WO2021167282A1 - 편광자, 편광판 및 이를 포함하는 광학표시장치 - Google Patents
편광자, 편광판 및 이를 포함하는 광학표시장치 Download PDFInfo
- Publication number
- WO2021167282A1 WO2021167282A1 PCT/KR2021/001647 KR2021001647W WO2021167282A1 WO 2021167282 A1 WO2021167282 A1 WO 2021167282A1 KR 2021001647 W KR2021001647 W KR 2021001647W WO 2021167282 A1 WO2021167282 A1 WO 2021167282A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polarizer
- polarizing plate
- polyvinyl alcohol
- film
- based film
- Prior art date
Abstract
폴리비닐알코올계 필름을 포함하고 10℃/분의 승온 속도에서 시차 주사 열량계 측정시 흡열 피크가 50℃ 내지 60℃인 것인 편광자; 편광자 및 편광자의 일면과 다른 일면 각각에 적층된 제1보호 필름, 제2보호필름을 구비하고, 열기계적 분석시 최초 수축 개시 온도가 70℃ 초과 90℃ 이하인 것인 편광판; 및 이를 포함하는 광학표시장치가 제공된다.
Description
본 발명은 편광자, 편광판 및 이를 포함하는 광학표시장치에 관한 것이다. 보다 상세하게는, 본 발명은 홀(hole) 형성 후 고온에서 방치 및/또는 열 충격 하에서 기포 발생이 없거나 또는 기포 발생이 시인되지 않고, 고온에서 방치 및/또는 열 충격 하에서 신뢰성이 우수하고, 빛샘을 개선할 수 있는, 편광자, 편광판 및 이를 포함하는 광학표시장치에 관한 것이다.
편광판은 편광자, 편광자의 적어도 일면에 적층된 보호층을 포함할 수 있다. 편광판은 광학표시장치에 사용되어 고온 및/또는 열 충격에서 장기간 노출될 수 밖에 없다. 편광판의 주요 물성인 편광은 편광판 중 편광자에 의해 주로 나온다. 편광자는 요오드로 염색한 폴리비닐알콜계 필름을 1축으로 연신하여 제조된다. 그러나, 편광판을 고온 및/또는 열충격에서 장기간 방치할 경우 신뢰성이 떨어질 수 있다.
편광자는 폴리비닐알코올계 필름을 연신시켜 제조될 수 있다. 일반적으로 편광자는 폴리비닐알코올계 필름을 염착, 연신시켜 제조된다. 기존에 알려진 폴리비닐알코올계 필름은 연신비와 연신 온도에 한계가 있어, 이로부터 제조된 편광자는 고온 및/또는 열 충격에서 방치될 경우 신뢰성 개선에 한계가 있었다. 폴리비닐알코올계 필름을 고 연신비 및 고 연신 온도에서 연신할 경우 연신 과정에서 폴리비닐알코올계 필름이 파단되거나 용융되어 편광자 자체를 제조할 수 없을 수도 있다.
한편, 편광판은 광학표시장치에 장착 시 카메라가 장착되는 비표시영역의 일부를 형성할 수 있다. 카메라 구동을 위한 광 투과 영역을 확보하기 위하여 편광판 특히 편광자의 일부에는 화학적 방법 또는 광학적 방법(레이저 조사 등)에 의해 홀을 형성하게 된다. 홀은 편광자의 일부가 뚫린 구멍 형태로 형성될 수도 있고 또는 뚫리지 않는 대신에 홀이 형성되지 않은 부분 대비 광 투과율이 상대적으로 높은 상태로 형성될 수도 있다. 그런데 편광판을 고온 및/또는 열 충격 하에서 방치 시 홀 주변에 기포가 발생됨으로써 기포가 시인되거나 기포에 의한 굴절률 차이로 비 편광 부분이 발생하여 빛샘으로 불량이 발생하거나 표시 영역에서의 화질도 좋지 않을 수 있다.
본 발명의 배경 기술은 한국공개특허 제10-2013-0078606호 등에 개시되어 있다.
본 발명의 목적은 홀 형성 후 고온 및/또는 열 충격 하에서 기포 발생이 없거나 기포 발생이 시인되지 않고, 고온 및/또는 열 충격 하에서 신뢰성이 우수하며, 빛샘을 개선한 편광자 및 편광판을 제공하는 것이다.
본 발명의 다른 목적은 홀 형성 후 고온 및/또는 열 충격 하에서 기포 발생이 없거나 기포 발생이 시인되지 않고, 고온 및/또는 열 충격 하에서 신뢰성이 우수하며, 빛샘을 개선한 편광자 및 편광판을 간단하고 경제적인 방법을 제공하는 것이다.
본 발명의 일 관점은 편광자이다.
1.편광자는 폴리비닐알코올계 필름을 포함하고, 10℃/분의 승온 속도에서 시차 주사 열량계 측정시 흡열 피크가 50℃ 내지 60℃이다.
2.1에서, 상기 폴리비닐알코올계 필름은 친수성 작용기 및 소수성 작용기를 모두 가질 수 있다.
3.1-2에서, 상기 폴리비닐알코올계 필름은 연화점이 약 65℃ 내지 약 71℃일 수 있다.
본 발명의 다른 관점은 편광판이다.
