発揮する微細Ｂｉ粒子の個数密度及び粗大Ｂｉ粒子の個数密度について、さらに調査及び検討を行った。その結果、上述の化学組成の鋼材において、上述の式（１）を満たすことを前提に、円相当径が０．１～１．０μｍの微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２であり、かつ、円相当径が１０．０μｍ以上の粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下であれば、高周波焼入れ時の溶融割れを抑制でき、かつ、熱間加工割れも抑制できることを、本発明者らは見出した。
　以上の知見に基づいて完成した本実施形態による鋼材は、次の構成を有する。
　［１］
　鋼材であって、
　質量％で、
　Ｃ：０．０５～０．３０％、
　Ｓｉ：０．０５～０．４５％、
　Ｍｎ：０．３０～２．００％、
　Ｐ：０．０３０％以下、
　Ｓ：０．０１０～０．０９５％、
　Ｃｒ：０．０１～２．００％、
　Ｂｉ：０．００５１～０．１５００％、及び、
　Ｎ：０．００３０～０．０２５０％、を含有し、
　残部はＦｅ及び不純物からなり、式（１）を満たし、
　前記鋼材中において、
　円相当径が０．１～１．０μｍの微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２であり、
　円相当径が１０．０μｍ以上の粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下である、
　鋼材。
　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ≦１．００　（１）
　ここで、式中の各元素記号には、対応する元素の含有量が質量％で代入される。元素が含有されていない場合、対応する元素記号には「０」が代入される。
　［２］
　鋼材であって、
　質量％で、
　Ｃ：０．０５～０．３０％、
　Ｓｉ：０．０５～０．４５％、
　Ｍｎ：０．３０～２．００％、
　Ｐ：０．０３０％以下、
　Ｓ：０．０１０～０．０９５％、
　Ｃｒ：０．０１～２．００％、
　Ｂｉ：０．００５１～０．１５００％、及び、
　Ｎ：０．００３０～０．０２５０％、を含有し、
　さらに、第１群～第５群からなる群から選択される１種以上を含有し、
　残部はＦｅ及び不純物からなり、式（１）を満たし、
　前記鋼材中において、
　円相当径が０．１～１．０μｍの微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２であり、
　円相当径が１０．０μｍ以上の粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下である、
　鋼材。
　［第１群］
　Ａｌ：０．０６０％以下、及び、
　Ｍｇ：０．０１００％以下、からなる群から選択される１種以上
　［第２群］
　Ｔｉ：０．１５００％以下、
　Ｎｂ：０．０８００％以下、
　Ｗ：０．４０００％以下、及び、
　Ｚｒ：０．２０００％以下、からなる群から選択される１種以上
　［第３群］
　Ｃａ：０．０１００％以下、
　Ｔｅ：０．０１００％以下、
　Ｂ：０．００５０％以下、
　Ｓｎ：０．０１００％以下、及び、
　希土類元素：０．０１００％以下、からなる群から選択される１種以上
　［第４群］
　Ｃｏ：０．０１００％以下、
　Ｓｅ：０．０１００％以下、
　Ｓｂ：０．０１００％以下、及び、
　Ｉｎ：０．０１００％以下、からなる群から選択される１種以上
　［第５群］
　Ｖ：０．２００％以下、
　Ｍｏ：１．００％以下、
　Ｃｕ：０．２０％以下、及び、
　Ｎｉ：０．２０％以下、からなる群から選択される１種以上
　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ≦１．００　（１）
　ここで、式中の各元素記号には、対応する元素の含有量が質量％で代入される。元素が含有されていない場合、対応する元素記号には「０」が代入される。
　［３］
　［２］に記載の鋼材であって、
　前記第１群を含有する、
　鋼材。
　［４］
　［２］又は［３］に記載の鋼材であって、
　前記第２群を含有する、
　鋼材。
　［５］
　［２］～［４］のいずれか１項に記載の鋼材であって、
　前記第３群を含有する、
　鋼材。
　［６］
　［２］～［５］のいずれか１項に記載の鋼材であって、
　前記第４群を含有する、
　鋼材。
　［７］
　［２］～［６］のいずれか１項に記載の鋼材であって、
　前記第５群を含有する、
　鋼材。
　以下、本実施形態の鋼材について詳述する。元素に関する「％」は、特に断りがない限り、質量％を意味する。
　［本実施形態の鋼材の特徴］
　本実施形態の鋼材は、次の特徴１～特徴４を満たす。
　（特徴１）
　化学組成が、質量％で、Ｃ：０．０５～０．３０％、Ｓｉ：０．０５～０．４５％、Ｍｎ：０．３０～２．００％、Ｐ：０．０３０％以下、Ｓ：０．０１０～０．０９５％、Ｃｒ：０．０１～２．００％、Ｂｉ：０．００５１～０．１５００％、Ｎ：０．００３０～０．０２５０％、Ａｌ：０～０．０６０％、Ｍｇ：０～０．０１００％、Ｔｉ：０～０．１５００％、Ｎｂ：０～０．０８００％、Ｗ：０～０．４０００％、Ｚｒ：０～０．２０００％、Ｃａ：０～０．０１００％、Ｔｅ：０～０．０１００％、Ｂ：０～０．００５０％、Ｓｎ：０～０．０１００％、希土類元素：０～０．０１００％、Ｃｏ：０～０．０１００％、Ｓｅ：０～０．０１００％、Ｓｂ：０～０．０１００％、Ｉｎ：０～０．０１００％以下、Ｖ：０～０．２００％、Ｍｏ：０～１．００％、Ｃｕ：０～０．２０％、及び、Ｎｉ：０～０．２０％以下、を含有し、残部がＦｅ及び不純物からなる。
　（特徴２）
　各元素含有量が特徴１の範囲内であることを前提として、式（１）を満たす。
　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ≦１．００　（１）
　ここで、式中の各元素記号には、対応する元素の含有量が質量％で代入される。元素が含有されていない場合、対応する元素記号には「０」が代入される。
　（特徴３）
　鋼材中において、円相当径が０．１～１．０μｍの微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２である。
　（特徴４）
　鋼材中において、円相当径が１０．０μｍ以上の粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下である。
　以下、各特徴１～特徴４について説明する。
　［（特徴１）化学組成について］
　本実施形態の鋼材の化学組成は、次の元素を含有する。
　Ｃ：０．０５～０．３０％
　炭素（Ｃ）は、鋼材を素材として製造された機械構造用部品の硬さを高め、機械構造用部品の疲労強度を高める。Ｃ含有量が０．０５％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、Ｃ含有量が０．３０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、粒界にＣが偏析する。この場合、粒界でのＣ濃度が高くなる。Ｃ濃度が高まれば、融点が低下する。そのため、高周波焼入れ時に溶融割れが発生しやすくなる。
　したがって、Ｃ含有量は０．０５～０．３０％である。
　Ｃ含有量の好ましい下限は０．０８％であり、さらに好ましくは０．１０％であり、さらに好ましくは０．１３％である。
　Ｃ含有量の好ましい上限は０．２８％であり、さらに好ましくは０．２５％であり、さらに好ましくは０．２３％である。
　Ｓｉ：０．０５～０．４５％
　シリコン（Ｓｉ）は、製鋼工程において鋼を脱酸する。Ｓｉはさらに、機械構造用部品の硬さを高め、機械構造用部品の疲労強度を高める。Ｓｉ含有量が０．０５％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、ＳｉはＣとの親和力が弱い。そのため、Ｓｉ含有量が０．４５％を超えれば、他の元素含有量が本実施形態の範囲内であっても、高周波誘導加熱時において、Ｃは、Ｓｉが固溶している粒内よりも、粒界に偏析しやすくなる。その結果、高周波焼入れ時に溶融割れが発生しやすくなる。
　したがって、Ｓｉ含有量は０．０５～０．４５％である。
　Ｓｉ含有量の好ましい下限は０．０７％であり、さらに好ましくは０．１０％であり、さらに好ましくは０．１３％である。
　Ｓｉ含有量の好ましい上限は０．４３％であり、さらに好ましくは０．４０％であり、さらに好ましくは０．３８％である。
　Ｍｎ：０．３０～２．００％
　マンガン（Ｍｎ）は、製鋼工程において鋼を脱酸する。Ｍｎはさらに、Ｃとの親和力が強い。そのため、加熱時において、ＣはＭｎが固溶している粒内に留まる。そのため、Ｃの粒界への偏析が抑制され、高周波焼入れ時の溶融割れの発生が抑制される。Ｍｎ含有量が０．３０％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、Ｍｎ含有量が２．００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の硬さが過剰に高まる。その結果、鋼材の被削性が低下する。
　したがって、Ｍｎ含有量は０．３０～２．００％である。
　Ｍｎ含有量の好ましい下限は０．３５％であり、さらに好ましくは０．４０％であり、さらに好ましくは０．５０％であり、さらに好ましくは０．６０％である。
　Ｍｎ含有量の好ましい上限は１．９０％であり、さらに好ましくは１．７０％であり、さらに好ましくは１．５０％であり、さらに好ましくは１．４０％である。
