WO2021171993A1 - ラテックス組成物 - Google Patents

ラテックス組成物 Download PDF

Info

Publication number
WO2021171993A1
WO2021171993A1 PCT/JP2021/004673 JP2021004673W WO2021171993A1 WO 2021171993 A1 WO2021171993 A1 WO 2021171993A1 JP 2021004673 W JP2021004673 W JP 2021004673W WO 2021171993 A1 WO2021171993 A1 WO 2021171993A1
Authority
WO
WIPO (PCT)
Prior art keywords
latex
weight
conjugated diene
sulfur
parts
Prior art date
Application number
PCT/JP2021/004673
Other languages
English (en)
French (fr)
Inventor
小出村 順司
実紗 林
Original Assignee
日本ゼオン株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本ゼオン株式会社 filed Critical 日本ゼオン株式会社
Priority to EP21759973.7A priority Critical patent/EP4112685A4/en
Priority to US17/800,622 priority patent/US20230101503A1/en
Priority to JP2022503233A priority patent/JPWO2021171993A1/ja
Priority to CN202180015164.XA priority patent/CN115135712A/zh
Publication of WO2021171993A1 publication Critical patent/WO2021171993A1/ja

Abstract

共役ジエン系重合体ラテックスに、硫黄系加硫剤の水分散液、およびキサントゲン化合物を配合してなるラテックス組成物であって、前記硫黄系加硫剤の水分散液が、硫黄系加硫剤を、アニオン系界面活性剤を用いて水中に分散させたものであるラテックス組成物を提供する。

Description

ラテックス組成物
 本発明は、ラテックス組成物に関し、得られるディップ成形体などの膜成形体を、引張強度および引裂強度などの機械的強度が高く、かつ、機械的強度の安定性に優れたものとすることができるラテックス組成物、ならびに、このようなラテックス組成物からなる膜成形体、ディップ成形体、接着剤組成物に関する。
 従来、天然ゴムのラテックスを含有するラテックス組成物をディップ成形して、乳首、風船、手袋、バルーン、サック等の人体と接触して使用されるディップ成形体などの膜成形体が得られることが知られている。しかしながら、天然ゴムのラテックスは、人体に即時型アレルギー(Type I)の症状を引き起こすような蛋白質を含有するため、生体粘膜又は臓器と直接接触するディップ成形体としては問題がある場合があった。そのため、天然ゴムのラテックス中の蛋白質を精製等により除去したり、天然ゴムに代えて合成ゴムのラテックスを用いたりする検討がされてきている。
 たとえば、特許文献1には、ディップ成形用組成物として、合成ゴムである合成ポリイソプレンのラテックスに、酸化亜鉛、硫黄および加硫促進剤を配合してなるラテックス組成物が開示されている。しかしながら、この特許文献1の技術では、天然ゴムに由来する蛋白質による即時型アレルギー(Type I)の発生を防止できる一方で、ディップ成形体とした場合に、ディップ成形体に含まれる加硫促進剤が原因で、人体に触れた際に、遅延型アレルギー(Type IV)のアレルギー症状を発生させることがあった。そして、遅延型アレルギー(Type IV)の症状を引き起こすような加硫促進剤を配合しない場合、得られるディップ成形体は、引張強度および引裂強度などの機械的強度、ならびに、機械的強度の安定性が十分なものではなかった。そのため、遅延型アレルギー(Type IV)の症状を引き起こすような加硫促進剤を配合しない場合における、ディップ成形体の引張強度および引裂強度などの機械的強度、ならびに、機械的強度の安定性の改善が望まれていた。
国際公開第2014/129547号
 本発明は、このような実状に鑑みてなされたものであり、得られるディップ成形体などの膜成形体を、引張強度および引裂強度などの機械的強度が高く、かつ、機械的強度の安定性に優れたものとすることができるラテックス組成物、ならびに、このようなラテックス組成物からなる膜成形体、ディップ成形体、接着剤組成物を提供することを目的とする。
 本発明者等は、上記目的を達成するために鋭意検討を行った結果、共役ジエン系重合体ラテックスに、硫黄系加硫剤、およびキサントゲン化合物を配合してなるラテックス組成物において、硫黄系加硫剤を、アニオン系界面活性剤を用いて水中に分散させた分散液の状態で配合することにより、上記目的を達成できることを見出し、本発明を完成させるに至った。
 すなわち、本発明によれば、共役ジエン系重合体ラテックスに、硫黄系加硫剤の水分散液、およびキサントゲン化合物を配合してなるラテックス組成物であって、前記硫黄系加硫剤の水分散液が、硫黄系加硫剤を、アニオン系界面活性剤を用いて水中に分散させたものであるラテックス組成物が提供される。
 本発明のラテックス組成物において、前記硫黄系加硫剤の配合量が、前記共役ジエン系重合体ラテックス中に含まれる共役ジエン系重合体100重量部に対し、0.1~1.0重量部であることが好ましく、0.1~0.6重量部であることがより好ましい。
 本発明のラテックス組成物において、前記キサントゲン化合物は、ノニオン系界面活性剤および/またはノニオニックアニオン系界面活性剤を用いて水中に分散させた水分散液の状態で、前記共役ジエン系重合体ラテックスに配合されたものであることが好ましい。
 本発明のラテックス組成物において、前記共役ジエン系重合体ラテックスが、合成ポリイソプレンのラテックス、スチレン-イソプレン-スチレンブロック共重合体のラテックス、蛋白質を除去した天然ゴムのラテックスまたはニトリル基含有共役ジエン系共重合体のラテックスであることが好ましい。
 本発明のラテックス組成物において、前記共役ジエン系重合体ラテックスが、カルボキシ変性共役ジエン系重合体のラテックスであることが好ましい。
 また、本発明によれば、上記ラテックス組成物からなる膜成形体、ディップ成形体、接着剤組成物が提供される。
 本発明によれば、得られるディップ成形体などの膜成形体を、引張強度および引裂強度などの機械的強度が高く、かつ、機械的強度の安定性に優れたものとすることができるラテックス組成物、ならびに、このようなラテックス組成物からなる膜成形体、ディップ成形体、接着剤組成物を提供することができる。
 本発明のラテックス組成物は、共役ジエン系重合体ラテックスに、硫黄系加硫剤の水分散液、およびキサントゲン化合物を配合してなるラテックス組成物であって、
 前記硫黄系加硫剤の水分散液が、硫黄系加硫剤を、アニオン系界面活性剤を用いて水中に分散させたものである。
<共役ジエン系重合体のラテックス>
 本発明で用いる共役ジエン系重合体ラテックスとしては、特に限定されないが、たとえば、合成ポリイソプレンのラテックス、スチレン-イソプレン-スチレンブロック共重合体(SIS)のラテックス、蛋白質を除去した天然ゴム(脱蛋白質天然ゴム)のラテックス、ニトリル基含有共役ジエン系共重合体のラテックスなどが挙げられる。これらのなかでも、合成ポリイソプレンのラテックス、SISのラテックス、脱蛋白質天然ゴムのラテックスなどのイソプレン単位を含有する重合体のラテックスが好ましく、合成ポリイソプレンのラテックスが特に好ましい。
 共役ジエン系重合体のラテックスとして合成ポリイソプレンのラテックスを用いる場合には、合成ポリイソプレンのラテックスに含まれる合成ポリイソプレンは、イソプレンの単独重合体であってもよいし、イソプレンと共重合可能な他のエチレン性不飽和単量体とを共重合したものであってもよい。合成ポリイソプレン中のイソプレン単位の含有量は、柔軟で、引張強度に優れるディップ成形体などの膜成形体が得られやすいことから、全単量体単位に対して、好ましくは70重量%以上、より好ましくは90重量%以上、さらに好ましくは95重量%以上、特に好ましくは100重量%(イソプレンの単独重合体)である。
 イソプレンと共重合可能な他のエチレン性不飽和単量体としては、たとえば、ブタジエン、クロロプレン、1,3-ペンタジエン等のイソプレン以外の共役ジエン単量体;アクリロニトリル、メタクリロニトリル、フマロニトリル、α-クロロアクリロニトリル等のエチレン性不飽和ニトリル単量体;スチレン、アルキルスチレン等のビニル芳香族単量体;(メタ)アクリル酸メチル(「アクリル酸メチルおよび/またはメタクリル酸メチル」の意味であり、以下、(メタ)アクリル酸エチルなども同様。)、(メタ)アクリル酸エチル、(メタ)アクリル酸ブチル、(メタ)アクリル酸-2-エチルヘキシル等のエチレン性不飽和カルボン酸エステル単量体;などが挙げられる。これらのイソプレンと共重合可能な他のエチレン性不飽和単量体は、1種単独でも、複数種を併用してもよい。
 合成ポリイソプレンは、従来公知の方法、たとえばトリアルキルアルミニウム-四塩化チタンからなるチーグラー系重合触媒やn-ブチルリチウム、sec-ブチルリチウムなどのアルキルリチウム重合触媒を用いて、不活性重合溶媒中で、イソプレンと、必要に応じて用いられる共重合可能な他のエチレン性不飽和単量体とを溶液重合して得ることができる。溶液重合により得られた合成ポリイソプレンの重合体溶液は、そのまま、合成ポリイソプレンラテックスの製造に用いてもよいが、該重合体溶液から固形の合成ポリイソプレンを取り出した後、有機溶媒に溶解して、合成ポリイソプレンラテックスの製造に用いることもできる。
 上述した方法により合成ポリイソプレンの重合体溶液を得た場合には、重合体溶液中に残った重合触媒の残渣などの不純物を取り除いてもよい。また、重合中または重合後の溶液に、後述する老化防止剤を添加してもよい。また、市販の固形の合成ポリイソプレンを用いることもできる。
 合成ポリイソプレン中のイソプレン単位としては、イソプレンの結合状態により、シス結合単位、トランス結合単位、1,2-ビニル結合単位、3,4-ビニル結合単位の4種類が存在する。得られるディップ成形体などの膜成形体の引張強度向上の観点から、合成ポリイソプレンに含まれるイソプレン単位中のシス結合単位の含有割合は、全イソプレン単位に対して、好ましくは70重量%以上、より好ましくは90重量%以上、さらに好ましくは95重量%以上である。
 合成ポリイソプレンの重量平均分子量は、ゲル・パーミーエーション・クロマトグラフィー分析による標準ポリスチレン換算で、好ましくは10,000~5,000,000、より好ましくは500,000~5,000,000、さらに好ましくは800,000~3,000,000である。合成ポリイソプレンの重量平均分子量を上記範囲とすることにより、ディップ成形体などの膜成形体の引張強度、引張伸び、および引裂強度がより向上するとともに、合成ポリイソプレンラテックスが製造しやすくなる傾向がある。
 また、合成ポリイソプレンのポリマー・ムーニー粘度(ML1+4、100℃)は、好ましくは50~80、より好ましくは60~80、さらに好ましくは70~80である。
 合成ポリイソプレンラテックスを得るための方法としては、たとえば、(1)有機溶媒に溶解または微分散した合成ポリイソプレンの溶液または微細懸濁液を、乳化剤の存在下に、水中で乳化し、必要により有機溶媒を除去して、合成ポリイソプレンラテックスを製造する方法、(2)イソプレン単独または、イソプレンとそれと共重合可能なエチレン性不飽和単量体との混合物を、乳化剤の存在下に、乳化重合もしくは懸濁重合して、直接、合成ポリイソプレンラテックスを製造する方法、が挙げられるが、イソプレン単位中のシス結合単位の割合が高い合成ポリイソプレンを用いることができ、引張強度等の機械的特性に優れるディップ成形体などの膜成形体が得られやすい点から、上記(1)の製造方法が好ましい。
 上記(1)の製造方法で用いる有機溶媒としては、たとえば、ベンゼン、トルエン、キシレン等の芳香族炭化水素溶媒;シクロペンタン、シクロペンテン、シクロヘキサン、シクロヘキセン等の脂環族炭化水素溶媒;ペンタン、ヘキサン、ヘプタン等の脂肪族炭化水素溶媒;塩化メチレン、クロロホルム、二塩化エチレン等のハロゲン化炭化水素溶媒;等を挙げることができる。これらのうち、脂環族炭化水素溶媒、脂肪族炭化水素溶媒が好ましく、ペンタン、シクロヘキサン、n-ヘキサンがより好ましく、n-ヘキサンが特に好ましい。
 なお、有機溶媒の使用量は、合成ポリイソプレン100重量部に対して、好ましくは2,000重量部以下、より好ましくは20~1,500重量部、さらに好ましくは500~1,500重量部である。
 上記(1)の製造方法で用いる乳化剤としては、イオン性乳化剤を用いることが好ましく、中でも、アニオン性乳化剤を用いることがより好ましい。アニオン性乳化剤としては、たとえば、ラウリン酸ナトリウム、ミリスチン酸カリウム、パルミチン酸ナトリウム、オレイン酸カリウム、リノレン酸ナトリウム、ロジン酸ナトリウム、ロジン酸カリウム等の脂肪酸塩;ドデシルベンゼンスルホン酸ナトリウム、ドデシルベンゼンスルホン酸カリウム、デシルベンゼンスルホン酸ナトリウム、デシルベンゼンスルホン酸カリウム、セチルベンゼンスルホン酸ナトリウム、セチルベンゼンスルホン酸カリウム等のアルキルベンゼンスルホン酸塩;ジ(2-エチルヘキシル)スルホコハク酸ナトリウム、ジ(2-エチルヘキシル)スルホコハク酸カリウム、ジオクチルスルホコハク酸ナトリウム等のアルキルスルホコハク酸塩;ラウリル硫酸ナトリウム、ラウリル硫酸カリウム等のアルキル硫酸エステル塩;ポリオキシエチレンラウリルエーテル硫酸ナトリウム、ポリオキシエチレンラウリルエーテル硫酸カリウム等のポリオキシエチレンアルキルエーテル硫酸エステル塩;ラウリルリン酸ナトリウム、ラウリルリン酸カリウム等のモノアルキルリン酸塩;等が挙げられる。
