WO2015151574A1 - レーザ溶接良否判定方法および良否判定機構を備えるレーザ溶接装置 - Google Patents
レーザ溶接良否判定方法および良否判定機構を備えるレーザ溶接装置 Download PDFInfo
- Publication number
- WO2015151574A1 WO2015151574A1 PCT/JP2015/053000 JP2015053000W WO2015151574A1 WO 2015151574 A1 WO2015151574 A1 WO 2015151574A1 JP 2015053000 W JP2015053000 W JP 2015053000W WO 2015151574 A1 WO2015151574 A1 WO 2015151574A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- molten pool
- quality
- welding
- width
- laser
- Prior art date
Abstract
本発明に係るレーザ溶接良否判定方法は、レーザ溶接中に溶接品質の良否を判定する方法であって、被溶接材(7)にレーザ光(2)を照射することにより形成された溶融池を撮影して前記溶融池の画像データを取得する工程と、取得した前記溶融池の画像データから、溶接方向に直交する方向の前記溶融池の幅を計測する工程と、計測した前記溶融池の幅から溶込み深さを算定する工程と、計測した前記溶融池の幅と算定した前記溶込み深さとから溶接品質の良否を判定する工程とを有することで、溶接ビードの内部欠陥の影響を強く受ける溶接品質の判定精度が向上する。
Description
本発明は、レーザ溶接の技術に関し、特に、レーザ溶接中に溶接の良否を判定する方法および該良否判定方法を実施する機構を備えるレーザ溶接装置に関するものである。
レーザ溶接は、集光したレーザ光(パルス波または連続波)を熱源として被溶接材に照射し、被溶接材を局部的に溶融・凝固させて接合する方法である。レーザ光は、光学系レンズによって極めて小さな点に集光することが容易なため、他の溶接法に比してエネルギー密度を大きく高めることができる。その結果、レーザ溶接は、高速・高精度の深溶込み溶接が可能、溶接変形が少ない等の特長を有する。
レーザ溶接は、適用できる被溶接材の範囲が広く、鉄鋼材料(例えば、ステンレス鋼、炭素鋼)やアルミ合金やニッケル合金などの金属材料に加えて、樹脂材料やセラミックス材料などの非金属材料にも適用可能である。また、溶接継手の形態として、突合わせ溶接や重ね溶接などが可能であり、例えば自動車工業分野における、車体、燃料ポンプ、インジェクタ(燃料噴射弁)、エアーフローセンサ、応力・ひずみセンサーなど種々の製品の溶接プロセスに利用されている。
溶接された製品(溶接継手)の溶接品質を表わす指標は製品によって異なるが、一般的に、継手の強度と密閉性とが重要な指標になる。要求される継手強度と密閉性とを達成するためには、十分な量の溶込み深さを確保し、かつ溶接部(溶接ビード)に欠陥(例えば、溶接割れ、ブローホール)が発生しないことが必須条件である。
溶接作業の自動化は、そのコスト低減効果が非常に大きく、レーザ溶接は、上記のような特長から自動溶接機に適した溶接方法である。一方、溶接は、本質的に、溶接部への投入熱量と溶接部からの放熱量との微妙なバランスの上に成り立っているため、溶接の施工条件の変動や周囲環境の変動の影響を受け易く、溶接品質がばらつき易いという技術的難しさがある。そのため、溶接の自動化を進めるにあたって、溶接中に溶接品質の良否を正確かつ迅速に判定する方法が求められる。
例えば、特許文献1(WO 2011/024904)には、レーザ溶接による溶接部の溶接良否を判定する方法であって、高速度カメラを用いて前記溶接部ないしその近傍を撮影し、撮影した画像内の単位長さ辺りのスパッタ数や高輝度部面積やキーホールの検出頻度などのパラメータを解析し、この解析したパラメータと、あらかじめ作成した対照テーブルとの対比により前記溶接部の溶接の良否を判定して、この溶接良否結果をモニタ上に表示するレーザ溶接良否判定方法が開示されている。また、レーザ溶接による溶接部の溶接良否を判定する装置であって、前記溶接部ないしその近傍を撮影する高速度カメラと、撮影した画像内のパラメータを画像解析して、溶接部の溶接良否を判定する解析部と、この解析部で判定された前記溶接部の溶接良否を表示するモニタを備えたレーザ溶接良否判定装置が開示されている。
特許文献1(WO 2011/024904)によると、レーザ溶接による溶接部の良否判定のみならず剪断強度予測や破断モード予測をインプロセスで行うことができ、その結果、高速で且つ高精度なレーザ溶接に対応した品質管理を行うことが可能である、とされている。しかしながら、特許文献1の良否判定方法は、ピットやブローホール等の溶接ビードの表面欠陥の発生率を推定することはできるが、溶接ビードの内部欠陥の影響を強く受ける継手強度や密閉性といった溶接品質の判定が困難という課題がある。
