WO2022139214A1 - 강도 및 내식성이 향상된 마르텐사이트계 스테인리스강 및 이의 제조 방법 - Google Patents
강도 및 내식성이 향상된 마르텐사이트계 스테인리스강 및 이의 제조 방법 Download PDFInfo
- Publication number
- WO2022139214A1 WO2022139214A1 PCT/KR2021/017715 KR2021017715W WO2022139214A1 WO 2022139214 A1 WO2022139214 A1 WO 2022139214A1 KR 2021017715 W KR2021017715 W KR 2021017715W WO 2022139214 A1 WO2022139214 A1 WO 2022139214A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- stainless steel
- corrosion resistance
- martensitic stainless
- improved strength
- hot
- Prior art date
Abstract
Description
C | Si | Mn | Ni | Cu | Cr | Mo | V | N | C+N | Mo+V | 식(1) | |
실시예1 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 13.5 | 1.05 | 0.07 | 0.02 | 0.40 | 1.12 | 19.4 |
실시예2 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 13.5 | 0.95 | 0.05 | 0.02 | 0.40 | 1.00 | 17.0 |
실시예3 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 13.5 | 1.1 | 0.15 | 0.02 | 0.40 | 1.25 | 21.8 |
실시예4 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 14.5 | 1.05 | 0.07 | 0.02 | 0.40 | 1.12 | 20.5 |
실시예5 | 0.4 | 0.5 | 0.6 | 0.5 | 0.5 | 13.9 | 1.1 | 0.15 | 0.025 | 0.43 | 1.25 | 22.4 |
실시예6 | 0.36 | 0.3 | 0.4 | 0.3 | 0.001 | 13.1 | 0.95 | 0.05 | 0.01 | 0.37 | 1.00 | 16.4 |
실시예7 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 13.5 | 1.05 | 0.3 | 0.02 | 0.40 | 1.35 | 23.3 |
비교예1 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 13.5 | 0.5 | 0.001 | 0.02 | 0.40 | 0.5 | 7.8 |
비교예2 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 13.5 | 0.5 | 0.04 | 0.02 | 0.40 | 0.54 | 8.4 |
비교예3 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 12.5 | 1.05 | 0.07 | 0.02 | 0.40 | 1.12 | 18.2 |
비교예4 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 13.5 | 0.001 | 0.001 | 0.02 | 0.40 | 0.00 | 0.0 |
비교예5 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 13.5 | 0.001 | 0.07 | 0.02 | 0.40 | 0.07 | 1.0 |
비교예6 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 13.5 | 0.1 | 0.07 | 0.02 | 0.40 | 0.17 | 2.4 |
비교예7 | 0.38 | 0.4 | 0.45 | 0.4 | 0.05 | 13.5 | 0.1 | 0.07 | 0.02 | 0.40 | 0.17 | 2.4 |
비교예8 | 0.3 | 0.5 | 0.5 | 0.2 | 0.05 | 13.2 | 0 | 0 | 0.02 | 0.32 | 0.00 | 0.0 |
비교예9 | 0.45 | 0.35 | 0.55 | 0.2 | 0.05 | 14.0 | 0 | 0 | 0.025 | 0.48 | 0.00 | 0.0 |
비교예10 | 0.5 | 0.4 | 0.45 | 0.2 | 0.05 | 14.7 | 0.65 | 0.125 | 0.03 | 0.53 | 0.78 | 13.4 |
식(2) | (Mo+V) in M7C3 | (Mo+V) in M23C6 | Z 상 석출 여부 | VN 석출 여부 |
M7C3 크기(㎛) | 냉연소둔재 탄화물 밀도 (개/100㎛2) |
소려 후 경도(Hv) |
|
실시예1 | -10 | 4.29 | 14.1 | O | O | 6.2 | 49 | 620 |
실시예2 | -14 | 3.70 | 12.2 | O | O | 10 | 44 | 555 |
실시예3 | 3 | 5.67 | 14.3 | O | O | 4 | 53 | 635 |
실시예4 | -10 | 3.94 | 13.3 | O | O | 7 | 45 | 582 |
실시예5 | 50 | 5.54 | 13.6 | O | O | 9 | 55 | 643 |
실시예6 | -8 | 3.71 | 12.8 | O | O | 5 | 42 | 520 |
실시예7 | 28 | 2.93 | 14.8 | O | O | 3.5 | 58 | 650 |
비교예1 | -227 | 2.90 | 13.2 | X | X | 19 | 36 | 480 |
비교예2 | -220 | 2.93 | 13.2 | X | X | 16 | 37 | 484 |
비교예3 | -10 | 4.69 | 13.3 | O | O | 12 | 33 | 430 |
비교예4 | -30 | 0.00 | 0.0 | X | X | 67 | 35 | 473 |
비교예5 | -19 | 1.40 | 0.0 | O | O | 50 | 40 | 501 |
비교예6 | -18 | 1.72 | 1.5 | O | O | 25 | 43 | 496 |
비교예7 | -18 | 2.92 | 6.8 | O | O | 14 | 38 | 517 |
비교예8 | -18 | 0.00 | 0.0 | X | X | 38 | 32 | 453 |
비교예9 | -38 | 0.00 | 0.0 | X | X | 74 | 59 | 751 |
비교예10 | -15 | 3.67 | 6.9 | O | O | 45 | 78 | 847 |
Claims (20)
- 중량%로, C: 0.3 내지 0.5%, N: 0.01 내지 0.025%, Si: 0.3 내지 0.5%, Mn: 0.4 내지 0.6, Cr: 13.1 내지 14.5%, Mo: 0.95 내지 1.10%, V: 0.05 내지 0.3%, Ni: 0.3 내지 0.5%, Cu: 0.001 내지 0.5%, 나머지는 Fe 및 불가피한 불순물을 포함하고, 하기 식 (1)을 만족하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강판.식(1): 16.4 ≤ (Cr+3.3Mo+16N)*(Mo+V) ≤ 23.3여기서, Cr, N, Mo, V는 각 원소의 함량(중량%)을 의미한다.
