WO2017018453A1 - モデル材用樹脂組成物、サポート材用樹脂組成物、光造形品、および、光造形品の製造方法 - Google Patents
モデル材用樹脂組成物、サポート材用樹脂組成物、光造形品、および、光造形品の製造方法 Download PDFInfo
- Publication number
- WO2017018453A1 WO2017018453A1 PCT/JP2016/072038 JP2016072038W WO2017018453A1 WO 2017018453 A1 WO2017018453 A1 WO 2017018453A1 JP 2016072038 W JP2016072038 W JP 2016072038W WO 2017018453 A1 WO2017018453 A1 WO 2017018453A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resin composition
- weight
- parts
- component
- support material
- Prior art date
Abstract
インクジェット光造形法によりモデル材(4)を造形するために使用されるモデル材用樹脂組成物であって、樹脂組成物全体100重量部に対して、19~49重量部の非水溶性単官能エチレン性不飽和単量体(A)と、15~50重量部の二官能以上の多官能エチレン性不飽和単量体(B)と、10~45重量部のオリゴマー(C)と、光重合開始剤(D)と、を含有する、モデル材用樹脂組成物。このモデル材用樹脂組成物によって、寸法精度が良好な光造形品を得ることができる。
Description
本発明は、インクジェット光造形法に用いられるモデル材用樹脂組成物およびサポート材用樹脂組成物、これらの樹脂組成物を用いて造形される光造形品、ならびに、該光造形品の製造方法に関する。
従来、立体造形物を作成する方法として、紫外線等を照射することにより硬化する光硬化性樹脂組成物を用いた造形法が広く知られている。具体的に、このような造形法では、光硬化性樹脂組成物に紫外線等を照射して硬化させることにより、所定の形状を有する硬化層を形成する。その後、該硬化層の上にさらに光硬化性樹脂組成物を供給して硬化させることにより、新たな硬化層を形成する。前記工程を繰り返し行うことにより、立体造形物を作製する。
前記造形法の中でも、近年、ノズルから光硬化性樹脂組成物を吐出させ、その直後に紫外線等を照射して硬化させることにより、所定の形状を有する硬化層を形成するインクジェット方式による光造形法(以下、インクジェット光造形法という)が報告されている(特開2004-255839号公報、特開2010-155889号公報、特開2010-155926号公報および特開2012-111226号公報)。インクジェット光造形法は、光硬化性樹脂組成物を貯留する大型の樹脂液槽および暗室の設置が不要である。そのため、従来法に比べて、造形装置を小型化することができる。インクジェット光造形法は、CAD(Computer Aided Design)データに基づいて、自由に立体造形物を作成可能な3Dプリンターによって実現される造形法として、注目されている。
インクジェット光造形法において、中空形状等の複雑な形状を有する光造形品を造形する場合には、モデル材を支えるために、該モデル材とサポート材とを組み合わせて形成する(特開2004-255839号公報、特開2010-155889号公報および特開2012-111226号公報)。サポート材は、モデル材と同様に、光硬化性樹脂組成物に紫外線等を照射して硬化させることにより作成される。モデル材を作成した後は、サポート材を、物理的に剥離する、または、有機溶媒もしくは水に溶解させることにより、前記サポート材を除去することができる。
さらに、特開2012-111226号公報には、インクジェット光造形法により、光硬化時および硬化後の水または吸湿による膨潤変形が極めて少ないモデル材用樹脂組成物、硬化後の硬化物が水への溶解性に優れ、除去が容易であるサポート材用樹脂組成物、ならびに、これらの樹脂組成物を用いて造形される光造形品が開示されている。
しかしながら、従来のモデル材用樹脂組成物およびサポート材用樹脂組成物を用いて造形される光造形品は、寸法精度が悪化するという問題があった。その原因としては、例えば、モデル材用樹脂組成物を光硬化させることにより得られるモデル材の硬化不足または硬化収縮の増大が考えられる。また、サポート材用樹脂組成物の非重合性成分の浸み出し、または、サポート材用樹脂組成物を光硬化させることにより得られるサポート材の自立性不足が考えられる。
本発明は、前記現状に鑑みてなされたものであり、寸法精度が良好な光造形品を得るためのモデル材用樹脂組成物およびサポート材用樹脂組成物、これらの樹脂組成物を用いて造形される光造形品、ならびに、該光造形品の製造方法を提供することを目的とする。
本発明者らは、前記課題について種々検討を行ったところ、モデル材用樹脂組成物中の非水溶性単官能エチレン性不飽和単量体の含有量を所定の範囲にすることにより、前記モデル材用樹脂組成物を光硬化させることにより得られるモデル材の硬化性が良好となり、かつ、硬化収縮が抑制されることを見出した。また、本発明者らは、サポート材用樹脂組成物中の非重合成分の含有量を減らすことにより、造形中の非重合成分の浸み出しが抑制できるとともに、水溶性単官能エチレン性不飽和単量体の含有量を増やすことにより、自立性に優れたサポート材が得られることを見出した。そして、本発明者らは、モデル材用樹脂組成物およびサポート材用樹脂組成物のいずれかによって課題を解決することにより、寸法精度が良好な光造形品が得られることを見出した。
本発明は、前記知見に基づいてなされたものであり、その要旨は、以下の通りである。
〔1〕インクジェット光造形法によりモデル材を造形するために使用されるモデル材用樹脂組成物であって、樹脂組成物全体100重量部に対して、19~49重量部の非水溶性単官能エチレン性不飽和単量体(A)と、15~50重量部の二官能以上の多官能エチレン性不飽和単量体(B)と、10~45重量部のオリゴマー(C)と、光重合開始剤(D)と、を含有する、モデル材用樹脂組成物。
〔2〕前記(A)成分の含有量は、樹脂組成物全体100重量部に対して、25~47重量部である、前記〔1〕に記載のモデル材用樹脂組成物。
〔3〕前記(B)成分の含有量は、樹脂組成物全体100重量部に対して、20~45重量部である、前記〔1〕または〔2〕に記載のモデル材用樹脂組成物。
〔4〕前記(C)成分は、ウレタン(メタ)アクリレートオリゴマー、エポキシ(メタ)アクリレートオリゴマー、および、ポリエステル(メタ)アクリレートオリゴマーから選択される1種以上である、前記〔1〕~〔3〕のいずれか一つに記載のモデル材用樹脂組成物。
〔5〕前記(C)成分の含有量は、樹脂組成物全体100重量部に対して、15~30重量部である、前記〔1〕~〔4〕のいずれか一つに記載のモデル材用樹脂組成物。
〔6〕前記(D)成分の含有量は、樹脂組成物全体100重量部に対して、3~15重量部である、前記〔1〕~〔5〕のいずれか一つに記載のモデル材用樹脂組成物。
〔7〕さらに、保存安定化剤(F)を、樹脂組成物全体100重量部に対して、0.05~3.0重量部含有する、前記〔1〕~〔6〕のいずれか一つに記載のモデル材用樹脂組成物。
〔8〕インクジェット光造形法によりサポート材を造形するために使用されるサポート材用樹脂組成物であって、樹脂組成物全体100重量部に対して、20~50重量部の水溶性単官能エチレン性不飽和単量体(G)と、20~49重量部のオキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコール(H)と、35重量部以下の水溶性有機溶剤(I)と、光重合開始剤(D)と、を含有する、サポート材用樹脂組成物。
〔9〕前記(G)成分の含有量は、樹脂組成物全体100重量部に対して、25~45重量部である、前記〔8〕に記載のサポート材用樹脂組成物。
〔10〕前記(H)成分の含有量は、樹脂組成物全体100重量部に対して、25~45重量部である、前記〔8〕または〔9〕に記載のサポート材用樹脂組成物。
〔11〕前記(D)成分の含有量は、樹脂組成物全体100重量部に対して、5~20重量部である、前記〔8〕~〔10〕のいずれか一つに記載のサポート材用樹脂組成物。
〔12〕前記(I)成分の含有量は、樹脂組成物全体100重量部に対して、5重量部以上である、前記〔8〕~〔11〕のいずれか一つに記載のサポート材用樹脂組成物。
〔13〕さらに、保存安定化剤(F)を、樹脂組成物全体100重量部に対して、0.05~3.0重量部含有する、前記〔8〕~〔12〕のいずれか一つに記載のサポート材用樹脂組成物。
〔14〕インクジェット光造形法により、前記〔1〕~〔7〕のいずれか一つに記載のモデル材用樹脂組成物を光硬化させることにより得られるモデル材を含む、光造形品。
〔15〕インクジェット光造形法により、前記〔14〕に記載の光造形品を製造する方法であって、前記〔1〕~〔7〕のいずれか一つに記載のモデル材用樹脂組成物を光硬化させることによりモデル材を得るとともに、前記〔8〕~〔13〕のいずれか一つに記載のサポート材用樹脂組成物を光硬化させることによりサポート材を得る工程(I)と、前記サポート材を除去する工程(II)とを有する、光造形品の製造方法。
〔16〕前記工程(I)では、紫外線LEDを用いて、前記モデル材用樹脂組成物および前記サポート材用樹脂組成物を光硬化させる、前記〔15〕に記載の光造形品の製造方法。
本発明によれば、寸法精度が良好な光造形品を得るためのモデル材用樹脂組成物およびサポート材用樹脂組成物、これらの樹脂組成物を用いて造形される光造形品、ならびに、該光造形品の製造方法を提供することができる。
以下、本発明の一実施形態(以下、本実施形態ともいう)について詳しく説明する。本発明は、以下の内容に限定されるものではない。なお、以下の説明において「(メタ)アクリレート」とは、アクリレートおよびメタクリレートの総称であり、アクリレートおよびメタクリレートの一方または両方を意味するものである。「(メタ)アクリロイル」、「(メタ)アクリル」についても同様である。
1.モデル材用樹脂組成物
本実施形態に係るモデル材用樹脂組成物は、樹脂組成物全体100重量部に対して、19~49重量部の非水溶性単官能エチレン性不飽和単量体(A)と、15~50重量部の二官能以上の多官能エチレン性不飽和単量体(B)と、10~45重量部のオリゴマー(C)と、光重合開始剤(D)と、を含有する。
本実施形態に係るモデル材用樹脂組成物は、樹脂組成物全体100重量部に対して、19~49重量部の非水溶性単官能エチレン性不飽和単量体(A)と、15~50重量部の二官能以上の多官能エチレン性不飽和単量体(B)と、10~45重量部のオリゴマー(C)と、光重合開始剤(D)と、を含有する。
<非水溶性単官能エチレン性不飽和単量体(A)>