したがって、本発明の目的は、溶接ビードの内部欠陥の影響を強く受ける溶接品質の判定精度が向上するレーザ溶接良否判定方法および該良否判定方法を実施する機構を備えるレーザ溶接装置を提供することにある。
(I)本発明の一態様は、レーザ溶接中に溶接品質の良否を判定する方法であって、
被溶接材にレーザ光を照射することにより形成された溶融池を撮影して前記溶融池の画像データを取得する工程と、
取得した前記溶融池の画像データから、溶接方向に直交する方向の前記溶融池の幅を計測する工程と、
計測した前記溶融池の幅から溶込み深さを算定する工程と、
計測した前記溶融池の幅と算定した前記溶込み深さとから溶接品質の良否を判定する工程とを有することを特徴とするレーザ溶接良否判定方法を提供する。
被溶接材にレーザ光を照射することにより形成された溶融池を撮影して前記溶融池の画像データを取得する工程と、
取得した前記溶融池の画像データから、溶接方向に直交する方向の前記溶融池の幅を計測する工程と、
計測した前記溶融池の幅から溶込み深さを算定する工程と、
計測した前記溶融池の幅と算定した前記溶込み深さとから溶接品質の良否を判定する工程とを有することを特徴とするレーザ溶接良否判定方法を提供する。
また、本発明は、上記の発明に係るレーザ溶接良否判定方法(I)において、以下のような改良や変更を加えることができる。
(i)前記溶融池の幅を計測する工程は、前記被溶接材の溶融時の放射光の輝度を輝度閾値とし、前記溶融池の画像データ中で前記輝度閾値以上の輝度を示す部分を溶融池として検出し、前記溶接方向に直交する方向において前記輝度閾値を示す2点間の距離のうち最大のものを前記溶融池の幅として計測する工程である。
(ii)前記溶込み深さを算定する工程は、あらかじめ定めたデータベースに、計測された前記溶融池の幅を照合して前記溶込み深さを算定する工程である。
(iii)前記レーザ溶接良否判定方法は、取得した前記溶融池の画像データから、溶接方向の前記溶融池の長さを計測する工程を更に有し、前記溶込み深さを算定する工程は、計測した前記溶融池の幅と計測した前記溶融池の長さとから前記溶込み深さを算定する工程である。
(iv)前記溶込み深さを算定する工程は、あらかじめ定めたデータベースに、計測した前記溶融池の幅と長さとを照合して前記溶込み深さを算定する工程である。
(v)前記溶接品質の良否を判定する工程は、計測した前記溶融池の幅と計測した前記溶融池の長さと算定した前記溶込み深さとから前記溶接品質の良否を判定する工程である。
(i)前記溶融池の幅を計測する工程は、前記被溶接材の溶融時の放射光の輝度を輝度閾値とし、前記溶融池の画像データ中で前記輝度閾値以上の輝度を示す部分を溶融池として検出し、前記溶接方向に直交する方向において前記輝度閾値を示す2点間の距離のうち最大のものを前記溶融池の幅として計測する工程である。
(ii)前記溶込み深さを算定する工程は、あらかじめ定めたデータベースに、計測された前記溶融池の幅を照合して前記溶込み深さを算定する工程である。
(iii)前記レーザ溶接良否判定方法は、取得した前記溶融池の画像データから、溶接方向の前記溶融池の長さを計測する工程を更に有し、前記溶込み深さを算定する工程は、計測した前記溶融池の幅と計測した前記溶融池の長さとから前記溶込み深さを算定する工程である。
(iv)前記溶込み深さを算定する工程は、あらかじめ定めたデータベースに、計測した前記溶融池の幅と長さとを照合して前記溶込み深さを算定する工程である。
(v)前記溶接品質の良否を判定する工程は、計測した前記溶融池の幅と計測した前記溶融池の長さと算定した前記溶込み深さとから前記溶接品質の良否を判定する工程である。
(II)本発明の他の一態様は、レーザ溶接中に溶接品質の良否を判定する方法であって、
被溶接材にレーザ光を照射することにより形成された溶融池を撮影して前記溶融池の画像データを取得する工程と、
取得した前記溶融池の画像データから、溶接方向に直交する方向の前記溶融池の幅を計測する工程と、
計測した前記溶融池の幅とあらかじめ定めたデータベースの溶込み深さとから溶接品質の良否を判定する工程とを備えることを特徴とするレーザ溶接良否判定方法を提供する。
被溶接材にレーザ光を照射することにより形成された溶融池を撮影して前記溶融池の画像データを取得する工程と、
取得した前記溶融池の画像データから、溶接方向に直交する方向の前記溶融池の幅を計測する工程と、
計測した前記溶融池の幅とあらかじめ定めたデータベースの溶込み深さとから溶接品質の良否を判定する工程とを備えることを特徴とするレーザ溶接良否判定方法を提供する。
また、本発明は、上記の発明に係るレーザ溶接良否判定方法(II)において、以下のような改良や変更を加えることができる。
(vi)前記溶融池の幅を計測する工程は、前記被溶接材の溶融時の放射光の輝度を輝度閾値とし、前記溶融池の画像データ中で前記輝度閾値以上の輝度を示す部分を溶融池として検出し、前記溶接方向に直交する方向において前記輝度閾値を示す2点間の距離のうち最大のものを前記溶融池の幅として計測する工程である。
