WO2020059902A1 - 실리콘산화물 코팅층이 형성된 양극 소재, 그를 포함하는 양극과 나트륨이온전지 및 그의 제조 방법 - Google Patents

실리콘산화물 코팅층이 형성된 양극 소재, 그를 포함하는 양극과 나트륨이온전지 및 그의 제조 방법 Download PDF

Info

Publication number
WO2020059902A1
WO2020059902A1 PCT/KR2018/011046 KR2018011046W WO2020059902A1 WO 2020059902 A1 WO2020059902 A1 WO 2020059902A1 KR 2018011046 W KR2018011046 W KR 2018011046W WO 2020059902 A1 WO2020059902 A1 WO 2020059902A1
Authority
WO
WIPO (PCT)
Prior art keywords
sodium ion
ion battery
silicon oxide
metal oxide
positive electrode
Prior art date
Application number
PCT/KR2018/011046
Other languages
English (en)
French (fr)
Inventor
조우석
김경수
정구진
유지상
Original Assignee
전자부품연구원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 전자부품연구원 filed Critical 전자부품연구원
Priority to PCT/KR2018/011046 priority Critical patent/WO2020059902A1/ko
Publication of WO2020059902A1 publication Critical patent/WO2020059902A1/ko

Abstract

본 발명은 나트륨이온전지의 전지 특성을 개선할 수 있는 실리콘산화물 코팅층이 형성된 양극 소재, 그를 포함하는 양극과 나트륨이온전지 및 그의 제조 방법에 관한 것이다. 본 발명은 Na1-xMeO2(Me = Ni, Fe and Mn, 0<x<1)로 표시되는 O3 층상계 구조를 갖는 금속산화물과, 금속산화물의 표면에 실리콘산화물로 코팅된 실리콘산화물 코팅층을 포함하는 나트륨이온전지용 양극 소재를 제공한다.