- 제1항에 있어서,하기 식 (2)을 만족하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강판.식(2): -14 ≤-36442+248C+365Cr+373Mo+530V+365Fe+350Si+312Mn+331Ni+506Cu ≤ 50여기서, C, Cr, Mo, V, Fe, Si, Mn, Ni, Cu 는 각 원소의 함량(중량%)을 의미한다.
- 제1항에 있어서,하기 식 (3)을 만족하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강판.식(3): 0.37 ≤ C+N ≤ 0.43
- 제1항에 있어서,하기 식 (4)을 만족하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강판.식(4): 1.0 ≤ Mo+V ≤ 1.35
- 제1항에 있어서,페라이트를 기지조직으로 하고,(Cr,Fe,Mo,V)7C3으로 표현되는 1차 탄화물 및 (Cr,Fe,Mo,V)23C6으로 표현되는 2차 탄화물을 포함하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강판.
- 제5항에 있어서,상기 1차 탄화물 내, (Mo+V)의 중량%가 2.93 내지 5.67%인 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강판.
- 제5항에 있어서,상기 2차 탄화물 내, (Mo+V)의 중량%가 12.2 내지 14.8%인 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강판.
- 제1항에 있어서,상기 1차 탄화물의 입경이 10㎛ 이하인 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강판.
- 제1항에 있어서,길이 방향으로, 탄화물 편차가 10개/100㎛2 이하인 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강판.
- 제1항에 있어서,냉간 압연 후, 탄화물의 분포밀도는 42 내지 58개/100㎛2인 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강판.
- 중량%로, C: 0.3 내지 0.5%, N: 0.01 내지 0.025%, Si: 0.3 내지 0.5%, Mn: 0.4 내지 0.6, Cr: 13.1 내지 14.5%, Mo: 0.95 내지 1.10%, V: 0.05 내지 0.3%, Ni: 0.3 내지 0.5%, Cu: 0.001 내지 0.5%, 나머지는 Fe 및 불가피한 불순물을 포함하고, 하기 식 (1)을 만족하는 슬라브를 열간 압연하는 단계;열간 압연 직후, 600 내지 900℃의 온도범위에서 상소둔 열처리하는 단계;열연 소둔재를 냉간 압연하는 단계; 및냉연재를 강화 열처리하는 단계;를 포함하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스강의 제조 방법.식(1): 16.4 ≤ (Cr+3.3Mo+16N)*(Mo+V) ≤ 23.3여기서, Cr, N, Mo, V는 각 원소의 함량(중량%)을 의미한다.
- 제11항에 있어서,상기 열연 소둔재는 페라이트를 기지조직으로 하고,(Cr,Fe,Mo,V)7C3으로 표현되는 1차 탄화물 및 (Cr,Fe,Mo,V)23C6으로 표현되는 2차 탄화물을 포함하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스강의 제조 방법.
- 제11항에 있어서,상기 1차 탄화물 내, (Mo+V)의 중량%가 2.93 내지 5.67%인 강도 및 내식성이 향상된 마르텐사이트계 스테인리스강의 제조 방법.
- 제11항에 있어서,상기 2차 탄화물 내, (Mo+V)의 중량%가 12.2 내지 14.8%인 강도 및 내식성이 향상된 마르텐사이트계 스테인리스강의 제조 방법.
- 제11항에 있어서,상기 1차 탄화물의 입경이 10㎛ 이하인 강도 및 내식성이 향상된 마르텐사이트계 스테인리스강의 제조 방법.
- 제11항에 있어서,냉간 압연 후, 42 내지 58개/100㎛2 이하의 탄화물이 분포하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스 열연소둔 강의 제조방법.
- 제11항에 있어서,상기 강화 열처리는,980 내지 1,050℃의 온도에서 소입하는 단계,400 내지 600℃의 온도에서 1분 내지 1시간 동안 소려하는 단계;를 포함하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스강의 제조 방법.
- 제17항에 있어서,강화 열처리 후, 비커스 경도는 520 내지 650 Hv인 강도 및 내식성이 향상된 마르텐사이트계 스테인리스강의 제조 방법.
- 제11항에 있어서,하기 식 (2)을 만족하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스강의 제조 방법.식(2): -14 ≤-36442+248C+365Cr+373Mo+530V+365Fe+350Si+312Mn+331Ni+506Cu ≤ 50여기서, C, Cr, Mo, V, Fe, Si, Mn, Ni, Cu 는 각 원소의 함량(중량%)을 의미한다.
- 제11항에 있어서,하기 식 (3) 및 식 (4)를 만족하는 강도 및 내식성이 향상된 마르텐사이트계 스테인리스강의 제조 방법.식(3): 0.37 ≤ C+N ≤ 0.43식(4): 1.0 ≤ Mo+V ≤ 1.35