　Ｐ：０．０３０％以下
　燐（Ｐ）は不純物である。Ｐは粒界に偏析する。そのため、Ｐは鋼材の融点を低下させる。そのため、高周波焼入れ時に溶融割れが発生しやすくなる。
　したがって、Ｐ含有量は０．０３０％以下である。
　Ｐ含有量はなるべく低い方が好ましい。しかしながら、Ｐ含有量の過剰な低減は製造コストを高める。したがって、通常の工業生産を考慮すれば、Ｐ含有量の好ましい下限は０％超であり、さらに好ましくは０．００１％であり、さらに好ましくは０．００２％である。
　Ｐ含有量の好ましい上限は０．０２８％であり、さらに好ましくは０．０２６％であり、さらに好ましくは０．０２３％であり、さらに好ましくは０．０２０％である。
　Ｓ：０．０１０～０．０９５％
　硫黄（Ｓ）は硫化物系介在物を形成し、鋼材の被削性を高める。Ｓ含有量が０．０１０％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、Ｓは鋼材の融点を低下させる。そのため、Ｓ含有量が０．０９５％を超えれば、他の元素含有量が本実施形態の範囲内であっても、高周波焼入れ時に溶融割れが発生しやすくなる。
　したがって、Ｓ含有量は０．０１０～０．０９５％である。
　Ｓ含有量の好ましい下限は０．０１２％であり、さらに好ましくは０．０１５％であり、さらに好ましくは０．０１８％であり、さらに好ましくは０．０２０％である。
　Ｓ含有量の好ましい上限は０．０８０％であり、さらに好ましくは０．０７０％であり、さらに好ましくは０．０６０％である。
　Ｃｒ：０．０１～２．００％
　クロム（Ｃｒ）は、鋼材の焼入れ性を高める。そのため、機械構造用部品の内部硬さが高まる。その結果、機械構造用部品の疲労強度が高まる。Ｃｒはさらに、Ｃとの親和力が強い。そのため、加熱時において、ＣはＣｒが固溶している粒内に留まる。そのため、Ｃの粒界への偏析が抑制され、高周波焼入れ時の溶融割れの発生が抑制される。Ｃｒはさらに、Ｓと結合してＣｒ硫化物を形成する。この場合、粗大なＦｅＳの形成が抑制される。その結果、熱間加工時の鋼材の延性が向上し、熱間加工割れが抑制される。Ｃｒ含有量が０．０１％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、Ｃｒ含有量が２．００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の硬さが過剰に高まる。その結果、鋼材の被削性が低下する。
　したがって、Ｃｒ含有量は０．０１～２．００％である。
　Ｃｒ含有量の好ましい下限は０．０２％であり、さらに好ましくは０．０４％であり、さらに好ましくは０．０６％であり、さらに好ましくは０．０８％であり、さらに好ましくは０．１０％である。
　Ｃｒ含有量の好ましい上限は１．９０％であり、さらに好ましくは１．７０％であり、さらに好ましくは１．５０％であり、さらに好ましくは１．２０％である。
　Ｂｉ：０．００５１～０．１５００％
　ビスマス（Ｂｉ）は、鋼材中で介在物（Ｂｉ粒子）を形成する。そのため、高周波焼入れ時の溶融割れが抑制される。Ｂｉはさらに、鋼材の被削性を高める。Ｂｉ含有量が０．００５１％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、Ｂｉ含有量が０．１５００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、粗大なＢｉ粒子が生成する。粗大なＢｉ粒子は、鋼材の製造工程中の熱間加工時、又は、鋼材を素材として製造された機械構造用部品の製造工程中の熱間加工時において、割れの起点となりやすい。そのため、熱間加工割れが発生しやすくなる。
　したがって、Ｂｉ含有量は０．００５１～０．１５００％である。
　Ｂｉ含有量の好ましい下限は０．００８０％であり、さらに好ましくは０．０１００％であり、さらに好ましくは０．０１２０％であり、さらに好ましくは０．０１４０％であり、さらに好ましくは０．０１６０％である。
　Ｂｉ含有量の好ましい上限は０．１４００％であり、さらに好ましくは０．１３５０％であり、さらに好ましくは０．１３００％である。
　Ｎ：０．００３０～０．０２５０％
　窒素（Ｎ）は、機械構造用部品の製造工程中の熱間加工後の冷却過程で、窒化物及び／又は炭窒化物を形成して鋼材を析出強化する。その結果、機械構造用部品の疲労強度が高まる。Ｎ含有量が０．００３０％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、Ｎ含有量が０．０２５０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の熱間加工性が低下する。
　したがって、Ｎ含有量は０．００３０～０．０２５０％である。
　Ｎ含有量の好ましい下限は０．００３５％であり、さらに好ましくは０．００４０％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．００８０％である。
　Ｎ含有量の好ましい上限は０．０２４０％であり、さらに好ましくは０．０２３０％であり、さらに好ましくは０．０２００％であり、さらに好ましくは０．０１８０％であり、さらに好ましくは０．０１５０％である。
　本実施の形態による鋼材の化学組成の残部は、Ｆｅ及び不純物からなる。ここで、不純物とは、鋼材を工業的に製造する際に、原料としての鉱石、スクラップ、又は、製造環境などから混入されるものであって、意図的に含有されるものではなく、本実施形態による鋼材に悪影響を与えない範囲で許容されるものを意味する。
　不純物としては、上述の不純物（Ｐ、Ｓ）以外のあらゆる元素が挙げられる。不純物は１種だけであってもよいし、２種以上であってもよい。上述した不純物以外の他の不純物は、例えば、次のとおりである。Ｏ：０．００５０％以下、Ｔａ及びＺｎ：合計で０～０．０１％、Ｐｂ：０～０．０９％。
　［任意元素（Ｏｐｔｉｏｎａｌ　Ｅｌｅｍｅｎｔｓ）について］
　本実施形態の化学組成はさらに、Ｆｅの一部に代えて、第１群～第５群からなる群から選択される１種以上を含有してもよい。
　［第１群］
　Ａｌ：０．０６０％以下、及び、
　Ｍｇ：０．０１００％以下、からなる群から選択される１種以上
　［第２群］
　Ｔｉ：０．１５００％以下、
　Ｎｂ：０．０８００％以下、
　Ｗ：０．４０００％以下、及び、
　Ｚｒ：０．２０００％以下、からなる群から選択される１種以上
　［第３群］
　Ｃａ：０．０１００％以下、
　Ｔｅ：０．０１００％以下、
　Ｂ：０．００５０％以下、
　Ｓｎ：０．０１００％以下、及び、
　希土類元素：０．０１００％以下、からなる群から選択される１種以上
　［第４群］
　Ｃｏ：０．０１００％以下、
　Ｓｅ：０．０１００％以下、
　Ｓｂ：０．０１００％以下、及び、
　Ｉｎ：０．０１００％以下、からなる群から選択される１種以上
　［第５群］
　Ｖ：０．２００％以下、
　Ｍｏ：１．００％以下、
　Ｃｕ：０．２０％以下、及び、
　Ｎｉ：０．２０％以下、からなる群から選択される１種以上
　以下、各任意元素について説明する。
　［第１群：Ａｌ及びＭｇ］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、上述の第１群を含有してもよい。これらの元素は任意元素であり、いずれも、鋼を脱酸する。以下、第１群の各元素について説明する。
　Ａｌ：０．０６０％以下
　アルミニウム（Ａｌ）は任意元素であり、含有されなくてもよい。つまり、Ａｌ含有量は０％であってもよい。
　含有される場合、つまり、Ａｌ含有量が０％超である場合、Ａｌは鋼を脱酸する。Ａｌが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ａｌ含有量が０．０６０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、Ａｌは粗大な酸化物を形成する。粗大な酸化物は、機械構造用部品の疲労強度を低下する。
　したがって、Ａｌ含有量は０～０．０６０％である。含有される場合、Ａｌ含有量は０．０６０％以下である。
　Ａｌ含有量の好ましい下限は０．００１％であり、さらに好ましくは０．００２％であり、さらに好ましくは０．００３％であり、さらに好ましくは０．００５％であり、さらに好ましくは０．０１０％である。
　Ａｌ含有量の好ましい上限は０．０５５％であり、さらに好ましくは０．０５０％であり、さらに好ましくは０．０４５％である。
　Ｍｇ：０．０１００％以下
　マグネシウム（Ｍｇ）は任意元素であり、含有されなくてもよい。つまり、Ｍｇ含有量は０％であってもよい。
　含有される場合、つまり、Ｍｇ含有量が０％超である場合、Ｍｇは鋼を脱酸する。Ｍｇが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｍｇ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、Ｍｇは粗大な酸化物を形成する。粗大な酸化物は、機械構造用部品の疲労強度を低下する。
　したがって、Ｍｇ含有量は０～０．０１００％である。含有される場合、Ｍｇ含有量は０．０１００％以下である。
　Ｍｇ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００３％であり、さらに好ましくは０．０００５％である。