非水溶性単官能エチレン性不飽和単量体(A)は、光照射により重合して、モデル材用樹脂組成物を硬化させる成分である。上記(A)成分の含有量は、樹脂組成物全体100重量部に対して、19~49重量部とする。上記(A)成分の含有量が19重量部未満であると、モデル材用樹脂組成物を光硬化させることにより得られるモデル材は、硬化収縮が大きくなる。その結果、前記モデル材の寸法精度が悪化する。一方、上記(A)成分の含有量が49重量部を超えると、前記モデル材には、硬化不足が生じる。その結果、前記モデル材の寸法精度が悪化する。上記(A)成分の含有量は、25重量部以上であることが好ましく、47重量部以下であることが好ましい。
非水溶性単官能エチレン性不飽和単量体(A)は、光照射により重合して、モデル材用樹脂組成物を硬化させる成分である。上記(A)成分の含有量は、樹脂組成物全体100重量部に対して、19~49重量部とする。上記(A)成分の含有量が19重量部未満であると、モデル材用樹脂組成物を光硬化させることにより得られるモデル材は、硬化収縮が大きくなる。その結果、前記モデル材の寸法精度が悪化する。一方、上記(A)成分の含有量が49重量部を超えると、前記モデル材には、硬化不足が生じる。その結果、前記モデル材の寸法精度が悪化する。上記(A)成分の含有量は、25重量部以上であることが好ましく、47重量部以下であることが好ましい。
上記(A)成分は、エネルギー線により硬化する特性を有する分子内にエチレン性二重結合を1個有する非水溶性の重合性モノマーである。上記(A)成分としては、例えば、炭素数4~30の直鎖または分岐のアルキル(メタ)アクリレート〔例えば、メチル(メタ)アクリレート、エチル(メタ)アクリレート、イソブチル(メタ)アクリレート、ラウリル(メタ)アクリレート、ステアリル(メタ)アクリレート、イソステアリル(メタ)アクリレート、t-ブチル(メタ)アクリレート等〕、炭素数6~20の脂環含有(メタ)アクリレート〔例えば、シクロヘキシル(メタ)アクリレート、4-t-シクロヘキシル(メタ)アクリレート、イソボルニル(メタ)アクリレート、フェノキシエチル(メタ)アクリレート、ジシクロペンタニル(メタ)アクリレート等〕、炭素数5~20の複素環含有(メタ)アクリレート〔例えば、テトラヒドロフルフリル(メタ)アクリレート、4-(メタ)アクリロイルオキシメチル-2-メチル-2-エチル-1,3-ジオキソラン、4-(メタ)アクリロイルオキシメチル-2-シクロヘキシル-1,3-ジオキソラン、アダマンチル(メタ)アクリレート等〕等が挙げられる。これらは単独で用いてもよいし、2種以上を併用してもよい。なお、上記(A)成分が2種以上含まれる場合、上記含有量は、各(A)成分の含有量の合計である。
これらの中でも、モデル材用樹脂組成物の硬化性を向上させる観点から、イソボルニル(メタ)アクリレート、フェノキシエチル(メタ)アクリレート、および、テトラヒドロフルフリル(メタ)アクリレートから選択される1種以上であることが好ましい。さらに、モデル材用樹脂組成物が光硬化時の温度(50~90℃)に耐え得る耐熱性を有することにより、前記モデル材の寸法精度を向上させる観点から、イソボルニル(メタ)アクリレートであることがより好ましい。
<二官能以上の多官能エチレン性不飽和単量体(B)>
二官能以上の多官能エチレン性不飽和単量体(B)は、光照射により重合して、モデル材用樹脂組成物を硬化させる成分である。上記(B)成分の含有量は、樹脂組成物全体100重量部に対して、15~50重量部とする。上記(B)成分の含有量が15重量部未満であると、前記モデル材には、硬化不足が生じる。その結果、前記モデル材の寸法精度が悪化する。一方、上記(B)成分の含有量が50重量部を超えると、前記モデル材は、硬化収縮が大きくなる。その結果、前記モデル材の寸法精度が悪化する。上記(B)成分の含有量は、20重量部以上であることが好ましく、45重量部以下であることが好ましい。
二官能以上の多官能エチレン性不飽和単量体(B)は、光照射により重合して、モデル材用樹脂組成物を硬化させる成分である。上記(B)成分の含有量は、樹脂組成物全体100重量部に対して、15~50重量部とする。上記(B)成分の含有量が15重量部未満であると、前記モデル材には、硬化不足が生じる。その結果、前記モデル材の寸法精度が悪化する。一方、上記(B)成分の含有量が50重量部を超えると、前記モデル材は、硬化収縮が大きくなる。その結果、前記モデル材の寸法精度が悪化する。上記(B)成分の含有量は、20重量部以上であることが好ましく、45重量部以下であることが好ましい。
上記(B)成分は、エネルギー線により硬化する特性を有する分子内にエチレン性二重結合を2個以上有する重合性モノマーである。上記(B)成分としては、例えば、炭素数10~25の直鎖または分岐のアルキレングリコールジ(メタ)アクリレートまたはアルキレングリコールトリ(メタ)アクリレート〔例えば、トリプロピレングリコールジ(メタ)アクリレート、1,6-ヘキサンジオールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、1,9-ノナンジオールジ(メタ)アクリレート、3-メチル-1,5-ペンタンジオールジ(メタ)アクリレート、2-n-ブチル-2-エチル-1,3-プロパンジオールジ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート等〕、炭素数10~30の脂環含有ジ(メタ)アクリレート〔例えば、ジメチロールトリシクロデカンジ(メタ)アクリレート等〕等が挙げられる。これらは単独で用いてもよいし、2種以上を併用してもよい。なお、上記(B)成分が2種以上含まれる場合、上記含有量は、各(B)成分の含有量の合計である。
これらの中でも、モデル材用樹脂組成物の硬化性を向上させる観点から、トリプロピレングリコールジ(メタ)アクリレート、1,6-ヘキサンジオールジ(メタ)アクリレート、および、ペンタエリスリトールトリ(メタ)アクリレートから選択される1種以上であることが好ましい。さらに、モデル材用樹脂組成物が光硬化時の温度(50~90℃)に耐え得る耐熱性を有することにより、前記モデル材の寸法精度を向上させる観点から、1,6-ヘキサンジオールジ(メタ)アクリレート、または、ペンタエリスリトールトリ(メタ)アクリレートであることがより好ましい。
<オリゴマー(C)>
オリゴマー(C)は、光照射により重合してモデル材用樹脂組成物を硬化させ、かつ、該硬化により得られるモデル材の破断強度を高める成分である。上記(C)成分の含有量は、樹脂組成物全体100重量部に対して、10~45重量部とする。上記(C)成分の含有量が10重量部未満であると、前記モデル材は、硬化収縮がやや大きくなる。その結果、前記モデル材の寸法精度が悪化する可能性がある。また、前記モデル材の破断強度が劣る。一方、上記(C)成分の含有量が45重量部を超えると、モデル材用樹脂組成物の粘度が高くなる。そのため、前記モデル材用樹脂組成物をインクジェットヘッドから吐出させる際、ジェッティング特性が悪化して、飛行曲がりを起こす可能性がある。その結果、前記モデル材の寸法精度が悪化する可能性がある。上記(C)成分の含有量は、15重量部以上であることが好ましく、30重量部以下であることが好ましい。
オリゴマー(C)は、光照射により重合してモデル材用樹脂組成物を硬化させ、かつ、該硬化により得られるモデル材の破断強度を高める成分である。上記(C)成分の含有量は、樹脂組成物全体100重量部に対して、10~45重量部とする。上記(C)成分の含有量が10重量部未満であると、前記モデル材は、硬化収縮がやや大きくなる。その結果、前記モデル材の寸法精度が悪化する可能性がある。また、前記モデル材の破断強度が劣る。一方、上記(C)成分の含有量が45重量部を超えると、モデル材用樹脂組成物の粘度が高くなる。そのため、前記モデル材用樹脂組成物をインクジェットヘッドから吐出させる際、ジェッティング特性が悪化して、飛行曲がりを起こす可能性がある。その結果、前記モデル材の寸法精度が悪化する可能性がある。上記(C)成分の含有量は、15重量部以上であることが好ましく、30重量部以下であることが好ましい。
上記(C)成分としては、例えば、ウレタン(メタ)アクリレートオリゴマー、エポキシ(メタ)アクリレートオリゴマー、ポリエステル(メタ)アクリレートオリゴマー、ポリエーテル(メタ)アクリレートオリゴマー等が挙げられる。これらは単独で用いてもよいし、2種以上を併用してもよい。これらの中でも、モデル材用樹脂組成物の硬化性を向上させる観点から、ウレタン(メタ)アクリレートオリゴマー、エポキシ(メタ)アクリレートオリゴマー、および、ポリエステル(メタ)アクリレートオリゴマーから選択される1種以上であることが好ましい。さらに、モデル材用樹脂組成物が光硬化時の温度(50~90℃)に耐え得る耐熱性を有することにより、前記モデル材の寸法精度を向上させる観点から、ウレタン(メタ)アクリレートオリゴマーであることがより好ましい。
また、ウレタン(メタ)アクリレートオリゴマー、エポキシ(メタ)アクリレートオリゴマー、ポリエステル(メタ)アクリレートオリゴマー、および、ポリエーテル(メタ)アクリレートオリゴマーの中でも、二官能以上の多官能オリゴマーであることが好ましく、二官能のオリゴマーであることがより好ましい。
なお、上記(C)成分が2種以上含まれる場合、上記含有量は、各(C)成分の含有量の合計である。
ここで、本明細書中において「オリゴマー」は、重量平均分子量が800~10000である。重量平均分子量は、GPC(Gel Permeation Chromatography)で測定したポリスチレン換算の重量平均分子量を意味する。
<光重合開始剤(D)>
光重合開始剤(D)は、紫外線、近紫外線または可視光領域の波長の光を照射するとラジカル反応を促進する化合物であれば、特に限定されない。上記(D)成分としては、例えば、炭素数14~18のベンゾイン化合物〔例えば、ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインプロピルエーテル、ベンゾインイソブチルエーテル等〕、炭素数8~18のアセトフェノン化合物〔例えば、アセトフェノン、2,2-ジエトキシ-2-フェニルアセトフェノン、2,2-ジエトキシ-2-フェニルアセトフェノン、1,1-ジクロロアセトフェノン、2-ヒドロキシ-2-メチル-フェニルプロパン-1-オン、ジエトキシアセトフェノン、1-ヒドロキシシクロヘキシルフェニルケトン、2-メチル-1-[4-(メチルチオ)フェニル]-2-モルホリノプロパン-1-オン等〕、炭素数14~19のアントラキノン化合物〔例えば、2-エチルアントラキノン、2-t-ブチルアントラキノン、2-クロロアントラキノン、2-アミルアントラキノン等〕、炭素数13~17のチオキサントン化合物〔例えば、2,4-ジエチルチオキサントン、2-イソプロピルチオキサントン、2-クロロチオキサントン等〕、炭素数16~17のケタール化合物〔例えば、アセトフェノンジメチルケタール、ベンジルジメチルケタール等〕、炭素数13~21のベンゾフェノン化合物〔例えば、ベンゾフェノン、4-ベンゾイル-4’-メチルジフェニルサルファイド、4,4’-ビスメチルアミノベンゾフェノン等〕、炭素数22~28のアシルフォスフィンオキサイド化合物〔例えば、2,4,6-トリメチルベンゾイル-ジフェニル-フォスフィンオキサイド、ビス-(2、6-ジメトキシベンゾイル)-2,4,4-トリメチルペンチルフォスフィンオキサイド、ビス(2,4,6-トリメチルベンゾイル)-フェニルフォスフィンオキサイド〕、これらの化合物の混合物等が挙げられる。これらは単独で用いてもよいし、2種以上を併用してもよい。これらの中でも、モデル材用樹脂組成物を光硬化させることにより得られるモデル材が黄変しにくいという耐光性の観点から、2,4,6-トリメチルベンゾイル-ジフェニル-フォスフィンオキサイドであることが好ましい。また、入手可能なアシルフォスフィンオキサイド化合物としては、例えば、BASF社製のDAROCURE TPO等が挙げられる。
