WO2023013487A1 - 多液型硬化性組成物およびその利用 - Google Patents

多液型硬化性組成物およびその利用 Download PDF

Info

Publication number
WO2023013487A1
WO2023013487A1 PCT/JP2022/028867 JP2022028867W WO2023013487A1 WO 2023013487 A1 WO2023013487 A1 WO 2023013487A1 JP 2022028867 W JP2022028867 W JP 2022028867W WO 2023013487 A1 WO2023013487 A1 WO 2023013487A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
curable composition
epoxy resin
polyoxyalkylene polymer
weight
Prior art date
Application number
PCT/JP2022/028867
Other languages
English (en)
French (fr)
Inventor
博志 神山
Original Assignee
株式会社カネカ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社カネカ filed Critical 株式会社カネカ
Priority to JP2023540281A priority Critical patent/JPWO2023013487A1/ja
Publication of WO2023013487A1 publication Critical patent/WO2023013487A1/ja

Abstract

引張特性と引き裂き強さとに優れる硬化物を提供し得る多液型硬化性組成物の提供を課題とする。特定の反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ）、エポキシ樹脂硬化剤（Ｂ）、アミノシラン（Ｃ）、およびメルカプタン化合物（Ｄ）を含むＡ剤と、エポキシ樹脂（Ｅ）を含むＢ剤と、を含み、前記Ａ剤および／または前記Ｂ剤に水酸基含有ポリオキシアルキレン系重合体（Ｆ）を含む、多液型硬化性組成物を提供する。

Description

多液型硬化性組成物およびその利用
　本発明は、多液型硬化性組成物、ならびにそれを用いた硬化物および防水材に関する。本発明はまた、多液型硬化性組成物を用いた防水構造物の製造方法に関する。
　建築業界で使われている塗膜防水材において、主剤としてポリオール樹脂（樹脂成分）を、硬化剤（架橋剤）としてポリイソシアネートを用いた、２液型ウレタン塗膜防水材がよく使用されている。その一方で、ポリイソシアネートは毒性が強く、環境への悪影響も大きいことから、ポリイソシアネートに代わる材料が求められている。
　そこで、ポリイソシアネートに代わる材料として、例えば、特許文献１には、１分子内に２個以上の反応性ケイ素基を含有する変性シリコーン化合物と、メルカプトシラン化合物と、エポキシ樹脂と、を配合する技術が開示されている。
　また、特許文献２には、特定の反応性ケイ素基を有するポリオキシアルキレン系重合体、特定の反応性ケイ素基を有する（メタ）アクリル酸エステル系重合体、およびエポキシ樹脂硬化剤、を含むＡ剤と、エポキシ樹脂、およびシラノール縮合触媒、を含むＢ剤、を含む多液型の硬化性組成物が開示されている。
日本国特開平９－２７９０４８号公報 日本国特開２０２１－２４９５８号公報
　しかしながら、上記の技術では、引張特性および引き裂き強さの両立の観点で、改善の余地があった。
　そこで、本発明の目的は、引張特性と引き裂き強さとに優れる硬化物を提供し得る多液型硬化性組成物を提供することにある。
　本発明者らは、上記課題を解決するために鋭意研究を重ねた結果、特定のポリオキシアルキレン系重合体およびエポキシ樹脂を含む多液型硬化性組成物に対して、アミノシラン（Ｃ）、メルカプタン化合物（Ｄ）、および水酸基含有ポリオキシアルキレン系重合体（Ｆ）を配合することにより、引張特性と引き裂き強さとに優れる硬化物を提供し得る多液型硬化性組成物が得られることを初めて見出し、本発明を完成させるに至った。
　したがって、本発明の一態様は、一般式（１）に示す反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ）、エポキシ樹脂硬化剤（Ｂ）、アミノシラン（Ｃ）、およびメルカプタン化合物（Ｄ）を含むＡ剤と、エポキシ樹脂（Ｅ）を含むＢ剤と、を含み、前記Ａ剤および／または前記Ｂ剤に水酸基含有ポリオキシアルキレン系重合体（Ｆ）を含む、多液型硬化性組成物である。
－Ｓｉ（Ｒ）３－ａ（Ｘ）ａ　　　（１）
　（式中、Ｒは、それぞれ独立に、炭素原子数１～２０の炭化水素基、または－ＯＳｉ（Ｒ’）３（Ｒ’は、それぞれ独立に、炭素原子数１～２０の炭化水素基である。）で示されるトリオルガノシロキシ基であり、Ｒとしての炭化水素基は、置換されていてもよく、かつ、ヘテロ含有基を有してもよい。Ｘは、それぞれ独立に、水酸基または加水分解性基である。ａは、１～３の整数である。）
　本発明の一態様によれば、引張特性と引き裂き強さに優れる硬化物を提供し得る多液型硬化性組成物を提供することができる。
　本発明の実施の一形態について、以下に詳細に説明する。なお、本明細書において特記しない限り、数値範囲を表す「Ａ～Ｂ」は、「Ａ以上、Ｂ以下」を意味する。また、本明細書中に記載された文献の全てが、本明細書中において参考文献として援用される。
　〔１．本発明の概要〕
　本発明の一実施形態に係る多液型硬化性組成物（以下、「本多液型硬化性組成物」と称する。）は、一般式（１）に示す反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ）、エポキシ樹脂硬化剤（Ｂ）、アミノシラン（Ｃ）、およびメルカプタン化合物（Ｄ）を含むＡ剤と、エポキシ樹脂（Ｅ）を含むＢ剤と、を含み、前記Ａ剤および／または前記Ｂ剤に水酸基含有ポリオキシアルキレン系重合体（Ｆ）を含む。
－Ｓｉ（Ｒ）３－ａ（Ｘ）ａ　　　（１）
　（式中、Ｒは、それぞれ独立に、炭素原子数１～２０の炭化水素基、または－ＯＳｉ（Ｒ’）３（Ｒ’は、それぞれ独立に、炭素原子数１～２０の炭化水素基である。）で示されるトリオルガノシロキシ基であり、Ｒとしての炭化水素基は、置換されていてもよく、かつ、ヘテロ含有基を有してもよい。Ｘは、それぞれ独立に、水酸基または加水分解性基である。ａは、１～３の整数である。）
　塗膜防水材では、安価な２液ウレタン製品（残存イソシアネート含有）が一般的に使用されているが、環境規制のために、非イソシアネート化が求められていた。しかし、例えば、特許文献１および２に示すように、非イソシアネート系の硬化剤を用いた場合には、引張特性と引き裂き強さとの点で改善の余地がある。特に、硬化性組成物を低粘度化かつ低コスト化するために、可塑剤および低価格のフィラーを含む場合には、上記の問題が大きく生じる。
　そこで、本発明者は、上記課題を解決し得る手段について鋭意検討を行った結果、以下の知見を得ることに成功した。
・特定のポリオキシアルキレン系重合体およびエポキシ樹脂を含む多液型硬化性組成物に対して、アミノシラン（Ｃ）、メルカプタン化合物（Ｄ）、および水酸基含有ポリオキシアルキレン系重合体（Ｆ）を配合することにより、引張特性および引き裂き強さに優れる硬化物を提供し得る多液型硬化性組成物が得られる。
・特に、上記多液型硬化性組成物が、無機フィラー（例えば、炭酸カルシウム）、可塑剤等を含む場合にも、アミノシラン（Ｃ）、メルカプタン化合物（Ｄ）、および水酸基含有ポリオキシアルキレン系重合体（Ｆ）を配合することにより、引張特性および引き裂き強さに優れる硬化物を提供し得る多液型硬化性組成物が得られる。
　したがって、本発明の一態様によると、環境に対応した、引張特性および引き裂き強さに優れる本多液型硬化性組成物を提供することができる。また、本発明の一態様によると、本多液型硬化性組成物は、安価な材料である、炭酸カルシウム（無機フィラー）、可塑剤等の含有量を増やして利用できるため、コストダウンの観点でも有利である。
　上述の通り、本発明の一態様による構成によれば、毒性の強いイソシアネートを使用することなく、引張特性および引き裂き強さが優れた防水材を製造することができる。これにより、例えば、目標１２「持続可能な消費生産形態を確保する」や目標１４「持続可能な開発のために、海・海洋資源を保全し、持続可能な形で利用する」等の持続可能な開発目標（ＳＤＧｓ）の達成に貢献できる。以下、本多液型硬化性組成物の構成について詳説する。
　〔２．多液型硬化性組成物〕
　本多液型硬化性組成物は、上述の通り、特定の反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ）、エポキシ樹脂硬化剤（Ｂ）、アミノシラン（Ｃ）、およびメルカプタン化合物（Ｄ）を含むＡ剤と、エポキシ樹脂（Ｅ）を含むＢ剤と、を含み、前記Ａ剤および／または前記Ｂ剤に水酸基含有ポリオキシアルキレン系重合体（Ｆ）を含む。
　（２－１．反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ））
　本発明の一実施形態に係るポリオキシアルキレン系重合体（Ａ）は、一般式（１）に示す反応性ケイ素基を有する。
－Ｓｉ（Ｒ）３－ａ（Ｘ）ａ　　　（１）
　（式中、Ｒは、それぞれ独立に、炭素原子数１～２０の炭化水素基、または－ＯＳｉ（Ｒ’）３（Ｒ’は、それぞれ独立に、炭素原子数１～２０の炭化水素基である。）で示されるトリオルガノシロキシ基であり、Ｒとしての炭化水素基は、置換されていてもよく、かつ、ヘテロ含有基を有してもよい。Ｘは、それぞれ独立に、水酸基または加水分解性基である。ａは、１～３の整数である。）
　Ｒの炭化水素基の炭素数は１～１０が好ましく、１～５がより好ましく、１～３がさらに好ましい。Ｒの具体例としては、例えば、メチル基、エチル基、クロロメチル基、メトキシメチル基、Ｎ，Ｎ－ジエチルアミノメチル基、を挙げることができるが、好ましくは、メチル基、エチル基、クロロメチル基、メトキシメチル基であり、より好ましくは、メチル基、メトキシメチル基である。当該構成によれば、貯蔵安定性と反応性とが両立しやすいという利点を有する。
　Ｘとしては、例えば、水酸基、ハロゲン、アルコキシ基、アシルオキシ基、ケトキシメート基、アミノ基、アミド基、酸アミド基、アミノオキシ基、メルカプト基、アルケニルオキシ基などが挙げられる。これらの中では、加水分解性が穏やかで取扱いやすいことからメトキシ基、エトキシ基などのアルコキシ基がより好ましく、メトキシ基、エトキシ基が特に好ましい。
