WO2014068955A1 - 光ファイバテープ心線 - Google Patents
光ファイバテープ心線 Download PDFInfo
- Publication number
- WO2014068955A1 WO2014068955A1 PCT/JP2013/006388 JP2013006388W WO2014068955A1 WO 2014068955 A1 WO2014068955 A1 WO 2014068955A1 JP 2013006388 W JP2013006388 W JP 2013006388W WO 2014068955 A1 WO2014068955 A1 WO 2014068955A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- optical fiber
- coating layer
- fiber ribbon
- core
- monomer
- Prior art date
Abstract
Description
Claims (2)
- 複数の光ファイバ心線と、
オリゴマー状の非結晶性のポリプロピレングリコールを含む紫外線硬化樹脂を備えるとともに、前記光ファイバ心線の周囲に構成された一括被覆層を有し、
前記一括被覆層は、
12MPa以上20MPa以下の平衡弾性率、及び
5%以上9%以下の降伏点伸び
を備え、
前記一括被覆層と前記光ファイバ心線の最外層との密着力が、
12N/cm以上15N/cm以下
である、光ファイバテープ心線。 - 請求項1に記載の光ファイバテープ心線を使用した光ファイバケーブル。