WO2021125696A3 - 알루미늄합금 도금강판, 열간성형 부재 및 이들의 제조방법 - Google Patents
알루미늄합금 도금강판, 열간성형 부재 및 이들의 제조방법 Download PDFInfo
- Publication number
- WO2021125696A3 WO2021125696A3 PCT/KR2020/018115 KR2020018115W WO2021125696A3 WO 2021125696 A3 WO2021125696 A3 WO 2021125696A3 KR 2020018115 W KR2020018115 W KR 2020018115W WO 2021125696 A3 WO2021125696 A3 WO 2021125696A3
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- steel sheet
- aluminum alloy
- hot
- plated steel
- formed member
- Prior art date
Abstract
본 발명의 일 실시형태는 소지강판; 및 상기 소지강판 상에 형성된 알루미늄합금 도금층;을 포함하고, 상기 알루미늄합금 도금층은 중량%로, Zn: 21~35%, Si: 1~6.9%, Fe: 2~12%, 잔부 Al 및 기타 불가피한 불순물을 포함하는 표면 품질 및 용접성이 우수한 알루미늄합금 도금강판, 열간성형 부재 및 이들의 제조방법을 제공한다.
Priority Applications (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2022519555A JP2022550142A (ja) | 2019-12-18 | 2020-12-11 | アルミニウム合金めっき鋼板、熱間成形部材及びこれらの製造方法 |
US17/765,306 US20220372608A1 (en) | 2019-12-18 | 2020-12-11 | Aluminum alloy-plated steel sheet, hot-formed member, and methods for manufacturing aluminum alloy-plated steel sheet and hot-formed member |
CN202080084510.5A CN114761601A (zh) | 2019-12-18 | 2020-12-11 | 铝合金镀覆钢板、热成型部件及它们的制造方法 |
EP20901128.7A EP4079922A4 (en) | 2019-12-18 | 2020-12-11 | ALUMINUM ALLOY CLAD STEEL SHEET, HOT FORMED PART AND METHOD OF MANUFACTURING ALUMINUM ALLOY CLAD STEEL SHEET AND HOT FORMED PART |
JP2024000852A JP2024041853A (ja) | 2019-12-18 | 2024-01-05 | アルミニウム合金めっき鋼板、熱間成形部材及びこれらの製造方法 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020190170140A KR20210078277A (ko) | 2019-12-18 | 2019-12-18 | 알루미늄합금 도금강판, 열간성형 부재 및 이들의 제조방법 |
KR10-2019-0170140 | 2019-12-18 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2021125696A2 WO2021125696A2 (ko) | 2021-06-24 |
WO2021125696A3 true WO2021125696A3 (ko) | 2021-08-05 |
Family
ID=76477811
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/KR2020/018115 WO2021125696A2 (ko) | 2019-12-18 | 2020-12-11 | 알루미늄합금 도금강판, 열간성형 부재 및 이들의 제조방법 |
Country Status (6)
Country | Link |
---|---|
US (1) | US20220372608A1 (ko) |
EP (1) | EP4079922A4 (ko) |
JP (2) | JP2022550142A (ko) |
KR (2) | KR20210078277A (ko) |
CN (1) | CN114761601A (ko) |
WO (1) | WO2021125696A2 (ko) |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN117136252A (zh) * | 2020-12-18 | 2023-11-28 | 浦项股份有限公司 | 热压成型用镀覆钢板及其制造方法 |
KR102530077B1 (ko) * | 2021-10-06 | 2023-05-08 | 현대제철 주식회사 | 열간 프레스용 강판 및 이를 이용하여 제조된 핫 스탬핑 부품 |
CN114150252B (zh) * | 2021-11-30 | 2023-08-29 | 马鞍山钢铁股份有限公司 | 一种镀层热成形钢板、具有优良胶粘性能的热冲压零部件及制造方法和应用 |
DE102022115400A1 (de) * | 2022-06-21 | 2023-12-21 | Thyssenkrupp Steel Europe Ag | Blechformteil mit verbesserten Schweißeigenschaften |