Description

실리콘산화물 코팅층이 형성된 양극 소재, 그를 포함하는 양극과 나트륨이온전지 및 그의 제조 방법
본 발명은 나트륨이온전지 및 그의 제조 방법에 관한 것으로, 더욱 상세하게는 양극 소재의 표면에 실리콘산화물을 코팅하여 전지 특성을 향상시킨 실리콘산화물 코팅층이 형성된 양극 소재, 그를 포함하는 양극과 나트륨이온전지 및 그의 제조 방법에 관한 것이다.
전자제품의 디지털화와 고성능화 등으로 소비자의 요구가 바뀜에 따라 시장요구도 박형, 경량화와 고에너지 밀도에 의한 고용량을 지니는 전지의 개발로 흐름이 바뀌고 있는 상황이다. 또한, 미래의 에너지 및 환경 문제를 대처하기 위하여 하이브리드 전기 자동차나 전기 자동차, 및 연료전지 자동차의 개발이 활발히 진행되고 있는 바, 자동차 전원용으로 전지의 대형화가 요구되고 있다.
소형 경량화 및 고용량으로 충방전 가능한 전지로서 리튬이차전지가 실용화되고 있으며, 소형 비디오 카메라, 휴대전화, 노트퍼스컴 등의 휴대용 전자 및 통신기기 등에 이용되고 있다. 리튬이차전지는 양극, 음극, 전해질로 구성되며, 충전에 의해 양극 소재로부터 나온 리튬이온이 음극 소재에 삽입되고 방전시 다시 탈리되는 등의 양 전극을 왕복하면서 에너지를 전달하는 역할을 하기 때문에 충방전이 가능하다.
한편, 최근에는 리튬 대신에 나트륨을 이용한 나트륨 기반 이차전지(이하 '나트륨이온전지'라 함)의 연구가 다시 재조명 되고 있다. 나트륨은 자원 매장량이 풍부하기 때문에 리튬 대신에 나트륨을 이용한 이차전지를 제작할 수 있다면 이차전지를 낮은 비용으로 제조할 수 있게 된다.
나트륨이온전지의 상용화를 위해 중요 소재인 양극 소재에 대한 연구가 활발하게 진행되고 있다. 양극 소재 중 층상계 구조를 가지는 금속산화물 Na1 - xMeO2(Me = Mn, Fe, Co, Ni 등)이 상용화 가능성이 높은 양극 소재로 주목받고 있다.
이러한 양극 소재 중 고가의 Co를 포함하지 않는 Ni-Fe-Mn계 양극 소재는 O3구조를 가지며 높은 가역용량의 확보가 가능한 것으로 알려져 있다. 하지만 Ni-Fe-Mn계 양극 소재는 출력 및 수명 특성과 관련된 전지 특성이 현저히 떨어지는 단점을 가지고 있다.
[선행기술문헌]
[특허문헌]
공개특허공보 제2017-0098529호 (2017.08.30. 공개)
이러한 Ni-Fe-Mn계 양극 소재의 단점은, 양극 소재의 표면에 나트륨 잔존물이 존재하며, 대기 노출 시 그 양이 현저히 증가하여 전지 특성을 저하시키는 요인으로 작용한다.
따라서 본 발명의 목적은 양극 소재의 표면 개질을 통해서 나트륨 잔존물과 같은 표면 부산물에 의한 저항을 저감시켜 안정적인 수명 특성을 확보하여 전지 특성을 향상시킬 수 있는 실리콘산화물 코팅층이 형성된 양극 소재, 그를 포함하는 양극과 나트륨이온전지 및 그의 제조 방법을 제공하는 데 있다.
상기 목적을 달성하기 위하여, 본 발명은 표면에 실리콘산화물 코팅층이 형성된 양극 소재, 그를 포함하는 양극과 나트륨이온전지 및 그의 제조 방법을 제공한다.
본 발명은 Na1 - xMeO2 (Me = Ni, Fe and Mn, 0<x<1)로 표시되는 O3 층상계 구조를 갖는 금속산화물; 및 상기 금속산화물의 표면에 실리콘산화물로 코팅된 실리콘산화물 코팅층;을 포함하는 나트륨이온전지용 양극 소재를 제공한다.
상기 금속산화물은 Na1 - xNiaFebMncO2 (a+b+c=1)으로 표시될 수 있다.
본 발명은 또한, Na1 - xMeO2 (Me = Ni, Fe and Mn, 0<x<1)로 표시되는 O3 층상계 구조를 갖는 금속산화물을 준비하는 단계; 및 상기 금속산화물의 표면에 실리콘산화물로 코팅하여 실리콘산화물 코팅층을 형성하는 단계;를 포함하는 나트륨이온전지용 양극 소재의 제조 방법을 제공한다.
상기 형성하는 단계는, 상기 금속산화물에 TEOS(tetraethyl orthosilicate)를 투입하는 단계; 상기 TEOS를 열처리로 실리콘산화물로 변환하는 단계; 및 상기 실리콘산화물이 상기 금속산화물의 표면에 코팅되어 실리콘산화물 코팅층을 형성하는 단계;를 포함할 수 있다.
상기 투입하는 단계에서, 상기 금속산화물 95 내지 99.5 wt%에 상기 TEOS 0.5 내지 5 wt%가 투입될 수 있다.
본 발명은 또한, 상기의 양극 소재를 포함하는 나트륨이온전지용 양극을 제공한다.
그리고 본 발명은 상기 양극을 포함하는 나트륨이온전지를 제공한다.
본 발명에 따르면, O3 층상계 구조를 갖는 금속산화물의 표면에 실리콘산화물 코팅층을 형성함으로써, 양극 소재의 표면에 존재할 수 있는 나트륨 잔존물과 같은 표면 부산물에 의한 저항을 저감시켜 안정적인 수명 특성을 확보하여 전지 특성을 향상시킬 수 있다.