　Ｍｇ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００７０％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．００４０％である。
　［第２群：Ｔｉ、Ｎｂ、Ｗ及びＺｒ］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、上述の第２群を含有してもよい。これらの元素は任意元素であり、いずれも、析出物を形成して、機械構造用部品の靱性を高める。以下、第２群の各元素について説明する。
　Ｔｉ：０．１５００％以下
　チタン（Ｔｉ）は任意元素であり、含有されなくてもよい。つまり、Ｔｉ含有量は０％であってもよい。
　含有される場合、つまり、Ｔｉ含有量が０％超である場合、Ｔｉは、機械構造用部品の製造工程中の熱間加工工程の冷却過程において、炭化物及び／又は炭窒化物を形成して、結晶粒を微細化する。これにより、機械構造用部品の靱性が高まる。Ｔｉが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｔｉ含有量が０．１５００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が飽和して、製造コストが高くなる。
　したがって、Ｔｉ含有量は０～０．１５００％である。含有される場合、Ｔｉ含有量は０．１５００％以下である。
　Ｔｉ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．００８０％である。
　Ｔｉ含有量の好ましい上限は０．１４００％であり、さらに好ましくは０．１２００％であり、さらに好ましくは０．１０００％であり、さらに好ましくは０．０５００％であり、さらに好ましくは０．０２００％であり、さらに好ましくは０．０１５０％である。
　Ｎｂ：０．０８００％以下
　ニオブ（Ｎｂ）は任意元素であり、含有されなくてもよい。つまり、Ｎｂ含有量は０％であってもよい。
　含有される場合、つまり、Ｎｂ含有量が０％超である場合、Ｎｂは、機械構造用部品の製造工程中の熱間加工工程の冷却過程において、炭化物及び／又は炭窒化物を形成して、結晶粒を微細化する。これにより、機械構造用部品の靱性が高まる。Ｎｂが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｎｂ含有量が０．０８００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が飽和して、製造コストが高くなる。
　したがって、Ｎｂ含有量は０～０．０８００％である。含有される場合、Ｎｂ含有量は０．０８００％以下である。
　Ｎｂ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．００８０％である。
　Ｎｂ含有量の好ましい上限は０．０７００％であり、さらに好ましくは０．０６００％であり、さらに好ましくは０．０５００％であり、さらに好ましくは０．０２００％であり、さらに好ましくは０．０１５０％である。
　Ｗ：０．４０００％以下
　タングステン（Ｗ）は任意元素であり、含有されなくてもよい。つまり、Ｗ含有量は０％であってもよい。
　含有される場合、つまり、Ｗ含有量が０％超である場合、Ｗは、機械構造用部品の製造工程中の熱間加工工程の冷却過程において、炭化物及び／又は炭窒化物を形成して、結晶粒を微細化する。これにより、機械構造用部品の靱性が高まる。Ｗが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｗ含有量が０．４０００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が飽和して、製造コストが高くなる。
　したがって、Ｗ含有量は０～０．４０００％である。含有される場合、Ｗ含有量は０．４０００％以下である。
　Ｗ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．０５００％である。
　Ｗ含有量の好ましい上限は０．３５００％であり、さらに好ましくは０．３０００％であり、さらに好ましくは０．２０００％である。
　Ｚｒ：０．２０００％以下
　ジルコニウム（Ｚｒ）は任意元素であり、含有されなくてもよい。つまり、Ｚｒ含有量は０％であってもよい。
　含有される場合、つまり、Ｚｒ含有量が０％超である場合、Ｚｒは、機械構造用部品の製造工程中の熱間加工工程の冷却過程において、炭化物及び／又は炭窒化物を形成して、結晶粒を微細化する。これにより、機械構造用部品の靱性が高まる。Ｚｒが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｚｒ含有量が０．２０００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が飽和して、製造コストが高くなる。
　したがって、Ｚｒ含有量は０～０．２０００％である。含有される場合、Ｚｒ含有量は０．２０００％以下である。
　Ｚｒ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００２０％であり、さらに好ましくは０．００５０％である。
　Ｚｒ含有量の好ましい上限は０．１５００％であり、さらに好ましくは０．１０００％であり、さらに好ましくは０．０５００％であり、さらに好ましくは０．０１００％である。
　［第３群：Ｃａ、Ｔｅ、Ｂ、Ｓｎ及び希土類元素］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、上述の第３群を含有してもよい。これらの元素は任意元素であり、いずれも鋼材の被削性を高める。以下、第３群の各元素について説明する。
　Ｃａ：０．０１００％以下
　カルシウム（Ｃａ）は、任意元素であり、含有されなくてもよい。つまり、Ｃａ含有量は０％であってもよい。
　含有される場合、つまり、Ｃａ含有量が０％超である場合、Ｃａは鋼材の被削性を高める。Ｃａが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｃａ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、粗大酸化物を形成する。この場合、機械構造用部品の疲労強度が低下する。
　したがって、Ｃａ含有量は０～０．０１００％である。含有される場合、Ｃａ含有量は０．０１００％以下である。
　Ｃａ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００１５％である。
　Ｃａ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００７０％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．００３０％であり、さらに好ましくは０．００２０％である。
　Ｔｅ：０．０１００％以下
　テルル（Ｔｅ）は、任意元素であり、含有されなくてもよい。つまり、Ｔｅ含有量は０％であってもよい。
　含有される場合、つまり、Ｔｅ含有量が０％超である場合、Ｔｅは鋼材の被削性を高める。Ｔｅが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｔｅ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材に熱間加工割れが発生しやすくなる。
　したがって、Ｔｅ含有量は０～０．０１００％である。含有される場合、Ｔｅ含有量は０．０１００％以下である。
　Ｔｅ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００３％であり、さらに好ましくは０．００１０％である。
　Ｔｅ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００８５％であり、さらに好ましくは０．００８０％である。
　Ｂ：０．００５０％以下
　ボロン（Ｂ）は、任意元素であり、含有されなくてもよい。つまり、Ｂ含有量は０％であってもよい。
　含有される場合、つまり、Ｂ含有量が０％超である場合、Ｂは鋼材の被削性を高める。Ｂが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｂ含有量が０．００５０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材に熱間加工割れが発生しやすくなる。
　したがって、Ｂ含有量は０～０．００５０％である。含有される場合、Ｂ含有量は０．００５０％以下である。
　Ｂ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％である。
　Ｂ含有量の好ましい上限は０．００４０％であり、さらに好ましくは０．００３５％であり、さらに好ましくは０．００３０％である。
　Ｓｎ：０．０１００％以下
　スズ（Ｓｎ）は、任意元素であり、含有されなくてもよい。つまり、Ｓｎ含有量は０％であってもよい。
　含有される場合、つまり、Ｓｎ含有量が０％超である場合、Ｓｎは鋼材の被削性を高める。Ｓｎが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｓｎ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材に熱間加工割れが発生しやすくなる。
　したがって、Ｓｎ含有量は０～０．０１００％である。含有される場合、Ｓｎ含有量は０．０１００％以下である。