 これらアニオン性乳化剤の中でも、脂肪酸塩、アルキルベンゼンスルホン酸塩、アルキルスルホコハク酸塩、アルキル硫酸エステル塩およびポリオキシエチレンアルキルエーテル硫酸エステル塩が好ましく、脂肪酸塩およびアルキルベンゼンスルホン酸塩が特に好ましい。
 また、合成ポリイソプレン由来の、微量に残留する重合触媒(特に、アルミニウムとチタニウム)をより効率的に除去でき、ラテックス組成物を製造する際における、凝集物の発生が抑制されることから、アルキルベンゼンスルホン酸塩、アルキルスルホコハク酸塩、アルキル硫酸エステル塩およびポリオキシエチレンアルキルエーテル硫酸エステル塩からなる群から選ばれる少なくとも1種と、脂肪酸塩とを併用して用いることが好ましく、アルキルベンゼンスルホン酸塩と、脂肪酸塩とを併用して用いることが特に好ましい。ここで、脂肪酸塩としては、ロジン酸ナトリウムおよびロジン酸カリウムが好ましく、また、アルキルベンゼンスルホン酸塩としては、ドデシルベンゼンスルホン酸ナトリウムおよびドデシルベンゼンスルホン酸カリウムが好ましい。また、これらの乳化剤は、1種単独でも2種以上を併用してもよい。
 なお、上述したように、アルキルベンゼンスルホン酸塩、アルキルスルホコハク酸塩、アルキル硫酸エステル塩およびポリオキシエチレンアルキルエーテル硫酸エステル塩からなる群から選ばれる少なくとも1種と、脂肪酸塩とを併用して用いることにより、得られるラテックスが、アルキルベンゼンスルホン酸塩、アルキルスルホコハク酸塩、アルキル硫酸エステル塩およびポリオキシエチレンアルキルエーテル硫酸エステル塩の中から選ばれた少なくとも1種と、脂肪酸塩とを含有するものとなる。
 また、アニオン性乳化剤以外のイオン性乳化剤としては、α,β-不飽和カルボン酸のスルホエステル、α,β-不飽和カルボン酸のサルフェートエステル、スルホアルキルアリールエーテル等の共重合性の乳化剤が挙げられる。
 さらに、ディップ成形する際に使用する凝固剤による凝固を阻害しない範囲であれば、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェノールエーテル、ポリオキシエチレンアルキルエステル、ポリオキシエチレンソルビタンアルキルエステル等の非イオン性乳化剤も併用してもよい。
 上記(1)の製造方法で用いる乳化剤の使用量は、合成ポリイソプレン100重量部に対して、好ましくは0.1~50重量部、より好ましくは0.5~30重量部である。なお、2種類以上の乳化剤を用いる場合においては、これらの合計の使用量を上記範囲とすることが好ましい。すなわち、たとえば、アルキルベンゼンスルホン酸塩、アルキルスルホコハク酸塩、アルキル硫酸エステル塩およびポリオキシエチレンアルキルエーテル硫酸エステル塩の中から選ばれた少なくとも1種と、脂肪酸塩とを併用する場合には、これらの使用量の合計を上記範囲とすることが好ましい。乳化剤の使用量を上記範囲とすることにより、乳化時の凝集物の発生をより抑制することができる。
 また、アニオン性乳化剤として、アルキルベンゼンスルホン酸塩、アルキルスルホコハク酸塩、アルキル硫酸エステル塩およびポリオキシエチレンアルキルエーテル硫酸エステル塩の中から選ばれた少なくとも1種と、脂肪酸塩とを併用する場合には、これらの使用割合を、「脂肪酸塩」:「アルキルベンゼンスルホン酸塩、アルキルスルホコハク酸塩、アルキル硫酸エステル塩およびポリオキシエチレンアルキルエーテル硫酸エステル塩の中から選ばれた少なくとも1種の乳化剤の合計」の重量比で、1:1~10:1の範囲とすることが好ましく、1:1~7:1の範囲とすることがより好ましい。アルキルベンゼンスルホン酸塩、アルキルスルホコハク酸塩、アルキル硫酸エステル塩およびポリオキシエチレンアルキルエーテル硫酸エステル塩の中から選ばれた少なくとも1種の乳化剤の使用割合を上記範囲とすることにより、合成ポリイソプレンの取り扱い時に発生する泡立ちを抑制することができ、これにより、長時間の静置や、消泡剤の添加などの操作が不要になり、作業性の改善およびコストダウンに繋がる。
 上記(1)の製造方法で使用する水の量は、合成ポリイソプレンの有機溶媒溶液100重量部に対して、好ましくは10~1,000重量部、より好ましくは30~500重量部、最も好ましくは50~100重量部である。使用する水の種類としては、硬水、軟水、イオン交換水、蒸留水、ゼオライトウォーターなどが挙げられ、軟水、イオン交換水および蒸留水が好ましい。
 有機溶媒に溶解または微分散した合成ポリイソプレンの溶液または微細懸濁液を、乳化剤の存在下、水中で乳化する装置は、一般に乳化機または分散機として市販されているものであれば特に限定されず使用できる。合成ポリイソプレンの溶液または微細懸濁液に、乳化剤を添加する方法としては、特に限定されず、予め、水もしくは合成ポリイソプレンの溶液または微細懸濁液のいずれか、あるいは両方に添加してもよいし、乳化操作を行っている最中に、乳化液に添加してもよく、一括添加しても、分割添加してもよい。
 乳化装置としては、たとえば、商品名「ホモジナイザー」(IKA社製)、商品名「ポリトロン」(キネマティカ社製)、商品名「TKオートホモミキサー」(特殊機化工業社製)等のバッチ式乳化機;商品名「TKパイプラインホモミキサー」(特殊機化工業社製)、商品名「コロイドミル」(神鋼パンテック社製)、商品名「スラッシャー」(日本コークス工業社製)、商品名「トリゴナル湿式微粉砕機」(三井三池化工機社製)、商品名「キャビトロン」(ユーロテック社製)、商品名「マイルダー」(太平洋機工社製)、商品名「ファインフローミル」(太平洋機工社製)等の連続式乳化機;商品名「マイクロフルイダイザー」(みずほ工業社製)、商品名「ナノマイザー」(ナノマイザー社製)、商品名「APVガウリン」(ガウリン社製)等の高圧乳化機;商品名「膜乳化機」(冷化工業社製)等の膜乳化機;商品名「バイブロミキサー」(冷化工業社製)等の振動式乳化機;商品名「超音波ホモジナイザー」(ブランソン社製)等の超音波乳化機;等が挙げられる。なお、乳化装置による乳化操作の条件は、特に限定されず、所望の分散状態になるように、処理温度、処理時間などを適宜選定すればよい。
 上記(1)の製造方法においては、乳化操作を経て得られた乳化物から、有機溶媒を除去することが望ましい。
 乳化物から有機溶媒を除去する方法としては、得られる合成ポリイソプレンラテックス中における、有機溶媒(好ましくは脂環族炭化水素溶媒または脂肪族炭化水素溶媒)の含有量を500重量ppm以下とすることのできる方法が好ましく、たとえば、減圧蒸留、常圧蒸留、水蒸気蒸留、遠心分離等の方法を採用することができる。
 消泡剤を添加しながら、有機溶媒を除去することもできる。消泡剤を添加することにより、合成ポリイソプレンの泡立ちを抑制することができる。
 さらに、有機溶媒を除去した後、必要に応じ、合成ポリイソプレンラテックスの固形分濃度を上げるために、減圧蒸留、常圧蒸留、遠心分離、膜濃縮等の方法で濃縮操作を施してもよく、特に、合成ポリイソプレンラテックスの固形分濃度を上げるとともに、合成ポリイソプレンラテックス中の乳化剤の残留量を低減することができるという観点より、遠心分離を行うことが好ましい。
 遠心分離は、たとえば、連続遠心分離機を用いて、遠心力を、好ましくは100~10,000G、遠心分離前の合成ポリイソプレンラテックスの固形分濃度を、好ましくは2~15重量%、遠心分離機に送り込む流速を、好ましくは500~1700Kg/hr、遠心分離機の背圧(ゲージ圧)を、好ましくは0.03~1.6MPaの条件にて実施することが好ましく、遠心分離後の軽液として、合成ポリイソプレンラテックスを得ることができる。そして、これにより、合成ポリイソプレンラテックス中における、乳化剤の残留量を低減することができる。
 合成ポリイソプレンラテックスの固形分濃度は、好ましくは30~70重量%、より好ましくは40~70重量%、さらに好ましくは50~70重量%である。固形分濃度を上記範囲の下限以上とすることにより、後述するディップ成形体などの膜成形体が破れにくくなる。また、固形分濃度を上記範囲の上限以下とすることにより、合成ポリイソプレンラテックスの粘度が高くなりすぎることを防止し、配管での移送や調合タンク内での撹拌が容易なものとなる。
 合成ポリイソプレンラテックスの体積平均粒子径は、好ましくは0.1~10μm、より好ましくは0.5~3μm、さらに好ましくは0.5~2.0μmである。この体積平均粒子径を上記範囲とすることにより、ラテックス粘度が適度なものとなり取り扱いやすくなるとともに、合成ポリイソプレンラテックスを貯蔵した際に、ラテックス表面に皮膜が生成することを抑制できる。
 また、合成ポリイソプレンラテックスには、ラテックスの分野で通常配合される、pH調整剤、消泡剤、防腐剤、架橋剤、キレート剤、酸素捕捉剤、分散剤、老化防止剤等の添加剤を配合してもよい。
 pH調整剤としては、たとえば、水酸化ナトリウム、水酸化カリウムなどのアルカリ金属の水酸化物;炭酸ナトリウム、炭酸カリウムなどのアルカリ金属の炭酸塩;炭酸水素ナトリウムなどのアルカリ金属の炭酸水素塩;アンモニア;トリメチルアミン、トリエタノールアミンなどの有機アミン化合物;等が挙げられるが、アルカリ金属の水酸化物またはアンモニアが好ましい。
 また、共役ジエン系重合体のラテックスとしては、上述したように、スチレン-イソプレン-スチレンブロック共重合体(SIS)のラテックスを用いることもできる。なお、SISにおいては、「S」はスチレンブロック、「I」はイソプレンブロックをそれぞれ表す。
 SISのラテックスに含まれるSISは、従来公知の方法、たとえばn-ブチルリチウムなどの活性有機金属を開始剤として、不活性重合溶媒中で、イソプレンとスチレンとをブロック共重合して得ることができる。そして、得られたSISの重合体溶液は、SISラテックスの製造にそのまま用いてもよいが、該重合体溶液から固形のSISを取り出した後、その固形のSISを有機溶媒に溶解して、SISラテックスの製造に用いることもできる。SISラテックスの製造方法としては、特に限定されないが、有機溶媒に溶解または微分散したSISの溶液または微細懸濁液を、乳化剤の存在下に、水中で乳化し、必要により有機溶媒を除去して、SISラテックスを製造する方法が好ましい。
 この際、合成した後に重合体溶液中に残った重合触媒の残渣などの不純物を取り除いてもよい。また、重合中または重合後の溶液に、後述する老化防止剤を添加してもよい。また、市販の固形のSISを用いることもできる。
 有機溶媒としては、上記合成ポリイソプレンの場合と同様のものを使用することができ、芳香族炭化水素溶媒および脂環族炭化水素溶媒が好ましく、シクロヘキサンおよびトルエンが特に好ましい。
 なお、有機溶媒の使用量は、SIS100重量部に対して、通常50~2,000重量部、好ましくは80~1,000重量部、より好ましくは100~500重量部、さらに好ましくは150~300重量部である。
 乳化剤としては、上記合成ポリイソプレンの場合と同様のものを例示することができ、アニオン性乳化剤が好適であり、ロジン酸カリウムおよびドデシルベンゼンスルホン酸ナトリウムが特に好ましい。
 乳化剤の使用量は、SIS100重量部に対して、好ましくは0.1~50重量部、より好ましくは0.5~30重量部である。乳化剤の使用量を上記範囲とすることにより、得られるラテックスの安定性を向上させることができる。
 上述したSISラテックスの製造方法で使用する水の量は、SISの有機溶媒溶液100重量部に対して、好ましくは10~1,000重量部、より好ましくは30~500重量部、最も好ましくは50~100重量部である。使用する水の種類としては、硬水、軟水、イオン交換水、蒸留水、ゼオライトウォーターなどが挙げられる。また、メタノールなどのアルコールに代表される極性溶媒を水と併用してもよい。
 SISの有機溶媒溶液または微細懸濁液を、乳化剤の存在下、水中で乳化する装置は、上記合成ポリイソプレンの場合と同様のものを例示することができる。そして、乳化剤の添加方法は、特に限定されず、予め水もしくはSISの有機溶媒溶液または微細懸濁液のいずれか、あるいは両方に添加してもよいし、乳化操作を行っている最中に、乳化液に添加してもよく、一括添加しても、分割添加してもよい。
 上述したSISラテックスの製造方法においては、乳化操作を経て得られた乳化物から、有機溶媒を除去して、SISラテックスを得ることが好ましい。乳化物から有機溶媒を除去する方法は、特に限定されず、減圧蒸留、常圧蒸留、水蒸気蒸留、遠心分離等の方法を採用することができる。
 また、有機溶媒を除去した後、必要に応じ、SISラテックスの固形分濃度を上げるために、減圧蒸留、常圧蒸留、遠心分離、膜濃縮等の方法で濃縮操作を施してもよい。
 消泡剤を添加しながら、有機溶媒を除去することもできる。消泡剤を添加することにより泡立ちを抑制することができる。
 SISラテックスの固形分濃度は、好ましくは30~70重量%、より好ましくは40~70重量%、さらに好ましくは50~70重量%である。固形分濃度を上記範囲の下限以上とすることにより、後述するディップ成形体などの膜成形体が破れにくくなる。また、固形分濃度を上記範囲の上限以下とすることにより、SISラテックスの粘度が高くなりすぎることを防止し、配管での移送や調合タンク内での撹拌が容易なものとなる。
 また、SISラテックスには、ラテックスの分野で通常配合される、pH調整剤、消泡剤、防腐剤、架橋剤、キレート剤、酸素捕捉剤、分散剤、老化防止剤等の添加剤を配合しても良い。pH調整剤としては、上記合成ポリイソプレンの場合と同様のものを例示することができ、アルカリ金属の水酸化物またはアンモニアが好ましい。なお、この際におけるSISラテックスのpHは特に限定されないが、後述するように、SISラテックス等を用いてラテックス組成物とし、該ラテックス組成物を所定の条件で熟成させる際に、熟成前のラテックス組成物のpHが、10以上となっていることが好ましい。