도 1은 본 발명에 따른 나트륨이온전지용 양극 소재의 제조 방법에 따른 흐름도이다.
도 2는 도 1의 실리콘산화물 코팅층을 형성하는 단계를 보여주는 상세 흐름도이다.
도 3은 비교예에 따른 나트륨이온전지용 양극 소재를 보여주는 사진이다.
도 4는 실시예에 따른 나트륨이온전지용 양극 소재를 보여주는 사진이다.
도 5는 실시예에 따른 나트륨이온전지용 양극 소재의 SEM-EDS 분석 결과를 보여주는 사진이다.
도 6은 비교예 및 실시예에 따른 양극 소재를 사용한 나트륨이온전지의 충방전 특성을 보여주는 그래프이다.
도 7은 비교예 및 실시예에 따른 양극 소재를 사용한 나트륨이온전지의 출력 특성을 보여주는 그래프이다.
도 8은 비교예 및 실시예에 따른 양극 소재를 사용한 나트륨이온전지의 수명 특성을 보여주는 그래프이다.
하기의 설명에서는 본 발명의 실시예를 이해하는데 필요한 부분만이 설명되며, 그 이외 부분의 설명은 본 발명의 요지를 흩트리지 않는 범위에서 생략될 것이라는 것을 유의하여야 한다.
이하에서 설명되는 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념으로 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 따라서 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 바람직한 실시예에 불과할 뿐이고, 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.
이하, 첨부된 도면을 참조하여 본 발명의 실시예를 보다 상세하게 설명하고자 한다.
도 1은 본 발명에 따른 나트륨이온전지용 양극 소재의 제조 방법에 따른 흐름도이다. 도 2는 도 1의 실리콘산화물 코팅층을 형성하는 단계를 보여주는 상세 흐름도이다.
도 1 및 도 2를 참조하면, 본 발명에 따른 나트륨이온전지용 양극 소재의 제조 방법은 Na1 - xMeO2(Me = Ni, Fe and Mn, 0<x<1)로 표시되는 층상계 구조를 갖는 금속산화물을 준비하는 단계(S10)와, 금속산화물의 표면에 실리콘산화물로 코팅하여 실리콘산화물 코팅층을 형성하는 단계(S30)를 포함한다.
S10단계에 대해서 구체적으로 설명하면 다음과 같다. S10단계에서는 금속산화물은 분말 형태로 제조한다.
먼저 (Me)OH2(Me = Ni, Fe and Mn)로 표시되는 금속산화물 전구체와 Na2CO3를 포함하는 나트륨 전구체를 혼합하여 전구체 혼합물을 제조한다.
그리고 전구체 혼합물을 소성하여 O3 층상계 구조를 갖는 금속산화물을 제조한다. 이때 소성은 760 내지 960℃에서 14 내지 34시간 수행될 수 있다.
이때 금속산화물의 나트륨 함량이 1미만이 되도록 Na2CO3의 투입 양을 조절할 수 있다.
S10단계에서 제조된 금속산화물은 분말 형태로, Na1 - xMeO2(Me = Ni, Fe and Mn, 0<x<1)로 표시되는 O3 층상계 구조를 갖는다.
S30단계에 대해서 구체적으로 설명하면 다음과 같다.
먼저 S31단계에서 금속산화물에 TEOS(tetraethyl orthosilicate)를 투입한다. 즉 금속산화물 95 내지 99.5 wt%에 TEOS 0.5 내지 5 wt%가 투입한다. TEOS는 열처리를 통해서 실리콘산화물로 변환된다.
이때 S31단계는 용액 공정으로 진행되며, 금속산화물과 TEOS을 투입한 혼합액을 제조한 후, 금속산화물과 TEOS가 균일하게 혼합될 수 있도록 상온에서 일정 시간 교반한다. 그리고 혼합물을 필터링한 후 건조시켜 용매를 제거함으로써, 금속산화물의 표면에 TEOS가 흡착된 분말을 획득할 수 있다.
그리고 S33단계 TEOS를 열처리로 실리콘산화물로 변환시킨 후, S35단계에서 실리콘산화물을 금속산화물의 표면에 코팅하여 실리콘산화물 코팅층을 형성한다. 즉 금속산화물의 표면에 TEOS가 흡착된 분말을 열처리 설비에 투입한 후 공기 분위기에서 열처리 함으로써, 금속산화물의 표면에 흡착된 TEOS가 실리콘산화물로 변환되어 실리콘산화물 코팅층으로 형성된다.
본 발명의 제조 방법으로 제조된 양극 소재의 전기화학적 특성을 확인하기 위해서, 아래와 같이 실시예 및 비교예에 따른 양극 소재를 제조하였다.
비교예에 따른 양극 소재로는 Na 함량이 0.9인 Na0 . 9(Ni0.25Fe0.25Mn0.5)O2를 사용하였다. 비교예에 따른 양극 소재의 합성은 전구체인 (Ni0 . 25Fe0 . 25Mn0 . 5)OH2와 Na2CO3와 함께 정량비로 혼합한 후, 860℃에서 24시간 소성함으로서 제조하였다.