(vii)前記レーザ溶接良否判定方法は、取得した前記溶融池の画像データから、溶接方向の前記溶融池の長さを計測する工程を更に有し、前記溶接品質の良否を判定する工程は、計測した前記溶融池の幅と計測した前記溶融池の長さと前記データベースの溶込み深さとから溶接品質の良否を判定する工程である。
(vi)前記溶融池の幅を計測する工程は、前記被溶接材の溶融時の放射光の輝度を輝度閾値とし、前記溶融池の画像データ中で前記輝度閾値以上の輝度を示す部分を溶融池として検出し、前記溶接方向に直交する方向において前記輝度閾値を示す2点間の距離のうち最大のものを前記溶融池の幅として計測する工程である。
(vii)前記レーザ溶接良否判定方法は、取得した前記溶融池の画像データから、溶接方向の前記溶融池の長さを計測する工程を更に有し、前記溶接品質の良否を判定する工程は、計測した前記溶融池の幅と計測した前記溶融池の長さと前記データベースの溶込み深さとから溶接品質の良否を判定する工程である。
(III)本発明の更に他の一態様は、レーザ溶接中に溶接品質の良否を判定する機構を備えるレーザ溶接装置であって、
被溶接材にレーザ光を照射することにより溶融池を形成するレーザヘッドと、
溶接品質の良否を判定するレーザ溶接良否判定機構とを具備し、
前記レーザ溶接良否判定機構は、前記溶融池を撮影して該溶融池の画像データを取得する撮影装置と、前記画像データを解析処理するデータ処理装置とを有し、
前記データ処理装置は、
前記溶融池の画像データの輝度を測定する輝度測定機構と、
前記輝度に基づいて、溶接方向に直交する方向の前記溶融池の幅を測定する溶融池形状測定機構と、
前記溶融池の幅に対応する溶込み深さを記録した第一データベースと、
前記溶融池の幅と前記溶込み深さとに基づく溶接品質の良否判断を記録した第二データベースとを備えることを特徴とするレーザ溶接装置を提供する。
被溶接材にレーザ光を照射することにより溶融池を形成するレーザヘッドと、
溶接品質の良否を判定するレーザ溶接良否判定機構とを具備し、
前記レーザ溶接良否判定機構は、前記溶融池を撮影して該溶融池の画像データを取得する撮影装置と、前記画像データを解析処理するデータ処理装置とを有し、
前記データ処理装置は、
前記溶融池の画像データの輝度を測定する輝度測定機構と、
前記輝度に基づいて、溶接方向に直交する方向の前記溶融池の幅を測定する溶融池形状測定機構と、
前記溶融池の幅に対応する溶込み深さを記録した第一データベースと、
前記溶融池の幅と前記溶込み深さとに基づく溶接品質の良否判断を記録した第二データベースとを備えることを特徴とするレーザ溶接装置を提供する。
(IV)本発明の更に他の一態様は、レーザ溶接中に溶接品質の良否を判定する機構を備えるレーザ溶接装置であって、
被溶接材にレーザ光を照射することにより溶融池を形成するレーザヘッドと、
溶接品質の良否を判定するレーザ溶接良否判定機構とを具備し、
前記レーザ溶接良否判定機構は、前記溶融池を撮影して該溶融池の画像データを取得する撮影装置と、前記画像データを解析処理するデータ処理装置とを有し、
前記データ処理装置は、
前記溶融池の画像データの輝度を測定する輝度測定機構と、
前記輝度に基づいて、溶接方向に直交する方向の前記溶融池の幅を測定する溶融池形状測定機構と、
前記溶融池の幅に対応する溶込み深さと、前記溶融池の幅と前記溶込み深さとに基づく溶接品質の良否判断を記録したデータベースとを備えることを特徴とするレーザ溶接装置を提供する。
被溶接材にレーザ光を照射することにより溶融池を形成するレーザヘッドと、
溶接品質の良否を判定するレーザ溶接良否判定機構とを具備し、
前記レーザ溶接良否判定機構は、前記溶融池を撮影して該溶融池の画像データを取得する撮影装置と、前記画像データを解析処理するデータ処理装置とを有し、
前記データ処理装置は、
前記溶融池の画像データの輝度を測定する輝度測定機構と、
前記輝度に基づいて、溶接方向に直交する方向の前記溶融池の幅を測定する溶融池形状測定機構と、
前記溶融池の幅に対応する溶込み深さと、前記溶融池の幅と前記溶込み深さとに基づく溶接品質の良否判断を記録したデータベースとを備えることを特徴とするレーザ溶接装置を提供する。
本発明によれば、溶接ビードの内部欠陥の影響を強く受ける溶接品質の判定精度が向上するレーザ溶接良否判定方法を提供することができる。また、該良否判定方法を実施する機構を備えるレーザ溶接装置を提供することができる。
以下、本発明の実施形態について、図面を参照しながら具体的に説明する。なお、本発明は、ここで取り上げた実施形態に限定されることはなく、発明の技術的思想を逸脱しない範囲で適宜組み合わせや改良が可能である。
[第1実施形態]
図1は、本発明の第1実施形態に係るレーザ溶接装置の構成例および利用例を示す模式図である。本実施形態では、溶接継手としてステンレス鋼板(板厚2.0mm)を用いた突合せ溶接とし、熱源となるレーザとしてファイバーレーザ(波長1070~1080nm)を用いた場合を例として説明する。当然のことながら、他の材料からなる溶接継手であってもよいし、他の波長のレーザ光を使用してもよい。