　ポリオキシアルキレン系重合体（Ａ）が有する反応性ケイ素基としては、具体的には、トリメトキシシリル基、トリエトキシシリル基、トリス（２－プロペニルオキシ）シリル基、トリアセトキシシリル基、ジメトキシメチルシリル基、ジエトキシメチルシリル基、ジメトキシエチルシリル基、（クロロメチル）ジメトキシシリル基、（クロロメチル）ジエトキシシリル基、（メトキシメチル）ジメトキシシリル基、（メトキシメチル）ジエトキシシリル基、（Ｎ，Ｎ－ジエチルアミノメチル）ジメトキシシリル基、（Ｎ，Ｎ－ジエチルアミノメチル）ジエトキシシリル基などが挙げられるが、これらに限定されない。これらの中では、メチルジメトキシシリル基、トリメトキシシリル基、トリエトキシシリル基、（クロロメチル）ジメトキシシリル基、（メトキシメチル）ジメトキシシリル基、（メトキシメチル）ジエトキシシリル基、（Ｎ，Ｎ－ジエチルアミノメチル）ジメトキシシリル基が高い活性を示し、良好な機械物性を有する硬化物が得られるため好ましく、高剛性の硬化物が得られることから、トリメトキシシリル基、トリエトキシシリル基がより好ましく、トリメトキシシリル基がさらに好ましい。
　ポリオキシアルキレン系重合体（Ａ）は、１つの末端部位に平均して１個より多い反応性ケイ素基を有していてもよい。１つの末端部位に平均して１個より多い反応性ケイ素基を有するとは、ポリオキシアルキレン系重合体（Ａ）に、下記の一般式（２）で示されるような１つの末端部位に２個以上の反応性ケイ素基を有するポリオキシアルキレンが含まれていることを示している。すなわち、ポリオキシアルキレン系重合体（Ａ）は、１つの末端部位に２個以上の反応性ケイ素基を有するポリオキシアルキレンのみを含むものであってもよいし、１つの末端部位に２個以上の反応性ケイ素基を有するポリオキシアルキレンと、１つの末端部位に１個の反応性ケイ素基を有するポリオキシアルキレンの両方を含むものであってもよい。また、１分子のポリオキシアルキレンが有する複数の末端部位として、２個以上の反応性ケイ素基を有する末端部位と、１個の反応性ケイ素基を有する末端部位の双方があってもよい。さらに、ポリオキシアルキレン系重合体（Ａ）は、総体としては、１つの末端部位に平均して１個より多い反応性ケイ素基を有するが、反応性ケイ素基を有さない末端部位を有するポリオキシアルキレンを含むものであってもよい。
　本多液型硬化性組成物における、ポリオキシアルキレン系重合体（Ａ）の末端部位は、一般式（２）：
Figure JPOXMLDOC01-appb-C000002
 　（式中、Ｒ１、Ｒ３は、それぞれ独立に、２価の炭素数１～６の結合基であり、Ｒ１、Ｒ３に隣接するそれぞれの炭素原子と結合する原子は、炭素、酸素、窒素のいずれかである。Ｒ２、Ｒ４は、それぞれ独立に、水素、または炭素数１～１０の炭化水素基である。ｎは、１～１０の整数である。Ｒ５は、置換または非置換の炭素数１～２０の炭化水素基である。Ｘは、水酸基または加水分解性基である。ｃは、１～３の整数である。）で表されることが好ましい。
　Ｒ１、Ｒ３としては、２価の炭素数１～６の有機基であってよく、酸素原子を含んでもよく、炭化水素基であってもよい。該炭化水素基の炭素数は１～４が好ましく、１～３がより好ましく、１～２がさらに好ましい。Ｒ１の具体例としては、例えば、ＣＨ２ＯＣＨ２、ＣＨ２Ｏ、ＣＨ２を挙げることができるが、好ましくは、ＣＨ２ＯＣＨ２である。Ｒ３の具体例としては、例えば、ＣＨ２、ＣＨ２ＣＨ２を挙げることができるが、好ましくは、ＣＨ２である。
　Ｒ２、Ｒ４の炭化水素基の炭素数としては１～５が好ましく、１～３がより好ましく、１～２がさらに好ましい。Ｒ２、Ｒ４の具体例としては、例えば、水素原子、メチル基、エチル基を挙げることができるが、好ましくは、水素原子、メチル基であり、より好ましくは水素原子である。
　一般式（２）で表される末端部位は、特に好ましい態様によると、Ｒ１がＣＨ２ＯＣＨ２であり、Ｒ３がＣＨ２であり、Ｒ２およびＲ４がそれぞれ水素原子である。ｎは１～５の整数が好ましく、１～３の整数がより好ましく、１または２がさらに好ましい。ただし、ｎは、１つの値に限定されるものではなく、複数の値が混在していてもよい。
　ポリオキシアルキレン系重合体（Ａ）が有する反応性ケイ素基は、１つの末端部位に平均して１．０個より多く有していることが好ましく、１．１個以上であることがより好ましく、１．５個以上であることが更に好ましく、２．０個以上であることがより更に好ましい。また、５個以下であることが好ましく、３個以下であることがより好ましい。
　ポリオキシアルキレン系重合体（Ａ）１分子中に含まれる、１個より多くの反応性ケイ素基を有する末端部位の数は、平均して０．５個以上であることが好ましく、１．０個以上であることがより好ましく、１．１個以上であることがさらに好ましく、１．５個以上であることがより更に好ましい。また、４個以下であることが好ましく、３個以下であることがより好ましい。
　ポリオキシアルキレン系重合体（Ａ）は、末端部位以外に反応性ケイ素基を有しても良いが、末端部位にのみ有することが、高伸びで、低弾性率を示すゴム状硬化物が得られやすくなるため好ましい。
　ポリオキシアルキレン系重合体（Ａ）が有する反応性ケイ素基の１分子当たりの平均個数は、１．０個より多いことが好ましく、１．２個以上がより好ましく、１．３個以上がさらに好ましく、１．５個以上がより更に好ましく、１．７個以上が特に好ましい。また、６．０個以下が好ましく、５．５個以下がより好ましく、５．０個以下が最も好ましい。１分子当たりの反応性ケイ素基の平均個数が１．０個以下では、高強度の硬化物が得られなくなる可能性がある。１分子当たりの反応性ケイ素基の平均個数が６．０個を超えると、高伸びの硬化物が得られなくなる可能性がある。
　＜主鎖構造＞
　ポリオキシアルキレン系重合体（Ａ）の主鎖骨格には特に制限はなく、例えば、ポリオキシエチレン、ポリオキシプロピレン、ポリオキシブチレン、ポリオキシテトラメチレン、ポリオキシエチレン－ポリオキシプロピレン共重合体、ポリオキシプロピレン－ポリオキシブチレン共重合体などが挙げられる。その中でも、ポリオキシプロピレンが好ましい。
　ポリオキシアルキレン系重合体（Ａ）の数平均分子量はＧＰＣにおけるポリスチレン換算分子量において３０００～１０００００、より好ましくは３０００～５００００であり、特に好ましくは３０００～３００００である。数平均分子量が３０００未満では、反応性ケイ素基の導入量が多くなり、製造コストの点で不都合になる場合があり、１０００００を越えると、高粘度となる為に作業性の点で不都合な傾向がある。
　ポリオキシアルキレン系重合体（Ａ）の分子量としては、反応性ケイ素基導入前の有機重合体前駆体を、ＪＩＳ　Ｋ　１５５７の水酸基価の測定方法と、ＪＩＳ　Ｋ　００７０に規定されたよう素価の測定方法の原理に基づいた滴定分析により、直接的に末端基濃度を測定し、有機重合体の構造（使用した重合開始剤によって定まる分岐度）を考慮して求めた末端基換算分子量で示すことも出来る。ポリオキシアルキレン系重合体（Ａ）の末端基換算分子量は、有機重合体前駆体の一般的なＧＰＣ測定により求めた数平均分子量と上記末端基換算分子量の検量線を作成し、ポリオキシアルキレン系重合体（Ａ）のＧＰＣにより求めた数平均分子量を末端基換算分子量に換算して求めることも可能である。
　ポリオキシアルキレン系重合体（Ａ）の分子量分布（Ｍｗ／Ｍｎ）は特に限定されないが、狭いことが好ましく、２．０未満が好ましく、１．６以下がより好ましく、１．５以下がさらに好ましく、１．４以下が特に好ましく、１．２以下が最も好ましい。ポリオキシアルキレン系重合体（Ａ）の分子量分布は、ＧＰＣ測定により得られる数平均分子量と重量平均分子量から求めることが出来る。
　また、本発明のポリオキシアルキレン系重合体（Ａ）の主鎖構造は直鎖状であっても分岐状であってもよい。
　本発明の一実施形態に係るポリオキシアルキレン系重合体（Ａ）は、高粘度のポリオキシアルキレン系重合体（Ａ－１）および低粘度のポリオキシアルキレン系重合体（Ａ－２）を混合して用いることが好ましい。
　ポリオキシアルキレン系重合体（Ａ－１）の粘度は、特に限定されないが、６．０Ｐａ・ｓ～５０Ｐａ・ｓが好ましく、７．０Ｐａ・ｓ～４８Ｐａ・ｓがより好ましく、８．０Ｐａ・ｓ～４５Ｐａ・ｓがさらに好ましい。当該構成によれば、得られる多液型硬化性組成物の接着性、および硬化物の引っ張り伸びが向上するとの利点を有する。
　ポリオキシアルキレン系重合体（Ａ－２）の粘度は、特に限定されないが、１Ｐａ・ｓ～５Ｐａ・ｓが好ましく、１．５Ｐａ・ｓ～４Ｐａ・ｓがより好ましく、２Ｐａ・ｓ～３Ｐａ・ｓがさらに好ましい。当該構成によれば、得られる多液型硬化性組成物が低粘度化するとの利点を有する。
　ポリオキシアルキレン系重合体（Ａ－１）とポリオキシアルキレン系重合体（Ａ－２）の重量比（Ａ－１）：（Ａ－２）は、は９５：５～５０：５０であることが好ましい。この範囲であると、柔軟性と高いせん断接着強度を示す硬化物を得ることができる。さらに、高剛性と柔軟性を両立する点で、（Ａ－１）：（Ａ－２）は８０：２０～５０：５０であることが好ましく、７０：３０～５０：５０であることがより好ましい。
　＜ポリオキシアルキレン系重合体（Ａ）の合成方法＞
　次に、ポリオキシアルキレン系重合体（Ａ）の合成方法について説明する。
　ポリオキシアルキレン系重合体（Ａ）の主鎖への反応性ケイ素基の導入は、公知の方法で行えばよい。例えば、以下の方法が挙げられる。
　方法Ｉ：ヒドロキシ基等の官能基を有する有機重合体に、この官能基に対して反応性を示す活性基および不飽和基を有する化合物を反応させ、不飽和基を有する有機重合体を得る。次いで、得られた不飽和基を有する有機重合体に、ヒドロシリル化によって、反応性ケイ素基を有するヒドロシラン化合物を反応させる。
　方法Ｉにおいて使用し得る反応性を示す活性基および不飽和基を有する化合物としては、例えば、アリルグリシジルエーテル等の不飽和基含有エポキシ化合物、塩化アリル、塩化メタリル、臭化ビニル、臭化アリル、臭化メタリル、ヨウ化ビニル、ヨウ化アリル、ヨウ化メタリル等の炭素－炭素二重結合を有する化合物等が挙げられる。
　また、炭素－炭素三重結合を有する化合物としては、例えば、塩化プロパルギル、１－クロロ－２－ブチン、４－クロロ－１－ブチン、１－クロロ－２－オクチン、１－クロロ－２－ペンチン、１，４－ジクロロ－２－ブチン、５－クロロ－１－ペンチン、６－クロロ－１－ヘキシン、臭化プロパルギル、１－ブロモ－２－ブチン、４－ブロモ－１－ブチン、１－ブロモ－２－オクチン、１－ブロモ－２－ペンチン、１，４－ジブロモ－２－ブチン、５－ブロモ－１－ペンチン、６－ブロモ－１－ヘキシン、ヨウ化プロパルギル、１－ヨード－２－ブチン、４－ヨード－１－ブチン、１－ヨード－２－オクチン、１－ヨード－２－ペンチン、１，４－ジヨード－２－ブチン、５－ヨード－１－ペンチン、６－ヨード－１－ヘキシン等の炭素－炭素三重結合を有するハロゲン化炭化水素化合物等が挙げられる。これらの中では、塩化プロパルギル、臭化プロパルギル、およびヨウ化プロパルギルがより好ましい。
　炭素－炭素三重結合を有するハロゲン化炭化水素化合物と同時に、塩化ビニル、塩化アリル、塩化メタリル、臭化ビニル、臭化アリル、臭化メタリル、ヨウ化ビニル、ヨウ化アリル、およびヨウ化メタリルなどの炭素－炭素三重結合を有するハロゲン化炭化水素以外の不飽和結合を有する炭化水素化合物を使用してもよい。
　方法Ｉにおいて使用し得るヒドロシラン化合物としては、例えば、ハロゲン化シラン類、アルコキシシラン類、アシロキシシラン類、ケトキシメートシラン類等が挙げられる。ヒドロシラン化合物は、これらに限定されない。
　ハロゲン化シラン類としては、例えば、トリクロロシラン、メチルジクロロシラン、ジメチルクロロシラン、フェニルジクロロシラン等が挙げられる。