실시예에 따른 양극 소재는 비교예에 따른 양극 소재에 대해서 아래와 같이 실리콘산화물 코팅층을 형성하는 공정을 추가적으로 수행하여 제조하였다.
먼저 무수 에탄올 70 mL에 금속산화물 무게 대비 1wt%의 TEOS를 투입하여 약 10분간 교반하여 코팅 용액을 제조하였다. 제조된 코팅 용액을 상온에서 1시간 교반시킨 후, 필터링 후 80도에서 용매를 건조하여 금속산화물의 표면에 TEOS가 흡착된 분말을 제조하였다.
그리고 금속산화물의 표면에 TEOS가 흡착된 분말을 튜브 전기로에서 열처리함으로써, 실시예에 따른 양극 소재를 제조하였다. 이때 열처리는 700도에서 4시간 동안 공기 분위기에서 진행하였다. 열처리 과정에서 금속산화물의 표면에 흡착된 TEOS는 실리콘산화물로 변환되어 실리콘산화물 코팅층을 형성한다.
실시예 및 비교예에 따른 양극 소재를 이용한 나트륨이온전지의 전기화학적 특성 평가를 위하여, CR2032 코인셀을 제조하였다. 이때 음극은 Na 금속, 분리막은 글래스 파이버(glass fiber), 전해액은 1M의 NaClO4가 용해된 EC:PC(1:1)을 사용하였다.
도 3은 비교예에 따른 나트륨이온전지용 양극 소재를 보여주는 사진이다. 도 4는 실시예에 따른 나트륨이온전지용 양극 소재를 보여주는 사진이다. 도 3 및 도 4의 사진은 SEM 사진이며, (b) 사진은 (a) 사진을 확대한 것이다.
도 3 및 도 4에 도시된 바와 같이, 실시예에 따른 양극 소재와 비교예에 따른 양극 소재를 비교하면, 실시예에 따른 양극 소재의 표면에 실리콘산화물 코팅층이 형성되어 있는 것을 확인할 수 있었다.
도 5는 실시예에 따른 나트륨이온전지용 양극 소재의 SEM-EDS 분석 결과를 보여주는 사진이다.
도 5를 참조하면, 실시예에 따른 양극 소재가 Na, Ni, Fe, Mn, Si를 포함하고, 양극 소재의 표면에 Si가 균일하게 분포되어 있는 것을 확인할 수 있다.
즉 실시예에 따른 양극 소재는 표면에 실리콘산화물 소재의 실리콘산화물 코팅층이 형성되어 있음을 확인할 수 있다.
도 6은 비교예 및 실시예에 따른 양극 소재를 사용한 나트륨이온전지의 충방전 특성을 보여주는 그래프이다.
도 6을 참조하면, 0.1C에서의 충방전 특성을 평가한 그래프로부터, 실시예에따른 양극 소재를 사용한 나트륨이온전지의 과전압이 개선된 것을 확인 할 수 있다.
따라서 비교예에 따른 나트륨이온전지의 방전 용량은 161 mAh/g이지만, 실시예에 따른 나트륨이온전지의 방전 용량은 175 mAh/g으로 향상된 것을 확인할 수 있다.
표 1은 비교예 및 실시예에 따른 양극 소재를 사용한 나트륨이온전지의 0.1C 내지 5C에서의 출력 특성을 측정한 값이다. 표 1에서 Na 0.9.는 비교예를 나타내고, H.TEOS는 실시예를 나타낸다.
Figure PCTKR2018011046-appb-T000001
도 7은 비교예 및 실시예에 따른 양극 소재를 사용한 나트륨이온전지의 출력 특성을 보여주는 그래프이다.
표 1 및 도 7을 참조하면, 실시예가 우수한 출력 특성을 나타내는 것을 확인할 수 있다. 특히 방전 곡선을 보면, 실시예에 따른 나트륨이온전지가 과전압이 현저히 개선되어 용량이 증가하는 것을 알 수 있다. 이것은 실시예에 따른 나트륨이온전지가 에너지밀도(Wh) 측면에서도 더욱 우수한 특성을 나타내는 것을 의미한다.
표 2는 비교예 및 실시예에 따른 양극 소재를 사용한 나트륨이온전지의 1회, 50 및 100회 사이클 후 용량 유지율을 측정한 값이다. 이때 수명 향상 여부 확인을 위한 0.5C에서 상온 사이클 특성 평가로 진행하였다.
Figure PCTKR2018011046-appb-T000002
도 8은 비교예 및 실시예에 따른 양극 소재를 사용한 나트륨이온전지의 수명 특성을 보여주는 그래프이다.
표 2 및 도 8을 참조하면, 100 사이클 후 용량 유지율을 비교하면, 비교예는 82%, 실시예는 88%로 실리콘산화물 코팅으로 수명 특성이 개선된 것을 확인할 수 있다.
이와 같이 본 발명에는 O3 층상계 구조를 갖는 금속산화물의 표면에 실리콘산화물 코팅층을 형성함으로써, 양극 소재의 표면에 존재할 수 있는 나트륨 잔존물과 같은 표면 부산물에 의한 저항을 저감시키고, 이를 통해서 나트륨이온전지의 안정적인 수명 특성을 확보하여 전지 특성을 향상시킬 수 있다.
한편, 본 명세서와 도면에 개시된 실시예들은 이해를 돕기 위해 특정 예를 제시한 것에 지나지 않으며, 본 발명의 범위를 한정하고자 하는 것은 아니다. 여기에 개시된 실시예들 이외에도 본 발명의 기술적 사상에 바탕을 둔 다른 변형예들이 실시 가능하다는 것은, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게는 자명한 것이다.