図1は、本発明の第1実施形態に係るレーザ溶接装置の構成例および利用例を示す模式図である。本実施形態では、溶接継手としてステンレス鋼板(板厚2.0mm)を用いた突合せ溶接とし、熱源となるレーザとしてファイバーレーザ(波長1070~1080nm)を用いた場合を例として説明する。当然のことながら、他の材料からなる溶接継手であってもよいし、他の波長のレーザ光を使用してもよい。
本実施形態におけるレーザ溶接の方法・手順を説明する。
レーザ発振器(図示なし)で発生したレーザ光2は、伝送ファイバー1を経由してレーザヘッド3内に導入され、レーザヘッド3内のコリメーションレンズ4およびハーフミラー5を通過した後にレーザ光用集光レンズ6によって集光され、ステンレス鋼板が突合せられた被溶接材7に照射される。被溶接材7が固定されている場合はレーザヘッド3を図中の溶接方向に移動させて溶接し、レーザヘッド3が固定されている場合は被溶接材7を図中の溶接方向と逆方向に移動させて溶接する。言い換えると、被溶接材7に照射するレーザ光2の被溶接材7に対する相対移動方向が溶接方向となる。
レーザ光2の照射により被溶接材7の表面に溶融池が形成され、被溶接材7の溶融に起因する放射光が放出される。溶融池からの放射光は、集光レンズ6を通過し、ハーフミラー5によってコリメーションレンズ4と異なる方向に反射され、撮影装置9(例えば、カメラ)の前に取り付けられたカメラ用集光レンズ8により集光されて、撮影装置(カメラ)9に入射する。カメラ9で撮影された画像データは、データ処理装置10により解析処理され、解析結果が表示装置11(例えば、画像モニタ)に表示される。
本実施形態においては、ハーフミラー5がレーザ光2の光軸上に設置されているため、カメラ9の光軸もレーザ光2の光軸上に設置されているのと同義になる。その結果、カメラ9が撮影した溶融池の形状は、実際の溶融池と同じ形状を有する。従って、レーザ光用集光レンズ6およびカメラ用集光レンズ8の焦点距離と、撮影した画像の溶融池の大きさとから実際の溶融池の大きさを算出することができる。
図2は、第1実施形態のレーザ溶接装置のカメラで撮影された溶融池の一例を示す画像データである。図中の白色の領域は溶融池の範囲を示している。
図2に示したように、取得した溶融池の画像データから、画像処理方法を用いて溶融池の幅と長さとを測定することができる。本発明においては、溶接方向の直交方向における溶融池の最大長さを溶融池の幅と定義し、溶接方向における溶融池の最大長さを溶融池の長さと定義する。
図3は、溶融池の幅および長さを測定する方法の一例を示す模式図である。溶融池の幅を測定する場合、溶接方向と直交する方向に沿って輝度分布を計測する。輝度はデータ処理装置10内の輝度計測機構(図示なし)で計測される。図3に示したように、溶接方向から見た溶融池の中央(溶接方向の直交方向における溶融池の中央)は、集光されたレーザ光が照射される領域(入熱量が放熱量よりも大きい領域)なので溶融池の温度が高くなり、放射光の輝度も高くなる。溶接方向から見た溶融池の両端(溶接方向の直交方向における溶融池の両端)は、レーザ光の照射領域から離れているため放熱量が多くなり、被溶接材7(母材)が溶融状態を保つ境界(例えば、融点)に位置することから、放射光の輝度も低くなる。溶融池の幅の例としては1~20mmがある。
溶融池の長さを測定する場合は、溶接方向に沿って輝度分布を計測する。図3に示したように、溶融池の図中左側(溶接方向前方)は、レーザ照射後からの経過時間が短い領域(入熱量が放熱量よりも大きい領域)なので溶融池の温度が高く、放射光の輝度も高くなる。溶融池の図中右側(溶接方向後方)ほど冷却が進み(入熱量よりも放熱量が大きくなって)溶融池の温度が下がり、放射光の輝度も低くなる。溶融池の長さの例としては3~20mmがある。
溶融池の判定にあたっては、被溶接材の溶融時の放射光の輝度を別途測定し、溶融状態か否かを判断する輝度閾値をあらかじめ定めておくことが好ましい。取得した画像データ中でその輝度閾値以上の輝度を示すひとまとまりの部分を溶融池と判定し、輝度閾値未満の輝度の部分を溶融池以外の部分と判定して溶融池の形状を検出する。
次に、検出された溶融池の幅方向(溶接方向の直交方向)において、輝度閾値を示す2点間の距離を求める。この2点間の距離が最大となる位置が溶融池の幅である。溶融池の長さ(溶接方向の長さ)も同様に求めることができる。このように溶融池の形状(幅および長さ)の推移は、4ヶ所の輝度変化から測定される。例えば、画像全体を2値化することにより、溶融池の周縁の任意2点間距離を容易に測定することができる。
図4は、第1実施形態により得られた溶接ビードの断面形状の一例を示す模式図である。図4は溶接方向から見た溶接部分の断面図である。溶接ビード12は、溶融池が冷却後に固化したものであり、溶接作業中は溶融池であった部分である。つまり、溶接ビード幅は溶融池の幅と同じである。レーザを直進させて溶接した際の溶融池の幅と溶込み深さとには相関があり、溶込み深さが深くなるほど溶融池の幅は広くなりやすい。これは、被溶接材7の深さ方向を溶かす間に被溶接材7の幅方向にも熱が伝わることにより、結果として溶融池が幅広くなるためである。
