WO2020029001A1 - 一种阀门的制作方法 - Google Patents

一种阀门的制作方法 Download PDF

Info

Publication number
WO2020029001A1
WO2020029001A1 PCT/CN2018/098918 CN2018098918W WO2020029001A1 WO 2020029001 A1 WO2020029001 A1 WO 2020029001A1 CN 2018098918 W CN2018098918 W CN 2018098918W WO 2020029001 A1 WO2020029001 A1 WO 2020029001A1
Authority
WO
WIPO (PCT)
Prior art keywords
parts
valve
manufacturing
sand
mold
Prior art date
Application number
PCT/CN2018/098918
Other languages
English (en)
French (fr)
Inventor
周天毫
Original Assignee
苏州速腾电子科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 苏州速腾电子科技有限公司 filed Critical 苏州速腾电子科技有限公司
Priority to PCT/CN2018/098918 priority Critical patent/WO2020029001A1/zh
Publication of WO2020029001A1 publication Critical patent/WO2020029001A1/zh

Abstract

一种阀门的制作方法包括以下几个步骤：(1)制作模具；(2)型砂造型；(3)熔炼；(4)浇注；(5)冷却；(6)回火；(7)除油。此阀门制作方法，采用精炼的钢液，同时在浇注前进行孕育，浇注后得到的阀门表面缩孔少，内部气孔少；同时，整体硬度差别小，分阶段冷却和回火处理提高了阀门表面的硬度；最后采取了除油处理，阀门整体干净，光亮。