Claims (10)

  1. Na1 - xMeO2 (Me = Ni, Fe and Mn, 0<x<1)로 표시되는 O3 층상계 구조를 갖는 금속산화물; 및
    상기 금속산화물의 표면에 실리콘산화물로 코팅된 실리콘산화물 코팅층;
    을 포함하는 나트륨이온전지용 양극 소재.
  2. 제1항에 있어서,
    상기 금속산화물은 Na1 - xNiaFebMncO2 (a+b+c=1)으로 표시되는 것을 특징으로 하는 나트륨이온전지용 양극 소재.
  3. Na1 - xMeO2 (Me = Ni, Fe and Mn, 0<x<1)로 표시되는 O3 층상계 구조를 갖는 금속산화물을 준비하는 단계; 및
    상기 금속산화물의 표면에 실리콘산화물로 코팅하여 실리콘산화물 코팅층을 형성하는 단계;
    를 포함하는 나트륨이온전지용 양극 소재의 제조 방법.
  4. 제3항에 있어서, 상기 준비하는 단계에서,
    상기 금속산화물은 Na1 - xNiaFebMncO2 (a+b+c=1)으로 표시되는 것을 특징으로 하는 나트륨이온전지용 양극 소재의 제조 방법.
  5. 제4항에 있어서, 상기 형성하는 단계에서,
    상기 금속산화물에 TEOS(tetraethyl orthosilicate)를 투입하는 단계;
    상기 TEOS를 열처리로 실리콘산화물로 변환하는 단계; 및
    상기 실리콘산화물이 상기 금속산화물의 표면에 코팅되어 실리콘산화물 코팅층을 형성하는 단계;
    를 포함하는 것을 특징으로 하는 나트륨이온전지용 양극 소재의 제조 방법.
  6. 제5항에 있어서,
    상기 투입하는 단계에서,
    상기 금속산화물 95 내지 99.5 wt%에 상기 TEOS 0.5 내지 5 wt%가 투입되는 것을 특징으로 하는 나트륨이온전지용 양극 소재의 제조 방법.
  7. Na1 - xMeO2 (Me = Ni, Fe and Mn, 0<x<1)로 표시되는 O3 층상계 구조를 갖는 금속산화물과, 상기 금속산화물의 표면에 실리콘산화물로 코팅된 실리콘산화물 코팅층을 구비하는 양극 소재를 포함하는 나트륨이온전지용 양극.
  8. 제7항에 있어서,
    상기 금속산화물은 Na1 - xNiaFebMncO2 (a+b+c=1)으로 표시되는 것을 특징으로 하는 나트륨이온전지용 양극.
  9. Na1 - xMeO2 (Me = Ni, Fe and Mn, 0<x<1)로 표시되는 O3 층상계 구조를 갖는 금속산화물과, 상기 금속산화물의 표면에 실리콘산화물로 코팅된 실리콘산화물 코팅층을 구비하는 양극 소재를 함유하는 양극을 포함하는 나트륨이온전지.
  10. 제9항에 있어서,
    상기 금속산화물은 Na1 - xNiaFebMncO2 (a+b+c=1)으로 표시되는 것을 특징으로 하는 나트륨이온전지.
PCT/KR2018/011046 2018-09-19 2018-09-19 실리콘산화물 코팅층이 형성된 양극 소재, 그를 포함하는 양극과 나트륨이온전지 및 그의 제조 방법 WO2020059902A1 (ko)