本実施形態で使用した板厚2mmのステンレス鋼に対し、種々の溶接条件(レーザ出力:500~3000W、ビームスポット径:0.1~1.2mm、溶接速度:10~100mm/s)でレーザ溶接を行ったところ、溶込み深さの増加に伴って溶融池の幅も増加することを確認した。このような知見に基づき、種々の溶融池の幅に対応する溶接ビードの深さ(=溶込み深さ)の記録をデータベースとしてあらかじめ作成し、データ処理装置10に保存しておくことが好ましい。溶込み深さは、溶接部分の強度や密閉性といった溶接品質に特に影響するので、溶接良否の判定基準として溶込み深さを用いることは溶接品質の判定精度の向上に寄与する。取得した画像データから求めた溶融池の幅と上記データベースとを照合することにより、溶接中に溶込み深さを推測・算定することができる。
さらに、得られた溶融池の幅と溶込み深さとを用いて溶接品質の良否を判断するためのデータベースを作成し、データ処理装置10に保存しておくことが好ましい。所定値以上の溶込み深さを確保できれば、溶接強度を担保できる。言い換えると、要求される溶接強度を確保するためには、所定値以上の溶込み深さを確保する必要がある。一方、溶融池の幅が広くなり過ぎると、望まない溶接変形が生じたり溶接部の残留応力が増大したりするため、溶融池の幅を所定値以下にすることが好ましい。言い換えると、溶接変形や残留応力を抑制するためには、所定値以下の溶融池の幅とする必要がある。
ただし、前述したように、溶接パラメータの変動(例えば、レーザ出力のゆらぎ、レーザヘッドと被溶接材との距離の変動に伴うビームスポット径のゆらぎ)や周囲環境の変動(例えば、気温の変動)により、被溶接材の溶融状態にはばらつきが生じ易い(例えば、溶融池の幅が同じでも溶込み深さがばらつくことがある)。そのため、データベースの作成に際し、それらのばらつきを考慮することがより好ましい。
図5は、溶融池形状のばらつきを考慮したデータベース(溶融池の幅と溶込み深さとの関係)に基づいた溶接品質の良否判定基準の一例を示す模式図である。図5に示したように、画像データから得られた溶融池の幅と溶込み深さとが、図中の斜線領域(OK)に入るか否かで、溶接品質の良否を判定する。溶融池の画像データ(被溶接材の表面情報)から溶込み深さ(被溶接材の内部情報)を得ることができ、その溶込み深さを溶接の判定基準に用いることにより、溶接ビードの内部状態と強く相関する溶接品質(例えば、溶接強度や密閉性)の良否を判定することができるので、溶接品質の判定精度を向上することができる。
また、溶融池の幅と長さとの両方のデータに基づいた溶込み深さのデータベースを作成すれば、適切な溶接速度の情報も含んだデータベースとなる。画像データから溶融池の幅と長さとの両方を測定し、これらを該データベースと照合して溶込み深さを推定・算定することにより、より高精度に溶接品質の良否を判定することができる。
図6は、本実施形態の溶接品質良否判定方法を示すフローチャート(図2~5の工程の流れ)である。図6に示したように、まず、溶融池をカメラで撮影して該溶融池の画像データをデータ処理装置に入力する。次に、取得した画像データに画像処理を行い、溶融池の形状(幅、長さ)を計測する。
溶融池の幅データを主体として溶接品質の良否を判定する場合は、あらかじめ作成した溶融池幅と溶込み深さとの関係のデータベースから溶込み深さを推測・算定する。溶込み深さデータを算定した後、溶融池幅および溶込み深さが溶接品質の良否の何れの領域に入るかを、あらかじめ作成した良否判定データベース(溶融池の幅と溶込み深さとの関係に基づいた溶接品質の良否判定データベース)と参照して、溶接品質の良否を判定する。
溶融池の幅データと長さデータとの両方を用いて溶接品質の良否を判定する場合は、あらかじめ作成した溶融池幅と溶融池長さと溶込み深さとの関係のデータベースから溶込み深さを推測・算定する。溶込み深さのデータを算定した後、溶融池幅と溶融池長さと溶込み深さとが溶接品質の良否の何れの領域に入るかを、あらかじめ作成した良否判定データベース(溶融池幅と溶融池長さと溶込み深さとの関係に基づいた溶接品質の良否判定データベース)と参照して、溶接品質の良否を判定する。
[第2実施形態]
図7は、第2実施形態に係る溶接品質良否判定方法を示すフローチャートである。先の第1実施形態においては、取得した画像データから計測した溶融池幅(または、溶融池幅と溶融池長さ)を用いて溶込み深さを推測・算定し、溶融池幅と溶込み深さとが(または、溶融池幅と溶融池長さと溶込み深さとが)適切な値の範囲に入っているか否かで溶接品質の良否を判定した。それに対し、第2実施形態は、図7に示したように、計測した溶融池幅(または、溶融池幅と溶融池長さ)を用いて溶込み深さを推測・算定する工程を省略している点において第1実施形態と異なる。すなわち、第2実施形態においては、計測した溶融池幅(または、溶融池幅と溶融池長さ)の値から、直接溶接品質の良否を判定するものである。本実施形態は、溶融池幅と溶込み深さとの関係において、ばらつきが小さい場合に有効である。
図7は、第2実施形態に係る溶接品質良否判定方法を示すフローチャートである。先の第1実施形態においては、取得した画像データから計測した溶融池幅(または、溶融池幅と溶融池長さ)を用いて溶込み深さを推測・算定し、溶融池幅と溶込み深さとが(または、溶融池幅と溶融池長さと溶込み深さとが)適切な値の範囲に入っているか否かで溶接品質の良否を判定した。それに対し、第2実施形態は、図7に示したように、計測した溶融池幅(または、溶融池幅と溶融池長さ)を用いて溶込み深さを推測・算定する工程を省略している点において第1実施形態と異なる。すなわち、第2実施形態においては、計測した溶融池幅(または、溶融池幅と溶融池長さ)の値から、直接溶接品質の良否を判定するものである。本実施形態は、溶融池幅と溶込み深さとの関係において、ばらつきが小さい場合に有効である。
より具体的には、良否判定データベースとして、入力される溶融池幅データ(または、溶融池幅データと溶融池長さデータ)に対して、該入力データに対応する溶込み深さデータと、該溶込み深さデータおよび入力データの組み合わせから判定される適正範囲データとをまとめたデータベースを用いることにより、溶融池幅(または、溶融池幅と溶融池長さ)の測定値のみから、直接溶接品質の良否判定が可能になる。本実施形態によれば、図6で示す判定方法よりも判定フローが簡素化するため、より高速に(より短時間で)良否判定することができる。
[第3実施形態]
図8は、本発明の第3実施形態に係るレーザ溶接装置の構成例および利用例を示す模式図である。本実施形態では、溶接継手としてステンレス鋼板(板厚1.2mm)を用いた突合せ溶接とし、熱源となるレーザとして可視光~近赤外光(波長500~880nm)のレーザを用いた場合を例として説明する。
図8は、本発明の第3実施形態に係るレーザ溶接装置の構成例および利用例を示す模式図である。本実施形態では、溶接継手としてステンレス鋼板(板厚1.2mm)を用いた突合せ溶接とし、熱源となるレーザとして可視光~近赤外光(波長500~880nm)のレーザを用いた場合を例として説明する。
本実施形態におけるレーザ溶接の方法・手順を説明する。レーザ発振器(図示なし)で発生したレーザ光2は、伝送ファイバー1を経由してレーザヘッド3内に導入され、レーザヘッド3内のコリメーションレンズ4を通過した後にレーザ光用集光レンズ6によって集光され、上記のステンレス鋼板が突合せられた被溶接材7の表面に照射される。レーザ光2の照射により被溶接材7の表面に溶融池が形成され、被溶接材7の溶融に起因する放射光が放出される。
本実施形態は、レーザヘッド3内にハーフミラーが設置されておらず、カメラ9の光軸がレーザ光2の光軸上ではなく、レーザ光軸と所定の角度をなして設置されている点で第1実施形態と異なり、他を第1又は第2実施形態と同じにする。レーザヘッド3とカメラ9との相対位置を変えず、カメラ9の光軸(カメラ9に入射する放射光、図中の一点鎖線)とレーザ光軸との角度を一定に保持した状態で溶接する。本実施形態におけるカメラ9は、例えば、溶接方向に沿ったレーザ光2の後方で、カメラ9の光軸とレーザ光軸とのなす角度13が30°の位置に設置されている。当然のことながら、角度13は30°に限定されるものではない。
本実施形態においては、カメラ9に入射する放射光の軸とレーザ光軸とが同軸ではないため、カメラ9が撮影した溶融池の形状(例えば、幅、長さ、それらの比率)は、実際の溶融池の形状と一致しない。ただし、レーザヘッド3と被溶接材7とカメラ9との相対位置(例えば、レーザ光用集光レンズ6の焦点距離、カメラ9の光軸とレーザ光軸とのなす角度13、画像データにおける溶融池の形状)から、実際の溶融池の大きさを算出することができる。
[第4実施形態]
図9は、本発明の第4実施形態に係るレーザ溶接装置の構成例および利用例を示す模式図である。本実施形態では、溶接継手として外径が異なる二つの円筒状被溶接材14,15を用いた嵌め込み溶接とし、熱源となるレーザとして可視光~近赤外光(波長500~880nm)のレーザを用いた場合を例として説明する。
図9は、本発明の第4実施形態に係るレーザ溶接装置の構成例および利用例を示す模式図である。本実施形態では、溶接継手として外径が異なる二つの円筒状被溶接材14,15を用いた嵌め込み溶接とし、熱源となるレーザとして可視光~近赤外光(波長500~880nm)のレーザを用いた場合を例として説明する。
図9に示したように、本実施形態で用いるレーザ溶接装置は、第1実施形態のレーザ溶接装置と同様に、レーザヘッド3内でレーザ光2の光軸上にハーフミラー5が設置されており、カメラ9の光軸がレーザ光2の光軸上に設置されていると見なすことができる。また、本実施形態の嵌め込み溶接は、円筒状被溶接材15の内側空間に円筒状被溶接材14を嵌めこみ、嵌め込んだ二つの円筒状被溶接材を回転させながら該二つの円筒状被溶接材の接触部分にレーザ光2を照射して溶接を行った。このとき、円筒状被溶接材14,15の回転軸とレーザ光軸とのなす角度13’が60°になるように配置した。