　アルコキシシラン類としては、例えば、トリメトキシシラン、トリエトキシシラン、トリイソプロポキシシラン、ジメトキシメチルシラン、ジエトキシメチルシラン、ジイソプロポキシメチルシラン、（メトキシメチル）ジメトキシシラン、フェニルジメトキシシラン、１－［２－（トリメトキシシリル）エチル］－１，１，３，３－テトラメチルジシロキサン等が挙げられる。
　アシロキシシラン類としては、例えば、メチルジアセトキシシラン、フェニルジアセトキシシラン等が挙げられる。
　ケトキシメートシラン類としては、例えば、ビス（ジメチルケトキシメート）メチルシラン、ビス（シクロヘキシルケトキシメート）メチルシラン等が挙げられる。
　これらの中では、ハロゲン化シラン類、およびアルコキシシラン類が特に好ましい。アルコキシシラン類は、加水分解性が穏やかで取り扱いやすいために最も好ましい。
　アルコキシシラン類の中では、入手しやすい点、硬化性、および貯蔵安定性に優れる発泡体用樹脂組成物を得やすい点、発泡体用樹脂組成物を用いて引張強度に優れる発泡体を製造しやすい点等からジメトキシメチルシランが好ましい。また、硬化性に優れる発泡体用樹脂組成物を得やすい点から、トリメトキシシラン、およびトリエトキシシランも好ましい。
　方法ＩＩ：メルカプト基および反応性ケイ素基を有する化合物を、ラジカル開始剤および／またはラジカル発生源存在下でのラジカル付加反応によって、方法Ｉと同様にして得られた不飽和基を有する有機重合体の不飽和基部位に導入する方法。
　方法ＩＩにおいて使用し得るメルカプト基および反応性ケイ素基を有する化合物としては、例えば、３－メルカプト－ｎ－プロピルトリメトキシシラン、３－メルカプト－ｎ－プロピルメチルジメトキシシラン、３－メルカプト－ｎ－プロピルトリエトキシシラン、３－メルカプト－ｎ－プロピルメチルジエトキシシラン、メルカプトメチルトリメトキシシラン、メルカプトメチルトリエトキシシラン等が挙げられる。メルカプト基および反応性ケイ素基を有する化合物は、これらに限定されない。
　方法ＩＩＩ：分子中にヒドロキシ基、エポキシ基、イソシアネート基等の官能基を有する有機重合体に、これらの官能基に対して反応性を示す官能基および反応性ケイ素基を有する化合物を反応させる方法。
　方法ＩＩＩにおいて採用し得る、ヒドロキシ基を有する有機重合体と、イソシアネート基および反応性ケイ素基を有する化合物とを反応させる方法としては、特に限定されないが、例えば、特開平３－４７８２５号公報に示される方法等が挙げられる。
　方法ＩＩＩにおいて使用し得る、イソシアネート基および反応性ケイ素基を有する化合物としては、例えば、３－イソシアナト－ｎ－プロピルトリメトキシシラン、３－イソシアナト－ｎ－プロピルメチルジメトキシシラン、３－イソシアナト－ｎ－プロピルトリエトキシシラン、３－イソシアナト－ｎ－プロピルメチルジエトキシシラン、イソシアネトメチルトリメトキシシラン、イソシアナトメチルトリエトキシシラン、イソシアナトメチルジメトキシメチルシラン、イソシアナトメチルジエトキシメチルシラン等があげられる。イソシアネート基および反応性ケイ素基を有する化合物はこれらに限定されない。
　トリメトキシシラン等の１つのケイ素原子に３個の加水分解性基が結合しているシラン化合物は不均化反応が進行する場合がある。不均化反応が進むと、ジメトキシシランのような不安定な化合物が生じ、取り扱いが困難となることがある。しかし、３－メルカプト－ｎ－プロピルトリメトキシシランや３－イソシアナト－ｎ－プロピルトリメトキシシランでは、このような不均化反応は進行しない。このため、ケイ素含有基としてトリメトキシシリル基等の３個の加水分解性基が１つのケイ素原子に結合している基を用いる場合には、方法ＩＩまたは方法ＩＩＩの方法を用いることが好ましい。
　一方、下記式（２ａ）で表されるシラン化合物は不均化反応が進まない。
Ｈ－（ＳｉＲ２ａ ２Ｏ）ｍＳｉＲ２ａ ２－Ｒ３ａ－ＳｉＸ３　　　（２ａ）
　ここで、式（２ａ）において、Ｘは式（１ａ）と同じである。２ｍ＋２個のＲ２ａはそれぞれ独立に式（１ａ）のＲ１ａと同じである。Ｒ３ａは、炭素原子数１以上２０以下の置換または非置換の２価の炭化水素基を示す。ｍは０以上１９以下の整数を示す。
　このため、方法Ｉで、３個の加水分解性基が１つのケイ素原子に結合している基を導入する場合には、式（２ａ）で表されるシラン化合物を用いることが好ましい。入手性およびコストの点から、２ｍ＋２個のＲ２ａとしては、それぞれ独立に、炭素原子数１以上２０以下の炭化水素基が好ましく、炭素原子数１以上８以下の炭化水素基がより好ましく、炭素原子数１以上４以下の炭化水素基がさらに好ましい。Ｒ３ａとしては、炭素原子数１以上１２以下の２価の炭化水素基が好ましく、炭素原子数２以上８以下の２価の炭化水素基がより好ましく、炭素原子数２の２価の炭化水素基がさらに好ましい。ｍは１が最も好ましい。
　式（２ａ）で示されるシラン化合物としては、例えば、１－［２－（トリメトキシシリル）エチル］－１，１，３，３－テトラメチルジシロキサン、１－［２－（トリメトキシシリル）プロピル］－１，１，３，３－テトラメチルジシロキサン、１－［２－（トリメトキシシリル）ヘキシル］－１，１，３，３－テトラメチルジシロキサン等が挙げられる。
　上記の方法Ｉまたは方法ＩＩＩにおいて、末端にヒドロキシ基を有する有機重合体と、イソシアネート基および反応性ケイ素基を有する化合物とを反応させる方法は、比較的短い反応時間で高い転化率が得られるために好ましい。さらに、方法Ｉで得られた反応性ケイ素基を有する有機重合体は、方法ＩＩＩで得られる反応性ケイ素基を有する有機重合体よりも低粘度であり、作業性のよい発泡体用樹脂組成物が得られること、また、方法ＩＩで得られる反応性ケイ素基を有する有機重合体は、メルカプトシランに基づく臭気が強いことから、方法Ｉが特に好ましい。
　反応性ケイ素基を有するポリオキシアルキレン系重合体としては、例えば、特公昭４５－３６３１９号公報、特公昭４６－１２１５４号公報、特開昭５０－１５６５９９号公報、特開昭５４－６０９６号公報、特開昭５５－１３７６７号公報、特開昭５５－１３４６８号公報、特開昭５７－１６４１２３号公報、特公平３－２４５０号公報、米国特許３６３２５５７号、米国特許４３４５０５３号、米国特許４３６６３０７号、米国特許４９６０８４４号等の各公報に提案されている重合体が挙げられる。また、特開昭６１－１９７６３１号公報、特開昭６１－２１５６２２号公報、特開昭６１－２１５６２３号公報、特開昭６１－２１８６３２号公報、特開平３－７２５２７号公報、特開平３－４７８２５号公報、特開平８－２３１７０７号公報の各公報に提案されている数平均分子量６，０００以上、分子量分布（Ｍｗ／Ｍｎ）が１．６以下や１．３以下の高分子量で分子量分布が狭い反応性ケイ素基を有するポリオキシアルキレン系重合体等も好ましい。このような反応性ケイ素基を有するポリオキシアルキレン系重合体は単独で使用してもよく、２種以上を併用してもよい。
　ポリオキシアルキレン系重合体の１つの末端部位に平均して１．０個より多い反応性ケイ素基を導入する合成方法について、以下に説明する。
　１つの末端部位に平均して１．０個より多い反応性ケイ素基を有しているポリオキシアルキレン系重合体（Ａ）は、重合によって得られた水酸基末端重合体の１つの末端に２個以上の炭素－炭素不飽和結合を導入した後、炭素－炭素不飽和結合と反応する反応性ケイ素基含有化合物を反応させて得ることが好ましい。
　（重合）
　ポリオキシアルキレン系重合体（Ａ）は、亜鉛ヘキサシアノコバルテートグライム錯体等の複合金属シアン化物錯体触媒を用いた、水酸基を有する開始剤にエポキシ化合物を重合させる方法が好ましい。
　水酸基を有する開始剤としては、エチレングリコール、プロピレングリコール、グリセリン、ペンタエリスリトール、低分子量のポリオキシプロピレングリコール、ポリオキシプロピレントリオール、アリルアルコール、ポリプロピレンモノアリルエーテル、ポリプロピレンモノアルキルエーテル等の水酸基を１個以上有するものが挙げられる。
　エポキシ化合物としては、エチレンオキサイド、プロピレンオキサイド、等のアルキレンオキサイド類、メチルグリシジルエーテル、アリルグリシジルエーテル、等のグリシジルエーテル類、等が挙げられる。このなかでもプロピレンオキサイドが好ましい。
　（炭素－炭素不飽和結合の導入）
　１つの末端に２個以上の炭素－炭素不飽和結合を導入する方法としては、水酸基末端重合体に、アルカリ金属塩を作用させた後、先ず炭素－炭素不飽和結合を有するエポキシ化合物を反応させ、次いで炭素－炭素不飽和結合を有するハロゲン化炭化水素化合物を反応させる方法を用いるのが好ましい。この方法を用いることで、重合体主鎖の分子量や分子量分布を重合条件によって制御しつつ、さらに反応性基の導入を効率的かつ安定的に行うことが可能となる。
　本発明で用いるアルカリ金属塩としては、水酸化ナトリウム、ナトリウムメトキシド、ナトリウムエトキシド、水酸化カリウム、カリウムメトキシド、カリウムエトキシドが好ましく、ナトリウムメトキシド、カリウムメトキシドがより好ましい。入手性の点でナトリウムメトキシドが特に好ましい。
　アルカリ金属塩を作用させる際の温度としては、５０℃以上１５０℃以下が好ましく、１１０℃以上１４０℃以下がより好ましい。アルカリ金属塩を作用させる際の時間としては、１０分以上５時間以下が好ましく、３０分以上３時間以下がより好ましい。
　本発明で用いる炭素－炭素不飽和結合を有するエポキシ化合物として、特に一般式（３）：
Figure JPOXMLDOC01-appb-C000003
 　（式中のＲ１、Ｒ２は上記と同じである。）で表される化合物が好適に使用できる。具体的には、アリルグリシジルエーテル、メタリルグリシジルエーテル、グリシジルアクリレート、グリシジルメタクリレート、ブタジエンモノオキシド、１，４－シクロペンタジエンモノエポキシドが反応活性の点から好ましく、アリルグリシジルエーテルが特に好ましい。
　本発明で用いる炭素－炭素不飽和結合を有するエポキシ化合物の添加量は、重合体に対する炭素－炭素不飽和結合の導入量や反応性を考慮して任意の量を使用できる。特に、水酸基末端重合体が有する水酸基に対するモル比は、０．２以上であることが好ましく、０．５以上がより好ましい。また、５．０以下であることが好ましく、２．０以下であることがより好ましい。
　本発明において、水酸基を含有する重合体に対し炭素－炭素不飽和結合を有するエポキシ化合物を開環付加反応させる際の反応温度は、反応温度は６０℃以上、１５０℃以下であることが好ましく、１１０℃以上、１４０℃以下であることがより好ましい。
　本発明で用いる炭素－炭素不飽和結合を有するハロゲン化炭化水素化合物としては、塩化ビニル、塩化アリル、塩化メタリル、臭化ビニル、臭化アリル、臭化メタリル、ヨウ化ビニル、ヨウ化アリル、ヨウ化メタリルなどが挙げられ、取り扱いの容易さから塩化アリル、塩化メタリルを用いることがより好ましい。
　上記の炭素－炭素不飽和結合を有するハロゲン化炭化水素化合物の添加量は、特に制限はないが、水酸基末端重合体が有する水酸基に対するモル比は、０．７以上が好ましく、１．０以上がより好ましい。また、５．０以下が好ましく、２．０以下がより好ましい。
　炭素－炭素不飽和結合を有するハロゲン化炭化水素化合物を反応させる際の温度としては、５０℃以上１５０℃以下が好ましく、１１０℃以上１４０℃以下がより好ましい。反応時間としては、１０分以上５時間以下が好ましく、３０分以上３時間以下がより好ましい。