光重合開始剤(D)は、紫外線、近紫外線または可視光領域の波長の光を照射するとラジカル反応を促進する化合物であれば、特に限定されない。上記(D)成分としては、例えば、炭素数14~18のベンゾイン化合物〔例えば、ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインプロピルエーテル、ベンゾインイソブチルエーテル等〕、炭素数8~18のアセトフェノン化合物〔例えば、アセトフェノン、2,2-ジエトキシ-2-フェニルアセトフェノン、2,2-ジエトキシ-2-フェニルアセトフェノン、1,1-ジクロロアセトフェノン、2-ヒドロキシ-2-メチル-フェニルプロパン-1-オン、ジエトキシアセトフェノン、1-ヒドロキシシクロヘキシルフェニルケトン、2-メチル-1-[4-(メチルチオ)フェニル]-2-モルホリノプロパン-1-オン等〕、炭素数14~19のアントラキノン化合物〔例えば、2-エチルアントラキノン、2-t-ブチルアントラキノン、2-クロロアントラキノン、2-アミルアントラキノン等〕、炭素数13~17のチオキサントン化合物〔例えば、2,4-ジエチルチオキサントン、2-イソプロピルチオキサントン、2-クロロチオキサントン等〕、炭素数16~17のケタール化合物〔例えば、アセトフェノンジメチルケタール、ベンジルジメチルケタール等〕、炭素数13~21のベンゾフェノン化合物〔例えば、ベンゾフェノン、4-ベンゾイル-4’-メチルジフェニルサルファイド、4,4’-ビスメチルアミノベンゾフェノン等〕、炭素数22~28のアシルフォスフィンオキサイド化合物〔例えば、2,4,6-トリメチルベンゾイル-ジフェニル-フォスフィンオキサイド、ビス-(2、6-ジメトキシベンゾイル)-2,4,4-トリメチルペンチルフォスフィンオキサイド、ビス(2,4,6-トリメチルベンゾイル)-フェニルフォスフィンオキサイド〕、これらの化合物の混合物等が挙げられる。これらは単独で用いてもよいし、2種以上を併用してもよい。これらの中でも、モデル材用樹脂組成物を光硬化させることにより得られるモデル材が黄変しにくいという耐光性の観点から、2,4,6-トリメチルベンゾイル-ジフェニル-フォスフィンオキサイドであることが好ましい。また、入手可能なアシルフォスフィンオキサイド化合物としては、例えば、BASF社製のDAROCURE TPO等が挙げられる。
上記(D)成分の含有量は、樹脂組成物全体100重量部に対して、3~15重量部であることが好ましい。上記(D)成分の含有量が上記範囲であると、モデル材用樹脂組成物の硬化性が良好となり、モデル材の寸法精度が向上する。上記(D)成分の含有量は、5重量部以上であることがより好ましく、13重量部以下であることがより好ましい。なお、上記(D)成分が2種以上含まれる場合、上記含有量は、各(D)成分の含有量の合計である。
<表面調整剤(E)>
表面調整剤(E)は、樹脂組成物の表面張力を適切な範囲に調整するために含有させてもよい。樹脂組成物の表面張力を適切な範囲に調整することにより、モデル材用樹脂組成物とサポート材用樹脂組成物とが界面で混ざり合うことを抑制することができる。その結果、これらの樹脂組成物を用いて、寸法精度が良好な光造形品を得ることができる。この効果を得るため、上記(E)成分の含有量は、樹脂組成物全体100重量部に対して、0.005~3.0重量部であることが好ましい。
表面調整剤(E)は、樹脂組成物の表面張力を適切な範囲に調整するために含有させてもよい。樹脂組成物の表面張力を適切な範囲に調整することにより、モデル材用樹脂組成物とサポート材用樹脂組成物とが界面で混ざり合うことを抑制することができる。その結果、これらの樹脂組成物を用いて、寸法精度が良好な光造形品を得ることができる。この効果を得るため、上記(E)成分の含有量は、樹脂組成物全体100重量部に対して、0.005~3.0重量部であることが好ましい。
上記(E)成分としては、例えば、シリコーン系化合物等が挙げられる。シリコーン系化合物としては、例えば、ポリジメチルシロキサン構造を有するシリコーン系化合物等が挙げられる。具体的には、ポリエーテル変性ポリジメチルシロキサン、ポリエステル変性ポリジメチルシロキサン、ポリアラルキル変性ポリジメチルシロキサン等が挙げられる。これらとして、商品名でBYK-300、BYK-302、BYK-306、BYK-307、BYK-310、BYK-315、BYK-320、BYK-322、BYK-323、BYK-325、BYK-330、BYK-331、BYK-333、BYK-337、BYK-344、BYK-370、BYK-375、BYK-377、BYK-UV3500、BYK-UV3510、BYK-UV3570(以上、ビックケミー社製)、TEGO-Rad2100、TEGO-Rad2200N、TEGO-Rad2250、TEGO-Rad2300、TEGO-Rad2500、TEGO-Rad2600、TEGO-Rad2700(以上、デグサ社製)、グラノール100、グラノール115、グラノール400、グラノール410、グラノール435、グラノール440、グラノール450、B-1484、ポリフローATF-2、KL-600、UCR-L72、UCR-L93(共栄社化学社製)等を用いてもよい。これらは単独で用いてもよいし、2種以上を併用してもよい。なお、上記(E)成分が2種以上含まれる場合、上記含有量は、各(E)成分の含有量の合計である。
<保存安定化剤(F)>
本実施形態に係るモデル材用樹脂組成物は、さらに、保存安定化剤(F)を含有することが好ましい。保存安定化剤(F)は、樹脂組成物の保存安定性を高めることができる。また、熱エネルギーにより重合性化合物が重合することで生じるヘッド詰まりを防止することができる。これらの効果を得るため、上記(F)成分の含有量は、樹脂組成物全体100重量部に対して、0.05~3.0重量部であることが好ましい。
本実施形態に係るモデル材用樹脂組成物は、さらに、保存安定化剤(F)を含有することが好ましい。保存安定化剤(F)は、樹脂組成物の保存安定性を高めることができる。また、熱エネルギーにより重合性化合物が重合することで生じるヘッド詰まりを防止することができる。これらの効果を得るため、上記(F)成分の含有量は、樹脂組成物全体100重量部に対して、0.05~3.0重量部であることが好ましい。
上記(F)成分としては、例えば、ヒンダードアミン系化合物(HALS)、フェノール系酸化防止剤、リン系酸化防止剤等が挙げられる。具体的には、ハイドロキノン、メトキノン、ベンゾキノン、p-メトキシフェノール、ハイドロキノンモノメチルエーテル、ハイドロキノンモノブチルエーテル、TEMPO、4-ヒドロキシ-TEMPO、TEMPOL、クペロンAl、IRGASTAB UV-10、IRGASTAB UV-22、FIRSTCURE ST-1(ALBEMARLE社製)、t-ブチルカテコール、ピロガロール、BASF社製のTINUVIN 111 FDL、TINUVIN 144、TINUVIN 292、TINUVIN XP40、TINUVIN XP60、TINUVIN 400等が挙げられる。これらは単独で用いてもよいし、2種以上を併用してもよい。なお、上記(F)成分が2種以上含まれる場合、上記含有量は、各(F)成分の含有量の合計である。
<水溶性単官能エチレン性不飽和単量体(G)>
本実施形態に係るモデル材用樹脂組成物は、水溶性単官能エチレン性不飽和単量体(G)を含有しないことが好ましい。モデル材用樹脂組成物が上記(G)成分を含むと、光硬化時および硬化後の水または吸湿により、前記モデル材の膨潤変形が起こる場合がある。その結果、前記モデル材の寸法精度が悪化する可能性がある。上記(G)成分の詳細については後述する。
本実施形態に係るモデル材用樹脂組成物は、水溶性単官能エチレン性不飽和単量体(G)を含有しないことが好ましい。モデル材用樹脂組成物が上記(G)成分を含むと、光硬化時および硬化後の水または吸湿により、前記モデル材の膨潤変形が起こる場合がある。その結果、前記モデル材の寸法精度が悪化する可能性がある。上記(G)成分の詳細については後述する。
モデル材用樹脂組成物には、本発明の効果を阻害しない範囲で、必要により、その他の添加剤を含有させることができる。その他の添加剤としては、例えば、酸化防止剤、着色剤、紫外線吸収剤、光安定剤、重合禁止剤、連鎖移動剤、充填剤等が挙げられる。
本実施形態に係るモデル材用樹脂組成物は、特に限定されるものではないが、例えば、上記(A)~(D)成分、および、必要により、上記(E)~(G)成分、その他の添加剤を、混合攪拌装置等を用いて均一に混合することにより、製造することができる。
このようにして製造された本実施形態に係るモデル材用樹脂組成物は、インクジェットヘッドからの吐出性を良好にする観点から、25℃における粘度が、70mPa・s以下であることが好ましい。なお、モデル材用樹脂組成物の粘度の測定は、JIS Z 8803に準拠し、R100型粘度計を用いて行われる。
2.サポート材用樹脂組成物
本実施形態に係るサポート材用樹脂組成物は、樹脂組成物全体100重量部に対して、20~50重量部の水溶性単官能エチレン性不飽和単量体(G)と、20~49重量部のオキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコール(H)と、35重量部以下の水溶性有機溶剤(I)と、光重合開始剤(D)と、を含有する。
本実施形態に係るサポート材用樹脂組成物は、樹脂組成物全体100重量部に対して、20~50重量部の水溶性単官能エチレン性不飽和単量体(G)と、20~49重量部のオキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコール(H)と、35重量部以下の水溶性有機溶剤(I)と、光重合開始剤(D)と、を含有する。
<水溶性単官能エチレン性不飽和単量体(G)>