Description

一种阀门的制作方法 技术领域
本发明涉及一种阀门的制作方法，属于阀门加工技术领域。
背景技术
阀门是流体输送***中的控制部件，具有截止、调节、导流、防止逆流、稳压、分流或溢流泄压等功能。阀门根据材质分为铸铁阀门，铸钢阀门，不锈钢阀门，铬钼钢阀门，铬钼钒钢阀门，双相钢阀门，塑料阀门，非标订制等阀门材质。目前在铸钢行业中，铸钢件在铸造时通常要制造模具、浇注再进行阀门的后期处理，处理不当则得到的铸钢容易产生裂纹、砂眼、气孔等缺陷，影响了产品的质量，因此，合理的生产工艺成为本领域技术人员亟待解决的技术问题。
发明内容
为了克服现有技术的不足，本发明提供了一种阀门的制作方法。
本发明是通过以下技术方案来实现的：
一种阀门的制作方法，包括以下几个步骤：
(1)制作模具：根据阀门的形状制作模具，模具上设置有冒口和浇口；
(2)型砂造型：在模具周围采用耐热型砂制作砂型，取出模具，得到砂型；
(3)熔炼：将钢材置于三相电弧炉中，升温至1500-1650℃，转入脱碳炉，通入氧气，同时，加入精炼剂，得到钢液；
(4)浇注：往钢液中加入孕育剂，反应5-8min后，往砂型中浇注钢液，浇注温度为1500-1600℃；
(5)冷却：快速冷却至800-900℃，保温10-20min；快速降温至350-400℃，保温20-30min；快速冷却至室温后；清理阀门表面，切除浇口、冒口、铲磨毛刺和披缝等凸出物，再次清理残砂；
(6)回火：将阀门加热至350-400℃，保温20-30min；冷却至室温后加热至600-700℃，保温10-15min；缓慢冷却至室温；
(7)除油：将阀门置于除油剂中浸泡30-40min，冲洗烘干后即可得到阀门。
所述的一种阀门的制作方法，所述精炼剂包括以下重量份数的原料：氟化钠10-15份、氯化镁10-15份、氯化钾5-10份、氟化钡10-15份、碳酸铝2-6份和氧化钙1-5份。
所述的一种阀门的制作方法，所述孕育剂包括以下重量份数的原料：铁1-5份、钙1-5份、铝5-10份、锶1-3份、钡1-3份和镧1-3份。
所述的一种阀门的制作方法，所述除油剂包括以下重量份数的原料：面粉3-8份、聚丙烯酰胺10-15份、柚子皮提取物10-15份、柠檬酸钠1-3份、椰子油脂肪酸二乙醇酰胺10-15份和水40-50份。
所述的一种阀门的制作方法，所述柚子皮提取物是通过以下步骤获得的：将柚子皮晒干后置于乙醇溶液中，回流萃取60-80min；过滤，将乙醇进行浓缩，进行喷雾干燥后得到柚子皮萃取物。
所述的一种阀门的制作方法，所述除油剂是通过以下步骤获得的：将水加热至50-60℃，加入面粉和柚子皮提取物，充分搅拌混合后，加入柠檬酸，然后再加入聚丙烯酰胺和椰子油脂肪酸二乙醇酰胺，搅拌混合后得到除油剂。
本发明所达到的有益效果：
本发明的阀门制作方法，采用精炼的钢液，同时在浇注前进行孕育，浇注后得到的阀门表面缩孔少，内部气孔少；同时，整体硬度差别小，分阶段冷却和回火处理提高了阀门表面的硬度；最后采取了除油处理，阀门整体干净，光亮。
本发明的精炼剂组分简单，能够去除钢液内的杂质，提高钢液纯度，保证钢液的表面均匀；
本发明的孕育剂组分简单，能够细化晶粒，优化晶核形成，提高阀门本身的硬度；
本发明的除油剂组分环保，除油效果好，对环境污染小，采用柚子皮提取物去油效果好同时充分利用柚子皮；提取方法简单，配合面粉、聚丙烯酰胺、柠檬酸钠和椰子油脂肪酸二乙醇酰胺，去油能力强。
具体实施方式
以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
实施例1
一种阀门的制作方法，包括以下几个步骤：
(1)制作模具：根据阀门的形状制作模具，模具上设置有冒口和浇口；
(2)型砂造型：在模具周围采用耐热型砂制作砂型，取出模具，得到砂型；
(3)熔炼：将钢材置于三相电弧炉中，升温至1500-1650℃，转入脱碳炉，通入氧气，同时，加入精炼剂，得到钢液；
(4)浇注：往钢液中加入孕育剂，反应5-8min后，往砂型中浇注钢液，浇注温度为1500-1600℃；
(5)冷却：快速冷却至800-900℃，保温10-20min；快速降温至350-400℃，保温20-30min；快速冷却至室温后；清理阀门表面，切除浇口、冒口、铲磨毛刺和披缝等凸出物，再次清理残砂；
(6)回火：将阀门加热至350-400℃，保温20-30min；冷却至室温后加热至600-700℃，保温10-15min；缓慢冷却至室温；
(7)除油：将阀门置于除油剂中浸泡30-40min，冲洗烘干后即可得到阀门。
所述精炼剂包括以下重量份数的原料：氟化钠10份、氯化镁10份、氯化钾5份、氟化钡10份、碳酸铝6份和氧化钙5份。
所述孕育剂包括以下重量份数的原料：铁1份、钙1份、铝10份、锶1份、钡1份和镧1份。
所述除油剂包括以下重量份数的原料：面粉8份、聚丙烯酰胺10份、柚子皮提取物10份、柠檬酸钠1份、椰子油脂肪酸二乙醇酰胺10份和水50份。
所述柚子皮提取物是通过以下步骤获得的：将柚子皮晒干后置于乙醇溶液中，回流萃取60-80min；过滤，将乙醇进行浓缩，进行喷雾干燥后得到柚子皮萃取物。
所述除油剂是通过以下步骤获得的：将水加热至50-60℃，加入面粉和柚子皮提取物，充分搅拌混合后，加入柠檬酸，然后再加入聚丙烯酰胺和椰子油脂肪酸二乙醇酰胺，搅拌混合后得到除油剂。
实施例2
一种阀门的制作方法，包括以下几个步骤：
(1)制作模具：根据阀门的形状制作模具，模具上设置有冒口和浇口；
(2)型砂造型：在模具周围采用耐热型砂制作砂型，取出模具，得到砂型；
(3)熔炼：将钢材置于三相电弧炉中，升温至1500-1650℃，转入脱碳炉，通入氧气，同时，加入精炼剂，得到钢液；
(4)浇注：往钢液中加入孕育剂，反应5-8min后，往砂型中浇注钢液，浇注温度为1500-1600℃；
(5)冷却：快速冷却至800-900℃，保温10-20min；快速降温至350-400℃，保温20-30min；快速冷却至室温后；清理阀门表面，切除浇口、冒口、铲磨毛刺和披缝等凸出物，再次清理残砂；
(6)回火：将阀门加热至350-400℃，保温20-30min；冷却至室温后加热至600-700℃，保温10-15min；缓慢冷却至室温；
(7)除油：将阀门置于除油剂中浸泡30-40min，冲洗烘干后即可得到阀门。
所述精炼剂包括以下重量份数的原料：氟化钠15份、氯化镁15份、氯化钾5份、氟化钡10份、碳酸铝2份和氧化钙1份。
所述孕育剂包括以下重量份数的原料：铁5份、钙5份、铝5份、锶3份、钡3份和镧3份。
所述除油剂包括以下重量份数的原料：面粉3份、聚丙烯酰胺15份、柚子皮提取物15份、柠檬酸钠3份、椰子油脂肪酸二乙醇酰胺15份和水40份。
所述柚子皮提取物是通过以下步骤获得的：将柚子皮晒干后置于乙醇溶液中，回流萃取60-80min；过滤，将乙醇进行浓缩，进行喷雾干燥后得到柚子皮萃取物。
所述除油剂是通过以下步骤获得的：将水加热至50-60℃，加入面粉和柚子皮提取物，充分搅拌混合后，加入柠檬酸，然后再加入聚丙烯酰胺和椰子油脂肪酸二乙醇酰胺，搅拌混合后得到除油剂。
实施例3
一种阀门的制作方法，包括以下几个步骤：
(1)制作模具：根据阀门的形状制作模具，模具上设置有冒口和浇口；
(2)型砂造型：在模具周围采用耐热型砂制作砂型，取出模具，得到砂型；
(3)熔炼：将钢材置于三相电弧炉中，升温至1500-1650℃，转入脱碳炉，通入氧气，同时，加入精炼剂，得到钢液；
(4)浇注：往钢液中加入孕育剂，反应5-8min后，往砂型中浇注钢液，浇注温度为1500-1600℃；
(5)冷却：快速冷却至800-900℃，保温10-20min；快速降温至350-400℃，保温20-30min；快速冷却至室温后；清理阀门表面，切除浇口、冒口、铲磨毛刺和披缝等凸出物，再次清理残砂；
(6)回火：将阀门加热至350-400℃，保温20-30min；冷却至室温后加热至600-700℃，保温10-15min；缓慢冷却至室温；
(7)除油：将阀门置于除油剂中浸泡30-40min，冲洗烘干后即可得到阀门。
所述精炼剂包括以下重量份数的原料：氟化钠12份、氯化镁12份、氯化钾8份、氟化钡12份、碳酸铝5份和氧化钙3份。
所述孕育剂包括以下重量份数的原料：铁2份、钙2份、铝8份、锶2份、钡2份和镧2份。
所述除油剂包括以下重量份数的原料：面粉5份、聚丙烯酰胺12份、柚子皮提取物12份、柠檬酸钠2份、椰子油脂肪酸二乙醇酰胺12份和水45份。
所述柚子皮提取物是通过以下步骤获得的：将柚子皮晒干后置于乙醇溶液中，回流萃取60-80min；过滤，将乙醇进行浓缩，进行喷雾干燥后得到柚子皮萃取物。
所述除油剂是通过以下步骤获得的：将水加热至50-60℃，加入面粉和柚子皮提取物，充分搅拌混合后，加入柠檬酸，然后再加入聚丙烯酰胺和椰子油脂肪酸二乙醇酰胺，搅拌混合后得到除油剂。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变形，这些改进和变形也应视为本发明的保护范围。