　Ｓｎ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％である。
　Ｓｎ含有量の好ましい上限は０．００９５％であり、さらに好ましくは０．００９０％であり、さらに好ましくは０．００８５％であり、さらに好ましくは０．００８０％である。
　希土類元素：０．０１００％以下
　希土類元素（ＲＥＭ）は、任意元素であり、含有されなくてもよい。つまり、ＲＥＭ含有量は０％であってもよい。
　含有される場合、つまり、ＲＥＭ含有量が０％超である場合、ＲＥＭは鋼材の被削性を高める。ＲＥＭが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、ＲＥＭ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材に熱間加工割れが発生しやすくなる。
　したがって、ＲＥＭ含有量は０～０．０１００％である。含有される場合、ＲＥＭ含有量は０．０１００％以下である。
　ＲＥＭ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％である。
　ＲＥＭ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００７０％であり、さらに好ましくは０．００５５％である。
　本明細書におけるＲＥＭとは、原子番号２１番のスカンジウム（Ｓｃ）、原子番号３９番のイットリウム（Ｙ）、及び、ランタノイドである原子番号５７番のランタン（Ｌａ）～原子番号７１番のルテチウム（Ｌｕ）からなる群から選択される１種又は２種以上の元素である。また、本明細書におけるＲＥＭ含有量とは、これらの元素の合計含有量である。
　［第４群：Ｃｏ、Ｓｅ、Ｓｂ及びＩｎ］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、上述の第４群を含有してもよい。これらの元素は任意元素であり、いずれも鋼材の脱炭を抑制する。以下、第４群の各元素について説明する。
　Ｃｏ：０．０１００％以下
　コバルト（Ｃｏ）は、任意元素であり、含有されなくてもよい。つまり、Ｃｏ含有量は０％であってもよい。
　含有される場合、つまり、Ｃｏ含有量が０％超である場合、Ｃｏは、熱間加工時に鋼材の脱炭を抑制する。Ｃｏが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｃｏ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材に熱間加工割れが発生しやすくなる。
　したがって、Ｃｏ含有量は０～０．０１００％である。含有される場合、Ｃｏ含有量は０．０１００％以下である。
　Ｃｏ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％である。
　Ｃｏ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００７０％である。
　Ｓｅ：０．０１００％以下
　セレン（Ｓｅ）は、任意元素であり、含有されなくてもよい。つまり、Ｓｅ含有量は０％であってもよい。
　含有される場合、つまり、Ｓｅ含有量が０％超である場合、Ｓｅは、熱間加工時に鋼材の脱炭を抑制する。Ｓｅが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｓｅ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材に熱間加工割れが発生しやすくなる。
　したがって、Ｓｅ含有量は０～０．０１００％である。含有される場合、Ｓｅ含有量は０．０１００％以下である。
　Ｓｅ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％である。
　Ｓｅ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００７０％である。
　Ｓｂ：０．０１００％以下
　アンチモン（Ｓｂ）は、任意元素であり、含有されなくてもよい。つまり、Ｓｂ含有量は０％であってもよい。
　含有される場合、つまり、Ｓｂ含有量が０％超である場合、Ｓｂは、熱間加工時に鋼材の脱炭を抑制する。Ｓｂが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｓｂ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材に熱間加工割れが発生しやすくなる。
　したがって、Ｓｂ含有量は０～０．０１００％である。含有される場合、Ｓｂ含有量は０．０１００％以下である。
　Ｓｂ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％である。
　Ｓｂ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００７０％である。
　Ｉｎ：０．０１００％以下
　インジウム（Ｉｎ）は、任意元素であり、含有されなくてもよい。つまり、Ｉｎ含有量は０％であってもよい。
　含有される場合、つまり、Ｉｎ含有量が０％超である場合、Ｉｎは、熱間加工時に鋼材の脱炭を抑制する。Ｉｎが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｉｎ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材に熱間加工割れが発生しやすくなる。
　したがって、Ｉｎ含有量は０～０．０１００％である。含有される場合、Ｉｎ含有量は０．０１００％以下である。
　Ｉｎ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％である。
　Ｉｎ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００７０％である。
　［第５群：Ｖ、Ｍｏ、Ｃｕ及びＮｉ］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、上述の第５類を含有してもよい。これらの元素は任意元素であり、いずれも機械構造用部品の疲労強度を高める。以下、第５群の各元素について説明する。
　Ｖ：０．２００％以下
　バナジウム（Ｖ）は任意元素であり、含有されなくてもよい。つまり、Ｖ含有量は０％であってもよい。
　含有される場合、つまり、Ｖ含有量が０％超である場合、Ｖは析出物を形成し、機械構造用部品の疲労強度を高める。Ｖはさらに、Ｃと結合してオーステナイト粒内にＣを固定する。そのため、Ｖは、高周波焼入れ時において、溶融割れの発生を抑制する。Ｖが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｖ含有量が０．２００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の硬さが過剰に高まる。その結果、鋼材の被削性が低下する。
　したがって、Ｖ含有量は０～０．２００％である。含有される場合、Ｖ含有量は０．２００％以下である。
　Ｖ含有量の好ましい下限は０．００１％であり、さらに好ましくは０．００５％であり、さらに好ましくは０．０１０％であり、さらに好ましくは０．０１５％である。
　Ｖ含有量の好ましい上限は０．１９５％であり、さらに好ましくは０．１９０％であり、さらに好ましくは０．１８５％であり、さらに好ましくは０．１５０％である。
　Ｍｏ：１．００％以下
　モリブデン（Ｍｏ）は任意元素であり、含有されなくてもよい。つまり、Ｍｏ含有量は０％であってもよい。
　含有される場合、つまり、Ｍｏ含有量が０％超である場合、Ｍｏは機械構造用部品の疲労強度を高める。Ｍｏが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｍｏ含有量が１．００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の硬さが過剰に高まる。その結果、熱間加工性が低下する。
　したがって、Ｍｏ含有量は０～１．００％である。含有される場合、Ｍｏ含有量は１．００％以下である。
　Ｍｏ含有量の好ましい下限は０．０１％であり、さらに好ましくは０．０５％であり、さらに好ましくは０．１０％である。
　Ｍｏ含有量の好ましい上限は０．９０％であり、さらに好ましくは０．８０％であり、さらに好ましくは０．６０％であり、さらに好ましくは０．４０％である。
　Ｃｕ：０．２０％以下
　銅（Ｃｕ）は任意元素であり、含有されなくてもよい。つまり、Ｃｕ含有量は０％であってもよい。
　含有される場合、つまり、Ｃｕ含有量が０％超である場合、Ｃｕは機械構造用部品の疲労強度を高める。Ｃｕが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｃｕは、Ｓｉと同様に、高周波焼入れ時における溶融割れの発生を促進する。そのため、Ｃｕ含有量が０．２０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、高周波焼入れ時に溶融割れが発生しやすくなる。
　したがって、Ｃｕ含有量は０～０．２０％である。含有される場合、Ｃｕ含有量は０．２０％以下である。
　Ｃｕ含有量の好ましい下限は０．０１％であり、さらに好ましくは０．０２％であり、さらに好ましくは０．０３％である。
　Ｃｕ含有量の好ましい上限は０．１５％であり、さらに好ましくは０．１３％であり、さらに好ましくは０．１０％である。
　Ｎｉ：０．２０％以下
　ニッケル（Ｎｉ）は任意元素であり、含有されなくてもよい。つまり、Ｎｉ含有量は０％であってもよい。
　含有される場合、つまり、Ｎｉ含有量が０％超である場合、Ｎｉは機械構造用部品の疲労強度を高める。Ｎｉが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｎｉは、Ｓｉ及びＣｕと同様に、高周波焼入れ時における溶融割れの発生を促進する。そのため、Ｎｉ含有量が０．２０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、高周波焼入れ時に溶融割れが発生しやすくなる。
　したがって、Ｎｉ含有量は０～０．２０％である。含有される場合、Ｎｉ含有量は０．２０％以下である。
　Ｎｉ含有量の好ましい下限は０．０１％であり、さらに好ましくは０．０２％であり、さらに好ましくは０．０３％である。
　Ｎｉ含有量の好ましい上限は０．１５％であり、さらに好ましくは０．１３％であり、さらに好ましくは０．１０％である。
　［鋼材の化学組成の測定方法］
　本実施形態の鋼材の化学組成は、ＪＩＳ　Ｇ０３２１：２０１７に準拠した周知の成分分析法で測定できる。具体的には、ドリルを用いて、鋼材の表面から１ｍｍ深さ以上の内部から、切粉を採取する。採取された切粉を酸に溶解させて溶液を得る。溶液に対して、ＩＣＰ－ＡＥＳ（Ｉｎｄｕｃｔｉｖｅｌｙ　Ｃｏｕｐｌｅｄ　Ｐｌａｓｍａ　Ａｔｏｍｉｃ　Ｅｍｉｓｓｉｏｎ　Ｓｐｅｃｔｒｏｍｅｔｒｙ）を実施して、化学組成の元素分析を実施する。Ｃ含有量及びＳ含有量については、周知の高周波燃焼法（燃焼－赤外線吸収法）により求める。Ｎ含有量については、周知の不活性ガス融解－熱伝導度法を用いて求める。Ｏ含有量については、周知の不活性ガス溶融－赤外線吸収法を用いて求める。
　なお、各元素含有量は、本実施形態で規定された有効数字に基づいて、測定された数値の端数を四捨五入して、本実施形態で規定された各元素含有量の最小桁までの数値とする。たとえば、本実施形態の鋼材のＣ含有量は小数第二位までの数値で規定される。したがって、Ｃ含有量は、測定された数値の小数第三位を四捨五入して得られた小数第二位までの数値とする。
　本実施形態の鋼材のＣ含有量以外の他の元素含有量も同様に、測定された値に対して、本実施形態で規定された最小桁までの数値の端数を四捨五入して得られた値を、当該元素含有量とする。
　なお、四捨五入とは、端数が５未満であれば切り捨て、端数が５以上であれば切り上げることを意味する。
　［（特徴２）式（１）について］
　本実施形態の鋼材はさらに、各元素含有量が上記範囲内であることを前提として、式（１）を満たす。
　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ≦１．００　（１）
　ここで、式中の各元素記号には、対応する元素の含有量が質量％で代入される。元素が含有されていない場合、対応する元素記号には「０」が代入される。つまり、任意元素であるＶが含有されない場合、式（１）は次のとおりとなる。
　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）≦１．００　（１）
　ｆｎ１を次のとおり定義する。
　ｆｎ１＝Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ
　なお、任意元素であるＶが含有されない場合、ｆｎ１は次のとおりとなる。
　ｆｎ１＝Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）
　ｆｎ１は、鋼材の硬さの指標である。Ｃ、Ｓｉ、Ｍｎ、Ｃｒ及びＶは、鋼材を素材として製造された機械構造用部品の内部硬さを高める。一方、Ｓは、機械構造用部品の内部硬さを低下する。
　鋼材中の各元素含有量が本実施形態の範囲内であっても、ｆｎ１が０．２５未満であれば、機械構造用部品の内部硬さが過剰に低下する。その結果、機械構造用部品の疲労強度が低下する。一方、鋼材中の各元素含有量が本実施形態の範囲内であっても、ｆｎ１が１．００を超えれば、鋼材の硬さが過剰に高まる。その結果、鋼材の被削性が低下する。
　したがって、ｆｎ１は０．２５～１．００である。
　ｆｎ１の好ましい下限は０．２８であり、さらに好ましくは０．３０であり、さらに好ましくは０．３３である。
　ｆｎ１の好ましい上限は０．９８であり、さらに好ましくは０．９５であり、さらに好ましくは０．９０である。
　［（特徴３）微細Ｂｉ粒子について］
　本実施形態の鋼材では、特徴１及び特徴２を満たすことを前提として、円相当径が０．１～１．０μｍの微細Ｂｉ粒子（以下、単に微細Ｂｉ粒子ともいう）の個数密度は８０～８０００個／ｍｍ２である。微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２であれば、高周波焼入れ時の溶融割れの発生が抑制される。
　Ｂｉは、鋼材中において、Ｂｉ単体の粒子又はＢｉを含有する粒子の形態で存在する。本明細書において、Ｂｉ単体の粒子又はＢｉを含有する粒子を総称してＢｉ粒子と定義する。本明細書において、微細Ｂｉ粒子とは、円相当径が０．１～１．０μｍであるＢｉ粒子を意味する。Ｂｉは重元素であるため、Ｂｉ粒子は反射電子像において、周囲よりも高輝度で観察される。微細Ｂｉ粒子は、他の粒子（析出物又は介在物）と接触せずに鋼材中に単独で存在してもよい。また、微細Ｂｉ粒子は、他の粒子に付着又は接触して鋼材中に存在していてもよい。
　上述のとおり、高周波誘導加熱時において、Ｂｉ粒子は、オーステナイト粒界をピンニングする。Ｂｉ粒子の円相当径が０．１～１．０μｍであれば、オーステナイト粒界のピンニング効果は高まる。高周波焼入れ時において、オーステナイト粒が微細に維持されれば、オーステナイト粒の粒界面積が増大する。粒界面積が増大すれば、粒界に偏析するＣの濃度が減少する。その結果、溶融割れの発生が抑制される。鋼材が特徴１及び特徴２を満たし、さらに後述の特徴４を満たす場合であっても、微細Ｂｉ粒子が８０個／ｍｍ２未満であれば、上記効果が十分に得られない。
　一方、鋼材が特徴１、特徴２及び特徴４を満たしても、微細Ｂｉ粒子の個数密度が８０００個／ｍｍ２を超えれば、上記効果が飽和し、さらに、製造コストが高くなる。
　したがって、本実施形態の鋼材では、円相当径が０．１～１．０μｍの微細Ｂｉ粒子の個数密度は８０～８０００個／ｍｍ２である。
　微細Ｂｉ粒子の個数密度の好ましい下限は９０個／ｍｍ２であり、さらに好ましくは９５個／ｍｍ２であり、さらに好ましくは１００個／ｍｍ２である。微細Ｂｉ粒子の個数密度の好ましい上限は７９００個／ｍｍ２であり、さらに好ましくは６０００個／ｍｍ２であり、さらに好ましくは３０００個／ｍｍ２であり、さらに好ましくは１０００個／ｍｍ２であり、さらに好ましくは９００個／ｍｍ２であり、さらに好ましくは８００個／ｍｍ２である。
　［（特徴４）粗大Ｂｉ粒子について］
　本実施形態の鋼材において、円相当径が１０．０μｍ以上のＢｉ粒子である粗大Ｂｉ粒子（以下、単に粗大Ｂｉ粒子ともいう）の個数密度は１０個／ｍｍ２以下である。粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下であれば、鋼材の製造工程中の熱間加工時、又は、鋼材を素材とした機械構造用部品の製造工程中の熱間加工時の割れ（熱間加工割れ）を抑制することができる。熱間加工は例えば、熱間圧延、熱間鍛造等である。
　本明細書において、粗大Ｂｉ粒子とは、円相当径が１０．０μｍ以上のＢｉ粒子を意味する。後述する粗大Ｂｉ粒子の個数密度測定方法において、粒子の円相当径が１０．０μｍ以上であり、かつ、反射電子像において周囲よりも高輝度で観察されれば、その粒子を、粗大Ｂｉ粒子と判断する。粗大Ｂｉ粒子は、他の粒子（析出物又は介在物）と接触せずに鋼材中に単独で存在してもよい。また、粗大Ｂｉ粒子は、他の粒子に付着又は接触して鋼材中に存在していてもよい。粗大Ｂｉ粒子の円相当径の上限は特に限定されないが、本実施形態の化学組成の場合、粗大Ｂｉ粒子の円相当径の上限は５０．０μｍである。
　上述のとおり、鋼材中の微細Ｂｉ粒子により、高周波焼入れ時の溶融割れが抑制される。しかしながら、鋼材中のＢｉは、微細Ｂｉ粒子ではなく粗大Ｂｉ粒子を形成する場合がある。粗大Ｂｉ粒子は、鋼材の熱間加工割れの起点となり得る。
　鋼材が特徴１～特徴３を満たしても、粗大Ｂｉ粒子が１０個／ｍｍ２を超えれば、鋼材に熱間加工割れが発生する場合がある。したがって、本実施形態の鋼材では、円相当径が１０．０μｍ以上の粗大Ｂｉ粒子の個数密度は１０個／ｍｍ２以下である。
　粗大Ｂｉ粒子の個数密度の好ましい上限は８個／ｍｍ２であり、さらに好ましくは７個／ｍｍ２であり、さらに好ましくは６個／ｍｍ２であり、さらに好ましくは５個／ｍｍ２である。
　粗大Ｂｉ粒子の個数密度はなるべく低い方が好ましい。すなわち、粗大Ｂｉ粒子の個数密度は０個／ｍｍ２であることが好ましい。しかしながら、粗大Ｂｉ粒子の個数密度の過剰な低減は製造コストを引き上げる。したがって、通常の工業生産性を考慮すれば、粗大Ｂｉ粒子の個数密度の好ましい下限は１個／ｍｍ２であり、さらに好ましくは２個／ｍｍ２である。
　なお、本実施形態の鋼材中には、上述の微細Ｂｉ粒子及び粗大Ｂｉ粒子だけではなく、１．０μｍ超～１０．０μｍ未満の中間Ｂｉ粒子（以下、単に中間Ｂｉ粒子ともいう）も存在する場合がある。しかしながら、中間Ｂｉ粒子は、熱間加工割れ及び高周波焼入れ時の溶融割れに影響を与えにくい。したがって、熱間加工割れの抑制及び溶融割れの抑制において、中間Ｂｉ粒子は考慮しなくてよい。