水溶性単官能エチレン性不飽和単量体(G)は、光照射により重合して、サポート材用樹脂組成物を硬化させる成分である。また、サポート材用樹脂組成物を光硬化させることにより得られるサポート材をすばやく水に溶解させる成分である。上記(G)成分の含有量は、樹脂組成物全体100重量部に対して、20~50重量部とする。上記(G)成分の含有量が20重量部未満であると、前記サポート材における自立性が充分ではない。そのため、該サポート材をモデル材の下層に配置した際、前記モデル材を充分に支えることができない。その結果、前記モデル材の寸法精度が悪化する。一方、上記(G)成分の含有量が50重量部を超えると、前記サポート材は、水への溶解性が劣る。前記サポート材を完全に除去するまでの水への浸漬時間が長くなると、モデル材がわずかに膨張する。その結果、前記モデル材の微細構造部分において、寸法精度が悪化する場合がある。上記(G)成分の含有量は、25重量部以上であることが好ましく、45重量部以下であることが好ましい。
水溶性単官能エチレン性不飽和単量体(G)は、光照射により重合して、サポート材用樹脂組成物を硬化させる成分である。また、サポート材用樹脂組成物を光硬化させることにより得られるサポート材をすばやく水に溶解させる成分である。上記(G)成分の含有量は、樹脂組成物全体100重量部に対して、20~50重量部とする。上記(G)成分の含有量が20重量部未満であると、前記サポート材における自立性が充分ではない。そのため、該サポート材をモデル材の下層に配置した際、前記モデル材を充分に支えることができない。その結果、前記モデル材の寸法精度が悪化する。一方、上記(G)成分の含有量が50重量部を超えると、前記サポート材は、水への溶解性が劣る。前記サポート材を完全に除去するまでの水への浸漬時間が長くなると、モデル材がわずかに膨張する。その結果、前記モデル材の微細構造部分において、寸法精度が悪化する場合がある。上記(G)成分の含有量は、25重量部以上であることが好ましく、45重量部以下であることが好ましい。
上記(G)成分は、エネルギー線により硬化する特性を有する分子内にエチレン性二重結合を1個有する水溶性の重合性モノマーである。上記(G)成分としては、例えば、炭素数5~15の水酸基含有(メタ)アクリレート〔例えば、ヒドロキシエチル(メタ)アクリレート、ヒドロキシプロピル(メタ)アクリレート、4-ヒドロキシブチル(メタ)アクリレート等〕、Mn200~1,000の水酸基含有(メタ)アクリレート〔ポリエチレングリコールモノ(メタ)アクリレート、モノアルコキシ(炭素数1~4)ポリエチレングリコールモノ(メタ)アクリレート、ポリプロピレングリコールモノ(メタ)アクリレート、モノアルコキシ(炭素数1~4)ポリプロピレングリコールモノ(メタ)アクリレート、PEG-PPGブロックポリマーのモノ(メタ)アクリレート等〕、炭素数3~15の(メタ)アクリルアミド誘導体〔(メタ)アクリルアミド、N-メチル(メタ)アクリルアミド、N-エチル(メタ)アクリルアミド、N-プロピル(メタ)アクリルアミド、N-ブチル(メタ)アクリルアミド、N,N’-ジメチル(メタ)アクリルアミド、N,N’-ジエチル(メタ)アクリルアミド、N-ヒドロキシエチル(メタ)アクリルアミド、N-ヒドロキシプロピル(メタ)アクリルアミド、N-ヒドロキシブチル(メタ)アクリルアミド等〕、(メタ)アクリロイルモルフォリン等が挙げられる。これらは単独で用いてもよいし、2種以上を併用してもよい。なお、上記(G)成分が2種以上含まれる場合、上記含有量は、各(G)成分の含有量の合計である。
これらの中でも、サポート材用樹脂組成物の硬化性を向上させる観点から、N,N’-ジメチル(メタ)アクリルアミド、N-ヒドロキシエチル(メタ)アクリルアミド、(メタ)アクリロイルモルフォリン等であることが好ましい。さらに、人体への皮膚低刺激性の観点から、N-ヒドロキシエチル(メタ)アクリルアミド、(メタ)アクリロイルモルフォリンであることがより好ましい。
<オキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコール(H)>
オキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコール(H)は、前記サポート材の水への溶解性を高めることができる。上記(H)成分の含有量は、樹脂組成物全体100重量部に対して、20~49重量部とする。上記(H)成分の含有量が20重量部未満であると、前記サポート材は、水への溶解性が劣る。サポート材を完全に除去するまでの水への浸漬時間が長くなると、モデル材がわずかに膨張する。その結果、前記モデル材の微細構造部分において、寸法精度が悪化する場合がある。一方、上記(H)成分の含有量が49重量部を超えると、サポート材用樹脂組成物を光硬化させる際、上記(H)成分の浸み出しが生じる場合がある。上記(H)成分の浸み出しが生じると、サポート材とモデル材との界面における密着性が悪くなる。その結果、前記モデル材は、硬化収縮する際に前記サポート材から剥がれやすくなり、寸法精度が悪化する場合がある。また、上記(H)成分の含有量が49重量部を超えると、サポート材用樹脂組成物の粘度が高くなる。そのため、前記サポート材用樹脂組成物をインクジェットヘッドから吐出させる際、ジェッティング特性が悪化して、飛行曲がりを起こす可能性がある。その結果、前記サポート材の寸法精度が悪化する。よって、該サポート材の上層に成形されたモデル材の寸法精度も悪化する。上記(H)成分の含有量は、25重量部以上であることが好ましく、45重量部以下であることが好ましい。
オキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコール(H)は、前記サポート材の水への溶解性を高めることができる。上記(H)成分の含有量は、樹脂組成物全体100重量部に対して、20~49重量部とする。上記(H)成分の含有量が20重量部未満であると、前記サポート材は、水への溶解性が劣る。サポート材を完全に除去するまでの水への浸漬時間が長くなると、モデル材がわずかに膨張する。その結果、前記モデル材の微細構造部分において、寸法精度が悪化する場合がある。一方、上記(H)成分の含有量が49重量部を超えると、サポート材用樹脂組成物を光硬化させる際、上記(H)成分の浸み出しが生じる場合がある。上記(H)成分の浸み出しが生じると、サポート材とモデル材との界面における密着性が悪くなる。その結果、前記モデル材は、硬化収縮する際に前記サポート材から剥がれやすくなり、寸法精度が悪化する場合がある。また、上記(H)成分の含有量が49重量部を超えると、サポート材用樹脂組成物の粘度が高くなる。そのため、前記サポート材用樹脂組成物をインクジェットヘッドから吐出させる際、ジェッティング特性が悪化して、飛行曲がりを起こす可能性がある。その結果、前記サポート材の寸法精度が悪化する。よって、該サポート材の上層に成形されたモデル材の寸法精度も悪化する。上記(H)成分の含有量は、25重量部以上であることが好ましく、45重量部以下であることが好ましい。
上記(H)成分とは、活性水素化合物に少なくともエチレンオキサイドおよび/またはプロピレンオキサイドが付加したものである。上記(H)成分としては、例えば、ポリエチレングリコール、ポリプロピレングリコール等が挙げられる。これらは単独で用いてもよいし、2種以上を併用してもよい。活性水素化合物としては、1~4価アルコール、アミン化合物等が挙げられる。これらの中でも、2価アルコールまたは水であることが好ましい。なお、上記(H)成分が2種以上含まれる場合、上記含有量は、各(H)成分の含有量の合計である。
上記(H)成分の数平均分子量Mnは、100~5,000であることが好ましい。上記(H)成分のMnが上記範囲内であると、光硬化前の上記(G)成分と相溶し、かつ、光硬化後の上記(G)成分と相溶しない。その結果、前記サポート材の自立性を高め、かつ、該サポート材の水への溶解性を高めることができる。上記(H)成分のMnは、200~3,000であることがより好ましく、400~2,000であることがさらに好ましい。
<水溶性有機溶剤(I)>
水溶性有機溶剤(I)は、前記サポート材の水への溶解性を向上させる成分である。また、サポート材用樹脂組成物を低粘度に調整する成分である。上記(I)成分の含有量は、樹脂組成物全体100重量部に対して、35重量部以下とする。上記(I)成分の含有量が35重量部を超えると、前記サポート材用樹脂組成物を光硬化させる際、上記(I)成分の浸み出しが生じる。そのため、該サポート材の上層に成形されたモデル材は、寸法精度が悪化する。上記(I)成分の含有量は、前記サポート材の水への溶解性を向上させ、かつ、前記サポート材用樹脂組成物を低粘度に調整する観点から、5重量部以上であることが好ましく、10重量部以上であることがより好ましい。また、上記(I)成分の含有量は、30重量部以下であることが好ましい。
水溶性有機溶剤(I)は、前記サポート材の水への溶解性を向上させる成分である。また、サポート材用樹脂組成物を低粘度に調整する成分である。上記(I)成分の含有量は、樹脂組成物全体100重量部に対して、35重量部以下とする。上記(I)成分の含有量が35重量部を超えると、前記サポート材用樹脂組成物を光硬化させる際、上記(I)成分の浸み出しが生じる。そのため、該サポート材の上層に成形されたモデル材は、寸法精度が悪化する。上記(I)成分の含有量は、前記サポート材の水への溶解性を向上させ、かつ、前記サポート材用樹脂組成物を低粘度に調整する観点から、5重量部以上であることが好ましく、10重量部以上であることがより好ましい。また、上記(I)成分の含有量は、30重量部以下であることが好ましい。
上記(I)成分としては、例えば、エチレングリコールモノアセテート、プロピレングリコールモノアセテート、ジエチレングリコールモノアセテート、ジプロピレングリコールモノアセテート、トリエチレングリコールモノアセテート、トリプロピレングリコールモノアセテート、テトラエチレングリコールモノアセテート、テトラプロピレングリコールモノアセテート、エチレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテル、ジエチレングリコールモノメチルエーテル、ジプロピレングリコールモノメチルエーテル、トリエチレングリコールモノメチルエーテル、トリプロピレングリコールモノメチルエーテル、テトラエチレングリコールモノメチルエーテル、テトラプロピレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、プロピレングリコールモノエチルエーテル、ジエチレングリコールモノエチルエーテル、ジプロピレングリコールモノエチルエーテル、トリエチレングリコールモノエチルエーテル、トリプロピレングリコールモノエチルエーテル、テトラエチレングリコールモノエチルエーテル、テトラプロピレングリコールモノエチルエーテル、エチレングリコールモノプロピルエーテル、プロピレングリコールモノプロピルエーテル、ジエチレングリコールモノプロピルエーテル、ジプロピレングリコールモノプロピルエーテル、トリエチレングリコールモノプロピルエーテル、トリプロピレングリコールモノプロピルエーテル、テトラエチレングリコールモノプロピルエーテル、テトラプロピレングリコールモノプロピルエーテル、エチレングリコールモノブチルエーテル、プロピレングリコールモノブチルエーテル、ジエチレングリコールモノブチルエーテル、ジプロピレングリコールモノブチルエーテル、トリエチレングリコールモノブチルエーテル、トリプロピレングリコールモノブチルエーテル、テトラエチレングリコールモノブチルエーテル、テトラプロピレングリコールモノブチルエーテル、エチレングリコールジアセテート、プロピレングリコールジアセテート、ジエチレングリコールジアセテート、ジプロピレングリコールジアセテート、トリエチレングリコールジアセテート、トリプロピレングリコールジアセテート、テトラエチレングリコールジアセテート、テトラプロピレングリコールジアセテート、エチレングリコールジメチルエーテル、プロピレングリコールジメチルエーテル、ジエチレングリコールジメチルエーテル、ジプロピレングリコールジメチルエーテル、トリエチレングリコールジメチルエーテル、トリプロピレングリコールジメチルエーテル、テトラエチレングリコールジメチルエーテル、テトラプロピレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、プロピレングリコールジエチルエーテル、ジエチレングリコールジエチルエーテル、ジプロピレングリコールジエチルエーテル、トリエチレングリコールジエチルエーテル、トリプロピレングリコールジエチルエーテル、テトラエチレングリコールジエチルエーテル、テトラプロピレングリコールジエチルエーテル、エチレングリコールジプロピルエーテル、プロピレングリコールジプロピルエーテル、ジエチレングリコールジプロピルエーテル、ジプロピレングリコールジプロピルエーテル、トリエチレングリコールジプロピルエーテル、トリプロピレングリコールジプロピルエーテル、テトラエチレングリコールジプロピルエーテル、テトラプロピレングリコールジプロピルエーテル、エチレングリコールジブチルエーテル、プロピレングリコールジブチルエーテル、ジエチレングリコールジブチルエーテル、ジプロピレングリコールジブチルエーテル、トリエチレングリコールジブチルエーテル、トリプロピレングリコールジブチルエーテル、テトラエチレングリコールジブチルエーテル、テトラプロピレングリコールジブチルエーテル、エチレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート、ジエチレングリコールモノメチルエーテルアセテート、ジプロピレングリコールモノメチルエーテルアセテート、トリエチレングリコールモノメチルエーテルアセテート、トリプロピレングリコールモノメチルエーテルアセテート、テトラエチレングリコールモノメチルエーテルアセテート、テトラプロピレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート、ジプロピレングリコールモノエチルエーテルアセテート、トリエチレングリコールモノエチルエーテルアセテート、トリプロピレングリコールモノエチルエーテルアセテート、テトラエチレングリコールモノエチルエーテルアセテート、テトラプロピレングリコールモノエチルエーテルアセテート、エチレングリコールモノプロピルエーテルアセテート、プロピレングリコールモノプロピルエーテルアセテート、ジエチレングリコールモノプロピルエーテルアセテート、ジプロピレングリコールモノプロピルエーテルアセテート、トリエチレングリコールモノプロピルエーテルアセテート、トリプロピレングリコールモノプロピルエーテルアセテート、テトラエチレングリコールモノプロピルエーテルアセテート、テトラプロピレングリコールモノプロピルエーテルアセテート、エチレングリコールモノブチルエーテルアセテート、プロピレングリコールモノブチルエーテルアセテート、ジエチレングリコールモノブチルエーテルアセテート、ジプロピレングリコールモノブチルエーテルアセテート、トリエチレングリコールモノブチルエーテルアセテート、トリプロピレングリコールモノブチルエーテルアセテート、テトラエチレングリコールモノブチルエーテルアセテート、テトラプロピレングリコールモノブチルエーテルアセテート等が挙げられる。これらは単独で用いてもよいし、2種以上を併用してもよい。これらの中でも、サポート材の水への溶解性を向上させ、かつ、サポート材用樹脂組成物を低粘度に調整する観点から、トリエチレングリコールモノメチルエーテル、または、ジプロピレングリコールモノメチルエーテルアセテートであることがより好ましい。なお、上記(I)成分が2種以上含まれる場合、上記含有量は、各(I)成分の含有量の合計である。
<光重合開始剤(D)>
光重合開始剤(D)としては、本実施形態に係るモデル材用樹脂組成物と同様の成分を用いることができる。上記(D)成分の含有量は、樹脂組成物全体100重量部に対して、5~20重量部であることが好ましい。上記(D)成分の含有量が上記範囲であると、サポート材用樹脂組成物の自立性が良好となる。そのため、該サポート材の上層に成形されたモデル材は、寸法精度が向上する。上記(D)成分の含有量は、7重量部以上であることがより好ましく、18重量部以下であることがより好ましい。なお、上記(D)成分が2種以上含まれる場合、上記含有量は、各(D)成分の含有量の合計である。
光重合開始剤(D)としては、本実施形態に係るモデル材用樹脂組成物と同様の成分を用いることができる。上記(D)成分の含有量は、樹脂組成物全体100重量部に対して、5~20重量部であることが好ましい。上記(D)成分の含有量が上記範囲であると、サポート材用樹脂組成物の自立性が良好となる。そのため、該サポート材の上層に成形されたモデル材は、寸法精度が向上する。上記(D)成分の含有量は、7重量部以上であることがより好ましく、18重量部以下であることがより好ましい。なお、上記(D)成分が2種以上含まれる場合、上記含有量は、各(D)成分の含有量の合計である。
<表面調整剤(E)>
表面調整剤(E)は、本実施形態に係るモデル材用樹脂組成物と同様の成分を同様の含有量で用いることができる。
表面調整剤(E)は、本実施形態に係るモデル材用樹脂組成物と同様の成分を同様の含有量で用いることができる。
<保存安定化剤(F)>
本実施形態に係るサポート材用樹脂組成物は、さらに、保存安定化剤(F)を含有することが好ましい。保存安定化剤(F)は、本実施形態に係るモデル材用樹脂組成物と同様の成分を同様の含有量で用いることができる。
本実施形態に係るサポート材用樹脂組成物は、さらに、保存安定化剤(F)を含有することが好ましい。保存安定化剤(F)は、本実施形態に係るモデル材用樹脂組成物と同様の成分を同様の含有量で用いることができる。
サポート材用樹脂組成物には、本発明の効果を阻害しない範囲で、必要により、その他の添加剤を含有させることができる。その他の添加剤としては、例えば、酸化防止剤、着色剤、紫外線吸収剤、光安定剤、重合禁止剤、連鎖移動剤、充填剤等が挙げられる。
本実施形態に係るサポート材用樹脂組成物の製造方法は、特に限定されるものではない。例えば、上記(D)、(G)~(I)成分、および、必要により、上記(E)、(F)成分、その他の添加剤を、混合攪拌装置等を用いて均一に混合することにより、製造することができる。
このようにして製造された本実施形態に係るサポート材用樹脂組成物は、インクジェットヘッドからの吐出性を良好にする観点から、25℃における粘度が、70mPa・s以下であることが好ましい。なお、サポート材用樹脂組成物の粘度の測定は、JIS Z 8803に準拠し、R100型粘度計を用いて行われる。
3.光造形品およびその製造方法
本実施形態に係る光造形品は、インクジェット光造形法により、本実施形態に係るモデル材用樹脂組成物を光硬化させることによりモデル材を得るとともに、本実施形態に係るサポート材用樹脂組成物を光硬化させることによりサポート材を得る工程(I)と、上記サポート材を除去する工程(II)とを経て製造される。上記工程(I)および上記工程(II)は、特に限定されないが、例えば、以下の方法により行われる。
本実施形態に係る光造形品は、インクジェット光造形法により、本実施形態に係るモデル材用樹脂組成物を光硬化させることによりモデル材を得るとともに、本実施形態に係るサポート材用樹脂組成物を光硬化させることによりサポート材を得る工程(I)と、上記サポート材を除去する工程(II)とを経て製造される。上記工程(I)および上記工程(II)は、特に限定されないが、例えば、以下の方法により行われる。
<工程(I)>
図1は、本実施形態に係る光造形品の製造方法における工程(I)を模式的に示す図である。図1に示すように、三次元造形装置1は、インクジェットヘッドモジュール2および造形テーブル3を含む。インクジェットヘッドモジュール2は、モデル材用樹脂組成物を充填したモデル材用インクジェットヘッド21と、サポート材用樹脂組成物を充填したサポート材用インクジェットヘッド22と、ローラー23と、光源24とを有する。
図1は、本実施形態に係る光造形品の製造方法における工程(I)を模式的に示す図である。図1に示すように、三次元造形装置1は、インクジェットヘッドモジュール2および造形テーブル3を含む。インクジェットヘッドモジュール2は、モデル材用樹脂組成物を充填したモデル材用インクジェットヘッド21と、サポート材用樹脂組成物を充填したサポート材用インクジェットヘッド22と、ローラー23と、光源24とを有する。
まず、インクジェットヘッドモジュール2を図1中の造形テーブル3に対して、X方向およびY方向に走査させるとともに、モデル材用インクジェットヘッド21からモデル材用樹脂組成物を吐出させ、かつ、サポート材用インクジェットヘッド22からサポート材用樹脂組成物を吐出させることにより、モデル材用樹脂組成物とサポート材用樹脂組成物とからなる樹脂組成物層を形成する。そして、上記樹脂組成物層の上面を平滑にするために、ローラー23を用いて、余分なモデル材用樹脂組成物およびサポート材用樹脂組成物を除去する。そして、これらの樹脂組成物に、光源24を用いて光を照射することにより、造形テーブル3上に、モデル材4およびサポート材5からなる硬化層を形成する。
次に、造形テーブル3を、上記硬化層の厚み分だけ、図1中のZ方向に降下させる。その後、上述と同様の方法で、上記硬化層の上にさらにモデル材4およびサポート材5からなる硬化層を形成する。これらの工程を繰返し行うことにより、モデル材4およびサポート材5からなる硬化物6を作製する。
樹脂組成物を硬化させる光としては、例えば、遠赤外線、赤外線、可視光線、近紫外線、紫外線等が挙げられる。これらの中でも、硬化作業の容易性および効率性の観点から、近紫外線または紫外線であることが好ましい。
光源24としては、水銀灯、メタルハライドランプ、紫外線LED、紫外線レーザー等が挙げられる。これらの中でも、設備の小型化および省電力の観点から、紫外線LEDであることが好ましい。なお、光源24として紫外線LEDを用いた場合、紫外線の積算光量は、500mJ/cm2程度であることが好ましい。
<工程(II)>
図2は、本実施形態に係る光造形品の製造方法における工程(II)を模式的に示す図である。図2に示すように、工程(I)で作製したモデル材4およびサポート材5からなる硬化物6は、容器7に入れた溶媒8中に浸漬させる。これにより、サポート材5を溶媒8に溶解させて、除去することができる。