　（反応性ケイ素基の導入）
　反応性ケイ素基の導入方法は、上記で説明した３種類の方法が利用でき、特に限定されず、他の公知の方法を利用することができる。
　（２－２．エポキシ樹脂硬化剤（Ｂ））
　本多液型硬化性組成物における、エポキシ樹脂硬化剤（Ｂ）は、第三級アミンを有するエポキシ樹脂硬化剤であることが好ましい。当該構成によれば、硬化物の引き裂き強さが向上するという利点を有する。
　第三級アミンを有するエポキシ樹脂硬化剤（Ｂ）としては、第三級アミンを有する化合物であれば使用できる。具体的には、例えば、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラメチル－１，３－ジミノプロパン、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラメチル－１，６－ジミノヘキサン、Ｎ，Ｎ－ジメチルベンジルアミン、Ｎ－メチル－Ｎ－（ジメチルアミノプロピル）アミノエタノール、２，４，６－トリス（ジメチルアミノメチル）フェノール、トリプロピルアミン、ＤＢＵ、ＤＢＮ、およびこれら第三級アミン類の塩類を例示することができるが、これらに限定されるものではない。これらは、１種のみを使用してもよく、２種以上を併用してもよく、（Ｂ）成分以外の公知のエポキシ樹脂硬化剤をさらに添加してもよい。
　第三級アミンを有するエポキシ樹脂硬化剤（Ｂ）は、芳香族アミンであることが好ましく、アミノ基を３つ以上有することがさらに好ましい。具体的には、２，４，６－トリス（ジメチルアミノメチル）フェノールを例示することができる。
　エポキシ樹脂硬化剤（Ｂ）の含有量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～１０重量部であることが好ましく、０．５～９．０重量部であることがより好ましく、１．０～８．０重量部であることがさらに好ましく、２．０～７．０重量部であることが特に好ましい。エポキシ樹脂硬化剤（Ｂ）の含有量が上記の範囲内であれば、硬化物の引き裂き強さ向上と低コスト化とが両立し易いという利点を有する。
　（２－３．アミノシラン（Ｃ））
　本多液型硬化性組成物における、アミノシラン（Ｃ）としては、例えば、γ－アミノプロピルトリエトキシシラン、Ｎ－β－（アミノエチル）－γ－アミノプロピルトリメトキシシラン、Ｎ－β－（アミノエチル）－γ－アミノプロピルメチルジメトキシシラン等が挙げられる。これらは、１種のみを使用してもよく、２種以上を併用してもよい。市販品として、例えば、Ｓｉｌｑｕｅｓｔ　Ａ－１１２０（モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製）、Ｓｉｌｑｕｅｓｔ　Ａ－１１１０（モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製）、ＫＢＭ－６０２（信越化学工業株式会社製）、ＫＢＭ－６０３（信越化学工業株式会社製）、ＫＢＭ－９０３（信越化学工業株式会社製）等を用いてもよい。
　アミノシラン（Ｃ）の含有量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～５．０重量部であることが好ましく、０．２～４．５重量部であることがより好ましく、０．３～４．０重量部であることがさらに好ましく、０．４～３．８重量部であることが特に好ましい。アミノシラン（Ｃ）の含有量が上記の範囲内であれば、硬化物の引き裂き強さ向上と低コスト化とが両立し易いという利点を有する。
　（２－４．メルカプタン化合物（Ｄ））
　本多液型硬化性組成物における、メルカプタン化合物（Ｄ）としては、例えば、ｎ－ドデシルメルカプタン、ｔｅｒｔ－ドデシルメルカプタン、ラウリルメルカプタン、トリメチロールプロパントリス（３－メルカプトプロピオネート）、ペンタエリスリトールテトラキス（３－メルカプトプロピオネート）、３－メルカプトプロピルトリメトキシシラン、３－メルカプトプロピルメチルジメトキシシラン、３－メルカプトプロピルクロロメチルジメトキシシラン、３－メルカプトプロピルメトキシメチルジメトキシシラン、（メルカプトメチル）ジメトキシメチルシラン、（メルカプトメチル）トリメトキシシラン等が挙げられる。これらは、１種のみを使用してもよく、２種以上を併用してもよい。市販品として、例えば、Ｚ６０６２（ダウ・ケミカル日本株式会社製）、チオカルコール２０（花王株式会社製）、ＫＢＭ－８０２（信越化学工業株式会社製）、ＫＢＭ－８０３（信越化学工業株式会社製）等を用いてもよい。
　メルカプタン化合物（Ｄ）の含有量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、０．２～５．０重量部であることが好ましく、０．２２～４．５重量部であることがより好ましく、０．２４～４．０重量部であることがより好ましく、０．２６～３．８重量部であることが特に好ましい。メルカプタン化合物（Ｄ）の含有量が上記の範囲内であれば、硬化物の引き裂き強さ向上と低コスト化とが両立し易いという利点を有する。
　（２－５．エポキシ樹脂（Ｅ））
　本多液型硬化性組成物における、前記エポキシ樹脂（Ｅ）は、エポキシ基を１分子中に少なくとも２個以上有するエポキシ樹脂であることが好ましい。当該構成によれば、硬化物の引き裂き強さが向上するという利点を有する。
　エポキシ樹脂（Ｅ）としては、エピクロルヒドリン－ビスフェノールＡ型エポキシ樹脂、エピクロルヒドリン－ビスフェノールＦ型エポキシ樹脂、テトラブロモビスフェノールＡのグリシジルエーテル等の難燃型エポキシ樹脂、ノボラック型エポキシ樹脂、水添ビスフェノールＡ型エポキシ樹脂、ビスフェノールＡプロピレンオキシド付加物のグリシジルエーテル型エポキシ樹脂、ｐ－オキシ安息香酸グリシジルエーテルエステル型エポキシ樹脂、ｍ－アミノフェノール系エポキシ樹脂、ジアミノジフェニルメタン系エポキシ樹脂、ウレタン変性エポキシ樹脂、各種脂環式エポキシ樹脂、Ｎ，Ｎ－ジグリシジルアニリン、Ｎ，Ｎ－ジグリシジル－ｏ－トルイジン、トリグリシジルイソシアヌレート、ポリアルキレングリコールジグリシジルエーテル、グリセリン等の多価アルコールのグリシジルエーテル、ヒダントイン型エポキシ樹脂、石油樹脂等の不飽和重合体のエポキシ化物等が例示されるが、これらに限定されるものではなく、一般に使用されているエポキシ樹脂が使用され得る。エポキシ基を１分子中に少なくとも２個有するエポキシ樹脂が、硬化に際し反応性が高く、また硬化物が３次元的網目をつくりやすい等の点から好ましい。さらに好ましいものとしては、ビスフェノールＡ型エポキシ樹脂類、ノボラック型エポキシ樹脂等が挙げられる。
　エポキシ樹脂（Ｅ）の含有量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との重量比（Ａ）：（Ｅ）が、９０：１０～５０：５０であることが好ましい。（Ａ）の割合が９０％より大きくなると強度が低下し、５０％より小さくなると柔軟性が低下し、硬くなりすぎる。さらに、８０：２０～６０：４０が柔軟性と強度のバランスの点でより好ましい。
　（２－６．水酸基含有ポリオキシアルキレン系重合体（Ｆ））
　本多液型硬化性組成物は、前記Ａ剤および／または前記Ｂ剤に水酸基含有ポリオキシアルキレン系重合体（Ｆ）を含む。本多液型硬化性組成物において、水酸基含有ポリオキシアルキレン系重合体（Ｆ）は、可塑剤として機能する。本多液型硬化性組成物が水酸基含有ポリオキシアルキレン系重合体（Ｆ）を含むことにより、当該組成物の粘度低下、コスト低下や、当該組成物からの硬化物の硬度、弾性率等の特性を調整するとともに、当該硬化物にアルキッド系塗料を塗装した場合の塗膜を乾燥させやすくすることができる。
　水酸基含有ポリオキシアルキレン系重合体（Ｆ）は、ポリオキシアルキレン系重合体（Ａ）の可塑剤として用いられるため、オキシアルキレン系重合体（Ａ）が有する反応性ケイ素基のような室温で架橋しうる基を含まないことが好ましい。
　水酸基含有ポリオキシアルキレン系重合体（Ｆ）の主鎖は、主鎖を構成する単量体単位の６０％以上、好ましくは８０％以上が、一般式：
－Ｒｆ－Ｏ－
　（式中、Ｒｆは２価の炭化水素基であるが、その大部分が炭素数３または４のアルキレン基であるとき最も好ましい）で示される繰返し単位を有するものであるのが好ましい。Ｒｆの具体例としては、
Figure JPOXMLDOC01-appb-C000004
 等が挙げられる。水酸基含有ポリオキシアルキレン系重合体（Ｆ）の分子鎖は１種だけの繰返し単位からなっていてもよいし、２種以上の繰返し単位からなっていてもよいが、Ｒｆとしては特に、
Figure JPOXMLDOC01-appb-C000005
 で示されるものであるのが好ましい。
　水酸基含有ポリオキシアルキレン系重合体（Ｆ）の具体例としては、特に限定されないが、例えば、ポリオキシエチレン、ポリオキシプロピレン、ポリオキシブチレン、ポリオキシテトラメチレン、ポリオキシエチレン－ポリオキシプロピレン共重合体、ポリオキシプロピレン－ポリオキシブチレン共重合体等が挙げられる。中でも、時間経過に伴って生じるブリードを抑制する観点から、ポリオキシプロピレンが好ましい。
　水酸基含有ポリオキシアルキレン系重合体（Ｆ）は、反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ）の可塑剤として作用するものであるため、その数平均分子量は、ポリオキシアルキレン系重合体（Ａ）より小さいことが必要である。水酸基含有ポリオキシアルキレン系重合体（Ｆ）の数平均分子量は、３００以上が好ましく、８００以上がより好ましく、１０００以上がさらに好ましい。上限は、１５０００以下が好ましく、１００００以下がより好ましく、８０００以下がさらに好ましく、５０００以下が特に好ましい。水酸基含有ポリオキシアルキレン系重合体（Ｆ）の数平均分子量が３００以上であると、揮発し難いとの効果を奏する。また、水酸基含有ポリオキシアルキレン系重合体（Ｆ）の数平均分子量が１５０００以下であると、多液型硬化性組成物が低粘度化し易いとの効果を奏する。水酸基含有ポリオキシアルキレン系重合体（Ｆ）の数平均分子量は、末端基分析によって得られた数平均分子量に相当する分子量である。
　水酸基含有ポリオキシアルキレン系重合体（Ｆ）の分子量分布は、小さい程粘度が低くなり、好ましい。水酸基含有ポリオキシアルキレン系重合体（Ｆ）の分子量分布は、例えば、Ｍｗ／Ｍｎが１．６以下であり、好ましくは、１．５以下である。水酸基含有ポリオキシアルキレン系重合体（Ｆ）の分子量分布（Ｍｗ／Ｍｎ）は、ＧＰＣ（ポリスチレン換算）を用いて測定する。
　水酸基含有ポリオキシアルキレン系重合体（Ｆ）の含有量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、５重量部以上が好ましく、１０重量部以上がより好ましく、２０重量部以上がさらに好ましい。上限は、１５０重量部以下が好ましく、１００重量部以下がより好ましく、５０重量部以下がさらに好ましい。水酸基含有ポリオキシアルキレン系重合体（Ｆ）の含有量が５重量部以上であると、可塑剤としての効果が十分に発揮できる。また、水酸基含有ポリオキシアルキレン系重合体（Ｆ）の含有量が１５０重量部以下であると、硬化物の適度な機械強度が得られる。なお、水酸基含有ポリオキシアルキレン系重合体（Ｆ）は、重合体製造時に配合することも可能である。