KR20240094462A (ko) * | 2022-12-16 | 2024-06-25 | 주식회사 포스코 | 도금강판 및 그 제조방법 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2001303229A (ja) * | 2000-02-17 | 2001-10-31 | Nippon Steel Corp | プレス成形性およびメッキ密着性に優れた高強度合金化溶融亜鉛メッキ鋼板およびその製造方法 |
JP2013122079A (ja) * | 2011-12-12 | 2013-06-20 | Jfe Steel Corp | Al系めっき鋼材及びその製造方法 |
KR20150074882A (ko) * | 2013-12-24 | 2015-07-02 | 주식회사 포스코 | 열간 프레스 성형용 도금강판 및 그 제조방법 |
KR20190076796A (ko) * | 2017-12-22 | 2019-07-02 | 주식회사 포스코 | 용접 액화 취성에 대한 저항성 및 도금 밀착성이 우수한 알루미늄 합금 도금강판 |
KR20190078438A (ko) * | 2017-12-26 | 2019-07-04 | 주식회사 포스코 | 열간 프레스 성형용 도금강판, 이를 이용한 성형부재 및 이들의 제조방법 |
Family Cites Families (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP3006586B1 (en) * | 2013-06-07 | 2019-07-31 | Nippon Steel Corporation | Heat-treated steel material and method for producing same |
KR101528067B1 (ko) * | 2013-12-20 | 2015-06-10 | 주식회사 포스코 | 용접성 및 내식성이 우수한 열간 프레스 성형용 도금강판 및 그 제조방법 |
WO2017017484A1 (en) * | 2015-07-30 | 2017-02-02 | Arcelormittal | Method for the manufacture of a hardened part which does not have lme issues |
KR102065287B1 (ko) * | 2015-12-24 | 2020-01-10 | 주식회사 포스코 | 도금성 및 용접성이 우수한 오스테나이트계 용융 알루미늄 도금강판 및 그 제조방법 |
KR101858868B1 (ko) * | 2016-12-23 | 2018-05-16 | 주식회사 포스코 | 충격특성이 우수한 열간성형용 도금강판, 열간성형 부재 및 그들의 제조방법 |
RU2019128560A (ru) * | 2017-03-27 | 2021-04-28 | Ниппон Стил Корпорейшн | Алюминированный стальной лист |
-
2019
- 2019-12-18 KR KR1020190170140A patent/KR20210078277A/ko not_active Application Discontinuation
-
2020
- 2020-12-11 EP EP20901128.7A patent/EP4079922A4/en active Pending
- 2020-12-11 WO PCT/KR2020/018115 patent/WO2021125696A2/ko unknown
- 2020-12-11 US US17/765,306 patent/US20220372608A1/en active Pending
- 2020-12-11 JP JP2022519555A patent/JP2022550142A/ja active Pending
- 2020-12-11 CN CN202080084510.5A patent/CN114761601A/zh active Pending
-
2021
- 2021-12-03 KR KR1020210171784A patent/KR102560002B1/ko active IP Right Grant
-
2024
- 2024-01-05 JP JP2024000852A patent/JP2024041853A/ja active Pending
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2001303229A (ja) * | 2000-02-17 | 2001-10-31 | Nippon Steel Corp | プレス成形性およびメッキ密着性に優れた高強度合金化溶融亜鉛メッキ鋼板およびその製造方法 |
JP2013122079A (ja) * | 2011-12-12 | 2013-06-20 | Jfe Steel Corp | Al系めっき鋼材及びその製造方法 |
KR20150074882A (ko) * | 2013-12-24 | 2015-07-02 | 주식회사 포스코 | 열간 프레스 성형용 도금강판 및 그 제조방법 |
KR20190076796A (ko) * | 2017-12-22 | 2019-07-02 | 주식회사 포스코 | 용접 액화 취성에 대한 저항성 및 도금 밀착성이 우수한 알루미늄 합금 도금강판 |
KR20190078438A (ko) * | 2017-12-26 | 2019-07-04 | 주식회사 포스코 | 열간 프레스 성형용 도금강판, 이를 이용한 성형부재 및 이들의 제조방법 |
Also Published As
Publication number | Publication date |
---|---|
EP4079922A4 (en) | 2022-12-21 |
JP2022550142A (ja) | 2022-11-30 |
JP2024041853A (ja) | 2024-03-27 |
US20220372608A1 (en) | 2022-11-24 |
CN114761601A (zh) | 2022-07-15 |