図2は、本実施形態に係る光造形品の製造方法における工程(II)を模式的に示す図である。図2に示すように、工程(I)で作製したモデル材4およびサポート材5からなる硬化物6は、容器7に入れた溶媒8中に浸漬させる。これにより、サポート材5を溶媒8に溶解させて、除去することができる。
サポート材を溶解させる溶媒8としては、例えば、イオン交換水、蒸留水、水道水、井戸水等が挙げられる。これらの中でも、不純物が比較的少なく、かつ、安価に入手できるという観点から、イオン交換水であることが好ましい。
以上の工程により得られた光造形品は、本実施形態に係るモデル材用樹脂組成物を光硬化させることにより得られるモデル材を含む。上述のように、本実施形態に係るモデル材用樹脂組成物は、光硬化させることにより得られるモデル材の硬化性が良好で、かつ、硬化収縮が大きくなりにくい。よって、寸法精度が良好なモデル材が得られる。また、本実施形態に係るサポート材用樹脂組成物は、光硬化させる際、非重合成分の浸み出しが生じにくい。さらに、本実施形態に係るサポート材用樹脂組成物を光硬化させることにより得られるサポート材は、自立性に優れている。そのため、該サポート材の上層には、寸法精度が良好なモデル材が形成される。以上より、本実施形態に係るモデル材用樹脂組成物および本実施形態に係るサポート材用樹脂組成物を用いて製造された光造形品は、寸法精度が良好である。
以下、本実施形態をより具体的に開示した実施例を示す。なお、本発明はこれらの実施例のみに限定されるものではない。
<モデル材用樹脂組成物>
(モデル材用樹脂組成物の製造)
表1に示す配合で、(A)~(G)成分を、混合攪拌装置を用いて均一に混合し、実施例M1~M17および比較例m1~m6のモデル材用樹脂組成物を製造した。そして、これらのモデル材用樹脂組成物を用いて、以下の評価を行った。
(モデル材用樹脂組成物の製造)
表1に示す配合で、(A)~(G)成分を、混合攪拌装置を用いて均一に混合し、実施例M1~M17および比較例m1~m6のモデル材用樹脂組成物を製造した。そして、これらのモデル材用樹脂組成物を用いて、以下の評価を行った。
なお、本実施例では、後述するように、照射手段として紫外線LEDを用いて、モデル材用樹脂組成物を硬化させた。実施例M16のモデル材用樹脂組成物については、(D)成分の含有量が3重量部未満であることから、紫外線LEDを照射しても、充分に硬化しなかった。したがって、実施例M16のモデル材用樹脂組成物については、硬化収縮以降の評価を行わなかった。さらに、実施例M17のモデル材用樹脂組成物については、(D)成分の含有量が15重量部を超えることから、(D)成分が充分に溶解せず、溶け残りが生じた。これにより、実施例M17のモデル材用樹脂組成物に紫外線LEDを照射しても、充分に硬化しなかった。したがって、実施例M17のモデル材用樹脂組成物については、以下の評価をすべて行わなかった。なお、実施例M16およびM17のモデル材用樹脂組成物は、照射手段として水銀灯またはメタルハライドランプを用いた場合には、(D)成分の含有量がそれぞれ1重量部および20重量部であっても硬化した。
また、比較例m1のモデル材用樹脂組成物については、(A)成分の含有量が49重量部を超えることから、照射手段の種類に関係なく、光を照射しても、充分に硬化しなかった。したがって、比較例m1のモデル材用樹脂組成物については、硬化収縮以降の評価を行わなかった。
IBOA:イソボルニルアクリレート[SR506D(エチレン性二重結合/1分子:1個)、アルケマ社製]
THFA:テトラヒドロフルフリルアクリレート[ビスコート#150(エチレン性二重結合/1分子:1個)、大阪有機化学工業社製]
PEA:フェノキシエチルアクリレート[SR3339(エチレン性二重結合/1分子:1個)、アルケマ社製]
HDDA:1,6-ヘキサンジオールジアクリレート[SR238(エチレン性二重結合/1分子:2個)、アルケマ社製]
TPGDA:トリプロピレングリコールジアクリレート[SR306(エチレン性二重結合/1分子:2個)、アルケマ社製]
PE-3A:ペンタエリスリトールトリアクリレート[ライトアクリレートPE-3A(エチレン性二重結合/1分子:3個)、共栄社化学社製]
CN991:ウレタンアクリレートオリゴマー[CN991(エチレン性二重結合/1分子:2個)、アルケマ社製]
EBECRYL3708:エポキシアクリレートオリゴマー[EBECRYL3708(エチレン性二重結合/1分子:2個)、ダイセル・オルネクス社製]
CN2203:ポリエステルアクリレートオリゴマー[CN2203(エチレン性二重結合/1分子:2個)、アルケマ社製]
DAROCURE TPO:2,4,6-トリメチルベンゾイル-ジフェニル-フォスフィンオキサイド[DAROCURE TPO、BASF社製]
TEGO-Rad2100:ポリジメチルシロキサン構造を有するシリコンアクリレート[TEGO-Rad2100、エボニック デグサ ジャパン社製]
H-TEMPO:4-ヒドロキシ-2,2,6,6-テトラメチルピペリジン-N-オキシル[HYDROXY-TEMPO、エボニック デグサ ジャパン社製]
ACMO:アクリロイルモルフォリン[ACMO(エチレン性二重結合/1分子:1個)、KJケミカルズ社製]
THFA:テトラヒドロフルフリルアクリレート[ビスコート#150(エチレン性二重結合/1分子:1個)、大阪有機化学工業社製]
PEA:フェノキシエチルアクリレート[SR3339(エチレン性二重結合/1分子:1個)、アルケマ社製]
HDDA:1,6-ヘキサンジオールジアクリレート[SR238(エチレン性二重結合/1分子:2個)、アルケマ社製]
TPGDA:トリプロピレングリコールジアクリレート[SR306(エチレン性二重結合/1分子:2個)、アルケマ社製]
PE-3A:ペンタエリスリトールトリアクリレート[ライトアクリレートPE-3A(エチレン性二重結合/1分子:3個)、共栄社化学社製]
CN991:ウレタンアクリレートオリゴマー[CN991(エチレン性二重結合/1分子:2個)、アルケマ社製]
EBECRYL3708:エポキシアクリレートオリゴマー[EBECRYL3708(エチレン性二重結合/1分子:2個)、ダイセル・オルネクス社製]
CN2203:ポリエステルアクリレートオリゴマー[CN2203(エチレン性二重結合/1分子:2個)、アルケマ社製]
DAROCURE TPO:2,4,6-トリメチルベンゾイル-ジフェニル-フォスフィンオキサイド[DAROCURE TPO、BASF社製]
TEGO-Rad2100:ポリジメチルシロキサン構造を有するシリコンアクリレート[TEGO-Rad2100、エボニック デグサ ジャパン社製]
H-TEMPO:4-ヒドロキシ-2,2,6,6-テトラメチルピペリジン-N-オキシル[HYDROXY-TEMPO、エボニック デグサ ジャパン社製]
ACMO:アクリロイルモルフォリン[ACMO(エチレン性二重結合/1分子:1個)、KJケミカルズ社製]
(粘度の測定)
各モデル材用樹脂組成物の粘度は、R100型粘度計(東機産業社製)を用いて、25℃、コーン回転数5rpmの条件下で測定し、下記の基準において評価した。評価結果を表2に示す。
○:粘度 ≦ 70mPa・s
×:粘度 > 70mPa・s
各モデル材用樹脂組成物の粘度は、R100型粘度計(東機産業社製)を用いて、25℃、コーン回転数5rpmの条件下で測定し、下記の基準において評価した。評価結果を表2に示す。
○:粘度 ≦ 70mPa・s
×:粘度 > 70mPa・s
(硬化性の評価)
まず、ポリエチレンテレフタレートからなるフィルム(A4300、東洋紡社製、100mm×150mm×厚さ188μm)上に、各モデル材用樹脂組成物を、それぞれバーコーター(#4)により印刷して、厚さ3μmの印字膜を形成した。この印字膜に、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させた。このようにして硬化させた印字膜を指で触り、指へのインクの付着の有無を目視で調べることにより、下記の基準において硬化性を評価した。なお、この評価は、画像部分から非印刷部分に向かって指で画像を擦って行った。評価結果を表2に示す。
○:表面はさらさらしており、指への付着感は無かった。
△:表面はややしっとりとしており、指への付着感はペタペタ感が有った。
×:表面はべたべたしており、指に未硬化インクの一部が付着した。
まず、ポリエチレンテレフタレートからなるフィルム(A4300、東洋紡社製、100mm×150mm×厚さ188μm)上に、各モデル材用樹脂組成物を、それぞれバーコーター(#4)により印刷して、厚さ3μmの印字膜を形成した。この印字膜に、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させた。このようにして硬化させた印字膜を指で触り、指へのインクの付着の有無を目視で調べることにより、下記の基準において硬化性を評価した。なお、この評価は、画像部分から非印刷部分に向かって指で画像を擦って行った。評価結果を表2に示す。
○:表面はさらさらしており、指への付着感は無かった。
△:表面はややしっとりとしており、指への付着感はペタペタ感が有った。
×:表面はべたべたしており、指に未硬化インクの一部が付着した。
(試験片の作成)
評価に用いるガラス板(商品名「GLASS PLATE」、アズワン社製、200mm×200mm×厚さ5mm)は、平面視で四角形である。前記ガラス板の上面の四辺に厚さ1mmのスペーサーを配置して、10cm×10cmの正方形の領域を形成した。その領域内に各モデル材用樹脂組成物を注型した後、別の上記ガラス板を重ねて載せた。そして、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させた。その後、硬化物をガラス板から離型し、カッターで幅5mm、長さ50mmの形状に切り出して、試験片を得た。該試験片について、下記の方法で性能評価を行った。なお、評価結果は、試験片5枚について評価して得られた結果の平均結果を示す。
評価に用いるガラス板(商品名「GLASS PLATE」、アズワン社製、200mm×200mm×厚さ5mm)は、平面視で四角形である。前記ガラス板の上面の四辺に厚さ1mmのスペーサーを配置して、10cm×10cmの正方形の領域を形成した。その領域内に各モデル材用樹脂組成物を注型した後、別の上記ガラス板を重ねて載せた。そして、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させた。その後、硬化物をガラス板から離型し、カッターで幅5mm、長さ50mmの形状に切り出して、試験片を得た。該試験片について、下記の方法で性能評価を行った。なお、評価結果は、試験片5枚について評価して得られた結果の平均結果を示す。
(硬化収縮の評価)
まず、調整した28%ヨウ化カリウム水溶液中に、各モデル材用樹脂組成物から得られた試験片を浸した。その際、上記試験片は、水溶液中に浮かんでいた。次に、上記試験片が水浴内中層部に浮遊する状態になるまで、上記水溶液に純水を加えた。この際のヨウ化カリウム水溶液の比重を計算し、試験片の比重とした。また、各モデル材用樹脂組成物の比重は、密度比重計DA-130(京都電子工業社製)で測定した。硬化収縮は、下記(i)式により求め、下記の基準において評価した。評価結果を表2に示す。
