WO2019125065A1 - 가공성이 우수한 에틸렌/1-부텐 공중합체 - Google Patents
가공성이 우수한 에틸렌/1-부텐 공중합체 Download PDFInfo
- Publication number
- WO2019125065A1 WO2019125065A1 PCT/KR2018/016503 KR2018016503W WO2019125065A1 WO 2019125065 A1 WO2019125065 A1 WO 2019125065A1 KR 2018016503 W KR2018016503 W KR 2018016503W WO 2019125065 A1 WO2019125065 A1 WO 2019125065A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbon atoms
- ethylene
- group
- butene copolymer
- molecular weight
- Prior art date
Abstract
Description
Claims