Claims (6)

  1. 一种阀门的制作方法，其特征是，包括以下几个步骤：
    (1)制作模具：根据阀门的形状制作模具，模具上设置有冒口和浇口；
    (2)型砂造型：在模具周围采用耐热型砂制作砂型，取出模具，得到砂型；
    (3)熔炼：将钢材置于三相电弧炉中，升温至1500-1650℃，转入脱碳炉，通入氧气，同时，加入精炼剂，得到钢液；
    (4)浇注：往钢液中加入孕育剂，反应5-8min后，往砂型中浇注钢液，浇注温度为1500-1600℃；
    (5)冷却：快速冷却至800-900℃，保温10-20min；快速降温至350-400℃，保温20-30min；快速冷却至室温后；清理阀门表面，切除浇口、冒口、铲磨毛刺和披缝等凸出物，再次清理残砂；
    (6)回火：将阀门加热至350-400℃，保温20-30min；冷却至室温后加热至600-700℃，保温10-15min；缓慢冷却至室温；
    (7)除油：将阀门置于除油剂中浸泡30-40min，冲洗烘干后即可得到阀门。
  2. 根据权利要求1所述的一种阀门的制作方法，其特征是，所述精炼剂包括以下重量份数的原料：氟化钠10-15份、氯化镁10-15份、氯化钾5-10份、氟化钡10-15份、碳酸铝2-6份和氧化钙1-5份。
  3. 根据权利要求1所述的一种阀门的制作方法，其特征是，所述孕育剂包括以下重量份数的原料：铁1-5份、钙1-5份、铝5-10份、锶1-3份、钡1-3份和镧1-3份。
  4. 根据权利要求1所述的一种阀门的制作方法，其特征是，所述除油剂包括以下重量份数的原料：面粉3-8份、聚丙烯酰胺10-15份、柚子皮提取物10-15份、柠檬酸钠1-3份、椰子油脂肪酸二乙醇酰胺10-15份和水40-50份。
  5. 根据权利要求4所述的一种阀门的制作方法，其特征是，所述柚子皮提取物是通过以下步骤获得的：将柚子皮晒干后置于乙醇溶液中，回流萃取60-80min；过滤，将乙醇进行浓缩，进行喷雾干燥后得到柚子皮萃取物。
  6. 根据权利要求4或5所述的一种阀门的制作方法，其特征是，所述除油 剂是通过以下步骤获得的：将水加热至50-60℃，加入面粉和柚子皮提取物，充分搅拌混合后，加入柠檬酸，然后再加入聚丙烯酰胺和椰子油脂肪酸二乙醇酰胺，搅拌混合后得到除油剂。
PCT/CN2018/098918 2018-08-06 2018-08-06 一种阀门的制作方法 WO2020029001A1 (zh)