図10は、第4実施形態により得られた溶接ビードの断面形状の一例を示す模式図である。本実施形態における溶接ビード12の幅(すなわち、溶融池の幅)は、平面にレーザ照射した場合の溶融池幅と異なり、円筒状被溶接材14,15の回転軸とレーザ光軸とのなす角度13’に依存する。そのため、カメラ9で取り込んだ画像データの解析にあたり、この角度を用いて画像データの溶融池幅を補正することが好ましい。また、本実施形態においては、円筒状被溶接材の周方向に溶接していることから、厳密には溶融池の表面は溶接方向で曲面となる(溶融池の長さ方向の断面は円弧形状となる)。そのため、実際の溶融池長さを求めるためには、溶融池中央から被溶接材の回転軸までの距離(溶接部の回転半径)を用いて、取り込んだ画像データの溶融池長さを補正することが好ましい。ただし、溶接部における円筒状被溶接材の径が溶融池長さに比して十分大きい場合は、溶融池の表面を平面に近似できるため、取り込んだ画像データの溶融池長さをそのまま採用してもよい。
溶接品質の良否判定は、前述の第1実施形態と同様にして行うことができる。具体的には、カメラ9を用いて溶融池の画像データを取得し、データ処理装置10に搭載する画像処理プログラムで解析処理して溶融池の幅(または、幅と長さ)を計測する。その後、データ処理装置10にあらかじめ記憶させた溶融池幅と溶込み深さとの関係のデータベース、または溶融池幅と溶融池長さと溶込み深さとの関係のデータベースから溶込み深さを推測・算定する。溶込み深さデータを推測・算定した後、データ処理装置10にあらかじめ記憶させた良否判定データベース(溶融池幅の閾値と溶込み深さの閾値とに基づくデータベース、または溶融池幅の閾値と溶融池長さの閾値と溶込み深さの閾値とに基づくデータベース)と参照して、溶接品質の良否を判定する。
図11および図12は、第4実施形態により得られた溶接ビードの断面形状の他の例を示す模式図である。図11,12に示したように、本実施形態の溶接継手は、円筒状被溶接材14,15の突合わせ継手であってもよい。また、本実施形態は、溶接品質の良否判定方法が第2実施形態と同様であってもよいし、レーザ溶接装置が第3実施形態と同様の構成を有していてもよい。
[第5実施形態]
図13は、本発明の第5実施形態に係るレーザ溶接装置の構成例および利用例を示す模式図である。本実施形態では、溶接継手として外径が異なる二つの円筒状被溶接材16,17を用いた重ね溶接とし、熱源となるレーザとしてファイバーレーザ(波長1070~1080nm)を用いた場合を例として説明する。
図13は、本発明の第5実施形態に係るレーザ溶接装置の構成例および利用例を示す模式図である。本実施形態では、溶接継手として外径が異なる二つの円筒状被溶接材16,17を用いた重ね溶接とし、熱源となるレーザとしてファイバーレーザ(波長1070~1080nm)を用いた場合を例として説明する。
図13に示したように、本実施形態で用いるレーザ溶接装置は、第1実施形態のレーザ溶接装置と同様の構成を有している。また、本実施形態の重ね溶接は、円筒状被溶接材16の内側空間に円筒状被溶接材17を嵌めこみ、嵌め込んだ二つの円筒状被溶接材を回転させながら外側の円筒状被溶接材16の上からレーザ光2を垂直に照射し、円筒状被溶接材16をレーザ光で貫通させて(溶融池が円筒状被溶接材16を貫通して円筒状被溶接材17に到達するようにして)、溶接を行った。このとき、円筒状被溶接材16,17の回転軸とレーザ光軸とが直交するように配置した。
図14は、第5実施形態により得られた溶接ビードの断面形状の一例を示す模式図である。本実施形態における溶接ビード12の幅(すなわち、溶融池の幅)は、平面にレーザ照射した場合の溶融池幅と同じであるため、第1実施形態と同様にして溶込み深さを推測・算定し、溶接品質の良否を判定することができる。また、溶融池長さを計測する場合は、第4実施形態と同様に、円筒状被溶接材16の外径に応じて画像データの溶融池長さを補正した上で、溶接品質の良否判定に用いればよい。
図15は、第5実施形態により得られた溶接ビードの断面形状の他の一例を示す模式図である。図15に示したように、本実施形態の溶接継手は、同じ外径を有する二つの円柱状被溶接材18,19の突合わせ継手であってもよい。
上述した実施形態は、本発明の理解を助けるために具体的に説明したものであり、本発明は、説明した全ての構成を備えることに限定されるものではない。例えば、ある実施形態の構成の一部を他の実施形態の構成に置き換えることが可能であり、ある実施形態の構成に他の実施形態の構成を加えることも可能である。さらに、各実施形態の構成の一部について、削除・他の構成に置換・他の構成の追加をすることが可能である。
1…伝送ファイバー、2…レーザ光、3…レーザヘッド、4…コリメーションレンズ、5…ハーフミラー、6…集光レンズ、7…被溶接材、8…集光レンズ、9…撮影装置(カメラ)、10…データ処理装置、11…表示装置、12…溶接ビード、13,13’…レーザ光軸となす角度、14~17…円筒状被溶接材、18,19…円柱状被溶接材。
Claims (11)
- レーザ溶接中に溶接品質の良否を判定する方法であって、