　水酸基含有ポリオキシアルキレン系重合体（Ｆ）は、通常の苛性アルカリを用いる重合法によって製造されたものでよいが、亜鉛ヘキサシアノコバルテート等の複合金属シアン化物錯体を触媒として用いる重合法によって製造されたものも用いることができる。
　（２－７．無機フィラー）
　本多液型硬化性組成物は、無機フィラーをさらに含むことが好ましい。無機フィラーは、安価な材料であるため、コストダウンを可能とする。
　無機フィラーとしては、特に限定されないが、例えば、炭酸カルシウム、炭酸マグネシウム、炭酸バリウム、硫酸バリウム、ケイソウ土、焼成クレー、クレー、タルク、バライト、無水石膏、酸化チタン、ベントナイト、有機ベントナイト、酸化第二鉄、アルミニウム微粉末、フリント粉末、酸化亜鉛、活性亜鉛華、マイカ、亜鉛華、鉛白、リトポン、硫化亜鉛、シラスバルーン、ガラスミクロバルーン等が挙げられる。中でも、より安価であるという観点から、炭酸カルシウムが好ましい。これら無機フィラーは、単独で使用してもよく、２種以上を組み合わせて使用してもよい。
　無機フィラーの含有量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、例えば、５０～３００重量部であることが好ましく、５０～２００重量部であることがより好ましく、５０重量部～１８０重量部であることがより好ましく、６０～１６０重量部であることがより好ましく、７０～１５０重量部であることがさらに好ましい。無機フィラーの含有量が上記の範囲内であれば、多液型硬化性組成物の低粘度化と低コスト化とが両立しやすいという利点を有する。
　無機フィラーは、Ａ剤に含まれてもよいし、Ｂ剤に含まれてもよいし、Ａ剤およびＢ剤の両方に含まれてもよい。無機フィラーは、吸着水の観点から、好ましくは、Ｂ液（Ｂ剤）に含まれる。
　（２－８．硬化触媒）
　本多液型硬化性組成物は、硬化触媒をさらに含むことが好ましい。硬化触媒としては、縮合触媒として使用し得るものである限り、特に制限はなく、任意のものを使用し得る。
　硬化触媒としては、例えば、ジブチル錫ジラウレート、ジブチル錫ジアセテート、ジブチル錫ジエチルヘキサノエート、ジブチル錫ジオクテート、ジブチル錫ジメチルマレート、ジブチル錫ジエチルマレート、ジブチル錫ジブチルマレート、ジブチル錫ジイソオクチルマレート、ジブチル錫ジトリデシルマレート、ジブチル錫ジベンジルマレート、ジブチル錫マレエート、ジオクチル錫ジアセテート、ジオクチル錫ジステアレート、ジオクチル錫ジラウレート、ジオクチル錫ジエチルマレート、ジオクチル錫ジイソオクチルマレート等のジアルキル錫ジカルボキシレート類、例えば、ジブチル錫ジメトキシド、ジブチル錫ジフェノキシド等のジアルキル錫アルコキサイド類、例えば、ジブチル錫ジアセチルアセトナート、ジブチル錫ジエチルアセトアセテートなどのジアルキル錫の分子内配位性誘導体類、例えば、ジブチル錫オキサイドやジオクチル錫オキサイド等のジアルキル錫オキサイドと例えば、ジオクチルフタレート、ジイソデシルフタレート、メチルマレエート等のエステル化合物との反応物、ジアルキル錫オキサイド、カルボン酸およびアルコール化合物を反応させて得られる錫化合物、例えば、ジブチル錫ビストリエトキシシリケート、ジオクチル錫ビストリエトキシシリケート等のジアルキル錫オキサイドとシリケート化合物との反応物、およびこれらジアルキル錫化合物のオキシ誘導体（スタノキサン化合物）等の４価の錫化合物類；例えば、オクチル酸錫、ナフテン酸錫、ステアリン酸錫、フェルザチック酸錫等の２価の錫化合物類、あるいはこれらと後述のラウリルアミン等のアミン系化合物との反応物および混合物；例えば、モノブチル錫トリスオクトエートやモノブチル錫トリイソプロポキシド等のモノブチル錫化合物やモノオクチル錫化合物等のモノアルキル錫類；例えば、テトラブチルチタネート、テトラプロピルチタネート、テトラ（２－エチルヘキシル）チタネート、イソプロポキシチタンビス（エチルアセトアセテート）等のチタン酸エステル類；アルミニウムトリスアセチルアセトナート、アルミニウムトリスエチルアセトアセテート、ジ－イソプロポキシアルミニウムエチルアセトアセテート等の有機アルミニウム化合物類；カルボン酸ビスマス、カルボン酸鉄、カルボン酸チタニウム、カルボン酸鉛、カルボン酸バナジウム、カルボン酸ジルコニウム、カルボン酸カルシウム、カルボン酸カリウム、カルボン酸バリウム、カルボン酸マンガン、カルボン酸セリウム、カルボン酸ニッケル、カルボン酸コバルト、カルボン酸亜鉛、カルボン酸アルミニウム等のカルボン酸（２－エチルヘキサン酸、ネオデカン酸、バーサチック酸、オレイン酸、ナフテン酸等）金属塩、あるいはこれらと後述のラウリルアミン等のアミン系化合物との反応物および混合物；ジルコニウムテトラアセチルアセトナート、ジルコニウムトリブトキシアセチルアセトナート、ジブトキシジルコニウムジアセチルアセトナート、ジルコニウムアセチルアセトナートビス（エチルアセトアセテート）、チタンテトラアセチルアセトナート等のキレート化合物類；メチルアミン、エチルアミン、プロピルアミン、イソプロピルアミン、ブチルアミン、アミルアミン、ヘキシルアミン、オクチルアミン、２－エチルヘキシルアミン、ノニルアミン、デシルアミン、ラウリルアミン、ペンタデシルアミン、セチルアミン、ステアリルアミン、シクロヘキシルアミン等の脂肪族第一アミン類；ジメチルアミン、ジエチルアミン、ジプロピルアミン、ジイソプロピルアミン、ジブチルアミン、ジアミルアミン、ジオクチルアミン、ジ（２－エチルヘキシル）アミン、ジデシルアミン、ジラウリルアミン、ジセチルアミン、ジステアリルアミン、メチルステアリルアミン、エチルステアリルアミン、ブチルステアリルアミン等の脂肪族第二アミン類；トリアミルアミン、トリヘキシルアミン、トリオクチルアミン等の脂肪族第三アミン類；トリアリルアミン、オレイルアミン、などの脂肪族不飽和アミン類；ラウリルアニリン、ステアリルアニリン、トリフェニルアミン等の芳香族アミン類；および、その他のアミン類として、モノエタノールアミン、ジエタノールアミン、トリエタノールアミン、ジエチレントリアミン、トリエチレンテトラミン、オレイルアミン、シクロヘキシルアミン、ベンジルアミン、ジエチルアミノプロピルアミン、キシリレンジアミン、エチレンジアミン、ヘキサメチレンジアミン、トリエチレンジアミン、グアニジン、ジフェニルグアニジン、２，４，６－トリス（ジメチルアミノメチル）フェノール、モルホリン、Ｎ－メチルモルホリン、２－エチル－４－メチルイミダゾール、１，８－ジアザビシクロ（５，４，０）ウンデセン－７（ＤＢＵ）等のアミン系化合物、あるいはこれらのアミン系化合物のカルボン酸等との塩；ラウリルアミンとオクチル酸錫の反応物あるいは混合物のようなアミン系化合物と有機錫化合物との反応物および混合物；過剰のポリアミンと多塩基酸とから得られる低分子量ポリアミド樹脂；過剰のポリアミンとエポキシ化合物との反応生成物；γ－アミノプロピルトリメトキシシラン、γ－アミノプロピルトリエトキシシラン、γ－アミノプロピルトリイソプロポキシシラン、γ－アミノプロピルメチルジメトキシシラン、γ－アミノプロピルメチルジエトキシシラン、Ｎ－（β－アミノエチル）アミノプロピルトリメトキシシラン、Ｎ－（β－アミノエチル）アミノプロピルメチルジメトキシシラン、Ｎ－（β－アミノエチル）アミノプロピルトリエトキシシラン、Ｎ－（β－アミノエチル）アミノプロピルメチルジエトキシシラン、Ｎ－（β－アミノエチル）アミノプロピルトリイソプロポキシシラン、γ－ウレイドプロピルトリメトキシシラン、Ｎ－フェニル－γ－アミノプロピルトリメトキシシラン、Ｎ－ベンジル－γ－アミノプロピルトリメトキシシラン、Ｎ－ビニルベンジル－γ－アミノプロピルトリエトキシシラン等を挙げることができる。また、これらを変性した誘導体である、アミノ変性シリルポリマー、シリル化アミノポリマー、不飽和アミノシラン錯体、フェニルアミノ長鎖アルキルシラン、アミノシリル化シリコーン等のアミノ基を有するシランカップリング剤；等のシラノール縮合触媒、さらにはフェルザチック酸等の脂肪酸や有機酸性リン酸エステル化合物等他の酸性触媒、塩基性触媒等の公知のシラノール縮合触媒等が例示できる。これら硬化触媒は、単独で使用してもよく、２種以上を組み合わせて使用してもよい。
　硬化触媒の含有量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、例えば、０．１～５重量部であることが好ましく、０．２～２重量部であることがより好ましく、０．３～１重量部であることがさらに好ましい。硬化触媒の含有量が上記の範囲内であれば、硬化性と低コスト化とが両立しやすいという利点を有する。
　（２－９．脱水剤）
　本多液型硬化性組成物は、さらに、脱水剤を含むことが好ましい。本多液型硬化性組成物が脱水剤を含むことにより、貯蔵安定性に優れるという利点を有する。
　脱水剤としては、特に限定されないが、例えば、ビニルシラン、トシルイソシアネート、ビニルトリメトキシシラン、酸化カルシウム、ゼオライト、ｐ－トルエンスルホニルイソシアネート、３－エチル－２－メチル－２－（３－メチルブチル）－１，３－オキサゾリジン等が挙げられる。これら脱水剤は、単独で使用してもよく、２種以上を組み合わせて使用してもよい。
　脱水剤の含有量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、例えば、０．１～１０重量部であり、０．１～５．０重量部であることが好ましく、１．０～３．０重量部であることがより好ましい。脱水剤の含有量がポリオキシアルキレン系重合体（Ａ）１００重量部に対して０．１重量部以上であると、水の存在下で反応するポリオキシアルキレン系重合体（Ａ）が過剰に反応してしまうことを防ぐことができるという利点を有する。また、脱水剤の含有量がポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して３．０重量部以下であると、貯蔵安定性と低コスト化とが両立し易いという利点を有する。
　（２－１０．その他の成分）
　本多液型硬化性組成物は、上記の他に、添加剤として、充填剤、接着性付与剤、タレ防止剤、酸化防止剤、光安定剤、紫外線吸収剤、粘着付与樹脂、低分子可塑剤、その他の樹脂等を添加してもよい。また、本多液型硬化性組成物には、硬化性組成物または硬化物の諸物性の調整を目的として、必要に応じて各種添加剤を添加してもよい。このような添加物としては、例えば、溶剤、希釈剤、光硬化性物質、酸素硬化性物質、表面性改良剤、シリケート、硬化性調整剤、ラジカル禁止剤、金属不活性化剤、オゾン劣化防止剤、リン系過酸化物分解剤、滑剤、顔料、防かび剤、難燃剤、発泡剤等が挙げられる。
　＜充填剤＞
　本多液型硬化性組成物には、無機フィラー以外の種々の充填剤を配合することができる。充填剤としては、例えば、ＰＶＣ粉末、ＰＭＭＡ粉末等が挙げられる。
　充填剤の使用量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、０．５～１００重量部が好ましく、１～６０重量部がより好ましい。
　本多液型硬化性組成物の軽量化（低比重化）の目的で、有機バルーンを添加してもよい。
　＜接着性付与剤＞
