WO2013189601A1 - Bande métallique revêtue d'un seul côté - Google Patents
Bande métallique revêtue d'un seul côté Download PDFInfo
- Publication number
- WO2013189601A1 WO2013189601A1 PCT/EP2013/001816 EP2013001816W WO2013189601A1 WO 2013189601 A1 WO2013189601 A1 WO 2013189601A1 EP 2013001816 W EP2013001816 W EP 2013001816W WO 2013189601 A1 WO2013189601 A1 WO 2013189601A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal strip
- metal
- coated
- steel
- coating
- Prior art date
Abstract
La présente invention concerne un procédé de fabrication d'une bande métallique revêtue, comprenant les étapes consistant à : (i) utiliser un empilement de bandes métalliques comprenant une première bande métallique et une seconde bande métallique, la première bande métallique présentant une première surface intérieure et une première surface extérieure et la seconde bande métallique présentant une seconde surface intérieure et une seconde surface extérieure ; (ii) disposer un matériau de revêtement sur l'empilement de bandes métalliques, au moins la première surface extérieure et la seconde surface extérieure étant revêtues du matériau de revêtement et au moins une partie de la première surface intérieure et de la seconde surface intérieure n'étant pas revêtues du matériau de revêtement ; (iii) séparer la première bande métallique et la seconde bande métalliques revêtues pour obtenir deux bandes métalliques revêtues d'un seul côté.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP12004618.0 | 2012-06-20 | ||
EP12004618 | 2012-06-20 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2013189601A1 true WO2013189601A1 (fr) | 2013-12-27 |
Family
ID=48699719
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2013/001816 WO2013189601A1 (fr) | 2012-06-20 | 2013-06-20 | Bande métallique revêtue d'un seul côté |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2013189601A1 (fr) |
Citations (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3177085A (en) | 1960-07-27 | 1965-04-06 | Nalco Chemical Co | Silica sol-masking in galvanizing process |
US3177053A (en) * | 1959-12-28 | 1965-04-06 | Armco Steel Corp | Differentially coated galvanized strip |
US3181963A (en) * | 1960-11-08 | 1965-05-04 | Wheeling Steel Corp | Alkali metal borate masking in galvanizing process |
US3383250A (en) * | 1964-10-07 | 1968-05-14 | Armco Steel Corp | Method for producing one side metallic coated strip |
GB1303057A (fr) * | 1969-09-29 | 1973-01-17 | ||
US4120997A (en) | 1976-05-11 | 1978-10-17 | Inland Steel Company | Process for producing one-side galvanized sheet material |
EP0000860A1 (fr) * | 1977-08-17 | 1979-03-07 | VOEST-ALPINE Aktiengesellschaft | Procédé et appareillage pour l'obtention de tôles revêtues sur une face par galvanisation à chaud |
JPS5443838A (en) * | 1977-09-16 | 1979-04-06 | Mitsubishi Heavy Ind Ltd | One-side plating process for long-sized metal sheet |
GB2008619A (en) * | 1977-10-25 | 1979-06-06 | Arbed | Hot Dip Metal Coating One Face of a Metal Sheet |
JPS54108835A (en) * | 1978-02-15 | 1979-08-25 | Nippon Kokan Kk <Nkk> | Surface treatment of one side of steel strip |
JPS5554556A (en) * | 1978-10-14 | 1980-04-21 | Toyota Motor Corp | One side plating method for metal sheet |
JPS56105462A (en) * | 1980-01-25 | 1981-08-21 | Nippon Steel Corp | Production of steel plate with hot-dipped coating on one side thereof |
JPS5719367A (en) * | 1980-07-09 | 1982-02-01 | Sumitomo Metal Ind Ltd | Production of one side plated steel plate |
US4409265A (en) * | 1981-01-21 | 1983-10-11 | Mannesmann Aktiengesellschaft | Method and apparatus for the one-sided coating of continuous metal strip |
US4610389A (en) * | 1985-02-25 | 1986-09-09 | Comet Research, Inc. | Method for treating a single side of a metallic sheet |
-
2013
- 2013-06-20 WO PCT/EP2013/001816 patent/WO2013189601A1/fr active Application Filing
Patent Citations (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3177053A (en) * | 1959-12-28 | 1965-04-06 | Armco Steel Corp | Differentially coated galvanized strip |