被溶接材にレーザ光を照射することにより形成された溶融池を撮影して前記溶融池の画像データを取得する工程と、
取得した前記溶融池の画像データから、溶接方向に直交する方向の前記溶融池の幅を計測する工程と、
計測した前記溶融池の幅から溶込み深さを算定する工程と、
計測した前記溶融池の幅と算定した前記溶込み深さとから溶接品質の良否を判定する工程とを有することを特徴とするレーザ溶接良否判定方法。 - 請求項1に記載のレーザ溶接良否判定方法において、
前記溶融池の幅を計測する工程は、前記被溶接材の溶融時の放射光の輝度を輝度閾値とし、前記溶融池の画像データ中で前記輝度閾値以上の輝度を示す部分を溶融池として検出し、前記溶接方向に直交する方向において前記輝度閾値を示す2点間の距離のうち最大のものを前記溶融池の幅として計測する工程であることを特徴とするレーザ溶接良否判定方法。 - 請求項1又は請求項2に記載のレーザ溶接良否判定方法において、
前記溶込み深さを算定する工程は、あらかじめ定めたデータベースに、計測された前記溶融池の幅を照合して前記溶込み深さを算定する工程であることを特徴とするレーザ溶接良否判定方法。 - 請求項1又は請求項2に記載のレーザ溶接良否判定方法において、
該レーザ溶接良否判定方法は、取得した前記溶融池の画像データから、溶接方向の前記溶融池の長さを計測する工程を更に有し、
前記溶込み深さを算定する工程は、計測した前記溶融池の幅と計測した前記溶融池の長さとから前記溶込み深さを算定する工程であることを特徴とするレーザ溶接良否判定方法。 - 請求項4に記載のレーザ溶接良否判定方法において、
前記溶込み深さを算定する工程は、あらかじめ定めたデータベースに、計測した前記溶融池の幅と長さとを照合して前記溶込み深さを算定する工程であることを特徴とするレーザ溶接良否判定方法。 - 請求項4又は請求項5に記載のレーザ溶接良否判定方法において、
前記溶接品質の良否を判定する工程は、計測した前記溶融池の幅と計測した前記溶融池の長さと算定した前記溶込み深さとから前記溶接品質の良否を判定する工程であることを特徴とするレーザ溶接良否判定方法。 - レーザ溶接中に溶接品質の良否を判定する方法であって、
被溶接材にレーザ光を照射することにより形成された溶融池を撮影して前記溶融池の画像データを取得する工程と、
取得した前記溶融池の画像データから、溶接方向に直交する方向の前記溶融池の幅を計測する工程と、
計測した前記溶融池の幅とあらかじめ定めたデータベースの溶込み深さとから溶接品質の良否を判定する工程とを有することを特徴とするレーザ溶接良否判定方法。 - 請求項7に記載のレーザ溶接良否判定方法において、
前記溶融池の幅を計測する工程は、前記被溶接材の溶融時の放射光の輝度を輝度閾値とし、前記溶融池の画像データ中で前記輝度閾値以上の輝度を示す部分を溶融池として検出し、前記溶接方向に直交する方向において前記輝度閾値を示す2点間の距離のうち最大のものを前記溶融池の幅として計測する工程であることを特徴とするレーザ溶接良否判定方法。 - 請求項7又は請求項8に記載のレーザ溶接良否判定方法において、
該レーザ溶接良否判定方法は、取得した前記溶融池の画像データから、溶接方向の前記溶融池の長さを計測する工程を更に有し、
前記溶接品質の良否を判定する工程は、計測した前記溶融池の幅と計測した前記溶融池の長さと前記データベースの溶込み深さとから溶接品質の良否を判定する工程であることを特徴とするレーザ溶接良否判定方法。 - レーザ溶接中に溶接品質の良否を判定する機構を備えるレーザ溶接装置であって、
被溶接材にレーザ光を照射することにより溶融池を形成するレーザヘッドと、
溶接品質の良否を判定するレーザ溶接良否判定機構とを具備し、
前記レーザ溶接良否判定機構は、前記溶融池を撮影して該溶融池の画像データを取得する撮影装置と、前記画像データを解析処理するデータ処理装置とを有し、
前記データ処理装置は、
前記溶融池の画像データの輝度を測定する輝度測定機構と、
前記輝度に基づいて、溶接方向に直交する方向の前記溶融池の幅を測定する溶融池形状測定機構と、
前記溶融池の幅に対応する溶込み深さを記録した第一データベースと、
前記溶融池の幅と前記溶込み深さとに基づく溶接品質の良否判断を記録した第二データベースとを備えることを特徴とするレーザ溶接装置。 - レーザ溶接中に溶接品質の良否を判定する機構を備えるレーザ溶接装置であって、
被溶接材にレーザ光を照射することにより溶融池を形成するレーザヘッドと、
溶接品質の良否を判定するレーザ溶接良否判定機構とを具備し、
前記レーザ溶接良否判定機構は、前記溶融池を撮影して該溶融池の画像データを取得する撮影装置と、前記画像データを解析処理するデータ処理装置とを有し、
前記データ処理装置は、
前記溶融池の画像データの輝度を測定する輝度測定機構と、
前記輝度に基づいて、溶接方向に直交する方向の前記溶融池の幅を測定する溶融池形状測定機構と、
前記溶融池の幅に対応する溶込み深さと、前記溶融池の幅と前記溶込み深さとに基づく溶接品質の良否判断を記録したデータベースとを備えることを特徴とするレーザ溶接装置。