WO2016031828A1 - ガラス板 - Google Patents
ガラス板 Download PDFInfo
- Publication number
- WO2016031828A1 WO2016031828A1 PCT/JP2015/073899 JP2015073899W WO2016031828A1 WO 2016031828 A1 WO2016031828 A1 WO 2016031828A1 JP 2015073899 W JP2015073899 W JP 2015073899W WO 2016031828 A1 WO2016031828 A1 WO 2016031828A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- glass plate
- main surface
- light
- less
- glass
- Prior art date
Abstract
Description
第1主表面、前記第1主表面に対向する第2主表面、並びに、前記第1主表面および前記第2主表面を接続する端面からなり、前記第1主表面および前記第2主表面が実質的に矩形であるガラス板であって、
前記ガラス板は、波長550nmの光の吸収係数が1m-1以下であり、波長400~700nmの範囲の光の吸収係数の最大値αmax(m-1)と、最小値αmin(m-1)と、の比(αmax/αmin)が10以下であり、
前記ガラス板内部に複数の泡が存在し、前記端面の任意の一つを基準端面とし、前記第1主表面と前記基準端面とが共有する辺を基準辺とするとき、前記基準辺に平行な方向における前記泡の長さの最大値が500μm以下であることを特徴とするガラス板を提供する。
(目視判定)
複数の泡が存在するガラス板の一方の主表面に、拡散インキをドットパターン状に印刷して、一方の主表面に散乱部材を形成されたガラス導光板を作成した。このガラス板の寸法は、485mm×284mm×t2mmであった。
泡間最短距離による影響について、シミュレーション解析により評価した。このシミュレーション解析には、光線追跡ソフト(LightTools:サイバーネットシステム社製)を用いた。
11:第1主表面
12:第2主表面
13:端面
13a:基準端面
14:基準辺
20:ガラス
30:泡
100:導光板ユニット
200:導光板
300:反射部材
400:散乱部材
Claims (7)
- 第1主表面、前記第1主表面に対向する第2主表面、並びに、前記第1主表面および前記第2主表面を接続する端面からなり、前記第1主表面および前記第2主表面が実質的に矩形であるガラス板であって、
前記ガラス板は、波長550nmの光の吸収係数が1m-1以下であり、波長400~700nmの範囲の光の吸収係数の最大値αmax(m-1)と、最小値αmin(m-1)と、の比(αmax/αmin)が10以下であり、
前記ガラス板内部に複数の泡が存在し、前記端面の任意の一つを基準端面とし、前記第1主表面と前記基準端面とが共有する辺を基準辺とするとき、前記基準辺に平行な方向における前記泡の長さの最大値が500μm以下であることを特徴とするガラス板。 - 波長400~700nmの範囲の光の吸収係数の最大値αmaxが1m-1以下である請求項1に記載のガラス板。
- 前記泡の最大径となる位置を通過する仮想線を泡の長軸とするとき、
前記ガラス板内部に存在する泡の70%以上が、前記基準端面と、前記長軸と、がなす角度が85~95度である、請求項1または2に記載のガラス板。 - 前記基準端面に垂直な方向における泡間最短距離が5mm以上であり、かつ、
前記基準端面に平行な方向における泡間最短距離が1.5mm以上である、請求項1~3のいずれか1項に記載のガラス板。 - 前記第1主表面における長さが10~130mmの範囲である線傷の数及び(最大径+最小径)/2が0.1~0.3mmの範囲である付着異物の数の和をI1とし、前記第2主表面における長さが10~130mmの範囲である線傷の数及び(最大径+最小径)/2が0.1~0.3mmの範囲である付着異物の数の和をI2とするとき、2<│I1-I2│である、請求項1~4のいずれか1項に記載のガラス板。
- 前記第1主表面および前記第2主表面の少なくとも1辺の長さが200mm以上であり、前記ガラス板の厚さが0.5~10mmである、請求項1~5のいずれか1項に記載のガラス板。
- 前記泡の最大径を長径とし、前記泡の最小径を短径とするとき、前記長径と前記短径との比(長径/短径)が1.1以上である、請求項1~6のいずれか1項に記載のガラス板。