　［微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度の測定方法］
　微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度は、次の方法で測定できる。
　鋼材（棒鋼）の軸方向（圧延方向）に対して垂直な断面のうち、Ｒ／２部を含む試験片を採取する。ここで、Ｒ／２部とは、鋼材の軸方向に垂直な断面における、半径Ｒの中央部を意味する。採取した試験片の表面のうち、上記鋼材の軸方向に対して垂直な断面に相当する表面を観察面とする。観察面を鏡面研磨する。走査型電子顕微鏡（Ｓｃａｎｎｉｎｇ　Ｅｌｅｃｔｒｏｎ　Ｍｉｃｒｏｓｃｏｐｅ：ＳＥＭ）を用いて、１０００倍の倍率で、鏡面研磨後の観察面のＲ／２部を２０視野観察する。各視野の面積を１００μｍ×１２０μｍとする。
　ＳＥＭ観察により得られた各視野の反射電子像に基づいて、周知の画像解析の粒子解析方法を用いて、粗大Ｂｉ粒子及び微細Ｂｉ粒子の個数密度を調べる。具体的には、鋼材の母相と粒子との界面に基づいて、鋼材中の粒子を特定する。ここでいう粒子は、介在物又は析出物である。画像解析を行い、特定された粒子の円相当径を求める。具体的には、特定された各粒子の面積を求める。求めた面積と同じ面積の円での直径を、当該粒子の円相当径（μｍ）とする。
　Ｂｉは重元素であるため、反射電子像において高輝度で観察される。そのため、上記ＳＥＭ観察により得られた反射電子像中で観察される粒子のうち、円相当径が０．１～１．０μｍの粒子であって、かつ、周囲よりも高輝度で観察される粒子を、微細Ｂｉ粒子と特定する。また、ＳＥＭ観察により得られた反射電子像で観察される粒子のうち、円相当径が１０．０μｍ以上の粒子であって、かつ、周囲よりも高輝度で観察される粒子を、粗大Ｂｉ粒子と特定する。
　なお、後述の実施例において、上記方法により特定された微細Ｂｉ粒子及び粗大Ｂｉ粒子の化学組成を、ＳＥＭに備えられたエネルギー分散型Ｘ線分析装置（ＥＤＸ：Ｅｎｅｒｇｙ　Ｄｉｓｐｅｒｓｉｖｅ　Ｘ－ｒａｙ　ｓｐｅｃｔｒｏｓｃｏｐｙ）を用いて分析した結果、いずれもＢｉ粒子であることを確認できている。なお、確認したときのＥＤＸのビーム径は０．１～１．０μｍであった。
　上記の方法で微細Ｂｉ粒子及び粗大Ｂｉ粒子を特定する。各視野で特定された微細Ｂｉ粒子の総個数と、２０視野の総面積（０．２４ｍｍ２）とに基づいて、微細Ｂｉ粒子の単位面積当たりの個数（個／ｍｍ２）を求める。また、各視野で特定された粗大Ｂｉ粒子の総個数と、２０視野の総面積（０．２４ｍｍ２）とに基づいて、粗大Ｂｉ粒子の単位面積当たりの個数（個／ｍｍ２）を求める。
　［本実施形態の鋼材の効果］
　以上のとおり、本実施形態の鋼材は特徴１～特徴４を満たす。そのため、本実施形態の鋼材では、被削性に優れ、熱間加工時の割れ及び高周波焼入れ時の溶融割れを抑制でき、機械構造用部品とした場合に優れた疲労強度を有する。
　［本実施形態の鋼材の好ましい用途］
　本実施形態の鋼材は、例えば、機械構造用部品の素材として広く適用可能である。本実施形態の鋼材は特に、機械構造用部品の製造工程において、高周波焼入れを実施する場合に、好適である。ただし、高周波焼入れを実施しない場合であっても、本実施形態の鋼材は、機械構造用部品の素材として適用可能である。
　［製造方法］
　本実施形態の鋼材の製造方法の一例を説明する。以降に説明する鋼材の製造方法は、本実施形態による鋼材を製造するための一例である。したがって、上述の構成を有する鋼材は、以降に説明する製造方法以外の他の製造方法により製造されてもよい。しかしながら、以降に説明する製造方法は、本実施形態による鋼材の製造方法の好ましい一例である。
　本実施形態による鋼材の製造方法の一例は、次の工程を含む。
　（工程１）精錬工程
　（工程２）鋳造工程
　（工程３）熱間加工工程
　なお、熱間加工工程は任意の工程である。以下、各工程について説明する。
　［（工程１）精錬工程］
　精錬工程では、上述の特徴１及び特徴２を満たす化学組成を有する溶鋼を製造する。精錬工程は、一次精錬工程と二次精錬工程とを含む。
　一次精錬工程では、周知の方法で製造された溶銑に対して、転炉での精錬を実施する。二次精錬工程では、溶鋼に対して合金元素を添加して、溶鋼の化学組成が、特徴１及び特徴２を満たすようにする。具体的には、二次精錬工程では、周知の精錬方法で溶鋼を攪拌しながら、Ｂｉ以外の溶鋼の成分調整を実施する。その後、溶鋼を攪拌しながら、ワイヤーにより溶鋼にＢｉを添加し、Ｂｉの成分調整を行う。
　二次精錬工程では、次の条件を満たす。
　（条件）
　溶鋼にＢｉを添加した後、二次精錬工程での攪拌終了までの時間Ｔを１５分超～６０分未満とする。
　二次精錬工程において、Ｂｉを添加した後、二次精錬工程での攪拌終了までの時間は、１５分超～６０分未満である。Ｂｉを添加した後、二次精錬工程での攪拌終了までの時間が１５分以下の場合、溶鋼中でＢｉが十分に拡散しない。この場合、鋼材中に粗大Ｂｉ粒子が過剰に多く生成する。Ｂｉを添加した後、二次精錬工程での攪拌終了までの時間が６０分以上の場合、微細Ｂｉ粒子同士が凝集しやすくなる。そのため、微細Ｂｉ粒子の個数密度が減少する。
　二次精錬工程で、Ｂｉを添加した後、二次精錬工程での攪拌終了までの時間が１５分超であれば、溶鋼中でＢｉが十分に拡散する。そのため、鋼材中に微細Ｂｉ粒子が十分に生成する。さらに、二次精錬工程で、Ｂｉを添加した後、二次精錬工程での攪拌終了までの時間が６０分未満であれば、微細Ｂｉ粒子同士の凝集を十分に抑制できる。そのため、微細Ｂｉ粒子の個数密度が８０個／ｍｍ２以上となり、粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下になる。
　溶鋼にＢｉを添加した後、二次精錬工程での攪拌終了までの時間の好ましい上限は５０分であり、さらに好ましくは４０分である。Ｂｉを添加した後、二次精錬工程での攪拌終了までの時間の好ましい下限は２０分であり、さらに好ましくは３０分である。
　なお、Ｂｉを添加した後、二次精錬工程での攪拌終了までの溶鋼の温度は１５１０～１５６０℃である。
　［（工程２）鋳造工程］
　鋳造工程では、溶鋼を用いて、周知の鋳造方法により鋳片（スラブ又はブルーム）又は鋼塊（インゴット）を製造する。鋳造方法はたとえば、連続鋳造法や造塊法である。
　［（工程３）熱間加工工程］
　熱間加工工程は、任意の工程である。つまり、熱間加工工程は実施してもよいし、実施しなくてもよい。
　熱間加工工程を実施する場合、熱間加工工程では、上記鋳造工程で製造された鋳片又は鋼塊に対して、熱間加工を実施して、本実施形態の鋼材を製造する。本実施形態の鋼材は例えば、棒鋼である。熱間加工工程は例えば、熱間圧延であってもよく、熱間鍛造であってもよい。
　熱間加工工程において熱間圧延を実施する場合、例えば、粗圧延工程のみであってもよいし、粗圧延工程と、仕上げ圧延工程とを実施してもよい。粗圧延工程は例えば、分塊圧延である。仕上げ圧延工程は例えば、連続圧延機を用いた仕上げ圧延である。連続圧延機では例えば、一対の水平ロールを有する水平スタンドと、一対の垂直ロールを有する垂直スタンドとが交互に一列に配列される。粗圧延工程及び仕上げ圧延工程での加熱温度は例えば、１０００～１３００℃である。
　以上の製造工程により、本実施形態の鋼材が製造される。上述のとおり、本製造方法は熱間加工工程を省略してもよい。つまり、本実施形態の鋼材は、鋳造品（鋳片又はインゴット）であってもよい。また、本実施形態の鋼材は、熱間加工工程を実施して製造されてもよい。
　［機械構造用部品の製造方法］
　上述のとおり、本実施形態の鋼材は、機械構造用部品の素材となる。機械構造用部品は例えば、自動車用途の部品である。機械構造用部品は例えば、足回り部品、車軸、クランクシャフト等である。
　本実施形態の鋼材を素材として用いた機械構造用部品は、例えば、次の周知の製造方法により製造される。
　初めに、本実施形態の鋼材を熱間加工して、機械構造用部品の粗形状の中間品を製造する。熱間加工は例えば、熱間鍛造である。製造された中間品を機械加工により所定の形状に切削する。切削後の中間品に対して、高周波焼入れ及び焼戻しを実施する。以上の工程により、機械構造用部品が製造される。
　本実施形態の鋼材では、化学組成中の各元素含有量が本実施形態の範囲内であり、かつ、式（１）を満たす。さらに、円相当径が０．１～１．０μｍの微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２であり、円相当径が１０．０μｍ以上の粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下である。つまり、本実施形態の鋼材は特徴１～特徴４を満たす。そのため、本実施形態の鋼材では、優れた被削性が得られる。さらに、本実施形態の鋼材を素材として製造された機械構造用部品では優れた疲労強度が得られる。さらに、鋼材の製造工程中又は機械構造用部品の製造工程中での熱間加工割れが抑制される。さらに、本実施形態の鋼材を素材とした機械構造用部品を製造する場合、高周波焼入れを実施しても、溶融割れが抑制される。
　実施例により本実施形態の鋼材の効果をさらに具体的に説明する。以下の実施例での条件は、本実施形態の鋼材の実施可能性及び効果を確認するために採用した一条件例である。したがって、本実施形態の鋼材はこの一条件例に限定されない。