4.편광판은 편광자 및 상기 편광자의 일면과 다른 일면에 각각 적층된 보호 필름을 포함하고, 상기 편광판은 10℃/분의 승온 속도에서 열기계적 분석시 최초 수축 개시 온도가 70℃ 초과 90℃ 이하이다.
5.4에서, 상기 편광자는 폴리비닐알코올계 필름을 포함하고, 10℃/분의 승온 속도에서 시차 주사 열량계 측정시 흡열 피크가 50℃ 내지 60℃일 수 있다.
6.4-5에서, 상기 폴리비닐알코올계 필름은 친수성 작용기 및 소수성 작용기를 모두 가질 수 있다.
7.4-6에서, 상기 보호 필름은 트리아세틸셀룰로스, 폴리에틸렌테레프탈레이트, 또는 비정성 환상 폴리올레핀 수지 필름을 포함할 수 있다.
8.4-7에서, 상기 보호 필름은 10℃/분의 승온 속도에서 열기계적 분석시 최초 수축 개시 온도가 70℃ 내지 130℃일 수 있다.
본 발명의 또 다른 관점은 광학표시장치이다.
광학표시장치는 본 발명의 편광자 또는 본 발명의 편광판을 포함한다.
본 발명은 홀 형성 후 고온 및/또는 열 충격 하에서 기포 발생이 없거나 기포 발생이 시인되지 않고, 고온 및/또는 열 충격 하에서 신뢰성이 우수하며, 빛샘을 개선한 편광자 및 편광판을 제공하였다.
본 발명은 홀 형성 후 고온 및/또는 열 충격 하에서 기포 발생이 없거나 기포 발생이 시인되지 않고, 고온 및/또는 열 충격 하에서 신뢰성이 우수하며, 빛샘을 개선한 편광자 및 편광판을 간단하고 경제적인 방법을 제공하였다.
도 1은 본 발명 일 실시예의 편광판의 열기계적 분석에 의한 최초 수축 개시 온도를 나타낸 것이다.
도 2는 실시예 1(점선)과 비교예 1(실선)의 편광자의 시차 주사 열량계 측정에 의한 흡열 피크를 나타낸 것이다.
도면 및 첨부한 실시예에 의해 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명을 상세히 설명한다. 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.
본 명세서에서 편광자의 "시차 주사 열량계(DSC) 측정 시 흡열 피크"는 편광자 5mg 내지 10mg에 대해 열 흐름(heat flow) 방식; -50℃ 내지 200℃ 온도 범위; 10℃/분의 승온 속도; 질소 분위기 하에서 시차 주사 열량계 측정하였을 때 최초 흡열 피크를 의미한다. 도 2를 참조하면, 온도 상승에 따라 열 흐름(heat flow)이 계속해서 증가하다가 일시적으로 감소하는 지점의 온도를 흡열 피크로 정의하였다.
본 명세서에서 편광판의 "열기계적(TMA) 분석시 최초 수축 개시 온도"는 8mm x 5mm(편광자의 MD x 편광자의 TD) 편광판 샘플에 대해 연신 방향(예:편광자의 MD)으로 -50℃ 내지 200℃ 온도 범위; 0.02N 내지 0.05N의 하중; 10℃/분의 승온 속도, 질소 분위기 하에서 열기계적 분석하였을 때 최초 수축 개시 온도를 의미한다.
도 1을 참조하면, 도 1은 본 발명의 편광판의 열기계적 분석시 최초 수축 개시 온도의 다양한 실시예들을 나타낸 것이다. 상기 승온 속도에 따라 승온할 수록 편광판의 시편 크기는 계속해서 유지 또는 증가하다가 어느 온도 시점에서 수축을 시작하게 되며 이때 수축이 시작되는 온도인 변곡점을 열기계적(TMA) 분석시 최초 수축 개시 온도로 정의한다. 상기 최초 수축 개시 온도 측정을 위한 편광판 샘플의 두께는 50㎛ 내지 170㎛가 될 수 있다.
본 명세서에서 보호필름의 "열기계적(TMA) 분석시 최초 수축 개시 온도"는 8mm x 5mm(보호필름의 MD x 보호필름의 TD)의 시편에 대해 상기 편광판과 동일한 방법으로 측정된 값일 수 있다.
본 명세서에서 수치 범위 기재 시 "X 내지 Y"는 X 이상 Y 이하(X≤ 그리고 ≤Y)를 의미한다.
본 명세서에서 "(메트)아크릴"은 아크릴 및/또는 메타아크릴을 의미한다.
본 발명자는 하기 상술되는 편광자 및 편광판에 의해서, 홀 형성 후 고온 및/또는 열 충격 하에서 기포 발생이 없거나 기포 발생이 시인되지 않고, 고온 및/또는 열 충격 하에서 신뢰성이 우수하고, 빛샘을 개선하고, 간단하고 경제적인 방법으로 제조되어 공정성과 경제성이 우수하였음을 확인하고 본 발명을 완성하였다.
이하, 본 발명의 일 실시예에 따른 편광자를 설명한다.