　本多液型硬化性組成物には、接着性付与剤を添加することができる。
　接着性付与剤としては、シランカップリング剤、シランカップリング剤の反応物を添加することができる。
　シランカップリング剤の具体例としては、γ－アミノプロピルトリメトキシシラン、γ－アミノプロピルメチルジメトキシシラン、Ｎ－β－アミノエチル－γ－アミノプロピルトリメトキシシラン、Ｎ－β－アミノエチル－γ－アミノプロピルメチルジメトキシシラン、Ｎ－フェニル－γ－アミノプロピルトリメトキシシラン、（２－アミノエチル）アミノメチルトリメトキシシランなどのアミノ基含有シラン類；γ－イソシアネートプロピルトリメトキシシラン、γ－イソシアネートプロピルトリエトキシシラン、γ－イソシアネートプロピルメチルジメトキシシラン、α－イソシアネートメチルトリメトキシシラン、α－イソシアネートメチルジメトキシメチルシラン等のイソシアネート基含有シラン類；γ－メルカプトプロピルトリメトキシシラン、γ－メルカプトプロピルトリエトキシシラン、γ－メルカプトプロピルメチルジメトキシシラン等のメルカプト基含有シラン類；γ－グリシドキシプロピルトリメトキシシラン、β－（３，４－エポキシシクロヘキシル）エチルトリメトキシシラン等のエポキシ基含有シラン類、が挙げられる。
　上記接着性付与剤は１種類のみで使用しても良いし、２種類以上混合使用しても良い。また、各種シランカップリング剤の反応物も使用できる。
　シランカップリング剤の使用量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～２０重量部が好ましく、特に０．５～１０重量部が好ましい。
　＜タレ防止剤＞
　本多液型硬化性組成物には、必要に応じてタレを防止し、作業性を良くするためにタレ防止剤を添加しても良い。タレ防止剤としては特に限定されないが、例えば、ポリアミドワックス類；水添ヒマシ油誘導体類；ステアリン酸カルシウム、ステアリン酸アルミニウム、ステアリン酸バリウム等の金属石鹸類等が挙げられる。これらタレ防止剤は単独で用いてもよく、２種以上併用してもよい。
　タレ防止剤の使用量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～２０重量部が好ましい。
　＜酸化防止剤＞
　本多液型硬化性組成物には、酸化防止剤（老化防止剤）を使用することができる。酸化防止剤を使用すると硬化物の耐候性を高めることができる。酸化防止剤としてはヒンダードフェノール系、モノフェノール系、ビスフェノール系、ポリフェノール系が例示できる。酸化防止剤の具体例は特開平４－２８３２５９号公報や特開平９－１９４７３１号公報にも記載されている。
　酸化防止剤の使用量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～１０重量部が好ましく、特に０．２～５重量部が好ましい。
　＜光安定剤＞
　本多液型硬化性組成物には、光安定剤を使用することができる。光安定剤を使用すると硬化物の光酸化劣化を防止できる。光安定剤としてベンゾトリアゾール系、ヒンダードアミン系、ベンゾエート系化合物等が例示できるが、特にヒンダードアミン系が好ましい。
　光安定剤の使用量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～１０重量部が好ましく、特に０．２～５重量部が好ましい。
　＜紫外線吸収剤＞
　本多液型硬化性組成物には、紫外線吸収剤を使用することができる。紫外線吸収剤を使用すると硬化物の表面耐候性を高めることができる。紫外線吸収剤としてはベンゾフェノン系、ベンゾトリアゾール系、サリチレート系、置換トリル系および金属キレート系化合物等が例示できるが、特にベンゾトリアゾール系が好ましく、市販名チヌビンＰ、チヌビン２１３、チヌビン２３４、チヌビン３２６、チヌビン３２７、チヌビン３２８、チヌビン３２９、チヌビン５７１（以上、ＢＡＳＦ製）が挙げられる。
　紫外線吸収剤の使用量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～１０重量部が好ましく、特に０．２～５重量部が好ましい。
　＜粘着付与樹脂＞
　本多液型硬化性組成物には、基材への接着性や密着性を高める目的、あるいはその他必要に応じて粘着付与樹脂を添加できる。粘着付与樹脂としては、特に制限はなく通常使用されているものを使うことができる。
　具体例としては、テルペン系樹脂、芳香族変性テルペン樹脂、水素添加テルペン樹脂、テルペン－フェノール樹脂、フェノール樹脂、変性フェノール樹脂、キシレン－フェノール樹脂、シクロペンタジエン－フェノール樹脂、クマロンインデン樹脂、ロジン系樹脂、ロジンエステル樹脂、水添ロジンエステル樹脂、キシレン樹脂、低分子量ポリスチレン系樹脂、スチレン共重合体樹脂、スチレン系ブロック共重合体およびその水素添加物、石油樹脂（例えば、Ｃ５炭化水素樹脂、Ｃ９炭化水素樹脂、Ｃ５Ｃ９炭化水素共重合樹脂等）、水添石油樹脂、ＤＣＰＤ樹脂等が挙げられる。これらは単独で用いても良く、２種以上を併用しても良い。
　粘着付与樹脂の使用量は、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、２～１００重量部が好ましく、５～５０重量部であることがより好ましく、５～３０重量部であることがさらに好ましい。
　＜低分子可塑剤＞
　本多液型硬化性組成物には、低分子可塑剤を添加できる。低分子可塑剤として、より具体的には、フタル酸ジイソノイル、２－エトキシエタノール、フタル酸ビス（２－エチルヘキシル）、フタル酸ジイソデシル等が好ましい。これらの低分子可塑剤は、単独で使用してもよく、２種以上を組み合わせて使用してもよい。
　本多液型硬化性組成物における低分子可塑剤の含有量は、特に限定されないが、ポリオキシアルキレン系重合体（Ａ）とエポキシ樹脂（Ｅ）との合計１００重量部に対して、例えば、５～１５０重量部であることが好ましく、２０～１００重量部であることがより好ましく、３０～８０重量部であることがさらに好ましい。当該構成によれば、多液型硬化性組成物の低粘度化と、硬化物の引き裂き強さと、が両立し易いという利点を有する。
　（２－１１．用途）
　本多液型硬化性組成物は、防水材、建築用弾性シーリング材、サイディングボード用シーリング材、複層ガラス用シーリング材、車両用シーリング材等建築用および工業用のシーリング材、太陽電池裏面封止剤などの電気・電子部品材料、電線・ケーブル用絶縁被覆材などの電気絶縁材料、粘着剤、接着剤、弾性接着剤、コンタクト接着剤、タイル用接着剤、反応性ホットメルト接着剤、塗料、粉体塗料、コーティング材、発泡体、缶蓋等のシール材、放熱シート、電気電子用ポッティング剤、フィルム、ガスケット、マリンデッキコーキング、注型材料、各種成形材料、人工大理石、および、網入りガラスや合わせガラス端面（切断部）の防錆・防水用封止材、自動車や船舶、家電等に使用される防振・制振・防音・免震材料、自動車部品、電機部品、各種機械部品などにおいて使用される液状シール材等の様々な用途に利用可能である。
　〔３．硬化物〕
　本発明の一実施形態において、本多液型硬化性組成物を硬化させてなる、硬化物（以下、「本硬化物」と称する。）を提供する。
　本硬化物は、本多液型硬化性組成物を硬化して形成されたものである。本発明の一実施形態において、本硬化物は、成分（Ａ）、成分（Ｂ）、成分（Ｃ）、および成分（Ｄ）を含むＡ剤と、成分（Ｅ）および成分（Ｆ）を含むＢ剤と、を含む多液型硬化性組成物を、加熱せずに室温で硬化させることによって形成されたものである。また、本発明の一実施形態において、本硬化物は、成分（Ａ）、成分（Ｂ）、成分（Ｃ）、成分（Ｄ）、および成分（Ｆ）を含むＡ剤と、成分（Ｅ）を含むＢ剤と、を含む多液型硬化性組成物を、加熱せずに室温で硬化させることによって形成されたものである。さらに、本発明の一実施形態において、本硬化物は、成分（Ａ）、成分（Ｂ）、成分（Ｃ）、成分（Ｄ）、および成分（Ｆ）を含むＡ剤と、成分（Ｅ）および成分（Ｆ）を含むＢ剤と、を含む多液型硬化性組成物を、加熱せずに室温で硬化させることによって形成されたものである。なお、本多液型硬化性組成物が、溶剤等の揮発成分を含む場合、当該揮発成分は、養生期間に揮発する。したがって、本硬化物は、本多液型硬化性組成物に含まれる揮発成分を実質的に含まない。
　〔４．防水材〕
　本発明の一実施形態において、本硬化物を含む防水材（以下、「本防水材」と称する。）を提供する。
　本防水材は、継ぎ目がない塗膜を形成し、防水の信頼性が高いことから、高い防水性能を必要とする屋根用透湿性塗膜防水材として、特に有用である。建物の屋根用透湿性塗膜防水材は、野地板などの屋根用下地材に塗布する防水材である。本防水材の用途は、特に限定されないが、天井、屋上、ベランダ、用水路、車庫等の屋外の防水材として使用されることが好ましい。
　本発明の一実施形態において、本防水材は、本硬化物の他に、防水材が一般に含み得る任意の成分を含んでいてもよい。そのような成分は、１種であってもよいし、２種以上であってもよい。また、そのような成分の含有量も特に限定されず、本発明の効果を奏する限り、当業者により適宜設定され得る。
　〔５．防水構造物の製造方法〕
　本発明の一実施形態において、本多液型硬化性組成物を建築物の下地に塗布する工程を含む、防水構造物の製造方法を提供する。本多液型硬化性組成物は、上述の通り、引張特性および引き裂き強さに優れる硬化物を提供できるため、本多液型硬化性組成物を建築物の下地に塗布することにより、防水機能に優れた防水構造物を提供できる。
　本多液型硬化性組成物を建築物の下地に塗布する方法としては、特に限定されないが、例えば、本多液型硬化性組成物を建築物の下地に直接塗布する場合の他、下地にプライマーが塗られた上に塗布すること等が挙げられる。
　また、本発明の一実施形態において、本多液型硬化性組成物を硬化させてなる塗膜の上に、トップコートを塗付する工程を含む、防水構造物の製造方法を提供する。本多液型硬化性組成物を硬化させてなる塗膜の上に、トップコートを塗付することにより、防水機能がより高まる。
　本発明は上述した各実施形態に限定されるものではなく、請求項に示した範囲で種々の変更が可能であり、異なる実施形態にそれぞれ開示された技術的手段を適宜組み合わせて得られる実施形態についても本発明の技術的範囲に含まれる。
　すなわち、本発明の一態様は、以下を含む。
＜１＞一般式（１）に示す反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ）、エポキシ樹脂硬化剤（Ｂ）、アミノシラン（Ｃ）、およびメルカプタン化合物（Ｄ）を含むＡ剤と、エポキシ樹脂（Ｅ）を含むＢ剤と、を含み、
　前記Ａ剤および／または前記Ｂ剤に水酸基含有ポリオキシアルキレン系重合体（Ｆ）を含む、多液型硬化性組成物。
－Ｓｉ（Ｒ）３－ａ（Ｘ）ａ　　　（１）
　（式中、Ｒは、それぞれ独立に、炭素原子数１～２０の炭化水素基、または－ＯＳｉ（Ｒ’）３（Ｒ’は、それぞれ独立に、炭素原子数１～２０の炭化水素基である。）で示されるトリオルガノシロキシ基であり、Ｒとしての炭化水素基は、置換されていてもよく、かつ、ヘテロ含有基を有してもよい。Ｘは、それぞれ独立に、水酸基または加水分解性基である。ａは、１～３の整数である。）