　表１～表４の化学組成を有する鋼材を製造した。表２は表１の続きであり、表４は表３の続きである。なお、いずれの試験番号においても、Ｏ（酸素）含有量は質量％で０．００５０％以下であった。また、Ｔａ及びＺｎの合計含有量は、質量％で０～０．０１％であった。また、Ｐｂ含有量は、質量％で０～０．０９％であった。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
　具体的には、７０トン転炉を用いて、精錬工程（一次精錬工程、及び、二次精錬工程）を実施した。一次精錬工程では、周知の方法で製造された溶銑に対して転炉での精錬を同じ条件で実施した。二次精錬工程では、元素を添加して、溶鋼の化学組成が、表１～表４の化学組成を有する溶鋼を製造した。具体的には、周知の方法で二次精錬を実施して、溶鋼を攪拌しながら、Ｂｉ以外の元素の成分の調整を実施した。その後さらに、溶鋼を攪拌しながら、ワイヤーにてＢｉを添加し、溶鋼中のＢｉの成分調整を行った。
　Ｂｉを溶鋼に添加した後、二次精錬での攪拌終了までの時間Ｔ（分）は、表５及び表６に示すとおりであった。なお、Ｂｉを溶鋼に添加した後、二次精錬での攪拌終了までの溶鋼温度は１５１０～１５６０℃であった。以上の工程により、表１～表４の化学組成の溶鋼を製造した。
Figure JPOXMLDOC01-appb-T000005
Figure JPOXMLDOC01-appb-T000006
　溶鋼を用いて、連続鋳造法により、３００ｍｍ×４００ｍｍの横断面を有する鋳片（ブルーム）を製造した。この鋳片を加熱した後、鋳片を分塊圧延して、横断面が１８０ｍｍ×１８０ｍｍのビレットを製造した。なお、分塊圧延時の鋳片の加熱温度は１２５０℃であった。
　さらに、ビレットに対して仕上げ圧延に相当する熱間鍛造を実施して、直径８０ｍｍの鋼材（棒鋼）を製造した。なお、熱間鍛造時のビレットの加熱温度は１２５０℃であった。以上の製造工程により、鋼材を製造した。
　［評価試験］
　各試験番号の鋼材に対して、次の評価試験を実施した。
　（試験１）化学組成分析試験
　（試験２）熱間加工割れ評価試験
　（試験３）微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度測定試験
　（試験４）溶融割れ評価試験
　（試験５）被削性評価試験（ドリル寿命試験）
　（試験６）疲労強度評価試験（回転曲げ疲労試験）
　以下、各評価試験について説明する。
　［（試験１）化学組成分析試験］
　各試験番号の鋼材に対して、上述の［鋼材の化学組成の測定方法］に記載の周知の成分分析法により、化学組成を測定した。その結果、各試験番号の鋼材の化学組成は、表１～表４に記載のとおりであった。
　［（試験２）熱間加工割れ評価試験］
　製造された各試験番号の鋼材の表面を目視で観察した。目視での観察の結果、鋼材の表面において、鋼材の長手方向１ｍ当たり３箇所以上の明確な割れが観察される場合、熱間加工割れが発生したと判断した。目視での観察の結果、鋼材の表面において鋼材の長手方向１ｍ当たり３箇所以上の明確な割れが観察されない場合、熱間加工割れが抑制されたと判断した。
　熱間加工割れの評価結果を表５及び表６の「熱間加工割れ」欄に示す。熱間加工割れが抑制された場合、「Ｅ」（Ｅｘｃｅｌｌｅｎｔ）で表記する。熱間加工割れが発生した場合、「ＮＡ」（Ｎｏｔ　Ａｃｃｅｐｔｅｄ）で表記する。
　［（試験３～試験６）微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度測定試験、溶融割れ評価試験、被削性評価試験及び疲労強度評価試験について］
　［機械構造用部品の模擬中間品の製造］
　各試験番号の鋼材を素材とした機械構造用部品の製造工程中の熱間鍛造を模擬した熱処理を実施した。具体的には、鋼材を加熱して、鋼材を１１００℃で３０分保持した。その後、鋼材を大気中で放冷した。以上の熱処理を施した鋼材を、以降では、「機械構造用部品の模擬中間品（又は、単に模擬中間品）」という。機械構造用部品の模擬中間品は、直径８０ｍｍの棒鋼であった。
　［（試験３）微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度測定試験］
　［鋼材の微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度］
　各試験番号の鋼材を用いて、上述の［微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度の測定方法］に記載の方法に基づいて、各試験番号の鋼材の微細Ｂｉ粒子の個数密度（個／ｍｍ２）、及び、粗大Ｂｉ粒子の個数密度（個／ｍｍ２）を求めた。鋼材の軸方向（圧延方向）に対して垂直な断面（横断面）のうち、Ｒ／２部を含む試験片を採取した。この試験片を用いて、各試験番号の微細Ｂｉ粒子の個数密度（個／ｍｍ２）、及び、粗大Ｂｉ粒子の個数密度（個／ｍｍ２）を求めた。得られた微細Ｂｉ粒子の個数密度の結果を表５及び表６の「鋼材」欄の「微細Ｂｉ粒子個数密度（個／ｍｍ２）」欄に示す。得られた粗大Ｂｉ粒子の個数密度の結果を表５及び表６の「鋼材」欄の「粗大Ｂｉ粒子個数密度（個／ｍｍ２）」欄に示す。
　［模擬中間品の微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度］
　各試験番号の機械構造用部品の模擬中間品を用いて、上述の［微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度の測定方法］に記載の方法に基づいて、各試験番号の微細Ｂｉ粒子の個数密度（個／ｍｍ２）、及び、粗大Ｂｉ粒子の個数密度（個／ｍｍ２）を求めた。模擬中間品（棒鋼）の軸方向（圧延方向）に対して垂直な断面（横断面）のうち、Ｒ／２部を含む試験片を採取した。この試験片を用いて、各試験番号の微細Ｂｉ粒子の個数密度（個／ｍｍ２）、及び、粗大Ｂｉ粒子の個数密度（個／ｍｍ２）を求めた。得られた微細Ｂｉ粒子の個数密度の結果を表５及び表６の「模擬中間品」欄の「微細Ｂｉ粒子個数密度（個／ｍｍ２）」欄に示す。得られた粗大Ｂｉ粒子の個数密度の結果を表５及び表６の「模擬中間品」欄の「粗大Ｂｉ粒子個数密度（個／ｍｍ２）」欄に示す。
　なお、機械構造用部品の模擬中間品は、素材である鋼材に対して熱間鍛造を模擬する熱処理を実施して製造した。熱間鍛造を模擬する１１００℃の熱処理を実施するだけでは、微細Ｂｉ粒子の個数密度及び粗大Ｂｉ粒子の個数密度には影響しない。そのため、機械構造用部品の模擬中間品の微細Ｂｉ粒子の個数密度及び粗大Ｂｉ粒子の個数密度は、鋼材の微細Ｂｉ粒子の個数密度及び粗大Ｂｉ粒子の個数密度と実質的に同じである。
　［（試験４）溶融割れ評価試験］
　機械構造用部品の模擬中間品の軸方向（圧延方向）に対して垂直な断面のＲ／２部から、幅１０ｍｍ、厚さ３ｍｍ、長さ１０ｍｍの試験片を採取した。試験片の長手方向は、機械構造用部品の模擬中間品の軸方向（圧延方向）と平行であった。また、試験片の長手方向に平行な中心軸は、Ｒ／２部と一致した。
　富士電波工機株式会社製の熱サイクル試験装置を用いて、試験片に対して、高周波焼入れの模擬試験を実施した。具体的には、高周波コイルを用いて試験片を１００℃／秒の昇温速度で１３９０℃まで加熱した。そして、試験片を１３９０℃で１５秒間保持した。その後、試験片を水冷した。
　水冷後の試験片を、試験片の長手方向での中央位置で、長手方向に垂直な方向に切断した。そして、切断面を観察面とした。観察面を機械研磨した。機械研磨後の観察面をピクラール試薬にて腐食した。腐食された観察面を４００倍の光学顕微鏡で観察し、溶融割れの有無を目視で確認した。観察視野は２視野とした。各観察視野を２５０μｍ×４００μｍとした。
　観察面の２つの観察視野の少なくとも一方において、粒界で幅が５μｍ以上の明瞭に腐食されている領域（腐食領域）が観察される場合、溶融割れが発生したと判断した。粒界で幅が５μｍ以上の明瞭に腐食されている領域とは、例えば、図１に示すとおり、視野中の粒界における腐食領域１０のような、最大の幅が５μｍ以上となる領域を意味する。一方、図２のように、２つの観察視野のいずれにおいても粒界に腐食領域が観察されない場合、溶融割れが抑制されたと判断した。
　溶融割れの評価結果を表５及び表６の「溶融割れ」欄に示す。溶融割れが抑制された場合、「Ｅ」で表記する。溶融割れが発生した場合、「ＮＡ」で表記する。表６の「溶融割れ」欄の「－」は、溶融割れ評価試験を実施していないことを意味する。
　［（試験５）被削性評価試験（ドリル寿命試験）］
　機械構造用部品の模擬中間品から被削性評価試験用の試験片を切り出した。具体的には、直径８０ｍｍの模擬中間品の軸方向（圧延方向）に対して垂直な断面のうち、外表面から径方向に２１ｍｍの深さ位置を、ドリルを用いて穿孔した。工具として、株式会社不二越製の型番ＳＤ３．０のドリルを使用した。穿孔条件として、１回転当たりの送り量を０．２５ｍｍ／ｒｅｖとした。また、１穴の穿孔深さを９ｍｍとした。穿孔中、穿孔箇所に対して、潤滑剤として水溶性の切削油を継続して供給した。
　上述の穿孔条件でドリル穿孔を実施して、鋼材の被削性を評価した。評価指標として、最大切削速度ＶＬ１０００（ｍ／分）を用いた。最大切削速度ＶＬ１０００とは、１０００ｍｍ長の穴開けが可能なドリルの最速の切削速度を意味する。