편광자는 10℃/분의 승온 속도 하에서 시차 주사 열량계 측정시 흡열 피크가 50℃ 내지 60℃이다. 상기 시차 주사 열량계 측정시 흡열 피크는 편광자를 시차 주사 열량 측정에 의해 승온시켰을 때 연신 공정에서 편광자가 받은 열 이력에 의한 상전이 온도를 의미한다. 상기 흡열 피크 범위에서 편광자에 홀을 형성하였을 때 고온 및/또는 열 충격 하에 방치시 홀 주변에 기포가 생기는 불량을 막을 수 있고 기포 발생이 시인되지 않을 수 있다. 또한, 상기 흡열 피크 범위에서, 편광자는 고온 및/또는 열 충격 하에서 편광자의 수축이 현저하게 억제되어 편광자 또는 편광자를 포함하는 편광판을 고온 및/또는 열충격 하에서 방치시켰을 때 편광도 또는 광투과도 변화량이 현저하게 낮을 수 있으며, 빛샘도 낮아지게 할 수 있다. 예를 들면, 흡열 피크는 51℃ 내지 59℃가 될 수 있다.
편광자는 두께가 약 5㎛ 내지 약 30㎛, 구체적으로 약 5㎛ 내지 약 15㎛가 될 수 있다. 상기 범위에서, 편광판에 적용될 수 있고, 편광판의 박형화를 구현할 수 있다.
편광자는 하기 상술되는 폴리비닐알코올계 필름을 하기 상술되는 공정으로 처리함으로써 제조된다.
폴리비닐알코올계 필름은 친수성 작용기 및 소수성 작용기를 함유한다. 소수성 작용기는 폴리비닐알코올계 필름에 존재하는 친수성 작용기인 수산기(OH기) 이외에 추가로 존재한다. 상기 친수성 작용기 및 소수성 작용기를 모두 함유하는 폴리비닐알코올계 필름을 하기 상술되는 공정에 의해 제조함으로써 본 발명의 흡열 피크 및 수축 개시 온도에 도달할 수 있다.
소수성 작용기는 폴리비닐알코올계 필름을 구성하는 폴리비닐알코올계 수지의 주쇄, 측쇄 중 1종 이상에 존재한다. 상기 "주쇄"는 상기 폴리비닐알코올계 수지의 주 골격을 형성하는 부분을 의미하고, 상기 "측쇄"는 상기 주쇄에 연결된 골격을 의미한다. 바람직하게는, 소수성 작용기는 폴리비닐알코올계 수지의 주쇄에 존재할 수 있다.
친수성 작용기 및 소수성 작용기가 도입된 폴리비닐알코올계 수지는 아세트산 비닐, 포름산 비닐, 프로피온산 비닐, 부티르산 비닐, 피발산 비닐, 아세트산 이소프로페닐 등의 비닐 에스테르 1종 또는 2종 이상의 단량체와 소수성 작용기를 제공하는 단량체를 중합하여 제조될 수 있다. 바람직하게는 상기 비닐 에스테르 단량체는 아세트산 비닐을 포함할 수 있다. 상기 소수성 작용기를 제공하는 단량체는 에틸렌, 프로필렌 등을 포함하는 탄화수소(Hydrocarbon) 반복 단위를 제공하는 단량체를 포함할 수 있다.
폴리비닐알코올계 필름은 연화점이 약 65℃ 내지 약 71℃, 예를 들면 약 67℃ 내지 약 69℃가 될 수 있다. 상기 범위에서, 연신 공정에서 용융 및 파단이 없는 효과가 있을 수 있다.
폴리비닐알코올계 필름은 필름의 길이 방향(machine direction)으로 측정된 인장 강도가 약 80MPa 내지 약 120MPa, 바람직하게는 약 90MPa 내지 약 110MPa가 될 수 있다. 상기 범위에서 연신 공정에서 용융 및 파단이 없고 폴리비닐알코올 분자 사슬이 효과적으로 배향하여 편광도가 높을 수 있으며 본 발명의 편광자에 용이하게 도달되도록 할 수 있다. 상기 폴리비닐알코올계 필름의 인장강도는 25℃에서 UTM(Universal Testing Machine)을 이용하여 ASTM D882 규격으로 측정될 수 있다.
폴리비닐알코올계 필름은 두께가 약 0㎛ 초과 약 50㎛ 이하, 예를 들면 약 10㎛ 내지 약 50㎛가 될 수 있다. 상기 범위에서, 필름 연신 시 필름의 용융 및 파단이 없을 수 있다.
편광자는 상기 폴리비닐알코올계 필름을 하기 상술되는, 염착 공정, 연신 공정, 가교 공정의 순서로 처리함으로써 제조된다.
염착 공정은 폴리비닐알코올계 필름을 이색성 물질 함유 염착조에서 처리하는 것을 포함한다. 염착 공정에서는 폴리비닐알코올계 필름을 이색성 물질 함유 염착조에서 침지하게 된다. 이색성 물질 함유 염착조는 이색성 물질 및 붕산을 포함하는 수용액을 포함한다. 염착조는 이색성 물질과 붕소 화합물을 함께 포함함으로써 폴리비닐알코올계 필름을 염착시키고 하기 상술되는 연신 조건에서 연신되더라도 폴리비닐알코올계 필름의 파단이 없을 수 있다.
이색성 물질은 요오드로서 요오드화칼륨, 요오드화수소, 요오드화리튬, 요오드화나트륨, 요오드화아연, 요오드화리튬, 요오드화알루미늄, 요오드화납, 요오드화구리 중 1종 이상을 포함할 수 있다. 이색성 물질은 염착조 바람직하게는 염착 용액 중 약 0.5mol/ml 내지 약 10mol/ml, 바람직하게는 약 0.5mol/ml 내지 약 5mol/ml로 포함될 수 있다. 상기 범위에서, 균일한 염착이 가능한 효과가 있을 수 있다.