KR102560002B1 (ko) | 2023-07-26 |
WO2021125696A2 (ko) | 2021-06-24 |
KR20210078277A (ko) | 2021-06-28 |
EP4079922A2 (en) | 2022-10-26 |
KR20210151035A (ko) | 2021-12-13 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2021125696A3 (ko) | 알루미늄합금 도금강판, 열간성형 부재 및 이들의 제조방법 | |
WO2016104879A8 (ko) | 프레스성형시 내파우더링성이 우수한 hpf 성형부재 및 이의 제조방법 | |
WO2016093598A8 (ko) | 표면품질 및 도금 밀착성이 우수한 초고강도 용융아연도금강판 및 그 제조방법 | |
WO2013089262A8 (ja) | Al系めっき鋼材及びその製造方法 | |
KR101788114B1 (ko) | 열간 프레스용 강판 및 열간 프레스용 강판을 이용한 열간 프레스 부재의 제조 방법 | |
MX2018007749A (es) | Lamina de acero recubierta con aleacion de aluminio-hierro para formacion en prensa caliente, que tiene excelente resistencia de fractura retardada de hidrogeno, resistencia de desprendimiento y soldabilidad, y el miembro formado en caliente usando la misma. | |
WO2018009041A8 (ko) | 균열전파 저항성 및 연성이 우수한 열간성형 부재 및 이의 제조방법 | |
WO2008093508A1 (ja) | リン酸塩処理性に優れた高強度合金化溶融亜鉛めっき鋼板 | |
WO2021125855A3 (ko) | 무방향성 전기강판 및 그 제조방법 | |
WO2016190538A8 (ko) | 내박리성이 우수한 hpf 성형부재 및 그 제조방법 | |
WO2009041511A1 (ja) | 親水性膜形成用組成物および親水性部材 | |
WO2017105026A8 (ko) | 화성처리성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법 | |
WO2016105115A8 (ko) | 표면품질, 도금밀착성 및 성형성이 우수한 고강도 용융아연도금강판 및 그 제조방법 | |
WO2017105025A8 (ko) | 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법 | |
WO2020111742A3 (ko) | 전기강판 및 그 제조 방법 | |
MX2015008230A (es) | Lamina de acero recocida y galvanizada aleada por inmersion en caliente y metodo para fabricar el mismo. | |
MX2021006198A (es) | Lamina de acero chapada con al-fe para formacion en prensa caliente que tiene excelente resistencia a la corrosion y soldabilidad por puntos y metodo de manufactura de la misma. | |
MA47727A (fr) | Procédé de soudage par points par résistance pour assembler des tôles d'acier revêtues de zinc | |
WO2007082786A8 (de) | Verzinktes walzhartes kaltgewalztes flachprodukt und verfahren zu seiner herstellung | |
WO2021125685A3 (ko) | 무방향성 전기강판 및 그 제조방법 | |
MX2020005506A (es) | Lamina de acero enchapada a base de aluminio, metodo de fabricacion de lamina de acero enchapada a base de aluminio, y metodo de fabricacion de componente para vehiculo. | |
MX2016010001A (es) | Lamina de acero galvano-recocida y metodo para la produccion de la misma. | |
WO2019154690A3 (de) | Wässrige suspension enthaltend metallcarbid-partikel | |
MX2020006336A (es) | Un sustrato de acero recubierto. | |
WO2021125858A3 (ko) | 법랑용 강판 및 그 제조방법 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 20901128 Country of ref document: EP Kind code of ref document: A2 |
|
ENP | Entry into the national phase |
Ref document number: 2022519555 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: 2020901128 Country of ref document: EP Effective date: 20220718 |