　最大切削速度ＶＬ１０００が３５ｍ／分以上である場合、優れた被削性が得られたと判断した（表５及び表６中の「被削性」欄で「Ｅ」で表記）。一方、最大切削速度ＶＬ１０００が３５ｍ／分未満である場合、十分な被削性が得られなかったと判断した（表５及び表６中の「被削性」欄で「ＮＡ」で表記）。なお、表６の「被削性」欄の「－」は、被削性評価試験を実施していないことを意味する。
　［（試験６）疲労強度評価試験（回転曲げ疲労試験）］
　次の試験方法により、鋼材を素材として製造された機械構造用部品を想定した疲労試験片を用いて、疲労強度を評価した。
　機械構造用部品の模擬中間品から、回転曲げ疲労試験片を採取した。図３は各模擬機械構造用部品の中間品から採取した回転曲げ疲労試験片の側面図である。図３中の「φ」の数値は、その部位での直径（ｍｍ）を意味する。
　疲労試験片は丸棒試験片であり、平行部の直径が８ｍｍ、掴み部の直径が１２ｍｍであった。疲労試験片の長手方向は、模擬中間品の軸方向と平行であった。具体的には、旋盤加工により、模擬中間品の表面から３．５ｍｍの深さまで切削して、平行部を作製した。したがって、平行部の表面は、少なくとも、棒鋼の表面から深さ５ｍｍの範囲内に相当した。疲労試験片は、鋼材を用いた機械構造用部品の製造工程において、熱間加工後の中間品に対して切削加工を実施した後の機械構造用部品を想定した。疲労試験片の平行部に仕上げ研磨を実施し、表面粗さを調整した。具体的には、ＪＩＳ　Ｂ　０６０１（２００１）に準拠した、表面の中心線平均粗さ（Ｒａ）を３．０μｍ以内とし、最大高さ（Ｒｍａｘ）を９．０μｍ以内にした。
　なお、高周波焼入れ前の模擬機械構造用部品の中間品から採取した回転曲げ疲労試験片を用いた試験により、疲労強度が十分に高ければ、高周波焼入れを実施した後の機械構造用部品においても、優れた疲労強度が得られることは、当業者にも周知の技術常識である。そこで、疲労試験片を用いて、室温（２３℃）、大気雰囲気にて、回転数３６００ｒｐｍの両振りの条件で小野式回転曲げ疲労試験を行った。複数の試験片に対して加える応力を変えて疲労試験を実施し、１０７サイクル後に破断しなかった最も高い応力を、疲労強度（ＭＰａ）とした。
　得られた疲労強度が２３０ＭＰａ以上であれば、十分な疲労強度が得られたと判断した。疲労強度評価の結果を表５及び表６の「疲労強度」欄に示す。疲労強度が２３０ＭＰａ以上の場合、優れた疲労強度が得られたと判断した（「Ｅ」で表記）。一方、疲労強度が２３０ＭＰａ未満の場合、十分な疲労強度が得られなかったと判断した（「ＮＡ」で表記）。なお、表６の「疲労強度」欄の「－」は、疲労強度評価試験を実施していないことを意味する。
　［試験結果］
　表１～表６を参照して、試験番号１～４６の鋼材は、特徴１～特徴４を満たした。そのため、熱間加工割れ及び溶融割れが十分に抑制された。さらに、最大切削速度ＶＬ１０００は３５ｍ／分以上であり、優れた被削性が得られた。さらに、疲労強度は２３０ＭＰａ以上であり、優れた疲労強度が得られた。
　一方、試験番号４７では、Ｃ含有量が高すぎた。そのため、溶融割れが発生した。
　試験番号４８では、Ｃ含有量が低すぎた。そのため、疲労強度が低かった。
　試験番号４９では、Ｓｉ含有量が高すぎた。そのため、溶融割れが発生した。
　試験番号５０では、Ｍｎ含有量が高すぎた。そのため、被削性が低かった。
　試験番号５１では、Ｍｎ含有量が低すぎた。そのため、溶融割れが発生した。
　試験番号５２では、Ｐ含有量が高すぎた。そのため、溶融割れが発生した。
　試験番号５３では、Ｓ含有量が高すぎた。そのため、溶融割れが発生した。
　試験番号５４では、Ｓ含有量が低すぎた。そのため、被削性が低かった。
　試験番号５５では、Ｃｒ含有量が高すぎた。そのため、被削性が低かった。
　試験番号５６では、Ｂｉ含有量が高すぎた。そのため、粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２を超えた。そのため、熱間加工割れが発生した。
　試験番号５７では、Ｂｉ含有量が低すぎた。そのため、被削性が低かった。さらに、微細Ｂｉ粒子の個数密度が８０個／ｍｍ２未満であった。その結果、溶融割れが発生した。
　試験番号５８では、Ｎ含有量が高すぎた。そのため、熱間加工割れが発生した。
　試験番号５９及び６０では、ｆｎ１の値が高すぎた。つまり、ｆｎ１が式（１）を満たさなかった。そのため、十分な被削性が得られなかった。
　試験番号６１及び６２では、ｆｎ１の値が低すぎた。つまり、ｆｎ１が式（１）を満たさなかった。そのため、十分な疲労強度が得られなかった。
　試験番号６３～６５では、精錬工程において、Ｂｉ添加後攪拌終了までの時間Ｔ（分）が短すぎた。そのため、粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２を超えた。そのため、熱間加工割れが発生した。
　試験番号６６～６８では、精錬工程において、Ｂｉ添加後攪拌終了までの時間Ｔ（分）が長すぎた。そのため、微細Ｂｉ粒子の個数密度が８０個／ｍｍ２未満であり、溶融割れが発生した。
　以上、本開示の実施の形態を説明した。しかしながら、上述した実施の形態は本開示を実施するための例示に過ぎない。したがって、本開示は上述した実施の形態に限定されることなく、その趣旨を逸脱しない範囲内で上述した実施の形態を適宜変更して実施することができる。

Claims (7)

  1. 　鋼材であって、
    　質量％で、
    　Ｃ：０．０５～０．３０％、
    　Ｓｉ：０．０５～０．４５％、
    　Ｍｎ：０．３０～２．００％、
    　Ｐ：０．０３０％以下、
    　Ｓ：０．０１０～０．０９５％、
    　Ｃｒ：０．０１～２．００％、
    　Ｂｉ：０．００５１～０．１５００％、及び、
    　Ｎ：０．００３０～０．０２５０％、を含有し、
    　残部はＦｅ及び不純物からなり、式（１）を満たし、
    　前記鋼材中において、
    　円相当径が０．１～１．０μｍの微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２であり、
    　円相当径が１０．０μｍ以上の粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下である、
    　鋼材。
    　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ≦１．００　（１）
    　ここで、式中の各元素記号には、対応する元素の含有量が質量％で代入される。元素が含有されていない場合、対応する元素記号には「０」が代入される。
  2. 　鋼材であって、
    　質量％で、
    　Ｃ：０．０５～０．３０％、
    　Ｓｉ：０．０５～０．４５％、
    　Ｍｎ：０．３０～２．００％、
    　Ｐ：０．０３０％以下、
    　Ｓ：０．０１０～０．０９５％、
    　Ｃｒ：０．０１～２．００％、
    　Ｂｉ：０．００５１～０．１５００％、及び、
    　Ｎ：０．００３０～０．０２５０％、を含有し、
    　さらに、第１群～第５群からなる群から選択される１種以上を含有し、
    　残部はＦｅ及び不純物からなり、式（１）を満たし、
    　前記鋼材中において、
    　円相当径が０．１～１．０μｍの微細Ｂｉ粒子の個数密度が８０～８０００個／ｍｍ２であり、
    　円相当径が１０．０μｍ以上の粗大Ｂｉ粒子の個数密度が１０個／ｍｍ２以下である、
    　鋼材。
    　［第１群］
    　Ａｌ：０．０６０％以下、及び、
    　Ｍｇ：０．０１００％以下、からなる群から選択される１種以上
    　［第２群］
    　Ｔｉ：０．１５００％以下、
    　Ｎｂ：０．０８００％以下、
    　Ｗ：０．４０００％以下、及び、
    　Ｚｒ：０．２０００％以下、からなる群から選択される１種以上
    　［第３群］
    　Ｃａ：０．０１００％以下、
    　Ｔｅ：０．０１００％以下、
    　Ｂ：０．００５０％以下、
    　Ｓｎ：０．０１００％以下、及び、
    　希土類元素：０．０１００％以下、からなる群から選択される１種以上
    　［第４群］
    　Ｃｏ：０．０１００％以下、
    　Ｓｅ：０．０１００％以下、
    　Ｓｂ：０．０１００％以下、及び、
    　Ｉｎ：０．０１００％以下、からなる群から選択される１種以上
    　［第５群］
    　Ｖ：０．２００％以下、
    　Ｍｏ：１．００％以下、
    　Ｃｕ：０．２０％以下、及び、
    　Ｎｉ：０．２０％以下、からなる群から選択される１種以上
    　０．２５≦Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ≦１．００　（１）
    　ここで、式中の各元素記号には、対応する元素の含有量が質量％で代入される。元素が含有されていない場合、対応する元素記号には「０」が代入される。
  3. 　請求項２に記載の鋼材であって、
    　前記第１群を含有する、
    　鋼材。
  4. 　請求項２に記載の鋼材であって、
    　前記第２群を含有する、
    　鋼材。
  5. 　請求項２に記載の鋼材であって、
    　前記第３群を含有する、
    　鋼材。
  6. 　請求項２に記載の鋼材であって、
    　前記第４群を含有する、
    　鋼材。
  7. 　請求項２に記載の鋼材であって、
    　前記第５群を含有する、
    　鋼材。
PCT/JP2022/035434 2021-09-24 2022-09-22 鋼材 WO2023048248A1 (ja)