붕소 화합물은 폴리비닐알코올계 필름 연신시 폴리비닐알코올계 필름의 용융 파단이 없도록 하는데 도움을 줄 수 있다. 붕소 화합물은 염착 공정 이후에 실시되는 연신 공정에서 폴리비닐알코올계 필름을 고온 및 고 연신비로 연신하더라도 필름의 용융 및 파단이 없도록 하는데 도움을 줄 수 있다.
붕소 화합물은 붕산, 붕사 중 1종 이상을 포함할 수 있다. 붕소 화합물은 염착조 바람직하게는 염착 수용액 중 약 0.1중량% 내지 약 5중량%, 바람직하게는 약 0.3중량% 내지 약 3중량%로 포함될 수 있다. 상기 범위에서, 연신 공정에서 용융 및 파단이 없으며 고 신뢰성을 달성하는 효과가 있을 수 있다.
염착 용액의 온도는 약 20℃ 내지 약 50℃, 구체적으로 약 25℃ 내지 약 40℃로 하는 것이 바람직할 수 있다. 염착 공정에서는 폴리비닐알코올계 필름을 염착조 내에서 약 30초 내지 약 120초, 구체적으로 약 40초 내지 약 80초로 침지함으로써 수행될 수 있다.
연신 공정은 염착된 폴리비닐알코올계 필름을 연신비 약 5.7배 이상, 예를 들면 약 5.7배 내지 약 7배, 바람직하게는 약 5.8배 내지 약 7배로 연신 온도 약 58℃ 이상, 예를 들면 약 58℃ 내지 약 65℃에서 연신시키는 것을 포함한다. 종래 폴리비닐알코올계 필름은 상술한 연신비와 연신 온도에서 연신할 경우 폴리비닐알코올계 필름의 용융 및/또는 파단이 있어서 편광자를 제조할 수 없다.
연신 공정은 습식 연신 또는 건식 연신 중 어느 하나에서 수행된다. 바람직하게는 연신 공정에서 붕소 화합물을 적용하기 위하여 연신 공정은 습식 연신을 포함한다. 습식 연신은 붕소 화합물을 포함하는 수용액 중에서 폴리비닐알코올계 필름을 기계적 방향으로 1축 연신하는 것을 포함한다.
붕소 화합물은 붕산, 붕사 중 1종 이상, 바람직하게는 붕산을 포함할 수 있다. 붕소 화합물은 연신조 바람직하게는 연신 수용액 중 약 0.5중량% 내지 약 10중량%, 바람직하게는 약 1중량% 내지 약 5중량%로 포함될 수 있다. 상기 범위에서, 연신 공정에서 용융 및 파단이 없으며 고 신뢰성을 달성하는 효과가 있을 수 있다.
가교 공정은 연신 공정 처리된 폴리비닐알코올계 필름에서 이색성 물질의 흡착을 강하게 하기 위하여 처리된다. 가교 공정에서 사용하는 가교 용액은 붕소 화합물을 포함한다. 붕소 화합물은 상술한 이색성 물질의 흡착을 강하게 하면서 편광자를 고온 또는 열충격 하에 방치하더라도 신뢰성을 개선하는데 도움을 줄 수 있다.
붕소 화합물은 붕산, 붕사 중 1종 이상을 포함할 수 있다. 붕소 화합물은 가교조 바람직하게는 가교 수용액 중 약 0.5중량% 내지 약 10중량%, 바람직하게는 약 1중량% 내지 약 5중량%로 포함될 수 있다. 상기 범위에서, 연신 공정에서 용융 및 파단이 없으며 고 신뢰성을 달성하는 효과가 있을 수 있다.
염착 공정 처리 전에, 폴리비닐알코올계 필름을 수세 공정, 팽윤 공정 중 1종 이상을 추가로 포함할 수 있다.
수세 공정은 폴리비닐알코올계 필름을 물로 세척하는 것으로, 폴리비닐알코올계 필름에 묻어있는 이물질을 제거한다.
팽윤 공정은 폴리비닐알코올계 필름을 소정 온도 범위의 팽윤조에서 침지시킴으로써 이색성 물질의 염착, 연신을 보다 용이하게 할 수 있다. 팽윤 공정은 약 15℃ 내지 약 35℃, 바람직하게는 약 20℃ 내지 약 30℃에서, 약 30초 내지 약 50초 동안 처리하는 것을 포함할 수 있다.
가교 공정 처리 이후에, 폴리비닐알코올계 필름을 보색 공정으로 추가 처리할 수 있다. 보색 처리는 폴리비닐알코올계 필름의 내구성을 좋게 할 수 있다. 보색조는 요오드화칼륨 약 0중량% 초과 약 10중량% 이하, 바람직하게는 약 1중량% 내지 약 5중량%를 포함할 수 있다.