○:硬化収縮 ≦ 10%
△:10% < 硬化収縮 < 13%
×:硬化収縮 ≧ 13%
まず、調整した28%ヨウ化カリウム水溶液中に、各モデル材用樹脂組成物から得られた試験片を浸した。その際、上記試験片は、水溶液中に浮かんでいた。次に、上記試験片が水浴内中層部に浮遊する状態になるまで、上記水溶液に純水を加えた。この際のヨウ化カリウム水溶液の比重を計算し、試験片の比重とした。また、各モデル材用樹脂組成物の比重は、密度比重計DA-130(京都電子工業社製)で測定した。硬化収縮は、下記(i)式により求め、下記の基準において評価した。評価結果を表2に示す。
○:硬化収縮 ≦ 10%
△:10% < 硬化収縮 < 13%
×:硬化収縮 ≧ 13%
(ガラス転移点Tgの測定)
各モデル材用樹脂組成物から得られた試験片のガラス転移点Tgは、熱重量測定装置(TG-DTA2000S Thermo Plus EvoII DSC8230、株式会社リガク製)を用いて測定した。測定は、昇温温度:10℃/min、測定温度範囲:-60℃~200℃で行った。測定結果を表2に示す。
各モデル材用樹脂組成物から得られた試験片のガラス転移点Tgは、熱重量測定装置(TG-DTA2000S Thermo Plus EvoII DSC8230、株式会社リガク製)を用いて測定した。測定は、昇温温度:10℃/min、測定温度範囲:-60℃~200℃で行った。測定結果を表2に示す。
(破断強度の評価)
オートグラフ(株式会社島津製作所製)を用いて、各モデル材用樹脂組成物から得られた試験片を試験速度50mm/minで引張り、JIS K7113に準じて引張破断強度を測定し、破断強度とした。破断強度は、下記の基準において評価した。評価結果を表2に示す。
○:破断強度 ≧ 30MPa
×:破断強度 < 30MPa
オートグラフ(株式会社島津製作所製)を用いて、各モデル材用樹脂組成物から得られた試験片を試験速度50mm/minで引張り、JIS K7113に準じて引張破断強度を測定し、破断強度とした。破断強度は、下記の基準において評価した。評価結果を表2に示す。
○:破断強度 ≧ 30MPa
×:破断強度 < 30MPa
表2の結果から分かるように、本発明の要件を全て満たす実施例M1~M16のモデル材用樹脂組成物は、インクジェットヘッドからの吐出に適した粘度を示した。また、実施例M1~M15のモデル材用樹脂組成物を光硬化させることにより得られるモデル材は、優れた硬化性を示し、かつ、硬化収縮が抑制された。これにより、形成されたモデル材の寸法精度は良好であった。さらに、該モデル材は、破断強度が高かった。
また、(B)成分の含有量が45重量部以下、かつ、(C)成分の含有量が15重量部以上である実施例M1~M6、M8、M10~M15のモデル材用樹脂組成物から得られるモデル材は、硬化収縮がより抑制された。さらに、(D)成分の含有量が5重量部以上である実施例M1~M9、M11~M15のモデル材用樹脂組成物から得られるモデル材は、より優れた硬化性を示した。
一方、比較例m1のモデル材用樹脂組成物は、(A)成分の含有量が49重量部を超えることから、モデル材の硬化不足が生じた。比較例m2のモデル材用樹脂組成物は、(A)成分の含有量が19重量部未満であることから、モデル材の硬化収縮が生じた。比較例m3のモデル材用樹脂組成物は、(B)成分の含有量が50重量部を超えることから、モデル材の硬化収縮が生じた。比較例m4のモデル材用樹脂組成物は、(B)成分の含有量が15重量部未満であることから、モデル材の硬化不足が生じた。比較例m5のモデル材用樹脂組成物は、(C)成分の含有量が10重量部未満であることから、モデル材がやや硬化収縮し、かつ、モデル材の破断強度が劣った。比較例m6のモデル材用樹脂組成物は、(C)成分の含有量が45重量部を超えることから、粘度が高かった。
<サポート材用樹脂組成物>
(サポート材用樹脂組成物の製造)
表3に示す配合で、(D)~(F)、(G)~(I)成分を、混合攪拌装置を用いて均一に混合し、実施例S1~S17および比較例s1~s6のサポート材用樹脂組成物を製造した。そして、これらのサポート材用樹脂組成物を用いて、以下の評価を行った。
(サポート材用樹脂組成物の製造)
表3に示す配合で、(D)~(F)、(G)~(I)成分を、混合攪拌装置を用いて均一に混合し、実施例S1~S17および比較例s1~s6のサポート材用樹脂組成物を製造した。そして、これらのサポート材用樹脂組成物を用いて、以下の評価を行った。
なお、本実施例では、後述するように、照射手段として紫外線LEDを用いて、サポート材用樹脂組成物を硬化させた。実施例S17のサポート材用樹脂組成物については、(D)成分の含有量が20重量部を超えることから、(D)成分が充分に溶解せず、溶け残りが生じた。これにより、実施例S17のサポート材用樹脂組成物に紫外線LEDを照射しても、満足に硬化しなかった。したがって、実施例S17のサポート材用樹脂組成物については、以下の評価をすべて行わなかった。なお、実施例S17のサポート材用樹脂組成物は、照射手段として水銀灯またはメタルハライドランプを用いた場合には、(D)成分の含有量が25重量部であっても硬化した。
HEAA:N-ヒドロキシエチルアクリルアミド[HEAA(エチレン性二重結合/1分子:1個)、KJケミカルズ社製]
ACMO:アクリロイルモルフォリン[ACMO(エチレン性二重結合/1分子:1個)、KJケミカルズ社製]
DMAA:N,N’-ジメチルアクリルアミド[DMAA(エチレン性二重結合/1分子:1個)、KJケミカルズ社製]
PPG-400:ポリプロピレングリコール[ユニオールD400(分子量400)、日油社製]
PPG-1000:ポリプロピレングリコール[ユニオールD1000(分子量1000)、日油社製]
PEG-400:ポリエチレングリコール[PEG#400(分子量400)、日油社製]
PEG-1000:ポリエチレングリコール[PEG#1000(分子量1000)、日油社製]
MTG:トリエチレングリコールモノメチルエーテル[MTG、日本乳化剤社製]
DPMA:ジプロピレングリコールモノメチルエーテルアセテート[ダワノールDPMA、ダウケミカル社製]
ACMO:アクリロイルモルフォリン[ACMO(エチレン性二重結合/1分子:1個)、KJケミカルズ社製]
DMAA:N,N’-ジメチルアクリルアミド[DMAA(エチレン性二重結合/1分子:1個)、KJケミカルズ社製]
PPG-400:ポリプロピレングリコール[ユニオールD400(分子量400)、日油社製]
PPG-1000:ポリプロピレングリコール[ユニオールD1000(分子量1000)、日油社製]
PEG-400:ポリエチレングリコール[PEG#400(分子量400)、日油社製]
PEG-1000:ポリエチレングリコール[PEG#1000(分子量1000)、日油社製]
MTG:トリエチレングリコールモノメチルエーテル[MTG、日本乳化剤社製]
DPMA:ジプロピレングリコールモノメチルエーテルアセテート[ダワノールDPMA、ダウケミカル社製]
(粘度の測定)
各サポート材用樹脂組成物の粘度は、R100型粘度計(東機産業社製)を用いて、25℃、コーン回転数5rpmの条件下で測定し、下記の基準において評価した。評価結果を表4に示す。
○:粘度 ≦ 70mPa・s
×:粘度 > 70mPa・s
各サポート材用樹脂組成物の粘度は、R100型粘度計(東機産業社製)を用いて、25℃、コーン回転数5rpmの条件下で測定し、下記の基準において評価した。評価結果を表4に示す。
○:粘度 ≦ 70mPa・s
×:粘度 > 70mPa・s
(水への溶解性)
直径50mmのアルミカップに、各サポート材用樹脂組成物2.0gを採取した。次に、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させ、サポート材を得た。その後、サポート材をアルミカップから離型した。続いて、ビーカーに入れたイオン交換水500ml中に、上記サポート材を浸漬した。10分毎にサポート材を目視で観察し、浸漬開始から完全溶解または元の形状が無くなるまでに要した時間(以下、水溶解時間という)を計測し、下記の基準において溶解性を評価した。評価結果を表4に示す。
○:水溶解時間 ≦ 1時間
△:1時間 < 水溶解時間 <1.5時間
×:水溶解時間 ≧ 1.5時間
直径50mmのアルミカップに、各サポート材用樹脂組成物2.0gを採取した。次に、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させ、サポート材を得た。その後、サポート材をアルミカップから離型した。続いて、ビーカーに入れたイオン交換水500ml中に、上記サポート材を浸漬した。10分毎にサポート材を目視で観察し、浸漬開始から完全溶解または元の形状が無くなるまでに要した時間(以下、水溶解時間という)を計測し、下記の基準において溶解性を評価した。評価結果を表4に示す。
○:水溶解時間 ≦ 1時間
△:1時間 < 水溶解時間 <1.5時間
×:水溶解時間 ≧ 1.5時間
(油状浸み出しの評価)
100mm×100mmのアルミ箔に、各サポート材用樹脂組成物1.0gを採取した。次に、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させ、サポート材を得た。なお、この時点でサポート材は固体状態である。このサポート材を2時間放置し、サポート材表面における油状浸み出しの有無を目視で観察し、下記の基準において評価した。評価結果を表4に示す。
○:油状浸み出しが全く観察されなかった
△:わずかに油状浸み出しが観察された
×:油状浸み出しが多く観察された
100mm×100mmのアルミ箔に、各サポート材用樹脂組成物1.0gを採取した。次に、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させ、サポート材を得た。なお、この時点でサポート材は固体状態である。このサポート材を2時間放置し、サポート材表面における油状浸み出しの有無を目視で観察し、下記の基準において評価した。評価結果を表4に示す。
○:油状浸み出しが全く観察されなかった
△:わずかに油状浸み出しが観察された
×:油状浸み出しが多く観察された
(自立性の評価)
評価に用いるガラス板(商品名「GLASS PLATE」、アズワン社製、200mm×200mm×厚さ5mm)は、平面視で四角形である。前記ガラス板の上面の四辺に厚さ1mmのスペーサーを配置して、10cm×10cmの正方形の領域を形成した。その領域内に各サポート材用樹脂組成物を注型した後、別の上記ガラス板を重ねて載せた。そして、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させ、サポート材を得た。その後、サポート材をガラス板から離型し、カッターで縦10mm、横10mmの形状に切り出して、試験片を得た。次に、該試験片を10枚重ねて、高さ10mmの試験片群を得た。該試験片群は、上から100gの重しを乗せ、そのまま30℃に設定したオーブンの中に入れ、1時間放置した。その後、試験片の形状を観察し、下記の基準において自立性を評価した。評価結果を表4に示す。