 このようにして得られるSISラテックスに含まれる、SIS中のスチレンブロックにおけるスチレン単位の含有量は、全単量体単位に対して、好ましくは70~100重量%、より好ましくは90~100重量%、さらに好ましくは100重量%である。
 また、SIS中のイソプレンブロックにおけるイソプレン単位の含有量は、全単量体単位に対して、好ましくは70~100重量%、より好ましくは90~100重量%、さらに好ましくは100重量%である。
 なお、SIS中のスチレン単位とイソプレン単位の含有割合は、「スチレン単位:イソプレン単位」の重量比で、通常1:99~90:10、好ましくは3:97~70:30、より好ましくは5:95~50:50、さらに好ましくは10:90~30:70の範囲である。
 SISの重量平均分子量は、ゲル・パーミーエーション・クロマトグラフィー分析による標準ポリスチレン換算で、好ましくは10,000~1,000,000、より好ましくは50,000~500,000、さらに好ましくは100,000~300,000である。SISの重量平均分子量を上記範囲とすることにより、ディップ成形体などの膜成形体の引張強度と柔軟性のバランスが向上するとともに、SISのラテックスが製造しやすくなる傾向がある。
 SISラテックス中のラテックス粒子(SIS粒子)の体積平均粒子径は、好ましくは0.1~10μm、より好ましくは0.5~3μm、さらに好ましくは0.5~2.0μmである。ラテックス粒子の体積平均粒子径を上記範囲とすることにより、ラテックス粘度が適度なものとなり取り扱いやすくなるとともに、SISラテックスを貯蔵した際に、ラテックス表面に皮膜が生成することを抑制できる。
 また、共役ジエン系重合体のラテックスとしては、上述したように、ニトリル基含有共役ジエン系共重合体のラテックスを用いることもできる。
 ニトリル基含有共役ジエン系共重合体は、共役ジエン単量体にエチレン性不飽和ニトリル単量体を共重合してなる共重合体であり、これらに加えて、必要に応じて用いられる、これらと共重合可能な他のエチレン性不飽和単量体を共重合してなる共重合体であってもよい。
 共役ジエン単量体としては、たとえば、1,3-ブタジエン、イソプレン、2,3-ジメチル-1,3-ブタジエン、2-エチル-1,3-ブタジエン、1,3-ペンタジエンおよびクロロプレンなどが挙げられる。これらのなかでも、1,3-ブタジエンおよびイソプレンが好ましく、1,3-ブタジエンがより好ましい。これらの共役ジエン単量体は、単独で、または2種以上を組合せて用いることができる。ニトリル基含有共役ジエン系共重合体中における、共役ジエン単量体により形成される共役ジエン単量体単位の含有割合は、好ましくは56~78重量%であり、より好ましくは56~73重量%、さらに好ましくは56~68重量%である。共役ジエン単量体単位の含有量を上記範囲とすることにより、得られるディップ成形体などの膜成形体を、引張強度を十分なものとしながら、風合いおよび伸びにより優れたものとすることができる。
 エチレン性不飽和ニトリル単量体としては、ニトリル基を含有するエチレン性不飽和単量体であれば特に限定されないが、たとえば、アクリロニトリル、メタクリロニトリル、フマロニトリル、α-クロロアクリロニトリル、α-シアノエチルアクリロニトリルなどが挙げられる。なかでも、アクリロニトリルおよびメタクリロニトリルが好ましく、アクリロニトリルがより好ましい。これらのエチレン性不飽和ニトリル単量体は、単独で、または2種以上を組合せて用いることができる。ニトリル基含有共役ジエン系共重合体中における、エチレン性不飽和ニトリル単量体により形成されるエチレン性不飽和ニトリル単量体単位の含有割合は、好ましくは20~40重量%であり、より好ましくは25~40重量%、さらに好ましくは30~40重量%である。エチレン性不飽和ニトリル単量体単位の含有量を上記範囲とすることにより、得られるディップ成形体などの膜成形体を、引張強度を十分なものとしながら、風合いおよび伸びにより優れたものとすることができる。
 共役ジエン単量体およびエチレン性不飽和ニトリル単量体と共重合可能なその他のエチレン性不飽和単量体としては、たとえば、カルボキシル基を含有するエチレン性不飽和単量体であるエチレン性不飽和カルボン酸単量体;スチレン、アルキルスチレン、ビニルナフタレン等のビニル芳香族単量体;フルオロエチルビニルエーテル等のフルオロアルキルビニルエーテル;(メタ)アクリルアミド、N-メチロール(メタ)アクリルアミド、N,N-ジメチロール(メタ)アクリルアミド、N-メトキシメチル(メタ)アクリルアミド、N-プロポキシメチル(メタ)アクリルアミド等のエチレン性不飽和アミド単量体;(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸ブチル、(メタ)アクリル酸-2-エチルヘキシル、(メタ)アクリル酸トリフルオロエチル、(メタ)アクリル酸テトラフルオロプロピル、マレイン酸ジブチル、フマル酸ジブチル、マレイン酸ジエチル、(メタ)アクリル酸メトキシメチル、(メタ)アクリル酸エトキシエチル、(メタ)アクリル酸メトキシエトキシエチル、(メタ)アクリル酸シアノメチル、(メタ)アクリル酸-2-シアノエチル、(メタ)アクリル酸-1-シアノプロピル、(メタ)アクリル酸-2-エチル-6-シアノヘキシル、(メタ)アクリル酸-3-シアノプロピル、(メタ)アクリル酸ヒドロキシエチル、(メタ)アクリル酸ヒドロキシプロピル、グリシジル(メタ)アクリレート、ジメチルアミノエチル(メタ)アクリレート等のエチレン性不飽和カルボン酸エステル単量体;ジビニルベンゼン、ポリエチレングリコールジ(メタ)アクリレート、ポリプロピレングリコールジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトール(メタ)アクリレート等の架橋性単量体;などを挙げることができる。これらのエチレン性不飽和単量体は単独で、または2種以上を組み合わせて使用することができる。
 エチレン性不飽和カルボン酸単量体としては、カルボキシル基を含有するエチレン性不飽和単量体であれば特に限定されないが、たとえば、アクリル酸、メタクリル酸などのエチレン性不飽和モノカルボン酸単量体;イタコン酸、マレイン酸、フマル酸等のエチレン性不飽和多価カルボン酸単量体;無水マレイン酸、無水シトラコン酸等のエチレン性不飽和多価カルボン酸無水物;フマル酸モノブチル、マレイン酸モノブチル、マレイン酸モノ-2-ヒドロキシプロピル等のエチレン性不飽和多価カルボン酸部分エステル単量体;などが挙げられる。これらのなかでも、エチレン性不飽和モノカルボン酸が好ましく、メタクリル酸が特に好ましい。これらのエチレン性不飽和カルボン酸単量体はアルカリ金属塩またはアンモニウム塩として用いることもできる。また、エチレン性不飽和カルボン酸単量体は単独で、または2種以上を組合せて用いることができる。ニトリル基含有共役ジエン系共重合体中における、エチレン性不飽和カルボン酸単量体により形成されるエチレン性不飽和カルボン酸単量体単位の含有割合は、好ましくは2~5重量%であり、より好ましくは2~4.5重量%、さらに好ましくは2.5~4.5重量%である。エチレン性不飽和カルボン酸単量体単位の含有量を上記範囲とすることにより、得られるディップ成形体などの膜成形体を、引裂強度を十分なものとしながら、風合いにより優れたものとすることができる。
 ニトリル基含有共役ジエン系共重合体中における、その他のエチレン性不飽和単量体により形成されるその他の単量体単位の含有割合は、好ましくは10重量%以下であり、より好ましくは5重量%以下、さらに好ましくは3重量%以下である。
 ニトリル基含有共役ジエン系共重合体は、上述した単量体を含有してなる単量体混合物を共重合することにより得られるが、乳化重合により共重合する方法が好ましい。乳化重合方法としては、従来公知の方法を採用することができる。
 上述した単量体を含有してなる単量体混合物を乳化重合する際には、通常用いられる、乳化剤、重合開始剤、分子量調整剤等の重合副資材を使用することができる。これら重合副資材の添加方法は特に限定されず、初期一括添加法、分割添加法、連続添加法などいずれの方法でもよい。
 乳化剤としては、特に限定されないが、たとえば、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェノールエーテル、ポリオキシエチレンアルキルエステル、ポリオキシエチレンソルビタンアルキルエステル等の非イオン性乳化剤;ドデシルベンゼンスルホン酸カリウム、ドデシルベンゼンスルホン酸ナトリウムなどのアルキルベンゼンスルホン酸塩、高級アルコール硫酸エステル塩、アルキルスルホコハク酸塩等のアニオン性乳化剤;アルキルトリメチルアンモニウムクロライド、ジアルキルアンモニウムクロライド、ベンジルアンモニウムクロライド等のカチオン性乳化剤;α,β-不飽和カルボン酸のスルホエステル、α,β-不飽和カルボン酸のサルフェートエステル、スルホアルキルアリールエーテル等の共重合性乳化剤などを挙げることができる。なかでも、アニオン性乳化剤が好ましく、アルキルベンゼンスルホン酸塩がより好ましく、ドデシルベンゼンスルホン酸カリウムおよびドデシルベンゼンスルホン酸ナトリウムが特に好ましい。これらの乳化剤は、単独で、または2種以上を組合せて用いることができる。乳化剤の使用量は、単量体混合物100重量部に対して、好ましくは0.1~10重量部である。
 重合開始剤としては、特に限定されないが、たとえば、過硫酸ナトリウム、過硫酸カリウム、過硫酸アンモニウム、過リン酸カリウム、過酸化水素等の無機過酸化物;ジイソプロピルベンゼンハイドロパーオキサイド、クメンハイドロパーオキサイド、t-ブチルハイドロパーオキサイド、1,1,3,3-テトラメチルブチルハイドロパーオキサイド、2,5-ジメチルヘキサン-2,5-ジハイドロパーオキサイド、ジ-t-ブチルパーオキサイド、ジ-α-クミルパーオキサイド、アセチルパーオキサイド、イソブチリルパーオキサイド、ベンゾイルパーオキサイド等の有機過酸化物;アゾビスイソブチロニトリル、アゾビス-2,4-ジメチルバレロニトリル、アゾビスイソ酪酸メチル等のアゾ化合物;などを挙げることができる。これらの重合開始剤は、それぞれ単独で、または2種類以上を組み合わせて使用することができる。重合開始剤の使用量は、単量体混合物100重量部に対して、好ましくは0.01~10重量部、より好ましくは0.01~2重量部である。
 また、過酸化物開始剤は還元剤との組み合わせで、レドックス系重合開始剤として使用することができる。この還元剤としては、特に限定されないが、硫酸第一鉄、ナフテン酸第一銅等の還元状態にある金属イオンを含有する化合物;メタンスルホン酸ナトリウム等のスルホン酸化合物;ジメチルアニリン等のアミン化合物;などが挙げられる。これらの還元剤は単独で、または2種以上を組合せて用いることができる。還元剤の使用量は、過酸化物100重量部に対して3~1000重量部であることが好ましい。
 乳化重合する際に使用する水の量は、使用する全単量体100重量部に対して、80~600重量部が好ましく、100~200重量部が特に好ましい。
 単量体の添加方法としては、たとえば、反応容器に使用する単量体を一括して添加する方法、重合の進行に従って連続的または断続的に添加する方法、単量体の一部を添加して特定の転化率まで反応させ、その後、残りの単量体を連続的または断続的に添加して重合する方法等が挙げられ、いずれの方法を採用してもよい。単量体を混合して連続的または断続的に添加する場合、混合物の組成は、一定としても、あるいは変化させてもよい。また、各単量体は、使用する各種単量体を予め混合してから反応容器に添加しても、あるいは別々に反応容器に添加してもよい。
 さらに、必要に応じて、キレート剤、分散剤、pH調整剤、脱酸素剤、粒子径調整剤等の重合副資材を用いることもでき、これらは種類、使用量とも特に限定されない。
 乳化重合を行う際の重合温度は、特に限定されないが、通常、3~95℃、好ましくは5~60℃である。重合時間は5~40時間程度である。
 以上のように単量体混合物を乳化重合し、所定の重合転化率に達した時点で、重合系を冷却したり、重合停止剤を添加したりして、重合反応を停止する。重合反応を停止する際の重合転化率は、好ましくは90重量%以上、より好ましくは93重量%以上である。
 重合停止剤としては、特に限定されないが、たとえば、ヒドロキシルアミン、ヒドロキシアミン硫酸塩、ジエチルヒドロキシルアミン、ヒドロキシアミンスルホン酸およびそのアルカリ金属塩、ジメチルジチオカルバミン酸ナトリウム、ハイドロキノン誘導体、カテコール誘導体、ならびに、ヒドロキシジメチルベンゼンチオカルボン酸、ヒドロキシジエチルベンゼンジチオカルボン酸、ヒドロキシジブチルベンゼンジチオカルボン酸などの芳香族ヒドロキシジチオカルボン酸およびこれらのアルカリ金属塩などが挙げられる。重合停止剤の使用量は、単量体混合物100重量部に対して、好ましくは0.05~2重量部である。
 重合反応を停止した後、所望により、未反応の単量体を除去し、固形分濃度やpHを調整することで、ニトリル基含有共役ジエン系共重合体のラテックスを得ることができる。
 また、ニトリル基含有共役ジエン系共重合体のラテックスには、必要に応じて、老化防止剤、防腐剤、抗菌剤、分散剤などを適宜添加してもよい。
 ニトリル基含有共役ジエン系共重合体のラテックスの数平均粒子径は、好ましくは60~300nm、より好ましくは80~150nmである。粒子径は、乳化剤および重合開始剤の使用量を調節するなどの方法により、所望の値に調整することができる。
 また、共役ジエン系重合体のラテックスとして、上述したように、蛋白質を除去した天然ゴム(脱蛋白質天然ゴム)のラテックスを用いることもできる。脱蛋白質天然ゴムのラテックスとしては、天然ゴムラテックス中の蛋白質を、たとえば蛋白質分解酵素や界面活性剤などにより分解し、洗浄や遠心分離などにより除去する方法などの、公知の蛋白質除去法により得られる、いわゆる「脱蛋白質天然ゴムラテックス」として知られているものを用いることができる。