＜２＞前記アミノシラン（Ｃ）の含有量が、前記ポリオキシアルキレン系重合体（Ａ）と前記エポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～３．０重量部である、＜１＞に記載の多液型硬化性組成物。
＜３＞前記メルカプタン化合物（Ｄ）の含有量が、前記ポリオキシアルキレン系重合体（Ａ）と前記エポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～３．０重量部である、＜１＞または＜２＞に記載の多液型硬化性組成物。
＜４＞無機フィラーをさらに含む、＜１＞～＜３＞のいずれかに記載の多液型硬化性組成物。
＜５＞前記無機フィラーの含有量が、前記ポリオキシアルキレン系重合体（Ａ）と前記エポキシ樹脂（Ｅ）との合計１００重量部に対して、５０～３００重量部である、＜４＞に記載の多液型硬化性組成物。
＜６＞前記ポリオキシアルキレン系重合体（Ａ）の末端部位が、一般式（２）：
Figure JPOXMLDOC01-appb-C000006
 　（式中、Ｒ１、Ｒ３は、それぞれ独立に、２価の炭素数１～６の結合基であり、Ｒ１、Ｒ３に隣接するそれぞれの炭素原子と結合する原子は、炭素、酸素、窒素のいずれかである。Ｒ２、Ｒ４は、それぞれ独立に、水素、または炭素数１～１０の炭化水素基である。ｎは、１～１０の整数である。Ｒ５は、置換または非置換の炭素数１～２０の炭化水素基である。Ｘは、水酸基または加水分解性基である。ｃは、１～３の整数である。）で表される、＜１＞～＜５＞のいずれかに記載の多液型硬化性組成物。
＜７＞前記エポキシ樹脂硬化剤（Ｂ）が、第三級アミンを有するエポキシ樹脂硬化剤である、＜１＞～＜６＞のいずれかに記載の多液型硬化性組成物。
＜８＞前記アミノシラン（Ｃ）が、γ－アミノプロピルトリエトキシシラン、Ｎ－β－（アミノエチル）－γ－アミノプロピルトリメトキシシラン、およびＮ－β－（アミノエチル）－γ－アミノプロピルメチルジメトキシシランからなる群より選択される少なくとも１種である、＜１＞～＜７＞のいずれかに記載の多液型硬化性組成物。
＜９＞前記メルカプタン化合物（Ｄ）が、ｎ－ドデシルメルカプタン、ｔｅｒｔ－ドデシルメルカプタン、ラウリルメルカプタン、トリメチロールプロパントリス（３－メルカプトプロピオネート）、ペンタエリスリトールテトラキス（３－メルカプトプロピオネート）、３－メルカプトプロピルトリメトキシシラン、３－メルカプトプロピルメチルジメトキシシラン、３－メルカプトプロピルクロロメチルジメトキシシラン、３－メルカプトプロピルメトキシメチルジメトキシシラン、（メルカプトメチル）ジメトキシメチルシラン、および（メルカプトメチル）トリメトキシシランからなる群より選択される少なくとも１種である、＜１＞～＜８＞のいずれかに記載の多液型硬化性組成物。
＜１０＞前記エポキシ樹脂（Ｅ）が、エポキシ基を１分子中に少なくとも２個有するエポキシ樹脂である、＜１＞～＜９＞のいずれかに記載の多液型硬化性組成物。
＜１１＞前記水酸基含有ポリオキシアルキレン系重合体（Ｆ）が、数平均分子量が３００以上の水酸基を含有するポリオキシアルキレン系重合体である、＜１＞～＜１０＞のいずれかに記載の多液型硬化性組成物。
＜１２＞＜１＞～＜１１＞のいずれかに記載の多液型硬化性組成物を硬化させてなる、硬化物。
＜１３＞＜１２＞に記載の硬化物を含む、防水材。
＜１４＞＜１＞～＜１１＞のいずれかに記載の多液型硬化性組成物を建築物の下地に塗布する工程を含む、防水構造物の製造方法。
＜１５＞＜１＞～＜１１＞のいずれかに記載の多液型硬化性組成物を硬化させてなる塗膜の上に、トップコートを塗付する工程を含む、防水構造物の製造方法。
　本発明の一態様は、以下を含んでもよい。
＜１６＞一般式（１）に示す反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ）、エポキシ樹脂硬化剤（Ｂ）、アミノシラン（Ｃ）、およびメルカプタン化合物（Ｄ）を含むＡ剤と、エポキシ樹脂（Ｅ）を含むＢ剤と、を含み、
　前記Ａ剤および／または前記Ｂ剤に水酸基含有ポリオキシアルキレン系重合体（Ｆ）を含む、多液型硬化性組成物。
－Ｓｉ（Ｒ）３－ａ（Ｘ）ａ　　　（１）
　（式中、Ｒは、それぞれ独立に、炭素原子数１～２０の炭化水素基、または－ＯＳｉ（Ｒ’）３（Ｒ’は、それぞれ独立に、炭素原子数１～２０の炭化水素基である。）で示されるトリオルガノシロキシ基であり、Ｒとしての炭化水素基は、置換されていてもよく、かつ、ヘテロ含有基を有してもよい。Ｘは、それぞれ独立に、水酸基または加水分解性基である。ａは、１～３の整数である。）
＜１７＞前記メルカプタン化合物（Ｄ）の含有量が、前記ポリオキシアルキレン系重合体（Ａ）と前記エポキシ樹脂（Ｅ）との合計１００重量部に対して、０．２～５．０重量部である、＜１６＞に記載の多液型硬化性組成物。
＜１８＞無機フィラーをさらに含む、＜１６＞または＜１７＞に記載の多液型硬化性組成物。
＜１９＞前記無機フィラーの含有量が、前記ポリオキシアルキレン系重合体（Ａ）と前記エポキシ樹脂（Ｅ）との合計１００重量部に対して、５０～１８０重量部である、＜１８＞に記載の多液型硬化性組成物。
＜２０＞前記アミノシラン（Ｃ）の含有量が、前記ポリオキシアルキレン系重合体（Ａ）と前記エポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～５．０重量部である、＜１６＞～＜１９＞のいずれかに記載の多液型硬化性組成物。
＜２１＞前記ポリオキシアルキレン系重合体（Ａ）の末端部位が、一般式（２）：
Figure JPOXMLDOC01-appb-C000007
 　（式中、Ｒ１、Ｒ３は、それぞれ独立に、２価の炭素数１～６の結合基であり、Ｒ１、Ｒ３に隣接するそれぞれの炭素原子と結合する原子は、炭素、酸素、窒素のいずれかである。Ｒ２、Ｒ４は、それぞれ独立に、水素、または炭素数１～１０の炭化水素基である。ｎは、１～１０の整数である。Ｒ５は、置換または非置換の炭素数１～２０の炭化水素基である。Ｘは、水酸基または加水分解性基である。ｃは、１～３の整数である。）で表される、＜１６＞～＜２０＞のいずれかに記載の多液型硬化性組成物。
＜２２＞前記エポキシ樹脂硬化剤（Ｂ）が、第三級アミンを有するエポキシ樹脂硬化剤である、＜１６＞～＜２１＞のいずれかに記載の多液型硬化性組成物。
＜２３＞前記アミノシラン（Ｃ）が、γ－アミノプロピルトリエトキシシラン、Ｎ－β－（アミノエチル）－γ－アミノプロピルトリメトキシシラン、およびＮ－β－（アミノエチル）－γ－アミノプロピルメチルジメトキシシランからなる群より選択される少なくとも１種である、＜１６＞～＜２２＞のいずれかに記載の多液型硬化性組成物。
＜２４＞前記メルカプタン化合物（Ｄ）が、ｎ－ドデシルメルカプタン、ｔｅｒｔ－ドデシルメルカプタン、ラウリルメルカプタン、トリメチロールプロパントリス（３－メルカプトプロピオネート）、ペンタエリスリトールテトラキス（３－メルカプトプロピオネート）、３－メルカプトプロピルトリメトキシシラン、３－メルカプトプロピルメチルジメトキシシラン、３－メルカプトプロピルクロロメチルジメトキシシラン、３－メルカプトプロピルメトキシメチルジメトキシシラン、（メルカプトメチル）ジメトキシメチルシラン、および（メルカプトメチル）トリメトキシシランからなる群より選択される少なくとも１種である、＜１６＞～＜２３＞のいずれかに記載の多液型硬化性組成物。
＜２５＞前記エポキシ樹脂（Ｅ）が、エポキシ基を１分子中に少なくとも２個有するエポキシ樹脂である、＜１６＞～＜２４＞のいずれかに記載の多液型硬化性組成物。
＜２６＞前記水酸基含有ポリオキシアルキレン系重合体（Ｆ）が、数平均分子量が３００以上の水酸基を含有するポリオキシアルキレン系重合体である、＜１６＞～＜２５＞のいずれかに記載の多液型硬化性組成物。
＜２７＞＜１６＞～＜２６＞のいずれかに記載の多液型硬化性組成物を硬化させてなる、硬化物。
＜２８＞＜２７＞に記載の硬化物を含む、防水材。
＜２９＞＜１６＞～＜２６＞のいずれかに記載の多液型硬化性組成物を建築物の下地に塗布する工程を含む、防水構造物の製造方法。
＜３０＞＜１６＞～＜２６＞のいずれかに記載の多液型硬化性組成物を硬化させてなる塗膜の上に、トップコートを塗付する工程を含む、防水構造物の製造方法。
　以下、本発明を実施例に基づいてより詳細に説明するが、本発明はこれら実施例に限定されるものではない。
　〔材料〕
　実施例および比較例で使用した材料は、以下の通りである。
　＜ポリオキシアルキレン系重合体（Ａ）＞
　下記の合成例に基づき製造した反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ－１）、および（Ａ－２）を使用した。
　＜エポキシ樹脂硬化剤（Ｂ）＞
　２，４，６－トリス（ジメチルアミノメチル）フェノール：（日新化成株式会社製の「Ａｎｃａｍｉｎｅ　Ｋ５４」）
　＜アミノシラン（Ｃ）＞
　Ｎ－（２－アミノエチル）－３－アミノプロピルトリメトキシシラン：（モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製の「Ｓｉｌｑｕｅｓｔ　Ａ－１１２０」）
　γ－アミノプロピルトリメトキシシラン：（モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製の「Ｓｉｌｑｕｅｓｔ　Ａ－１１１０」）
　＜メルカプタン化合物（Ｄ）＞
　（メルカプトシラン）
　３－メルカプトプロピルトリメトキシシラン：（ダウ・ケミカル日本株式会社製の「Ｚ６０６２」）
　（メルカプタン）
　ｎ－ドデシルメルカプタン：（花王株式会社製の「チオカルコール２０」）
　トリメチロールプロパントリス（３－メルカプトプロピオネート）：（ＳＣ有機化学株式会社製の「Ｌｅｃａｄ８０３」
　＜エポキシ樹脂（Ｅ）＞
　ビスフェノールＡ型エポキシ樹脂：（三菱ケミカル株式会社製の「Ｅｐｉｋｏｔｅ　８２８」）
　＜水酸基含有ポリオキシアルキレン系重合体（Ｆ）＞
　ポリプロピレングリコール樹脂：（三井化学株式会社製の「アクトコール２１－５６」）
　＜無機フィラー＞
　炭酸カルシウム：（白石カルシウム株式会社製の「ホワイトンＳＢ」）
　＜硬化触媒＞
　錫触媒：（日本化学産業株式会社製の「ＭＳＣＡＴ－０１」）
　＜低分子可塑剤＞
　フタル酸ジイソノイル：（株式会社ジェイ・プラス製の「ＤＩＮＰ」）
　エチルセルソルブ：（ナカライテスク株式会社製）
　＜脱水剤＞
　ビニルシラン：（モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製の「Ａ－１７１」）
　＜その他の成分＞
　（充填剤）
　カーボンブラック（旭カーボン株式会社製の「アサヒサーマル」）
　〔測定および評価方法〕
　実施例および比較例における測定および評価を、以下の方法で行った。
　（引張特性）
　（株）島津製オートグラフ（ＡＧＳ－Ｊ）を用い、２３℃５０％ＲＨで、引張強度試験を行った。ＪＩＳ　Ａ　６０２１のウレタン系高伸長型（旧１類）に準じた評価を実施した。具体的には、引張強度および引張伸びは、ＪＩＳ３号で打ち抜いた。引張測定は、５００ｍｍ／ｍｉｎで行った。
　（引き裂き強さ）
　（株）島津製オートグラフ（ＡＧＳ－Ｊ）を用い、２３℃５０％ＲＨで、引張強度試験を行った。ＪＩＳ　Ａ　６０２１のウレタン系高伸長型（旧１類）に準じた評価を実施した。引き裂き強さは、ＪＩＳ　Ｋ　６２５２に規定する切込みなしアングル形ダンベルで打抜いたものを使用した。