일 구체예에에서, 편광자의 일 부분에는 비 편광 영역을 형성하는 홀이 형성될 수 있다. 홀은 편광자를 광학표시장치에 적용시 카메라 등을 형성하는 영역을 이룰 수 있다. 홀 형성 방법은 특별히 제한되지 않는다. 예를 들면, 홀은 화학적 방법 또는 레이저 조사 등을 포함하는 광학적 방법에 의해 형성될 수 있다. 홀은 편광자의 일부가 뚫린 구멍 형태로 형성될 수도 있고 또는 뚫리지 않는 대신에 홀이 형성되지 않은 부분 대비 광 투과율이 상대적으로 높은 상태로 형성될 수도 있다.
편광자는 홀 형성 후 하기 상술되는 고온 및/또는 열 충격 하에서 홀 경계면에서의 기포 크기(직경)의 최대값이 약 100㎛ 이하, 예를 들면 약 0㎛ 내지 약 100㎛일 수 있다. 홀 주변에 발생한 기포 크기가 약 100㎛ 이하일 때, 실제 디스플레이에서 홀 주변의 블랙 매트릭스에 의해 기포가 가려져 사용자의 눈에 시인되지 않을 수 있다. 또한, 여러 개의 기포가 연결되어 홀 주변에 발생하더라도 홀 중심에서 바깥쪽 방향으로의 기포 크기의 최대값이 약 100㎛ 이하이면 동일한 이유로 시인되지 않을 수 있다.
이하, 본 발명의 일 실시예의 편광판을 설명한다.
편광판은 편광자 및 편광자의 일면과 다른 일면 각각에 적층된 제1보호 필름, 제2보호필름을 구비하고, 편광판은 열기계적 분석시 최초 수축 개시 온도가 70℃ 초과 90℃ 이하이다. 상기 범위에서, 편광판의 고온 또는 열충격 하에서 처리하였을 때 신뢰성이 우수할 수 있다. 또한, 상기 범위에서, 홀 형성 후 고온 및/또는 열 충격 하에서 기포 발생이 없거나 기포 발생이 시인되지 않을 수 있다. 예를 들면, 최초 수축 개시 온도는 70℃ 초과 85℃ 이하, 70℃ 초과 80℃ 이하가 될 수 있다.
일 구체예에서, 편광판은 하기 식 1에 따른 편광도 변화량(△P1)이 약 3% 이하, 예를 들면 약 0% 내지 약 3%가 될 수 있고, 하기 식 2에 따른 편광도 변화량이 약 3% 이하, 예를 들면 약 0% 내지 약 3%가 될 수 있다: 상기 범위에서, 편광판을 고온 또는 열충격 하에서 처리하였을 때에도 편광도 변화량이 낮아서 신뢰성, 공정성, 경제성이 우수할 수 있다:
[식 1]
△P1 = |P1 - P0|
(상기 식 1에서, P0는 편광판의 최초 편광도(단위:%),
P1은 편광판을 95℃에서 500시간 방치한 후의 편광도(단위:%))
[식 2]
△P2 = |P2 - P0|
(상기 식 2에서, P0는 편광판의 최초 편광도(단위:%),
P2는 편광판을 -40℃에서 30분, 80℃에서 30분 방치하는 것을 1사이클로 하여 100사이클 반복 후의 편광도(단위:%)).
편광자
편광자는 상술된 본 발명 일 실시예의 편광자를 포함한다.
제1보호필름
제1보호필름은 편광자 일면에 적층되어, 편광자를 보호하고, 편광판의 기계적 강도를 높일 수 있다. 제1보호필름은 광학적으로 투명한, 보호필름을 포함할 수 있다.
보호 필름은 광학적으로 투명한 수지를 용융 및 압출하여 형성될 수 있다. 필요할 경우에는 연신 공정을 더 추가할 수도 있다. 상기 수지는 트리아세틸셀룰로스 등을 포함하는 셀룰로스 에스테르계 수지, 비정성 환상 폴리올레핀(cyclic olefin polymer, COP) 등을 포함하는 고리형 폴리올레핀계 수지, 폴리카보네이트계 수지, 폴리에틸렌테레프탈레이트(PET) 등을 포함하는 폴리에스테르계 수지, 폴리에테르술폰계 수지, 폴리술폰계 수지, 폴리아미드계 수지, 폴리이미드계 수지, 비환형-폴리올레핀계 수지, 폴리메틸메타아크릴레이트 수지 등을 포함하는 폴리아크릴레이트계 수지, 폴리비닐알코올계 수지, 폴리염화비닐계 수지, 폴리염화비닐리덴계 수지 중 하나 이상을 포함할 수 있다.
일 구체예에서, 제1보호 필름은 10℃/분의 승온 속도에서 열기계적 분석시 최초 수축 개시 온도가 70℃ 내지 130℃, 바람직하게는 75℃ 내지 125℃, 80℃ 내지 120℃, 80℃ 내지 115℃, 85℃ 내지 100℃가 될 수 있다. 상기 범위에서, 편광자와 함께 포함되어 편광판의 고온 및 열충격에 의한 신뢰성을 높이고, 홀 기포 발생을 억제할 수 있다.
제1보호필름의 두께는 약 5㎛ 내지 약 200㎛, 구체적으로, 약 20㎛ 내지 약 40㎛가 될 수 있다. 상기 범위에서, 편광판에 사용될 수 있다.
제1보호필름의 상부면에는 기능성 코팅층, 예를 들면 하드코팅층, 내지문성층, 반사방지층 등이 더 형성될 수 있다.
