WO2017111061A1 - クリーニングブレード - Google Patents
クリーニングブレード Download PDFInfo
- Publication number
- WO2017111061A1 WO2017111061A1 PCT/JP2016/088454 JP2016088454W WO2017111061A1 WO 2017111061 A1 WO2017111061 A1 WO 2017111061A1 JP 2016088454 W JP2016088454 W JP 2016088454W WO 2017111061 A1 WO2017111061 A1 WO 2017111061A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- surface treatment
- elastic body
- treatment layer
- mpa
- elastic modulus
- Prior art date
Abstract
Description
図1に示すように、クリーニングブレード1は、ブレード本体(これ自体をクリーニングブレードともいう)10と支持部材20とを備えており、ブレード本体10と支持部材20とは図示されない接着剤を介して接合されている。ブレード本体10は、ゴム基材の成形体である弾性体11で構成される。弾性体11は、その表層部に表面処理層12が形成されている。表面処理層12は、弾性体11の表層部に表面処理液を含浸させ硬化することにより形成したものであり、表面処理液に含有されるイソシアネート化合物を含む硬化物であって弾性体11と反応したものである。表面処理層12は、弾性体11のクリーニング対象と当接する部分に少なくとも形成すればよいが、本実施形態では、弾性体11の表面全体の表層部に表面処理層12を形成してある。
(ゴム弾性体の作製)
ポリオールとしてカプロラクトン系ポリオール(分子量2,000)100質量部とイソシアネート化合物として4,4’―ジフェニルメタンジイソシアネート(MDI)55質量部とを115℃×20分間反応させた後、架橋剤として1,4-ブタンジオール11.5質量部、トリメチロールプロパン2.9質量部を混合し、140℃に保った金型で40分間加熱硬化させた。成形後、幅15mm、厚さ2.0mm、長さ350mmに切断加工し、ゴム弾性体とした。得られたゴム弾性体は弾性率が20MPaであった。
2官能イソシアネート化合物としてMDI(日本ポリウレタン工業(株)製、分子量250.25)と、2官能ポリオールとしてPDO(東京化成工業(株)製、分子量76.09と、3官能ポリオールとしてTMP(三菱ガス化学(株)製、分子量134.17)と、有機溶剤としてMEKとを、イソシアネート基と水酸基との比率が1.2、また、2官能ポリオールと3官能ポリオールとの比率が85/15となるように混合し、濃度3質量%の表面処理液を調製した。ここで、表面処理液の濃度(質量%)は、表面処理液の全体の質量に対するイソシアネート化合物及びポリオールの質量の割合とする。
表面処理液を23℃に保ったまま、ゴム弾性体を処理液に10秒間浸漬後、50℃で保たれたオーブンで10分間加熱した。その後、表面処理されたゴム弾性体を支持部材に接着してクリーニングブレードとした。これにより、弾性率21MPaで厚さ30μmの表面処理層を有し、表面処理層とゴム弾性体との弾性率差1.0MPaのクリーニングブレードを得た。
実施例1と同様の手順でゴム弾性体を得た。得られたゴム弾性体は20MPaであった。そして、濃度8質量%とした以外は、実施例1と同様な表面処理液を用い、実施例1と同様の手順でゴム弾性体の表面処理をおこなった。これにより、弾性率25MPaで厚さ30μmの表面処理層を有し、表面処理層とゴム弾性体との弾性率差5.0MPaのクリーニングブレードを得た。
MDIを62質量部、1,4-ブタンジオール13.3質量部、トリメチロールプロパン3.3質量部とした以外は実施例1と同様の手順でゴム弾性体を得た。得られたゴム弾性体の弾性率は36MPaであった。そして、濃度20質量%とした以外は、実施例1と同様な表面処理液を用い、実施例1と同様の手順でゴム弾性体の表面処理をおこなった。弾性率64MPaで厚さ30μmの表面処理層を有し、表面処理層とゴム弾性体との弾性率差28MPaのクリーニングブレードを得た。