 本発明で用いる共役ジエン系重合体としては、上述したように、合成ポリイソプレン、スチレン-イソプレン-スチレンブロック共重合体(SIS)、ニトリル基含有共役ジエン系共重合体、脱蛋白質天然ゴムなどを用いることができるが、これらに限定されず、ブタジエン重合体、スチレン-ブタジエン共重合体などを用いてもよい。
 ブタジエン重合体は、共役ジエン単量体としての1,3-ブタジエンの単独重合体であってもよいし、共役ジエン単量体としての1,3-ブタジエンと共重合可能な他のエチレン性不飽和単量体とを共重合してなる共重合体であってもよい。
 また、スチレン-ブタジエン共重合体は、共役ジエン単量体としての1,3-ブタジエンにスチレンを共重合してなる共重合体であり、これらに加えて、必要に応じて用いられる、これらと共重合可能な他のエチレン性不飽和単量体を共重合してなる共重合体であってもよい。
 また、本発明で用いる共役ジエン系重合体は、酸性基を有する単量体により変性して得られる酸変性共役ジエン系重合体であってもよく、カルボキシ変性されたカルボキシ変性共役ジエン系重合体であることが好ましい。カルボキシ変性共役ジエン系重合体は、上述した共役ジエン系重合体を、カルボキシル基を有する単量体により変性することにより得ることができる。なお、ニトリル基含有共役ジエン系共重合体として、可能なその他のエチレン性不飽和単量体として、エチレン性不飽和カルボン酸単量体を使用した場合には、既にカルボキシ変性されているため、後述するカルボキシル基を有する単量体による変性は、必ずしも必要でない。
 共役ジエン系重合体を、カルボキシル基を有する単量体により変性する方法としては、特に限定されないが、たとえば、共役ジエン系重合体に、カルボキシル基を有する単量体を水相中でグラフト重合する方法が挙げられる。カルボキシル基を有する単量体を水相中でグラフト重合する方法としては、特に限定されず、従来公知の方法を用いればよいが、たとえば、共役ジエン系重合体のラテックスに、カルボキシル基を有する単量体と、グラフト重合触媒とを添加した後、水相中で、共役ジエン系重合体に、カルボキシル基を有する単量体を反応させる方法が好ましい。
 グラフト重合触媒としては、特に限定されないが、たとえば、過硫酸ナトリウム、過硫酸カリウム、過硫酸アンモニウム、過リン酸カリウム、過酸化水素等の無機過酸化物;ジイソプロピルベンゼンハイドロパーオキサイド、クメンハイドロパーオキサイド、t-ブチルハイドロパーオキサイド、1,1,3,3-テトラメチルブチルハイドロパーオキサイド、ジ-t-ブチルパーオキサイド、イソブチリルパーオキサイド、ベンゾイルパーオキサイド等の有機過酸化物;2,2’-アゾビスイソブチロニトリル、アゾビス-2,4-ジメチルバレロニトリル、アゾビスイソ酪酸メチル等のアゾ化合物;等を挙げることができるが、得られるディップ成形体などの膜成形体の引張強度がより向上するという観点から、有機過酸化物が好ましく、1,1,3,3-テトラメチルブチルハイドロパーオキサイドが特に好ましい。これらのグラフト重合触媒は、1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。
 上記グラフト重合触媒は、それぞれ単独で、あるいは2種類以上を組み合わせて使用することができる。グラフト重合触媒の使用量は、その種類によって異なるが、共役ジエン系重合体100重量部に対して、好ましくは0.1~10重量部、より好ましくは0.2~5重量部である。また、グラフト重合触媒を添加する方法としては、特に限定されず、一括添加、分割添加、連続添加等の公知の添加方法を採用することができる。
 また、有機過酸化物は、還元剤との組み合わせで、レドックス系重合開始剤として使用することができる。還元剤としては、特に限定されないが、たとえば、硫酸第一鉄、ナフテン酸第一銅等の還元状態にある金属イオンを含有する化合物;ヒドロキシメタンスルフィン酸ナトリウムなどのスルフィン酸塩;ジメチルアニリン等のアミン化合物;等が挙げられる。これらの還元剤は、1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。
 還元剤の添加量は、特に限定されないが、有機過酸化物1重量部に対して0.01~1重量部であることが好ましい。
 有機過酸化物および還元剤の添加方法は、特に限定されず、それぞれ、一括添加、分割添加、連続添加等の公知の添加方法を用いることができる。
 共役ジエン系重合体にカルボキシル基を有する単量体を反応させる際の反応温度は、特に限定されないが、好ましくは15~80℃、より好ましくは30~50℃である。共役ジエン系重合体にカルボキシル基を有する単量体を反応させる際の反応時間は、上記反応温度に応じて適宜設定すればよいが、好ましくは30~300分間、より好ましくは60~120分間である。
 共役ジエン系重合体にカルボキシル基を有する単量体を反応させる際における、共役ジエン系重合体のラテックスの固形分濃度は、特に限定されないが、好ましくは5~60重量%、より好ましくは10~40重量%である。
 カルボキシル基を有する単量体としては、たとえば、アクリル酸、メタクリル酸等のエチレン性不飽和モノカルボン酸単量体;イタコン酸、マレイン酸、フマル酸、ブテントリカルボン酸等のエチレン性不飽和多価カルボン酸単量体;フマル酸モノブチル、マレイン酸モノブチル、マレイン酸モノ2-ヒドロキシプロピル等のエチレン性不飽和多価カルボン酸の部分エステル単量体;無水マレイン酸、無水シトラコン酸等の多価カルボン酸無水物;などを挙げることができるが、カルボキシ変性による効果がより一層顕著になることから、エチレン性不飽和モノカルボン酸単量体が好ましく、アクリル酸およびメタクリル酸がより好ましく、メタクリル酸が特に好ましい。なお、これらの単量体は1種単独でも、2種以上を併用して用いてもよい。また、上記カルボキシル基は、アルカリ金属やアンモニア等との塩になっているものも含まれる。
 カルボキシル基を有する単量体の使用量は、共役ジエン系重合体100重量部に対して、好ましくは0.01~100重量部、より好ましくは0.01~40重量部、さらに好ましくは0.5~20重量部、よりさらに好ましくは2~5重量部である。カルボキシル基を有する単量体の使用量を上記範囲とすることにより、得られるラテックス組成物の粘度がより適度なものとなり、移送しやすくなるとともに、得られるラテックス組成物を用いて形成されるディップ成形体などの膜成形体の引裂強度がより向上する。
 カルボキシル基を有する単量体を共役ジエン系重合体のラテックスに添加する方法としては、特に限定されず、一括添加、分割添加、連続添加等の公知の添加方法を採用することができる。
 カルボキシ変性共役ジエン系重合体におけるカルボキシル基を有する単量体による変性率は、得られる共役ジエン系重合体ラテックス組成物の使用目的に応じて適宜制御すればよいが、好ましくは0.01~10重量%、より好ましくは0.2~5重量%であり、さらに好ましくは0.3~3重量%、特に好ましくは0.4~2重量%、たとえば0.4~1重量%である。なお、変性率は、下記式で表される。
  変性率(重量%)=(X/Y)×100
 なお、上記式においては、Xは、カルボキシ変性共役ジエン系重合体中における、カルボキシル基を有する単量体の単位の重量を、Yは、カルボキシ変性共役ジエン系重合体の重量をそれぞれ表す。Xは、カルボキシ変性共役ジエン系重合体について、H-NMR測定を行い、H-NMR測定の結果から算出する方法、あるいは、中和滴定により酸量を求め、求めた酸量から算出する方法などにより求めることができる。
 本発明で用いる共役ジエン系重合体(酸変性された共役ジエン系重合体を含む)のラテックスには、ラテックスの分野で通常配合される、pH調整剤、消泡剤、防腐剤、キレート化剤、酸素捕捉剤、分散剤、老化防止剤等の添加剤を配合してもよい。
 pH調整剤としては、たとえば、水酸化ナトリウム、水酸化カリウムなどのアルカリ金属の水酸化物;炭酸ナトリウム、炭酸カリウムなどのアルカリ金属の炭酸塩;炭酸水素ナトリウムなどのアルカリ金属の炭酸水素塩;アンモニア;トリメチルアミン、トリエタノールアミンなどの有機アミン化合物;等が挙げられるが、アルカリ金属の水酸化物またはアンモニアが好ましい。
 本発明で用いる共役ジエン系重合体(酸変性された共役ジエン系重合体を含む)のラテックスの固形分濃度は、好ましくは30~70重量%、より好ましくは40~70重量%、さらに好ましくは50~70重量%である。固形分濃度を上記範囲とすることにより、ラテックス中における凝集物の発生をより有効に抑制することができるとともに、ラテックスを貯蔵した際における重合体粒子の分離をより有効に抑制することができる。
 本発明のラテックス組成物は、上述した共役ジエン系重合体のラテックスに、硫黄系加硫剤の水分散液およびキサントゲン化合物を配合することにより、得ることができる。
 硫黄系加硫剤の水分散液は、硫黄系加硫剤を、アニオン系界面活性剤を用いて水中に分散させたものである。
 硫黄系加硫剤は、常温で固体であり、水に溶解しないため、通常は、粉末状態で用いられるものである。その一方で、本発明者等が検討したところ、硫黄系加硫剤を粉末状態のまま、キサントゲン化合物とともに、共役ジエン系重合体を含むラテックス組成物に配合すると、得られるディップ成形体などの膜成形体の引張強度や引裂強度などの機械的強度、および機械的強度の安定性が不十分になってしまうこと、これに対し、硫黄系加硫剤を、アニオン系界面活性剤を用いた水分散液の状態で、共役ジエン系重合体を含むラテックス組成物に配合することにより、得られるディップ成形体などの膜成形体の引張強度や引裂強度などの機械的強度、および機械的強度の安定性を向上させることを見出したものである。特に、本発明者等によれば、硫黄系加硫剤を粉末状態のまま、共役ジエン系重合体を含むラテックス組成物に配合した場合における、引張強度や引裂強度などの機械的強度、および機械的強度の安定性が不十分となってしまうとの課題は、硫黄系加硫剤を、キサントゲン化合物と組み合わせて用いた場合において発生する特有の課題であること、および、これに対し、硫黄系加硫剤を、アニオン系界面活性剤を用いた水分散液の状態で配合することにより、このようなキサントゲン化合物と組み合わせて用いた場合における特有の課題を解決できることを見出したものである。加えて、本発明者等によれば、硫黄系加硫剤を、アニオン系界面活性剤を用いた水分散液の状態で配合することにより、硫黄系加硫剤の使用量を比較的少なくした場合でも、十分な機械的強度、および機械的強度の十分な安定性を達成できることも見出したものであり、このように硫黄系加硫剤の使用量を低減できることにより、得られるディップ成形体などの膜成形体を、より均一な加硫密度を有するものしつつ、過加硫を抑制することもできるものである。
 硫黄系加硫剤としては、特に限定されないが、たとえば、粉末硫黄、硫黄華、沈降硫黄、コロイド硫黄、表面処理硫黄、不溶性硫黄等の硫黄;塩化硫黄、二塩化硫黄、モルホリン・ジスルフィド、アルキルフェノールジスルフィド、カプロラクタムジスルフィド(N,N’-ジチオ-ビス(ヘキサヒドロ-2H-アゼピノン-2))、含りんポリスルフィド、高分子多硫化物、2-(4’-モルホリノジチオ)ベンゾチアゾール等の硫黄含有化合物が挙げられる。これらのなかでも、硫黄が好ましく使用できる。硫黄系加硫剤は、1種単独で、あるいは2種以上を組み合わせて用いることができる。
 硫黄系加硫剤の水分散液中における硫黄系加硫剤の体積平均粒子径は、好ましくは0.01~10μmであり、より好ましくは0.1~5μm、さらに好ましくは0.5~2μmである。硫黄系加硫剤の体積平均粒子径を上記範囲とすることにより、硫黄系加硫剤の水分散液中における硫黄系加硫剤の分散性を高めることができる。
 硫黄系加硫剤の水分散液中における、硫黄系加硫剤の含有割合は、硫黄系加硫剤の水分散液全体に対して、好ましくは30~70重量%であり、より好ましくは40~60重量%である。硫黄系加硫剤の含有割合を上記範囲とすることにより、得られるディップ成形体などの膜成形体において、遅延型アレルギー(Type IV)の症状の発生を抑制しながら、引張強度をより高めることができる。
 アニオン系界面活性剤としては、特に限定されないが、たとえば、芳香族スルホン酸の誘導体、脂肪酸塩、アルキルベンゼンスルホン酸塩、アルキルスルホコハク酸塩、アルキル硫酸エステル塩、ポリオキシエチレンアルキルエーテル硫酸エステル塩、モノアルキルリン酸塩などが好ましく、芳香族スルホン酸の誘導体がより好ましい。なお、上記アニオン系界面活性剤は、それぞれ単独で、あるいは2種類以上を組み合わせて使用することができる。
 芳香族スルホン酸の誘導体としては、特に限定されないが、下記一般式(1)で表される化合物が好ましい。
Figure JPOXMLDOC01-appb-C000001
 (上記一般式(1)中、RおよびRは、それぞれ独立して、水素原子または任意の有機基であり、RおよびRは互いに結合して環構造を形成していてもよい。)
 RおよびRが互いに結合しない場合に、RおよびRとなりうる有機基としては、特に限定されないが、メチル基、エチル基、n-プロピル基、イソプロピル基、n-ブチル基、イソブチル基、sec-ブチル基、t-ブチル基、n-ペンチル基、n-ヘキシル基、n-ヘプチル基、n-オクチル基、n-ノニル基、n-デシル基などの炭素数1~30のアルキル基;シクロプロピル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基、シクロオクチル基などの炭素数3~30のシクロアルキル基;フェニル基、ビフェニル基、ナフチル基、アントラニル基などの炭素数6~30のアリール基;メトキシ基、エトキシ基、n-プロポキシ基、イソプロポキシ基、n-ブトキシ基、イソブトキシ基、sec-ブトキシ基、t-ブトキシ基、n-ペンチルオキシ基、n-ヘキシルオキシ基、フェノキシ基などの炭素数1~30のアルコキシ基;などが挙げられる。なお、これらの有機基は、置換基を有していてもよく、該置換基の位置としては、任意の位置とすることができる。
 また、RおよびRが互いに結合して環構造を形成する場合には、環構造としては、特に限定されないが、芳香族化合物が好ましく、ベンゼン、ナフタレンなどのベンゼン環を有する芳香族化合物がより好ましく、ナフタレンが特に好ましい。なお、これらの環構造は、置換基を有していてもよく、該置換基の位置としては、任意の位置とすることができる。