제2보호필름
제2보호필름은 편광자 다른 일면에 적층되어, 편광자를 보호하고, 편광판의 기계적 강도를 높일 수 있다. 제2보호필름은 제1보호필름 대비 동일 또는 이종의 수지로 형성된 필름을 포함할 있다.
일 구체예에서, 제1보호필름이 트리아세틸셀룰로스 등을 포함하는 셀룰로스 에스테르계 수지 필름일 때, 제2보호필름은 트리아세틸셀룰로스 등을 포함하는 셀룰로스 에스테르계 수지 필름일 수 있다.
다른 구체예에서, 제1보호필름이 폴리에틸렌테레프탈레이트(PET) 등을 포함하는 폴리에스테르계 수지 필름일 때, 제2보호필름은 비정성 환상 폴리올레핀(cyclic olefin polymer, COP) 등을 포함하는 고리형 폴리올레핀계 수지 또는 트리아세틸셀룰로스 등을 포함하는 셀룰로스 에스테르계 수지 필름일 수 있다.
제2보호필름은 제1보호필름 대비 동일 또는 이종의 두께를 가질 수 있다.
일 구체예에서, 제2호 필름은 10℃/분의 승온 속도에서 열기계적 분석시 최초 수축 개시 온도가 70℃ 내지 130℃, 바람직하게는 75℃ 내지 125℃, 80℃ 내지 120℃, 80℃ 내지 115℃, 85℃ 내지 100℃가 될 수 있다. 상기 범위에서, 편광자와 함께 포함되어 편광판의 고온 및 열충격에 의한 신뢰성을 높이고, 홀 기포 발생을 억제할 수 있다.
편광판 중 제1보호필름, 제2보호필름은 각각 접착층에 의해 접착될 수 있다. 접착층은 당업자에게 알려진 통상의 편광판용 접착제에 의해 형성될 수 있다. 예를 들면, 접착층은 수계 접착제 또는 광경화성 접착제에 의해 형성될 수 있다. 바람직하게는 광경화성 접착제로 접착층을 형성함으로써 아연 유기산 염 중 유기산 음이온의 화학적 가교율을 높이고 유기산 음이온의 화학적 가교를 위한 추가적인 UV 처리 공정이 없어 공정성을 개선할 수 있다.
광경화성 접착제는 에폭시계 화합물, (메트)아크릴계 화합물 중 1종 이상 및 개시제를 포함할 수 있다. 상기 개시제는 광 라디칼 개시제, 광 양이온 개시제 중 1종 이상을 포함할 수 있다. 광경화성 접착제는 산화 방지제, 안료 등의 통상의 첨가제를 더 포함할 수 있다. 접착층은 두께가 약 0.1㎛ 내지 약 10㎛가 될 수 있다. 상기 범위에서 광학표시장치에 사용할 수 있다.
편광판의 하부면에는 점착층이 더 적층되어 편광판을 액정패널에 점착시킬 수 있다. 점착층은 감압 점착제 등으로 형성될 수 있지만, 이에 제한되지 않는다.
이하, 본 발명 일 실시예에 따른 광학표시장치를 설명한다.
본 발명의 광학표시장치는 본 발명의 편광자 또는 본 발명의 편광판을 포함할 수 있다. 광학표시장치는 액정표시장치, 발광표시장치 중 하나 이상을 포함할 수 있다. 발광표시장치는 발광소자로서, 유기 또는 유-무기 발광소자를 포함하고, LED(light emitting diode), OLED(organic light emitting diode), QLED(quantum dot light emitting diode), 형광체 등의 발광 물질을 포함하는 소자를 의미할 수 있다.
이하, 본 발명의 바람직한 실시예를 통해 본 발명의 구성 및 작용을 더욱 상세히 설명하기로 한다. 다만, 이는 본 발명의 바람직한 예시로 제시된 것이며 어떠한 의미로도 이에 의해 본 발명이 제한되는 것으로 해석될 수는 없다.
실시예 1
(1)편광자의 제조
25℃의 물로 수세한 폴리비닐알코올 필름(TS-#3000, 일본 Kuraray社, 주쇄에 소수성 작용기를 함유함, 두께:30㎛, 인장 강도(@25℃): 98MPa)을 30℃ 물의 팽윤조에서 팽윤 처리하였다.
팽윤조를 통과한 상기 필름을 요오드화칼륨 1mol/ml및 붕산 1중량%를 포함하는 수용액을 함유하는 30℃의 염착조에서 65초 동안 처리하였다. 염착조를 통과한 상기 필름을 붕산 3중량%를 함유하는 60℃ 수용액인 습식 연신조에서 연신비 5.9배로 연신시켰다. 상기 연신조를 통과한 상기 필름을 붕산 3중량%를 함유하는 25℃ 수용액을 함유하는 가교조에서 65초 동안 처리하였다.
가교조를 통과한 상기 필름을 요오드화칼륨 4.5중량%를 함유하는 30℃ 수용액인 보색액을 포함하는 보색조에서 10초 동안 처리하였다. 보색조를 통과한 상기 필름을 수세하고 건조시켜 편광자(두께:12㎛)를 제조하였다.