US3177085A (en) | 1960-07-27 | 1965-04-06 | Nalco Chemical Co | Silica sol-masking in galvanizing process |
US3181963A (en) * | 1960-11-08 | 1965-05-04 | Wheeling Steel Corp | Alkali metal borate masking in galvanizing process |
US3383250A (en) * | 1964-10-07 | 1968-05-14 | Armco Steel Corp | Method for producing one side metallic coated strip |
GB1303057A (fr) * | 1969-09-29 | 1973-01-17 | ||
US4120997A (en) | 1976-05-11 | 1978-10-17 | Inland Steel Company | Process for producing one-side galvanized sheet material |
EP0000860A1 (fr) * | 1977-08-17 | 1979-03-07 | VOEST-ALPINE Aktiengesellschaft | Procédé et appareillage pour l'obtention de tôles revêtues sur une face par galvanisation à chaud |
JPS5443838A (en) * | 1977-09-16 | 1979-04-06 | Mitsubishi Heavy Ind Ltd | One-side plating process for long-sized metal sheet |
GB2008619A (en) * | 1977-10-25 | 1979-06-06 | Arbed | Hot Dip Metal Coating One Face of a Metal Sheet |
JPS54108835A (en) * | 1978-02-15 | 1979-08-25 | Nippon Kokan Kk <Nkk> | Surface treatment of one side of steel strip |
JPS5554556A (en) * | 1978-10-14 | 1980-04-21 | Toyota Motor Corp | One side plating method for metal sheet |
JPS56105462A (en) * | 1980-01-25 | 1981-08-21 | Nippon Steel Corp | Production of steel plate with hot-dipped coating on one side thereof |
JPS5719367A (en) * | 1980-07-09 | 1982-02-01 | Sumitomo Metal Ind Ltd | Production of one side plated steel plate |
US4409265A (en) * | 1981-01-21 | 1983-10-11 | Mannesmann Aktiengesellschaft | Method and apparatus for the one-sided coating of continuous metal strip |
US4610389A (en) * | 1985-02-25 | 1986-09-09 | Comet Research, Inc. | Method for treating a single side of a metallic sheet |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
KR102075278B1 (ko) | Lme 문제를 가지지 않는 경화 부품의 제조 방법 | |
US10287647B2 (en) | Method for producing a steel component having a metal coating protecting it against corrosion, and steel component | |
RU2429084C2 (ru) | Стальной плоский прокат и способ изготовления стального тонкого проката | |
KR101849480B1 (ko) | 자동차 부품 및 자동차 부품의 제조 방법 | |
JP5444650B2 (ja) | ホットプレス用めっき鋼板及びその製造方法 | |
JP2020056099A (ja) | アルミニウムをベースとする金属コーティングで被覆された鋼板 | |
JP2010501725A (ja) | 6−30重量%のMnを含有する熱間圧延鋼板または冷間圧延鋼板に金属保護層をめっきする方法 | |
EP2702178A1 (fr) | Composite de feuillard en acier et son procédé de fabrication | |
CA2991549A1 (fr) | Procede de fabrication d'une piece apte a la phosphatation a partir d'une tole d'acier revetue d'un revetement metallique a base d'aluminium | |
EP2808417A1 (fr) | Tôle d'acier destinée à l'emboutissage à chaud, son procédé de fabrication et procédé pour la production d'un élément embouti à chaud l'utilisant | |
US9440417B2 (en) | Method of making a metal-strip laminate | |
MX2014009731A (es) | Lamina de acero chapada para prensado en caliente y metodo de prensado en caliente de lamina de acero revestida. | |
EP2794951B1 (fr) | Substrat avec double couche stratifiée | |
JP2006299377A (ja) | 塗料密着性、塗装後耐食性に優れたAl系めっき鋼板及びこれを用いた自動車部材並びにAl系めっき鋼板の製造方法 | |
KR102068916B1 (ko) | 알루미늄 기반의 금속 코팅으로 코팅되고 티타늄을 포함하는 강판 | |
WO2009114349A1 (fr) | Tôle d'acier stratifiée | |
US20180179642A1 (en) | Component, in Particular Structural Component, for a Motor Vehicle, as well as a Method for Producing a Component | |
JP2922926B2 (ja) | 合金化亜鉛めっき帯鋼の製法 | |
WO2005024093A1 (fr) | Bande d'acier inoxydable recouverte d'aluminium | |
CN111575622B (zh) | 一种具有优异涂装性能的热成形零部件用的镀铝钢板及其制造方法及热成形零部件 | |
WO2016092720A1 (fr) | Procédé permettant de fabriquer un produit moulé à la presse à chaud et produit moulé à la presse à chaud | |
WO2013189601A1 (fr) | Bande métallique revêtue d'un seul côté | |
JP3130470B2 (ja) | プレス加工性及びメッキ密着性に優れる高強度溶融亜鉛メッキ鋼板 | |
JP2001355054A (ja) | 加工性に優れた溶融亜鉛−アルミニウム合金めっき鋼板とその製造方法 | |
JP2004002931A (ja) | 抵抗溶接性に優れたアルミニウムめっき鋼板とこれを用いた加工部品 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 13731687 Country of ref document: EP Kind code of ref document: A1 |
|
DPE1 | Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101) | ||
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 13731687 Country of ref document: EP Kind code of ref document: A1 |