 本発明においては、芳香族スルホン酸の誘導体としては、上記一般式(1)で表される化合物の中でも、特に好ましいものとして、RおよびRが互いに結合して環構造を形成して、上記一般式(1)においてベンゼン環構造を形成しているものが挙げられる。より具体的には、下記一般式(2)で表される構造を有する化合物を用いることが好ましい。
Figure JPOXMLDOC01-appb-C000002
 (上記一般式(2)中、Rは、置換基を有していてもよい2価の炭化水素基である。)
 上記一般式(2)において、Rは、置換基を有していてもよい2価の炭化水素基であればよく、特に限定されないが、炭素数1~10のアルキレン基が好ましく、メチレン基が特に好ましい。
 また、芳香族スルホン酸の誘導体としては、上記一般式(2)で表される構造を繰り返して有することが好ましく、上記一般式(2)で表される構造の繰り返し単位数は、特に限定されないが、好ましくは10~100個、より好ましくは20~50個である。
 芳香族スルホン酸の誘導体の重量平均分子量は、好ましくは500~100,000、より好ましくは3,000~50,000、さらに好ましくは5,000~30,000である。
 硫黄系加硫剤の水分散液中における、アニオン系界面活性剤の含有量は、特に限定されないが、硫黄系加硫剤100重量部に対して、好ましくは0.01~10重量部、より好ましくは0.1~8重量部、さらに好ましくは3~7重量部である。アニオン系界面活性剤の含有量を上記範囲とすることにより、硫黄系加硫剤の水分散液中における、硫黄系加硫剤の分散性をより高めることができ、これにより、得られるディップ成形体などの膜成形体の、引張強度および引裂強度をより高めることができ、かつ、引張強度および引裂強度の安定性をより高めることができる。
 硫黄系加硫剤の水分散液の製造方法としては、硫黄系加硫剤と、アニオン系界面活性剤と、水とを混合し、次いで、得られた混合液について解砕処理を行う方法が好ましい。ここで、解砕処理としては、水分散液中に含有される、硫黄系加硫剤の破砕や凝集の緩和を可能とすることができる処理であればよく、特に限定されないが、たとえば、せん断作用や摩砕作用を利用した解砕装置を用いる方法、攪拌式の解砕装置を用いる方法など、公知の解砕装置を用いる方法が挙げられる。具体的には、ロールミル、ハンマーミル、振動ミル、ジェットミル、ボールミル、遊星型ボールミル、ビーズミル、サンドミル、三本ロールミル等の解砕装置を使用することができる。これらのなかでも、ボールミル、遊星型ボールミル、またはビーズミルを使用して解砕処理を行う方法が好適である。
 たとえば、ボールミルを用いて解砕処理を行う場合には、メディアとして、メディアサイズが、好ましくはφ5~φ50mm、より好ましくはφ10~φ35mmであるものを使用し、回転数が、好ましくは10~300rpm、より好ましくは10~100rpm、処理時間が、好ましくは24~120時間、より好ましくは24~72時間の条件にて、解砕処理を行うことが好適である。また、遊星型ボールミルを用いて解砕処理を行う場合には、メディアとして、メディアサイズが、好ましくはφ0.1~φ5mm、より好ましくはφ0.3~φ3mmであるものを使用し、回転数が、好ましくは100~1000rpm、より好ましくは100~500rpm、処理時間が、好ましくは0.25~5時間、より好ましくは0.25~3時間の条件にて、解砕処理を行うことが好適である。さらに、ビーズミルを用いて解砕処理を行う場合には、メディアとして、メディアサイズが、好ましくはφ0.1~φ3mm、より好ましくはφ0.1~φ1mmであるものを使用し、回転数が、好ましくは1000~10000rpm、より好ましくは1000~5000rpm、処理時間が、好ましくは0.25~5時間、より好ましくは0.25~3時間の条件にて、解砕処理を行うことが好適である。
 本発明のラテックス組成物中における、硫黄系加硫剤の水分散液の配合量は、ラテックス組成物に含まれる共役ジエン系重合体100重量部に対する、硫黄系加硫剤の含有量が、好ましくは0.1~1.0重量部となる量、より好ましくは0.1~0.8重量部となる量、さらに好ましくは0.1~0.6重量部となる量、特に好ましくは0.2~0.6重量部となる量である。硫黄系加硫剤の水分散液の配合量を上記範囲とすることにより、得られるディップ成形体などの膜成形体において、遅延型アレルギー(Type IV)の症状の発生を抑制しながら、引裂強度をより高めることができる。本発明においては、硫黄系加硫剤を、アニオン系界面活性剤を用いた水分散液の状態でラテックス組成物に配合することにより、硫黄系加硫剤の配合量を比較的少なくした場合でも、十分な機械的強度、および機械的強度の十分な安定性を達成できるものである。
 本発明で用いるキサントゲン化合物は、硫黄系加硫剤と組み合わせて用いることで、加硫促進剤として作用する。すなわち、ラテックス組成物に、硫黄系加硫剤の水分散液として硫黄系加硫剤を配合し、ラテックス組成物中の共役ジエン系重合体を硫黄系加硫剤により加硫して、ディップ成形体などの膜成形体とする場合に、キサントゲン化合物は、加硫促進剤として作用する。また、キサントゲン化合物は、硫黄系加硫剤が配合されたラテックス組成物中において、加硫促進剤として作用し、加硫が行われた後に、加硫時に加わる熱等により、アルコールおよび二硫化炭素等に分解されるものである。たとえば、キサントゲン化合物は、膜成形体を製造する際に加わる熱(共役ジエン系重合体を加硫させる際における100~130℃程度の熱)によって、アルコールおよび二硫化炭素等に分解され、さらに、分解により生成した成分(アルコールおよび二硫化炭素等)が揮発する。これにより、得られる膜成形体は、キサントゲン化合物の残留量が低減されたものとなる。すなわち、本発明のラテックス組成物は、従来、遅延型アレルギー(Type IV)の症状の発生原因となっていた加硫促進剤(たとえば、ジチオカルバミン酸塩系加硫促進剤、チアゾール系加硫促進剤など)を含有することなく、キサントゲン化合物を加硫促進剤として含有するため、これにより、得られるディップ成形体などの膜成形体におけるキサントゲン化合物の残留量を低減させることができるため、得られる膜成形体について、遅延型アレルギー(Type IV)の症状の発生を抑制することが可能となる。
 キサントゲン化合物としては、特に限定されないが、たとえば、キサントゲン酸、キサントゲン酸塩、キサントゲン二硫化物(2つのキサントゲン酸が硫黄原子等を介して結合された化合物)、キサントゲン多硫化物(3以上のキサントゲン酸が硫黄原子等を介して結合された化合物)などが挙げられる。
 キサントゲン酸塩としては、キサントゲン酸構造を有するものであればよく、特に限定されないが、たとえば、一般式(ROC(=S)S)x-Z(ここで、Rは直鎖状または分岐状の炭化水素、Zは金属原子である。xはZの原子価と一致する数で、通常1~4、好ましくは2~4、特に好ましくは2である。)で表される化合物が挙げられる。
 上記一般式(ROC(=S)S)x-Zで表されるキサントゲン酸塩としては、特に限定されないが、たとえば、ジメチルキサントゲン酸亜鉛、ジエチルキサントゲン酸亜鉛、ジプロピルキサントゲン酸亜鉛、ジイソプロピルキサントゲン酸亜鉛、ジブチルキサントゲン酸亜鉛、ジペンチルキサントゲン酸亜鉛、ジヘキシルキサントゲン酸亜鉛、ジヘプチルキサントゲン酸亜鉛、ジオクチルキサントゲン酸亜鉛、ジ(2-エチルヘキシル)キサントゲン酸亜鉛、ジデシルキサントゲン酸亜鉛、ジドデシルキサントゲン酸亜鉛、ジメチルキサントゲン酸カリウム、エチルキサントゲン酸カリウム、プロピルキサントゲン酸カリウム、イソプロピルキサントゲン酸カリウム、ブチルキサントゲン酸カリウム、ペンチルキサントゲン酸カリウム、ヘキシルキサントゲン酸カリウム、ヘプチルキサントゲン酸カリウム、オクチルキサントゲン酸カリウム、2-エチルヘキシルキサントゲン酸カリウム、デシルキサントゲン酸カリウム、ドデシルキサントゲン酸カリウム、メチルキサントゲン酸ナトリウム、エチルキサントゲン酸ナトリウム、プロピルキサントゲン酸ナトリウム、イソプロピルキサントゲン酸ナトリウム、ブチルキサントゲン酸ナトリウム、ペンチルキサントゲン酸ナトリウム、ヘキシルキサントゲン酸ナトリウム、ヘプチルキサントゲン酸ナトリウム、オクチルキサントゲン酸ナトリウム、2-エチルヘキシルキサントゲン酸ナトリウム、デシルキサントゲン酸ナトリウム、ドデシルキサントゲン酸ナトリウム等が挙げられる。これらのなかでも、上記一般式(ROC(=S)S)x-Zにおけるxが2以上であるキサントゲン酸塩が好ましく、イソプロピルキサントゲン酸塩類、ブチルキサントゲン酸塩類がより好ましく、ジイソプロピルキサントゲン酸亜鉛、ジブチルキサントゲン酸亜鉛が特に好ましい。これらのキサントゲン酸塩は、1種単独でも、複数種を併用してもよい。
 キサントゲン二硫化物は、2つのキサントゲン酸が硫黄原子等を介して結合された化合物であり、特に限定されないが、ジメチルキサントゲンジスルフィド、ジエチルキサントゲンジスルフィド、ジイソプロピルキサントゲンジスルフィド、ジブチルキサントゲンジスルフィド、ジメチルキサントゲンポリスルフィド、ジエチルキサントゲンポリスルフィド、ジイソプロピルキサントゲンポリスルフィド、ジブチルキサントゲンポリスルフィドなどが挙げられ、これらのなかでも、ジイソプロピルキサントゲンジスルフィド、ジブチルキサントゲンジスルフィドが好ましい。
 キサントゲン多硫化物は、3以上のキサントゲン酸が硫黄原子等を介して結合された化合物であり、3つのキサントゲン酸が硫黄を介して結合されたキサントゲン三硫化物、4つのキサントゲン酸が硫黄を介して結合されたキサントゲン四硫化物、5つのキサントゲン酸が硫黄を介して結合されたキサントゲン五硫化物などが挙げられる。
 以上に例示したキサントゲン化合物のなかでも、得られるディップ成形体などの膜成形体の引裂強度をより高めることができるという観点より、キサントゲン酸塩が好ましく、ジイソプロピルキサントゲン酸亜鉛、ジブチルキサントゲン酸亜鉛が特に好ましい。
 なお、これらのキサントゲン化合物は、ラテックス組成物に、1種単独で含まれていてもよいが、2種以上が含まれていることが好ましい。たとえば、ラテックス組成物にキサントゲン酸を配合した場合には、配合したキサントゲン酸の一部が、キサントゲン酸塩の形態で存在することで、結果として、ラテックス組成物に2種以上のキサントゲン化合物が含まれることになってもよい。あるいは、ラテックス組成物に配合したキサントゲン酸の一部が、ラテックス組成物中の硫黄系加硫剤の作用により、キサントゲン二硫化物やキサントゲン多硫化物の形態で存在してもよい。同様に、ラテックス組成物にキサントゲン酸塩、キサントゲン二硫化物またはキサントゲン多硫化物を配合した場合においても、これらは、それぞれ、キサントゲン酸、キサントゲン酸塩、キサントゲン二硫化物、キサントゲン多硫化物のいずれかの形態で存在してもよい。
 キサントゲン化合物の使用量(複数のキサントゲン化合物が含まれることとなる場合には、その合計の使用量)は、ラテックスに含まれる共役ジエン系重合体100重量部に対して、好ましくは0.01~10重量部、より好ましくは0.1~7重量部、さらに好ましくは0.5~5重量部、よりさらに好ましくは1~3重量部である。キサントゲン化合物の使用量を上記範囲とすることにより、得られるディップ成形体などの膜成形体について、遅延型アレルギー(Type IV)の症状の発生を抑制しながら、引張強度をより向上させることができる。
 キサントゲン化合物としては、どのような方法で共役ジエン系重合体ラテックスに配合されたものであってもよく、特に限定されないが、たとえば、界面活性剤を用いて水中に分散させた水分散液の状態で、共役ジエン系重合体ラテックスに配合されたものであることが好ましい。すなわち、キサントゲン化合物を、界面活性剤を用いて水中に分散させることにより、キサントゲン化合物の水分散液を得た後、得られたキサントゲン化合物の水分散液を、共役ジエン系重合体ラテックスに配合することが好ましい。
 キサントゲン化合物を、水中に分散させる際に用いる界面活性剤としては、特に限定されないが、たとえば、ノニオン系界面活性剤、ノニオニックアニオン系界面活性剤、アニオン系界面活性剤等を挙げることができ、これらの中でも、得られるラテックス組成物を長期間熟成後に得られるディップ成形体などの膜成形体の引張強度をより優れたものとすることができるという観点より、ノニオン系界面活性剤、ノニオニックアニオン系界面活性剤を用いることが好ましい。
 キサントゲン化合物を水中に分散させる際に用いるアニオン系界面活性剤としては、特に限定されないが、硫黄系加硫剤の水分散液において硫黄系加硫剤を水中に分散させる際に用いるアニオン系界面活性剤と同様のものを挙げることができる。
 キサントゲン化合物を水中に分散させる際に用いるノニオン系界面活性剤としては、その分子主鎖中に、非イオン性の界面活性剤として作用するセグメントを有するものであれば、特に限定されないが、このような非イオン性の界面活性剤として作用するセグメントとしては、ポリオキシアルキレン構造が好適に挙げられる。
 ノニオン系界面活性剤の具体例としては、ポリオキシアルキレングリコール、ポリオキシアルキレンアルキルエーテル、ポリオキシアルキレンアルキルフェニルエーテル、ポリオキシエチレンスチレン化フェニルエーテル、ポリオキシエチレン(硬化)ヒマシ油、ポリオキシエチレンアルキルアミン、脂肪酸アルカノールアミドなどが挙げられる。
 ポリオキシアルキレングリコールとしては、たとえば、ポリオキシエチレングリコール、ポリオキシプロピレングリコール、ポリオキシエチレンポリオキシプロピレングリコールなどのポリオキシプロピレングリコールエチレンオキサイド付加物等が挙げられる。