(2)편광판의 제조
상기 제조한 편광자의 양면에 수계 접착제를 도포하고 편광자의 일면에 트리아세틸셀룰로오스(TAC) 필름(두께:30㎛, FujiTAC, Fuiji社)을 합지시키고 편광자의 다른 일면에 트리아세틸셀룰로오스(TAC) 필름(두께:20㎛, FujiTAC, Fuiji社, 수축 개시 온도: 90℃)을 합지시켜 편광판을 제조하였다.
실시예 2 내지 실시예 5
실시예 1에서 염착조, 연신조, 가교조에서 각 성분의 함량을 변경하고, 연신 온도 및 연신비를 하기 표 1과 같이 변경하고, 보호 필름의 종류를 하기 표 1과 같이 변경한 것을 제외하고는 실시예 1과 동일한 방법으로 편광자 및 편광판을 제조하였다.
비교예 1
25℃의 물로 수세한 폴리비닐알코올 필름(PE-#3000, 일본 Kuraray社, 주쇄에 소수성 작용기를 함유하지 않음, 두께:30㎛)을 30℃ 물의 팽윤조에서 팽윤 처리하였다.
팽윤조를 통과한 상기 필름을 요오드화칼륨 1mol/ml 및 붕산 1중량%를 포함하는 수용액을 함유하는 30℃의 염착조에서 65초 동안 처리하였다. 염착조를 통과한 상기 필름을 붕산 3중량%를 함유하는 53℃ 수용액인 습식 연신조에서 연신비 5.7배로 연신시켰다. 상기 연신조를 통과한 상기 필름을 붕산 3중량%를 함유하는 25℃ 수용액을 함유하는 가교조에서 65초 동안 처리하였다.
가교조를 통과한 상기 필름을 요오드화칼륨 4.5중량%를 함유하는 30℃ 수용액인 보색액을 포함하는 보색조에서 10초 동안 처리하였다. 보색조를 통과한 상기 필름을 수세하고 건조시켜 편광자(두께:12㎛)를 제조하였다.
제조한 편광자를 실시예 1과 동일한 방법을 실시하여 편광판을 제조하였다.
비교예 2
폴리비닐알코올 필름(PE-#3000, 일본 Kuraray社, 주쇄에 소수성 작용기를 포함하지 않음. 두께:30㎛)을 사용해서 실시예 1과 동일한 방법을 실시하였다.
실시예와 비교예에서 제조한 편광자, 편광판에 대하여 하기 표 1의 물성을 평가하고 그 결과를 하기 표 1, 도 2에 나타내었다.
(1)흡열 피크(단위: ℃): 편광자 5mg 내지 10mg을 준비하고, 열 흐름(heat flow) 방식, -50℃ 내지 200℃ 온도 범위에서, 10℃/분의 승온 속도, 질소 분위기 하에서 시차 주사 열량계(Discovery, TA Instruments社)로 처리하여 최초 흡열 피크를 얻었다.
(2)최초 수축 개시 온도(단위: ℃): 편광판을 8mm x 5mm(편광자의 MD x 편광자의 TD)로 절단하고, 편광자의 연신 방향으로, -50℃ 내지 200℃ 온도 범위에서, 10℃/분의 승온 속도, 하중 0.02N, 질소 분위기 하에서 열 기계 분석 장치(Q400 TMA, TA Instruments社)로 처리하여 최초 수축 개시 온도를 얻었다.
(3)홀 기포 발생 평가: 유리(0.5T), 홀(반지름 5mm의 원형) 가공된 실시예와 비교예의 편광자, OCA(Optically Clear Adhesive, 3M社, OCA-8371), 유리(0.5T) 순서로 부착한 후 UVA 광원으로 2J/cm2의 광량으로 UV 경화시켜 샘플을 제작하였다. 상기 샘플을 -40℃에서 30분, 80℃에서 30분하는 것을 1사이클로 하여 100사이클 반복한 후(하기 (4)에서의 열 충격 부여 조건과 동일함) 홀 주변에 기포 발생 여부를 확인하였다. 홀 주변에 발생한 기포 크기(기포 직경)의 최대값이 100㎛ 이하인 경우 "X", 홀 주변에 100㎛ 초과의 기포 발생이 있는 경우 "○"로 평가하였다. 홀 주변에 발생한 기포 크기가 100㎛ 이하인 경우 실제 디스플레이에서 홀 주변의 블랙 매트릭스에 의해 기포가 가려져 사용자의 눈에 시인되지 않을 수 있다. 단, 여러 개의 기포가 연결되어 홀 주변에 발생하더라도 홀 중심에서 바깥쪽 방향으로의 길이가 100㎛ 이하이면 동일 이유로 시인되지 않기 때문에 "X"로 평가하였다.
(3)편광도 변화량(단위: %): 편광판을 3cm x 7cm(편광자의 MD x 편광자의 TD)로 절단하고, 편광판을 95℃에서 500시간 방치하기 전과 방치한 후, 파장 380 내지 780nm에서 JASCO社 V-7100을 이용하여 편광도를 측정하였다. 상기 식 1에 따른 편광도 변화량을 계산하였다.
열 충격에 따른 편광도 변화와 관련하여, 편광판을 -40℃에서 30분, 80℃에서 30분 방치하는 것을 1사이클로 하여 100사이클 반복하였을 때, 사이클 반복 전과 사이클 반복 후의 파장 380 내지 780nm에서 JASCO社 V-7100을 이용하여 편광도를 측정하였다. 상기 식 2에 따른 편광도 변화량을 계산하였다.