　〔合成例１〕
　ポリオキシアルキレン系重合体（Ａ－１）の合成例を以下に示す。
　数平均分子量が約４８００のポリオキシプロピレングリコールを開始剤とし、亜鉛ヘキサシアノコバルテートグライム錯体触媒にてプロピレンオキサイドの重合を行い、両末端に水酸基を有する数平均分子量２８，０００（末端基換算分子量１８０００）、分子量分布Ｍｗ／Ｍｎ＝１．２１のポリオキシプロピレン（Ｐ－１）を得た。続いてこの水酸基末端ポリオキシプロピレン（Ｐ－１）の水酸基に対して１．０モル当量のナトリウムメトキシドを２８％メタノール溶液として添加した。真空脱揮によりメタノールを留去した後、重合体（Ｐ－１）の水酸基に対して、１．０モル当量のアリルグリシジルエーテルを添加して１３０℃で２時間反応を行った。その後、０．２８モル当量のナトリウムメトキシドのメタノール溶液を添加してメタノールを除去し、さらに１．７９モル当量の塩化アリルを添加して末端の水酸基をアリル基に変換した。得られた未精製のポリオキシプロピレンをｎ－ヘキサンと、水を混合攪拌した後、遠心分離により水を除去し、得られたヘキサン溶液からヘキサンを減圧脱揮することでポリマー中の金属塩を除去した。以上により、末端に複数の炭素－炭素不飽和結合を有するポリオキシプロピレン（Ｑ－１）を得た。重合体（Ｑ－１）は１つの末端に炭素－炭素不飽和結合が平均２．０個導入されていることがわかった。
　得られた（Ｑ－１）５００ｇに対し白金ジビニルジシロキサン錯体溶液（白金換算で３重量％のイソプロパノール溶液）５０μｌを加え、撹拌しながらジメトキシメチルシラン９．６ｇをゆっくりと滴下した。その混合溶液を１００℃で２時間反応させた後、未反応のジメトキシメチルシランを減圧下留去する事により、末端に複数のジメトキシメチルシリル基を有する数平均分子量２８，５００のポリオキシプロピレン（Ａ－１）を得た。ポリオキシアルキレン系重合体（Ａ－１）はジメトキシメチルシリル基を１つの末端に平均１．７個、一分子中に平均３．４個有することが分かった。
　〔合成例２〕
　ポリオキシアルキレン系重合体（Ａ－２）の合成例を以下に示す。
　ブタノールを開始剤とし、亜鉛ヘキサシアノコバルテートグライム錯体触媒にてプロピレンオキサイドの重合を行い、片方の末端に水酸基を有する数平均分子量７８００（末端基換算分子量５０００）、分子量分布Ｍｗ／Ｍｎ＝１．４８のポリオキシプロピレン（Ｐ－２）を得た。続いてこの水酸基末端ポリオキシプロピレン（Ｐ－２）の水酸基に対して１．２モル当量のナトリウムメトキシドを２８％メタノール溶液として添加した。真空脱揮によりメタノールを留去した後、重合体（Ｐ－２）の水酸基に対して、２．０モル当量の塩化アリルを添加して末端の水酸基をアリル基に変換し、未反応の塩化アリルを減圧脱揮により除去した。得られた未精製のポリオキシプロピレンをｎ－ヘキサンと、水を混合攪拌した後、遠心分離により水を除去し、得られたヘキサン溶液からヘキサンを減圧脱揮することでポリマー中の金属塩を除去した。以上により、アリル基を片末端のみに有するポリオキシプロピレン（Ｑ－２）を得た。得られた（Ｑ－２）５００ｇに対し白金ジビニルジシロキサン錯体（白金換算で３重量％の２－プロパノール溶液）５０μｌを加え、撹拌しながら、ジメトキシメチルシラン９．５ｇをゆっくりと滴下した。その混合溶液を１００℃で２時間反応させた後、未反応のジメトキシメチルシランを減圧下留去する事により、片末端のみにジメトキシメチルシリル基を有するポリオキシプロピレン（Ａ－２）を得た。ポリオキシアルキレン系重合体（Ａ－２）はジメトキシメチルシリル基を片末端のみに平均０．８個有することが分かった。
　〔実施例１〕
　反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ）として（Ａ－１）および（Ａ－２）と、エポキシ樹脂硬化剤（Ｂ）としてＡｎｋａｍｉｎｅ　Ｋ５４と、アミノシラン（Ｃ）としてＡ－１１２０と、メルカプタン化合物（Ｄ）としてＺ６０６２と、脱水剤としてビニルシランＡ－１７１と、硬化触媒としてＭＳＣＡＴ－０１とを、それぞれ表１に記載の量で添加し、手撹拌で２分間攪拌して、Ａ液（Ａ剤）を作製した。
　エポキシ樹脂（Ｅ）としてＥｐｉｋｏｔｅ　８２８と、水酸基含有ポリオキシアルキレン系重合体（Ｆ）としてアクトコール２１－５６と、無機フィラーとして炭酸カルシウム（ホワイトンＳＢ）と、充填剤としてカーボンブラック（アサヒサーマル）とを、それぞれ表１に記載の量で添加し、手撹拌で２分間攪拌し、その後、セラミック３本ロールを３回通過させて、Ｂ液（Ｂ剤）を作製した。
　次いで、表１に記載の量で、Ａ液（Ａ剤）、Ｂ液（Ｂ剤）およびＣ液（Ｃ剤）を順次ディスポーザブルのカップに添加し、手撹拌した。その後、スーパーミキサー（株式会社シンキー製、ＡＲＥ－２５０）で混合および脱泡した。混合および脱泡は、具体的には、５００ｒｐｍで２０秒間、１５００ｒｐｍで２０秒間、２０００ｒｐｍで４０秒間撹拌した後、１５００ｒｐｍで４０秒間脱泡することにより行った。次いで、脱泡後の混合物を、型枠（テフロン（登録商標）シート＋パッカー、厚さ２ｍｍ）に流し込んだ。
　これらの操作は、２時間以内に終了するように実行した。
　その後、２３℃５０％ＲＨ条件下で７日間の硬化養生を行った。得られた硬化物について、引張特性および引き裂き強さを評価した。結果を表１に示す。
　〔実施例２～１６、比較例１～６〕
　各成分の配合量を表１および表２に記載の通りに変更したこと以外は実施例１と同様の手順により、硬化性樹脂組成物および硬化物を作製した。得られた硬化物について、引張特性および引き裂き強さを評価した。結果を表１および表２に示す。
Figure JPOXMLDOC01-appb-T000008
Figure JPOXMLDOC01-appb-T000009
 　〔結果〕
　表１および表２より、実施例１～１６の硬化性組成物は、硬化物とした際に、引張特性および引き裂き強さに優れることが示された。すなわち、本発明の一実施形態によれば、引張特性および引き裂き強さに優れる硬化物を提供し得る硬化性組成物を提供できることが示された。
　一方、表１より、比較例１～６の硬化性組成物では、引張特性および引き裂き強さが不良となっている。すなわち、硬化性組成物が本多液型硬化性組成物の構成を満たさない場合、引張特性および引き裂き強さが不良となることが示された。
　本多液型硬化性組成物は、引張特性および引き裂き強さに優れる硬化物を提供できるため、防水材等に好適に利用することができる。

 

Claims (15)

  1. 　一般式（１）に示す反応性ケイ素基を有するポリオキシアルキレン系重合体（Ａ）、エポキシ樹脂硬化剤（Ｂ）、アミノシラン（Ｃ）、およびメルカプタン化合物（Ｄ）を含むＡ剤と、エポキシ樹脂（Ｅ）を含むＢ剤と、を含み、
    　前記Ａ剤および／または前記Ｂ剤に水酸基含有ポリオキシアルキレン系重合体（Ｆ）を含む、多液型硬化性組成物。
    －Ｓｉ（Ｒ）３－ａ（Ｘ）ａ　　　（１）
    　（式中、Ｒは、それぞれ独立に、炭素原子数１～２０の炭化水素基、または－ＯＳｉ（Ｒ’）３（Ｒ’は、それぞれ独立に、炭素原子数１～２０の炭化水素基である。）で示されるトリオルガノシロキシ基であり、Ｒとしての炭化水素基は、置換されていてもよく、かつ、ヘテロ含有基を有してもよい。Ｘは、それぞれ独立に、水酸基または加水分解性基である。ａは、１～３の整数である。）
  2. 　前記メルカプタン化合物（Ｄ）の含有量が、前記ポリオキシアルキレン系重合体（Ａ）と前記エポキシ樹脂（Ｅ）との合計１００重量部に対して、０．２～５．０重量部である、請求項１に記載の多液型硬化性組成物。
  3. 　無機フィラーをさらに含む、請求項１または２に記載の多液型硬化性組成物。
  4. 　前記無機フィラーの含有量が、前記ポリオキシアルキレン系重合体（Ａ）と前記エポキシ樹脂（Ｅ）との合計１００重量部に対して、５０～１８０重量部である、請求項３に記載の多液型硬化性組成物。
  5. 　前記アミノシラン（Ｃ）の含有量が、前記ポリオキシアルキレン系重合体（Ａ）と前記エポキシ樹脂（Ｅ）との合計１００重量部に対して、０．１～５．０重量部である、請求項１～４のいずれか１項に記載の多液型硬化性組成物。
  6. 　前記ポリオキシアルキレン系重合体（Ａ）の末端部位が、一般式（２）：
    Figure JPOXMLDOC01-appb-C000001
     　（式中、Ｒ１、Ｒ３は、それぞれ独立に、２価の炭素数１～６の結合基であり、Ｒ１、Ｒ３に隣接するそれぞれの炭素原子と結合する原子は、炭素、酸素、窒素のいずれかである。Ｒ２、Ｒ４は、それぞれ独立に、水素、または炭素数１～１０の炭化水素基である。ｎは、１～１０の整数である。Ｒ５は、置換または非置換の炭素数１～２０の炭化水素基である。Ｘは、水酸基または加水分解性基である。ｃは、１～３の整数である。）で表される、請求項１～５のいずれか１項に記載の多液型硬化性組成物。
  7. 　前記エポキシ樹脂硬化剤（Ｂ）が、第三級アミンを有するエポキシ樹脂硬化剤である、請求項１～６のいずれか１項に記載の多液型硬化性組成物。
  8. 　前記アミノシラン（Ｃ）が、γ－アミノプロピルトリエトキシシラン、Ｎ－β－（アミノエチル）－γ－アミノプロピルトリメトキシシラン、およびＮ－β－（アミノエチル）－γ－アミノプロピルメチルジメトキシシランからなる群より選択される少なくとも１種である、請求項１～７のいずれか１項に記載の多液型硬化性組成物。
  9. 　前記メルカプタン化合物（Ｄ）が、ｎ－ドデシルメルカプタン、ｔｅｒｔ－ドデシルメルカプタン、ラウリルメルカプタン、トリメチロールプロパントリス（３－メルカプトプロピオネート）、ペンタエリスリトールテトラキス（３－メルカプトプロピオネート）、３－メルカプトプロピルトリメトキシシラン、３－メルカプトプロピルメチルジメトキシシラン、３－メルカプトプロピルクロロメチルジメトキシシラン、３－メルカプトプロピルメトキシメチルジメトキシシラン、（メルカプトメチル）ジメトキシメチルシラン、および（メルカプトメチル）トリメトキシシランからなる群より選択される少なくとも１種である、請求項１～８のいずれか１項に記載の多液型硬化性組成物。
  10. 　前記エポキシ樹脂（Ｅ）が、エポキシ基を１分子中に少なくとも２個有するエポキシ樹脂である、請求項１～９のいずれか１項に記載の多液型硬化性組成物。
  11. 　前記水酸基含有ポリオキシアルキレン系重合体（Ｆ）が、数平均分子量が３００以上の水酸基を含有するポリオキシアルキレン系重合体である、請求項１～１０のいずれか１項に記載の多液型硬化性組成物。
  12. 　請求項１～１１のいずれか１項に記載の多液型硬化性組成物を硬化させてなる、硬化物。
  13. 　請求項１２に記載の硬化物を含む、防水材。
  14. 　請求項１～１１のいずれか１項に記載の多液型硬化性組成物を建築物の下地に塗布する工程を含む、防水構造物の製造方法。
  15. 　請求項１～１１のいずれか１項に記載の多液型硬化性組成物を硬化させてなる塗膜の上に、トップコートを塗付する工程を含む、防水構造物の製造方法。
PCT/JP2022/028867 2021-08-05 2022-07-27 多液型硬化性組成物およびその利用 WO2023013487A1 (ja)