 ポリオキシアルキレンアルキルエーテルとしては、たとえば、プロピレンオキサイドおよび/またはエチレンオキサイドが1~50個(好ましくは、1~10個)付加した直鎖状もしくは分岐鎖状エーテルが挙げられる。これらの中でも、プロピレンオキサイドが1~50個(好ましくは、1~10個)付加した直鎖状もしくは分岐鎖状エーテル、エチレンオキサイドが1~50個(好ましくは、1~10個)付加した直鎖状もしくは分岐鎖状エーテル、エチレンオキサイドとプロピレンオキサイドが合計2~50個(好ましくは、2~10個)ブロックもしくはランダムに付加した直鎖状もしくは分岐鎖状エーテルなどが挙げられる。ポリオキシアルキレンアルキルエーテルとしては、ポリオキシエチレンオレイルエーテル、ポリオキシエチレンオクチルドデシルエーテル、ポリオキシエチレンドデシルエーテル、ポリオキシエチレンラウリルエーテルなどが挙げられ、これらのなかでも、ポリオキシエチレンオレイルエーテルおよびポリオキシエチレンオクチルドデシルエーテルが好ましい。
 ポリオキシアルキレンアルキルフェニルエーテルとしては、アルキルフェノールに、プロピレンオキサイドおよび/またはエチレンオキサイドが1~50個(好ましくは、1~10個)付加した化合物などが挙げられる。
 ポリオキシエチレンスチレン化フェニルエーテルとしては、(モノ、ジ、トリ)スチレン化フェノールのエチレンオキサイド付加物などが挙げられ、これらのなかでも、ジスチレン化フェノールのエチレンオキサイド付加物である、ポリオキシエチレンジスチレン化フェニルエーテルが好ましい。
 ポリオキシエチレン(硬化)ヒマシ油としては、ヒマシ油もしくは硬化ヒマシ油のエチレンオキサイド付加物が挙げられる。
 脂肪酸アルカノールアミドとしては、たとえば、ラウリン酸ジエタノールアミド、パルミチン酸ジエタノールアミド、ミリスチン酸ジエタノールアミド、ステアリン酸ジエタノールアミド、オレイン酸ジエタノールアミド、パーム油脂肪酸ジエタノールアミド、ヤシ油脂肪酸ジエタノールアミド等が挙げられる。
 ノニオン系界面活性剤の中でも、ポリオキシアルキレン構造を有するノニオン系界面活性剤が好ましく、ポリオキシエチレン構造を有するノニオン系界面活性剤がより好ましく、ポリオキシエチレンのヒドロカルビル化エーテルであることがより好ましく、ポリオキシエチレンアルキルエーテルおよびポリオキシエチレンジスチレン化フェニルエーテルがさらに好ましく、ポリオキシエチレンジスチレン化フェニルエーテルが特に好ましい。ノニオン系界面活性剤は、1種単独で用いてもよく、2種以上を組み合わせて用いてもよい。
 キサントゲン化合物を水中に分散させる際に用いるノニオニックアニオン系界面活性剤としては、その分子主鎖中に、非イオン性の界面活性剤として作用するセグメント、および、アニオン性の界面活性剤として作用するセグメントを有するものであれば、特に限定されない。
 ノニオニックアニオン系界面活性剤としては、たとえば、下記一般式(3)で表される化合物などが挙げられる。
  R-O-(CRCR-SOM   (3)
 (上記一般式(3)中、Rは、炭素数6~16のアルキル基、または炭素数1~25のアルキル基で置換されていてもよい炭素数6~14のアリール基、R~Rは、水素およびメチル基よりなる群からそれぞれ独立して選ばれる基、Mは、アルカリ金属原子またはアンモニウムイオン、nは3~40である。)
 上記一般式(3)で表される化合物の具体例としては、ポリオキシエチレンラウリルエーテル硫酸塩、ポリオキシエチレンセチルエーテル硫酸塩、ポリオキシエチレンステアリルエーテル硫酸塩、ポリオキシエチレンオレイルエーテル硫酸塩などのポリオキシエチレンアルキルエーテル硫酸塩;ポリオキシエチレンノニルフェニルエーテル硫酸塩、ポリオキシエチレンオクチルフェニルエーテル硫酸塩、ポリオキシエチレンジスチリルエーテル硫酸塩などのポリオキシエチレンアリールエーテル硫酸塩;などが挙げられる。
 ノニオニックアニオン系界面活性剤の中でも、ポリオキシアルキレン構造を有するノニオニックアニオン系界面活性剤が好ましく、ポリオキシエチレン構造を有するノニオニックアニオン系界面活性剤がより好ましい。ノニオニックアニオン系界面活性剤は、1種単独で用いてもよく、2種以上を組み合わせて用いてもよい。
 キサントゲン化合物の水分散液中における、ノニオン系界面活性剤および/またはノニオニックアニオン系界面活性剤の含有量は、特に限定されないが、キサントゲン化合物100重量部に対して、好ましくは1~50重量部、より好ましくは3~30重量部、さらに好ましくは5~20重量部である。ノニオン系界面活性剤とノニオニックアニオン系界面活性剤とを併用する場合には、合計量が上記範囲となることが好ましい。
 キサントゲン化合物の水分散液の製造方法としては、キサントゲン化合物と、界面活性剤と、水とを混合し、次いで、得られた混合液について解砕処理を行う方法が好ましい。なお、解砕処理としては、上述した硫黄系加硫剤の水分散液の製造方法で説明した方法と同様の方法を挙げることができる。
 上述した共役ジエン系重合体のラテックスに、硫黄系加硫剤の水分散液およびキサントゲン化合物を配合する方法としては、特に限定されないが、硫黄系加硫剤の水分散液およびキサントゲン化合物の順に、これらを添加してもよいし、これらを同時に添加してもよい。
 また、本発明のラテックス組成物においては、上述した共役ジエン系重合体のラテックスに対し、硫黄系加硫剤の水分散液およびキサントゲン化合物に加えて、必要に応じて、活性化剤を添加してもよい。
 ラテックス組成物に、活性化剤を添加することにより、本発明のラテックス組成物を用いて、ラテックス組成物中の共役ジエン系重合体を硫黄系加硫剤により加硫してディップ成形体などの膜成形体とする際に、活性化剤が、上述したキサントゲン化合物とともに加硫促進剤として作用し、これにより、得られるディップ成形体などの膜成形体の引裂強度がより向上する。
 活性化剤としては、特に限定されないが、得られるディップ成形体などの膜成形体の引裂強度がより向上するという観点より、金属化合物を用いることが好ましい。金属化合物としては、特に限定されないが、たとえば、金属酸化物、炭素原子を少なくとも1つ含有する金属化合物などが挙げられる。金属化合物を構成する金属としては、特に限定されないが、典型金属(第1族元素、第2族元素、第12族元素、第13族元素、第14族元素、第15族元素、第16族元素、第17族元素、および第18族元素からなる群から選ばれる少なくとも1種の元素)が好ましく、第2族元素、第12族元素、第13族元素、第14族元素がより好ましく、亜鉛、マグネシウム、カルシウム、アルミニウム、鉛がさらに好ましく、亜鉛、マグネシウム、カルシウムが特に好ましく、亜鉛が最も好ましい。これらの金属化合物は、1種単独でも、複数種を併用してもよい。
 金属酸化物としては、特に限定されないが、得られるディップ成形体などの膜成形体の引裂強度がより向上するという観点より、酸化亜鉛、酸化マグネシウム、酸化チタン、酸化カルシウム、鉛酸化物、酸化鉄、酸化銅、酸化錫、酸化ニッケル、酸化クロム、酸化コバルト、および酸化アルミニウムが好ましく、酸化亜鉛がより好ましい。
 炭素原子を少なくとも1つ含有する金属化合物としては、得られるディップ成形体などの膜成形体の引裂強度がより向上するという観点より、炭酸塩、炭酸水素塩、水酸化物、有機金属化合物が好ましく、炭酸塩、炭酸水素塩、有機金属化合物がより好ましい。これらのなかでも、化合物自体の安定性に優れ、入手容易性にも優れるという観点より、炭酸塩、炭酸水素塩などの無機塩が特に好ましい。
 活性化剤の使用量は、ラテックス組成物に含まれる共役ジエン系重合体100重量部に対して、好ましくは0.01~10重量部、より好ましくは0.1~5重量部、さらに好ましくは1~3重量部である。活性化剤の使用量を上記範囲とすることにより、得られるディップ成形体などの膜成形体の引裂強度をより向上させることができる。
 活性化剤の配合方法は、最終的に共役ジエン系重合体のラテックスと活性化剤とが混合した状態となる方法であればよく、特に限定されない。
 また、ラテックス組成物には、得られるディップ成形体などの膜成形体において、遅延型アレルギー(Type IV)の症状の発生を抑制可能な範囲であれば、さらに加硫促進剤を添加してもよい。
 加硫促進剤としては、ディップ成形において通常用いられるものを使用することができ、たとえば、ジエチルジチオカルバミン酸、ジブチルジチオカルバミン酸、ジ-2-エチルヘキシルジチオカルバミン酸、ジシクロヘキシルジチオカルバミン酸、ジフェニルジチオカルバミン酸、ジベンジルジチオカルバミン酸などのジチオカルバミン酸類およびそれらの亜鉛塩;2-メルカプトベンゾチアゾール、2-メルカプトベンゾチアゾール亜鉛、2-メルカプトチアゾリン、ジベンゾチアジル・ジスルフィド、2-(2,4-ジニトロフェニルチオ)ベンゾチアゾール、2-(N,N-ジエチルチオ・カルバイルチオ)ベンゾチアゾール、2-(2,6-ジメチル-4-モルホリノチオ)ベンゾチアゾール、2-(4′-モルホリノ・ジチオ)ベンゾチアゾール、4-モルホニリル-2-ベンゾチアジル・ジスルフィド、1,3-ビス(2-ベンゾチアジル・メルカプトメチル)ユリアなどが挙げられる。加硫促進剤は、1種単独で、あるいは2種以上を組み合わせて用いることができる。なお、得られるディップ成形体などの膜成形体において、遅延型アレルギー(Type IV)の症状の発生をより抑制できるという観点より、キサントゲン化合物と加硫促進剤との合計の含有量に対する、キサントゲン化合物の含有割合は、好ましくは50重量%超であり、より好ましくは80重量%以上であり、さらに好ましくは100重量%である。
 さらに、ラテックス組成物には、さらに、老化防止剤;分散剤;カーボンブラック、シリカ、タルク等の補強剤;炭酸カルシウム、クレー等の充填剤;紫外線吸収剤;可塑剤;等の配合剤を必要に応じて配合することができる。
 老化防止剤としては、2,6-ジ-4-メチルフェノール、2,6-ジ-t-ブチルフェノール、ブチルヒドロキシアニソール、2,6-ジ-t-ブチル-α-ジメチルアミノ-p-クレゾール、オクタデシル-3-(3,5-ジ-t-ブチル-4-ヒドロキシフェニル)プロピオネート、スチレン化フェノール、2,2’-メチレン-ビス(6-α-メチル-ベンジル-p-クレゾール)、4,4’-メチレンビス(2,6-ジ-t-ブチルフェノール)、2,2’-メチレン-ビス(4-メチル-6-t-ブチルフェノール)、アルキル化ビスフェノール、p-クレゾールとジシクロペンタジエンのブチル化反応生成物、などの硫黄原子を含有しないフェノール系老化防止剤;2,2’-チオビス-(4-メチル-6-t-ブチルフェノール)、4,4’-チオビス-(6-t-ブチル-o-クレゾール)、2,6-ジ-t-ブチル-4-(4,6-ビス(オクチルチオ)-1,3,5-トリアジン-2-イルアミノ)フェノールなどのチオビスフェノール系老化防止剤;トリス(ノニルフェニル)ホスファイト、ジフェニルイソデシルホスファイト、テトラフェニルジプロピレングリコール・ジホスファイトなどの亜燐酸エステル系老化防止剤;チオジプロピオン酸ジラウリルなどの硫黄エステル系老化防止剤;フェニル-α-ナフチルアミン、フェニル-β-ナフチルアミン、p-(p-トルエンスルホニルアミド)-ジフェニルアミン、4,4’―(α,α-ジメチルベンジル)ジフェニルアミン、N,N-ジフェニル-p-フェニレンジアミン、N-イソプロピル-N’-フェニル-p-フェニレンジアミン、ブチルアルデヒド-アニリン縮合物などのアミン系老化防止剤;6-エトキシ-2,2,4-トリメチル-1,2-ジヒドロキノリンなどのキノリン系老化防止剤;2,5-ジ-(t-アミル)ハイドロキノンなどのハイドロキノン系老化防止剤;などが挙げられる。これらの老化防止剤は、1種単独で、または2種以上を併用することができる。
 老化防止剤の含有量は、共役ジエン系重合体100重量部に対して、好ましくは0.05~10重量部、より好ましくは0.1~5重量部、さらに好ましくは1~3重量部である。
 ラテックス組成物に各種配合剤を混合する方法としては、特に限定されないが、たとえば、上述したようにして共役ジエン系重合体のラテックス、硫黄系加硫剤、およびキサントゲン化合物を含有する組成物を得た後、ボールミル、ニーダー、ディスパー等の分散機を用いて、得られた組成物に、必要に応じて配合される各種配合剤を混合する方法などが挙げられる。また、各種配合剤のうち少なくとも一部については、後述する熟成の後に配合してもよい。
 なお、本発明のラテックス組成物の固形分濃度は、好ましくは10~60重量%、より好ましくは10~55重量%である。
 また、本発明においては、得られるディップ成形体などの膜成形体の機械的特性を十分なものとするという観点より、ディップ成形などの膜成形に供する前に、本発明のラテックス組成物に対して、熟成(前架橋または前加硫)を行うことが好ましい。熟成(前加硫)時間は、特に限定されないが、好ましくは8~120時間、より好ましくは24~72時間である。熟成(前加硫)の温度は、特に限定されないが、好ましくは20~40℃である。また、本発明のラテックス組成物を使用する際には、熟成(前加硫)を所定時間行った後、熟成(前加硫)条件を保ったまま(熟成(前加硫)を継続したまま)、ディップ成形などの膜成形を連続的に行ってもよく、この場合における熟成(前加硫)時間および熟成(前加硫)温度は、上記範囲とすればよい。特に、本発明のラテックス組成物は、硫黄系加硫剤を水分散液の状態で配合し、さらに、キサントゲン化合物を配合したものであるため、引張強度および引裂強度などの機械的強度が高く、かつ、機械的強度の安定性に優れた膜成形体を得ることができるものである。
<膜成形体>
 本発明の膜成形体としては、特に限定されないが、本発明のラテックス組成物をディップ成形して得られるディップ成形体であることが好適である。ディップ成形は、ラテックス組成物に型を浸漬し、型の表面に当該組成物を沈着させ、次に型を当該組成物から引き上げ、その後、型の表面に沈着した当該組成物を乾燥させる方法である。なお、ラテックス組成物に浸漬される前の型は予熱しておいてもよい。また、型をラテックス組成物に浸漬する前、または、型をラテックス組成物から引き上げた後、必要に応じて凝固剤を使用できる。
 凝固剤の使用方法の具体例としては、ラテックス組成物に浸漬する前の型を凝固剤の溶液に浸漬して型に凝固剤を付着させる方法(アノード凝着浸漬法)、ラテックス組成物を沈着させた型を凝固剤溶液に浸漬する方法(ティーグ凝着浸漬法)などがあるが、厚みムラの少ないディップ成形体が得られる点で、アノード凝着浸漬法が好ましい。