○:形状に変化がなかった
△:形状がわずかに変化し、重しが傾いた状態になった
×:形状が大きく変化した
評価に用いるガラス板(商品名「GLASS PLATE」、アズワン社製、200mm×200mm×厚さ5mm)は、平面視で四角形である。前記ガラス板の上面の四辺に厚さ1mmのスペーサーを配置して、10cm×10cmの正方形の領域を形成した。その領域内に各サポート材用樹脂組成物を注型した後、別の上記ガラス板を重ねて載せた。そして、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させ、サポート材を得た。その後、サポート材をガラス板から離型し、カッターで縦10mm、横10mmの形状に切り出して、試験片を得た。次に、該試験片を10枚重ねて、高さ10mmの試験片群を得た。該試験片群は、上から100gの重しを乗せ、そのまま30℃に設定したオーブンの中に入れ、1時間放置した。その後、試験片の形状を観察し、下記の基準において自立性を評価した。評価結果を表4に示す。
○:形状に変化がなかった
△:形状がわずかに変化し、重しが傾いた状態になった
×:形状が大きく変化した
表4の結果から分かるように、本発明の要件を全て満たす実施例S1~S16のサポート材用樹脂組成物は、インクジェットヘッドからの吐出に適した粘度であった。また、実施例S1~S16のサポート材用樹脂組成物を光硬化させることにより得られるサポート材は、水への溶解性が高く、かつ、油状浸み出しが抑制された。さらに、実施例S1~S15のサポート材用樹脂組成物を光硬化させることにより得られるサポート材は、充分な自立性を有していた。なお、実施例S16のサポート材用樹脂組成物は、(D)成分の含有量が5重量部未満であることから、紫外線LEDを照射しても、ラジカル反応が促進せず、得られるサポート材の自立性が充分ではなかった。実施例S16のサポート材用樹脂組成物は、照射手段として水銀灯またはメタルハライドランプを用いた場合には、(D)成分の含有量が3重量部であっても、得られるサポート材が充分な自立性を有する。
さらに、(G)成分の含有量が45重量部以下、かつ、(H)成分の含有量が25重量部以上である実施例S1~S8、S10、S11、S13~S16のサポート材用樹脂組成物から得られるサポート材は、水への溶解性がより高かった。(H)成分の含有量が45重量部以下、かつ、(I)成分の含有量が30重量部以下である実施例S1~S10、S12、S14~S16のサポート材用樹脂組成物から得られるサポート材は、油状浸み出しがより抑制された。(G)成分の含有量が25重量部以上である実施例S1~S7、S9~S12、S14、S15のサポート材用樹脂組成物から得られるサポート材は、より充分な自立性を有していた。
一方、比較例s1のサポート材用樹脂組成物は、(G)成分の含有量が20重量部未満であることから、サポート材の自立性が充分ではなかった。比較例s2のサポート材用樹脂組成物は、(G)成分の含有量が50重量部を超えることから、サポート材の水への溶解性が低かった。比較例s3のサポート材用樹脂組成物は、(H)成分の含有量が49重量部を超えることから、粘度が高く、かつ、サポート材において油状浸み出しが生じた。比較例s4のサポート材用樹脂組成物は、(I)成分の含有量が35重量部を超えることから、サポート材において油状浸み出しが生じた。比較例s5のサポート材用樹脂組成物は、(H)成分の含有量が20重量部未満であることから、サポート材の水への溶解性が低かった。また、比較例s5のサポート材用樹脂組成物は、(I)成分の含有量が35重量部を超えることから、サポート材において油状浸み出しが生じた。比較例s6のサポート材用樹脂組成物は、(H)成分の含有量が49重量部を超えることから、粘度が高く、かつ、サポート材において油状浸み出しが生じた。
<光造形品>
(密着性の評価)
評価に用いるガラス板(商品名「GLASS PLATE」、アズワン社製、200mm×200mm×厚さ5mm)は、平面視で四角形である。前記ガラス板の上面の四辺に厚さ1mmのスペーサーを配置して、10cm×10cmの正方形の領域を形成した。その領域内に各サポート材用樹脂組成物を注型した後、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させることにより、サポート材を得た。
(密着性の評価)
評価に用いるガラス板(商品名「GLASS PLATE」、アズワン社製、200mm×200mm×厚さ5mm)は、平面視で四角形である。前記ガラス板の上面の四辺に厚さ1mmのスペーサーを配置して、10cm×10cmの正方形の領域を形成した。その領域内に各サポート材用樹脂組成物を注型した後、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させることにより、サポート材を得た。
次に、上記サポート材の上面の四辺に厚さ1mmのスペーサーを配置することにより、10cm×10cmの領域を形成した。その領域内に各モデル材用樹脂組成物を注型した後、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用いて、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させることにより、モデル材を得た。
この状態で30℃の恒温槽に12時間放置した後、モデル材とサポート材との密着性の様子を目視にて確認することにより、下記の基準において評価した。結果を表5に示す。
○:モデル材とサポート材とは密着していた。
△:モデル材とサポート材とは密着していたが、モデル材とサポート材との界面を爪でひっかくと剥がれが生じた。
×:モデル材とサポート材との界面で剥がれが生じ、モデル材の硬化収縮でモデル材が反るように剥がれた。
○:モデル材とサポート材とは密着していた。
△:モデル材とサポート材とは密着していたが、モデル材とサポート材との界面を爪でひっかくと剥がれが生じた。
×:モデル材とサポート材との界面で剥がれが生じ、モデル材の硬化収縮でモデル材が反るように剥がれた。
表5の結果から分かるように、モデル材用樹脂組成物およびサポート材用樹脂組成物のうち、少なくとも一方が本発明の要件を満たす光造形品1~8は、モデル材とサポート材とが密着していた。さらに、モデル材用樹脂組成物およびサポート材用樹脂組成物の両方が本発明の要件を満たす光造形品1~4は、モデル材とサポート材との界面に剥がれが生じず、モデル材とサポート材とがより密着していた。このように、モデル材とサポート材とが密着していれば、寸法精度が良好な光造形品が得られる。
一方、モデル材用樹脂組成物およびサポート材用樹脂組成物の両方が本発明の要件を満たしていない光造形品9および10は、モデル材とサポート材との界面で剥がれが生じた。このように、モデル材とサポート材との密着性が悪いと、光造形品の寸法精度が悪化する。
本発明のモデル材用樹脂組成物およびサポート材用樹脂組成物は、光硬化させることにより、寸法精度が良好な光造形品を得ることができる。よって、これらの樹脂組成物は、インクジェット光造形法による光造形品の製造に好適に用いることができる。
Claims (16)
- インクジェット光造形法によりモデル材を造形するために使用されるモデル材用樹脂組成物であって、
樹脂組成物全体100重量部に対して、
19~49重量部の非水溶性単官能エチレン性不飽和単量体(A)と、
15~50重量部の二官能以上の多官能エチレン性不飽和単量体(B)と、
10~45重量部のオリゴマー(C)と、
光重合開始剤(D)と、
を含有する、モデル材用樹脂組成物。 - 前記(A)成分の含有量は、樹脂組成物全体100重量部に対して、25~47重量部である、請求項1に記載のモデル材用樹脂組成物。
- 前記(B)成分の含有量は、樹脂組成物全体100重量部に対して、20~45重量部である、請求項1または2に記載のモデル材用樹脂組成物。
- 前記(C)成分は、ウレタン(メタ)アクリレートオリゴマー、エポキシ(メタ)アクリレートオリゴマー、および、ポリエステル(メタ)アクリレートオリゴマーから選択される1種以上である、請求項1~3のいずれか一つに記載のモデル材用樹脂組成物。
- 前記(C)成分の含有量は、樹脂組成物全体100重量部に対して、15~30重量部である、請求項1~4のいずれか一つに記載のモデル材用樹脂組成物。
- 前記(D)成分の含有量は、樹脂組成物全体100重量部に対して、3~15重量部である、請求項1~5のいずれか一つに記載のモデル材用樹脂組成物。
- さらに、保存安定化剤(F)を、樹脂組成物全体100重量部に対して、0.05~3.0重量部含有する、請求項1~6のいずれか一つに記載のモデル材用樹脂組成物。
- インクジェット光造形法によりサポート材を造形するために使用されるサポート材用樹脂組成物であって、
樹脂組成物全体100重量部に対して、
20~50重量部の水溶性単官能エチレン性不飽和単量体(G)と、
20~49重量部のオキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコール(H)と、
35重量部以下の水溶性有機溶剤(I)と、
光重合開始剤(D)と、
を含有する、サポート材用樹脂組成物。 - 前記(G)成分の含有量は、樹脂組成物全体100重量部に対して、25~45重量部である、請求項8に記載のサポート材用樹脂組成物。
- 前記(H)成分の含有量は、樹脂組成物全体100重量部に対して、25~45重量部である、請求項8または9に記載のサポート材用樹脂組成物。
- 前記(D)成分の含有量は、樹脂組成物全体100重量部に対して、5~20重量部である、請求項8~10のいずれか一つに記載のサポート材用樹脂組成物。
- 前記(I)成分の含有量は、樹脂組成物全体100重量部に対して、5重量部以上である、請求項8~11のいずれか一つに記載のサポート材用樹脂組成物。
- さらに、保存安定化剤(F)を、樹脂組成物全体100重量部に対して、0.05~3.0重量部含有する、請求項8~12のいずれか一つに記載のサポート材用樹脂組成物。
- インクジェット光造形法により、請求項1~7のいずれか一つに記載のモデル材用樹脂組成物を光硬化させることにより得られるモデル材を含む、光造形品。
- インクジェット光造形法により請求項14に記載の光造形品を製造する方法であって、
請求項1~7のいずれか一つに記載のモデル材用樹脂組成物を光硬化させることによりモデル材を得るとともに、請求項8~13のいずれか一つに記載のサポート材用樹脂組成物を光硬化させることによりサポート材を得る工程(I)と、
前記サポート材を除去する工程(II)と、
を有する、光造形品の製造方法。 - 前記工程(I)では、紫外線LEDを用いて、前記モデル材用樹脂組成物および前記サポート材用樹脂組成物を光硬化させる、請求項15に記載の光造形品の製造方法。