MDIを69質量部、1,4-ブタンジオール15.2質量部、トリメチロールプロパン3.8質量部とし、160℃に保った金型を用いた以外は実施例1と同様の手順でゴム弾性体を得た。得られたゴム弾性体の弾性率は42MPaであった。そして、濃度15質量%とした以外は、実施例1と同様な表面処理液を用い、実施例1と同様の手順でゴム弾性体の表面処理をおこなった。弾性率63MPaで厚さ30μmの表面処理層を有し、表面処理層とゴム弾性体との弾性率差21MPaのクリーニングブレードを得た。
MDIを71質量部、1,4-ブタンジオール15.9質量部、トリメチロールプロパン3.9質量部とし、170℃に保った金型を用いた以外は実施例1と同様の手順でゴム弾性体を得た。得られたゴム弾性体の弾性率は55MPaであった。そして、実施例4と同様な表面処理液を用い、ゴム弾性体の表面処理をおこなった。弾性率87MPaで厚さ30μmの表面処理層を有し、表面処理層とゴム弾性体との弾性率差32MPaのクリーニングブレードを得た。
MDIを74質量部、1,4-ブタンジオール16.6質量部、トリメチロールプロパン4.1質量部とし、170℃に保った金型を用いた以外は実施例1と同様の手順でゴム弾性体を得た。得られたゴム弾性体の弾性率は60MPaであった。そして、実施例4と同様な表面処理液を用い、ゴム弾性体の表面処理をおこなった。弾性率95MPaで厚さ35μmの表面処理層を有し、表面処理層とゴム弾性体との弾性率差35MPaのクリーニングブレードを得た。
実施例3と同様の手順でゴム弾性体を得た。得られたゴム弾性体の弾性率は30MPaであった。また、表面処理は施さず、支持部材と接着してクリーニングブレードを得た。なお、表に示す表層弾性率にはゴム弾性体の値を示した。
実施例6と同様の手順でゴム弾性体を得た。得られたゴム弾性体の弾性率は60MPaであった。また、表面処理は施さず、支持部材と接着してクリーニングブレードを得た。なお、表に示す表層弾性率にはゴム弾性体の値を示した。
実施例6と同様の手順でゴム弾性体を得た。得られたゴム弾性体の弾性率は60MPaであった。そして、濃度35質量%とした以外は、実施例1と同様な表面処理液を用い、実施例1と同様の手順でゴム弾性体の表面処理をおこなった。弾性率99MPaで厚さ30μmの表面処理層を有し、表面処理層とゴム弾性体との弾性率差39MPaのクリーニングブレードを得た。
実施例1と同様の手順でゴム弾性体を得た。得られたゴム弾性体の弾性率は20MPaであった。そして、濃度1質量%とした以外は、実施例1と同様な表面処理液を用い、実施例1と同様の手順でゴム弾性体の表面処理をおこなった。弾性率20.3MPaで厚さ30μmの表面処理層を有し、表面処理層とゴム弾性体との弾性率差0.3MPaのクリーニングブレードを得た。
<表面処理層及びゴム弾性体の弾性率、並びにこれらの弾性率の差の評価>
実施例1~6及び比較例1~4のクリーニングブレードを用いて、耐カケ性、フィルミング抑制性及びクリーニング性の評価を行った。なお、これらの評価は、A3サイズカラーMFP 55枚/分機を用いて行った。
10 ブレード本体
11 弾性体
12 表面処理層
20 支持部材
Claims (2)
- ゴム基材の成形体である弾性体を有し、前記弾性体の被接触体と当接する部位に少なくとも表面処理層を有するクリーニングブレードであって、
前記表面処理層は、前記弾性体の表層部に含浸したイソシアネート化合物を含む硬化物であって前記弾性体と反応したもので形成され、
前記表面処理層の弾性率は95MPa以下であり、
前記弾性体の弾性率は20MPa以上60MPa以下であり、
前記表面処理層の弾性率と前記弾性体の弾性率との差は、1MPa以上であることを特徴とするクリーニングブレード。 - 請求項1に記載のクリーニングブレードにおいて、
前記表面処理層は、厚さが10μm以上50μm以下であることを特徴とするクリーニングブレード。