 凝固剤の具体例としては、塩化バリウム、塩化カルシウム、塩化マグネシウム、塩化亜鉛、塩化アルミニウムなどのハロゲン化金属;硝酸バリウム、硝酸カルシウム、硝酸亜鉛などの硝酸塩;酢酸バリウム、酢酸カルシウム、酢酸亜鉛など酢酸塩;硫酸カルシウム、硫酸マグネシウム、硫酸アルミニウムなどの硫酸塩;などの水溶性多価金属塩である。なかでも、カルシウム塩が好ましく、硝酸カルシウムがより好ましい。これらの水溶性多価金属塩は、1種単独で、または2種以上を併用することができる。
 凝固剤は、通常、水、アルコール、またはそれらの混合物の溶液として使用することができ、好ましくは水溶液の状態で使用する。この水溶液は、さらにメタノール、エタノールなどの水溶性有機溶媒やノニオン性界面活性剤を含有していてもよい。凝固剤の濃度は、水溶性多価金属塩の種類によっても異なるが、好ましくは5~50重量%、より好ましくは10~30重量%である。
 型をラテックス組成物から引き上げた後、通常、加熱して型上に形成された沈着物を乾燥させる。乾燥条件は適宜選択すればよい。
 次いで、加熱して、型上に形成されたディップ成形層を架橋させる。ディップ成形層の架橋は、通常、80~150℃の温度で、好ましくは10~130分の加熱処理を施すことにより行うことができる。加熱の方法としては、赤外線や加熱空気による外部加熱または高周波による内部加熱による方法が採用できる。なかでも、加熱空気による外部加熱が好ましい。なお、加熱処理を施す前に、ディップ成形層を、水、好ましくは30~70℃の温水に、1~60分程度浸漬し、水溶性不純物(たとえば、余剰の乳化剤や凝固剤等)を除去してもよい。水溶性不純物の除去操作は、ディップ成形層を加熱処理した後に行なってもよいが、より効率的に水溶性不純物を除去できる点から、加熱処理前に行なうことが好ましい。
 そして、ディップ成形層をディップ成形用型から脱着することによって、ディップ成形体が得られる。脱着方法としては、手で成形用型から剥したり、水圧や圧縮空気の圧力により剥したりする方法を採用することができる。なお、脱着後、更に60~120℃の温度で、10~120分の加熱処理を行なってもよい。
 ディップ成形体の膜厚は、好ましくは0.03~0.50mm、より好ましくは0.05~0.40mm、特に好ましくは0.08~0.30mmである。
 本発明のディップ成形体は、上述したラテックス組成物を用いて得られるものであるため、遅延型アレルギー(Type IV)の症状の発生を抑制しながら、引張強度および引裂強度などの機械的強度が高く、かつ、機械的強度の安定性にも優れるものであり、たとえば、手袋として特に好適に用いることができる。膜成形体が手袋である場合、膜成形体同士の接触面における密着を防止し、着脱の際の滑りをよくするために、タルク、炭酸カルシウムなどの無機微粒子または澱粉粒子などの有機微粒子を手袋表面に散布したり、微粒子を含有するエラストマー層を手袋表面に形成したり、手袋の表面層を塩素化したりしてもよい。
 また、本発明のディップ成形体は、上記手袋の他にも、哺乳瓶用乳首、スポイト、チューブ、水枕、バルーンサック、カテーテル、コンドームなどの医療用品;風船、人形、ボールなどの玩具;加圧成形用バック、ガス貯蔵用バックなどの工業用品;指サックなどにも用いることができる。
<接着剤組成物>
 また、本発明においては、上述した本発明のラテックス組成物を、接着剤組成物として用いることができる。
 接着剤組成物中における、本発明のラテックス組成物の含有量(固形分量)は、好ましくは5~60重量%、より好ましくは10~30重量%である。
 接着剤組成物は、本発明のラテックス組成物に加えて、接着剤樹脂を含有してなることが好ましい。接着剤樹脂としては、特に限定されないが、たとえば、レゾルシン-ホルムアルデヒド樹脂、メラミン樹脂、エポキシ樹脂およびイソシアネート樹脂を好適に使用することができ、これらのなかでも、レゾルシン-ホルムアルデヒド樹脂が好ましい。レゾルシン-ホルムアルデヒド樹脂は、公知のもの(たとえば、特開昭55-142635号公報に開示のもの)が使用できる。レゾルシンとホルムアルデヒドとの反応比率は、「レゾルシン:ホルムアルデヒド」のモル比で、通常、1:1~1:5、好ましくは1:1~1:3である。
 また、接着剤組成物の接着力をさらに高めるために、接着剤組成物には、従来から使用されている2,6-ビス(2,4-ジヒドロキシフェニルメチル)-4-クロロフェノールまたは類似の化合物、イソシアネート、ブロックイソシアネート、エチレン尿素、ポリエポキシド、変性ポリ塩化ビニル樹脂等を含有させることができる。
 さらに、接着剤組成物には、架橋助剤を含有させることができる。架橋助剤を含有させることにより、接着剤組成物を用いて得られる後述する複合体の機械的強度を向上させることができる。架橋助剤としては、p-キノンジオキシム等のキノンジオキシム;ラウリルメタクリレートやメチルメタクリレート等のメタクリル酸エステル;DAF(ジアリルフマレート)、DAP(ジアリルフタレート)、TAC(トリアリルシアヌレート)、TAIC(トリアリルイソシアヌレート)等のアリル化合物;ビスマレイミド、フェニルマレイミド、N,N-m-フェニレンジマレイミド等のマレイミド化合物;硫黄;等を挙げることができる。
 そして、本発明の接着剤組成物を用いて、接着剤層形成基材を得ることができる。接着剤層形成基材は、上述した本発明の接着剤組成物を用いて形成される接着剤層を、基材表面に形成して得られる。
 基材としては、特に限定されないが、たとえば繊維基材を用いることができる。繊維基材を構成する繊維の種類は、特に限定されず、たとえば、ビニロン繊維、ポリエステル繊維、ナイロン、アラミド(芳香族ポリアミド)等のポリアミド繊維、ガラス繊維、綿、レーヨン等が挙げられる。これらは、その用途に応じて、適宜選定することができる。繊維基材の形状は特に限定されず、たとえば、ステープル、フィラメント、コード状、ロープ状、織布(帆布等)等を挙げることができ、その用途に応じて適宜選定することができる。たとえば、接着剤層形成基材は、接着剤層を介して、ゴムと接着することにより、基材-ゴム複合体として用いることができる。基材-ゴム複合体としては、特に限定されないが、たとえば、繊維基材としてコード状のものを用いた芯線入りのゴム製歯付きベルト、帆布等の基布状の繊維基材を用いたゴム製歯付きベルト等が挙げられる。
 基材-ゴム複合体を得る方法としては、特に限定されないが、たとえば、浸漬処理等により接着剤組成物を基材に付着させて接着剤層形成基材を得て、接着剤層形成基材をゴム上に載置し、これを加熱および加圧する方法が挙げられる。加圧は、圧縮(プレス)成形機、金属ロール、射出成形機等を用いて行なうことができる。加圧の圧力は、好ましくは0.5~20MPa、より好ましくは2~10MPaである。加熱の温度は、好ましくは130~300℃、より好ましくは150~250℃である。加熱および加圧の処理時間は、好ましくは1~180分、より好ましくは5~120分である。加熱および加圧する方法により、ゴムの成形、および接着剤層形成基材とゴムとの接着を、同時に行なうことができるようになる。なお、加圧に用いる圧縮機の型の内面やロールの表面には、目的とする基材-ゴム複合体のゴムに所望の表面形状を付与するための型を形成させておくことが好ましい。
 また、基材-ゴム複合体の一態様として、基材-ゴム-基材複合体を挙げることができる。基材-ゴム-基材複合体は、たとえば、基材(2種以上の基材の複合体であってもよい。)と基材-ゴム複合体とを組み合わせて形成することができる。具体的には、基材としての芯線、ゴムおよび基材としての基布を重ね(このとき、芯線および基布には、接着剤組成物を適宜付着させて接着剤層形成基材としておく)、加熱しながら加圧することにより、基材-ゴム-基材複合体を得ることができる。
 接着剤層形成基材を用いて得られる基材-ゴム複合体は、本発明のラテックス組成物を用いてなるものであるため、機械的強度に優れたものであり、そのため、平ベルト、Vベルト、Vリブドベルト、丸ベルト、角ベルト、歯付ベルト等のベルトとして好適に用いることができる。また、このような接着剤層形成基材を用いて得られる基材-ゴム複合体は、耐油性に優れ、油中ベルトとして好適に用いることができる。さらに、接着剤層形成基材を用いて得られる基材-ゴム複合体は、ホース、チューブ、ダイアフラム等にも好適に使用できる。ホースとしては、単管ゴムホース、多層ゴムホース、編上式補強ホース、布巻式補強ホース等が挙げられる。ダイアフラムとしては、平形ダイアフラム、転動形ダイアフラム等が挙げられる。
 接着剤層形成基材を用いて得られる基材-ゴム複合体は、上記の用途以外にも、シール、ゴムロール等の工業用製品として用いることができる。シールとしては、回転用、揺動用、往復動等の運動部位シールと固定部位シールが挙げられる。運動部位シールとしては、オイルシール、ピストンシール、メカニカルシール、ブーツ、ダストカバー、ダイアフラム、アキュムレータ等が挙げられる。固定部位シールとしては、Oリング、各種ガスケット等が挙げられる。ゴムロールとしては、印刷機器、コピー機器等のOA機器の部品であるロール;紡糸用延伸ロール、紡績用ドラフトロール等の繊維加工用ロール;ブライドルロール、スナバロール、ステアリングロール等の製鉄用ロール;等が挙げられる。
 以下、実施例により本発明が詳細に説明されるが、本発明はこれらの実施例に限定されない。なお、以下の「部」は、特に断りのない限り、重量基準である。なお、各種の物性は以下のように測定した。
<固形分濃度>
 アルミ皿(重量:X1)に試料2gを精秤し(重量:X2)、これを105℃の熱風乾燥器内で2時間乾燥させた。次いで、デシケーター内で冷却した後、アルミ皿ごと重量を測定し(重量:X3)、下記の計算式にしたがって、固形分濃度を算出した。
 固形分濃度(重量%)=(X3-X1)×100/X2
<カルボキシ変性合成ポリイソプレンの変性率>
 カルボキシ変性合成ポリイソプレンのラテックスを構成するカルボキシ変性合成ポリイソプレンについて、水酸化ナトリウム水溶液を用いた中和滴定により、カルボキシ変性合成ポリイソプレン中におけるカルボキシル基の数を求めた。次いで、求めたカルボキシル基の数に基づいて、下記式にしたがって、カルボキシル基を有する単量体による変性率を求めた。
  変性率(重量%)=(X/Y)×100
 なお、上記式においては、Xは、カルボキシ変性合成ポリイソプレン中における、カルボキシル基を有する単量体の単位の重量を、Yは、カルボキシ変性合成ポリイソプレンの重量をそれぞれ表す。
<ディップ成形体の500%引張応力、引張強度、引張伸び>
 ASTM D412に基づいて、ディップ成形体を、ダンベル(商品名「スーパーダンベル(型式:SDMK-100C)」、ダンベル社製)で打ち抜き、引張強度測定用試験片を作製した。当該試験片をテンシロン万能試験機(商品名「RTG-1210」、オリエンテック社製)で引張速度500mm/minで引っ張り、伸び率が500%の時の引張応力(単位:MPa)、破断直前の引張強度(単位:MPa)、および破断直前の引張伸び(単位:%)を測定した。500%引張応力の値が低いほど、柔軟な風合いを有するディップ成形体であると判断できる。また、引張強度が高いほど、機械的強度に優れたディップ成形体であると判断できる。
 なお、ディップ成形体の500%引張応力および引張伸びの測定は、熟成(前加硫)時間を48時間としたディップ成形体について行った。また、ディップ成形体の引張強度の測定は、熟成(前加硫)時間を48時間としたディップ成形体、および熟成(前加硫)時間を96時間としたディップ成形体について行った。
<ディップ成形体の引張強度の変化率>
 上記により測定した、熟成(前加硫)時間を48時間としたディップ成形体の引張強度と、熟成(前加硫)時間を96時間としたディップ成形体の引張強度とから、下記式にしたがって、引張強度の変化率を算出した。引張強度の変化率が低いほど、引張強度の安定性に優れると判断できる。
 引張強度の変化率(%)={(熟成(前加硫)時間を96時間としたディップ成形体の引張強度)/(熟成(前加硫)時間を48時間としたディップ成形体の引張強度)}×100
<ディップ成形体の引裂強度>
 ASTM D624-00に基づいて、ディップ成形体を、23℃、相対湿度50%の恒温恒湿室で24時間以上放置した後、ダンベル(商品名「Die C」、ダンベル社製)で打ち抜き、引裂強度測定用の試験片を作製した。当該試験片をテンシロン万能試験機(商品名「RTG-1210」、A&D社製)で引張速度500mm/minで引っ張り、引裂強度(単位:N/mm)を測定した。引裂強度が高いほど、機械的強度に優れたディップ成形体であると判断できる。また、ディップ成形体の引裂強度の測定は、熟成(前加硫)時間を48時間としたディップ成形体、および熟成(前加硫)時間を96時間としたディップ成形体について行った。
<実施例1>
(カルボキシ変性合成ポリイソプレン(A-1)のラテックスの製造)
 合成ポリイソプレン(商品名「NIPOL IR2200L」、日本ゼオン社製)をn-ヘキサン(沸点:69℃)と混合し、攪拌しながら温度を60℃に昇温して溶解し、合成ポリイソプレン濃度15重量%である、合成ポリイソプレンのn-ヘキサン溶液(a)を調製した。
 一方、ロジン酸カリウムを水に添加し、温度を60℃に昇温して溶解し、濃度1.5重量%の乳化剤水溶液(b)を調製した。
 次に、上記にて得られた合成ポリイソプレンのn-ヘキサン溶液(a)と、乳化剤水溶液(b)とを、合成ポリイソプレンのn-ヘキサン溶液(a)中の合成ポリイソプレン100部に対して、乳化剤水溶液(b)中のロジン酸カリウムが10部となるように、ミキサー(製品名「マルチラインミキサーMS26-MMR-5.5L」、佐竹化学機械工業社製)を用いて混合し、続いて、乳化装置(製品名「マイルダーMDN310」、太平洋機工社製)を用いて、回転数4100rpmで混合および乳化することで、乳化分散液(c)を得た。なお、この際、合成ポリイソプレンのn-ヘキサン溶液(a)と乳化剤水溶液(b)との合計のフィード流速は2,000kg/hr、温度は60℃、背圧(ゲージ圧)は0.5MPaとした。