실시예 | 비교예 | |||||||
1 | 2 | 3 | 4 | 5 | 1 | 2 | ||
PVA 필름 | TS-#3000 | TS-#3000 | TS-#3000 | TS-#3000 | TS-#3000 | PE-#3000 | PE-#3000 | |
연신 온도(℃) | 60 | 60 | 58 | 60 | 60 | 53 | 60 | |
연신비 | 5.9 | 5.8 | 5.9 | 5.9 | 5.9 | 5.7 | 5.9 | |
제1보호필름 | TAC | TAC | TAC | COP** | TAC | TAC | TAC | |
제2보호필름 | TAC | TAC | TAC | TAC | COP** | TAC | TAC | |
흡열 피크 | 54 | 53 | 52 | 56 | 55 | 42 | -* | |
최초 수축 개시 온도 | 73 | 71 | 72 | 75 | 74 | 67 | -* | |
홀 기포 발생 | X | X | X | X | X | O | -* | |
편광도 변화량 | 식 1 | 0.10 | 0.15 | 0.12 | 0.08 | 0.07 | 0.21 | -* |
식 2 | 0.51 | 0.48 | 0.62 | 0.35 | 0.41 | 1.2 | -* |
표 1에서
*비교예 2는 연신시 폴리비닐알코올계 필름이 용융 파단되어 편광자를 제조할 수 없었음.
**COP: ZEON社, ZB12-052125
상기 표 1 및 도 2 에서와 같이, 본 발명의 편광자는 시차 주사 열량계 측정시 흡열 피크가 50℃ 내지 60℃이고, 본 발명의 편광판은 10℃/분의 승온 속도에서 열기계적 분석시 최초 수축 개시 온도가 70℃ 초과 90℃ 이하가 됨으로써, 홀에서 기포 발생 불량도 억제되었으며 고온 및 열충격 하에서 신뢰성이 우수하였다. 또한, 상기 표 1에서 도시되지 않았지만, 본 발명의 편광자 및 편광판은 광학표시장치에 적용시 빛샘 억제 효과가 우수하였다. 또한, 표 1에서 도시되지 않았지만, 본 발명의 편광판 역시 열기계적 분석시 최초 수축 개시 온도가 70℃ 초과 90℃ 이하가 되므로 홀 주변에서의 기포 발생이 억제될 수 있다.
반면에, 기존의 소수성 작용기를 포함하지 않는 폴리비닐알코올계 필름으로 제조된 비교예 1의 편광자는 상기 표 1 및 도 2에서와 같이 시차 주사 열량계 측정시 흡열 피크가 50℃ 미만이었으며, 비교예 1의 편광판은10℃/분의 승온 속도에서 열기계적 분석시 최초 수축 개시 온도가 70℃ 이하가 됨으로써, 고온 및 열충격 하에서 신뢰성이 좋지 못하고, 홀 기포 발생도 현저하였다.
기존의 소수성 작용기를 함유하지 않는 폴리비닐알코올계 필름을 본 발명의 실시예에 따라 제조한 비교예 2는 연신 과정에서 상기 필름이 용융 파단되어 편광자를 아예 제조할 수 없었다.
본 발명의 단순한 변형 내지 변경은 이 분야의 통상의 지식을 가진 자에 의하여 용이하게 실시될 수 있으며, 이러한 변형이나 변경은 모두 본 발명의 영역에 포함되는 것으로 볼 수 있다.
Claims (9)
- 폴리비닐알코올계 필름을 포함하고, 10℃/분의 승온 속도에서 시차 주사 열량계 측정시 흡열 피크가 50℃ 내지 60℃인 편광자.
- 제1항에 있어서, 상기 폴리비닐알코올계 필름은 친수성 작용기 및 소수성 작용기를 모두 갖는 것인, 편광자.
- 제1항에 있어서, 상기 폴리비닐알코올계 필름은 연화점이 약 65℃ 내지 약 71℃인 것인, 편광판.
- 편광자 및 상기 편광자의 일면과 다른 일면에 각각 적층된 보호 필름을 포함하는 편광판으로서,상기 편광판은 10℃/분의 승온 속도에서 열기계적 분석시 최초 수축 개시 온도가 70℃ 초과 90℃ 이하인 것인, 편광판.
- 제4항에 있어서, 상기 편광자는 폴리비닐알코올계 필름을 포함하고, 10℃/분의 승온 속도에서 시차 주사 열량계 측정시 흡열 피크가 50℃ 내지 60℃인 것인, 편광판.
- 제4항에 있어서, 상기 폴리비닐알코올계 필름은 친수성 작용기 및 소수성 작용기를 모두 갖는 것인, 편광판.
- 제4항에 있어서, 상기 보호 필름은 트리아세틸셀룰로스, 폴리에틸렌테레프탈레이트, 또는 비정성 환상 폴리올레핀 수지 필름을 포함하는 것인, 편광판.
- 제4항에 있어서, 상기 보호 필름은 10℃/분의 승온 속도에서 열기계적 분석시 최초 수축 개시 온도가 70℃ 내지 130℃인 것인, 편광판.
- 제1항 내지 제3항 중 어느 한 항의 편광자 또는 제4항 내지 제8항 중 어느 한 항의 편광판을 포함하는 것인, 광학표시장치.