WO2013166663A1 - 包覆有金属纳米颗粒的硅酸盐发光材料及其制备方法 - Google Patents
包覆有金属纳米颗粒的硅酸盐发光材料及其制备方法 Download PDFInfo
- Publication number
- WO2013166663A1 WO2013166663A1 PCT/CN2012/075207 CN2012075207W WO2013166663A1 WO 2013166663 A1 WO2013166663 A1 WO 2013166663A1 CN 2012075207 W CN2012075207 W CN 2012075207W WO 2013166663 A1 WO2013166663 A1 WO 2013166663A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal nanoparticles
- preparing
- silicate luminescent
- luminescent material
- metal
- Prior art date
Abstract
Description
Claims