 次いで、得られた乳化分散液(c)を、-0.01~-0.09MPa(ゲージ圧)の減圧下で80℃に加温し、n-ヘキサンを留去し、合成ポリイソプレンの水分散液(d)を得た。その際、消泡剤(商品名「SM5515」、東レ・ダウコーニング社製)を、乳化分散液(c)中の合成ポリイソプレンに対して300重量ppmの量になるよう、噴霧しながら連続添加した。なお、n-ヘキサンを留去する際には、乳化分散液(c)がタンクの容積の70体積%以下になるように調整し、かつ、攪拌翼として3段の傾斜パドル翼を用い、60rpmでゆっくり攪拌を実施した。
 そして、n-ヘキサンの留去が完了した後、得られた合成ポリイソプレンの水分散液(d)を、連続遠心分離機(製品名「SRG510」、アルファラバル社製)を用いて、8,000~9,000Gで遠心分離することで濃縮し、軽液としての固形分濃度60重量%の合成ポリイソプレンのラテックス(e)を得た。なお、遠心分離の条件は、遠心分離前の水分散液(d)の固形分濃度8重量%、連続遠心分離時の流速は1300kg/hr、遠心分離機の背圧(ゲージ圧)は0.1MPaとした。
 次いで、得られた合成ポリイソプレンのラテックス(e)中の合成ポリイソプレン100部に対して、蒸留水130部を添加して希釈した。そして、合成ポリイソプレンのラテックス(e)に、合成ポリイソプレン100部に対して、分散剤としてのβ-ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩(商品名「デモールT-45」、花王社製)0.8部を合成ポリイソプレン100部に対し4部の蒸留水で希釈したものを5分間かけて添加した。次いで、分散剤を添加した合成ポリイソプレンのラテックス(e)を、窒素置換された攪拌機付き反応容器に仕込み、撹拌しながら温度を30℃にまで加温した。また、別の容器を用い、カルボキシル基含有化合物としてのメタクリル酸3部と蒸留水16部とを混合してメタクリル酸希釈液を調製した。このメタクリル酸希釈液を、温度20℃に保った反応容器内に、30分間かけて添加した。
 さらに、別の容器を用い、蒸留水7部、ナトリウムホルムアルデヒドスルホキシレート(商品名「SFS」、三菱ガス化学社製)0.32部、硫酸第一鉄(商品名「フロストFe」、中部キレスト社製)0.01部からなる溶液(f)を調製した。この溶液(f)を反応容器内に移した後、1,1,3,3-テトラメチルブチルハイドロパーオキサイド(商品名「パーオクタH」、日本油脂社製)0.5部を添加して20℃で1時間反応させた後、遠心分離機にて濃縮することで、カルボキシ変性合成ポリイソプレン(A-1)のラテックスを得た。得られたカルボキシ変性合成ポリイソプレン(A-1)のラテックスについて、上記方法にしたがって変性率を測定したところ、変性率は0.5モル%であった。
(硫黄の水分散液の調製)
 硫黄0.5部、アニオン系界面活性剤としてのβ-ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩(商品名「デモールT-45」、花王社製)0.03部(硫黄100部に対し6.0部)、5%水酸化カリウム水溶液0.004部、および水0.42部を、ボールミル(商品名「磁製ボールミル」、日陶科学社製)により混合することで解砕処理を行うことで、硫黄の水分散液を得た。なお、ボールミルによる、混合条件としては、φ10mm~φ35mmのセラミック磁製ボール(φ10mm、φ15mm、φ20mm、φ25mm、φ30mmおよびφ35mmのセラミック磁製ボールを混合したもの)を使用し、50rpmで72時間とした。
(キサントゲン化合物の水分散液の調製)
 キサントゲン化合物としてのジイソプロピルキサントゲン酸亜鉛(商品名「ノクセラーZIX」、大内新興化学工業株式会社製、体積平均粒子径:14μm、95%体積累積径(D95):55μm)2.5部、ノニオン系界面活性剤としてのポリオキシエチレンジスチレン化フェニルエーテル(商品名「エマルゲンA-60」、花王社製)0.45部(ジイソプロピルキサントゲン酸亜鉛100部に対し18.0部)、および水2.05部を、ボールミル(商品名「磁製ボールミル」、日陶科学社製)により混合することで解砕処理を行うことで、キサントゲン化合物の水分散液を得た。なお、ボールミルによる、混合条件としては、φ10mm~φ35mmのセラミック磁製ボール(φ10mm、φ15mm、φ20mm、φ25mm、φ30mmおよびφ35mmのセラミック磁製ボールを混合したもの)を使用し、50rpmで72時間とした。
(ラテックス組成物の調製)
 上記にて得られたカルボキシ変性合成ポリイソプレン(A-1)のラテックスを撹拌しながら、カルボキシ変性合成ポリイソプレン(A-1)のラテックス中のカルボキシ変性合成ポリイソプレン(A-1)100部に対して、上記にて調製した硫黄の水分散液を、硫黄換算で0.5部となる量、およびキサントゲン化合物の水分散液を、ジイソプロピルキサントゲン酸亜鉛換算で2.5部となる量添加した。
 そして、得られた混合物を撹拌しながら、混合物中のカルボキシ変性合成ポリイソプレン(A-1)100部に対して、それぞれ固形分換算で、活性化剤としての酸化亜鉛1.5部、老化防止剤(商品名「Wingstay L」、グッドイヤー社製)2部となるように、各配合剤の水分散液を添加して、ラテックス組成物を得た。そして、得られたラテックス組成物を、2分割し、一方については、25℃に調整された恒温水槽で48時間熟成(前加硫)を行い、他方については、25℃に調整された恒温水槽で96時間熟成(前加硫)を行うことで、48時間熟成ラテックス組成物、および96時間熟成ラテックス組成物を得た。
(ディップ成形体の製造)
 市販のセラミック製手型(シンコー社製)を洗浄し、70℃のオーブン内で予備加熱した後、18重量%の硝酸カルシウムおよび0.05重量%のポリオキシエチレンラウリルエーテル(商品名「エマルゲン109P」、花王社製)を含有する凝固剤水溶液に5秒間浸漬し、凝固剤水溶液から取り出した。次いで、手型を70℃のオーブン内で30分以上乾燥させることで、手型に凝固剤を付着させて、手型を凝固剤により被覆した。
 その後、凝固剤で被覆された手型を、オーブンから取り出し、上記にて得られた48時間熟成ラテックス組成物に10秒間浸漬した。次いで、この手型を、室温で10分間風乾してから、60℃の温水中に5分間浸漬して水溶性不純物を溶出させて、手型にディップ成形層を形成した。その後、手型に形成したディップ成形層を、オーブンにより温度130℃、30分間の条件で加熱することにより加硫させた後、室温まで冷却し、タルクを散布してから手型から剥離して、手袋形状のディップ成形体(48時間熟成品)を得た。また、48時間熟成ラテックス組成物に代えて、96時間熟成ラテックス組成物を使用した以外は、上記と同様にして、手袋形状のディップ成形体(96時間熟成品)を得た。そして、得られたディップ成形体(48時間熟成品および96時間熟成品)を用いて、上記方法にしたがって、500%引張応力、引張強度、引張伸び、および引裂強度の測定を行った。結果を表1に示す。
<実施例2>
 硫黄の水分散液の添加量を、硫黄換算で1.0部となる量に変更した以外は、実施例1と同様にして、ラテックス組成物を調製した。そして、実施例1と同様に、ディップ成形体(48時間熟成品および96時間熟成品)を得て、同様に評価を行った。結果を表1に示す。
<実施例3>
 ノニオン系界面活性剤としてのポリオキシエチレンジスチレン化フェニルエーテルに代えて、ノニオニックアニオン系界面活性剤としてのポリオキシエチレンアルキルエーテル硫酸塩(商品名「アルコスコープNS-230」、東邦化学工業社製)0.3部(ジイソプロピルキサントゲン酸亜鉛100部に対し12.0部)を使用した以外は、実施例2と同様にして、キサントゲン化合物の水分散液を調製し、実施例2と同様に、ラテックス組成物を調製した。そして、実施例2と同様に、ディップ成形体(48時間熟成品および96時間熟成品)を得て、同様に評価を行った。結果を表1に示す。
<実施例4>
 ノニオン系界面活性剤としてのポリオキシエチレンジスチレン化フェニルエーテルに代えて、アニオン系界面活性剤としてのβ-ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩(商品名「デモールT-45」、花王社製)0.15部(ジイソプロピルキサントゲン酸亜鉛100部に対し6部)を使用した以外は、実施例2と同様にして、キサントゲン化合物の水分散液を調製し、実施例2と同様に、ラテックス組成物を調製した。そして、実施例2と同様に、ディップ成形体(48時間熟成品および96時間熟成品)を得て、同様に評価を行った。結果を表1に示す。
<実施例5>
 硫黄の水分散液の添加量を、硫黄換算で0.3部となる量に変更した以外は、実施例4と同様にして、ラテックス組成物を調製した。そして、実施例4と同様に、ディップ成形体(48時間熟成品および96時間熟成品)を得て、同様に評価を行った。結果を表1に示す。
<実施例6>
 硫黄の水分散液の添加量を、硫黄換算で0.1部となる量に変更した以外は、実施例4と同様にして、ラテックス組成物を調製した。そして、実施例4と同様に、ディップ成形体(48時間熟成品および96時間熟成品)を得て、同様に評価を行った。結果を表1に示す。
<比較例1>
 硫黄の水分散液に代えて、硫黄0.5部を、粉末の状態でカルボキシ変性合成ポリイソプレン(A-1)のラテックスに添加した以外は、実施例4と同様にして、ラテックス組成物を調製した。そして、実施例4と同様に、ディップ成形体(48時間熟成品および96時間熟成品)を得て、同様に評価を行った。結果を表1に示す。
<比較例2>
 キサントゲン化合物としてのジイソプロピルキサントゲン酸亜鉛に代えて、ジエチルジチオカルバミン酸亜鉛(商品名「ノクセラー EZ」、大内新興化学工業社製)0.3部、ジブチルジチオカルバミン酸亜鉛(商品名「ノクセラー BZ-P」、大内新興化学工業社製)0.5部、および2-メルカプトベンゾチアゾール亜鉛(商品名「ノクセラー MZ」、大内新興化学工業社製)0.7部を使用した以外は、比較例1と同様に、加硫促進剤の水分散液を調製し、比較例1と同様に、ラテックス組成物を調製した。そして、比較例1と同様に、ディップ成形体(48時間熟成品および96時間熟成品)を得て、同様に評価を行った。結果を表1に示す。
<比較例3>
 キサントゲン化合物の水分散液に代えて、比較例2で得られた加硫促進剤の水分散液を使用した以外は、実施例1と同様に、ラテックス組成物を調製した。そして、実施例1と同様に、ディップ成形体(48時間熟成品および96時間熟成品)を得て、同様に評価を行った。結果を表1に示す。
<比較例4>
 硫黄の水分散液の添加量を、硫黄換算で1.5部となる量に変更した以外は、比較例3と同様にして、ラテックス組成物を調製した。そして、比較例3と同様に、ディップ成形体(48時間熟成品および96時間熟成品)を得て、同様に評価を行った。結果を表1に示す。
Figure JPOXMLDOC01-appb-T000003
 表1に示すように、共役ジエン系重合体ラテックスに、アニオン性界面活性剤を用いて水中に分散させた硫黄系加硫剤の水分散液、およびキサントゲン化合物を配合してなるラテックス組成物は、引張応力が良好で、高い機械的強度を有するものであり、また、引張強度の変化率も高いことから、機械的強度の安定性にも優れるものであった(実施例1~6)。さらに、得られたラテックス組成物は、遅延型アレルギー(Type IV)の症状を引き起こすような加硫促進剤を配合していないため、ディップ成形体とした場合に、得られるディップ成形体は、遅延型アレルギー(Type IV)の発生を防止できるものであると考えられる。
 一方、ラテックス組成物が、水分散液でなく、粉末状態の硫黄を配合してなる場合、得られるディップ成形体は、機械的強度に劣るものであった(比較例1,2)。
 また、ラテックス組成物が、加硫促進剤として、キサントゲン化合物以外の化合物を含む場合、得られるディップ成形体は、機械的強度に劣るものであった(比較例3,4)。

Claims (9)

  1.  共役ジエン系重合体ラテックスに、硫黄系加硫剤の水分散液、およびキサントゲン化合物を配合してなるラテックス組成物であって、
     前記硫黄系加硫剤の水分散液が、硫黄系加硫剤を、アニオン系界面活性剤を用いて水中に分散させたものであるラテックス組成物。
  2.  前記硫黄系加硫剤の配合量が、前記共役ジエン系重合体ラテックス中に含まれる共役ジエン系重合体100重量部に対し、0.1~1.0重量部である請求項1に記載のラテックス組成物。
  3.  前記硫黄系加硫剤の配合量が、前記共役ジエン系重合体ラテックス中に含まれる共役ジエン系重合体100重量部に対し、0.1~0.6重量部である請求項2に記載のラテックス組成物。
  4.  前記キサントゲン化合物は、ノニオン系界面活性剤および/またはノニオニックアニオン系界面活性剤を用いて水中に分散させた水分散液の状態で、前記共役ジエン系重合体ラテックスに配合されたものである請求項1~3のいずれかに記載のラテックス組成物。
  5.  前記共役ジエン系重合体ラテックスが、合成ポリイソプレンのラテックス、スチレン-イソプレン-スチレンブロック共重合体のラテックス、蛋白質を除去した天然ゴムのラテックスまたはニトリル基含有共役ジエン系共重合体のラテックスである、請求項1~4のいずれかに記載のラテックス組成物。
  6.  前記共役ジエン系重合体ラテックスが、カルボキシ変性共役ジエン系重合体のラテックスである請求項1~5のいずれかに記載のラテックス組成物。
  7.  請求項1~6のいずれかに記載のラテックス組成物からなる膜成形体。
  8.  請求項1~6のいずれかに記載のラテックス組成物をディップ成形してなるディップ成形体。
  9.  請求項1~6のいずれかに記載のラテックス組成物からなる接着剤組成物。
PCT/JP2021/004673 2020-02-26 2021-02-08 ラテックス組成物 WO2021171993A1 (ja)